US20020052423A1 - Skeletal iron catalyst having improved attrition resistance and product selectivity in slurry-phase synthesis processes - Google Patents
Skeletal iron catalyst having improved attrition resistance and product selectivity in slurry-phase synthesis processes Download PDFInfo
- Publication number
- US20020052423A1 US20020052423A1 US09/895,621 US89562101A US2002052423A1 US 20020052423 A1 US20020052423 A1 US 20020052423A1 US 89562101 A US89562101 A US 89562101A US 2002052423 A1 US2002052423 A1 US 2002052423A1
- Authority
- US
- United States
- Prior art keywords
- iron
- catalyst
- skeletal
- particles
- iron alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Particulate skeletal iron catalyst is provided which contain at least about 50 wt. % iron with the remainder being a minor portion of a suitable non-ferrous metal and having characteristics of 0.062-1.0 mm particle size (62-1000 micron), 20-100 m2/g surface area, and 10-40 nm average pore diameter. Such skeletal iron catalysts are prepared and utilized for producing synthetic hydrocarbon products from CO and H2 feeds by Fischer-Tropsch synthesis process. Iron powder is mixed with non-ferrous metal powder selected from aluminum, antimony, silicon, tin or zinc powder to provide 20-80 wt. % initial iron content and melted together to form an iron alloy, then cooled to room temperature and pulverized to provide 0.1-10 mm iron alloy catalyst precursor particles. The iron alloy precursor particles are treated with NaOH or KOH caustic solution at 30-95° C. temperature to extract and/or leach out most of the non-ferrous metal portion, and then screened and treated by drying and reducing with hydrogen so as to provide smaller sized skeletal iron catalyst material. Such skeletal iron catalyst is utilized with CO+H2 feedstream for Fischer-Tropsch reactions in either a fixed bed or slurry bed type reactor at 180-500° C. temperature, 0.5-5.0 mPa pressure, and gas hourly space velocity of 0.5-3.0 L/g Fe/hr to produce desired hydrocarbon products.
Description
- This invention pertains to skeletal iron catalyst and its preparation and use in Fischer-Tropsch and similar slurry-phase synthesis processes. More particularly, such skeletal iron catalyst utilized in slurry phase synthesis processes for H2+CO feedstreams has increased attrition resistance and improved catalyst/product liquid separation, while providing increased selectivity for producing C2-C5 light olefin products.
- Slurry phase Fischer-Tropsch (F-T) synthesis process technology is an important known route for indirect coal liquefaction for synthesis of liquid fuels from H2+CO feedstreams. Precipitated iron is currently a commonly used catalyst for such Fischer-Tropsch processes. However, precipitated iron catalysts are undesirably fragile and break down easily under reaction conditions into very fine particles, so that separation of such fine catalyst particles from reaction product waxes is difficult to accomplish and results in inferior product quality and significant catalyst loss. Such catalyst problems hinders commercial use of the process.
- For overcoming this problem, improved skeletal iron catalysts made according to this invention are provided by utilizing caustic extraction and/or leaching non-ferrous metals from specific iron metal alloy particles, and such skeletal iron catalysts have good particle strength and attrition resistance. Literature studies on such catalysts to date have focused on improvement of catalyst activity in simple gas-solid hydrogenation reaction systems. Utilization of such improved skeletal iron catalyst in slurry-phase or three-phase gas-liquid-solid Fischer-Tropsch reaction processes fully realizes the advantages of such skeletal iron catalysts. By utilizing such improved skeletal iron catalysts, commercial slurry-bed Fischer-Tropsch synthesis processes to produce clean hydrocarbon liquid transportation fuels from syngas feedstreams is greatly facilitated.
- Light olefins C2− to C5− are key component materials in the petrochemical industry as important feedstocks and building blocks for the synthesis of a variety of chemical/petrochemical products. Conventionally, such light olefins are produced by thermal cracking of hydrocarbons ranging from ethane to vacuum gas oils, but not produced directly from natural gas which is essentially methane (CH4). Such thermal cracking is practiced under high temperatures (1,500-1,600° F.), thus requiring costly construction materials and consuming huge amounts of energy for feedstream heating and reaction. A commercially practiced technical route for making light olefins from natural gas is to first convert natural gas via steam reforming into a mixture of hydrogen and carbon monoxide, called synthesis gas or syngas. The current technology of converting syngas into olefins is a two-step catalytic conversion, the first step being catalytic conversion of syngas to methanol, followed by conversion of methanol into olefins. A unique catalyst/technology would be to directly convert synthesis gas into light olefins, without the necessity of an additional step for making methanol as an intermediate material. The skeletal iron catalyst, promoted with other metal ingredients and used in a fixed bed or in slurry-bed reactor system with liquid paraffin as the liquid medium, can advantageously convert syngas directly into light olefins C2-C5 under mild conditions in a temperature range of 180-500° C. and a pressure range of 0.5-5.0 mPa.
- Thus, this invention provides a unique skeletal iron catalyst having high activity for catalyzing the conversion of syngas feeds to a broad range of hydrocarbon products, and has high selectivity towards light olefins formation in a slurry-phase catalytic reactor system under mild conditions conventionally used in Fischer-Tropsch synthesis, so that the hydrocarbon product is rich in olefins for production of clean liquid transportation fuels and/or light olefins.
- This invention provides a unique skeletal iron catalyst material advantageously suitable for use in either fixed bed or slurry-phase Fischer-Tropsch synthesis processes for H2+CO feedstreams for producing clean liquid transportation fuels and light olefin products. The particulate skeletal iron catalyst contains at least 50 wt. % iron and preferably 60-90 wt. % iron, with remainder being smaller percentages of non-ferrous metal selected from the group including aluminum, antimony, nickel, tin and zinc and a promotor metal selected from the group of calcium, copper, chromium, magnesium, and potassium. The final skeletal iron catalyst should have a surface area of 20-100 m2/g and average pore diameter of about 10-40 nm.
- The unique skeletal iron catalyst material of this invention is made using a preparation method which includes providing an iron powder mixed with suitable non-ferrous metal powder selected from aluminum, antimony, silicon, tin, or zinc sufficient to initially provide 20-80 wt % iron, together with 0.01-5 wt. % of a non-ferrous promotor metal powder selected from calcium, copper, chromium, magnesium, or potassium. The mixed metal powders are heated and melted together to form an iron alloy precursor material, which is then pulverized to 0.1-10 mm (100-10,000 micron) particle size, followed by extracting and/or leaching the major portion of the non-ferrous metal from the iron using a suitable caustic solution of NaOH or KOH, and leaving mainly the iron portion as the skeletal iron catalyst precursor material. The resulting catalyst may be further pulverized and have smaller particle size than 0.1-10 mm precursor particle, surface area of 20-100 m2/g and an average pore diameter of 10-40 nm. The catalyst is next treated by drying and reducing with hydrogen at high space velocity and at 100-500° C. temperature for 2-12 hours, then transferred into water-free alcohol or liquid paraffin for storage.
- The preparation method and treatment procedures for this skeletal iron catalyst are relatively simple and inexpensive. This resulting skeletal iron catalyst has good particle strength and attrition resistance, and activity equivalent to that of precipitated iron catalyst because during reactions its skeletal structure is easily accessible to H2 and produces larger yields of gasoline-diesel fuel range hydrocarbons and variable amounts of wax products. Also in F-T synthesis process it is easier to separate the skeletal iron catalyst from the reactor liquid medium and product, and thus achieves high recovery of the catalyst and thereby provides light hydrocarbon liquid products containing low concentrations of undesired catalyst fines.
- Although the skeletal iron catalyst of this invention is useful in either a fixed bed or slurry bed type (F-T) reactors, its use in slurry bed reactors is preferred. For use in fixed bed catalytic reactors, the catalyst particle size should be 1.0-10 mm, and for use in slurry bed type reactors the catalyst particle size should be 0.1-3.0 mm. For Fischer-Tropsch synthesis process utilizing this skeletal iron catalyst, useful reaction conditions are 0.3-3.0:1 H2/CO molar ratio, 180-500° C. temperature, and 0.5-5.0 mPa pressure.
- The skeletal iron catalyst of this invention is made utilizing the following basic steps:
- 1. Catalyst Preparation. Mix iron powder and a non-ferrous metal powder selected from aluminum, antimony, silicon, tin or zinc in proportion of 20-80 wt. % iron and also add 0.01-5 wt. % of promotor metal powder selected from calcium, copper, chromium, magnesium or potassium into a suitable furnace such as an electric induction furnace and mix together such as by magnetic stirring. Then melt the mixed powders under inert gas protection to form an iron alloy material, cool the iron alloy to room temperature and pulverize it to provide 0.1-10 mm particle size precursor material. Contact the iron alloy particles with 10-50% NaOH or KOH caustic solution in a stirred container under inert gas protection of argon, hydrogen or nitrogen, maintain reaction temperature 30-95° C. for 2-150 minutes to provide a desired substantial degree of extraction and/or leaching a major portion of the non-ferrous metal, and leaving particles containg mainly ∞—Fe and some Fe3O4. Adding the iron alloy powder to the caustic solution is usually preferred rather than the reverse order, as it results in skeletal iron catalyst having larger pore size. The skeletal iron catalyst is further pulverized and screened to obtain a desired particle size for synthesis reactions.
- Alternatively, the iron alloy precursor particles can be mixed with solid sodium hydroxide powder in a weight ratio to the iron alloy powder of 5-10:1, add deionized water to from a paste while stirring and allow the reaction to proceed for 5-30 minutes, then add fresh NaOH or KOH solution (10-50% concentration) and maintain for 2-60 minutes at 30-95° C.
- Another procedure for the catalyst preparation utilizes spraying the iron alloy precursor particles with a high concentration (40-60%) NaOH or KOH solution and maintaining the reaction in wet state for 5-30 minutes, then add additional NaOH or KOH 10-50% solution and maintain for 2-60 minutes at 30-95° C. temperature to effect the extraction and/or leaching step of removing most of the non-ferrous metal from the iron alloy particles. Then wash the iron particles with de-ionized water to pH=7, displace water with water-free ethanol, and store the resulting skeletal iron catalyst having 0.1-10 mm particle size in ethanol. Use of moderate extraction temperature of 50-60° C. appears to facilitate more pores and increased surface area, while longer extraction times cause undesirable partial oxidation of the iron particles. Following such extraction or leaching step, the catalyst can be further pulverized and screened as desired to obtain appropriate particle size for the F-T synthesis reactions. The catalyst is next treated by drying and reducing with hydrogen at high space velocity and at 100-500° C. temperature for 2-12 hours, then the treated skeletal iron catalyst is transferred into water-free ethanol or liquid paraffin for storage before further usage.
- 2. Catalyst Treatment and Utilization. Before the skeletal iron catalyst is evaluated or utilized in slurry-phase Fischer-Tropsch reaction, the catalyst is treated by being dried and reduced with hydrogen. Such treating is done by passing high space velocity hydrogen stream over the ethanol-containing catalyst at 100-500° C. for 2-12 hours, which catalyst is converted to mainly ∞—Fe and is subsequently transferred into a liquid paraffin medium. Reaction conditions for slurry-phase Fischer-Tropsch synthesis process are 0.3-3.0:1 H2/CO molar ratio, catalyst loading 5-20 wt. % relative to the liquid paraffin, catalyst particle size 0.062-3.0 mm(62-3000 microns) 180-400° C. temperature, 0.5-5 mPa pressure and reaction duration 40-240 hours. After completion of such catalytic reaction, the resulting catalyst/wax slurry material is removed, settled, and filtered. After slurry settling, the extent of a catalyst/wax separation is investigated. Also, the wax containing catalyst is extracted with xylene and analyzed for change in particle size distribution.
- Compared with currently used fused iron and precipitated iron catalyst in Fischer-Tropsch synthesis processes, the skeletal iron catalyst of this invention provides the following advantages:
- 1. Catalyst preparation method is relatively simple and inexpensive.
- 2. For synthesis gas feed H2/CO molar ratio range of 0.5-3.0:1, the synthesis gas conversion is significantly higher than that obtained by using fused iron catalyst, and conversion of the feed is equivalent to that achieved by precipitated iron catalyst.
- 3. Product selectivity favors producing more lower molecular weight hydrocarbons and less wax, resulting in lower slurry viscosity which facilitates catalyst/wax separation.
- 4. The skeletal iron catalyst particles has higher attrition resistance, so that most of the skeletal iron catalyst can be recovered after synthesis reactions, resulting in very low catalyst loss and no significant effect on catalyst activity.
- The process of this invention for utilizing the skeletal iron catalyst will be described with reference to the following drawing, in which
- FIG. 1 depicts a flowsheet for a typical Fischer-Tropsch synthesis process utilizing a slurry phase reactor.
- As shown by FIG. 1, separate feedstreams of pressurized CO at10 and H2 at 12 are provided having H2/CO molar ratio range of 0.5-2.5:1, together with skeletal iron catalyst having particle size of 10-300 micron provided at 13. The feeds and catalyst are all introduced upwardly into a
slurry type reactor 14 containing skeletal iron catalyst in aslurry bed 15. Reaction condition inreactor 14 are maintained at 200-350° C. temperature, 1.0-5.0 mPa pressure, and gas hourly space velocity of 0.5-3.0 L/g Fe/h. - From the
reactor 14, a gas product is removed at 16. Also, a hydrocarbon liquid stream containing some catalyst particles is withdrawn frominternal cup 17 asstream 18 and passed to a catalyst/liquid separator 20, which may be a settler vessel and/or hydroclone separator or filter. From theseparator 20, a clean hydrocarbon liquid product containing minimal catalyst is removed at 22, and used catalyst particles concentrated in a small portion of hydrocarbon liquid are withdrawn at 24. If desired, a portion of the used catalyst particles at 24 can be recycled at 25 back to thereactor 14, as needed to reduce catalyst loss and improve process economics. The remaining portion of the used catalyst at 26 is discarded. - The skeletal iron catalyst preparation method and the catalyst used in Fischer-Tropsch synthesis process will be disclosed further by the following examples, which should not be construed as limiting in their scope.
- Mix powders iron, aluminum and a small amount of copper promotor metal powder in a respective weight proportion of 33:66:1 in an electric induction furnace, heat and melt the metal powders to form an iron metal alloy, then cool it to room temperature and pulverize the resulting iron alloy to 0.1-1.0 mm size precursor particles. Then provide a desired amount of 25% NaOH caustic solution in a stirred container, add the iron alloy precursor particles under hydrogen flow, into the caustic solution maintained at 85° C. temperature, and allow reaction to proceed for 30 minutes to extract and/or leach substantially the aluminum from the iron alloy particles. Wash the particles with deionized water to pH=7, displace water with water-free ethanol and store the resulting skeletal iron catalyst particles in ethanol.
- Before being evaluated in a reaction system, the ethanol-containing skeletal iron catalyst is dried and reduced under high space velocity hydrogen at 300° C. for 2 hours, then transferred into reaction medium (liquid paraffin) in a stirred slurry autoclave reactor. Conditions for Fischer-Tropsch synthesis reaction are feedstream H2/CO molar ratio 2.0:1, catalyst loading 6 wt. %, particle size 0.100-0.125 mm, temperature 270° C., pressure 1.6 mPa, space velocity 1.0 L/g Fe/h and reaction time 40 hours. Test conditions and analytical results compared with precipitated iron catalyst are shown in Table 1 below.
- Mix powders iron and aluminum together with a small amount of copper promoter metal powder in weight proportion 33:66:1 into electric induction furnace, heat and melt the powders to form iron metal alloy, then cool it to room temperature and pulverize the iron alloy to 0.1-1.0 mm size precursor particles as for Example 1. Then provide a desired amount of 25% concentration NaOH in a stirred container under hydrogen stream, add the Fe-Al alloy particles into the NaOH caustic solution maintained at 75° C. temperature, allow reaction for 30 minutes to extract and/or leach substantially aluminum from the iron alloy particles. Then wash the particles with de-ionized water to pH=7, displace water with water-free ethanol and store skeletal iron catalyst particles in ethanol.
- Next dry and reduce the ethanol-containing skeletal iron catalyst at 300° C. under high space velocity hydrogen for 2 hours, and then transfer the catalyst into liquid reaction medium (liquid paraffin) in a stirred slurry phase reactor. Conditions for slurry phase Fischer-Tropsch synthesis reaction are: catalyst loading 6 wt. %, particle size 0.100-0.125 mm, temperature 270° C., and reaction time 40 hours. Test conditions and analytical results are shown in Table 1.
- Mix iron and aluminum powders together with a small amount of copper promoter powder in weight ratio of 33:66:1 in an electric induction furnace, heat and melt the metal powders to form an iron-aluminum alloy, then cool to room temperature and pulverize to 0.1-1.0 mm precursor particle size same as for Example 1. Then add desired amount of 25% concentration NaOH caustic solution to a stirred container, add the Fe-Al alloy particles to the caustic solution maintained at 65° C. temperature, and allow reaction for 30 minutes to extract and/or leach substantially the aluminum from the iron alloy particles. Then wash the particles with de-ionized water to pH=7, displace water with water-free ethanol, and store the resulting skeletal iron catalyst in ethanol.
- Before the skeletal iron catalyst is evaluated in a reactor system, the ethanol-containing catalyst is dried and reduced at 300° C. under high space velocity H2 for 2 hours, and is then transferred into slurry phase reaction medium (liquid paraffin) in a stirred reactor. Conditions for Fischer-Tropsch slurry phase reaction are: catalyst loading 6 wt. %, particle size 0.100-0.125 mm, temperature 270° C. and reaction time 40 hours. The test conditions and analytical results are shown in Table 1.
- Mix iron and aluminum metal powders and small amount of copper promoter powder in weight proportion of 33:66:1 in an electric induction furnace, heat and melt the metal powder to form an iron metal alloy, then cool it to room temperature and pulverize the metal alloy to 0.1-1.0 mm precursor particles size same as for Example I. Then provide a desired volume of NaOH
caustic solution 25% concentration into a stirred container, add the Fe-Al alloy particles into the caustic solution maintained at 95° C. temperature, and allow reaction for 30 minutes to extract and/or leach substantially all the aluminum from the iron alloy particles. Then wash the particles with de-ionized water until pH=7, displace water with water-free ethanol, and store the skeletal iron catalyst in ethanol. - Before the skeletal iron catalyst is evaluated in a reactor system, the ethanol-containing catalyst is dried and reduced with high space velocity hydrogen at 300° C. for 2 hours; catalyst is subsequently transferred into a reaction medium (liquid paraffin) in a stirred autoclave reactor. Conditions for Fischer-Tropsch synthesis reaction are catalyst loading 6 wt. %, particle size 0.100-0.125 mm, temperature 270° C., and reaction time 40 hours. Test conditions and analytical results after reaction evaluation are listed below in Table 1.
TABLE 1 Comparisons of Skeletal Iron Catalyst and Precipitated Iron Catalyst in Fischer-Tropsch Slurry-Phase Synthesis Reaction under Identical Conditions* Skeletal Iron Catalyst Precipitated Example No. 1 2 3 4 Iron Catalyst Caustic Leaching 85 75 65 95 — Temperature for Iron Alloy Precursor Particles, ° C. Relative Separation of 20 20 25 25 100 Catalyst in Slurry, %** Catalyst Particle Size ˜50 40-50 30-40 ˜30 1-10 After Reaction, um CO Conversion Decline <5% <5% <5% <5% >20% in 50 hours, % Catalyst Loss in 0.01 0.01 0.01 0.01 1.38 50 hours, % - Based on the above results, it is noted that the skeletal iron catalyst examples of this invention retain larger particle size, have improved attritiion resistance during F-T reaction, and are much more easily separated from the reaction product liquid than the known precipitated iron catalyst having smaller particle size after the reaction. Also, the decline in CO conversion and catalyst loss in product wax are substantially less for the skeletal iron catalyst, thereby indicating its lower catalyst consumption for the Fischer-Tropsch synthesis process.
- Additional evaluations were made using this skeletal iron catalyst in a liquid paraffin medium in a slurry bed autoclave reactor. Reaction conditions for the H2+CO feedstream for olefins production were: catalyst loading 5-20 wt. % relative to the liquid paraffin, reaction duration 40-240 minutes. For a specific series of catalyst evaluation tests, the following results were obtained as listed below in Table 2.
TABLE 2 Reaction Results With Skeletal Iron Catalyst for H2/CO Feed Catalyst Parameters: Particle size, mm 0.062-0.30 (62-300 micron) Surface area, m2/g 22.5 Average pore size, nm 12.5 Reaction Conditions: System pressure, mPa 1.1-1.5 Reaction temperature, ° C. 273-283° C. Gas hourly space velocity, L/g Fe/hr 1.0-2.0 Conversion (single-pass), % CO 82.7-94.5 H2 30.0-39.6 Yields (single-pass), g/Nm3 (H2 + CO) C1+ 65.7-132.0 C1-C4 43.8-78.3 Hydrocarbon Distribution, Vol. % C1 15.3-20.3 C2-C4 39.0-49.3 C2 − C4-/C2 0 − C4 0 1.2-2.4 - Based on these results, it is noted that for slurry-bed Fischer-Tropsch synthesis reaction at conditions of temperature range 180-330° C., pressure range 0.5-3.0 mPa, gas hourly space velocity in the range of 0.5-3.0 L/gFe/h, and feed gas H2/CO mole ratio of 0.5-2.0:1, single-pass CO conversion of 83-95%, single-pass syngas conversion of 48-57%, single-pass hydrocarbon yield of 32-62 wt. % were achieved. About ⅕ to ⅓ of the hydrocarbon products are C2-C4 olefins.
- Although this invention has been disclosed broadly and also identifies specific embodiments, it will be understood that modifications and variations can be made within the scope of the invention as defined by the following claims.
Claims (13)
1. A particulate skeletal iron catalyst comprising at least about 50 wt. % iron with the remainder being non-ferrous metal selected from the group consisting of aluminum, antimony, nickel, tin and zinc, and a non-ferrous promotor metal selected from the group consisting of calcium, copper, chromium, magnesium and potassium, which non-ferrous metals have been substantially removed from the catalyst by a chemical extraction and/or leaching step and thereby providing iron alloy particles having a skeletal type structure of mainly iron, said catalyst having particle size smaller than 10 mm, surface area of 20-100 m2/g, and average pore diameter of 10-40 nm.
2. The skeletal iron catalyst of claim 1 , wherein said catalyst contains 60-90 wt. % iron, has surface area of 25-80 m2/g., and particle size of 0.02-5 mm (20-5000 microns).
3. A method for preparing a skeletal iron catalyst useful for Fischer-Tropsch synthesis processes, comprising the steps of:
a) providing a catalyst precursor metal alloy by mixing iron powder together with non-ferrous metal powder selected from aluminum, antimony, silicon, tin and zinc sufficient to provide iron content of 20-80 wt. % and 0.01-5.0 wt. % non-ferrous promotor metal powder selected from calcium, chromium, copper, magnesium and potassium; heating said mixed metal powders together under inert gas protection, while stirring said metal powders uniformly and melting the metal powders to form precursor iron alloy material, then cooling the melted iron alloy to room temperature and pulverizing the resulting iron alloy to provide skeletal iron catalyst precursor particles having 0.1-10 mm particle size;
b) contacting said skeletal iron alloy catalyst precursor particles with NaOH or KOH caustic solution having 10-50% concentration under inert argon, helium or hydrogen atmosphere, and heating the mixture to 30-95° C. temperature while maintaining reaction condition for 2-150 minutes and extracting and/or leaching out a major portion of the non-ferrous metal from the iron alloy precursor particles so as to provide a skeletal iron structure, then washing said particles with ion-free water until pH=7, displacing the water with alcohol, and placing the resulting skeletal iron catalyst particles in ethanol; and
c) treating said skeletal iron catalyst particles by drying and reducing with hydrogen at high space velocity at 100-500° C. temperature for 2-12 hours, then transferring the treated skeletal iron catalyst into water-free ethanol or liquid paraffin for storage.
4. The skeletal iron catalyst preparation method of claim 3 , wherein step (b) is treating said skeletal iron catalyst precursor particles by adding sufficient said NaOH or KOH caustic solution into a stirred container under hydrogen atmosphere and heating the solution to 30-95° C. temperature, then adding the iron alloy precursor particles into the caustic solution at suitable periodic time intervals, while maintaining the reaction condition for 5-150 minutes for extracting and /or leaching out a major portion of the non-ferrous metal from the iron alloy precursor particles, then washing the iron alloy precursor particles with deionized water until pH=7, displacing the water with alcohol, and placing the resulting skeletal iron alloy catalyst particles in ethanol.
5. The skeletal iron catalyst preparation method of claim 3 , wherein step (b) is mixing said iron alloy precursor particles with solid sodium hydroxide (NaOH) powder at weight ratio of the sodium hydroxide to the iron alloy particles of 5-10:1, then adding deionized water dropwise to wet the mixture to provide a paste but not a fluid state while stirring so that reaction proceeds under a wet paste state; after the reaction has proceeded 5-30 minutes while gas release gradually decreases, adding to said paste mixture fresh NaOH or KOH 10-50% concentration solution and maintaining for 2-60 minutes at 50-95° C. temperature; then washing the iron alloy particles with deionized water to pH=7, displacing water with water-free ethanol and storing in ethanol.
6. The skeletal iron catalyst preparation method of claim 3 , wherein step (b) includes placing said iron alloy precursor particles in a stirred container, spraying the particles with a 40-60% concentration NaOH or KOH solution, maintaining reaction in a wet but not fluid state for 5-30 minutes, adding NaOH or KOH caustic solution of 10-50% concentration and maintaining for 2-60 minutes at 50-90° C. temperature, then washing the iron alloy particles with deionized water to pH=7, then displacing the water with water-free ethanol and storing in ethanol.
7. The catalyst preparation method of claim 3 , wherein said mixed metal powders are iron, aluminum and copper having an initial respective weight ratio of 33:66:1.
14. (Amended) The skeletal iron catalyst of claim 1 , wherein the catalyst particle size after Fischer-Tropsch synthesis reaction is 0.025-1.0 mm. (25-1000 microns).
15. The catalyst preparation method of claim 3 , wherein the step (b) catalyst precursor metal alloy extraction and/or leaching temperature is 50-95° C., and the treated skeletal iron catalyst particle size is 0.062-3.0 mm. (62-3000 microns).
16. The skeletal iron catalyst preparation method of claim 3 , wherein said non-ferrous metal powder is aluminum and said promotor metal powder is copper.
17. The skeletal iron catalyst preparation method of claim 3 , wherein said metal powder mixture is heated and melted in an electric induction furnace during magnetic stirring.
18. The skeletal iron catalyst preparation method of claim 3 , wherein the iron alloy catalyst particle extracting/leaching temperature is 65-95° C., particle size is 30-50 microns, and relative separation of the catalyst in F-T synthesis product liquid slurry is 20-25 % of the initial height in the product liquid slurry.
19. A method for preparing a skeletal iron catalyst particularly useful for Fischer-Tropsch synthesis processes, comprising the steps of:
a) providing a catalyst precursor metal alloy by mixing iron powder together with aluminum powder sufficient to provide iron content of 20-80 wt. % and 0.01-5.0 wt. % copper powder, heating said mixed metal powders together in an electric induction furnace under inert gas protection, while mixing said metal powders uniformly by magnetic stirring and melting the metal powders to form precursor iron alloy material, then cooling the melted precursor iron alloy to room temperature and pulverizing the resulting iron alloy to provide skeletal iron catalyst precursor particles having 0.1-10 mm particle size;
b) contacting said skeletal iron alloy catalyst precursor particles with NaOH or KOH caustic solution having 10-50% concentration under inert hydrogen atmosphere by adding sufficient NaOH or KOH caustic solution having 10-50% concentration into a stirred container under the hydrogen atmosphere and heating the solution to 30-95° C. temperature, then adding the iron alloy precursor particles into the caustic solution at suitable periodic time intervals, while maintaining the reaction condition for 2-150 minutes and extracting and/or leaching out a major portion of the non-ferrous metal from the iron alloy precursor particles so as to provide a skeletal iron structure having particle size smaller than 10 mm, then washing said skeletal iron particles with ion-free water until pH=7, displacing the water with alcohol, and placing the resulting skeletal iron catalyst particles in ethanol; and
c) treating the skeletal iron catalyst particles by drying and reducing with hydrogen at high space velocity at 200-500° C. temperature for 2-12 hours, then transferring the treated skeletal iron catalyst into water-free ethanol or liquid paraffin for storage.