UA73314C2 - Method to make profiled and flat roofing sheets - Google Patents
Method to make profiled and flat roofing sheets Download PDFInfo
- Publication number
- UA73314C2 UA73314C2 UA2002021614A UA2002021614A UA73314C2 UA 73314 C2 UA73314 C2 UA 73314C2 UA 2002021614 A UA2002021614 A UA 2002021614A UA 2002021614 A UA2002021614 A UA 2002021614A UA 73314 C2 UA73314 C2 UA 73314C2
- Authority
- UA
- Ukraine
- Prior art keywords
- mixing
- polymer composition
- polyethylene
- roofing sheets
- components
- Prior art date
Abstract
Description
Опис винаходуDescription of the invention
Винахід відноситься до виробництва будівельних матеріалів, конкретніше до способу виготовлення 2 профільованих і плоских покрівельних листів з полімерної композиції призначених для пристрою покрівель і стінових огороджень будинків і споруджень.The invention relates to the production of building materials, more specifically to the method of manufacturing 2 profiled and flat roofing sheets from a polymer composition intended for the device of roofs and wall enclosures of buildings and structures.
Відомий спосіб одержання полімерної композиції для виготовлення тротуарної плитки, покрівельної черепиці (ПА, А, 20487) на основі відходів полімерних матеріалів, який включає змішування їх з цільовими добавками при нагріванні, причому змішування роблять шляхом пластикації при регульованих тиску і температурі відходів 70 різних полімерів з цільовими добавками у виді антипір ну і/або модифікатора, і/або пороутворювача, і/або відходів рослинного чи походження неорганічного.There is a known method of obtaining a polymer composition for the production of paving slabs, roofing tiles (PA, A, 20487) based on waste polymer materials, which includes mixing them with targeted additives during heating, and the mixing is done by plasticizing at controlled pressure and temperature waste 70 different polymers with targeted additives in the form of fire retardant and/or modifier, and/or pore former, and/or waste of vegetable or inorganic origin.
Однак даний спосіб не забезпечує фізико-механічні показники: атмосферостійкість, світлостійкість і довговічність виробу. У виробах, виготовлених по цьому способу відсутні ні добавки, що запобігають їхнє старіння в умовах експлуатації, тобто відсутні світлостабілізатори, що поглинають УФ-випромінювання в комбінації з антиоксидантом чи синергичною сумішшю двох антиоксидантів, а також модифікатор, підвищуючий механічні властивості.However, this method does not provide physical and mechanical indicators: weather resistance, light resistance and durability of the product. In the products made by this method, there are no additives that prevent their aging under operating conditions, that is, there are no light stabilizers that absorb UV radiation in combination with an antioxidant or a synergistic mixture of two antioxidants, as well as a modifier that increases mechanical properties.
Відома полімерна композиція для покрівельних матеріалів |З, А, 1781250), яка включає бутилкаучук, мінеральний наповнювач і барвник. Для готування композиції використовують бутилкаучук і поліетилен низької щільності. Змішані попередньо компоненти вивантажують на вальці, де пластицируют при температурі валків до-вО0си листують. Листи подають на каландр, де композиції" каландрується при температурі валків верхнього 100-1102С, середнього 100-1052С; и нижнього 95-10026.A known polymer composition for roofing materials (Z, A, 1781250), which includes butyl rubber, a mineral filler and a dye. To prepare the composition, butyl rubber and low-density polyethylene are used. The pre-mixed components are unloaded on rollers, where they are plasticized at the temperature of the rollers until they are sheeted. The sheets are fed to the calender, where the composition is calendered at the temperature of the upper rolls of 100-1102С, the middle one of 100-1052С, and the lower one of 95-10026.
Недоліком даної композиції є те, що композиція на основі бутилкаучуку утворюється з низькими фізико-механічними показниками і не відрізняється довговічністю через газопроникність, тому що при різких перепадах температур утворяться здуття і відшарування матеріалу від основи. Крім цього, при виготовленні сч даної композиції необхідна додаткова операція попереднього змішування компонентів у резинозмішувачах при о температурі 110-150 шляхом перемішування протягом 10-25 хвилин.The disadvantage of this composition is that the composition based on butyl rubber is formed with low physical and mechanical parameters and does not differ in durability due to gas permeability, because swelling and detachment of the material from the base will occur with sharp temperature changes. In addition, during the production of this composition, an additional operation of pre-mixing the components in rubber mixers at a temperature of 110-150 o by mixing for 10-25 minutes is necessary.
В основу винаходу покладена задача шляхом створення умов у технологічному процесі розробити спосіб виготовлення профільованих і плоских покрівельних листів, що забезпечує високі фізико-механічні властивості і - 20 довговічність виробу при зменшені протягу технологічного процесу.The invention is based on the task of creating conditions in the technological process to develop a method of manufacturing profiled and flat roofing sheets, which ensures high physical and mechanical properties and - 20 durability of the product with a reduced draft of the technological process.
Ця задача вирішується тим, що в способі виготовлення профільованих і плоских покрівельних листів із - полімерної композиції з наступним формуванням, яке сполучне в полімерній композиції використовують с вторинний поліетилен і/або поліетиленові відходи, причому пластикацію і змішування складових полімерної композиції проводять на змішувально-підігрівальних вальцях, а формування покрівельних аркушів здійснюють на «9 з каландрах і/або в прес-формах. Відповідно заявленому винаходу названа полімерна композиція містить, мас.ч.: М вторинний поліетилен і/або поліетиленові відходи 100 наповнювач 5-50 пігменти 0,5-10,0 « 20 бутилкаучук 1-1,5 -о антиоксидант 0,1-2,5 с світостабілізатор (Уф-абсорбер (УФА) 0,1-2,5 :з» змазувальна речовина (парафін) 0,2-1,0This problem is solved by the fact that in the method of manufacturing profiled and flat roofing sheets from a polymer composition with subsequent formation, which binds in the polymer composition, secondary polyethylene and/or polyethylene waste are used, and plasticization and mixing of the components of the polymer composition are carried out on mixing and heating rollers , and the formation of roofing sheets is carried out on "9" with calenders and/or in molds. According to the claimed invention, the named polymer composition contains, by weight: M secondary polyethylene and/or polyethylene waste 100 filler 5-50 pigments 0.5-10.0 « 20 butyl rubber 1-1.5 -o antioxidant 0.1-2 .5 s light stabilizer (Ultraviolet absorber (UVA) 0.1-2.5:z» lubricant (paraffin) 0.2-1.0
Заявлений спосіб призначений для виготовлення профільованих і плоских покрівельних листів на основі 75 колишньої вживаної поліетиленової плівки. 7 Відповідно до заявленого винаходу застосування як поліолефіна відпрацьованої поліетиленової плівки дає о можливість випускати екологічно чистий покрівельний матеріал з високою стійкістю до агресивних середовищ, морозостійкістю та водовідштовхувальними властивостями. Застосування як наповнювача відходів рослинного о походження, наприклад лузги рису і/або неорганічного походження, дозволяє підвищити фізико-механічні - 20 0 властивості за рахунок армування композиції, а застосування бутилкаучуку як модифікатора у кількості мас.ч.;The claimed method is intended for the production of profiled and flat roofing sheets based on 75% former used polyethylene film. 7 According to the claimed invention, the use of used polyethylene film as a polyolefin makes it possible to produce environmentally friendly roofing material with high resistance to aggressive environments, frost resistance and water-repellent properties. The use of waste of vegetable origin, such as rice husk and/or inorganic origin, as a filler allows to increase the physical and mechanical - 20 0 properties due to the reinforcement of the composition, and the use of butyl rubber as a modifier in the amount of parts by weight;
Їх 1,0-1,5 дозволяє підвищити еластичність і ударну в'язкість. Використання в якості інших хімічних добавок світлостабілізатора (УФ-абсорбера (УФА), антиоксидант і як змащувальної речовини парафіну, запобігає старінню готових виробів у процесі їхньої експлуатації.Their 1.0-1.5 increases elasticity and impact strength. The use of a light stabilizer (UV absorber (UVA), antioxidant and paraffin as a lubricant) as other chemical additives prevents the aging of finished products during their operation.
Пластикація і змішування на вальцях дозволяє застосовувати відходи поліетилену без попередньої 25 підготовки.Plasticizing and mixing on rollers allows the use of polyethylene waste without prior preparation.
ГФ) Полімерну композицію виготовляють на змішувально-підігрівальних вальцях. Поліетиленові відходи й інші юю компоненти подають на поверхню попередньо нагрітих до температури 200-2402С обертових валків, де вони піддаються сумарній дії сил тертя, стиску, напрузі зсуву, а також дії температури поверхні валків.GF) The polymer composition is made on mixing and heating rollers. Polyethylene waste and other waste components are fed to the surface of rotating rolls preheated to a temperature of 200-2402C, where they are subjected to the combined effect of friction, compression, shear stress, as well as the effect of the surface temperature of the rolls.
Пластикація і перемішування з іншими компонентами відбувається до гомогенізації маси. Отримана композиція бо калібрується по товщині і надходить на формування виробу.Plasticization and mixing with other components occurs until the mass is homogenized. The resulting composition is calibrated in terms of thickness and enters the product formation.
Для кращого розуміння даного винаходу приводяться наступні приклади його конкретного виконання.For a better understanding of this invention, the following examples of its specific implementation are given.
Приклад. 10кг, поліетиленових відходів, кг. наповнювача, О,5кг. пігментів і інші хімічні добавки завантажують у межвалковий зазор розігрітих вальців. З полімерної композиції одержують лист розміром 2000х85О0мм. Після 65 гомогенізації отриманої композиції формування роблять у нагрітих прес-формах. При цьому тиск формування -Д-Example. 10 kg, polyethylene waste, kg. filler, O.5 kg. pigments and other chemical additives are loaded into the interroll gap of heated rolls. A sheet with a size of 2000x85O0mm is obtained from the polymer composition. After homogenization of the obtained composition, molding is done in heated molds. At the same time, the formation pressure -D-
складає 10-3З2кгс/см7.is 10-3Z2 kgf/cm7.
Після формування виріб піддають механічній обробці. Формування листів може також проводитися на каландрах.After forming, the product is subjected to mechanical processing. Forming of sheets can also be done on calenders.
У таблиці 1 приведені приклади виготовлення композиції.Table 1 shows examples of composition production.
У таблиці 2 представлені фізико-механічні показники отриманої композиції.Table 2 presents the physical and mechanical parameters of the obtained composition.
Як видно з таблиці 2 найбільш оптимальними є сполуки компонентів у композиціях 2, 3, 4, що дозволяють одержати новий технічний ефект у порівнянні з відомим. Підвищення фізико-механічних властивостей дозволяє застосовувати виріб з даних композицій як покрівельні матеріали, а саме в гарантованій водонепроникності, 70 екологічній безпеці, підвищеній морозостійкості, еластичності, стійкості до атмосферних впливів, стійкості до дії кислот і лугів, з високою межею міцності на вигин і ударною в'язкістю. ів заповновя 111100001805 255060 (076. внтоюсидат 0000000 отолот5|зо свитостебілятор УФ збсорвер 005 ол 162530 змащувальна речовина - парафін|Ом (02 би о БІ см о -As can be seen from Table 2, the most optimal are the combinations of components in compositions 2, 3, 4, which allow obtaining a new technical effect in comparison with the known one. The increase in physical and mechanical properties allows the product from these compositions to be used as roofing materials, namely, in guaranteed waterproofness, 70 environmental safety, increased frost resistance, elasticity, resistance to atmospheric influences, resistance to the action of acids and alkalis, with a high limit of bending strength and shock viscosity iv filling 111100001805 255060 (076. vntoysidat 0000000 otolot5|zo svitostabiliator UV zbsorver 005 ol 162530 lubricant - paraffin|Om (02 bi o BI cm o -
Морозостійкість: кількість циклів перемінного заморо-жування і відтавання без помітних ознак | 40 до до 5 25 20Frost resistance: the number of cycles of alternating freezing and thawing without noticeable signs 40 to to 5 25 20
Не ііі БА БА АЙ ПН По По яNo iii BA BA AY Mon Po Po i
Спосіб, що заявляється, знайде застосування для виробництва покрівельних матеріалів з полімерної о композиції, на основі вторинного поліетилену та відходів поліетилену. со і -The proposed method will be used for the production of roofing materials from a polymer composition based on secondary polyethylene and polyethylene waste. co and -
Claims (1)