US20060090512A1 - Press molding apparatus and method of producing a glass optical element using the apparatus - Google Patents
Press molding apparatus and method of producing a glass optical element using the apparatus Download PDFInfo
- Publication number
- US20060090512A1 US20060090512A1 US11/311,403 US31140305A US2006090512A1 US 20060090512 A1 US20060090512 A1 US 20060090512A1 US 31140305 A US31140305 A US 31140305A US 2006090512 A1 US2006090512 A1 US 2006090512A1
- Authority
- US
- United States
- Prior art keywords
- mold
- molds
- shape
- induction heating
- pressing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
In a press molding apparatus for press molding a plurality of glass materials into a plurality of glass optical elements by the use of a pressing mold including upper and lower molds each of which has a plurality of molding surfaces, at least one of the upper and the lower molds is a heat generator within which heat is generated when the heat generator is subjected to a high-frequency induction heating by an induction heating coil. The heat generator having a plurality of shape-processed portions (130) produced by partially processing a shape of the heat generator in order that a temperature distribution of the heat generator is adjusted. The apparatus simultaneously press forms, into the glass optical elements, the glass materials supplied between the molding surfaces of the upper and the lower molds which are subjected to the high-frequency induction heating.
Description
- This invention relates to production of a glass optical element such as an optical lens and, in particular, to a press molding apparatus for press molding a preform (obtained by preliminarily forming a glass material) in a heated and softened state to provide a predetermined shape. This invention also relates to a method of producing a glass optical element by the use of the above-mentioned press-forming apparatus.
- Recently, in a field of production of an optical element such as an optical lens, it is desired to obtain a high-accuracy lens shape without carrying out surface polishing. To this end, proposal is made of a method comprising the steps of preparing a preform by preliminarily forming a glass material into a provisional shape approximate to a desired shape, heating and softening the preform, and pressing the preform by the use of a pressing mold having a high-accuracy pressing surface (for example, see Japanese Unexamined Patent Publication JP 2001-10829 A).
- A press molding apparatus of the type is formed so that a plurality of (for example, four) preforms are simultaneously pressed by the use of a pressing mold comprising an upper mold and a lower mold. The upper and the lower molds are surrounded by an induction heating coil so that the upper and the lower molds are heated to a predetermined temperature by high-frequency induction heating. The upper and the lower molds clamp and press the preforms preliminarily heated and softened to thereby provide each preform with a high-accuracy processed surface.
- For example,
FIG. 1 shows a basic structure of a typical press molding apparatus of the type mentioned above. The press molding apparatus illustrated inFIG. 1 has a pressing mold comprising anupper mold 502 and alower mold 504. Each of the upper and thelower molds lower molds members member 506 is attached to afixed shaft 510 while the lower supportingmember 508 is attached to adrive shaft 512 of a motor mechanism or the like. The upper and thelower molds molding portions lower molds lower molds induction heating coils lower molds lower molds - In the meanwhile, upon producing the optical element by precision pressing, accuracy and productivity are important aspects.
- In this sense, anisothermal pressing (Japanese Unexamined Patent Publication JP 08-133756 A) has contributed to epoch-making progress. Specifically, by shortening a heating cycle of the pressing mold as compared with existing isothermal pressing, a cycle time required to form the glass optical element can be shortened to the order of several tens of seconds. In addition, surface accuracy and profile accuracy can be kept superior.
- Taking the production efficiency into account, attention is directed to a method of obtaining a plurality of optical elements in one heating cycle, i.e., a multiproduct batch process. As far as the heating cycle is essential and requires a predetermined time period, the productivity can be improved if a plurality of optical elements are simultaneously produced in the heating cycle.
- In the anisothermal pressing, a glass material is preliminarily heated at a position apart from the pressing mold and thereafter supplied to the pressing mold so that the glass material supplied to the pressing mold is made at a preheat temperature different from that of the pressing mold (frequently, at a temperature higher than that of the pressing mold). In order to avoid product variation, a plurality of glass materials are heated to the same preheat temperature to be uniform in viscosity when they are supplied to the pressing mold. The pressing mold is also heated to a predetermined temperature. In this event, a plurality of molding surfaces must be heated under the conditions as same as possible and, after pressing, must be cooled under the conditions as same as possible. Heating of the molding surfaces under the same condition (i.e., thermal uniformity) is a problem which is not negligible.
- As a heat source, use may be made of various options such as resistance heating and induction heating. In order to heat the molding surfaces under the same condition and to avoid occurrence of a local temperature gramoldnt in each single molding surface, the heat source and the molding surfaces are limited in position relative to each other and the molding surfaces are located at an equal distance from the heat source. Thus, upon designing the apparatus, consideration must be made about thermal uniformity. Furthermore, rapid temperature elevation as efficient as possible contributes to the productivity. In view of continuous production, the heating condition must be easily reproducible.
- In the meanwhile, one of design options for the pressing mold capable of simultaneously producing a plurality of optical elements is to dispose a plurality of molding surfaces in a single-line arrangement (see JP 2001-10829 A). Such single-line arrangement is advantageous in the following respects. That is, the structure of the pressing mold is simple. In particular, consideration will be made of supply of the glass materials to the pressing mold. In a state where the glass materials are arranged in a single line, a supplying member is split by a straight line into two parts to drop the glass materials through a gap between the two parts. With such a simple mechanism, the glass materials are simultaneously supplied onto the pressing mold (i.e., to the respective molding surfaces).
- In order to drop the glass material in a heated and softened state, the glass material in the softened state is floated on a floating saucer by the use of a gas and then dropped and supplied to the pressing mold. This technique is advantageous in that the glass material is stably supplied without damaging the surface of the glass material. For example, by arranging a plurality of floating saucers in a single line and splitting each floating saucer into two parts, the glass materials are simultaneously dropped through gaps between the two parts onto the molding surfaces arranged in a single line. In this case, the apparatus is relatively simple in structure. Thereafter, press molding can be immediately performed before the temperature of the glass material is changed from the preheat temperature. The above-mentioned technique is very advantageous in that the productivity is high and a plurality of optical elements can be stably produced with high accuracy under a thermally uniform condition.
- However, the single-line arrangement of the molding surfaces is disadvantageous in the following respect. Specifically, it is difficult to uniformly heat the molding surfaces in the single-line arrangement. Generally, it is difficult to uniformly distribute the heat from the heat source to a plurality of molding surfaces arranged in a single line so that the molding surfaces are heated under the same condition. In case where three or more molding surfaces are arranged in a single line, heat energy supplied from the heat source is different in amount between the molding surface at the center and the molding surfaces at both ends. Such difficulty is encountered by any kind of heat source. For example, even in case where a high-frequency induction heating apparatus extremely high in heat efficiency and high in responsiveness upon temperature elevation and temperature drop (i.e., high in productivity) is used, it is not easy in actual design to arrange the induction heating coil so that all molding surfaces are heated under the same condition.
- It is therefore an object of this invention to provide a press molding apparatus and a method of producing a glass optical element which are capable of increasing a temperature elevation rate of a pressing mold.
- It is another object of this invention to provide a press molding apparatus and a method of producing a glass optical element which are capable of improving thermal uniformity in a pressing mold.
- It is still another object of this invention to provide an apparatus and a method for producing a glass optical element which are high in accuracy and productivity.
- Other objects of this invention will become clear as the description proceeds.
- According to this invention, there is provided a press molding apparatus for preparing a plurality of glass optical elements from a plurality of glass materials, comprising upper and lower molds each of which comprises a plurality of molding surfaces, and an induction heating device for heating the upper and lower molds, at least one of the upper and lower mold comprising a heat generator within which heat is generated when the heat generator is subjected to high-frequency induction heating by the induction heating device, the heat generator comprising a shape-processed portion produced by processing a shape of the heat generator in order that a temperature distribution of the heat generator is adjusted when the heat generator is subjected to high-frequency induction heating.
- According to this invention, there is also provided a method of press molding a plurality of glass materials into a plurality of glass optical elements by use of a pressing mold comprising upper and lower molds each of which comprises a plurality of molding surfaces, at least one of the upper and lower mold comprising a heat generator within which heat is generated when the heat generator is subjected to high-frequency induction heating, the heat generator comprising a shape-processed portion produced by processing a shape of the heat generator in order that a temperature distribution of the heat generator is adjusted when the heat generator is subjected to high-frequency induction heating, comprising the steps of subjecting the upper and the lower molds to the high-frequency induction heating so that the molding surfaces of the upper mold and the lower mold have predetermined temperatures, and simultaneously press molding, into the glass optical elements, the glass materials supplied between the molding surfaces of the upper and the lower molds.
-
FIG. 1 shows an existing press molding apparatus; -
FIG. 2 shows a press molding apparatus according to a first embodiment of this invention; -
FIG. 3 is a plan view of an example of a lower mold inFIG. 2 ; -
FIGS. 4A to 4C show first through third modifications of the lower mold inFIG. 3 ; -
FIG. 5 shows a fourth modification of the lower mold inFIG. 3 ; -
FIG. 6 shows a fifth modification of the lower mold according to the first embodiment of the invetion; -
FIG. 7 shows a press molding apparatus according to a second embodiment of this invention; -
FIG. 8 is a plan view of a lower mold inFIG. 7 ; -
FIGS. 9A and 9B shows a press molding apparatus according to a third embodiment of this invention; -
FIG. 10 shows a press molding apparatus according to a fourth embodiment of this invention; -
FIG. 11A is a plan view of a lower mother mold inFIG. 10 ; -
FIG. 11B is a plan view of a support arm used with the pressing mold ofFIG. 10 ; -
FIG. 12 shows a press molding apparatus according to a fifth embodiment of this invention; -
FIG. 13 is a plan view of a lower mold inFIG. 12 ; -
FIG. 14 is a view showing temperature distribution achieved by the fifth embodiment; -
FIG. 15 is a view similar toFIG. 14 with respect to a comparative example; -
FIG. 16 is a sectional view of a pressing mold according to a sixth embodiment of this invention; and -
FIG. 17 is a sectional view of a pressing mold according to a seventh embodiment of this invention. - At first, the principle of this invention will be described.
- The present inventors have found that the above-mentioned problems can be solved by improving the shape of a pressing mold.
- Specifically, a heat generator for generating heat by high-frequency induction generates heat easily in an area around its surface and also in a portion having an acute-angled shape. By modifying the shape of the heat generator by, for instance, placing a cutout or a perforation, or making the corner which is preferably rounded, it is possible to promote overall heating or to relatively suppress heating in a local area as compared with a remaining area. Thus, by processing the shape of the heat generator for generating heat by induction heating, heat promotion is performed to increase the temperature elevation efficiency or heat promotion or suppression is locally performed to achieve thermal uniformity. Thus, it is possible to equalize the thermal conditions of a plurality of molding surfaces and to control the heating with high accuracy. In other words, the shape of the heat generator is given a function of adjusting temperature distribution.
- The inventors have found out that, even if a pressing mold supporting a plurality of molding surfaces disposed in a linear arrangement is used, those parts difficult in temperature elevation are subjected to a shaping process for improving the heating efficiency so that overall thermal uniformity is achieved and a plurality of molding surfaces of the pressing molds are heated under the same condition. As a consequence, a glass optical element can be formed with high accuracy.
- In
FIG. 1 , each of the upper and thelower molds lower molds - Now, preferred embodiments of this invention will be described in detail with reference to the drawing.
- At first referring to
FIG. 2 , a press molding apparatus according to a first embodiment of this invention will be described. For example, the press molding apparatus is used to produce a medium-aperture lens having a diameter of 17 mm by the use of a preform having a flat spherical shape. The press molding apparatus has a pressing mold comprising anupper mold 102 and alower mold 104 for clamping and pressing the preform. Each of the upper and thelower molds lower molds lower molds members main shafts main shaft 110 is fixed to an apparatus frame (not shown) while the lowermain shaft 112 is driven by a motor (not shown) in a vertical direction. Thus, by driving the lowermain shaft 112, the upper and thelower molds lower molds lower molds lower molds - Referring to
FIG. 3 , thelower mold 104 and theinduction heating coil 116 therearound are shown in plan view as seen from the above. Although not shown in the figure, theupper mold 102 is similar in shape in plan view to thelower mold 104. Thelower mold 104 has a pair oflong sides 104 a extending in parallel to each other and a pair of semicircular arc shapedsides 104 b located at opposite ends of thelong sides 104 a. Each of the semicircular arc-shapedsides 104 b defines an arc of a half circle having a radius equal to a half of the distance between the twolong sides 104 a (i.e., the width of the lower mold 104). Theinduction heating coil 116 is wound around thelower mold 104 in a shape corresponding to an outer periphery of thelower mold 104. Longitudinal ends of thelower mold 104 may be formed into a shape such that the distance from theinduction heating coil 116 is greater or a shape such that the distance between the molding portion (which will later be described) and the longitudinal end in the longitudinal direction is greater than that in the transversal direction. - The
lower mold 104 has an upper surface provided with the molding portions (recessed portions) 120, six in number, for imparting a glass product shape to the preforms. Thesemolding portions 120 are arranged in a single line along the longitudinal direction of thelower mold 104. The sixmolding portions 120 have preform pressing surfaces as molding surfaces A, B, C, D, E, and F, respectively. It is noted here that theupper mold 102 also has six molding portions formed at positions corresponding to themolding portions 120 of thelower mold 104. - The
lower mold 104 is provided with a number ofperforations 130 arranged in a zone along the outer periphery thereof. Theperforations 130 serve to promote heating when high-frequency induction heating is performed and to improve the temperature elevation rate of thelower mold 104. Presumably, such heating promotion effect is obtained for the following reason. Upon high-frequency induction heating, there arises a phenomenon, called a skin effect, such that an electric current flows in the vicinity of the outer periphery of thelower mold 104. Presence of theperforations 130 narrows a flow path of the electric current to increase an electric resistance. As a consequence, Joule heat is generated to elevate the temperature. For example, each of theperforations 130 is a through hole having a circular section and penetrating thelower mold 104 in its thickness direction. Theperforation 130 has an inner diameter preferably within a range between 0.5 mm and 5.0 mm. If the inner diameter of theperforation 130 is smaller than 0.5 mm, the heating promotion effect is weak. If the inner diameter exceeds 5.0 mm, the number of perforations which can be formed is decreased so that the heating promotion effect is decreased. - If the
perforations 130 are densely arranged in thelower mold 104 in a local region corresponding to an area relatively uneasily heated during high-frequency induction heating (hereinafter may be referred to as a relatively uneasily heated area), temperature distribution of thelower mold 104 can be kept uniform. Distribution of easily heated areas is determined by the distance from a peripheral edge of thelower mold 104, the shapes and the sizes of theinduction heating coil 116 and thelower mold 104, the position of themolding portion 120 in thelower mold 104, and so on. Taking these factors into consideration, theperforations 130 are preferably formed in the local region corresponding to the uneasily heated area. For example, within a peripheral region along the outer periphery of thelower mold 104, theperforations 130 are preferably formed in a local region relatively apart from eachmolding portion 120. More specifically, theperforations 130 are preferably formed, within the peripheral region along the outer periphery of thelower mold 104, in a local region corresponding to an area between adjacent ones of the molding surfaces A to F (for example, a local region a corresponding to an area between the molding surfaces A and B, a local region b corresponding to an area between the molding surfaces B and C). Such local region is referred to as “a local region corresponding to an area between adjacent ones of the molding surfaces”. - The
upper mold 102 is also provided with perforations similar to those of thelower mold 104. The arrangement of the perforations is similar to that of theperforations 130 in thelower mold 104. - Next, description will be made of a method of producing a lens (as a glass optical element) according to the embodiment. At first, by high-frequency induction heating of the induction heating coils 114 and 116, the upper and the
lower molds lower mold 104 after the preforms are preheated to a temperature higher than that of the molding surfaces A to F of the upper and thelower molds lower mold 104, the preforms are positioned above the molding surfaces A to F of thelower mold 104 by the use of a positioning member (not shown) and are dropped onto thelower mold 104. Thereafter, the lowermain shaft 112 is moved upward to press the six preforms between the upper and thelower molds perforations 130 formed in the upper and thelower molds lower molds lower molds lower molds perforations 130 are densely arranged in the upper and thelower molds lower molds lower molds main shaft 112 is moved downward to open or separate the upper and thelower molds lower mold 104 are sucked and removed. Thus, lenses surface-processed with high precision are obtained as the glass optical elements. - As described above, according to the press molding apparatus and the production method according to the embodiment, the upper and the
lower molds perforations 130 to generate a greater amount of heat upon high-frequency induction heating. Therefore, the upper and thelower molds perforations 130 are densely arranged in the local region corresponding to the relatively uneasily heated area mentioned above. Therefore, temperature distribution in each of the upper and thelower molds - Next, description will be made of first through third modifications of the above-mentioned embodiment. In the above-mentioned embodiment, the upper and the
lower molds perforations 130. Instead of theperforations 130, a plurality of cutouts illustrated inFIGS. 4A to 40 may be provided. The cutouts are formed on an outer peripheral end face (side end face) E of each of the upper and thelower molds FIG. 4A , the outer peripheral end face E of each mold is subjected to knurling to continuously form a plurality of V-shapedcutouts 302. In the second modification illustrated inFIG. 4B , a number ofcutouts 304 are formed on the outer peripheral end face E of each mold at predetermined intervals. Each of the cutouts has a curved bottom. In the third modification illustrated inFIG. 4C , a number ofcutouts 306 are formed on the outer peripheral end face E of each mold at predetermined intervals. Each of thecutouts 306 has a flat bottom. In the modifications illustrated inFIGS. 4A to 4C, those regions around thecutouts 302 to 306 locally generate a greater amount of heat upon high-frequency induction heating. Therefore, like in the above-mentioned embodiment, the temperature elevation rate of each mold can be improved. Furthermore, by densely forming thecutouts 302 to 306 in the relatively uneasily heated area of each of the upper and thelower molds lower molds - It is possible to use a combination of the
perforations 130 in the above-mentioned embodiment and the cutouts in the modifications. - Next, description will be made of a fourth modification of the above-mentioned embodiment. Referring to
FIG. 6 , alower mold 400 is shown in plan view. An upper mold to be combined with thelower mold 400 is similar in shape in plan view to thelower mold 400 and is not illustrated in the figure. As shown inFIG. 5 , thelower mold 400 has an elongated shape and is provided with sixmolding portions 420 arranged along its longitudinal direction to provide the preforms with a predetermined shape. Thelower mold 400 has a number ofperforations 430 formed throughout an entire periphery thereof. Specifically, theperforations 430 in a peripheral region of thelower mold 400 are particularly densely formed in local regions relatively apart from themolding portions 420, as compared with those regions closer to themolding portions 420. More specifically, within the region along the outer periphery of thelower mold 400, theperforations 430 are particularly densely arranged in a local region corresponding to an area between adjacent ones of the molding surfaces A to F (for example, a local region a corresponding to the space between the molding surfaces A and B). In the fourth modification also, a greater amount of heat is generated around theperforations 430 during high-frequency induction heating. Therefore, it is possible to increase the temperature elevation rate of each of thelower mold 400 and the upper mold and to achieve uniform temperature distribution in each mold. Instead of theperforations 430, the cutouts illustrated inFIGS. 4A to 4C may be provided. Alternatively, use may be made of a combination of theperforations 430 and the cutouts. - Next, description will be made of a fifth modification of the above-mentioned embodiment. Referring to
FIG. 6 , alower mold 500 is shown in plan view. An upper mold to be combined with thelower mold 500 is similar in shape in plan view to thelower mold 500 and is not illustrated in the figure. As illustrated inFIG. 6 , thelower mold 500 has a circular shape and is provided with a plurality ofmolding portions 520 in its center region. Thelower mold 500 has a number ofperforations 530 similar to those of the above-mentioned first embodiment. Theperforations 530 are uniformly arranged throughout an entire outer periphery of thelower mold 500. In this modification also, by the heat promotion effect of theperforations 530, the temperature elevation rate of each of thelower mold 500 and the upper mold is increased and the temperature distribution in each mold is kept uniform. Instead of theperforations 530, the cutouts illustrated inFIGS. 4A to 4C may be provided. Alternatively, use may be made of a combination of theperforations 530 and the cutouts. - Next, description will be made of second through fourth embodiments of this invention. In each of these embodiments, a pressing mold comprises a plurality of lower and upper mold members having molding surfaces, respectively, and a mother mold supporting the lower and the upper mold members. The mother mold is made of a material easily heated by induction heating. The lower and the upper mold members are heated by heat conduction from the mother mold. The mother mold in each of these embodiments corresponds to one specific example of “the upper mold and/or the lower mold” in this invention.
- Referring to
FIG. 7 , a press molding apparatus according to a second embodiment comprises amother mold 600 having an elongated shape and six pairs of upper andlower mold members mother mold 600 to be vertically movable. Each of the upper and thelower mold members mother mold 600 is made of a tungsten alloy and has a thermal expansion coefficient slightly greater than that of cemented carbide. Themother mold 600, theupper mold members 602, and thelower mold members 604 are supported on atray 606 and transferred into a forming chamber (not shown). Between each of thelower mold members 604 and thetray 606, aspacer 608 is inserted to adjust the thickness of each lens. Thetray 606 is mounted on a lowermain shaft 612 driven in the vertical direction by a motor mechanism (not shown). By moving the lowermain shaft 612 upward, theupper mold members 602 are brought into contact with a head (lower end face) of an uppermain shaft 610 fixed to an apparatus frame (not shown). Themother mold 600 is surrounded by aninduction heating coil 614 to heat themother mold 600, theupper mold members 602, and thelower mold members 604 by high-frequency induction heating. Theinduction heating coil 614 is wound around themother mold 600 of an elongated shape. - Referring to
FIG. 8 , the pressing mold (themother mold 600, theupper mold members 602, and the lower mold members 604) is seen from the above. InFIG. 8 , the sixlower mold members 604 have upper surfaces as molding surfaces A to F. In a peripheral region along the outer periphery of themother mold 600, local regions corresponding to areas between every adjacent ones of the molding surfaces A to F are provided withperforations 630. Theperforations 630 may be replaced by the cutouts illustrated inFIGS. 4A to 4C. Alternatively, use may be made of a combination of theperforations 630 and the cutouts. - As a specific example, a biconvex lens having an outer diameter of 15 mm was produced by the use of the above-mentioned press molding apparatus and a spherical preform P of barium borosilicate glass (having a transition point of 512° C. and a sagging point of 545° C.). Specifically, the spherical preform P was placed between each of the
upper mold members 602 and each of thelower mold members 604 of themother mold 600. Themother mold 600 was mounted on thetray 606 and introduced into a forming chamber (not shown) kept in an inactive atmosphere. Thetray 606 was placed on the lower main shaft 612 (FIG. 7 ). Thereafter, the lowermain shaft 612 was moved upward so that themother mold 600 is located inside theinduction heating coil 614. Theinduction heating coil 614 is supplied with a high-frequency current to induction heat themother mold 600. At this time, the temperature of each of the lower molding surfaces A to F (the upper surfaces of the lower mold members 604) was measured by a mold temperature monitoring thermocouple inserted into each of thelower mold members 604. On the other hand, the temperature of each of the upper molding surfaces (the lower surfaces of the upper mold members 602) was measured by a mold temperature monitoring thermocouple inserted into each of theupper mold members 602. As a result, the temperature deviation among the lower molding surfaces A to F and the upper molding surfaces A to F was not greater than ±10° C. Then, the preform was heated by theinduction heating coil 614 to 596° C. (the temperature corresponding to the glass viscosity of 108 poises). Thereafter, the lowermain shaft 612 was further moved upward to bring the upper surfaces of theupper mold members 602 into contact with the head of the uppermain shaft 610 so that the preform P in a softened state was pressed. Subsequently, the lenses thus formed were cooled to a temperature not higher than the glass transition point. Thereafter, the lowermain shaft 612 was moved downward and the lenses were removed together with the pressing mold. As a result, the lenses thus obtained were excellent in surface accuracy with less astigmatic aberration and without nonuniform extension. - Referring to
FIGS. 9A and 9B , description will be made of a press molding apparatus according to a third embodiment of this invention. The press molding apparatus according to the third embodiment comprises anupper mother mold 802 and alower mother mold 804 attached to an uppermain shaft 806 and a lowermain shaft 808, respectively. Each of the upper and thelower mother mold upper mother mold 802 and thelower mother mold 804 are provided with fourupper mold members 812 and fourlower mold members 814, respectively. The upper and thelower mother molds upper mold members 812 is provided with asleeve 816 formed at its outer periphery and fitted to thelower mold member 814 with a small clearance to be slidable along thelower mold member 814. Thesleeve 816 thus serves to prevent axial offset between upper and lower surface of a lens. Theupper mother mold 802 is provided withguide pins 818 while thelower mother mold 804 is provided withguide holes 820 to be engaged with the guide pins 818. Each of the upper and thelower mother molds upper mold members 812, thelower mold members 814, and thesleeves 816 is made of sintered silicon carbide with silicon carbide formed by CVD on the surface thereof.FIG. 9B shows the shape of thelower mother mold 804 in plan view. Theupper mother mold 802 is similar in shape in plan view to thelower mother mold 804 and is not illustrated in the figure. Thelower mold members 814 have preform pressing surfaces as molding surfaces A to D. Within a region along the outer periphery of thelower mother mold 804, a plurality ofperforations 830 are formed in local regions corresponding to areas between every adjacent ones of the molding surfaces A to D. Theperforations 830 may be replaced by the cutouts illustrated inFIGS. 4A to 4C. Alternatively, use may be made of a combination of theperforations 830 and the cutouts. - As a specific example, a biconvex lens (one surface being a spherical surface, the other surface being an aspherical surface) having an outer diameter of 15 mm was formed by pressing barium borosilicate glass (having a transition point of 512° C. and a sagging point of 545° C.) using the above-mentioned press molding apparatus. Specifically, preforms of a marble-like shape prepared by hot forming and having no surface defect were preheated to 470° C. The preforms, four in number, were supplied onto the
lower mold members 814, four in number, of thelower mother mold 804 preheated to about 470° C. Immediately thereafter, thelower mother mold 804 was moved upward to be coupled with theupper mother mold 802 preheated to 470° C. At this time, the guide pins 818 and the guide holes 820 were engaged with each other and thesleeves 816 were fitted over thelower mold members 814, respectively. By high-frequency induction heating by theinduction heating coil 822, the upper and thelower mother molds lower mother mold 804 was moved upward to perform press molding at a pressure of 70 kg/cm2. After completion of the pressing, the lenses thus formed were cooled at a cooling rate of 50° C./min to a temperature not higher than the glass transition point. At this time, each of theupper mold members 812 followed the shrinkage of the lens and the lens was cooled under the weight of theupper mold member 812 alone. In other words, the upper surface of the lens was kept in contact with theupper mold member 812 during cooling. When the temperature was lowered to 490° C., thelower mother mold 804 was moved downward to separate the upper and thelower mother molds lower mother mold 804 was further moved downward to a lower part of a forming chamber (not shown). By the use of a suction pad, four lenses were removed. The lenses thus removed may thereafter be annealed if desired. In these molds (the upper and thelower mother molds lower mold members 812 and 814), substantially uniform heating and cooling were performed. The lenses thus obtained were high in surface accuracy and excellent in surface quality. In addition, eccentricity or decenter after centration was well suppressed. - Next, description will be made of a fourth embodiment of this invention. Referring to
FIG. 10 , a press molding apparatus according to the fourth embodiment comprises upper andlower mother molds lower mother molds lower mother molds lower induction coils lower mother molds FIG. 1A shows the shape of thelower mother mold 804 in plan view. Theupper mother mold 802 is similar in shape in plan view to thelower mother mold 804 and is not illustrated in the figure. In this embodiment also, within a region along the outer periphery of thelower mother mold 804, a plurality ofperforations 830 are formed in local regions corresponding to areas between every adjacent ones of molding surfaces A to F. Theperforations 830 may be replaced by the cutouts illustrated inFIGS. 4A to 4C. Alternatively, use may be made of a combination of theperforations 830 and the cutouts. - As a specific example, a biconvex lens having a diameter of 10 mm was formed by the use of the above-mentioned press molding apparatus. At first, the upper and the
lower mother molds FIG. 10 to obtain mold temperatures shown in Table 1. Three kinds of the mold temperatures were set as shown in Table 1. The temperature deviation among the lower molding surfaces A to F and the upper molding surfaces (the lower surfaces of the upper mold members 812) was measured by the use of a mold temperature monitoring thermocouple. As a result, the temperature deviation was not greater than ±10° C.TABLE 1 at the start of pressing releasing preform temperature mold temperature temperature (viscosity (poise)) (viscosity (poise)) (° C.) 680 (105.8) 549 (1010.2) 485 643 (106.8) 567 (109.2) 495 615 (107.4) 590 (108.2) 505 - On the other hand, apart from the preheating of the pressing mold, six preforms were preheated. Referring to
FIG. 11B , asupport arm 900 which can be opened and closed is provided with six split-type floating saucers 902 (made of glassy carbon) mounted thereon and arranged in series at intervals equal to those of the upper and the lower molds. The six preforms were floated on the floatingsaucers 902 by air stream blowing up from the below and preheated. Thereafter, thesupport arm 900 was transferred in synchronism with the temperature elevation of the pressing mold and inserted between the upper and the lower induction heating coils. Thesupport arm 900 was placed at a position directly above the sixlower mold members 814. By quickly opening thesupport arm 900, the floatingsaucers 902 were split to simultaneously drop and supply the preforms onto the molding surfaces A to F (FIG. 11A ). The preforms were preheated at three different preheat temperatures as illustrated in Table 1. Thereafter, thesupport arm 900 was immediately retreated from the position above thelower mother mold 804. The induction heating coils were deenergized. The lowermain shaft 808 was moved upward so that pressing was performed under the pressure of 70 kg/cm2. After completion of the pressing, the lenses thus formed were cooled down to the temperature not higher than the glass transition point. During cooling, each lens was applied with the weight of theupper mold 812 alone. Thereafter, thelower mother mold 804 was moved downward by about 40 mm to separate or part the upper and thelower mother molds - As a result, under any forming condition shown in Table 1, high-quality lenses were continuously obtained. Thus, it is understood that, according to this embodiment, a large amount of lenses can be continuously produced with high efficiency.
- As a comparative example for the fourth embodiment, six lenses were press formed by the use of a press molding apparatus similar in structure to that of the fourth embodiment except that upper and lower mother mold have no perforations. As a result, the lenses press formed in four molding surfaces (B-E) except two molding surfaces located at opposite ends exhibited extension error and were not excellent in surface accuracy.
- As a specific example for the fourth embodiment, press molding was performed by the use of the press molding apparatus in which the perforations were formed throughout an entire periphery of the mother mold and particularly densely formed in the local regions corresponding to the areas between every adjacent ones of the molding surfaces (see
FIG. 5 ). As a result, it was possible to shorten the time before the target temperature (Table 1) was reached. - Next referring to
FIG. 12 , description will be made of a fifth embodiment of this invention. For example, a press molding apparatus according to the fifth embodiment is used to produce a medium-aperture lens having a diameter of 17 mm by the use of a preform prepared by preliminarily forming a glass material into a flat spherical shape. As illustrated inFIG. 12 , the press molding apparatus comprises a pressing mold set including anupper mold 102 and alower mold 104. Each of the upper and thelower molds lower molds lower molds - The
upper mold 102 comprises a pair of left and right upper pressingmolds lower mold 104 comprises a pair of left and rightpressing molds pressing molds pressing molds pressing molds plates 106 a and 106 b, respectively. The supportingplates 106 a and 106 b have upper surfaces attached to upper supportingshafts shafts shaft 118 through acommon base 114. On the other hand, the lowerpressing molds plates plates shafts shafts drive shaft 120 through acommon base 116. Thedrive shaft 120 is driven by a driving mechanism having an AC servo motor to linearly move in the vertical direction. Thedrive shaft 120 has acenter axis 120 a coincident with the center of each of the upper and thelower molds drive shaft 120 moves in the vertical direction, the upper and thelower molds - Referring to
FIG. 13 , the lower mold 104 (lower pressingmolds induction heating coil 124 therearound are shown in plan view as seen from the above. The upper mold 102 (upperpressing molds lower mold 104 and is not illustrated in the figure. The lowerpressing molds lower mold 104. The lowerpressing mold 104 a has a pair oflong sides 202 extending in the longitudinal direction, an innershort side 204 perpendicular to the long sides 202 (and nearest to the center position O), and an outershort side 206 faced to the inner short side 204 (and farthest from the center position O). The outershort side 206 defines an arc of a half circle having a radius equal to a half of the distance between the two long sides 202 (i.e., the width of the lowerpressing mold 104 a). The other lowerpressing mold 104 b is symmetrical in shape with the lowerpressing mold 104 a with respect to the center position O. Preferably, a gap of 0.5-3 mm is formed between the innershort sides 204 of the lowerpressing molds - The
induction heating coil 124 is wound around both of the lowerpressing molds pressing molds induction heating coil 122 around the upperpressing molds induction heating coil 124. - The lower
pressing mold 104 a has an upper surface provided with threemolding portions 200 for imparting a glass product shape to preforms. Likewise, the lowerpressing mold 104 b has an upper surface provided with threemolding portions 200. These sixmolding portions 200 are arranged in a single line on a center line M defining the center of the lowerpressing molds molding portions 200 have preform pressing surfaces as molding surfaces A, B, C, D, E, and F, respectively. - Each of the lower
pressing molds pressing molds pressing molds short side 204 and thelong sides 202 in each of the lowerpressing molds lower mold 104. Instead of the curve R, the corners may be chamfered or may be formed into an obtuse-angled shape. Alternatively, the innershort sides 204 of the lowerpressing molds - Description will be made of the arrangement of the molding surfaces A to F in each of the lower
pressing molds short side 206 and the interval d6 between the molding surface F and the outershort side 206 are equal to the above-mentioned interval (d1 et al). On the other hand, the interval d3 between the molding surfaces C and D adjacent to each other with the center position O interposed therebetween is greater than the above-mentioned interval (d1 et al). The shortest distance d7 from the molding surface C to the innershort side 204 is substantially equal to the shortest distance d8 from the molding surface C to thelong side 202. Likewise, the shortest distance from the molding surface D to the innershort side 204 is substantially equal to the shortest distance from the molding surface D to thelong side 202. The above-mentioned relationship of d0 to d8 is determined in order to minimize the temperature difference in the molding surfaces A to F during high-frequency induction heating. - The position of the lower supporting
shaft 112 a (FIG. 12 ) in the horizontal plane corresponds to the center position (i.e., the molding surface B) of the molding surfaces A to C of the lowerpressing mold 104 a in its alignment direction. Likewise, the position of the lower supportingshaft 112 b (FIG. 12 ) in the horizontal plane corresponds to the center position (i.e., the molding surface E) of the molding surfaces D to F of the lowerpressing mold 104 b in its alignment direction. With this structure, the pressure is uniformly applied to the preforms on the molding surfaces A to F. Similarly, the positions of the upper supportingshafts pressing molds - Each of the lower
pressing molds pressing molds pressing molds - Next, description will be made of a method of producing a lens (as a glass optical element) according to this embodiment. At first, by high-frequency induction heating of the induction heating coils 122 and 124, the upper
pressing molds pressing molds pressing molds pressing molds pressing molds pressing molds pressing molds pressing molds drive shaft 120 is moved upward to close the upperpressing molds pressing molds shafts shafts pressing molds pressing molds drive shaft 120 is moved downward to open or separate the upper and thelower molds lower mold 104 are sucked and removed. Thus, the lenses surface-processed with high precision are obtained. - Next referring to
FIGS. 14 and 15 , description will be made of the effect achieved by the rounded corners of the upperpressing molds pressing molds FIG. 14 , the temperature distribution was measured at a plurality of positions along the center line M defining the center in the widthwise direction with respect to the lowerpressing molds FIG. 15 shows the result of similar measurement in case where the lowerpressing molds FIG. 15 , in the lowerpressing molds pressing molds FIG. 14 , the temperature difference throughout the lowerpressing molds FIG. 14 is preferred. - In this embodiment, each of the corners of the lower
pressing molds pressing molds pressing molds - As described above, the press molding apparatus according to this embodiment of
FIG. 14 , the upperpressing molds pressing molds pressing molds pressing molds - Furthermore, the upper
pressing molds shafts pressing molds shafts pressing molds pressing molds shafts shaft 118 while the lower supportingshafts common drive shaft 120. Therefore, pressing can be accurately performed by the use of the single driving mechanism. - The upper supporting
shafts pressing molds shafts pressing molds - The gap of 0.5-3 mm is kept between the upper
pressing molds pressing molds pressing molds pressing molds - Next referring to
FIG. 16 , description will be made of a press molding apparatus according to a sixth embodiment of this invention. The press molding apparatus according to the sixth embodiment comprises a pressing mold set including a pair of pressingmolds 60 each of which comprises amother mold 600 having an elongated shape and four pairs of upper andlower mold members mother mold 600 to be vertically movable. InFIG. 16 , only one of the twopressing molds 60 is illustrated. In eachpressing mold 60, theupper mold members 602 and thelower mold members 604 are respectively arranged in a single line. The twopressing molds 60 are placed so that theupper mold members 602 and thelower mold members 604 are respectively arranged in a single line (in a transversal or horizontal direction inFIG. 16 ). The pressing mold set is surrounded by an induction heating coil (not shown) wound in a generally elliptical shape substantially along the outer periphery of the pressing mold set. - Each of the upper and the
lower mold members mother mold 600 is made of a tungsten alloy and has a thermal expansion coefficient slightly greater than that of cemented carbide. Thepressing molds 60 are supported on atray 606 which is attached to an upper end of a lower supportingshaft 612 driven in a vertical direction. Above the lower supportingshaft 612, an upper supportingshaft 610 as a fixed shaft is arranged. By moving the lower supportingshaft 612 upward, theupper mold members 602 are brought into contact with a head (lower end face) of the upper supportingshaft 610. As a consequence, pressing is performed between the upper and thelower mold members - The two
pressing molds 60 are similar in shape in plan view to the lowerpressing molds FIG. 13 . That is, the twopressing molds 60 have a shape with rounded corners on adjacent sides. - As a specific example, a biconvex lens having an outer diameter of 15 mm was produced by the use of the above-mentioned press molding apparatus and a spherical preform P of barium borosilicate glass (having a transition point of 512° C. and a sagging point of 545° C.). Specifically, the spherical preform P was placed between each of the
upper mold members 602 and each of thelower mold members 604 of themother mold 600. Themother mold 600 was mounted on thetray 606 and introduced into a forming chamber (not shown) kept in an inactive atmosphere. Thetray 606 was placed on the lower supporting shaft 612 (FIG. 12 ). Thereafter, the lower supportingshaft 612 was moved upward so that thepressing molds 60 are located inside the induction heating coil. The induction heating coil is supplied with a high-frequency current to induction heat themother mold 600. At this time, the temperature of each of lower molding surfaces (upper surfaces of the lower mold members 604) was measured by a mold temperature monitoring thermocouple inserted into each of thelower mold members 604. On the other hand, the temperature of each of upper molding surfaces (lower surfaces of the upper mold members 602) was measured by a mold temperature monitoring thermocouple inserted into each of theupper mold members 602. As a result, the temperature deviation among the lower molding surfaces and the upper molding surfaces during the induction heating was not greater than ±10° C. Then, the preform was heated by the induction heating coil to 596° C. (the temperature corresponding to the glass viscosity of 108 poises). Thereafter, the lower supportingshaft 612 was further moved upward to bring the upper surfaces of theupper mold members 602 into contact with the head of the upper supportingshaft 610 so that the preform P in a softened state was pressed. Subsequently, the lenses thus formed were cooled to a temperature not higher than the glass transition point. Thereafter, the lower supportingshaft 612 was moved downward and the lenses were removed together with the pressing mold. As a result, the lenses thus obtained were excellent in surface accuracy with less astigmatic aberration and without nonuniform extension. - Referring to
FIG. 17 , description will be made of a press molding apparatus according to a seventh embodiment of this invention. The press molding apparatus according to the seventh embodiment comprises a pressing mold set including a pair of pressingmolds 80 each of which comprises anupper mother mold 802 and alower mother mold 804 provided with fourupper mold members 812 and fourlower mold members 814, respectively. InFIG. 17 , only one of the twopressing molds 80 is illustrated. In each of thepressing molds 80, theupper mold members 812 and thelower mold members 814 are respectively aligned in a single line so that molding surfaces are aligned in a single line. The pressing mold set comprising the twopressing molds 80 is arranged so that theupper mold members 812 and thelower mold members 814 are respectively aligned in a single line (in a transversal or horizontal direction inFIG. 17 ). The pressing mold set is surrounded by an induction heating coil (not shown) wound in a generally elliptical shape substantially along an outer periphery of the pressing mold set. Theupper mother mold 802 is supported by an upper supportingshaft 806 as a fixed shaft. Thelower mother mold 804 is fixed to a lower supportingshaft 808 driven in the vertical direction. - Each of the
upper mold members 812 is provided with asleeve 816 formed at its outer periphery and fitted to thelower mold member 814 with a small clearance to be slidable along thelower mold member 814. Thesleeve 816 thus serves to prevent axial offset between upper and lower surfaces of a lens. Theupper mother mold 802 is provided withguide pins 818 while thelower mother mold 804 is provided withguide holes 820 to be engaged with the guide pins 818. Each of the upper and thelower mother molds upper mold members 812, thelower mold members 814, and thesleeves 816 is made of sintered silicon carbide with silicon carbide formed by CVD on the surface thereof. - The two
pressing molds 80 are similar in shape in plan view to the lowerpressing molds FIG. 13 . That is, the twopressing molds 80 have a shape with rounded corners on adjacent sides. - As a specific example, a biconvex lens (one surface being a spherical surface, the other surface being an aspherical surface) having an outer diameter of 10 mm was formed by pressing barium borosilicate glass (having a transition point of 512° C. and a sagging point of 545° C.) using the above-mentioned press molding apparatus. Specifically, preforms of a flat spherical shape prepared by hot forming and having no surface defect were preheated to 470° C. The preforms, four in number, were supplied onto the
lower mold members 814, four in number, of thelower mother mold 804 preheated to about 470′. Immediately thereafter, thelower mother mold 804 was moved upward to be coupled with theupper mother mold 802 preheated to 470° C. At this time, the guide pins 818 and the guide holes 820 were engaged with each other and thesleeves 816 were fitted over thelower mold members 814, respectively. By high-frequency induction heating by the induction heating coil, the upper and thelower mother molds lower mother mold 804 was moved upward to perform press molding at a pressure of 70 kg/cm2. After completion of the pressing, the lenses thus formed were cooled at a cooling rate of 50° C./min to a temperature not higher than the glass transition point. At this time, each of theupper mold members 812 followed the shrinkage of the lens and the lens was cooled under the weight of theupper mold member 812 alone. In other words, the upper surface of the lens was kept in contact with theupper mold member 812 during cooling. When the temperature was lowered to 490° C., thelower mother mold 804 was moved downward to separate the upper and thelower mother molds lower mother mold 804 was further moved downward to a lower part of a forming chamber (not shown). By the use of a suction pad, four lenses were removed. The lenses thus removed may thereafter be annealed if desired. In these molds (the upper and thelower mother molds lower mold members 812 and 814), substantially uniform heating and cooling were performed. The lenses thus obtained were high in surface accuracy and excellent in surface quality. In addition, eccentricity or decenter after centration was excellent. - Next, description will be made of an eighth embodiment of this invention. A press molding apparatus according to the eighth embodiment comprises a pressing mold set including a pair of pressing molds which is similar in structure to those of the seventh embodiment except that an
upper mother mold 802 and alower mother mold 804 comprise threeupper mold members 812 and threelower mold members 814, respectively. Each of the upper and the lower mother molds and the upper and the lower mold members is similar in structure to that in the seventh embodiment (except the number of the upper and the lower mold members). Similar parts are designated by like reference numerals. The two pressing molds are similar in shape in plan view to the lowerpressing molds FIG. 13 . That is, the two pressing molds have a shape with rounded corners on adjacent sides. - As a specific example, a biconvex lens having a diameter of 10 mm was formed by the use of the above-mentioned press molding apparatus. At first, the upper and the
lower mother molds TABLE 1′ at the start of pressing releasing preform temperature mold temperature temperature (viscosity (poise)) (viscosity (poise)) (° C.) 680 (105.8) 549 (1010.2) 485 643 (106.8) 567 (109.2) 495 615 (107.4) 590 (108.2) 505 - Then, six preforms were floated on a transfer arm (not shown) by gas stream and transferred. Thereafter, the transfer arm was placed at a position directly above the six
lower mold members 814 and the preforms were simultaneously dropped and supplied onto thelower mold members 814. The preforms were preheated at three different preheat temperatures as shown in Table 1′. Thereafter, the transfer arm was immediately retreated from the position above thelower mother mold 804. The induction heating coils were deenergized. A lower supportingshaft 808 was moved upward and pressing was performed under the pressure of 70 kg/cm2. After completion of the pressing, the lenses thus formed were cooled down to the temperature not higher than the glass transition point. During cooling, each lens was applied with the weight of theupper mold 812 alone. Thereafter, thelower mother mold 804 was moved downward by about 40 mm to separate or part the upper and thelower mother molds - As a result, under any forming condition shown in Table 1′, high-quality lenses were continuously obtained. Thus, it is understood that, according to this embodiment, a large amount of lenses can be continuously produced with high efficiency.
- As a different example for the eighth embodiment, lenses were formed by the use of a press molding apparatus (see
FIG. 15 ) similar in structure to that of the eighth embodiment except that corners of the pressing molds are not rounded but angled. As a result, the lenses press formed in two molding surfaces (corresponding to C-D inFIG. 15 ) exhibited slightly inferior surface accuracy to the lenses press formed in four molding surfaces (corresponding to A-B and E-F). - Thus, the embodiments of this invention have been described with reference to the drawing. However, this invention is not restricted to the foregoing embodiments but may be modified in various manners within the scope of the appended claims. In the first through the fourth embodiments, both of the upper and the lower molds are provided with the perforations (or the cutouts). Alternatively, the perforations (or the cutouts) may be formed in only one of the upper and the lower molds.
- Thus, according to this invention, it is possible to collectively heat the molding surfaces by the induction heating coil to a desired temperature and to increase the heating rate of the upper and the lower molds because the upper mold and/or the lower mold is provided with the shape-processed heat generator having, for example, the perforations and/or the cutouts allowing a greater amount of heat to be locally generated during high-frequency induction heating.
- Furthermore, by forming the shape-processed heat generator having, for example, the perforations and/or the cutouts so that the temperatures of the molding surfaces approach one another during induction heating, the temperature distribution in the inside of the upper mold and/or the lower mold can be kept uniform.
- In the fifth through the eighth embodiments, the pressing mold set comprises the two upper and the two lower pressing molds (the upper
pressing molds pressing molds lower molds - As described above, according to this invention, the pressing mold set comprises a plurality of pressing molds. These pressing molds have a shape with the rounded corners as a processed shape of heat generator on adjacent sides. With this structure, excessive local concentration of heat during high-frequency induction heating can be avoided and the variation in temperature between the molding surfaces formed in the pressing molds is suppressed. As a result, it is possible to produce a plurality of optical elements with high accuracy.
Claims (22)
1. A method of manufacturing a glass optical element by use of a pressing mold comprising upper and lower molds each of which comprises a molding surface, at least one of said upper and lower molds comprising a heat generator within which heat is generated when said heat generator is subjected to high-frequency induction heating, said heat generator comprising a shape-processed portion produced by processing a shape of said heat generator in order that a temperature distribution of said heat generator is adjusted when said heat generator is subjected to high-frequency induction heating, comprising the steps of:
subjecting at least one of said upper and said lower molds to said high-frequency induction heating so that the molding surfaces of said upper mold and said lower mold have predetermined temperatures; and
press molding said glass material supplied between said molding surfaces of said upper and said lower molds into said glass optical element.
2. The method of claim 1 wherein said shape-processed portion comprises at least one of a perforation, cutout, curved surface, and obtuse angle.
3. The method of claim 2 wherein each of said upper and lower molds comprises a plurality of molding surfaces so that a plurality of said glass materials be press molded simultaneously.
4. The method of claim 3 wherein said shape-processed portion is located so that temperature of each molding surface on the upper mold or the lower mold be brought closer.
5. The method of claim 4 wherein said each of said upper and lower molds has a shape extended in a direction, said molding surfaces being arranged in the direction.
6. A method of manufacturing a glass optical element comprising:
preparing a pressing mold comprising upper and lower molds each of which comprises a molding surface, at least one of said upper and lower mold comprising a heat generator within which heat is generated when said heat generator is subjected to high-frequency induction heating,
processing a shape of said heat generator so that a temperature distribution of said heat generator is adjusted when said heat generator is subjected to high-frequency induction heating,
subjecting at least one of said upper and said lower molds to said high-frequency induction heating so that each of the molding surfaces of said upper mold and said lower mold have predetermined temperature; and
press molding a glass material supplied between said molding surfaces of said upper and said lower molds into said glass optical element.
7. The method of claim 6 wherein a shape-processed portion formed by said processing comprises at least one of a perforation, cutout, curved surface, and obtuse angle.
8. The method of claim 6 wherein each of said upper and lower molds comprises a plurality of molding surfaces so that a plurality of said glass materials be press molded simultaneously.
9. The method of claim 8 wherein a shape-processed portion formed by said processing is located so that temperature of each molding surface on the upper mold or the lower mold brought closer.
10. The method of claim 6 wherein each of said upper and lower molds comprises a plurality of molding surfaces,
which method further comprises, prior to said processing, measuring a temperature distribution of molding surfaces on upper or lower mold when said heat generator is subjected to high-frequency induction heating to observe a temperature deviation of said molding surfaces from each other, and said processing is carried out so that said deviation is reduced.
11. The method according to claim 1 , wherein said glass material is are heated to a preselected temperatures to be softened before said glass material are supplied between the molding surfaces of said upper and said lower molds.
12. The method according to claim 11 wherein said preselected temperature is higher than the temperatures of the molding surface of said upper and said lower molds when said glass materials are supplied between the molding surfaces of said upper and said lower molds.
13. The method according to claim 12 , wherein said glass materials are heated to the preselected temperature to be softened so that said glass materials have a viscosity not higher than 109 poises.
14. The method according to claim 1 , further comprising the steps of:
preparing a pressing mold set comprising a plurality of said pressing molds which are arranged so that the molding surfaces of the upper molds of said pressing molds are aligned in an upper single line and that the molding surfaces of the lower molds of said pressing mold are aligned in a lower single line parallel to said upper single line, each of the upper and the lower mold comprising the heat generator within which heat is generated when said heat generator is subjected to the high-frequency induction heating;
at least a pair of the adjacent heat generators of the upper molds or the lower molds comprises the shape processed portion comprising rounded corners formed on sides of the heat generators adjacent with each other.
15. The method of claim 14 , wherein said glass materials are heated to a preselected temperature to be softened before said glass material are supplied between the molding surfaces of said upper and said lower molds, said preselected temperature being higher than the temperatures of the molding surface of said upper and said lower molds when said glass materials are supplied between the molding surfaces of said upper and said lower molds.
16. The method according to claim 15 , wherein said glass materials are heated to the preselected temperature to be softened so that said glass materials have a viscosity not higher than 109 poises.
17. A press molding apparatus for preparing a plurality of glass optical elements from a plurality of glass materials, comprising:
upper and lower molds each of which comprises a plurality of molding surfaces; and
an induction heating device for heating said upper and lower molds;
at least one of said upper and lower mold comprising a heat generator within which heat is generated when said heat generator is subjected to high-frequency induction heating by said induction heating device;
said heat generator comprising a shape-processed portion produced by processing a shape of said heat generator in order that a temperature distribution of said heat generator is adjusted when said heat generator is subjected to high-frequency induction heating.
18. The apparatus according to claim 17 , wherein said shape-processed portion comprises a rounded surface.
19. The apparatus according to claim 17 , wherein said shape-processed portion comprises an acute-angled shape.
20. The apparatus according to claim 17 , wherein said shape-processed portion comprises a knurled shape.
21. The apparatus according to claim 17 , wherein said shape-processed portion comprises a chamfered corner.
22. The apparatus according to claim 17 , wherein said shape-processed portion comprises an obtuse-angled corner.