US20020058182A1 - Electrode and battery using the same - Google Patents
Electrode and battery using the same Download PDFInfo
- Publication number
- US20020058182A1 US20020058182A1 US10/029,955 US2995501A US2002058182A1 US 20020058182 A1 US20020058182 A1 US 20020058182A1 US 2995501 A US2995501 A US 2995501A US 2002058182 A1 US2002058182 A1 US 2002058182A1
- Authority
- US
- United States
- Prior art keywords
- electrode
- active material
- temperature
- electronic conducting
- rise
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
An electrode in which an active material 11 or 7, an electron conducting material 12 or a current collector 5 or 6 has PTC characteristics is used as at least one of positive and negative electrodes 1 and 2.
Description
- 1. Field of the Invention
- This invention relates to an electrode to be used in a battery and to a battery using the same. In particular, it relates to a lithium ion secondary battery with improved safety.
- 2. Description of the Related Art
- With the recent improvement of performance of electronic equipment, there has been a demand for improvement on batteries for use as a power source of the electronic equipment, especially rechargeable secondary batteries. Lithium ion secondary batteries have been attracting attention for their light weight, portability, and high capacity. Lithium ion secondary batteries, while advantageous for their high energy density, require sufficient safety measures because they use metallic lithium and a nonaqueous electrolytic solution.
- A safety valve for escape of increased inner pressure and a PTC (positive temperature coefficient) element which increases resistance according to heat generation caused by an external short-circuit to cut off an electric current have been proposed to date as safety measures.
- For example, JP-A-4-328278 (the term “JP-A” as used herein means an “unexamined published Japanese patent application”) proposes a cylindrical battery having a safety valve and a PTC element in the positive electrode cap. However, it is a generally followed practice that a safety valve is designed not to work so easily because, on the safety valve's working, moisture in the air tends to enter the battery and react with lithium present in the negative electrode.
- A PTC element, on the other hand, cuts off the circuit in case of an external short-circuit and causes no adverse influence. It could be the first safety component to work in case of abnormality by designing to work when the inner temperature reaches, for example, 120° C. due to a short-circuit.
- Problem to be Solved by the Invention
- When a short-circuit occurs in the inside of a battery, the cutoff of the external circuit by a PTC element does not mean a cutoff of a short-circuit inside the battery. If a short-circuit occurs in the battery and the inner temperature rises, the separator made of polyethylene, polypropylene, etc. which is interposed between a positive electrode and a negative electrode is expected to melt by the heat. The molten separator is expected to exude or enclose the nonaqueous electrolytic solution that has been held in the separator so that the ion conducting properties of the separator may be reduced to weaken the short-circuit current. However, a separator away from the heat generating part does not always melt.
- In an attempt to solve the above problem, JP-A-7-161389 proposes using an active material having PTC characteristics in itself in the positive electrode. However, since the resistance of a positive electrode active material having PTC characteristics is about 10−5 S/cm at a working temperature (room temperature), the battery will not function unless such a positive electrode active material is used in combination with an electrical conduction aid as demonstrated in Examples of the publication. With a conduction aid having no PTC behavior being added, even though a positive electrode active material exhibits PTC characteristics, a short-circuit current is to flow via the conduction aid.
- An object of the present invention is to settle the above-mentioned problems and to provide a highly safe lithium ion secondary battery which controls heat generation in case of an external and/or internal short-circuit.
- A first aspect of the electrode of the present invention is an electrode which comprises:
- an electrode active material layer containing an active material;
- and an electronic conducting current collector on which the electrode active material layer are formed wherein said electrode active material layer has the property of increasing its resistance with a rise in temperature (PTC).
- A second aspect of the electrode of the present invention according to the first aspect is an electrode wherein said active material has the property of increasing its resistance with a rise in temperature (PTC).
- A third aspect of the electrode of the present invention according to the first aspect is an electrode wherein said electrode active material layer comprises an active material particle and an electronic conducting material, and the electronic conducting material has the property of increasing its resistance with a rise in temperature (PTC).
- A fourth aspect of the electrode of the present invention according to the first aspect is an electrode wherein said electrode active material layer is composed of an active region having an electrode activity and a non-active region having no electrode activity by which said active region is isolated into a plurality of parts, and said non active region has the property of increasing resistance with a rise in temperature.
- A fifth aspect of the electrode or the present invention according to the first aspect is an electrode wherein said electrode active material layer is composed of an active region having an electrode activity and a non-active region having no electrode activity by which said active region is isolated into a plurality of parts, and said active region has the property of increasing resistance with a rise in temperature.
- A sixth aspect of the electrode of the present invention according to the first aspect is an electrode wherein said active material is made up of secondary particles comprising a plurality of active material particles having adhered on the surface thereof electronic conducting particles having the property of increasing resistance with a rise in temperature.
- A eighth aspect of the electrode of the present invention according to the first aspect is an electrode wherein said electronic conducting current collector has the property of increasing its resistance with a rise in temperature (PTC).
- A eighth aspect of the electrode of the present invention according to the eighth aspect is an electrode, wherein said electronic conducting current collector is composed of conductive plate to which an electronic conducting material having the property of increasing resistance with a rise in temperature is bonded.
- A ninth aspect of the electrode of the present invention according to the sixth aspect is an electrode, wherein said electronic conducting material is a polymer having a softening point not higher than 150° C.
- A tenth aspect of the battery of the present invention in a battery which comprises: a positive electrode; a negative electrode; and an electrolysis held between said positive electrode and said negative electrode, wherein at least one of the positive electrode and negative electrode comprises an electrode active material layer containing an active material and an electronic conducting current collector on which the electrode active material layer are formed, and said electrode active material layer has the property of increasing its resistance with a rise in temperature (PTC).
- A eleventh aspect of the battery of the present invention according to the tenth aspect is a battery, wherein said electrode active material layer is composed of an active region having an electrode activity and a non-active region having no electrode activity by which said active region is isolated into a plurality of parts, and said non active region has the property of increasing resistance with a rise in temperature.
- A twelfth aspect of the battery of the present invention according to the tenth aspect is a battery, wherein said electrode active material layer is composed of an active region having an electrode activity and a non-active region having no electrode activity by which said active region is isolated into a plurality of parts, and said active region has the property of increasing resistance with a rise in temperature.
- A thirteenth aspect of the battery of the present invention according to the tenth aspect is a battery, wherein said active material is made up of secondary particles comprising a plurality of active material particles having adhered on the surface thereof electronic conducting particles having the property of increasing resistance with a rise in temperature.
- A fourteenth aspect of the battery of the present invention according to the tenth aspect is a battery, wherein said electronic conducting current collector has the property of increasing its resistance with a rise in temperature (PTC).
- A fifteenth aspect of the battery of the present invention according to the fourteenth aspect is a battery, wherein said electronic conducting current collector is composed of metal to which an electronic conducting material having the property of increasing resistance with a rise in temperature is bonded.
- A sixteenth aspect of the battery of the present invention according to the thirteenth aspect is a battery, wherein said electronic conducting material is a polymer having a softening point not higher than 150° C.
- A seventeenth aspect of the battery of the present invention is a battery which comprises:
- an electrode active material layer containing an active material;
- and an electronic conducting current collector on which the electrode active material layer are formed,
- wherein said electronic conducting current collector has the property of increasing its resistance with a rise in temperature (PTC) electrode active material layer and
- said electrode active material layer is made of an plurality of parts electrical isolated each other.
- A eighteenth aspect of the battery of the present invention according to the seventeenth aspect is a battery, wherein said electronic conducting current collector is made of a conductive plate to which an electronic conducting material has the property of increasing its resistance with a rise in temperature (PTC) is bonded.
- A ninteenth aspect of the battery of the present invention is a battery which comprises: a positive electrode; a negative electrode; and an electrolysis held between said positive electrode and said negative electrode,
- wherein at least one of the positive electrode and negative electrode comprises an electrode active material layer made of an plurality of parts electrical isolated each other and an electronic conducting current collector on which the electrode active material layer are formed,
- and said electronic conducting current collector has the property of increasing its resistance with a rise in temperature (PTC).
- FIG. 1 is a schematic cross section of the main part of an example of the lithium ion secondary battery according to the present invention.
- FIG. 2 is a schematic cross section of the same battery as shown FIG. 1, in which the behavior of the positive electrode in case of an internal short-circuit is illustrated.
- FIG. 3 shows changes in battery voltage and temperature with time in a simulation of a short-circuit in the lithium ion secondary battery according to the present invention.
- FIG. 4 shows a schematic cross section of the electrode of the third embodiment of the present invention.
- FIG. 5 shows a schematic cross section of the conventional electrode in comparison with the FIG. 4.
- The embodiments for carrying out the present invention are described below with reference to the accompanying drawings.
- FIG. 1 is a schematic cross section of the main part of an embodiment of the lithium ion secondary battery according to the present invention. In FIG. 1
numeral 1 indicates a positive electrode comprising a positive electrodecurrent collector 5 having formed thereon a positive active material layer made up of a positive electrodeactive material 11, an electronic conductingmaterial 12 that is in contact with theactive material 11, and abinder 14.Numeral 2 is a negative electrode comprising a negative electrodecurrent collector 6 having formed thereon a negative electrode active material layer made up of a negativeactive material 7, such as carbon particles, and a binder.Numeral 3 indicates a separator holding an electrolytic solution containing lithium ions. - The electrode according to the present invention having the above-described structure is characterized in that the positive electrode
active material 11, the positive electrodecurrent collector 6 or the electronic conductingmaterial 12 in contact with the positive electrodeactive material 11 has PTC characteristics (the property of increasing electrical resistance with a rise in temperature). - While FIG. 1 is to illustrate the structure of the
positive electrode 1, the same structure also applies to thenegative electrode 2. In that case, a particulate negative electrodeactive material 7 and an electronic conducting material in contact with theactive material 7 are formed into a negative electrode by means of a binder, and thenegative electrode material 7, the electronic conducting material or thecurrent collector 6 has PTC characteristics. - FIG. 2 is a schematic cross section of the same battery as shown in FIG. 1, in which the behavior of the positive electrode in case of an internal short-circuit is illustrated. When an internal short-circuit taken place due to, for example, a
mediator 4, for example, dendrite shape of metallic lithium grown from thenegative electrode 2 as shown in FIG. 2, short-circuit currents circuit currents circuit currents - According to the present invention, since the positive electrode
active material 11, theelectronic conducting material 12 or theelectronic conducting material 13 constituting the positive electrodecurrent collector 5 has PTC characteristics, the short-circuit current 51 is decayed with the rise in temperature caused by the short-circuit. - In a battery, a voltage loss due to internal resistance is about 1 to 5% of the battery voltage at a generally employed current. Supposing the total voltage is applied to the internal resistant portion, if a short-circuit takes place, the short-circuit current would be 20 to 100 times the ordinary current. Therefore, it is expected that a short-circuit current would be reduced down to a normal level or even less if the internal resistance at the short-circuited part could be increased 100 times or more by a PTC function.
- The possibility of thermal runaway, while varying depending on the materials making up a battery, seems to increase after the battery temperature exceeds 150° C. Therefore, it is desirable that the PTC function works at a temperature of 150° C. so as to inhibit thermal runaway. Taking the time lag between the start and the completion of the PTC function into consideration, it is desirable for the PTC function to work from 120° C.
- In FIG. 1, at least one of the
current collectors active materials electronic conducting material 12 must be endowed with PTC characteristics. - Because a short-circuit current has its rise in the
active materials negative electrodes active material active material - The “resistance to reaction” of an electrode active material is considered to be the sum of resistance to electronic conduction and ionic conduction in the inside of the
active material active material active materials 11 have high resistance to electronic conduction originally so that the resistance to ionic conduction in the inside of theactive material 11 and the resistance to charge transfer on the surface of theactive material 11 usually takes the main part of resistance to reaction. In one feature of the present invention, the resistance to reaction has PTC behavior. More specifically, electronic conducting particles having PTC characteristics are adhered to the surface of the active material particles to form secondary particles of theactive material - It is also effective that the electronic conducting material has PTC characteristics. Since the positive electrode
active material 11 usually has in itself low electron conductivity, theelectronic conducting material 12 is incorporated to form thepositive electrode 1 in which theactive material 11 and theelectronic conducting material 12 are brought into contact. Use of an electronic conducting material having PTC characteristics enables the electrode to decay the short-circuit current. - In order for the positive electrode
current collector 5 to have PTC characteristics, thecurrent collector 5 can be made up ofmetal 15 to which theelectronic conducting material 13 having PTC characteristics is contacted as shown in FIG. 1. The negative electrodecurrent collector 6 can also be made to have PTC characteristics in the same manner. - Where only the
current collectors active material binder 14 have good electron conductivity in the lateral direction, cases are sometimes met with in which the active material layers become bypass for letting the short-circuit current to flow, failing to sufficiently decaying the short-circuit current, even when thecurrent collectors active material layer 20 into plural of active material regions byelectron insulator 21. - According to the feature, the
electron insulator 21 prevents the short-circuit current from bypassing. And the short-circuit current is cut early by means of the PTC function of thePTC layer 22 formed on theconductive layer 22 such as a metal plate or carbon plate. Therefore energy discharge owing to short-circuit is kept low, and safety of the secondary battery is kept. - With respect to isolation region, such as electron insulating material, by which active material regions are isolated, any size, any pitch and any kindness of electron insulating material are effective without being limited. As the electron insulating material, any material has electron insulating characteristic under the circumference in which the electrode is used, for example in the electrode for a litium ion secondary battery, electron insulating material used as other element of the battery, can be used. The size of the isolation region is desirably small in a range wherein a function of preventing a short-circuit current from bypassing can be kept. And pitch is desirably large with respect to acting as the real function of the electrode.
- In contradiction that, as shown in FIG. 5 in the case of conventional electrode in which only the current collectors is made to have PTC characteristics, and the active material layers20 formed on a whole surface of
PTC layer 22 on theconductive layer 23, the active material layers 20 has a good electron conductivity in the lateral direction, the short-circuit current is continued flowing by bypassing the cutting zone formed by the PTC function. And by continuing flowing a range of heated zone is expanded, the short-circuit current is continued flowing by further bypassing. Therefore in the case of a battery, large amount of energy is discharged. - Accordingly in such a case, it is required to previously limit the electron conductivity of the active material layers in their lateral direction by, for example, dividing the active material layers.
- Materials having no PTC characteristics are used as an active material which forms the active material particles per se or the aforesaid secondary particles. Examples of useful positive electrode active materials are LiCoO2, LiNiO2, LiCo1−xNixO2, and LiMn2O4. Examples of useful negative electrode active materials are carbon particles, such as mesophase carbon microbeads (MCMB), graphite, and acetylene black.
- Specific but non-limiting examples of useful electronic conducting materials or electronic conducting particles having PTC characteristics include barium titanate, barium titanate doped with Sr, Pb, etc. (complex oxides), and electrically conductive polymers, such as polyethylene mixed with carbon black.
- The PTC function of the conductive polymer is controlled by the mixing ratio of a plastic and an electrically conducting material, such as carbon black. When the conductive polymer is used, the plastic malts by the heat of the short-circuit to cut off both the electron conducting path and the ion conducting path in the active material comprising the secondary particles, thereby to enhance the resistance to electronic conduction. When the conductive polymer is applied to the
electronic conducting material - The present invention will now be illustrated in greater detail by way of Examples of the lithium ion secondary battery shown in FIG. 1.
-
EMBODIMENT 1 - Preparation of Positive Electrode
- Ten parts of fine particles (average particle size: 10 μm) of an electronic conducting material having an electrical conductivity of 5 S/cm at room temperature and 5 μS/cm at a working temperature of 120° C. (selected from barium titanate, Sr-doped barium titanate, Pb-doped barium titanate, and a graphite/polyethylene mixture), 85 parts by weight of LiCoO2 as an active material, and 5 parts by weight of polyvinylidene fluoride (hereinafter abbreviated as PVDF) were dispersed in N-methylpyrrolidone (hereinafter abbreviated as NMP ) to prepare a positive electrode active material paste. The paste was applied to 20 μm thick aluminum foil as a positive electrode current collector with a doctor blade to a thickness of 150 μm, dried at 80° C., and pressed prepare a
positive electrode 1 having a positive electrodeactive material layer 3 having a thickness of 100 μm. - Preparation of Negative Electrode
- Ninety-five parts by weight of mesophase carbon microbeads (hereinafter abbreviated as MCHB) and 5 parts by weight of PVDF were dispersed in NMP to prepare a negative electrode active material paste. The paste was applied to 20 μm thick copper foil with a doctor blade to a thickness of 300 μm, dried at 80° C., and pressed to form a
negative electrode 4 having a negative electrodeactive material layer 6 having a thickness of 100 μm. - Preparation of Battery
- A 5 parts by weight of PVDF solution in NMP was applied to both sides of a porous polypropylene sheet (Cellguard #2400, produced by Hoechst Celanese Plastics Ltd.) as a
separator 7. Before the adhesive dried, thepositive electrode 1 and thenegative electrode 4 were stuck to each aide of theseparator 7, followed by drying at 80° C. to prepare an electrode laminate. - Ten electrode laminates were laid one on another, and current collecting tabs each connected to the end of every positive or negative current collector were spot-welded among the positive electrode laminates and the negative electrode laminates, respectively, to form a single battery body in which the positive electrodes and the negative electrodes were each connected in parallel.
- The battery body was immersed in an electrolytic solution consisting of 1.0 mol/dm3 of lithium hexafluorophosphate in a 1:1 (by mole) mixed solvent of ethylene carbonate and dimethyl carbonate, and the impregnated battery body was sealed into an aluminum laminate film (resin coated aluminum film) pack by heat sealing to complete a battery.
- The resulting battery was charged at 500 mA to 4.2 V at an ambient temperature of 25° C. After completion of the charge, an iron nail having a diameter of 2.5 mm was put in the center of the battery to run a simulation of an internal short-circuit. FIG. 3 shows the changes in battery voltage and temperature with time. As shown, in the instant the iron nail was put in (time0), the terminal voltage fell to 0 V but was gradually restored with time, which seemed to be because heat was generated at the short-circuited part immediately after the short-circuit whereby the electronic conducting particles having PTC characteristics in the vicinities of the short-circuited part functioned to decay the short-circuit current. The battery temperature started rising after the short-circuit, reaching the peak in about 5 minutes. Then it gradually dropped to room temperature. This shift of the peak of temperature is considered due to the time required for heat conduction because of the positional difference of the measuring point from the heat generating point (the short-circuited part).
- For comparison, a battery having no PTC function was produced in the same manner as described above, except for using artificial graphite (KS-6, produced by Lonza Ltd.) as electronic conducting particles. As a result of the same simulation of a short-circuit, the peak temperature exceeded 150° C., and restoration of the battery voltage was not observed.
-
EMBODIMENT 2 - Preparation of Positive Electrode
- LiCoO2 particles having an average particle size of 1 μm were made into secondary particles having an average particle size of 50 μm while powdering with high-density polyethylene having a softening point of 120° C. Eighty-five parts by weight of the resulting secondary particles, 10 parts by weight of artificial graphite (KS-6, produced by Lonza Ltd.) as electronic conducting particles, and 5 parts by weight of PVDF as a binder were dispersed in NMP to prepare a positive electrode active material paste. The paste was applied to 20 μm thick aluminum foil as a positive electrode
current collector 2 with a doctor blade to a thickness of 150 μm, dried at 80° C., and pressed to prepare apositive electrode 1 having a positive electrodeactive material layer 3 having a thickness of 100 μm. - Preparation of Negative Electrode
- Ninety-five parts by weight of MCMB and 5 parts by weight of PVDF were dispersed in NMP to prepare a negative electrode active material paste. The paste was applied to 20 μm thick copper foil with a doctor blade to a thickness of 150 μm, dried at 80° C., and pressed to form a
negative electrode 4 having a negative electrodeactive material layer 6 having a thickness of 100 μm. - Preparation of Battery
- A 5 parts by weight of PVDF solution in NMP was applied to both sides of a porous polypropylene sheet (Cellguard #2400, produced by Hoechst Celanese Plastics Ltd.) as a
separator 7. Before the adhesive dried, thepositive electrode 1 and thenegative electrode 4 were stuck to each side of theseparator 7, followed by drying at 80° C. to prepare an electrode laminate. - Ten electrode laminates were laid one on another, and current collecting tabs each connected to the end of every positive and negative current collector were spot-welded among the positive electrode laminates and the negative electrode laminates, respectively, to form a single battery body in which the positive electrode laminates and the negative electrode laminates were each connected in parallel.
- The battery body was immersed in an electrolytic solution consisting of 1.0 mol/dm3 of lithium hexafluorophosphate in a 1:1 (by mole) mixed solvent of ethylene carbonate and dimethyl carbonate, and the impregnated battery body was sealed into an aluminum laminate film pack by heat sealing to complete a battery.
- The resulting battery was charged at 500 mA to 4.2 V at an ambient temperature of 25° C. After completion of the charge, an iron nail having a diameter of 2.5 mm was put in the center of the battery to run a simulation of an internal short-circuit. Similarly to the behavior shown in FIG. 3, in the instant the iron nail was put in (time0), the terminal voltage fell to 0 V but was gradually restored with time. The voltage restoration seems to be because heat was generated at the short-circuited part immediately after the short-circuit whereby the high-density polyethylene clinging to the active material particles in the vicinities of the short-circuited part was softened and expanded to cut the electronic conducting path to the active material to thereby decay the short-circuit current.
-
EMBODIMENT 3 - Preparation of Positive Electrode
- Eighty-five parts by weight of LiCoO2 having an average particle size of 1 μm, 10 parts by weight of artificial graphite (KS-6, produced by Lonza Ltd.) as electronic conducting particles, and 5 parts by weight of PVDF as a binder were dispersed in NMP to prepare a positive electrode active material paste.
- Separately, a 50 μm thick sheet of an electrically conductive polymer consisting of 30% polyethylene and 70% carbon black and having an electrical conductivity of 5 S/cm at room temperature and 5 μS/cm at a working temperature of 120° C. was stuck to a 20 μm thick aluminum net to prepare a positive electrode
current collector 2. The positive electrode active material paste prepared above was applied to thecurrent collector 2 through a mask having slits at an opening ratio of 70% by means of a doctor blade to a thickness of 150 μm, dried at 80° C. so that the positive electrode active material layer made of an plurality of parts electrical isolated each other (referring to the FIG. 4), and proceed to prepare apositive electrode 1 having a positive electrodeactive material layer 3 having a thickness of 100 μm. - Preparation of Negative Electrode
- Ninety-five parts by weight of MCMB and 5 parts by weight of PVDF as a binder were dispersed in NMP to prepare a negative electrode active material paste. The paste was applied to 20 μm thick copper foil with a doctor blade to a thickness of 150 μm, dried at 80° C., and pressed to form a
negative electrode 4 having a negative electrodeactive material layer 6 having a thickness of 100 μm. - Preparation of Battery
- A 5 parts by weight of PVDF solution in NMP was applied to both sides of a porous polypropylene sheet (Cellguard #2400, produced by Hoechst Celanese Plastics Ltd.) as a
separator 7. Before the adhesive dried, thepositive electrode 1 and thenegative electrode 4 were stuck to each side of theseparator 7, followed by drying at 80° C. to prepare an electrode laminate. - Ten electrode laminates were laid one on another, and current collecting tabs each connected to the end of every positive or negative current collector were spot-welded among the positive electrode laminates and the negative electrode laminates, respectively, to form a single battery body in which the positive electrode laminates and the negative electrode laminates were each connected in parallel.
- The battery body was immersed in an electrolytic solution consisting of 1.0 mol/dm3 of lithium hexluorophosphate in a 1:1 (by mole) mixed solvent of ethylene carbonate and dimethyl carbonate, and the impregnated battery body was sealed into an aluminum laminate film pack by heat sealing to complete a battery.
- The resulting battery was charged at 500 mA to 4.2 V at an ambient temperature of 25° C. After completion of the charge, an iron nail having a diameter of 2.5 mm was put in the center of the battery to run a simulation of an internal short-circuit. As a result, the same changes in battery temperature and voltage as in FIG. 3 were observed. That is, in the instant the iron nail was put in (time0), the terminal voltage fell to 0 V but was gradually restored with time. The voltage restoration seems to be because heat was generated at the short-circuited part immediately after the short-circuit whereby the electrically conductive polymer having PTC characteristics in the vicinities of the short-circuited part functioned to cut off the electronic conducting path to the active material to thereby decay the short-circuit current.
-
EMBODIMENT 4 - Preparation of Positive Electrode
- Eighty-five parts by weight of LiCoO2 particles having an average particle size of 1 μm, 10 parts by weight of artificial graphite (KS-6, produced by Lonza Ltd.) as electronic conducting particles, and 5 parts by weight of PVDF as a binder were dispersed in NMP to prepare a positive electrode active material paste. The paste was applied to 20 μm thick aluminum foil as a positive electrode
current collector 2 with a doctor blade to a thickness of 150 μm, dried at 80° C., and pressed to prepare apositive electrode 1 having a positive electrodeactive material layer 3 having a thickness of 100 μm. - Preparation of Negative Electrode
- MCMB was powdered with high-density polyethylene having a softening point of 120° C. into particles having an average particle size of 50 μm. Ninety-five parts by weight of the resulting particles and 5 parts by weight of PVDF were dispersed in NMP to prepare a negative electrode active material paste. The paste was applied to 20 μm thick copper foil with a doctor blade to a thickness of 150 μm, dried at 80° C., and pressed to form a
negative electrode 4 having a negative electrodeactive material layer 6 having a thickness of 100 μm. - Preparation of Battery
- A 5 parts by weight of PVDF solution in NMP was applied to both sides of a porous polypropylene sheet (Cellguard #2400, produced by Hoechst Celanese Plastics Ltd.) as a
separator 7. Before the adhesive dried, thepositive electrode 1 and thenegative electrode 4 were stuck to eaeh side of theseparator 7, followed by drying at 80° C. to prepare an electrode laminate. - Ten electrode laminates were laid one on another, and current collecting tabs each connected to the end of every positive or negative current collector wore spot-welded among the positive electrode laminates and the negative electrode laminates, respectively, to form a single battery body in which the positive electrode laminates and the negative electrode laminates were each connected in parallel.
- The battery body was immersed in an electrolytic solution consisting of 1.0 mol/dm3 of lithium hexafluorophosphate in a 1:1 (by mole) mixed solvent of ethylene carbonate and dimethyl carbonate, and the impregnated battery body was sealed into an aluminum laminate film pack by heat sealing to complete a battery.
- The resulting battery was charged at 500 am to 4.2 V at an ambient temperature of 25° C. After completion of the charge, an iron nail having a diameter of 2.5 mm was put in the center of the battery to run a simulation of an internal short-circuit. As a result, the same changes in battery temperature and voltage as in FIG. 3 were observed. That is, in the instant the iron nail was put in (time0), the terminal voltage fell to 0 V but was gradually restored with time. The voltage restoration seems to be because heat was generated at the short-circuited part immediately after the short-circuit whereby the electrically conductive polymer having PTC characteristics in the vicinities of the short-circuited part functioned to cut off the electronic conducting path to the active material to thereby decay the short-circuit current.
- The present invention is applicable to the electrode for Electrolysis apparatus, the electrode for electro-plating the electrode for liquid crystal display and so on.
- As described above, the electrode according to the present invention comprises an active material, an electronic conducting material in contact with the active material, and an electronic conducting current collector to which the active material and the electronic conducting material are bonded with a binder, in which the active material, electronic conducting material or electronic conducting current collector has the property of increasing its resistance with a rise in temperature. Accordingly, in case of an internal short-circuit, the PTC function of the active material, the electronic conducting material or the electronic conducting material constituting the current collector which is in the path of the short-circuit current works to decay the short-circuit current thereby suppressing a rise in temperature. In the case that only electronic conducting current collector has the property of increasing its resistance with a rise in temperature, it is required that electrode active material layer is made of an plurality of parts electrical isolated each other for improving a safety.
- Where the active material is composed of a part having an electrode activity and a part having no electron activity, with the part having no electron activity exhibiting the property of increasing its resistance with a rise in temperature, the resistance to reaction of the active material increases at the time of a short-circuit to control the rise in temperature.
- Where the active material is made up of secondary particles compiling a plurality of active material particles to which electronic conducting particles having the property of increasing the resistance with a rise in temperature are clinging, the resistance to reaction of the active material increases at the time of a short-circuit to control the rise in temperature.
- The electronic conducting current collector can be endowed with PTC characteristics by the structure composed of metal to which an electronic conducting material having the property of increasing its resistance with a rise in temperature is joined.
- Where the electronic conducting material is a polymer having a softening point lower than 150° C., the polymer melts by the heat of a short-circuit. Where the polymer is applied to the active material, the melt cuts both the electron conducting path and the ion conducting path to increase the resistance to electron conduction. Where the polymer is applied to the electron conducting material, the melt cuts the electron conducting path.
- The battery according to the present invention comprises a positive electrode, a negative electrode, and an electrolytic solution held between the positive and negative electrodes, in which the above-described electrode endowed with PTC characteristics is used as a positive or negative electrode. The battery is of high safety because the temperature rise in case of an internal short-circuit can be suppressed.
Claims (19)
1. An electrode comprising:
an electrode active material layer containing an active material;
and an electronic conducting current collector on which the electrode active material layer are formed wherein said electrode active material layer has the property of increasing its resistance with a rise in temperature (PTC).
2. The electrode according to claim 1 , wherein said active material has the property of increasing its resistance with a rise in temperature (PTC).
3. The electrode according to claim 1 , wherein said electrode active material layer comprises an active material particle and an electronic conducting material, and the electronic conducting material has the property of increasing its resistance with a rise in temperature (PTC).
4. The electrode according to claim 1 , wherein said electrode active material layer is composed of an active region having an electrode activity and a non-active region having no electrode activity by which said active region is isolated into a plurality of parts, and said non active region has the property of increasing resistance with a rise in temperature.
5. The electrode according to claim 1 , wherein said electrode active material layer is composed of an active region having an electrode activity and a non-active region having no electrode activity by which said active region is isolated into a plurality of parts, and said active region has the property of increasing resistance with a rise in temperature.
6. The electrode according to claim 1 , wherein said active material is made up of secondary particles comprising a plurality of active material particles having adhered on the surface thereof electronic conducting particles having the property of increasing resistance with a rise in temperature.
7. The electrode according to claim 1 , wherein said electronic conducting current collector has the property of increasing its resistance with a rise in temperature (PTC).
8. The electrode according to claim 7 , wherein said electronic conducting current collector is composed of conductive plate to which an electronic conducting material having the property of increasing resistance with a rise in temperature is bonded.
9. The electrode according to claim 6 , wherein said electronic conducting material is a polymer having a softening point not higher than 150° C.
10. A battery comprising: a positive electrode; a negative electrode; and an electrolysis held between said positive electrode and said negative electrode, wherein at least one of the positive electrode and negative electrode comprises an electrode active material layer containing an active material and an electronic conducting current collector on which the electrode active material layer are formed, and said electrode active material layer has the property of increasing its resistance with a rise in temperature (PTC).
11. The battery according to claim 10 , wherein said electrode active material layer is composed of an active region having an electrode activity and a non-active region having no electrode activity by which said active region is isolated into a plurality of parts, and said non active region has the property of increasing resistance with a rise in temperature.
12. The battery according to claim 10 , wherein said electrode active material layer is composed of an active region having an electrode activity and a non-active region having no electrode activity by which said active region is isolated into a plurality of parts, and said active region has the property of increasing resistance with a rise in temperature.
13. The battery according to claim 10 , wherein said active material in made up of secondary particles comprising a plurality of active material particles having adhered on the surface thereof electronic conducting particles having the property of increasing resistance with a rise in temperature.
14. The battery according to claim 10 , wherein said electronic conducting current collector has the property of increasing its resistance with a rise in temperature (PTC).
15. The battery according to claim 14 , wherein said electronic conducting current collector is composed of metal to which an electronic conducting material having the property of increasing resistance with a rise in temperature is bonded.
16. The electrode according to claim 13 , wherein said electronic conducting material is a polymer having a softening point not higher than 150° C.
17. An electrode comprising:
an electrode active material layer containing an active material;
and an electronic conducting current collector on which the electrode active material layer are formed,
wherein said electronic conducting current collector has the property of increasing its resistance with a rise in temperature (PTC) electrode active material layer and
said electrode active material layer is made of an plurality of parts electrical isolated each other.
18. The electrode according to claim 17 , wherein said electronic conducting current collector is made of a conductive plate to which an electronic conducting material has the property of increasing its resistance with a rise in temperature (PTC) is bonded.
19. A battery comprising: a positive electrode; a negative electrode; and an electrolysis held between said positive electrode and said negative electrode,
wherein at least one of the positive electrode and negative electrode comprises an electrode active material layer made of an plurality of parts electrical isolated each other and an electronic conducting current collector on which the electrode active material layer are formed,
and said electronic conducting current collector has the property of increasing its resistance with a rise in temperature (PTC).