US20060001105A1 - Semiconductor device having optimized shallow junction geometries and method for fabrication thereof - Google Patents
Semiconductor device having optimized shallow junction geometries and method for fabrication thereof Download PDFInfo
- Publication number
- US20060001105A1 US20060001105A1 US11/179,210 US17921005A US2006001105A1 US 20060001105 A1 US20060001105 A1 US 20060001105A1 US 17921005 A US17921005 A US 17921005A US 2006001105 A1 US2006001105 A1 US 2006001105A1
- Authority
- US
- United States
- Prior art keywords
- oxide layer
- resistant
- etch
- type
- gate structure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
The present invention provides, in one embodiment, a method of fabricating a semiconductor device (100). The method comprises growing an oxide layer (120) on a gate structure (114) and a substrate (102) and implanting a dopant (124) into the substrate (102) and the oxide layer (120). Implantation is such that a portion of the dopant (124) remains in the oxide layer (120) to form an implanted oxide layer (126). The method further includes depositing a protective oxide layer (132) on the implanted oxide layer (126) and forming etch-resistant off-set spacers (134). The etch-resistant off-set spacers (134) are formed adjacent sidewalls of the gate structure (114) and on the protective oxide layer (132). The etch resistant off-set spacers having an inner perimeter (135) adjacent the sidewalls and an opposing outer perimeter (136). The method also comprises removing portions of the protective oxide layer (132) lying outside the outer perimeter (136) of the etch-resistant off-set spacers (134). Other embodiments of the present invention include a transistor device (200) and method of manufacturing an integrated circuit (300).
Description
- The present invention is directed in general to the manufacture of semiconductor devices, and, more specifically, to a method of fabricating transistor devices having optimized shallow junction geometries.
- The continuing push to produce faster semiconductor devices with lower power consumption has resulted in the miniaturization of semiconductor devices. In particular, smaller gate oxide thickness and channel width are conducive to the low voltage and faster operation of transistor devices, such as complementary metal oxide (CMOS) transistors. With shrinking process geometries, comes a number of new design problems, however.
- For instance, as gate dimensions are reduced, it has become necessary to adjust and better control the dimensions of the channel and doped regions of the substrate that are associated with the gate. This is necessary to prevent a number of short channel effects, such as hot carrier injection, leakage currents, drain induced barrier lowering (DIBL), threshold voltage variation and mobility degradation.
- Consider, for instance, the dimensions of shallow junctions and pocket region structures. Shallow junctions, also referred to as source drain extensions, or light or middle-doped drain (LDD and MDD, respectively) regions, are implanted as extensions to the larger and more heavily doped source and drain regions, to reduce hot carrier injection-induced damage to gate dielectric layers and drifting threshold voltage. Hot carriers, electrons with higher than average energy, form because of the stronger electric fields produced in small transistor device geometries. Shallow junctions, implanted before sidewall formation and source and drain implantation, provide a doping gradient between the source and drain regions and the channel. The lowered electric field in the vicinity of the channel region of such devices reduces the formation of hot carriers.
- Sub-0.1 micron transistor devices are also highly susceptible to leakage currents, or punch-through, when the transistor is off. Leakage currents can be reduced if the shallow junctions are formed with well-defined boundaries, as exemplified by an abrupt decrease in dopant concentration, to support low-voltage operation of the transistor and to define the width of the channel region of the transistor. The formation of abrupt shallow junctions can be problematic in certain instances, however.
- For, instance, to establish p-type doped shallow junctions in a positive channel metal oxide semiconductor (PMOS) transistor, a typical p-type dopant is boron (B+). Small dopants, such as boron, are subject to undesirable enhanced diffusion into implantation-caused damage to the lattice structures of silicon substrates during thermal annealing. This phenomenon, known as transient enhanced diffusion (TED), is undesirable because it decreases the abruptness of the change in dopant concentrations from the shallow junction to a p-well or n-well that the shallow junction is formed in. TED deters the formation of shallow junctions having suitably shallow depths (e.g., less than about 40 nm). TED can also cause dopants, such as boron, to diffuse into the channel region, thereby causing an unfavorable change in the dopant concentration in the channel resulting in punch-through, an increase in electron trapping, a decrease in low-field hole mobility, and a degraded on-current drive.
- Another approach to reduce leakage currents is to implant a lightly doped pocket or halo region, containing dopants of the opposite dopant type of the shallow junction, around the edges of the shallow junction. The dopants in the pocket region provide increases resistance in the channel region to reduce or prevent leakage currents. However, if the pocket regions on the source and drain sides of the transistor's channel region are too close to each other, then the pocket regions will overlap. Overlap, in turn, causes excessively high resistance in the channel region, thereby undesirably reducing the on-current of the device.
- One approach to reduce excessively close shallow junctions or overlapping pockets regions, is to introduce off-set spacers on the sides of gates prior to dopant implantation. The off-set spacers act as mask during the implantation of dopants to prevent dopants of the source and drain shallow junctions or pocket regions from being too close to each after the transistor is thermally annealed. This approach is not entirely successful, however, because the extent of diffusion of p-type and n-type dopants during thermal annealing are substantially different than each other.
- For instance, to establish n-type doped shallow junctions in a negative channel metal oxide semiconductor (NMOS) transistor, a typical n-type dopant is arsenic (As+) or phosphorus (P+). However, because of their higher mass and different electrical properties than boron, arsenic and phosphorus are not subject to TED to the same extent as boron. Consequently, the fabrication steps used to mitigate the short channel effects in PMOS transistors are not necessarily beneficial to mitigate the short channel effects in NMOS transistors. Indeed, if the junctions in an NMOS transistor are too far apart, this can detrimentally decrease the source to drain saturation current of the NMOS transistor, thereby reducing the operating speed of the device. Moreover, an abrupt shallow junction depth in NMOS transistors improves Vt roll-off, DIBL, gate-edge capacitance (Cge) and mobility degradation.
- Heretofore, however, the fabrication processes for PMOS and NMOS transistors in CMOS devices have resulted in the formation of shallow junctions having substantially the same geometries. As such, the geometries of one or both of the NMOS and PMOS shallow junctions have not been simultaneously optimized in both transistor types. Because current CMOS devices are constructed with compromised NMOS and PMOS shallow junction geometries, the performance of these devices is also compromised.
- Accordingly, what is needed in the art is an improved method of manufacturing shallow junctions having geometries that are separately optimized for NMOS and PMOS transistor configurations.
- To address the above-discussed deficiencies of the prior art, the present invention provides a method of fabricating a semiconductor device. The method comprises growing an oxide layer on a gate structure and a substrate and implanting a dopant into the substrate and the oxide layer. Implantation is such that a portion of the dopant remains in the oxide layer to form an implanted oxide layer. A protective oxide layer is deposited on the implanted oxide layer. The method also comprises forming etch-resistant off-set spacers adjacent sidewalls of the gate structure and on the protective oxide layer. The etch resistant off-set spacers have an inner perimeter adjacent the sidewalls and an opposing outer perimeter. The method additionally includes removing portions of the protective oxide layer lying outside of the outer perimeter of the etch-resistant off-set spacers.
- Another embodiment of the present invention is a metal oxide semiconductor (MOS) transistor device. The semiconductor device includes a gate structure on a substrate and an oxide layer on a sidewall of the gate structure and on a portion of the substrate adjacent the gate structure. The device further comprises a protective oxide layer on the oxide layer and an oxide etch-resistant off-set spacer. The oxide etch-resistant off-set spacer is adjacent the sidewall and located on the protective oxide layer. An outer perimeter of the oxide layer and the protective oxide layer are coextensive with an outer perimeter of the oxide etch-resistant off-set spacer.
- Still another embodiment of the present invention is a method of manufacturing an integrated circuit. The method includes forming metal oxide semiconductor (MOS) transistor devices, as described above, and interconnecting the MOS transistor devices with interconnects to form an operative integrated circuit.
- The foregoing has outlined preferred and alternative features of the present invention so that those of ordinary skill in the art may better understand the detailed description of the invention that follows. Additional features of the invention will be described hereinafter that form the subject of the claims of the invention. Those skilled in the art should appreciate that they can readily use the disclosed conception and specific embodiment as a basis for designing or modifying other structures for carrying out the same purposes of the present invention. Those skilled in the art should also realize that such equivalent constructions do not depart from the scope of the invention.
- The invention is best understood from the following detailed description when read with the accompanying FIGUREs. It is emphasized that in accordance with the standard practice in the semiconductor industry, various features may not be drawn to scale. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion. Reference is now made to the following descriptions taken in conjunction with the accompanying drawings, in which:
-
FIGS. 1A to 1I illustrate partial sectional views of selected steps in a method for fabricating a semiconductor device according to the principles of the present invention; -
FIGS. 2A and 2B illustrate partial sectional views of metal oxide semiconductor (MOS) transistor devices of the present invention; and -
FIGS. 3A and 3B illustrate partial sectional views of selected steps in a method for manufacturing an integrated circuit according to the principles of the present invention. - The present invention recognizes that for transistor devices having gate lengths of about 50 nanometers or less, it is advantageous to fabricate shallow junctions with separately optimized geometries. In certain transistor devices, for instance, MDD regions of an NMOS transistor are advantageously made shallower and having smaller off-sets, as compared to MDD regions for a PMOS transistor fabricated on the same substrate. The present invention presents fabrication processes that are separately optimized for PMOS and NMOS transistors facilitates the manufacture transistor devices having improved performance characteristics than previously realized.
- One embodiment of the present invention is illustrated in
FIGS. 1A to 1H, which illustrate sectional views of selected steps, at various stages of manufacture, of a method for fabricating asemiconductor device 100. Turning first toFIG. 1A , illustrated is a partial sectional view of a conventionally formedsemiconductor substrate 102, such as a silicon wafer. First and second portions of thesubstrate isolation trench 105. In such embodiments, the p-type substrate 104 is doped with and a p-type dopant, such as boron, while the n-type substrate 104 is preferably doped with an n-type dopant, such as arsenic or phosphorus. In some embodiments, theisolation trench 105 is formed to a depth of about 400 nanometers, using conventional procedures such as lithography and chemical vapor deposition (CVD) techniques to form shallow trench isolation structures. - Conventional procedures are used to form a gate structure, such as a first and
second gate structure gate 114 andgate dielectric 116. In certain configurations, the gate structure includes anNMOS gate structure 110 and aPMOS gate structure 112. Thegate 114 preferably comprises polysilicon, and thegate dielectric 116 comprises silicon oxide, although other well-known materials may also be used. As well known to those skilled in the art, silicon oxide and polysilicon layers can be formed over thesubstrate 102, and then patterned using lithography techniques to form thegate structures FIG. 1A . In certain advantageous embodiments, thegate structure length 118 of less than about 50 nanometers. -
FIG. 1B shows the partially completedtransistor device 100 ofFIG. 1A after growing anoxide layer 120 on thegate structure substrate 102. Theoxide layer 120 advantageously repairs damage to thegate structure gate structures oxide layer 120 is preferably between about 10 and about 80 Angstroms thick and is conformally grown on thegate structure substrate 102. In certain advantageous embodiments, theoxide layer 120 is a layer of silicon oxide thermally grown by subjecting the partially completed device to a temperature of between about 600 and about 900° C. for between about 10 and about 100 minutes in an oxygen containing environment. In certain preferred embodiments,oxide layer 120 is grown over both the first andsecond gate structures - Turning to
FIG. 1C , the partially completeddevice 100 is depicted, while implanting adopant 124 into thesubstrate 102 and theoxide layer 120. In the illustrated embodiment, thedopant 124 is an n-type dopant, such as phosphorus, arsenic or a combination thereof. Implantation is such that a portion of thedopant 124 remains in theoxide layer 120 to form an implantedoxide layer 126. During implantation, preferably afirst portion 122 of thesubstrate 102 andoxide layer 120 are exposed to thedopant 124. During such implantation, asecond portion 128 of thesubstrate 102 andoxide layer 120 are preferably protected from exposure to thedopant 124 by anoverlying layer 130, such as a photoresist, formed using conventional procedures. Thegate structure 110 advantageously acts as a mask to define the portion of thesubstrate 102 exposed to thedopant 124. - Of course, the selection of
dopant 124 type depends on the type of device being fabricated. In the illustrated embodiment, anarsenic dopant 124 is implanted at a dose of between about 2×1014 and about 2×1015 atoms/cm2, and more preferably between about 5×1014 and about 1×1015 atoms/cm2. Implanting also preferably includes applying an acceleration energy of between about 0.5 and about 5 keV, and more preferably between about 0.5 and about 2 keV. At such energies, a substantial portion of the n-type dopant 124 remains in theoxide layer 120, thereby forming the implantedoxide layer 126. For example, between about 10 percent to about 50 percent of a total dose of thedopant 124 used in implanting remains in the oxide layer, with the remaining dopant implanted in theunderlying substrate 102. -
FIG. 1D shows the partially completedtransistor device 100, after depositing aprotective oxide layer 132 over the oxide layers 120, 126. Theprotective oxide layer 132 advantageously serves as an etch stop during formation of an off-set layer as discussed below. Theprotective oxide layer 132 also can prevent the removal of the implantedoxide layer 126, during wet etching, which is further described below. Additionally, theprotective oxide layer 132 inhibits out-diffusion of thedopant 124 during a thermal anneal. In certain preferred embodiments of the method, the resistlayer 130, depicted inFIG. 1C , is removed before depositing theprotective oxide layer 132. In such embodiments, theprotective oxide layer 132 is thus deposited over both the implantedoxide layer 126 on the first portion of thesubstrate 122, and theoxide layer 120 on the second portion of thesubstrate 128. - As illustrated in
FIG. 1D , theprotective oxide layer 132 conforms to the surface ofoxide layer gate structure protective oxide layer 132 can be deposited by CVD of a silicon dioxide using a precursor, such as tetraethyl ortho-silicate (TEOS). The thickness of theprotective layer 132 may vary. Preferably, theprotective oxide layer 132 has a thickness of between about 25 and about 100 Angstroms. - Turning now to
FIG. 1E , illustrated is the partially completedtransistor device 100, after forming etch-resistant off-setspacers 134 adjacent sidewalls of thegate structure protective oxide layer 132. In certain preferred embodiments, the etch-resistant off-setspacers 134 are formed adjacent sidewalls of both the first andsecond gate structures spacers 134 serve as a mask layer to separate regions that will form MDD regions after thermal annealing, as discussed below. In addition, the etch-resistant offsetspacers 134 advantageously serve as an etch stop to prevent the removal of the implantedoxide layer 126. - In some advantageous configurations, the etch-resistant off-set spacer is an oxide etch-resistant off-set
spacer 134. That is, the oxide etch-resistant off-setspacer 134 has a higher resistance to wet etchants, such aqueous hydrofloric acid, than theprotective oxide layer 132. The oxide etch-resistant off-setspacer 134 facilitates removal of portions of the protective oxide layer as explained below. Suitable materials comprising the etch-resistant off-setspacers 134 include silicon nitride and silicon oxynitride. - In certain preferred embodiments, the etch-resistant off-set
spacer 134 is formed by depositing a layer of etch-resistant material, such as silicon nitride, over theprotective oxide layer 132 by chemical vapor deposition. Portions of the etch-resistant material are then removed by an anisotropic etch, such as a reactive ion etch (RIE). Thus, the etch resistant off-setspacer 134 has aninner perimeter 135 adjacent the sidewalls of thegate structure outer perimeter 136. The etch-resistant off-set spacer 133 can have a horizontal thickness of between about 25 and about 100 Angstroms. However, the thickness can be varied, depending on the design. -
FIG. 1F shows the partially completedtransistor device 100 after removing portions of theprotective oxide layer 132, shown inFIG. 1E , lying outside of the outer perimeter of the etch-resistant off-setspacers 136. The portions of theprotective oxide layer 132 that are removed lay over portions of thesubstrate 138 are separated from thegate structures spacers 134. - Portions of the
protective oxide layer 132 can be removed by exposing the partially completedtransistor device 100 to a wet etchant, such an aqueous solution of hydrogen fluoride (HF), in a wet-etch chamber. - In some configurations, is desirable to adjust the removal conditions so as to avoid removing the implanted
oxide layer 126. In such embodiments, a small portion (e.g., less than about 5 Angstroms) of theprotective oxide layer 132 laying outside of the of the outer perimeter of the etch-resistant off-setspacers 136 is retained. - In alternative embodiments, however, where a thermal anneal has already been performed to diffuse the
dopant 124 from the implantedoxide layer 126 into thesubstrate 102, more aggressive removal conditions can be used to substantially remove the entire portion of theprotective oxide layer 132 laying outside of the of the outer perimeter of the etch-resistant off-setspacers 136, as illustrated. - Turning now to
FIG. 1G , the partially completedtransistor device 100 is illustrated in preparation for a second implantation. Preferably the first portion of thesubstrate 122, and associated structures are protected from implantation by depositing asecond photoresist layer 140 over these structures. In some cases it is also desirable to remove any remaining portions of theoxide layer 120 that are not protected by thephotoresist layer 140 or thegate structure 112, because this allows better control of the second implantation. Removal can be accomplished via wet-etching similar to that described above. - Turning now to
FIG. 1H , shown is thetransistor device 100, while implanting asecond dopant 142 into thesubstrate 102. Preferably, thesecond dopant 142 is of the opposite dopant type as the first implanteddopant 124. As an example, where thefirst dopant 124 is an n-type dopant, thesecond dopant 142 is a p-type dopant, such as boron, and is implanted into the second portion of thesubstrate 128, such as an n-type substrate. Analogous to that described above, thesecond gate structure 112, advantageously serves as a mask to define the portion of thesubstrate 102 that is exposed to thesecond dopant 142. During the implant, - As noted above, portions of the
protective oxide layer 132 are removed before implanting asecond dopant 142 into thesubstrate 102. Removing portions of theprotective oxide layer 132 facilitates penetration and activation of thesecond dopant 142 in thesubstrate 102. - In other embodiments, the
second dopant 142 is implanted with sufficient energy such that only trace amounts (e.g., less than about 2 percent) of thesecond dopant 142 remain in theoxide layer 120. For example, implanting includes implanting boron difluoride (BF2) dopant at a dose of between about 3×1014 and about 3×1015 atoms/cm2, and more preferably between about 1×1015 and about 2×1015 atoms/cm2. Implanting thesecond dopant 142 preferably includes an acceleration energy of between about 1 and about 20 keV, and more preferably between about 3 and about 10 keV. - Turning now to
FIG. 1I , illustrated is an embodiment of the partially completedtransistor device 100 after performing a thermal anneal to form first and second dopant-type MDD regions 144, 146. In this embodiment, the first and second dopant-type MDD regions 144, 146 are n-type and p-type MDD regions, respectively. The thermal anneal is performed at a sufficient temperature and duration so as cause the first andsecond dopant oxide layer 126 and surface regions of thesubstrate 102, to deeper levels in the substrate. The thermal anneal also advantageously serves to activate the dopants, 124, 142, as well understood by those skilled in the art. - Preferably, only one thermal anneal is performed to form the MDD regions 144, 146 in both the first and second portions of the
substrate second dopant oxide layer 120 and in thesubstrate 102, as described above. The thermal anneal can comprise heating to a temperature of between about 900 and about 1100° C. for up to about 30 seconds, although other conditions may be used to suit theparticular dopants - In alternative aspects, however, two thermal anneals are performed. In such embodiments, a first thermal anneal is done after implanting the
dopant 124 into the first portion of thesubstrate 122 andoxide layer 126, such as depicted inFIG. 1C . A second thermal anneal is then done after implanting thesecond dopant 142 in the second portion of thesubstrate 128, such as illustrated inFIG. 1G . Preferably, the first thermal anneal comprises heating to a temperature of between about 800 and about 1000° C. for up to about 30 seconds, and the second thermal anneal comprises heating to a temperature of between about 1000 and about 1100° C. for up to about 5 seconds. -
FIGS. 2A and 2B illustrate another aspect of the present invention, a metal oxide semiconductor (MOS)transistor device 200. Any of the above-described embodiments of the methods for manufacturing thesemiconductor device 100 depicted inFIGS. 1A-1H may be used to fabricate theMOS devices 200 depicted inFIG. 2A or 2B. Turning initially toFIG. 2A , theMOS transistor device 200 includes agate structure 202 on asubstrate 204. In submicron applications, thegate structure 202 preferably has alength 206 of less than about 50 nanometers. - The
device 200 also includes anoxide layer 208 on a sidewall of thegate structure 210 and on a portion of thesubstrate 202 adjacent thegate structure 202. Theoxide layer 208 can be between about 10 and about 80 Angstroms thick, although other thicknesses can be used to suit particular device applications. Thedevice 200 further includes aprotective oxide layer 212 on the oxide layer. The thickness of the protective oxide layer 214 is between about 25 and about 100 Angstroms, and more preferably, between about 50 and about 100 Angstroms. In certain preferred embodiments, the thickness of the protective oxide layer on portions of the substrate adjacent to thesidewalls 216 is about double the thickness of thickness the protective oxide structures 214 adjacent thesidewalls 210. In such embodiments, theprotective oxide layer 212 thereby forms an L-, or horizontally inverted-L-, structure. - The
device 200 further includes an oxide etch-resistant off-setspacer 218 adjacent thesidewall 210 and located on theprotective oxide layer 212. Anouter perimeter 220 of theoxide layer 208 and theprotective oxide layer 212 is coextensive with anouter perimeter 220 of the oxide etch-resistant off-setspacer 218. The etch-resistant off-set spacer can have athickness 222 of between about 25 and about 100 Angstroms, and more preferably, between about 50 and about 80 Angstroms. Preferably, a second upperouter perimeter 224 of theoxide layer 208, theprotective oxide layer 212 and oxide etch-resistant off-setspacer 218 are coextensive with an outer perimeter of a ceiling of the gate structure 226. - Turning to
FIG. 2B , illustrated is one embodiment of theMOS transistor device 200. Analogous reference numbers are used to identify like structures depicted inFIG. 2A . In certain preferred embodiments, theMOS transistor device 200 further includes NMOS andPMOS transistors PMOS transistors second gate structures oxide layer 208, theprotective oxide layer 212, and the oxide etch-resistant off-setspacers 218, similar to that depicted inFIG. 2A . The NMOS andPMOS transistors CMOS device 200. - In some desirable configurations, the NMOS and
PMOS transistors type MDD regions type MDD regions type substrates PMOS transistors depth 244 of the n-type MDD regions are preferably about 30 to about 50 percent shallower than adepth 246 of the p-type MDD regions. For instance, in certain embodiments, the n-type MDD regions 236 have a substantially constant arsenic concentration of greater than about 1×1020 atoms/cm3 until adepth 244 of between about 200 and about 250 Angstroms. In other embodiments, the p-type MDD regions 238 have a substantially constant boron concentration of greater than about 1×1020 atoms/cm3 until adepth 246 of between about 350 and about 400 Angstroms. Of course, the depths and dopant concentrations in the n-type and p-type MDD regions - In certain advantageous embodiments of the
transistor device 200, the n-type and p-type MDD regions type MDD regions 236 can be closer together than the two p-type MDD regions 238. As an example, the two n-type MDD regions 236 on either side of thefirst gate structure 232 are separated by adistance 248 that is about 20 percent closer than thedistance 250 separating the two p-type MDD regions 238 on either side of thesecond gate structure 234. Consequently, the p-channel region 250 between the n-type MDD regions 236 is between about 10 and about 50 nanometers wide, and an n-channel region 254 between the p-type MDD regions 238 is between about 10 and about 50 nanometers. - The
transistor devices 200 made be the processes of the present invention have an number of desirable electrical performance characteristics. As further illustrated in the example section to follow,NMOS transistor 228 of the present invention have favorable ratios of drain currents in the presence (Idsat) and absence (Idoff) of an applied gate voltage (Vg=1.1 V) and constant drain voltage (Vd=1.1 V). For instance, for Idsat values up to about 800 μA/μm, the ratio of Idoff:Idsat is greater than about −10,000:1. -
NMOS transistor 228 can also have favorable gate to drain capacitance (Cgd) for small gate lengths (L). For example, in some embodiments having gate lengths between about 17 and about 50 nanometers, Cgd is greater than about 0.27 fF/μm. These electrical properties are consistent with the production of p-type MDD region geometries according to the principles of the present invention as set forth above, and in example section to follow. -
FIG. 2B also depicts other conventionally formed device structures, includinggate sidewall spacers 256, 258, and shallow trench isolation structure 260, included in preferred embodiments to form anactive transistor device 200. It should be noted that while the metal levels and corresponding interconnects are not shown, those who are skilled in the art understand how to complete such devices. -
FIGS. 3A and 3B illustrate another aspect of the present invention, a method of manufacturing anintegrated circuit 300. Sectional views of selected steps, at various stages of manufacture are illustrated and analogous reference numbers are used to indicate like structures depicted inFIGS. 2A and 2B . Turning toFIG. 3A , illustrated is a partial completedintegrated circuit 300, after formingMOS transistor devices transistor devices FIGS. 1A-1H andFIGS. 2A-2B , can be used to form theMOS transistor devices - For instance, the gate structure includes an
NMOS gate structure 332 and aPMOS 334 gate structure. In such embodiments, implanting dopant includes implanting a second dopant, of opposite dopant type to the dopant adjacent theNMOS gate 332, subsequent to removing portions of theprotective oxide layer 312 as described above. In some advantageous configurations, the transistor device includes NMOS andPMOS transistors - Turning to
FIG. 3B , illustrated is theintegrated circuit 300 after interconnecting saidMOS transistor device interconnects 370 to form an operativeintegrated circuit 300. Certain preferred embodiments, of the method of manufacturing theintegrated circuit 300 further includes using conventional method to form interleveldielectric levels 380. - Although the present invention has been described in detail, one of ordinary skill in the art should understand that they can make various changes, substitutions and alterations herein without departing from the scope of the invention.
Claims (9)
1-8. (canceled)
9. A metal oxide semiconductor (MOS) transistor device, comprising:
a gate structure on a substrate;
an oxide layer on a sidewall of said gate structure and on a portion of said substrate adjacent said gate structure;
a protective oxide layer on said oxide layer; and
an oxide etch-resistant off-set spacer adjacent said sidewall and located on said protective oxide layer, an outer perimeter of said oxide layer and said protective oxide layer coextensive with an outer perimeter of said oxide etch-resistant off-set spacer.
10. The MOS transistor device recited in claim 9 , wherein a second outer perimeter of said oxide layer, said protective oxide layer and said oxide etch-resistant off-set spacer are coextensive with an outer perimeter of a ceiling of said gate structure.
11. The MOS transistor device recited in claim 9 , further including an NMOS and a PMOS transistor, wherein each of said NMOS and PMOS transistors include said gate structures, said oxide layer and said protective oxide layers, and said oxide etch-resistant off-set spacers.
12. The MOS transistor device recited in claim 11 , wherein said NMOS and a PMOS transistor further includes n-type and p-type MDD regions, respectively, wherein said n-type MDD regions have a depth that is between about 30 and about 50 percent shallower than a depth of said p-type MDD structure.
13. The MOS transistor device recited in claim 12 , wherein said n-type MDD regions have a substantially constant arsenic concentration of greater than about 1×1020 atoms/cm3 until a depth of between about 200 and about 250 Angstroms, and said p-type MDD regions have a substantially constant boron concentration of greater than about 1×1020 atoms/cm3 until a depth of between about 350 and about 400 Angstroms.
14. The MOS transistor device recited in claim 12 , wherein a p-channel region between said n-type MDD regions is between about 10 and about 50 nanometers, and an n-channel region between said p-type MDD regions is between about 10 and about 50 nanometers.
15. The MOS transistor device recited in claim 11 , wherein said NMOS transistor has a Idoff:Idsat ratio of greater than about −10,000:1, when said Idsat is about 800 μA/μm or less and a Cgd of greater than about 0.27 fF/μm when said first gate structure has a length between about 17 and about 50 nanometers.
16-20. (canceled)