TWM650055U - Full-width aluminum film-faced fabric with aluminum film - Google Patents

Abstract

This invention discloses a full-width aluminum film-faced fabric with an aluminum film. The aluminum film-faced fabric is coated with a full-width water-based glue layer on an aluminum film material, and the full-width water-based glue layer is different from the surface heat on one side of the aluminum film material. Press-bond fabrics of equal width, and the process of making the aluminum film surface fabric includes preparing an aluminum film material, coating one surface of the aluminum film material with a full-width water-based glue layer, and The aforementioned aluminum film material with a full-width water-based adhesive layer is dried to form a dry water-based adhesive film material, a semi-finished product of an aluminum film-faced fabric is produced by hot-pressing the aforementioned dry water-based adhesive film material and a fabric of equal width, and a The aforementioned step of leaving the semi-finished aluminum film surface fabric to form an aluminum film surface fabric allows the aluminum film surface fabric with a full width and wide width of aluminum film to have the desired pattern or the effect of a full aluminum film, which can be used to reflect body temperature and enhance appearance. At the same time, it does not affect the feel of the aluminum film surface fabric itself, and can be used to make part or all of clothing, gloves, hats, tents or other waterproof fabrics for full-body equipment. At the same time, it can effectively reduce environmental pollution during production, and can have both Environmental protection effect.

Description

A full-width wide-width aluminum film-faced fabric

This invention relates to the technical field of fabric production, and specifically relates to an aluminum film-faced fabric with a full width and wide width of aluminum film, so that the surface of the aluminum film-faced fabric can have a full-width aluminum film pattern, and the feel of the aluminum film-faced fabric can be close to that of the fabric. The feel of ordinary fabric itself can improve the texture of aluminum film surface fabric, and at the same time, the environmental pollution during the manufacturing process can be greatly reduced.

Press, since the industrial revolution, the development of fabrics has made great progress in terms of materials, tailoring and functions. For example, breathability, perspiration, heat generation, flame retardancy and heat insulation are all worthy of investment in research and development. Since aluminum film has good flame retardant protection and heat insulation properties, in order to cope with people working in flammable or high-temperature environments, the industry has developed aluminum film fabrics or fabrics that are sewn onto the surface of the fabric. This kind of aluminum film Fabrics usually have a certain thickness and are not suitable for ordinary clothing in terms of feel or weight. They are mainly used for special clothing, such as fire-fighting clothing, thermal insulation clothing, etc.

However, in recent years, people's outdoor activities have increased, and they have even challenged different environments such as mountains and deep waters. The good flame retardant protection and heat insulation properties of the aforementioned aluminum film fabric can be used as jackets, pants, gloves, and tents for these outdoor activities. wait. In order to improve the aforementioned problems of poor touch and weight when sewing or pasting aluminum films onto fabrics, currently common aluminum film fabrics are printed using screen printing, which mainly uses screen printing to print the surface of the fabric. Aluminum film pattern, but when printing with screen printing, each layer of the structure must be printed separately, and the printing range depends on the size of the screen frame. When the required fabric is too large, the connections between the edges cannot be accurately connected, resulting in gaps. This further reduces the consistency of the overall printing pattern, and its water-wash resistance is poor. At the same time, the printed aluminum film pattern will also cause cracks due to the expansion and contraction of the fabric, thus losing its flame retardant and heat insulation effects.

In other words, there are several problems with the existing method of adding an aluminum film to the surface of clothing, which reduces its flame retardant and heat-insulating effects. It is also more difficult to form a full-width fabric for use in making different types of clothing, which limits its application. What's more, adding aluminum film to existing fabrics will destroy the feel of the original fabric, making the fabric feel hard and reducing the value of the fabric. How to solve the above problems is what the industry is looking forward to, and it is also the subject of this paper. Those who create and discuss whatever they want.

In view of the above-mentioned shortcomings and needs, the creator used his many years of experience in related technologies and product design and manufacturing to conduct research and creation on the above topics, and actively sought solutions. After continuous efforts in research and trial production, he finally successfully developed A kind of aluminum film surface fabric with full width and wide width, which can overcome the problems of existing fabrics not having full width and poor hand feel.

Therefore, the main purpose of this invention is to provide a full-width aluminum film-faced fabric with an aluminum film, so that the aluminum film-faced fabric can have a full-width pattern or a comprehensive aluminum film, which greatly improves its appearance and can be used for production. Part or all of clothing, gloves, hats, tents or other waterproof fabrics to improve its application and practicality.

In addition, another main purpose of this invention is to provide a method for making a full-width aluminum film-faced fabric with an aluminum film, which can make the feel of the aluminum film-faced fabric close to the feel of the original fabric itself, and can improve the reflective effect. The texture of the fabric can also reduce environmental pollution and has an environmental protection effect.

Based on this, this creation mainly uses the following technical means to specifically achieve the aforementioned purposes and effects. It is to coat an aluminum film material with a full-width water-based glue layer, and the full-width water-based glue layer is different from the aluminum film. The surface of one side of the material is hot-pressed and bonded to a fabric of equal width.

In this way, through the above-mentioned preparation process, the invention makes the aluminum film-faced fabric have a full-width pattern or a comprehensive aluminum film. The aluminum film-faced fabric can be used to make coats, tops, jackets, shoes, pants, and gloves. , tents, hats or waterproof fabrics, and can make the feel of the aluminum film surface fabric close to that of the original fabric before processing. At the same time, it can effectively reduce environmental pollution during production, thereby improving environmental friendliness and greatly improving its quality. Its application range and practicality can effectively improve its economic benefits.

Moreover, this invention uses the following technical means to further achieve the aforementioned purposes and effects; it includes: the aluminum film material has a continuous structure.

The aluminum film material can be selected from colored, electroplated, multi-color, patterned or processed aluminum films.

The full-width water-based glue layer is coated on one side of the aluminum film material using a pattern wheel or a full-width wheel with a complete surface.

The adhesive of the full-width water-based glue layer is a PU mixed glue.

In order to enable your review committee to further understand the composition, characteristics and other purposes of this invention, the following are some preferred embodiments of this invention, which are described in detail with drawings, and at the same time, those who are familiar with this technical field can implement it in detail. .

10:Aluminum film material

11: Protective carrier film

20: Full width water-based rubber layer

30: Dry water glue membrane material

50:fabric

60:Aluminum film surface fabric

S101: Prepare an aluminum membrane material

S102: Coat one surface of the aforementioned aluminum film material with a full-width water-based adhesive layer

S103: Dry the aforementioned aluminum film material with a full-width water-based glue layer to form a dry water-based glue film material

S104: Heat-press the aforementioned dry hydrocolloid film material and a fabric of equal width to produce a semi-finished product of aluminum film-faced fabric

S105: Let the semi-finished product of the aluminum film surface fabric stand still to form an aluminum film surface fabric

Figure 1: A schematic diagram of the three-dimensional appearance of this creation’s full-width aluminum film-covered fabric.

Figure 2: A schematic cross-sectional view of the full-width aluminum film-covered fabric of this creation.

Figure 3: A schematic diagram of the process of creating a full-width aluminum film-covered fabric.

Figure 4: The state of the aluminum film material and fabric before combining in the production method of this creation intention.

Figure 5: Schematic diagram of the cross-sectional state of the dry hydrocolloid membrane formed in the production method of this invention.

Figure 6A: A schematic diagram of the three-dimensional appearance of the dry hydrocolloid film material formed in the production method of this invention, to illustrate the state of it being a patterned glue layer.

Figure 6B: A schematic diagram of the three-dimensional appearance of the semi-dry hydrogel film formed in the production method of this invention, to illustrate the state of it being a comprehensive glue layer.

Figure 7: A schematic diagram of the semi-finished product forming the aluminum film surface fabric in the production method of this creation.

Figure 8A: A schematic diagram of the finished product appearance of the aluminum film-faced fabric formed in the production method of this invention, to illustrate the appearance of the patterned aluminum film.

Figure 8B: A schematic diagram of the appearance of the finished aluminum film-covered fabric formed in the production method of this invention, to illustrate that it is a full-scale aluminum film.

This creation is a full-width wide-width aluminum film-covered fabric. The technical content of this creation is explained below through specific specific implementation forms, so that people familiar with this technology can easily understand the advantages of this creation from the content disclosed in this specification. and efficacy. However, this invention can also be implemented or applied through other different specific implementation forms.

The full-width aluminum film-faced fabric with aluminum film in this invention is shown in Figures 1 and 2. The aluminum film-faced fabric (60) is coated with a full-width water-based glue layer (10) on an aluminum film material (10). 20), and the full-width water-based glue layer (20) is hot-pressed and combined with the aluminum film material (10) with a uniform width of fabric (50). As shown in Figure 3, the full-width wide width has an aluminum film. The manufacturing process of aluminum film surface fabric includes preparing an aluminum film material (S101), coating one surface of the aluminum film material with a full-width water-based glue layer (S102), and coating the aforementioned full-width water-based glue layer The aluminum film material is dried to form a dry hydrogel film material (S103), and the aforementioned dry water glue film material is The adhesive film material and a fabric of equal width are hot-pressed to form a semi-finished product of the aluminum film-faced fabric (S104), and the steps of leaving the aforementioned semi-finished product of the aluminum film-faced fabric to stand to form an aluminum film-faced fabric (S105), etc., so that the fabric It has a full-width pattern or a comprehensive reflective effect and is used to make part or all of clothing, gloves, hats, tents or other waterproof fabrics. The manufacturing process steps are shown in Figures 3 to 8A and 8B. Detailed description is as follows; (a). Preparing an aluminum film material (S101): As shown in Figure 4, prepare in advance to produce an aluminum film material (10). One side surface of the aluminum film material (10) has an Protect the carrier film (11), and the aluminum film material (10) can be made into a continuous type and have the same width and width as the fabric (50) to be combined, and the aluminum film material (10) can be selected from colored materials. , electroplated, multi-color, patterned or processed aluminum film; (b). Coat one of the surfaces of the aforementioned aluminum film material with a full-width water-based glue layer (S102): As shown in Figure 5, the aforementioned continuous type The aluminum film material (10) passes through a water-based glue tank, and a round pattern wheel or a full-surface wheel with a complete surface is used on one side of the aluminum film material (10) different from the protective carrier film (11) The surface is coated with a full-width water-based glue layer (20), so that the surface of the aluminum film material (10) has a full-width water-based glue layer (20) (as shown in Figure 6A) or a pattern-like one. Full-width water-based glue layer (20) [shown in Figure 6B]; (c). The aforementioned aluminum film material with full-width water-based glue layer is dried to form a dry water-based glue film material (S103): Figure 5, As shown in Figure 6A and Figure 6B, after completing the coating of the full-width water-based glue layer (20) of the aforementioned aluminum film material (10), the aluminum film material (10) is passed through an oven equipment to make the aluminum film material (100°C) 10) The full-width water-based glue layer (20) on one side surface is in a dry state to form a continuous dry water-based glue film material (30), and the film is rolled into a roll shape, wherein the full-width water-based glue layer The adhesive of (20) is a PU mixed glue; (d). S104: Hot-press the aforementioned dry hydrogel membrane material and a fabric of equal width to produce a semi-finished product of aluminum film-faced fabric (S104): as shown in Figure 7 As shown, after completing the aforementioned continuous drying hydrocolloid film material (30), hot pressing technology is used to make the dry hydrocolloid film material (30) and the corresponding The overlapping and combining of equal-width fabrics (50) at a hot-pressing temperature of 80°C to 150°C can effectively improve the firming effect of the full-width water-based adhesive layer (20) and the fabric (50), thereby forming an aluminum film surface The semi-finished product of the fabric (60); and (e). The semi-finished product of the aforementioned aluminum film-faced fabric is allowed to stand to form an aluminum film-faced fabric (S105): as shown in Figure 7, Figure 8A and Figure 8B, the aforementioned hot-pressed combination The semi-finished product of the aluminum film surface fabric (60) is left to rest. The method of resting is as follows: the semi-finished product of the aluminum film surface fabric (60) is allowed to stand until it reaches normal temperature, then the temperature is raised to between 30°C and 75°C for 24 hours, and then left to stand at ambient temperature. Let it dry completely at normal temperature, and finally remove the protective carrier film (11) of the aluminum film material (10), so that the entire width of the aluminum film surface fabric (60) becomes a full-shaped aluminum film material (10) [ As shown in Figure 8A] or as a patterned aluminum film material (10) [as shown in Figure 8B], the aluminum film surface fabric (60) is completed, and its appearance and cross-section are as shown in Figure 1, Figure 2 shown.

Through the above preparation process, the aluminum film surface fabric (60) is provided with a full-width or patterned aluminum film, so as to utilize the radiant heat blocking effect of the aluminum film surface fabric (60) to provide excellent permanent barrier. It has flame protection and heat insulation properties and can protect the human body from high temperature damage in dangerous environments. The aluminum film surface fabric (60) can be used to make coats, tops, jackets, shoes, pants, gloves, tents, hats or waterproof All or part of the fabric can make the feel of the aluminum film surface fabric (60) close to the feel of the original fabric (50) before processing. At the same time, it can effectively reduce environmental pollution during production, thereby improving environmental friendliness.

The above-mentioned embodiments are only preferred implementation modes of this invention and should not be used to limit the scope of protection of this invention. Any changes or modifications without substantive meaning made in the main design ideas and spirit of this invention will not solve the technical problems they solve. If the problem is still consistent with this creation, it should be included in the protection scope of this creation.

From this, it can be understood that this creation is an extremely creative creation. It not only effectively solves the problems faced by practitioners, but also greatly improves the effectiveness. There is no identical or similar product creation or public use in the same technical field. , and at the same time has the effect of improving, so this creation Having met the requirements of "novelty" and "progress" for a new type patent, an application for a new type patent is filed in accordance with the law.

10:Aluminum film material

20: Full width water-based rubber layer

50:fabric

60:Aluminum film surface fabric

Claims (5)

A full-width wide-width aluminum film-faced fabric with an aluminum film, which is coated with a full-width water-based glue layer on an aluminum film material, and a uniform width is bonded to the surface of the full-width water-based glue layer on one side different from the aluminum film material. wide fabric. A full-width wide-width aluminum film-faced fabric with an aluminum film as described in claim 1, wherein the aluminum film material has a continuous structure. The full-width wide-width aluminum film-covered fabric with aluminum film as described in claim 1 or 2, wherein the aluminum film material can be selected from colored, electroplated, multi-color, patterned or processed aluminum films. The full-width wide-width aluminum film-faced fabric with aluminum film as described in claim 1, wherein the full-width water-based glue layer is applied to one side surface of the aluminum film material using a patterned wheel or a full-surface wheel with a complete surface. Apply full width coating. A full-width wide-width aluminum film-covered fabric with an aluminum film as described in claim 1 or 4, wherein the adhesive of the full-width water-based glue layer is a PU mixed glue.

Images