US20070215301A1 - Method for making a low density multi-ply paperboard with high internal bond strength - Google Patents
Method for making a low density multi-ply paperboard with high internal bond strength Download PDFInfo
- Publication number
- US20070215301A1 US20070215301A1 US11/686,742 US68674207A US2007215301A1 US 20070215301 A1 US20070215301 A1 US 20070215301A1 US 68674207 A US68674207 A US 68674207A US 2007215301 A1 US2007215301 A1 US 2007215301A1
- Authority
- US
- United States
- Prior art keywords
- fiber
- paperboard
- starch
- anionic
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H23/00—Processes or apparatus for adding material to the pulp or to the paper
- D21H23/02—Processes or apparatus for adding material to the pulp or to the paper characterised by the manner in which substances are added
- D21H23/04—Addition to the pulp; After-treatment of added substances in the pulp
- D21H23/06—Controlling the addition
- D21H23/08—Controlling the addition by measuring pulp properties, e.g. zeta potential, pH
- D21H23/10—Controlling the addition by measuring pulp properties, e.g. zeta potential, pH at least two kinds of compounds being added
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H21/00—Non-fibrous material added to the pulp, characterised by its function, form or properties; Paper-impregnating or coating material, characterised by its function, form or properties
- D21H21/14—Non-fibrous material added to the pulp, characterised by its function, form or properties; Paper-impregnating or coating material, characterised by its function, form or properties characterised by function or properties in or on the paper
- D21H21/18—Reinforcing agents
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H23/00—Processes or apparatus for adding material to the pulp or to the paper
- D21H23/02—Processes or apparatus for adding material to the pulp or to the paper characterised by the manner in which substances are added
- D21H23/04—Addition to the pulp; After-treatment of added substances in the pulp
- D21H23/06—Controlling the addition
- D21H23/08—Controlling the addition by measuring pulp properties, e.g. zeta potential, pH
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H11/00—Pulp or paper, comprising cellulose or lignocellulose fibres of natural origin only
- D21H11/10—Mixtures of chemical and mechanical pulp
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H11/00—Pulp or paper, comprising cellulose or lignocellulose fibres of natural origin only
- D21H11/16—Pulp or paper, comprising cellulose or lignocellulose fibres of natural origin only modified by a particular after-treatment
- D21H11/20—Chemically or biochemically modified fibres
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
- D21H17/20—Macromolecular organic compounds
- D21H17/21—Macromolecular organic compounds of natural origin; Derivatives thereof
- D21H17/24—Polysaccharides
- D21H17/28—Starch
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
- D21H17/20—Macromolecular organic compounds
- D21H17/21—Macromolecular organic compounds of natural origin; Derivatives thereof
- D21H17/24—Polysaccharides
- D21H17/28—Starch
- D21H17/29—Starch cationic
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
- D21H17/20—Macromolecular organic compounds
- D21H17/33—Synthetic macromolecular compounds
- D21H17/34—Synthetic macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
- D21H17/41—Synthetic macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds containing ionic groups
- D21H17/44—Synthetic macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds containing ionic groups cationic
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
- D21H17/20—Macromolecular organic compounds
- D21H17/33—Synthetic macromolecular compounds
- D21H17/46—Synthetic macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
- D21H17/54—Synthetic macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds obtained by reactions forming in the main chain of the macromolecule a linkage containing nitrogen
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
- D21H17/63—Inorganic compounds
- D21H17/66—Salts, e.g. alums
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H27/00—Special paper not otherwise provided for, e.g. made by multi-step processes
- D21H27/30—Multi-ply
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H27/00—Special paper not otherwise provided for, e.g. made by multi-step processes
- D21H27/30—Multi-ply
- D21H27/38—Multi-ply at least one of the sheets having a fibrous composition differing from that of other sheets
Definitions
- the present application relates to a method for increasing the bond strength in a multi-ply paperboard that has high crosslinked cellulose fiber present in at least one of the plies.
- This application is directed to a method improving the internal bond strength of paperboard with greater than 25 percent crosslinked fiber in at least one ply.
- additives are added to the slurry in various combinations and order while maintaining the ionic demand of the slurry at less than zero. Paperboard with high ZDT, Scott Bond and Taber Stiffness is obtained.
- FIG. 1 is a schematic diagram of the pilot line.
- the density of the stratum will drop below 0.4 g/cc.
- the internal bond strength can drop so low as to not only be well below levels required for converting the paperboard into packaging products but also below the level where conventional methods of increasing the internal strength cannot provide enough increase to meet minimum levels needed for converting. This effect can occur either in the entire structure or some fraction within the structure.
- the present application provides a method for increasing the internal bond of low density paperboard back into the range which is useable for converting.
- a distinguishing characteristic of the present application is that at least one ply of the paperboard, whether a single-ply or a multiple-ply structure, contains crosslinked cellulose fibers and strength enhancing additives such as mechanically refined fiber, anionic and cationic starches and other additives to offset the board strength lost by adding the crosslinked cellulosic fibers.
- the crosslinked cellulosic fibers increase the bulk density of the insulating paperboard characteristics of the board.
- the paperboard also contains chemical pulp fibers.
- chemical pulp fibers useable in the present application are derived primarily from wood pulp. Suitable wood pulp fibers for use with the application can be obtained from well-known chemical processes such as the kraft and sulfite processes, with or without subsequent bleaching.
- Softwoods and hardwoods can be used. Details of the selection of wood pulp fibers are well known to those skilled in the art. For example, suitable cellulosic fibers produced from southern pine that are useable in the present application are available from a number of companies including Weyerhaeuser Company under the designations C-Pine, Chinook, CF416, FR416, and NB416. A bleached Kraft Douglas Fir pulp (D. Fir), and Grande Prairie Softwood, all manufactured by Weyerhaeuser are examples of northern softwoods that can be used.
- Non crosslinked cellulose fibers include chemithermomechanical pulp fibers (CTMP), bleached chemithermomechanical pulp fibers (BCTMP), thermomechanical pulp fibers (TMP), refiner groundwood pulp fibers, groundwood pulp fibers, TMP (thermomechanical pulp) made by Weyerhaeuser, Federal Way, Wash., and CTMP (chemi-thermomechanical pulp) obtained from NORPAC, Longview, Wash., sold as a CTMP NORPAC Newsprint Grade, jet dried cellulosic fibers and treated jet dried cellulosic fibers manufactured by the Weyerhaeuser Company by the method described in U.S. application Ser. No. 10/923,447 filed Aug. 20, 2004. These fibers are twisted kinked and curled. Additional fibers include flash dried and treated flash dried fibers as described in U.S. Pat. No. 6,837,970,
- Suitable crosslinking agents for making crosslinked fibers include carboxylic acid crosslinking agents such as polycarboxylic acids.
- carboxylic acid crosslinking agents such as polycarboxylic acids.
- Polycarboxylic acid crosslinking agents e.g., citric acid, propane tricarboxylic acid, and butane tetracarboxylic acid
- catalysts are described in U.S. Pat. Nos. 3,526,048; 4,820,307; 4,936,865; 4,975,209; and 5,221,285
- C 2 -C 9 polycarboxylic acids that contain at least three carboxyl groups e.g., citric acid and oxydisuccinic acid
- crosslinking agents is described in U.S. Pat. Nos. 5,137,537; 5,183,707; 5,190,563; 5,562,740; and 5,873,979.
- Polymeric polycarboxylic acids are also suitable crosslinking agents for making crosslinked fibers. These include polymeric polycarboxylic acid crosslinking agents are described in U.S. Pat. Nos. 4,391,878; 4,420,368; 4,431,481; 5,049,235; 5,160,789; 5,442,899; 5,698,074; 5,496,476; 5,496,477; 5,728,771; 5,705,475; and 5,981,739. Polyacrylic acid and related copolymers as crosslinking agents are described U.S. Pat. Nos. 5,549,791 and 5,998,511. Polymaleic acid crosslinking agents are described in U.S. Pat. No. 5,998,511 and U.S. Pat. No. 6,582,553. CHB405, a citric acid crosslinked cellulose fiber and CHB505, a polyacrylic acid crosslinked cellulose, both commercially available from Weyerhaeuser Company, Federal Way, Wash. were used in this work.
- crosslinked cellulosic fibers are present in at least one layer at a level of 25 to 80 percent by total fiber weight of the ply.
- the crosslinked fibers are present at a level of 40 to 75 percent by total fiber weight of the layer and in yet another embodiment they are present at a level of 50 to 70 percent by total fiber weight of the layer.
- the technology relies on the ability to balance the ionic demand in the wet end of the paper machine such that 1) anionic polymeric materials can be retained on the fibers and fines without excess remaining in the water system, 2) the fibers and system do not pass through the zero charge point which destabilizes retention and drainage 3) since pulp fibers are anionic, some cationic material can be added, however, adding too much cationic material without balancing the excess anionic demand will either cause the fibers to flocculate reducing formation and/or cause the drainage to drop, impacting the runnability.
- Each of the components used in the paperboard containing crosslinked fiber in this disclosure has a specific charge density typically measured by ionic demand titration.
- a Mutek PCD—Titrator was used for the particle charge titration coupled with the PCD 02 Particle Charge Detector for measuring the ionic demand of the component or fiber furnish. The method was performed according to a procedure from A.E. Staley Manufacturing, a subsidiary of Tate and Lyle, Decatur, Ill. The method is as follows.
- Ionic Demand refers to the amount of anionic or cationic charge required to neutralize the counter ion charge and is expressed in meq/g or ueq/kg.
- an additive with an ionic demand of +2.2 meq/g has an anionic demand of 2.2 meq/g; an additive with an ionic demand of ⁇ 1.8 meq/g has a cationic demand of 1.8 meq/g.
- Specific components whose ionic demand was measured by the Mutek method are noted in Table 1, other component values are from suppliers.
- the fiber slurry is anionic to start with and should remain anionic through the paper making process i.e. the ionic demand of the slurry should less than zero.
- Mechanically refined fiber can be added to the slurry to increase the strength of the paperboard.
- the mechanically refined fiber has a Canadian Standard Freeness of less than 125 mL CSF, a curl index of 1 ⁇ 3 or less of the unrefined fiber and a kink angle of 1 ⁇ 2or less of the unrefined fiber.
- mechanically refined fiber is added to the slurry followed by the addition of an anionic starch and then followed by addition of a cationic fixative. After each addition step the slurry ionic demand is less than zero.
- the slurry is deposited on a foraminous support, dewatered forming a web and dried to form a paperboard.
- Cationic fixatives such as cationic starch (e.g. STA-LOK® 300, STA-LOK® 330 and RediBOND®2038) have a low anionic demand i.e. less than 1 meq/g.
- Other cationic additives such as Kymene®557H have a high anionic demand (+2.2 meq/g).
- the cationic fixative has an anionic demand of greater than zero but less than one meq/g.
- the cationic fixative has an anionic demand of from 1 meq/g to 10 meq/g.
- the addition order of the additive can vary.
- mechanically refined fiber is added to the slurry followed by the addition of an anionic starch and then followed by addition of a cationic fixative. After each addition step the slurry ionic demand is less than zero.
- the slurry is deposited on a foraminous support, dewatered forming a web and dried to form a paperboard.
- mechanically refined fiber is added to the slurry followed by the addition of a cationic fixative and then followed by addition of an anionic starch. After each addition step the slurry ionic demand is less than zero.
- Fiber and polymer binders were applied to low density board so that internal bond strength increases by 100% or more with 10% or less increase in density.
- the effect of refining on freeness and ionic demand is shown in Table 11.
- mechanically refined fiber is mechanically refined wood pulp for example, Lodgepole Pine having a Canadian Standard Freeness ⁇ 125 mL, a index 1 ⁇ 2 or less of unrefined starting fiber and a kink angle of 1 ⁇ 2 or less of the unrefined starting fiber.
- Curl Index and kink angle were determined using a Fiber Quality Analyzer (FQA) as published in the Journal of Pulp and Paper Science 21(11):J367 (1995).
- FQA Fiber Quality Analyzer
- Mechanically refined fiber can be generated to meet these criteria by different refining methods which have different impact on conventional fiber properties.
- Table III shows the effect on Z-direction tensile and density of various formulations with mechanically refined fiber. ZDT was determined by TAPPI 541.
- Internal bond strength can be increased by replacing some of the cationic starch with a higher ionic strength molecule such as Kymene® as shown in the following example.
- a third technology is use of a starch excess.
- the general approach was to overcome the normal limits of effective wet-end starch, balancing the charge in the wet-end by adding excess anionic starch and fixing it to the fibers by adding cationic starch or other high charge density cationic polymers thus balancing the system to near neutral charge density.
- the neutralization was important to prevent excessive flocculation and large impacts on drainage.
- total starch content added to the wet can be increased to 2% to 5% based on dry fiber.
- Anionic starch such as RediBOND® 3050 supplied by National Starch & Chemical or Aniofax® AP25 supplied by Carolina Starches can be used.
- Cationic fixatives include common cationic starches like STA-LOK® 300 supplied by Staley Corp., Poly Aluminum Chloride (PAC) like Nalco ULTRION® 8187 or high charge density cationic polymers like M5133 and M5134, GALACTAOL® SP813D (anionic guar) and Kymene® 557H supplied by Hercules Corp.
- a high ionic demand is represented by a polymer that has an ionic demand of 1 meq/g to 17 meq/g, either as an anionic demand or as a cationic demand.
- Kymene®557H has an anionic demand of 2.2 meq/g and Hercobond®2000 has a cationic demand of 1.8 meq/g.
- the level of anionic starch needed to obtain high strength development depends on the charge density and more importantly on the retention. Typically, 2% to 5% addition level based on dry fiber is adequate.
- the amount of cationic fixative depends entirely on the size of the polymer and the cationic charge density. As defined herein, a fixative is a charged polymer that ionically bonds to a molecule of the opposite charge. In general the higher the charge density the smaller the amount required and for equal charge density the larger the polymer the smaller the amount required.
- the above described handsheet is the control.
- control handsheet as described above was adjusted as follows to the non-fiber portion. 40 lbs/t Aniofax AP25 was mixed with the fibers, followed by 20 lbs/t STA-LOK® 300 cationic starch. Kymene® 557H at 5#/t was added and the same combination of Stalok 300 and Aquapel 625 as in Example 1, i.e. 20 lb/t and 4 lb/t, respectively. Handsheets were evaluated for density, ZDT and Scott Bond; the results are in Table V1 combined with the results from Example 1.
- the handsheet formulation described in Example 2 was altered to contain mechanically refined fiber fibers so that the fiber portion of the furnish is:
- Single-ply handsheets designed to simulate the mid-ply of low density multi-ply paperboard were made. A 0.015 percent to 0.035 percent consistency slurry was used in these studies.
- Handsheet making equipment was standard 8′′ ⁇ 8′′ sheet mold modified with an extended headbox so that twice the normal volume of stock was used. This modification was necessary to improve handsheet formation when using materials designed to generate high bulk (e.g. crosslink fiber such as CHB405 and CHB505). Fiber weights are expressed as a weight percent of the total fiber dry weight; additives are based on weight of dry fiber.
- a series of handsheets were made using different levels of wet-end additives, different addition order and some changes in fiber furnish to demonstrate the level of internal bond strength that could be generated by starch loading the web.
- the additives were added to the slurry in the order across each sample row and the slurry stirred after each addition.
- Each handsheet was then coated with Polyvinyl Alcohol (PVA) coating, Celvol V24203 supplied by Celanese Ltd.
- PVA Polyvinyl Alcohol
- Celvol V24203 supplied by Celanese Ltd.
- the total coat weight was about 50 g/m 2 and was divided equally between each side of the sheet.
- the coating was added to the surface to facilitate testing Z-direction tensile (ZDT) and internal Scott Bond because low density structures without the coating tend to separate at the tape instead of the within the sheet.
- Samples 1, 2 and 9 can be considered the controls for this experiment.
- Sample number 9 is a fiber formulation designed to deliver low density paper and uses typical wet end chemistry (i.e. cationic starch and Kymene®557H). The result is a very low Scott Bond, but typical Taber Stiffness.
- Sample 2 incorporates mechanically refined fiber in an effort to increase the internal bond and, by itself, results in an increase in ZDT and Scott Bond, but not enough to reach the targets needed for converting multi-ply paperboard. It is estimated the minimum necessary ZDT needed for converting is about 175-190 kPa.
- Sample 1 incorporates mechanically refined fiber with a particle PVOH—known as a good binder but is hindered by issues with retention, cost and process reliability impacts.
- the increase in ZDT and Scott Bond for sample 1 begins to approach the amount needed for converting paperboard.
- Samples 3 and 4 show that by adding 4% total starch to the furnish the ZDT and Scott Bond essentially double. Adding mechanically refined fiber, Sample 4, gives an increase of about the same magnitude as it did to the original structure, Sample 2 v. Sample 4 and Sample 3 v. Sample 9.
- Sample 5 shows reversing the order (i.e. adding cationic starch first then anionic starch) in which the cationic and anionic starch are added makes no difference to the strength development
- Samples 6 and 7 are a case where the amount of anionic starch is doubled while the cationic starch remains constant.
- Kymeme® 557H a higher charge density cationic polymer, is used to balance the additional anionic charge.
- the result is further increase in internal bond, increasing ZDT by 500%, (Sample 6) over the control and Scott Bond is unaffected by the additional starch and Kymene® 557H.
- Sample 7 shows that by adding mechanically refined fiber the effect on ZDT is negative in this case, yet the Scott Bond increases.
- Sample 8 adjusts the source of cationic charge further, increasing the amount of Kymene®557H and decreasing the amount of cationic starch.
- Table XI-B the ionic demand of the system crosses from negative to positive at the last point of cationic starch addition and from Table XII the corresponding ZDT and Scott bond are further reduced indicating that when the ionic demand exceeds zero the effectiveness of the ionic binding system is reduced.
- PVA Polyvinyl Alcohol
- Celvol V24203 supplied by Celanese Ltd.
- the total coat weight was about 50 g/m 2 and was divided equally between each side of the sheet.
- the coating was added to the surface to facilitate testing Z-direction tensile (ZDT) and internal Scott Bond, because low density structures without the coating tend to separate at the tape instead of the within the sheet.
- Sample code 9 from Tables X1 and XII above is the base case.
- the fiber furnish used in all of the following examples was the same, only the chemical additives and the order of addition were changed.
- the fiber components were:
- Hercobond® 2000 supplied by Hercules Incorporated (anionic polyacrylamide, retention aid)
- PPD M-5133 supplied by Hercules Incorporated (cationic high charge density polymer)
- GALACTASOL® SP813D supplied by Hercules Incorporated (cationic guar gum)
- FIG. 1 shows the basic unit operations with the chemical addition points. indicated as lower case letters as in Table XV. The addition points have been labeled and should be used as a reference for the formulations shown in Table XV.
- PVA Polyvinyl Alcohol
- Celvol V24203 supplied by Celanese Ltd.
- the total coat weight was about 22 g/m 2 and was divided equally between each side of the sheet.
- the coating was added to the surface to facilitate testing Z-direction tensile (ZDT) and Internal Scott Bond, because low density structures without the coating tend to separate at the tape instead of the within the sheet.
- Starch loading resulted in an increase in density of ⁇ 10% in all cases and had no significant impact on stiffness.
Landscapes
- Paper (AREA)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US11/686,742 US20070215301A1 (en) | 2006-03-17 | 2007-03-15 | Method for making a low density multi-ply paperboard with high internal bond strength |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US78362406P | 2006-03-17 | 2006-03-17 | |
US11/686,742 US20070215301A1 (en) | 2006-03-17 | 2007-03-15 | Method for making a low density multi-ply paperboard with high internal bond strength |
Publications (1)
Publication Number | Publication Date |
---|---|
US20070215301A1 true US20070215301A1 (en) | 2007-09-20 |
Family
ID=38283737
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/686,742 Abandoned US20070215301A1 (en) | 2006-03-17 | 2007-03-15 | Method for making a low density multi-ply paperboard with high internal bond strength |
Country Status (6)
Country | Link |
---|---|
US (1) | US20070215301A1 (fr) |
EP (1) | EP1835075A1 (fr) |
JP (1) | JP2007254948A (fr) |
CN (1) | CN101054781A (fr) |
BR (1) | BRPI0702166A (fr) |
CA (1) | CA2581898A1 (fr) |
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20070151687A1 (en) * | 2005-12-30 | 2007-07-05 | Halabisky Donald D | Insulating paperboard |
WO2017065800A1 (fr) * | 2015-10-16 | 2017-04-20 | General Mills, Inc. | Produit en carton |
WO2017147392A1 (fr) | 2016-02-26 | 2017-08-31 | Ecolab Usa Inc. | Gestion du drainage dans la fabrication de papier multicouches |
US10273634B2 (en) * | 2014-08-18 | 2019-04-30 | Kemira Oyj | Strength agent, its use and method for increasing strength properties of paper |
US10415188B1 (en) * | 2016-06-28 | 2019-09-17 | Gpcp Ip Holdings Llc | Disposable cups made form recycled fiber |
Families Citing this family (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
SE1050985A1 (sv) * | 2010-09-22 | 2012-03-23 | Stora Enso Oyj | En pappers eller kartongprodukt och en process förtillverkning av en pappers eller en kartongprodukt |
CN105625078B (zh) * | 2014-12-01 | 2017-09-12 | 金东纸业(江苏)股份有限公司 | 一种造纸湿端的浆料系统 |
SE539344E (en) | 2015-03-02 | 2020-02-11 | Billerudkorsnaes Ab | Pulp mixture for production of a paper product with high strength in z-direction |
Citations (32)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4913773A (en) * | 1987-01-14 | 1990-04-03 | James River-Norwalk, Inc. | Method of manufacture of paperboard |
US5087324A (en) * | 1990-10-31 | 1992-02-11 | James River Corporation Of Virginia | Paper towels having bulky inner layer |
US5547541A (en) * | 1992-08-17 | 1996-08-20 | Weyerhaeuser Company | Method for densifying fibers using a densifying agent |
US5840787A (en) * | 1994-03-25 | 1998-11-24 | Weyerhaeuser Company | Cellulosic products using high-bulk cellulosic fibers |
US5906894A (en) * | 1994-03-25 | 1999-05-25 | Weyerhaeuser Company | Multi-ply cellulosic products using high-bulk cellulosic fibers |
US5942086A (en) * | 1994-08-16 | 1999-08-24 | Philip Chem-Solv, Inc. | Application of material to a substrate |
US5958180A (en) * | 1997-09-23 | 1999-09-28 | International Paper Company | Method for increasing the strength of a paper or paperboard product |
US6221212B1 (en) * | 1997-07-07 | 2001-04-24 | Stora Kopparbergs Bergslags Ab | Cardboard having great reigidity |
US6306251B1 (en) * | 1994-03-25 | 2001-10-23 | Weyerhaeuser Company | Multi-ply cellulosic products using high-bulk cellulosic fibers |
US20020011317A1 (en) * | 2000-03-06 | 2002-01-31 | Lee Jeffrey A. | Method of bleaching and providing papermaking fibers with durable curl |
US6413369B2 (en) * | 1999-12-15 | 2002-07-02 | Metso Paper Karlstad Ab | Arrangement and method for forming a multilayered paper or paperboard web |
US6413362B1 (en) * | 1999-11-24 | 2002-07-02 | Kimberly-Clark Worldwide, Inc. | Method of steam treating low yield papermaking fibers to produce a permanent curl |
US6413372B1 (en) * | 1999-04-20 | 2002-07-02 | National Starch And Chemical Investment Holding Corporation | Starch polymer combinations used in papermaking |
US20030015305A1 (en) * | 1999-12-09 | 2003-01-23 | Upm-Kymmene Corporation | Raw material for printing paper, a method for producing said raw material and a printing paper |
US6551457B2 (en) * | 2000-09-20 | 2003-04-22 | Akzo Nobel N.V. | Process for the production of paper |
US6723204B2 (en) * | 2002-04-08 | 2004-04-20 | Hercules Incorporated | Process for increasing the dry strength of paper |
US20040127869A1 (en) * | 2002-12-26 | 2004-07-01 | Sheng-Hsin Hu | Method of producing twisted, curly fibers |
US6802938B2 (en) * | 2000-01-26 | 2004-10-12 | International Paper Company | Low density paper and paperboard articles |
US20040213961A1 (en) * | 2003-04-04 | 2004-10-28 | Weyerhaeuser Company | Embossed insulating paperboard |
US20040211535A1 (en) * | 2003-04-04 | 2004-10-28 | Weyerhaeuser Company | Method for making an insulating paperboard |
US20040213930A1 (en) * | 2003-04-04 | 2004-10-28 | Weyerhaeuser Company | Hot cup made from an insulating paperboard |
US20040213978A1 (en) * | 2003-04-04 | 2004-10-28 | Weyerhaeuser Company | Insulating paperboard |
US20040231811A1 (en) * | 2001-06-21 | 2004-11-25 | Per Engstrand | Method of producing bleached thermomechanical pulp (tmp) or bleached chemithermomechanical pulp (ctmp) |
US20050217810A1 (en) * | 2004-03-31 | 2005-10-06 | Weyerhaeuser Company | Bleached polyacrylic acid crosslinked cellulosic fibers |
US20050217811A1 (en) * | 2004-03-31 | 2005-10-06 | Weyerhaeuser Company | Whitened crosslinked cellulosic fibers and related methods |
US20060144537A1 (en) * | 2004-12-30 | 2006-07-06 | Schwonke Paul A | Paperboard |
US20060144538A1 (en) * | 2004-12-30 | 2006-07-06 | Schwonke Paul A | Process for making a paperboard from a high consistency slurry containing high levels of crosslinked cellulosic fibers |
US20060213630A1 (en) * | 2005-03-22 | 2006-09-28 | Bunker Daniel T | Method for making a low density multi-ply paperboard with high internal bond strength |
US20070084574A1 (en) * | 2005-06-30 | 2007-04-19 | Bunker Daniel T | Insulating paperboard |
US20070137815A1 (en) * | 2005-12-20 | 2007-06-21 | Shearer Dwayne M | Smooth low density paperboard |
US20070151687A1 (en) * | 2005-12-30 | 2007-07-05 | Halabisky Donald D | Insulating paperboard |
US20080029236A1 (en) * | 2006-08-01 | 2008-02-07 | Williams Rick C | Durable paper |
Family Cites Families (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6419789B1 (en) * | 1996-10-11 | 2002-07-16 | Fort James Corporation | Method of making a non compacted paper web containing refined long fiber using a charge controlled headbox and a single ply towel made by the process |
US20020139502A1 (en) * | 1998-04-27 | 2002-10-03 | Hans Hallstrom | Process for the production of paper |
EP0953680A1 (fr) * | 1998-04-27 | 1999-11-03 | Akzo Nobel N.V. | Procédé pour la fabrication du papier |
-
2007
- 2007-03-15 CA CA002581898A patent/CA2581898A1/fr not_active Abandoned
- 2007-03-15 US US11/686,742 patent/US20070215301A1/en not_active Abandoned
- 2007-03-16 BR BRPI0702166-6A patent/BRPI0702166A/pt not_active Application Discontinuation
- 2007-03-16 CN CNA2007100886046A patent/CN101054781A/zh active Pending
- 2007-03-16 EP EP07251134A patent/EP1835075A1/fr not_active Withdrawn
- 2007-03-19 JP JP2007069826A patent/JP2007254948A/ja not_active Withdrawn
Patent Citations (48)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4913773A (en) * | 1987-01-14 | 1990-04-03 | James River-Norwalk, Inc. | Method of manufacture of paperboard |
US5087324A (en) * | 1990-10-31 | 1992-02-11 | James River Corporation Of Virginia | Paper towels having bulky inner layer |
US5547541A (en) * | 1992-08-17 | 1996-08-20 | Weyerhaeuser Company | Method for densifying fibers using a densifying agent |
US5840787A (en) * | 1994-03-25 | 1998-11-24 | Weyerhaeuser Company | Cellulosic products using high-bulk cellulosic fibers |
US5906894A (en) * | 1994-03-25 | 1999-05-25 | Weyerhaeuser Company | Multi-ply cellulosic products using high-bulk cellulosic fibers |
US20020096287A1 (en) * | 1994-03-25 | 2002-07-25 | Weyerhaeuser Company | Multi-ply cellulosic products using high-bulk cellulosic fibers |
US6736933B2 (en) * | 1994-03-25 | 2004-05-18 | Weyerhaeuser Company | Multi-ply cellulosic products using high-bulk cellulosic fibers |
US6306251B1 (en) * | 1994-03-25 | 2001-10-23 | Weyerhaeuser Company | Multi-ply cellulosic products using high-bulk cellulosic fibers |
US6716306B2 (en) * | 1994-03-25 | 2004-04-06 | Weyerhaeuser Company | High bulk cellulose fibers crosslinked with tartaric acid and method of making same |
US20030205342A1 (en) * | 1994-03-25 | 2003-11-06 | Weyerhaeuser Company | Multi-ply cellulosic products using high-bulk cellulosic fibers |
US6582553B2 (en) * | 1994-03-25 | 2003-06-24 | Weyerhaeuser Company | High bulk cellulosic fibers crosslinked with malic acid and process for making the same |
US20030051835A1 (en) * | 1994-03-25 | 2003-03-20 | Jewell Richard A. | Multi-ply cellulosic products using high-bulk cellulosic fibers |
US5942086A (en) * | 1994-08-16 | 1999-08-24 | Philip Chem-Solv, Inc. | Application of material to a substrate |
US6221212B1 (en) * | 1997-07-07 | 2001-04-24 | Stora Kopparbergs Bergslags Ab | Cardboard having great reigidity |
US5958180A (en) * | 1997-09-23 | 1999-09-28 | International Paper Company | Method for increasing the strength of a paper or paperboard product |
US6413372B1 (en) * | 1999-04-20 | 2002-07-02 | National Starch And Chemical Investment Holding Corporation | Starch polymer combinations used in papermaking |
US6413362B1 (en) * | 1999-11-24 | 2002-07-02 | Kimberly-Clark Worldwide, Inc. | Method of steam treating low yield papermaking fibers to produce a permanent curl |
US6878236B2 (en) * | 1999-12-09 | 2005-04-12 | Upm-Kymmene Corporation | Raw material for printing paper, a method for producing said raw material and a printing paper |
US20030015305A1 (en) * | 1999-12-09 | 2003-01-23 | Upm-Kymmene Corporation | Raw material for printing paper, a method for producing said raw material and a printing paper |
US6413369B2 (en) * | 1999-12-15 | 2002-07-02 | Metso Paper Karlstad Ab | Arrangement and method for forming a multilayered paper or paperboard web |
US6846529B2 (en) * | 2000-01-26 | 2005-01-25 | International Paper Company | Low density paperboard articles |
US6802938B2 (en) * | 2000-01-26 | 2004-10-12 | International Paper Company | Low density paper and paperboard articles |
US20040016524A1 (en) * | 2000-03-06 | 2004-01-29 | Lee Jeffrey A. | Method of bleaching and providing papermaking fibers with durable curl |
US20020011317A1 (en) * | 2000-03-06 | 2002-01-31 | Lee Jeffrey A. | Method of bleaching and providing papermaking fibers with durable curl |
US7291247B2 (en) * | 2000-03-06 | 2007-11-06 | Georgia-Pacific Consumer Operations Llc | Absorbent sheet made with papermaking fibers with durable curl |
US6627041B2 (en) * | 2000-03-06 | 2003-09-30 | Georgia-Pacific Corporation | Method of bleaching and providing papermaking fibers with durable curl |
US6551457B2 (en) * | 2000-09-20 | 2003-04-22 | Akzo Nobel N.V. | Process for the production of paper |
US20040231811A1 (en) * | 2001-06-21 | 2004-11-25 | Per Engstrand | Method of producing bleached thermomechanical pulp (tmp) or bleached chemithermomechanical pulp (ctmp) |
US6723204B2 (en) * | 2002-04-08 | 2004-04-20 | Hercules Incorporated | Process for increasing the dry strength of paper |
US20040127869A1 (en) * | 2002-12-26 | 2004-07-01 | Sheng-Hsin Hu | Method of producing twisted, curly fibers |
US7364639B2 (en) * | 2002-12-26 | 2008-04-29 | Kimberly-Clark Worldwide, Inc. | Method of producing twisted, curly fibers |
US20040213961A1 (en) * | 2003-04-04 | 2004-10-28 | Weyerhaeuser Company | Embossed insulating paperboard |
US20040213930A1 (en) * | 2003-04-04 | 2004-10-28 | Weyerhaeuser Company | Hot cup made from an insulating paperboard |
US20040211535A1 (en) * | 2003-04-04 | 2004-10-28 | Weyerhaeuser Company | Method for making an insulating paperboard |
US7056563B2 (en) * | 2003-04-04 | 2006-06-06 | Weyerhaeuser Company | Hot cup made from an insulating paperboard |
US7060159B2 (en) * | 2003-04-04 | 2006-06-13 | Weyerhaeuser Company | Insulating paperboard |
US7063771B2 (en) * | 2003-04-04 | 2006-06-20 | Weyerhaeuser Company | Embossed insulating paperboard |
US20040213978A1 (en) * | 2003-04-04 | 2004-10-28 | Weyerhaeuser Company | Insulating paperboard |
US7108765B2 (en) * | 2003-04-04 | 2006-09-19 | Weyerhaeuser Company | Method for making an insulating paperboard |
US20050217810A1 (en) * | 2004-03-31 | 2005-10-06 | Weyerhaeuser Company | Bleached polyacrylic acid crosslinked cellulosic fibers |
US20050217811A1 (en) * | 2004-03-31 | 2005-10-06 | Weyerhaeuser Company | Whitened crosslinked cellulosic fibers and related methods |
US20060144537A1 (en) * | 2004-12-30 | 2006-07-06 | Schwonke Paul A | Paperboard |
US20060144538A1 (en) * | 2004-12-30 | 2006-07-06 | Schwonke Paul A | Process for making a paperboard from a high consistency slurry containing high levels of crosslinked cellulosic fibers |
US20060213630A1 (en) * | 2005-03-22 | 2006-09-28 | Bunker Daniel T | Method for making a low density multi-ply paperboard with high internal bond strength |
US20070084574A1 (en) * | 2005-06-30 | 2007-04-19 | Bunker Daniel T | Insulating paperboard |
US20070137815A1 (en) * | 2005-12-20 | 2007-06-21 | Shearer Dwayne M | Smooth low density paperboard |
US20070151687A1 (en) * | 2005-12-30 | 2007-07-05 | Halabisky Donald D | Insulating paperboard |
US20080029236A1 (en) * | 2006-08-01 | 2008-02-07 | Williams Rick C | Durable paper |
Cited By (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20070151687A1 (en) * | 2005-12-30 | 2007-07-05 | Halabisky Donald D | Insulating paperboard |
US10273634B2 (en) * | 2014-08-18 | 2019-04-30 | Kemira Oyj | Strength agent, its use and method for increasing strength properties of paper |
WO2017065800A1 (fr) * | 2015-10-16 | 2017-04-20 | General Mills, Inc. | Produit en carton |
US10669675B2 (en) | 2015-10-16 | 2020-06-02 | General Mills, Inc. | Paperboard product |
US11753773B2 (en) | 2015-10-16 | 2023-09-12 | General Mills, Inc. | Paperboard product |
WO2017147392A1 (fr) | 2016-02-26 | 2017-08-31 | Ecolab Usa Inc. | Gestion du drainage dans la fabrication de papier multicouches |
US10415188B1 (en) * | 2016-06-28 | 2019-09-17 | Gpcp Ip Holdings Llc | Disposable cups made form recycled fiber |
US10731296B2 (en) * | 2016-06-28 | 2020-08-04 | Gpcp Ip Holdings Llc | Method for making paper product |
Also Published As
Publication number | Publication date |
---|---|
JP2007254948A (ja) | 2007-10-04 |
CN101054781A (zh) | 2007-10-17 |
EP1835075A1 (fr) | 2007-09-19 |
BRPI0702166A (pt) | 2007-12-11 |
CA2581898A1 (fr) | 2007-09-17 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP3183388B1 (fr) | Agent de résistance, son utilisation et procédé pour augmenter les propriétés de résistance de papier | |
US20070215301A1 (en) | Method for making a low density multi-ply paperboard with high internal bond strength | |
EP2622132B1 (fr) | Procédé d'amélioration de l'aptitude au passage sur machine de bande de papier humide, utilisation de solution et papier | |
US11214927B2 (en) | Method for increasing the strength properties of a paper or board product | |
US10781556B2 (en) | Dry strength composition, its use and method for making of paper, board or the like | |
US11427965B2 (en) | Dry strength composition, its use and method for making of paper, board or the like | |
US20060213630A1 (en) | Method for making a low density multi-ply paperboard with high internal bond strength | |
SE1050985A1 (sv) | En pappers eller kartongprodukt och en process förtillverkning av en pappers eller en kartongprodukt | |
Ehman et al. | Effect of nanofiber addition on the physical–mechanical properties of chemimechanical pulp handsheets for packaging | |
US6824649B2 (en) | Method for increasing filler retention of cellulosic fiber sheets | |
US20210002830A1 (en) | Method for manufacturing a multi-layered paperboard, multi-layered paperboard and composition for use in multi-layered paperboard manufacturing | |
CN112384655A (zh) | 制造多层纤维网的方法和多层纤维网 | |
CN117337237A (zh) | 包含nssc浆的瓦楞芯纸或挂面纸 | |
John et al. | Enhancement of Dry Strength in High Performance Linerboard Using a Dual |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: WEYERHAEUSER COMPANY, WASHINGTON Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:BUNKER, DANIEL T.;NAIENI, SHAHROKH;HALABISKY, DONALD D;REEL/FRAME:019109/0170;SIGNING DATES FROM 20070315 TO 20070329 |
|
AS | Assignment |
Owner name: WEYERHAEUSER NR COMPANY, WASHINGTON Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:WEYERHAEUSER COMPANY;REEL/FRAME:022835/0233 Effective date: 20090421 Owner name: WEYERHAEUSER NR COMPANY,WASHINGTON Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:WEYERHAEUSER COMPANY;REEL/FRAME:022835/0233 Effective date: 20090421 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |