TW202330806A - 光散射油墨組合物、以及使用該組合物之彩色濾光片和圖像顯示裝置 - Google Patents
光散射油墨組合物、以及使用該組合物之彩色濾光片和圖像顯示裝置 Download PDFInfo
- Publication number
- TW202330806A TW202330806A TW111148363A TW111148363A TW202330806A TW 202330806 A TW202330806 A TW 202330806A TW 111148363 A TW111148363 A TW 111148363A TW 111148363 A TW111148363 A TW 111148363A TW 202330806 A TW202330806 A TW 202330806A
- Authority
- TW
- Taiwan
- Prior art keywords
- light
- scattering
- ink composition
- scattering ink
- composition according
- Prior art date
Abstract
本發明涉及一種光散射油墨組合物、包含使用該光散射油墨組合物製造的光散射層的彩色濾光片以及包括該彩色濾光片的圖像顯示裝置，該光散射油墨組合物包含平均粒徑為150奈米至300奈米的第一散射粒子、平均粒徑為10奈米至90奈米的第二散射粒子、光聚合性化合物、以及光聚合引發劑，其中該第一散射粒子是二氧化鈦（TiO
2）。
Description
本發明係關於一種光散射油墨組合物、包含該光散射油墨組合物的彩色濾光片和圖像顯示裝置。
最近，作為實現彩色濾光片的方法中的一種，應用了使用顏料分散型感光性樹脂的顏料分散法。然而，從光源照射的光在透過彩色濾光片的過程中，光的一部分被彩色濾光片吸收而存在以下問題：光效率降低，並且還因包含在彩色濾光片中的顏料的特性而使顏色再現性降低。
作為解決這種問題的解決方案，已經提出了使用量子點的彩色濾光片。例如，韓國專利公開號10-2009-0036373揭露了藉由用由量子點螢光體製成的發光層代替現有的彩色濾光片來提高發光效率，從而可以提高顯示裝置的顯示品質。
然而，在包含量子點的彩色濾光片的情況下，存在以下問題：隨著量子點的效率（特別是藍色量子點的效率）降低，彩色濾光片的性能可能會略有下降，並且由於藍色量子點價格高，從而增加了整體製造成本。
因此，提出了一種彩色濾光片，其使用發射藍光的光源，該彩色濾光片具備含有紅色量子點粒子的紅色圖案層和含有綠色量子點粒子的綠色圖案層，在與藍色圖案層對應的位置具備不包含量子點粒子的透明圖案層，使紅色量子點粒子發射紅光，綠色量子點粒子發射綠光，並且透明圖案層使藍光原樣透過而呈現藍色。
這種透明圖案層包括散射粒子以確保透射光的均勻性。然而，當散射粒子的含量增加時，存在透射率降低的問題。作為替代方案，當散射粒子的含量減少時，存在無法獲得充分的散射（霧度）特性的問題。
此外，如果透明圖案層採用噴墨方法製作，則可以大幅減少製造製程、時間和成本。然而，由於現有的油墨組合物是含有溶劑的溶劑型，因此存在與鄰接的像素混色、形成塗膜後塗膜的平坦性降低的問題。作為替代方案，在製造不包含溶劑的無溶劑型油墨組合物的情況下，除了黏度變高而導致噴射性變差之外，還存在由於長時間存放時粒徑分佈的不均勻變化而導致的可靠性相關問題。
因此，為了解決上述問題而提出本發明。
[現有技術文獻]
[專利文獻]
（專利文獻 1）韓國專利公開第10-2009-0036373號。
[要解決的問題]
本發明旨在改善現有技術的上述問題，其目的在於提供一種光散射油墨組合物、由該光散射油墨組合物製備的光散射層、彩色濾光片、以及圖像顯示裝置，該光散射油墨組合物表現出優異的噴射性，並且在可以提高塗膜的透射率的同時能夠製造出光散射（霧度）特性優異的光散射層。
本發明的另一個目的在於提供一種光散射油墨組合物、由該光散射油墨組合物製備的光散射層、彩色濾光片以及圖像顯示裝置，該光散射油墨組合物即使在長時間存放的情況下，粒徑變化或粒徑分佈變化少，且存放穩定性和沉降穩定性得到改善。
然而，本發明所要解決的問題不限於上述問題，本領域技術人員將從以下描述中清楚地理解其他未提及的問題。
[解決問題的方案]
本發明提供一種光散射油墨組合物，該光散射油墨組合物包含平均粒徑為150奈米至300奈米的第一散射粒子、平均粒徑為10奈米至90奈米的第二散射粒子、光聚合性化合物、以及光聚合引發劑，其中該第一散射粒子是二氧化鈦（TiO
2）。
此外，本發明提供一種彩色濾光片，其包含由上述光散射油墨組合物製造的光散射層。
另外，本發明提供一種圖像顯示裝置，其包含上述彩色濾光片。
[發明效果]
本發明的光散射油墨組合物包含平均粒徑為150奈米至300奈米的二氧化鈦（TiO
2）作為第一散射粒子，同時包含平均粒徑為10奈米至90奈米的第二散射粒子，從而具有在提高塗膜的透光率的同時提高塗膜的光散射（霧度）特性的效果。
此外，該光散射油墨組合物表現出優異的噴射性，因此可以藉由噴墨印刷方式有效地製造彩色濾光片。
另外，本發明的光散射油墨組合物具有以下效果：即使在長時間存放的情況下，粒徑變化或粒徑分佈變化少，且存放穩定性和沉降穩定性得到大幅改善。
本發明提供一種光散射油墨組合物，該光散射油墨組合物包含平均粒徑為150奈米至300奈米的第一散射粒子、平均粒徑為10奈米至90奈米的第二散射粒子、光聚合性化合物、以及光聚合引發劑，其中該第一散射粒子是二氧化鈦（TiO
2）。
根據本發明的光散射油墨組合物包含平均粒徑為150奈米至300奈米的二氧化鈦（TiO
2）作為第一散射粒子，同時包含平均粒徑為10奈米至90奈米的第二散射粒子，從而具有以下的效果：在提高塗膜的透光率的同時提高塗膜的光散射（霧度）特性，噴射性優異，適用於噴墨印刷方式。
此外，本發明的光散射油墨組合物具有以下的效果：即使在長時間存放的情況下，粒徑變化或粒徑分佈變化少，且存放穩定性和沉降穩定性得到大幅改善。
具體而言，本發明的光散射油墨組合物的粒徑分佈（SPAN）可以為1.5以下，較佳為1.3以下。
此外，本發明的光散射油墨組合物表現出非常優異的沉降穩定性。具體地，當本發明的光散射油墨組合物在穩定性分析儀（Turbiscan）中放置24小時時，上部（頂部）的背散射變化率可以為-5%至0%。
在本發明的光散射油墨組合物中，當該光散射油墨組合物在穩定性分析儀中放置24小時時，中間部的背散射變化率可以為-0.3%至0.3%。在本發明中，上部（頂部）和中部（中間部）可以是本領域技術人員公認的在穩定性分析儀（Turbiscan）測試中分別識別為上部（頂部）和中部（中間部）的部分。
此外，本發明提供一種彩色濾光片，其包含由上述光散射油墨組合物製造的光散射層。
另外，本發明提供一種圖像顯示裝置，其包含上述彩色濾光片。
以下，對本發明的構成進行詳細說明。
＜
光散射油墨組合物
＞
本發明的光散射油墨組合物可以同時改善塗膜的透射率和光散射（霧度）特性，並表現出優異的噴射性，從而可有效地藉由噴墨印刷方式製造彩色濾光片。
光散射油墨組合物的特徵在於包含散射粒子、光聚合性化合物、以及光聚合引發劑。
此外，本發明的光散射油墨組合物的特徵可以在於其不包含溶劑。
散射粒子
在本發明中，散射粒子係用於藉由增加從藍色光源發出的光的路徑來增加整體光效率。
在本發明中，散射粒子包括平均粒徑為150奈米至300奈米的第一散射粒子以及平均粒徑為10奈米至90奈米的第二散射粒子。更佳地，第一散射粒子的平均粒徑可以為180奈米至250奈米，並且第二散射粒子的平均粒徑可以為15奈米至70奈米。如此，藉由混合使用二種平均粒徑彼此不同的散射粒子，可以在提高塗膜的透射率的同時還可以提高光散射（霧度）特性。
第一散射粒子的特徵在於其為二氧化鈦（TiO
2），並且係用於藉由散射從藍色光源發出的光來提高透射光的均勻性。
第二散射粒子的特徵在於可以使用傳統的無機材料，並且包括平均粒徑為10奈米至90奈米的金屬氧化物。當第二散射粒子的平均粒徑小於10奈米時，存在塗膜的光散射（霧度）特性降低的問題，並且當平均粒徑超過90奈米時，存在無法提高塗膜的透射率的問題。
作為第二散射粒子的金屬氧化物可以為包含選自由以下物質組成之群組中的一種金屬的氧化物：Li、Be、B、Na、Mg、Al、Si、K、Ca、Sc、V、Cr、Mn、Fe、Ni、Cu、Zn、Ga、Ge、Rb、Sr、Y、Mo、Cs、Ba、La、Hf、W、Tl、Pb、Ce、Pr、Nd、Pm、Sm、Eu、Gd、Tb、Dy、Ho、Er、Tm、Yb、Ti、Sb、Sn 、Zr、Nb、Ce、Ta、In、及其組合，但不限於此。
具體地，第二散射粒子可以包含氧化鈦（TiO
2）、氧化矽（SiO
2）、氧化鋇（BaO）、硫酸鋇（BaSO
4）、氧化鋅（ZnO）、氧化鋯（ZrO
2）、或其組合，在能夠提高塗膜透射率的同時能夠提高光散射（霧度）特性方面，較佳包含選自以下群組的至少一種：氧化鈦（TiO
2）、氧化鋅（ZnO）、氧化矽（SiO
2）、硫酸鋇（BaSO
4）、及氧化鋯（ZrO
2）。
第一散射粒子與第二散射粒子的重量比可以為30：70至70：30，較佳為40：60至60：40。當第一散射粒子與第二散射粒子滿足上述重量比範圍時，在可以提高塗膜的透射率的同時還可以一起提高光散射（霧度）特性，因此是較佳的。
相對於光散射油墨組合物的固體含量的總重量，散射粒子的含量可以為1至50重量%，較佳為2至40重量%，更佳為3至25重量%。當散射粒子滿足上述含量範圍時，可以提供塗膜的透射率以及霧度特性優異的光散射油墨組合物，因此是較佳的。
光聚合性化合物
在本發明中，光聚合性化合物可以包含由以下化學式1表示的化合物。
[化學式1]
（在化學式 1 中，
R
1至R
5各自獨立為氫原子、甲基或羥基；
R
6為直接鍵或碳原子數為1至4的伸烷基；
m為1至5的整數。）
由上述化學式1表示的化合物可以包含選自以下物質中的至少一種：二亞甲基二丙烯酸酯、三亞甲基二丙烯酸酯、四亞甲基二丙烯酸酯、五亞甲基二丙烯酸酯、六亞甲基二丙烯酸酯、二丙二醇二丙烯酸酯、三丙二醇二丙烯酸酯、四丙二醇二丙烯酸酯、五丙二醇二丙烯酸酯、二乙二醇二丙烯酸酯、三乙二醇二丙烯酸酯、四乙二醇二丙烯酸酯、五乙二醇二丙烯酸酯、二丁二醇二丙烯酸酯、三丁二醇二丙烯酸酯、四丁二醇二丙烯酸酯、戊丁二醇二丙烯酸酯、二甲基丙烯酸二亞甲基酯、三亞甲基二甲基丙烯酸酯、四亞甲基二甲基丙烯酸酯、戊二甲基丙烯酸酯、六亞甲基二甲基丙烯酸酯、二丙二醇二甲基丙烯酸酯、三丙二醇二甲基丙烯酸酯、四丙二醇二甲基丙烯酸酯、五丙二醇二甲基丙烯酸酯、二乙二醇二甲基丙烯酸酯、三乙二醇二甲基丙烯酸酯、四乙二醇二甲基丙烯酸酯、五乙二醇二甲基丙烯酸酯、二丁二醇二甲基丙烯酸酯、三丁二醇二甲基丙烯酸酯、四丁二醇二甲基丙烯酸酯、戊二醇二甲基丙烯酸酯、丙烯醯氧基羥丙基丙烯酸酯、及甘油二甲基丙烯酸酯，但不限於此。
當光聚合性化合物包含由上述化學式1表示的化合物時，由於可以提供具有優異噴射性的光散射油墨組合物，因此是較佳的。
在本發明中，光聚合性化合物作為在後述的光聚合引發劑的作用下能夠聚合的光聚合性化合物，其還可以包括單官能單體、雙官能單體、多官能單體等。
單官能單體的具體實例可以舉出：壬基苯基卡必醇丙烯酸酯、丙烯酸2-羥基-3-苯氧基丙酯、丙烯酸2-乙基己基卡必醇丙烯酸酯、丙烯酸2-羥基乙酯、及N-乙烯基吡咯烷酮等。
雙官能單體作為不包含由上述化學式1表示的化合物的物質，其具體實例可以舉出：新戊二醇二丙烯酸酯、新戊二醇二甲基丙烯酸酯、3-甲基戊二醇二丙烯酸酯、3-甲基戊二醇二甲基丙烯酸酯、雙酚A乙氧基化二甲基丙烯酸酯、1,9-壬二醇二（甲基）丙烯酸酯、三環癸烷二甲醇二丙烯酸酯、環氧丙烷改質之雙酚A二（甲基）丙烯酸酯等。
多官能單體的具體實例可以舉出：三羥甲基丙烷三丙烯酸酯、三羥甲基丙烷三甲基丙烯酸酯、季戊四醇三丙烯酸酯、季戊四醇三甲基丙烯酸酯、季戊四醇四丙烯酸酯、季戊四醇四甲基丙烯酸酯、季戊四醇五丙烯酸酯、季戊四醇五甲基丙烯酸酯、二季戊四醇六丙烯酸酯、二季戊四醇六甲基丙烯酸酯等，較佳可以舉出由以下化學式2表示的化合物：
[化學式 2]
（在化學式 2 中，
R
11為氫原子、碳原子數為1至6的烷基、碳原子數為1至6的羥烷基、羥基或由以下化學式3表示的官能團，
R
12為氫原子或甲基，
R
13為碳原子數為1至20的伸烷基，
p、q和r各自獨立為0至5的整數，
t為0或1。）
[化學式 3]
（在化學式 3 中，
R
14為氫原子或甲基，
R
15為碳原子數為1至20的伸烷基、伸苯基，或碳原子數為3至10的伸環烷基。
L為直接鍵或原子數為1至6的伸烷基，
n為0至5的整數。）
相對於上述光散射油墨組合物的固體含量的總重量，光聚合性化合物的含量可以為10至95重量%，較佳為10至90重量%。當光聚合性化合物的含量在上述範圍內時，可以提供噴射性優異的光散射油墨組合物，因此是較佳的。
光聚合引發劑
本發明的光散射油墨組合物包含光聚合引發劑。
本發明的光散射油墨組合物中包含的光聚合引發劑只要能夠使光聚合性化合物聚合即可，其種類可以沒有特別限制地使用。從聚合特性、引發效率、價格等觀點來看，光聚合引發劑可以選自由以下物質組成之群組中的至少一種：苯乙酮類化合物、二苯甲酮類化合物、三嗪類化合物、聯咪唑類化合物、肟類化合物、噻噸酮類化合物、及氧化膦化合物等，並且就提高塗膜的透射率而言，較佳包含氧化膦化合物。
苯乙酮類化合物例如可以舉出：二乙氧基苯乙酮、2-羥基-2-甲基-1-苯基丙烷-1-酮、1-羥基環己基苯基酮、2-甲基-1-（4-甲硫基苯基）-2-嗎啉聚異丙烷-1-酮、2-（4-甲基苄基）-2-（二甲基胺基）-1-（4-嗎啉代苯基）丁-1-酮等。
二苯甲酮類化合物例如可以舉出：二苯甲酮、鄰甲基苯甲醯基苯甲酸酯、4-苯基二苯甲酮、4-苯甲醯基-4'-甲基二苯硫醚、3,3',4,4'-四（三級丁基過氧羰基）二苯甲酮、2,4,6-三甲基二苯甲酮等。
三嗪類化合物例如可以舉出：2,4-雙（三氯甲基）-6-（4-甲氧基苯基）-1,3,5-三嗪、2,4-雙（三氯甲基）-6-（4-甲氧基萘基）-1,3,5-三嗪、2,4-雙（三氯甲基）-6-[2-（3,4-二甲氧基苯基）乙烯基]-1,3,5-三嗪等。
聯咪唑類化合物例如可以舉出：2,2'-雙（2-氯苯基）-4,4',5,5'-四苯基聯咪唑、2,2'-雙（鄰甲氧基苯基）-4,5,4',5'-四苯基-1,2'-聯咪唑、2,2'-雙（2,3-二氯苯基）-4,4',5,5'-四苯基聯咪唑、2,2-雙（2,6-二氯苯基）-4,4',5,5'-四苯基-1,2'-聯咪唑等，並且作為市售品可以舉出Tronly公司的HABI-107等。
肟類化合物例如可以舉出鄰乙氧基羰基-α-氧亞胺基-1-苯基丙-1-酮等，並且作為市售品可以舉出BASF公司的Irgacure® OXE-01、OXE-02和OXE-03等。
噻噸酮類化合物例如可以舉出：2-異丙基噻噸酮、2,4-二乙基噻噸酮、2,4-二氯噻噸酮、1-氯-4-丙氧基噻噸酮等。
氧化膦化合物例如可以舉出：2,4,6-三甲基苯甲醯基二苯基氧化膦、苯基雙（2,4,6-三甲基苯甲醯基）氧化膦等，並且作為市售品可以舉出BASF公司的Darocur TPO、IRGACURE-819等。
相對於上述光散射油墨組合物的固體含量的總重量，包含在本發明的光散射油墨組合物中的光聚合引發劑的含量可以為0.2至15重量%，較佳為0.5至7重量%。當光聚合引發劑滿足上述含量範圍時，具有使用光散射油墨組合物形成的像素部的強度以及該像素部的表面的平滑性變得良好的優點。
添加劑
除此之外，根據本發明的光散射油墨組合物還可以包含散射粒子分散劑、抗凝聚劑、紫外線吸收劑、填料、高分子化合物、消泡劑、表面活性劑、熱交聯劑、黏附力促進劑、抗氧劑等添加劑，以在不損害本發明的效果的範圍內提高性能。
相對於上述光散射油墨組合物的固體含量的總重量，上述添加劑的含量可以為0.001至10重量%，並且較佳地，含量可以為0.01至5重量%。
＜
彩色濾光片和圖像顯示裝置
＞
本發明將包含上述光散射油墨組合物或包含由該組合物製備的光散射層的彩色濾光片以及包含該彩色濾光片的圖像顯示裝置作為本發明的範圍。
在本發明的彩色濾光片和圖像顯示裝置中，適用與上述光散射油墨組合物相關的所有事項，並且除此之外可以沒有限制地適用與彩色濾光片和圖像顯示裝置相關的習知內容。
在下文中，將藉由實施例更詳細地描述本發明。然而，以下實施例旨在更詳細地說明本發明，並且本發明的範圍不受以下實施例的限制。
＜
實施例
＞
製備例：散射粒子分散液的製備
將散射粒子45重量份、作為分散劑的DISPERBYK-2001（BYK（畢克）化學公司製造）5重量份、作為光聚合性化合物的1,4-丁二醇二丙烯酸酯或1,6-己二醇二丙烯酸酯50重量份用珠磨機混合並分散12小時來製備散射粒子分散液。作為散射粒子使用以下表1的第一散射粒子和根據表1至表5的第二散射粒子來製備散射粒子分散液A1至A16。
在以下表1至表5中，將散射粒子的粒徑定義為散射粒子的平均直徑。
[表1]
| 散射粒子分散 | A1 | A2 | A3 | A4 | A5 | A6 | A7 | A8 |
| TiO 2粒徑（奈米） | 200 | 150 | 300 | 5 | 10 | 50 | 90 | 100 |
[表2]
| 散射粒子分散液 | A9 | A10 | A11 | A12 | A13 |
| ZnO第二散射粒子粒徑（奈米） | 5 | 10 | 50 | 90 | 100 |
[表3]
| 散射粒子分散液 | A14 |
| SiO 2第二散射粒子粒徑（奈米） | 50 |
[表4]
| 散射粒子分散液 | A15 |
| BaSO 4第二散射粒子粒徑 （奈米） | 50 |
[表5]
| 散射粒子分散液 | A16 |
| ZrO 2第二散射粒子粒徑（奈米） | 50 |
實施例
1
至實施例
12
以及比較例
1
至比較例
6
：光散射油墨組合物的製備
按照以下表6和表7中的組成和含量進行混合來製備光散射油墨組合物（單位：重量%）。
[表6]
| 單位（重量%） | 實施例 | |||||||||||||
| 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | 11 | 12 | 13 | ||
| 散射粒子分散液 | A1 | 9 | 9 | 9 | 9 | 9 | 9 | - | - | 6 | 14 | 9 | 9 | 9 |
| A2 | - | - | - | - | - | - | 9 | - | - | - | - | - | - | |
| A3 | - | - | - | - | - | - | - | 9 | - | - | - | - | - | |
| A4 | - | - | - | - | - | - | - | - | - | - | - | - | - | |
| A5 | 11 | - | - | - | - | - | 11 | 11 | 14 | 6 | - | - | - | |
| A6 | - | 11 | - | - | - | - | - | - | - | - | - | - | - | |
| A7 | - | - | 11 | - | - | - | - | - | - | - | - | - | - | |
| A8 | - | - | - | - | - | - | - | - | - | - | - | - | - | |
| A9 | - | - | - | - | - | - | - | - | - | - | - | - | - | |
| A10 | - | - | - | 11 | - | - | - | - | - | - | - | - | - | |
| A11 | - | - | - | - | 11 | - | - | - | - | - | - | - | - | |
| A12 | - | - | - | - | - | 11 | - | - | - | - | - | - | - | |
| A13 | - | - | - | - | - | - | - | - | - | - | - | - | - | |
| A14 | - | - | - | - | - | - | - | - | - | - | 11 | - | - | |
| A15 | - | - | - | - | - | - | - | - | - | - | - | 11 | - | |
| A16 | 11 | |||||||||||||
| 光聚合性化合物 | B1 | 20 | - | - | - | - | - | - | - | - | - | - | - | - |
| B2 | 59 | 79 | 79 | 79 | 79 | 79 | 79 | 79 | 79 | 79 | 79 | 79 | 79 | |
| 光聚合引發劑 | C | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 |
[表7]
A1至A16：根據上述製備例的散射粒子分散液A1至A16
B1：1,4-丁二醇二丙烯酸酯（Sigma-Aldrich公司）
B2：1,6-己二醇二丙烯酸酯（Sigma-Aldrich公司）
C：2,4,6-三甲基苯甲醯基二苯基氧化膦（Sigma-Aldrich公司）
| 單位（重量%） | 比較例 | ||||||
| 1 | 2 | 3 | 4 | 5 | 6 | ||
| 散射粒子分散液 | A1 | 10 | - | 9 | 9 | 9 | 9 |
| A2 | - | - | - | - | - | - | |
| A3 | - | - | - | - | - | - | |
| A4 | - | - | 11 | - | - | - | |
| A5 | - | 10 | - | - | - | - | |
| A6 | - | - | - | - | - | - | |
| A7 | - | - | - | - | - | - | |
| A8 | - | - | - | 11 | - | - | |
| A9 | - | - | - | - | 11 | - | |
| A10 | - | - | - | - | - | - | |
| A11 | - | - | - | - | - | - | |
| A12 | - | - | - | - | - | - | |
| A13 | - | - | - | - | - | 11 | |
| A14 | - | - | - | - | - | - | |
| A15 | - | - | - | - | - | - | |
| 光聚合性化合物 | B2 | 89 | 89 | 79 | 79 | 79 | 79 |
| 光聚合引發劑 | C | 1 | 1 | 1 | 1 | 1 | 1 |
實施例
使用在實施例和比較例中製備的光散射油墨組合物藉由以下方式評估以下物理性能，並且將其結果示於以下表8中。
1.
噴射性評估
使用噴墨液滴分析儀根據以下評估標準來評估上述實施例和比較例中製備的光散射油墨組合物的噴射性。
＜噴射性評估標準＞
○：噴墨噴嘴沒有堵塞，噴射出的墨滴呈直線噴射。
X：噴墨噴嘴出現堵塞或墨滴不呈直線噴射。
2.
塗膜透射
率評估
將上述實施例和比較例中製備的光散射油墨組合物塗布在5公分×5公分的玻璃基板上，然後作為紫外光源使用同時含有g、h和i線的1千瓦（kW）高壓汞燈以1000毫焦耳／平方公分（mJ/cm
2）進行照射，然後藉由在180℃的加熱烘箱中加熱30分鐘來製備光散射層。對於所製造的光散射層，使用QE-2100（Otsuka電子公司）根據以下的評估標準來評估塗膜透射率。
＜透射率評估標準＞
○：與比較例1相比，透射率為101%以上。
X：與比較例1相比，透射率小於101%。
3.
塗膜霧度
評估
將上述實施例和比較例中製備的光散射油墨組合物塗布在5公分×5公分的玻璃基板上，然後作為紫外光源使用同時含有g、h和i線的1千瓦（kW）高壓汞燈以1000毫焦耳／平方公分（mJ/cm
2）進行照射，然後藉由在180℃的加熱烘箱中加熱30分鐘來製備光散射層。對於所製備的光散射層，使用HM-150（村上色彩技術研究所（Murakami Color Research Laboratory公司））根據以下評估標準來評估塗膜的霧度。
＜霧度評估標準＞
○：與比較例1相比，霧度為99%以上。
X：與比較例1相比，霧度小於99%。
4.
粒徑變化率和粒徑分佈評估
使用ELSZ-2000ZS（Otsuka公司製造）分別測量實施例和比較例中製備的光散射油墨組合物的初始平均粒徑和在室溫下存放30天後的平均粒徑。根據由此計算出的粒徑變化率按照以下的評估標準來評估平均粒徑變化穩定性，並且將其結果如下表所示。並且，對於初始粒徑分佈（SPAN），使用以下等式1來評估粒徑分佈，並將其結果示於以下表中。
＜粒徑變化穩定性評估標準＞
○：粒徑變化率為5%以下。
△：粒徑變化率大於5%且10%以下。
X：粒徑變化率大於10%。
＜等式 1＞
5.
確認沉降穩定性（
Terbiscan
）
使用TURBISCAN LAB設備評估實施例和比較例中製備的光散射油墨組合物的沉降穩定性。將30公克的光散射油墨放入40毫升的Turbiscan用小瓶中，確認在室溫下放置24小時後的上部（頂部）和中部（中間部）的背散射變化率（ΔBacks scattering；ΔBS），並將其結果示於以下表中。
實驗結果
[表8]
| 評估結果 | 噴射性 | 透射率 | 霧度 | 粒徑變化率 | SPAN | 頂部ΔBS(%) | 中間部ΔBS(%) |
| 實施例 1 | O | O | O | O | 0.9 | -4.1 | -0.22 |
| 實施例2 | O | O | O | O | 1.1 | -4.3 | -0.3 |
| 實施例3 | O | O | O | O | 1.2 | -4.4 | -0.15 |
| 實施例4 | O | O | O | △ | 1 | -3.5 | -0.24 |
| 實施例5 | O | O | O | O | 1 | -3.5 | -0.2 |
| 實施例6 | O | O | O | △ | 1.2 | -3.6 | -0.28 |
| 實施例7 | O | O | O | △ | 0.9 | -3.8 | -0.11 |
| 實施例8 | O | O | O | △ | 1.1 | -4.5 | -0.16 |
| 實施例9 | O | O | O | △ | 0.8 | -3.8 | -0.19 |
| 實施例10 | O | O | O | △ | 1.3 | -4.5 | -0.1 |
| 實施例11 | O | O | O | O | 1.2 | -4 | -0.12 |
| 實施例12 | O | O | O | O | 1.1 | -3.9 | -0.21 |
| 實施例13 | O | O | O | O | 1.1 | -3.8 | -0.24 |
| 比較例1 | O | X | O | X | 1.6 | -6 | -0.5 |
| 比較例2 | O | O | X | X | 1.4 | -5.8 | 0.42 |
| 比較例3 | X | O | X | X | 1.5 | -4.4 | 0.37 |
| 比較例4 | O | X | O | X | 1.6 | -4.2 | 0.31 |
| 比較例5 | X | O | X | X | 1.6 | -4.6 | 0.44 |
| 比較例6 | O | X | O | X | 1.6 | -4.7 | 0.32 |
參考表8中的實驗結果，包含第一散射粒子、第二散射粒子以及由化學式1表示的化合物的根據實施例1至實施例13的光散射油墨組合物表現出優異的噴射性，同時塗膜的透射率以及霧度特性均優異。此外，在實施例的光散射油墨組合物的情況下，可以確認：粒徑變化率很低，為5%以下，初始粒徑分佈（SPAN）也呈現出0.3以下的小值，因此存放穩定性也優異，並且可以確認：室溫放置24小時後的上部（頂部）和中部（中間部）的背散射變化率（ΔBacks scattering；ΔBS）很小，因此沉降穩定性優異。
與此相對，在不包含第二散射粒子的比較例1的情況下，可以確認：透射率特性和沉降穩定性顯著降低，在不包含第一散射粒子的比較例2的情況下，霧度特性和沉降穩定性顯著降低。此外，在包含平均粒徑超出10奈米至90奈米範圍的第二散射粒子的比較例3至比較例6的情況下，可以確認：噴射性、透射率及／或霧度特性以及存放穩定性顯著降低。
無
無
：無。
Claims (15)
- 一種光散射油墨組合物，其係包含：平均粒徑為150奈米至300奈米的第一散射粒子、平均粒徑為10奈米至90奈米的第二散射粒子、光聚合性化合物、以及光聚合引發劑，其中 該第一散射粒子是二氧化鈦（TiO 2）。
- 如請求項1所述的光散射油墨組合物，其中，該第一散射粒子的平均粒徑為180奈米至250奈米，並且該第二散射粒子的平均粒徑為15奈米至70奈米。
- 如請求項1所述的光散射油墨組合物，其中，該光聚合性化合物包含由以下化學式1表示的化合物： [化學式1] 在化學式 1 中， R 1至R 5各自獨立為氫原子、甲基或羥基， R 6為直接鍵或碳原子數為1至4的伸烷基， m 為1至5的整數。
- 如請求項1所述的光散射油墨組合物，其中，該第二散射粒子係選自以下群組的至少一種：氧化鈦（TiO 2）、氧化鋅（ZnO）、氧化矽（SiO 2）、氧化鋇（BaO）、硫酸鋇（BaSO 4）、及氧化鋯（ZrO 2）。
- 如請求項1所述的光散射油墨組合物，其中，該第一散射粒子與該第二散射粒子的重量比為30：70至70：30。
- 如請求項1所述的光散射油墨組合物，其中，相對於該光散射油墨組合物的固體含量的總重量，該光聚合性化合物的含量為10至95重量%。
- 如請求項1所述的光散射油墨組合物，其中，該光聚合引發劑包含氧化膦類化合物。
- 如請求項1所述的光散射油墨組合物，其中，相對於該光散射油墨組合物的固體含量的總重量，該光聚合引發劑的含量為0.2至15重量%。
- 如請求項1所述的光散射油墨組合物，其中，該光散射油墨組合物更包含添加劑。
- 如請求項1所述的光散射油墨組合物，其中，該光散射油墨組合物不包含溶劑。
- 如請求項1至10中任一項所述的光散射油墨組合物，其中，當該光散射油墨組合物在室溫下儲存30天時，平均粒徑變化率為5%以下。
- 如請求項1至10中任一項所述的光散射油墨組合物，其中，該光散射油墨組合物的粒徑分佈（SPAN）為1.5以下。
- 如請求項1至10中任一項所述的光散射油墨組合物，其中，當該光散射油墨組合物在穩定性分析儀（Turbiscan）中放置24小時時，頂部的背散射變化率為-5%至0%。
- 一種彩色濾光片，其包含由如請求項1至13中任一項所述的光散射油墨組合物製造的光散射層。
- 一種圖像顯示裝置，其包含如請求項14所述的彩色濾光片。