US20010053863A1 - Allylated amide compounds and die attach adhesives prepared therefrom

Info

Publication number: US20010053863A1
Application number: US09/801,851
Authority: US
Inventors: Rose Schultz; Donald Herr; Chaodong Xiao
Original assignee: Individual
Current assignee: Individual
Priority date: 1998-07-02
Filing date: 2001-06-29
Publication date: 2001-12-20
Anticipated expiration: 2019-06-18
Also published as: CN1249302A; KR100566552B1; EP0970946A2; US6388037B2; KR20000011412A; SG105450A1; JP2000143597A

Abstract

Allylated amide compounds are formulated into curable compositions with a free radical curing agent, and optionally, one or more fillers, for use as adhesives in the manufacture of microelectronic devices.

Description

The priority of provisional application 60/091,509, filed Jul. 2, 1998, is claimed under 35 USC 119(e).[0001]

FIELD OF THE INVENTION

This invention relates to allylated amide compounds and adhesives prepared from those compounds.

BACKGROUND OF THE INVENTION

Adhesive compositions, particularly conductive adhesives, are used for a variety of purposes in the fabrication and assembly of semiconductor packages and microelectronic devices. The more prominent uses are the bonding of integrated circuit chips to lead frames or other substrates, and the bonding of circuit packages or assemblies to printed wire boards.

The requirements for conductive adhesives in electronic packaging are that they have good mechanical strength, curing properties that do not affect the component or the carrier, and thixotropic properties compatible with existing application equipment currently used in the industry.

Another important aspect of an adhesive bonding or interconnection technology is the ability to rework the bond. For single chip packaging involving high volume commodity products, a failed chip can be discarded without significant loss. However, it becomes expensive to discard multi-chip packages with only one failed chip; consequently, the ability to rework the failed chip would be a manufacturing advantage. Today, one of the primary thrusts within the semiconductor industry is to develop adhesives that will meet all the requirements for adhesive strength and flexibility, but that will also be reworkable.

Conventional adhesive technology uses low viscosity thermosetting organic materials, the most widely used being epoxy systems. In order to achieve the required mechanical performance, relatively high molecular weight thermoplastics would be the preferred compositions for adhesive materials. These materials, however, have high viscosity or even solid film form, which are drawbacks to the manufacturing process. Therefore, there is a need for new adhesives that are easily dispensable to conform with automated manufacturing processes and that are reworkable.

SUMMARY OF THE INVENTION

This invention relates to allylated amide compounds that can be used in curable compositions. Allylated in this context means that allyl moieties are bonded to the nitrogen of amide moieties.

In another embodiment, this invention is an adhesive composition for use in electronic devices that comprises one or more allylated amide compounds, a curing initiator, and optionally, one or more fillers. The composition optionally may also contain mono- or polyfunctional vinyl compounds.

In another embodiment, this invention is the cured adhesive that results from the just described curable adhesive composition.

In another embodiment, this invention is a electronic assembly comprising an electronic component bonded to a substrate with a cured adhesive composition prepared from a composition comprising one or more allylated amide compounds, a curing initiator, optionally one or more fillers, and optionally one or more mono- or polyfunctional vinyl compounds.

In another embodiment, this invention is a method for adhering an electronic component to a substrate with a cured adhesive prepared from a composition comprising one or more allylated amide compounds, a curing initiator, optionally one or more fillers, and optionally, one or more mono- or polyfunctional vinyl compounds, the method comprising applying the adhesive to the component or the substrate, contacting the component and the substrate, and curing the adhesive in situ.

DETAILED DESCRIPTION OF THE INVENTION

The allylated amide compounds, and vinyl compounds, used in the adhesive compositions of this invention are curable compounds, meaning that they are capable of polymerization, with or without crosslinking. As used in this specification, to cure will mean to polymerize, with or without crosslinking. Cross-linking, as is understood in the art, is the attachment of two polymer chains by bridges of an element, a molecular group, or a compound, and in general will take place upon heating. As cross-linking density is increased, the properties of a material can be changed from thermoplastic to thermosetting.

It is possible to prepare polymers of a wide range of cross-link density by the judicious choice and amount of mono- or polyfunctional compounds. The greater proportion of polyfunctional compounds reacted, the greater the cross-link density. In order to provide thermoplastic properties, adhesive compositions are prepared from mono-functional compounds to limit the cross-link density. However, a minor amount of poly-functional compounds can be added to provide some cross-linking and strength to the composition, provided the amount of poly-functional compounds is limited to an amount that does not diminish the desired thermoplastic properties. Within these parameters, the strength and elasticity of individual adhesives can be tailored to a particular end-use application.

The cross-link density can also be controlled to give a wide range of glass transition temperatures in the cured adhesive to withstand subsequent processing and operation temperatures.

In those cases where it is necessary to rework the assembly, the electronic component can be pried off the substrate, and any residue adhesive can be heated until it softens and is easily removed.

In the inventive adhesive compositions, the allylated amide compounds, and vinyl compounds if used in combination with the allylated amide compounds, will be present in the curable package adhesive compositions in an amount from 2 to 98 weight percent based on the organic components present (excluding any fillers).

The adhesive compositions will further comprise at least one free-radical initiator, which is defined to be a chemical species that decomposes to a molecular fragment having one or more unpaired electrons, highly reactive and usually short-lived, which is capable of initiating a chemical reaction by means of a chain mechanism. The free-radical initiator will be present in an amount of 0.1 to 10 percent, preferably 0.1 to 3.0 percent, by weight of the allylated amide compound, or combination of both allylated amide and vinyl compounds (excluding any filler). The free radical curing mechanism gives a fast cure and provides the composition with a long shelf life before cure. Preferred free-radical initiators include peroxides, such as butyl peroctoates and dicumyl peroxide, and azo compounds, such as 2,2′-azobis(2-methyl-propanenitrile) and 2,2′-azobis(2-methyl-butanenitrile).

Alternatively, the adhesive compositions may contain a photoinitiator, such as is sold by Ciba Specialty Chemicals under the trademark Irgacure, in lieu of the free-radical initiator, and the curing process may then be initiated by UV radiation. The photoinitiator will be present in an amount of 0.1 to 10 percent, preferably 0.1 to 3.0 percent, by weight of the allylated amide compound, or combination of both allylated amide and vinyl compounds (excluding any filler). In some cases, both photoinitiation and free-radical initiation may be desirable. For example, the curing process can be started by UV irradiation, and in a later processing step, curing can be completed by the application of heat to accomplish a free-radical cure.

In general, these compositions will cure within a temperature range of 50° to 250° C., and curing will be effected within a length of time of less than one minute to four hours. As will be understood, the time and temperature curing profile for each adhesive composition will vary, and different compositions can be designed to provide the curing profile that will be suited to the particular industrial manufacturing process.

Ease of application, even when thermoplastic properties are desired for the adhesive, is achieved by using relatively low molecular weight reactive oligomers or pre-polymers and curing these in situ after application to the electronic component or substrate. Applying the materials in an uncured state gives high processibility, and the resultant cured thermoplastic adhesive provides high mechanical performance.

Suitable conductive fillers for the adhesives are silver, copper, gold, palladium, platinum.

Allylated Amide Compounds

The allylated amide compounds suitable for use in the compositions of this invention have a structure represented by the formulas A and B as depicted here:

As used throughout this specification, the notation C(O) refers to a carbonyl group. For these specific formulae, when lower case “n” is the integer 1, the compound will be a mono-functional compound; and when lower case “n” is an integer 2 to 6, the compound will be a poly-functional compound.

Formula A represents those compounds in which:

R ⁹is H, an alkyl or alkyleneoxy group having 1 to 18 carbon atoms, allyl, aryl, or substituted aryl having the structure

in which R ¹⁰, R¹¹, and R¹²are independently H or an alkyl or alkyleneoxy group having 1 to 18 carbon atoms;

each X independently is an aromatic group selected from the aromatic groups having the structures (I) through (V):

and Q is a linear or branched chain alkyl, alkyloxy, alkyl amine, alkyl sulfide, alkylene, alkyleneoxy, alkylene amine, alkylene sulfide, aryl, aryloxy, or aryl sulfide species having up to about 100 atoms in the chain, which may contain saturated or unsaturated cyclic or heterocyclic substituents pendant from the chain or as part of the backbone in the chain, and in which any heteroatom present may or may not be directly attached to X;

or Q is a urethane having the structure:

in which each R ²independently is an alkyl, aryl, or arylalkyl group having 1 to 18 carbon atoms; R³is an alkyl or alkyloxy chain having up to 100 atoms in the chain, which chain may contain aryl substituents; X is O, S, N, or P; and v is 0 to50;

or Q is an ester having the structure:

in which R ³is an alkyl or alkyloxy chain having up to 100 atoms in the chain, which chain may contain aryl substituents;

or Q is a siloxane having the structure: —(CR ¹ ₂)_e—[SiR⁴—O]_f—SiR⁴ ₂—(CR¹ ₂)_g— in which the R¹substituent independently for each position is H or an alkyl group having 1 to 5 carbon atoms and the R⁴substituent independently for each position is an alkyl group having 1 to 5 carbon atoms or an aryl group, and e and g are independently 1 to 10 and f is 1 to 50; and

m is 0 or 1,and n is 1 to 6.

Formula B represents those compounds in which

R ⁹is H, or an alkyl or alkyleneoxy group having 1 to 18 carbon atoms, or an allyl group, or an aryl or substituted aryl having the structure

Z is a linear or branched chain alkyl, alkyloxy, alkyl amine, alkyl sulfide, alkylene, alkyleneoxy, alkylene amine, alkylene sulfide, aryl, aryloxy, or aryl sulfide species having up to about 100 atoms in the chain, which may contain saturated or unsaturated cyclic or heterocyclic substituents pendant from the chain or as part of the backbone in the chain, and in which any heteroatom present may or may not be directly attached to K;

or Z is a urethane having the structure:

in which each R ²independently is an alkyl, aryl, or arylalkyl group having 1 to 18 carbon atoms; R³is an alkyl or alkyloxy chain having up to 100 atoms in the chain, which chain may contain aryl substituents; X is O, S, N, or P; and v is 0 to 50;

or Z is an ester having the structure:

or Z is a siloxane having the structure: —(CR ¹ ₂)_e—[SiR⁴ ₂—O]_f—SiR⁴ ₂—(CR¹ ₂)_g— in which the R¹substituent independently for each position is H or an alkyl group having 1 to 5 carbon atoms and the R⁴substituent independently for each position is an alkyl group having 1 to 5 carbon atoms or an aryl group, and e and g are independently 1 to 10 and f is 1 to 50;

K is an aromatic group selected from the aromatic groups having the structures (VI) through (XIII) (although only one bond may be shown to represent connection to the aromatic group K, this will be deemed to represent any number of additional bonds as described and defined by n):

in which R ⁵, R⁶, and R⁷are a linear or branched chain alkyl, alkyloxy, alkyl amine, alkyl sulfide, alkylene, alkyleneoxy, alkylene amine, alkylene sulfide, aryl, aryloxy, or aryl sulfide species having up to about 100 atoms in the chain, which may contain saturated or unsaturated cyclic or heterocyclic substituents pendant from the chain or as part of the backbone in the chain, and in which any heteroatom present may or may not be directly attached to the aromatic ring; or R⁵, R⁶, and R⁷are a siloxane having the structure —(CR¹ ₂)_e—[SiR⁴ ₂—O]_f—SiR⁴ ₂—(CH₃)_g— in which the R¹substituent is H or an alkyl group having 1 to 5 carbon atoms and the R⁴substituent independently for each position is an alkyl group having 1 to 5 carbon atoms or an aryl group, and e is 1 to 10 and f is 1 to 50;

and m is 0 or 1 and n is 1 to 6.

Vinyl Compounds

The compounds suitable for use in the adhesive compositions of this invention have a structure represented by one of the formulae: [M-X _m]_n-Q or [M-Z_m]_n-K, in which m is 0 or 1, and n is 1 to 6.

M represents a vinyl group and can be the maleimide moiety having the structure:

in which R ¹is H or C₁to C₅alkyl; or or the vinyl moiety having the structure:

in which R ¹and R²are H or an alkyl having 1 to 5 carbon atoms, or together form a 5 to 9 membered ring with the carbons forming the vinyl group; B is C, S, N, O, C(O), O-C(O), C(O)-O, C(O)NH or C(O)N(R⁸), in which R⁸is C₁to C₅alkyl. Preferably, B is O, C(O), O-C(O), C(O)-O, C(O)NH or C(O)N(R⁸); more preferably B is O, C(O), or C(O)N(R⁸).

X independently is an aromatic group selected from the aromatic groups having the structures (I) through (V):

Preferably, X is structure (II), (III), (IV) or (V), and more preferably is structure (II).

Q and Z independently can be a linear or branched chain alkyl, alkyloxy, alkyl amine, alkyl sulfide, alkylene, alkyleneoxy, alkylene amine, alkylene sulfide, aryl, aryloxy, or aryl sulfide species having up to about 100 atoms in the chain, which may contain saturated or unsaturated cyclic or heterocyclic substituents pendant from the chain or as part of the backbone in the chain, and in which any heteroatom present may or may not be directly attached to X;

or Q and Z independently can be a urethane having the structure:

or Q and Z independently can be an ester having the structure:

or Q and Z independently can be a siloxane having the structure: —(CR ¹ ₂)_e—[SiR⁴—O]_f—SiR⁴ ₂—(CR¹ ₂)_g— in which the R¹substituent independently for each position is H or an alkyl group having 1 to 5 carbon atoms and the R⁴substituent independently for each position is an alkyl group having 1 to 5 carbon atoms or an aryl group, and e and g are independently 1 to 10 and f is 1 to 50.

Preferably, Q and Z will be a linear or branched chain alkyl, alkyloxy, alkylene, or alkyleneoxy species having up to about 100 atoms in the chain, as described with pendant saturated or unsaturated cyclic or heterocyclic substituents, or a siloxane as described, and more preferably is a linear or branched chain alkyl species or siloxane, as described.

Preferably, K is structure (VIII), (X) or (XI), more preferably is structure (X) or (XI), and most preferably is structure (X).

Other Composition Components

Depending on the nature of the substrate, the composition may also contain a coupling agent. A coupling agent as used herein is a chemical species containing a polymerizable functional group for reaction with the maleimide and other vinyl compound, and a functional group capable of condensing with metal hydroxides present on the surface of the substrate. Such coupling agents and the preferred amounts for use in compositions for particular substrates are known in the art. Suitable coupling agents are silanes, silicate esters, metal acrylates or methacrylates, titanates, and compounds containing a chelating ligand, such as phosphine, mercaptan, and acetoacetate. When present, coupling agents typically will be in amounts up to 10 percent by weight, and preferably in amounts of 0.1 to 3.0 percent by weight, of the allylated amide and vinyl compound, if any.

In addition, the compositions may contain compounds that lend additional flexibility and toughness to the resultant cured composition. Such compounds may be any thermoset or thermoplastic material having a Tg of 50° C. or less, and typically will be a polymeric material characterized by free rotation about the chemical bonds, such as can be obtained by the presence of carbon-carbon double bonds adjacent to carbon-carbon single bonds, the presence of ester and ether groups, and the absence of ring structures. Suitable such modifiers include polyacrylates, poly(butadiene), polyTHF (polymerized tetrahydrofuran), CTBN (carboxy-terminated butyronitrile) rubber, and polypropylene glycol. When present, toughening compounds may be in an amount up to about 15 percent by weight of the maleimide and other monofunctional vinyl compound.

Siloxanes may also be added to the compositions to impart elastomeric properties. Suitable siloxanes are the methacryloxypropyl-terminated polydimethyl siloxanes, and the aminopropyl-terminated polydimethylsiloxanes, available from United Chemical Technologies.

The composition may also contain organic fillers, such as, polymers to adjust rheology. Other additives known and used in the art may also be used for specific purposes, such as, adhesion promoters. The selection of the types and amounts suitable is within the expertise of one skilled in the art.

EXAMPLE 1

Preparation of Bis Phenol F-Bis(diallylamide)

[0067]
Bisphenol F (200.3 g, 1 mol) is solvated in tetrahydrofuran (THF) (500 mL) in a 2 L three-necked flask equipped with mechanical stirrer and reflux condenser. To this solution is added 1,2-epoxy-9-decene (308.5 g, 2 mol) and benzyldimethylamine (0.67 g, 5 mmol). The solution is warmed to 80° C. for 7 hours and then allowed to cool to room temperature. Solvent is removed in vacuo to yield an oil. [0068]
The intermediate isolated above (508.8 g, 1 mol) is dissolved in THF (1 L) and H[0069] ₂O (1 L) in a 3 L three-necked flask equipped with mechanical stirrer, reflux condenser and internal temperature probe under nitrogen. To this solution is added KMnO4 (316 g, 2 mol), and the resulting mixture warmed to 80° C. for 5 hours. The reaction is allowed to cool to room temperature and bulk solvent is removed in vacuo. The resulting material is solvated in CH₂Cl₂(1 L), filtered, and washed with H₂O (3×1 L). The isolated organics are dried over MgSO₄and solvent removed in vacuo to yield a diacid intermediate.
The above diacid (544.8 g, 1 mol) is combined with diallylamine (194.3 g, 2 mol) and CH[0070] ₂Cl₂(1 L) in a 3 L three-necked flask equipped with a mechanical stirrer, addition funnel and internal temperature probe under nitrogen. The solution is cooled to 4° C. in an ice bath. The addition funnel is charged with dicyclohexylcarbodiimide (DCC) (412.7 g, 2 mol) dissolved in CH₂Cl₂(300 mL), and this solution added to the stirred amine solution over the course of 60 minutes. The reaction is stirred on the ice bath for an additional 30 minutes. The mixture is allowed to warm to room temperature and further stirred for 4 hours. The solution is filtered to remove precipitated dicyclohexylurea (DCU). The isolated organics are dried over MgSO₄anhyd., filtered and solvent removed in vacuo to yield the bis(diallylamide) product.

EXAMPLE 2

Preparation of Poly(butadiene)bis(diallylamide)

[0071]
Diallylamine (97.15 g, 1 mol) is solvated in acetone (500 mL) in a 2 L three-necked flask equipped with mechanical stirrer, addition funnel and internal temperature probe under nitrogen. The solution is cooled on an ice bath. Maleinized poly(butadiene) (Ricon 131MA5, Ricon Resins Inc., 1766 g) dissolved in acetone (500 mL) is charged into the addition funnel and added to the cooled amine solution over the course of 60 minutes maintaining an internal temperature <10° C. The solution is stirred on ice for an additional 60 minutes, then allowed to warm to room temperature and stirred for another 2 hours. Solvent and residual diallylamine are removed in vacuo to yield the poly(diallylamide). [0072]

EXAMPLE 3

Preparation of Dimer Bis(diallylamide) or 10,11-Dioctyl-1,20-eicosyl bis(diallylamide)

Dimer acid (sold under the trademark Empol 1024 by Unichema, 20.5 g, 35.7 mmol) was solvated in anhydrous toluene (250 mL) in a 500 mL four-necked flask equipped with reflux condenser, addition funnel, and magnetic stirring under nitrogen. This solution was warmed to 80° C., and oxalyl chloride (12.5 mL, 143 mmol) was added dropwise over the course of 60 minutes. Evolution of CO[0073] ₂, CO and HCl was immediately evident. The reaction was stirred for an additional 3 hours after the addition was complete, allowed to cool to room temperature and solvent removed in vacuo to yield an orange oil. IR and ¹H NMR spectral data were consistent with the desired bis(acid chloride) product.
Diallyl amine (10.0 mL) was solvated in diethyl ether (Et[0074] ₂O) (200 mL) in a 500 mL three-necked flask equipped with mechanical stirrer, addition funnel and internal temperature probe under nitrogen. NaOH (3.2 g, 80 mmol) dissolved in H₂O (100 mL) was added to this solution. This solution was cooled to 4° C. on an ice bath. The bis(acid chloride) described above was solvated in Et₂O (20 mL), charged into the addition funnel and added to the stirred amine solution over the course of 30 minutes, maintaining an internal temperature <10° C. This solution was stirred on ice for an additional one hour, then allowed to warm to room temperature, and stirred for an additional 4 hours. The organic layer was isolated and washed with 5% HCl_aq(200 mL), and H₂O (2×200 mL). The isolated organics were dried over MgSO4 anhydrous, filtered, and the solvent removed in vacuo to yield an orange oil (87%), which exhibited IR and ¹H NMR spectral data consistent with the desired bis(diallylamide).

Claims

What is claimed is:

1. An allylated amide compound having the formula

in which m is 0 or 1, n is 1 to 6, and

(a) R⁹is H, an alkyl group having 1 to 18 carbon atoms, an alkyleneoxy group having 1 to 18 carbon atoms, an allyl group, an aryl group, or a substituted aryl group having the structure

in which R¹⁰, R¹¹, and R¹²are independently H or an alkyl or alkyleneoxy group having 1 to 18 carbon atoms;

(b) X is an aromatic group selected from the group of aromatic groups having the structures:

(c) Q is a linear or branched chain alkyl, alkyloxy, alkyl amine, alkyl sulfide, alkylene, alkyleneoxy, alkylene amine, alkylene sulfide, aryl, aryloxy, or aryl sulfide species having up to about 100 atoms in the chain, which may contain saturated or unsaturated cyclic or heterocyclic substituents pendant from the chain or as part of the chain, and in which any heteroatom present may or may not be directly attached to X.

2. The allylated amide compound according to

claim 1

in which Q is a linear or branched chain alkyl species having up to about 100 atoms in the chain, which may contain saturated or unsaturated cyclic or heterocyclic substituents pendant from the chain or as part of the chain, and in which any heteroatom present may or may not be directly attached to X.

3. The allylated amide compound according to

claim 1

in which Q is a urethane having the structure:

in which each R²independently is an alkyl, aryl, or arylalkyl group having 1 to 18 carbon atoms; R³is an alkyl or alkyloxy chain having up to 100 atoms in the chain, which chain may contain aryl substituents; X is O, S, N, or P; and v is 0 to 50.

4. The allylated amide compound according to

claim 1

in which Q is a siloxane having the structure (CR¹ ₂)_e—[SiR⁴ ₂—O]_f—SiR⁴ ₂—(CR¹ ₂)_g—

in which the R¹substituent independently for each position is H or an alkyl group having 1 to 5 carbon atoms, the R⁴substituent independently for each position is an alkyl group having 1 to 5 carbon atoms or an aryl group, e and g are independently 1 to 10, and f is 1 to 50.

5. The allylated amide compound according to

claim 1

in which Q is an ester having the structure:

in which R³is an alkyl or alkyloxy chain having up to 100 atoms in the chain, which chain may contain aryl substituents.

6. The allylated amide compound according to

claim 1

in which Q is an ester having the structure:

in which p is 1 to 100,

each R³can independently be an alkyl or alkyloxy chain having up to 100 atoms in the chain, which chain may contain aryl substituents,

or a siloxane having the structure —(CR¹ ₂)_e—[SiR⁴ ₂—O]_f—SiR⁴ ₂—(CR¹ ₂)_g— in which the R¹substituent independently for each position is H or an alkyl group having 1 to 5 carbon atoms, the R⁴substituent independently for each position is an alkyl group having 1 to 5 carbon atoms or an aryl group, e and g are independently 1 to 10, and f is 1 to 50.

7. The allylated amide compound according to

claim 1

in which Q is an ester having the structure:

in which p is 1 to 100,

8. An allylated amide compound having the formula

in which m is 0 or 1, n is 1-6, and

(a) R⁹is H, an alkyl or alkyleneoxy group having 1 to 18 carbon atoms, allyl, aryl, or substituted aryl having the structure

(b) K is an aromatic group selected from group of aromatic groups having the structures:

in which R⁵, R⁶, and R⁷are a linear or branched chain alkyl, alkyloxy, alkyl amine, alkyl sulfide, alkylene, alkyleneoxy, alkylene amine, alkylene sulfide, aryl, aryloxy, or aryl sulfide species having up to about 100 atoms in the chain, which may contain saturated or unsaturated cyclic or heterocyclic substituents pendant from the chain or as part of the backbone in the chain, and in which any heteratom present may or may not be directly attached to the aromatic ring; or

R⁵, R⁶, and R⁷are a siloxane having the structure —(CR¹ ₂)_e—[SiR⁴ ₂—O]_f—SiR⁴ ₂—(CH₃)_g— in which the R¹substituent is H or an alkyl group having 1 to 5 carbon atoms and the R⁴substituent independently for each position is an alkyl group having 1 to 5 carbon atoms or an aryl group, and e is 1 to 10 and f is 1 to 50;

and

(c) Z is a linear or branched chain alkyl, alkyloxy, alkyl amine, alkyl sulfide, alkylene, alkyleneoxy, alkylene amine, alkylene sulfide, aryl, aryloxy, or aryl sulfide species having up to about 100 atoms in the chain, which may contain saturated or unsaturated cyclic or heterocyclic substituents pendant from the chain or as part of the chain, and in which any heteroatom present may or may not be directly attached to K.

9. The allylated amide compound according to

claim 8

in which Z is a linear or branched chain alkyl species having up to about 100 atoms in the chain, which may contain saturated or unsaturated cyclic or heterocyclic substituents pendant from the chain or as part of the chain, and in which any heteroatom present may or may not be directly attached to K.

10. The allylated amide compound according to

claim 8

in which Z is a urethane having the structure:

11. The allylated amide compound according to

claim 8

in which Z is a siloxane having the structure: —(CR¹ ₂)_e—[SiR⁴ ₂—O]_f—SiR⁴ ₂—(CR¹ ₂)_g—

in which the R¹substituent independently for each position is H or an alkyl group having 1 to 5 carbon atoms, and the R⁴substituent independently for each position is an alkyl group having 1 to 5 carbon atoms or an aryl group, and e and g are independently 1 to 10 and f is 1 to 50.

12. The allylated amide compound according to

claim 8

in which Z is an ester having the structure:

13. The allylated amide compound according to

claim 8

in which Z is an ester having the structure:

in which p is 1 to 100,

14. The allylated amide compound according to

claim 8

in which Z is an ester having the structure:

in which p is 1 to 100,

15. The allylated amide compound according to any one of

claims 8

to

14

in which K is

in which p is 1 to 100.

16. The allylated amide compound according to any one of

claims 8

to

14

in which K is

in which R⁵, R⁶, and R⁷are a linear or branched chain alkyl, alkyloxy, alkyl amine, alkyl sulfide, alkylene, alkyleneoxy, alkylene amine, alkylene sulfide, aryl, aryloxy, or aryl sulfide species having up to about 100 atoms in the chain, which may contain saturated or unsaturated cyclic or heterocyclic substituents pendant from the chain or as part of the chain, and in which any heteroatom present may or may not be directly attached to the aromatic ring.

17. The allylated amide compound according to any one of

claims 8

to

14

in which K is

18. A curable adhesive composition comprising an allylated amide compound according to any one of claims 1 through 17, a curing initiator selected from the group consisting of a free-radical initiator and a photoinitiator, optionally a filter and optionally an adhesion promoter.

19. A curable adhesive composition comprising an allylated amide compound according to any one of claims 1 through 17 a curing initiator selected from the group consisting of an anionic and a cationic initiator, optionally a filler, and optionally an adhesion promoter.

20. A curable adhesive composition according to

claim 18

, further comprising a compound having the structure

[M-X_m]_n-Q in which m is 0 or 1 and n is 1 to 6, and

(a) M is a maleimide moiety having the structure:

in which R¹is H or an alkyl group having 1 to 5 carbon atoms;

and

(c) Q is a linear or branched chain alkyl, alkyloxy, alkyl amine, alkyl sulfide, alkylene, alkyleneoxy, alkylene amine, alkylene sulfide, aryl, aryloxy, or aryl sulfide species, which may contain saturated or unsaturated cyclic or heterocyclic substituents pendant from the chain or as part of the chain, and in which any heteratom present may or may not be directly attached to X; or

(d) Q is a urethane having the structure:

in which each R²independently is an alkyl, aryl, or arylalkyl group having 1 to 18 carbon atoms; R³is an alkyl or alkyloxy chain having up to 100 atoms in the chain, which chain may contain aryl substituents; X is O, S, N, or P; and v is 0 to 50; or

(e) Q is a siloxane having the structure: —(CR¹ ₂)_e—[SiR⁴ ₂—O]_f—SiR⁴ ₂—(CR¹ ₂)_g— in which the R¹substituent independently for each position is H or an alkyl group having 1 to 5 carbon atoms, and the R⁴substituent independently for each position is an alkyl group having 1 to 5 carbon atoms or an aryl group, and e and g are independently 1 to 10 and f is 1 to 50; or

(f) Q is an ester having the structure:

in which R³is an alkyl or alkyloxy chain having up to 100 atoms in the chain, which chain may contain aryl substituentsl; or

(g) Q is an ester having the structure:

in which p is 1 to 100, and

each R³can independently be an alkyl or alkyloxy chain having up to 100 atoms in the chain, which chain may contain aryl substituents; or

each R³can independently be a siloxane having the structure—(CR¹ ₂)_e—[SiR⁴ ₂—O]_f—SiR⁴ ₂—(CR¹ ₂)_g— in which the R¹substituent independently for each position is H or an alkyl group having 1 to 5 carbon atoms, the R⁴substituent independently for each position is an alkyl group having 1 to 5 carbon atoms or an aryl group, e and g are independently 1 to 10, and f is 1 to 50; or

(h) Q is an ester having the structure:

in which p is 1 to 100, and

each R³can independently be a siloxane having the structure—(CR¹ ₂)_e—[SiR⁴ ₂—O]_f—SiR⁴ ₂—(CR¹ ₂)_g— in which the R¹substituent independently for each position is H or an alkyl group having 1 to 5 carbon atoms, the R⁴substituent independently for each position is an alkyl group having 1 to 5 carbon atoms or an aryl group, e and g are independently 1 to 10, and f is 1 to 50.

21. A curable adhesive composition according to

claim 18

further comprising a compound having the structure

in which m is 0 or 1 and n is 1-6; and

(a) R¹and R²are H or an alkyl group having 1 to 5 carbon atoms, or together form a 5 to 9 membered ring with the carbons forming the vinyl group;

(b) B is C, S, N, O, C(O), C(O)NH or C(O)N(R⁸), in which R⁸is an alkyl group having 1 to 5 carbon atoms;

(c) X is an aromatic group selected from the group of aromatic groups having the structures:

and

(d) Q is a linear or branched chain alkyl, alkyloxy, alkyl amine, alkyl sulfide, alkylene, alkyleneoxy, alkylene amine, alkylene sulfide, aryl, aryloxy, or aryl sulfide species, which may contain saturated or unsaturated cyclic or heterocyclic substituents pendant from the chain or as part of the chain, and in which any heteratom present may or may not be directly attached to X; or

(e) Q is a urethane having the structure:

(f) Q is a siloxane having the structure: —(CR¹ ₂)_e—[SiR⁴ ₂—O]_f—SiR⁴ ₂—(CR¹ ₂)_g— in which the R¹substituent independently for each position is H or an alkyl group having 1 to 5 carbon atoms, and the R⁴substituent independently for each position is an alkyl group having 1 to 5 carbon atoms or an aryl group, and e and g are independently 1 to 10 and f is 1 to 50; or

(g) Q is an ester having the structure:

(h) Q is an ester having the structure:

in which p is 1 to 100, and

(i) Q is an ester having the structure:

in which p is 1 to 100, and

22. A curable adhesive composition according to

claim 18

further comprising a compound having the structure

[M-Z_m]_n-K in which m is 0 or 1 and n is 1-6, and

(a) M is a maleimide moiety having the structure

in which R¹is H or an alkyl having 1 to 5 carbon atoms;

in which R⁵, R⁶, and R⁷are a linear or branched chain alkyl, alkyloxy, alkyl amine, alkyl sulfide, alkylene, alkyleneoxy, alkylene amine, alkylene sulfide, aryl, aryloxy, or aryl sulfide species, which may contain saturated or unsaturated cyclic or heterocyclic substituents pendant from the chain or as part of the backbone in the chain, and in which any heteratom present may or may not be directly attached to the aromatic ring;

or R⁵, R⁶, and R⁷are a siloxane having the structure —(CR¹ ₂)_e—[SiR⁴ ₂—O]_f—SiR⁴ ₂—(CH₃)_g— in which the R¹substituent is H or an alkyl group having 1 to 5 carbon atoms and the R⁴substituent independently for each position is an alkyl group having 1 to 5 carbon atoms or an aryl group, and e is 1 to 10 and f is 1 to 50;

and

(c) Z is a linear or branched chain alkyl, alkyloxy, alkyl amine, alkyl sulfide, alkylene, alkyleneoxy, alkylene amine, alkylene sulfide, aryl, aryloxy, or aryl sulfide species, which may contain saturated or unsaturated cyclic or heterocyclic substituents pendant from the chain or as part of the chain, and in which any heteratom present may or may not be directly attached to K; or

(d) Z is a urethane having the structure:

in which each R²independently is an alkyl, aryl, or arylalkyl group having 1 to 18 carbon atoms; R³is an alkyl or alkyloxy chain having up to 100 atoms in the chain, which chain may contain aryl substituents; X is 0, S, N, or P; and v is 0 to 50; or

(e) Z is a siloxane having the structure: —(CR¹ ₂)_e—[SiR⁴ ₂—O]_f—SiR⁴ ₂—(CR¹ ₂)_g— in which the R¹substituent independently for each position is H or an alkyl group having 1 to 5 carbon atoms, and the R⁴substituent independently for each position is an alkyl group having 1 to 5 carbon atoms or an aryl group, and e and g are independently 1 to 10 and f is 1 to 50; or

(f) Z is an ester having the structure:

(g) Z is an ester having the structure:

in which p is 1 to 100, and

(h) Z is an ester having the structure:

in which p is 1 to 100, and

23. A curable adhesive composition according to

claim 18

further comprising a compound having the structure

in which m is 0 or 1 and n is 1-6; and

(b) B is C, S, N, C, C(O), C(O)NH or C(O)N(R⁸), in which R⁸is an alkyl group having 1 to 5 carbon atoms;

(c) K is an aromatic group selected from the group of aromatic groups having the structures:

in which R⁵, R⁶, and R⁷are a linear or branched chain alkyl, alkyloxy, alkyl amine, alkyl sulfide, alkylene, alkyleneoxy, alkylene amine, alkylene sulfide, aryl, aryloxy, or aryl sulfide species, which may contain saturated or unsaturated cyclic or heterocyclic substituents pendant from the chain or as part of the backbone in the chain, and in which any heteratom present may or may not be directly attached to the aromatic ring; or

and

(d) Z is a linear or branched chain alkyl, alkyloxy, alkyl amine, alkyl sulfide, alkylene, alkyleneoxy, alkylene amine, alkylene sulfide, aryl, aryloxy, or aryl sulfide species, which may contain saturated or unsaturated cyclic or heterocyclic substituents pendant from the chain or as part of the chain, and in which any heteratom present may or may not be directly attached to K; or

(e) Z is a urethane having the structure:

(f) Z is a siloxane having the structure: —(CR¹ ₂)_e—[SiR⁴ ₂—O]_f—SiR⁴ ₂—(CR¹ ₂)_g— in which the R¹substituent independently for each position is H or an alkyl group having 1 to 5 carbon atoms, and the R⁴substituent independently for each position is an alkyl group having 1 to 5 carbon atoms or an aryl group, and e and g are independently 1 to 10 and f is 1 to 50; or

(g) Z is an ester having the structure:

in which R³is an alkyl or alkyloxy chain having up to 100 atoms in the chain, which chain may contain aryl substituents; or

(h) Z is an ester having the structure:

in which p is 1 to 100, and

(i) Z is an ester having the structure:

in which p is 1 to 100, and

24. A curable adhesive composition according to

claim 19

further comprising a compound having the structure

[M-X_m]_n-Q in which m is 0 or 1 and n is 1 to 6, and

(a) M is a maleimide moiety having the structure:

in which R¹is H or an alkyl group having 1 to 5 carbon atoms;

and

(d) Q is a urethane having the structure:

(f) Q is an ester having the structure:

(g) Q is an ester having the structure:

in which p is 1 to 100, and

(h) Q is an ester having the structure:

in which p is 1 to 100, and

25. A curable adhesive composition according to

claim 19

further comprising a compound having the structure

in which m is 0 or 1 and n is 1-6; and

and

(e) Q is a urethane having the structure:

(g) Q is an ester having the structure:

(h) Q is an ester having the structure:

in which p is 1 to 100, and

(i) Q is an ester having the structure:

in which p is 1 to 100, and

each R³can independently be a siloxane having the structure —(CR¹ ₂)_e—[SiR⁴ ₂—O]_f—SiR⁴ ₂—(CR¹ ₂)_g— in which the R¹substituent independently for each position is H or an alkyl group having 1 to 5 carbon atoms, the R⁴substituent independently for each position is an alkyl group having 1 to 5 carbon atoms or an aryl group, e and g are independently 1 to 10, and f is 1 to 50.

26. A curable adhesive composition according to

claim 19

further comprising a compound having the structure

[M-Z_m]_n-K in which m is 0 or 1 and n is 1-6, and

(a) M is a maleimide moiety having the structure