TWI824084B - 化學暖暖包 - Google Patents
化學暖暖包 Download PDFInfo
- Publication number
- TWI824084B TWI824084B TW108145788A TW108145788A TWI824084B TW I824084 B TWI824084 B TW I824084B TW 108145788 A TW108145788 A TW 108145788A TW 108145788 A TW108145788 A TW 108145788A TW I824084 B TWI824084 B TW I824084B
- Authority
- TW
- Taiwan
- Prior art keywords
- moisture
- heating
- aforementioned
- foot
- sole
- Prior art date
Abstract
本發明之目的在提供一種化學暖暖包，其即便局部使用在身體部位，亦可對全身賦予溫熱效果。
化學暖暖包使用含有還原鐵粉作為氧化性金屬的發熱部，且將其收納在含有透濕度為650~1200g/m2
．day之透濕片的收納體，藉由將該化學暖暖包配設於足底部之至少一部分而使用，可賦予身體全體溫熱效果，不僅是足底部，可於手部、足部、肩部等促進血液循環。
Description
發明領域
本發明是有關於一種化學暖暖包，其配設於足底部之至少一部分而使用，可賦予全身優異之溫熱效果。
背景技術
習知化學暖暖包(所謂拋棄式暖暖包)廣為使用的是利用鐵等被氧化性金屬藉由與氧的接觸而產生氧化熱的發熱機制，並將含有被氧化性金屬的發熱部收納於具有透濕性的收納體。
以往，為了能簡便地獲得溫熱效果，化學暖暖包依照應用部位的不同，開發出拿在手上使用的形式、放入口袋中使用的形式、黏貼在衣服或皮膚上的形式等各式各樣者。又，以往為了謀求化學暖暖包的發熱性或使用感的提升，嘗試改善發熱體或收納體(例如參照專利文獻1及2等)。
然而，習知化學暖暖包中，即便可對所應用的身體部位局部賦予溫熱效果，亦無法藉由局部應用的化學暖暖包賦予身體整體溫熱效果。
先前技術文獻
專利文獻
專利文獻1：日本特開2003-265513號公報
專利文獻2：日本特開2007-61338號公報
發明概要
本發明之目的在提供一種化學暖暖包，其即便局部使用在身體部位，亦可對全身賦予溫熱效果。
本案發明人為了解決前述課題進行精心探討時發現，化學暖暖包使用含有還原鐵粉作為氧化性金屬的發熱部，且將其收納在含有透濕度為650~1200g/m2．day之透濕片的收納體，藉由將該化學暖暖包配設於足底部之至少一部分而使用，可賦予身體整體溫熱效果，不僅是足底部，可於手部、足部、肩部等促進血液循環。本發明是根據前述見解，藉由進一步反覆探討而完成。
即，本發明提供下揭態樣之發明。
第1項.一種化學暖暖包，其配設於足底部之至少一部分而使用，且具有：發熱部，其產生傳導至足底部的熱；及收納體，其收納前述發熱部，且於至少一面含有透濕片；前述發熱部含有還原鐵粉，且前述透濕片之透濕度為650~1200g/m2．day。
第2項.如第1項之化學暖暖包，其中發熱部更含有氧化促進劑及水。
第3項.如第1項或第2項之化學暖暖包，其中前述透濕片為具有細孔的通氣性樹脂層與纖維基材之積層片。
第4項.如第1項至第3項中任一項之化學暖暖包，其係於前述收納體之一面上設置有黏著層。
第5項.如第1項至第4項中任一項之化學暖暖包，其用以對手部、足部及肩部賦予溫熱效果。
第6項.一種化學暖暖包之用途，其用以製造配設於足底部之至少一部分而使用的溫熱工具，且前述化學暖暖包具有：發熱部，其產生傳導至足底部的熱；及收納體，其收納前述發熱部，且於至少一面含有透濕片；前述發熱部含有還
原鐵粉，且前述透濕片之透濕度為650~1200g/m2．day。
第7項.一種溫熱方法，包含有將化學暖暖包配設於需要溫熱效果者的足底部之至少一部分的步驟，且前述化學暖暖包具有：發熱部，其產生傳導至足底部的熱；及收納體，其收納前述發熱部，且於至少一面含有透濕片；前述發熱部含有還原鐵粉，且前述透濕片之透濕度為650~1200g/m2．day。
依據本發明之化學暖暖包，藉由應用在足底部，可促進手部、足部、肩部等的血液循環，作為能賦予身體全體優異溫熱效果的溫熱工具是有用的。
1:收納體
11:收納體中收納發熱體的收納部
12:收納體中構成黏合部分的端部(密封部)
2:基底
3:雙面膠帶
4:化學暖暖包
X:頂點
Y:端邊
圖1是俯視本發明中使用的收納體的一個態樣之示意圖。
圖2A是俯視試驗例中使用的透濕片與非透濕片之示意圖。圖2B是俯視試驗例中所製造的化學暖暖包之示意圖。
圖3A是從化學暖暖包4側俯視試驗例中使用的黏貼用試樣之示意圖。圖3B是從雙面膠帶3側俯視試驗例中使用的黏貼用試樣之示意圖。
用以實施發明之形態
本發明之化學暖暖包是配設於足底部之至少一部分而使用的化學暖暖包，特徵在於具有：發熱部，其產生傳導至足底部的熱；及收納體，其收納前述發熱部，且於至少一面含有透濕片；前述發熱部含有還原鐵粉，且前述透濕片之透濕度為650~1200g/m2．day。以下，詳述本發明之化學暖暖包。
[發熱部]
本發明之化學暖暖包中，為了產生傳導至足底部的熱，具備含有還原鐵粉的發熱部。藉由選擇還原鐵粉作為利用與氧的接觸而產生氧化熱的被氧化性金
屬，且使用後述具有特定透濕性的收納體，若配設於足底部之至少一部分而使用，則可賦予全身溫熱效果。
本發明中，所謂「發熱部」為產生傳導至足底部的熱之部位，並藉由含有被氧化性金屬及視需要摻合的其他成分之發熱性組成物構成。
所謂還原鐵粉為利用氫等將氧化鐵或鐵鹽等鐵化合物還原而製作的粉末狀鐵。
本發明中使用的還原鐵粉之粒徑範圍並無特殊限制，例如可舉例大於10μm且800μm以下。從更進一步地提升對全身的溫熱效果之觀點來看，還原鐵粉之粒徑範圍宜舉例大於10μm且500μm以下，更佳為大於10μm且300μm以下，尤佳為大於10μm且60μm以下。本發明中，還原鐵粉之粒徑範圍為根據日本工業規格「JIS 8815-1994篩分試驗方法通則」所規範方法求得之值。
本發明中使用的還原鐵粉之表觀密度並無特殊限制，例如可舉例1.0~4.0g/cm2，較佳為1.5~4.0g/cm2，更佳為2.0~4.0g/cm2。本發明中，表觀密度為根據日本工業規格「JIS Z 2504：2012金屬粉-表觀密度測定方法」所規範方法求得之值。
本發明中，發熱部中還原鐵粉之含量例如可舉例20~80重量%，較佳為25~70重量%，更佳為30~60重量%。
又，本發明中，為了氧的維持抑或對還原鐵粉的氧供給之促進，發熱部中亦可含有氧化促進劑。關於氧化促進劑之種類，只要能維持氧以及對還原鐵粉供給氧，則無特殊限制，例如可列舉：活性碳、碳黑、乙炔黑、竹炭、木炭、咖啡渣炭、石墨、煤、椰殼炭、瀝青炭、泥炭、褐煤等碳材料。該等氧化促進劑可單獨使用1種，並且亦可組合使用2種以上。
該等氧化促進劑中，宜舉例活性碳、碳黑、竹炭、木炭、咖啡渣炭，更佳為活性碳。
氧化促進劑之形狀並無特殊限制，從發熱效率之觀點來看，宜舉例粉末狀、粒狀或纖維狀，更佳為粉末狀。
當發熱部中含有氧化促進劑時，發熱部中氧化促進劑之含量並無特殊限制，例如可舉例1~30重量%，較佳為3~25重量%，更佳為5~23重量%。
又，為了促進還原鐵粉的氧化反應，發熱部中宜含有水。水可使用蒸餾水、離子交換水、純水、超純水、自來水、工業用水等中任一者。
當發熱部中含有水時，發熱部中水之含量並無特殊限制，例如可舉例5~50重量%，較佳為10~40重量%，更佳為15~35重量%。
又，為了維持水而將水有效率地供給至氧化反應場，發熱部中亦可含有保水劑。保水劑之種類並無特殊限制，例如可列舉：蛭石(vermiculite)、波來鐵、矽酸鈣、矽酸鎂、高嶺土、滑石、膨潤石、雲母、膨土、碳酸鈣、矽膠、氧化鋁、沸石、二氧化矽、矽藻土等無機多孔質物質；紙漿、木粉(鋸屑)、棉、澱粉類、纖維素類等有機物；聚丙烯酸系樹脂、聚磺酸系樹脂、馬來酸酐系樹脂、聚丙烯醯胺系樹脂、聚乙烯醇系樹脂、聚乙烯氧化物系樹脂、聚天冬胺酸系樹脂、聚麩胺酸系樹脂、聚海藻酸系樹脂等吸水性樹脂等。該等保水劑可單獨使用1種，並且亦可組合使用2種以上。
該等保水劑中，宜舉例蛭石、聚丙烯酸系樹脂、木粉、紙漿；更佳為蛭石、聚丙烯酸系樹脂。又，當保水劑使用無機多孔質物質時，亦可於發熱性組成物中確保空氣之流通。
當發熱部中含有保水劑時，關於發熱部中保水劑之含量，其含量並無特殊限制，例如可舉例1~20重量%，較佳為3~15重量%，更佳為3~7重量%。
又，為了促進還原鐵粉的氧化反應，發熱部中亦可含有水溶性鹽類。水溶性鹽類之種類並無特殊限制，例如可列舉：鹼金屬(鈉、鉀等)、鹼土類金屬(鈣、鎂等)或重金屬(鐵、銅、鋁、鋅、鎳、銀、鋇等)之硫酸鹽、碳酸氫鹽、
氯化物或氫氧化物等。該等水溶性鹽類中，從導電性、化學穩定性等觀點來看，宜舉例氯化鈉、氯化鉀、氯化鈣、氯化鎂、氯化鐵(II、III)等氯化物，更佳為氯化鈉等。該等水溶性鹽類可單獨使用1種，並且亦可組合使用2種以上。
當發熱部中含有水溶性鹽類時，關於發熱部中水溶性鹽類之含量，其含量並無特殊限制，例如可舉例0.1~10重量%，較佳為0.5~7重量%，更佳為0.5~5重量%。
發熱部中更可視需要含有還原鐵粉以外的被氧化金屬、螯合劑、香料、增稠劑、賦形劑、界面活性劑、氫生成抑制劑等其他添加劑。
使用作為發熱部的發熱性組成物可藉由混合預定量的前述成分來調製。使用作為發熱部的發熱性組成物之調製可於氧存在下進行，惟宜於減壓下或惰性氣體環境下調製。
本發明之化學暖暖包中，每一個收納體所收納發熱部量可於能應用在足底部的範圍內適當地設定，可舉例如5~30g，較佳為10~20g，更佳為12~18g。
[收納體]
本發明之化學暖暖包具有用以收納發熱部的收納體。本發明之化學暖暖包中，為了在使用時將氧或水蒸氣供給至發熱部，收納體於至少一面具有透濕度為650~1200g/m2．day的透濕片。藉由依此併用具有特定透濕度的透濕片之收納體以及含有還原鐵粉的發熱部，即便應用在足底部，亦可對全身賦予溫熱效果。
本發明中使用的透濕片之透濕度為650~1200g/m2．day即可，從更進一步地提升對全身的溫熱效果之觀點來看，該透濕片之透濕度宜舉例680~1150g/m2．day，更佳為700~1100g/m2．day。本發明中，透濕度為藉由日本工業規格「JIS Z0208-1975防濕包裝材料之透濕度試驗方法(杯式法)所規範方法於溫度40℃、濕度90%RH之條件下測得之值。
關於透濕片之素材，只要能具備前述透濕度，則無特殊限制，宜至少藉由通氣性樹脂層(具有細孔的樹脂層)來形成，從提升使用感之觀點來看，更宜為通氣性樹脂層與纖維基材之積層片。通氣性樹脂層與纖維基材之積層片只要從收納體的內部朝外部依序積層通氣性樹脂層及纖維基材即可。
通氣性樹脂層的構成樹脂並無特殊限制，例如可列舉：聚乙烯、聚丙烯、乙烯-醋酸乙烯酯共聚物、聚對苯二甲酸乙二酯、聚丙烯腈、乙烯-乙烯醇共聚物、聚醯胺、聚胺甲酸乙酯、聚苯乙烯、聚乙烯醇、聚氯乙烯、聚偏二氯乙烯、聚碳酸酯等。該等樹脂中，宜舉例聚乙烯、聚丙烯、乙烯醋酸乙烯酯共聚物。
又，通氣性樹脂層只要是設置有用以確保通氣性之細孔的樹脂膜即可。設置於樹脂膜的細孔之形狀、大小及數量可依照收納體所應具備透濕度適當地設定。
通氣性樹脂層之厚度可依照透濕片之層構造等適當地設定，例如可舉例15~150μm，較佳為30~100μm，更佳為50~80μm。
使用於透濕片的纖維基材具體可舉例不織布、織布。從使用感等觀點來看，宜舉例不織布。纖維基材232之素材並無特殊限制，例如可列舉：聚對苯二甲酸乙二酯、聚對苯二甲酸丁二酯、耐綸、聚丙烯、聚乙烯、維尼綸、嫘縈、丙烯酸、乙酸酯、聚氯乙烯等合成纖維；棉、麻、絲、紙等天然纖維；該等之混合纖維等。該等素材中，從提升使用感之觀點來看，宜舉例聚對苯二甲酸乙二酯、耐綸、聚丙烯，更佳為聚對苯二甲酸乙二酯、耐綸。
纖維基材之單位面積質量可依照透濕片之層構造等適當地設定，例如可舉例1~100g/m2，較佳為5~70g/m2，更佳為10~50g/m2。
通氣性樹脂層與纖維基材之積層可利用乾式層合、擠壓層合、熱層合等公知層合方法來進行。
本發明中使用的收納體只要於至少一面含有前述透濕片即可。本發明中使用的收納體宜為以下形狀：具有配置於足底部側的面以及配置於與其為相反側的面二面，當依此設為具有二面之形狀時，全面可由前述透濕片形成，又，亦可一面由前述透濕片形成，另一面則藉由低透濕度的片材(以下，有時標示為「非透濕片」)來形成。
前述非透濕片之透濕度例如可舉例10g/m2．day以下，且宜為5g/m2．day以下，較佳為2g/m2．day以下，更佳為1g/m2．day以下，尤佳為0g/m2．day。
非透濕片之素材並無特殊限制，宜舉例未設置有細孔的樹脂片。構成非透濕片的樹脂片之構成樹脂並無特殊限制，例如可列舉：聚乙烯、聚丙烯、乙烯-醋酸乙烯酯共聚物、聚對苯二甲酸乙二酯、聚丙烯腈、乙烯-乙烯醇共聚物、聚醯胺、聚胺甲酸乙酯、聚苯乙烯、聚乙烯醇、聚氯乙烯、聚偏二氯乙烯、聚碳酸酯等。該等樹脂中，宜舉例聚乙烯、聚丙烯、乙烯醋酸乙烯酯共聚物。
構成非透濕片的樹脂片之厚度可依照非透濕片之層構造等適當地設定，例如可舉例115~250μm，較佳為130~200μm，更佳為150~180μm。
又，非透濕片亦可視需要在未設置有細孔的樹脂片上積層纖維基材。於非透濕片中使用的纖維基材之素材或單位面積質量等與前述透濕質片材中所例示者相同。
又，於收納體之一面上宜設置有黏著層，以於使用時能固定在足底部。收納體中，當兩面皆由前述透濕片形成時，只要在其中一透濕片之表面設置黏著層即可，又，當一面由透濕片形成且另一面由非透濕片形成時，只要在非透濕片之表面設置黏著層即可。
黏著層可設置於收納體之一面的全面上，亦可局部設置於收納體
之一面上。
黏著層可使用黏著劑來形成。所謂黏著劑為以下組成物：含有於油劑或其他溶劑等之存在下顯示黏著性的聚合物(黏著性聚合物)，該黏著性聚合物分散或溶解於油劑或其他溶劑等中，呈現出黏著性。黏著劑中所含黏著性聚合物之種類或組成為公知，本發明中，可使用習知拋棄式暖暖包之黏著層中所使用之黏著劑。黏著劑之種類具體可舉例橡膠系黏著劑、丙烯酸系黏著劑、聚矽氧系黏著劑、胺甲酸乙酯系黏著劑等。
黏著層之塗佈量例如可舉例5~40g/m2，較佳為10~30g/m2，更佳為15~25g/m2。
又，當收納體之一面上設置有黏著層時，亦可於黏著層之外側表面設置能脫模的脫模層。當設置有脫模層時，可防止保存中的黏著層之乾燥、防止黏著層之黏著所致處理性之降低等。
脫模層可舉例：聚對苯二甲酸乙二酯、聚丙烯腈、乙烯-乙烯醇共聚物、聚丙烯等樹脂膜；施以聚矽氧加工等賦予脫模性加工的紙等。又，即便是在使用樹脂膜作為脫模層之情形時，亦可施行聚矽氧加工等賦予脫模性加工。
當收納體是由配置於足底部側的面以及配置於與其為相反側的面二面所構成之形狀時，藉由將前述透濕片2片抑或前述透濕片1片與前述非透濕片1片黏合收納發熱部的區域之周圍而形成。
黏合前述透濕片2片抑或前述透濕片1片與前述非透濕片1片的方法並無特殊限制，舉例言之，當前述透濕片或非透濕片中使用熱熔接性樹脂時，可利用該熱熔融性樹脂使端部熱熔接(熱封)，又，亦可使用接著劑來黏合端部。
收納體之形狀只要設定為能配設於足底部之至少一部分即可，可依照應用的足底部之部位適當地設定。舉例言之，若為從腳趾背之一部分遍及
趾背之根部部分來配設之情形，則可舉例如圖1所示，平視形狀為從直線狀之端邊朝一方向延伸且另一端邊構成圓形之形狀。又，收納體的一個形態可舉例略呈扁平狀，惟收納體中配置於足底部側的面可設置有凹部或凸部等，以迎合足底部之形狀。
收納體中收納前述發熱部的部分之面積(平視時收納有發熱部的部分之面積)例如可舉例20~180cm2，較佳為30~70cm2，更佳為35~60cm2。
[包裝形態]
本發明之化學暖暖包被包裝在具有氧屏蔽性的包裝材，且於未與空氣接觸的狀態下提供。使用時配設於足底部之至少一部分，藉此，發熱部會與空氣接觸，並開始發熱。
[使用方法]
本發明之化學暖暖包配設於足底部之至少一部分而使用。本發明之化學暖暖包藉由局部應用在足底部之至少一部分，可對手部、足部、肩部等全身賦予溫熱效果，並促進全身的血液循環。又，本發明之溫熱治療用之醫療機器可對全身賦予溫熱效果，因此，亦可在促進全身的血液循環、改善冰冷感、改善疲勞感、改善肌肉僵硬、活化胃腸蠕動、賦活免疫等目的下使用。
本發明之化學暖暖包可於足底部直接固定在皮膚上而使用，又，亦可於穿著襪子的狀態下固定在足底部而使用。又，本發明之化學暖暖包亦可固定在鞋子或拖鞋的鞋墊，藉由穿上該鞋子或拖鞋來使用。
本發明之化學暖暖包所應用足底部之部位並無特殊限制，例如可列舉：腳趾腹、腳趾腹之根部、足弓、屈小指短肌部分、足跟等。又，本發明之化學暖暖包只要設計成配設於足底部之至少一部分即可，舉例言之，可設計成配設於足底部之一部分，且同時亦配設於腳趾之表面部分或腳背之至少一部分。從更進一步地提升對全身的溫熱效果之觀點來看，配設本發明之化學暖暖
包的足底部之部位宜舉例至少腳趾腹之根部部分，更佳為腳趾腹之至少一部分與腳趾腹之根部部分，尤佳為從腳中趾之前端起0~1cm左右的部位朝足跟側到9~20cm左右的區域之足底部。
實施例
以下，列舉實施例等，具體說明本發明，惟本發明並未因該等而有任何限制。
試驗例1：擴及全身的溫熱效果之驗證試驗
1.化學暖暖包之調製
準備表1所示各透濕度的透濕片A~F。各透濕片之形狀如圖2A所示。另，各透濕片之透濕度是藉由日本工業規格「JIS Z0208-1975防濕包裝材料之透濕度試驗方法(杯式法)所規範方法，於溫度40℃、濕度90%RH之條件下進行測定。另，所準備的透濕片A~F，皆為利用乾式層合接著有聚對苯二甲酸乙二酯製造的水針不織布(單位面積質量30g/m2)與設置有細孔的聚乙烯膜(厚度60μm)之積層片，且透濕度可利用聚乙烯膜的細孔大小與數量來控制。
又，準備透濕度為0g/m2．day的非透濕片(厚度159μm)。非透濕片之形狀如圖2A所示。於該非透濕片之一面上塗佈黏著劑而構成21g/m2後，積層脫模片。
又，另外準備表2所示之各種鐵粉。另，鐵粉A是利用開口180μm的篩孔將鐵粉(「MR2」，(同和鐵粉工業股份有限公司製造)分級，藉由回收殘留於該篩孔的鐵粉來調製。鐵粉B是利用開口45μm的篩孔將鐵粉(「MR2」，(同和鐵粉工業股份有限公司製造)分級，藉由回收已通過該篩孔的鐵粉來調製。鐵粉C是使用鐵粉(「80AF」，(神戶製鋼所股份有限公司製造)。鐵粉D是利用開口180μm的篩孔將鐵粉(「80AF」，(神戶製鋼所股份有限公司製造)分級，藉由回收殘留於該篩孔的鐵粉來調製。另，表觀密度是藉由日本工業規格「JIS Z 2504：2012金屬粉-表觀密度測定方法」所規範方法進行測定。
使用前述各鐵粉，調製表3所示組成的發熱性組成物，並使用作為發熱體。以透濕片之不織布側與積層於非透濕片的黏著層分別構成外側之方式配置，利用前述透濕片與前述非透濕片夾持所調製的發熱體13g。於該狀態下，以平視下構成如圖2B之方式將兩片材的周緣部(寬度0.5cm)熱熔接，製造出於收納部中收納有發熱體的化學暖暖包(圖2B中包圍周圍的黑線部為熱熔融的周緣部)。另，所製造的化學暖暖包之收納體中，收納發熱部的部分之面積(平視時收納有發熱部的部分之面積)為57cm2。
[表3]
所製造的化學暖暖包敏捷地收納於非透氣性密封袋中而密封。另，所製造的化學暖暖包中，透濕片與發熱體中使用的鐵粉之組合如表4所示。
2.對全身的溫熱效果之評價
(1)黏貼用試樣之調製
切下市售新品襪子(構成素材：聚酯53重量%、耐綸42重量%及聚胺甲酸乙酯5重量%)的足底部位，取得長方形(長10cm、寬8cm)之底布。於該基底之一面上黏合前述中製得的化學暖暖包之黏著層側。再者，於該基底的另一面之兩端黏合2條雙面膠帶，製得黏貼用試樣。圖3A中顯示從化學暖暖包4側平視黏貼用試樣的圖，圖3B中顯示從雙面膠帶3側平視黏貼用試樣的圖。
(2)溫熱效果之測定
以29歲男性1名為被試驗者，利用以下方法進行血流量之測定。首先，將測定室內設定為溫度20℃、濕度30%RH，為了確認溫度及濕度穩定，將房間放置約1小時。接著，讓僅穿著襪子與游泳褲的被試驗者進入測定室，作成已脫下襪子的狀態而適應30分鐘後，利用都卜勒(Doppler)血流計(英特閣(INTEGRAL)股份有限公司製造「PeriScan」)，測定足部(右腳踝部分)、手部(右手背部分)及肩部(右肩之背面部分)的血流(黏貼前的血流)(黏貼前的血流量)。接著，圖3A所示頂點X之部分設為構成左腳底的中趾前端起靠近足跟1cm之部分，以頂點X構成趾側、端邊Y構成足跟側之方式，透過雙面膠帶3將黏貼用試樣黏合在腳底的趾
背到根部之區域，並維持該狀態60分鐘。
將黏貼用試樣黏合在足底部後經過60分鐘後，利用都卜勒血流計測定足部(右腳踝部分)、手部(右手背部分)及肩部(右肩之背面部分)的血流(黏貼後的血流)。從黏貼後的血流值減去黏貼前的血流值，藉此算出使用後的血流變化量。
又，以相同的被試驗者，將黏貼用試樣之黏貼部位變更為左腳底之足跟，利用相同方法進行血流之測定。另，當黏貼用試樣黏合在左腳底之足跟時，設為圖3A所示之頂點X配置於足跟之頂點側、端邊Y配置於腳趾側。
再者，以相同的被試驗者，將黏貼用試樣之黏貼部位變更為左肩，利用相同方法進行血流之測定。另，當黏貼用試樣黏合在左肩時，設為圖3A所示之頂點X配置於左肩之頸側、端邊Y配置於左腕側。
3.結果
表4中顯示結果。使用含有還原鐵的發熱體與透濕度為650~1200g/m2．day的透濕片之化學暖暖包中，若應用在足底部，則可確認手部、足部及肩部全體的血流量之增加，能賦予全身優異之溫熱效果(實施例1~3)。相對於此，當使用含有未還原鐵的發熱體時，不論透濕片之透濕度，若應用在足底部，手部或足部的血流量並不會增加(比較例1~5)。又，即便使用含有還原鐵的發熱體，使用透濕度未滿足650~1200g/m2．day的透濕片之化學暖暖包中，即便應用在足底部，賦予足部或肩部的溫熱效果亦屬有限(比較例6)。再者，比較例6之化學暖暖包中，即便應用在肩部，亦無法增加手的血流量。
Claims (6)
- 一種化學暖暖包，其配設於足底部之至少一部分而使用，且具有：發熱部，其產生傳導至足底部的熱；及收納體，其收納前述發熱部，且於至少一面含有透濕片；前述發熱部是以發熱性組成物構成，前述發熱性組成物含有還原鐵粉及5~50重量%的水，且前述透濕片之透濕度為650~1200g/m2．day。
- 如請求項1之化學暖暖包，其中構成發熱部之發熱性組成物更含有氧化促進劑。
- 如請求項1或2之化學暖暖包，其中前述透濕片為具有細孔的通氣性樹脂層與纖維基材之積層片。
- 如請求項1或2之化學暖暖包，其係於前述收納體之一面上設置有黏著層。
- 如請求項1或2之化學暖暖包，其用以對手部、足部及肩部賦予溫熱效果。
- 一種化學暖暖包之用途，其用以製造配設於足底部之至少一部分而使用的溫熱工具，且前述化學暖暖包具有：發熱部，其產生傳導至足底部的熱；及收納體，其收納前述發熱部，且於至少一面含有透濕片；前述發熱部是以發熱性組成物構成，前述發熱性組成物含有還原鐵粉及5~50重量%的水，且前述透濕片之透濕度為650~1200g/m2．day。