TW202143802A - 半導體處理腔室組件的調整方法 - Google Patents
半導體處理腔室組件的調整方法 Download PDFInfo
- Publication number
- TW202143802A TW202143802A TW110105715A TW110105715A TW202143802A TW 202143802 A TW202143802 A TW 202143802A TW 110105715 A TW110105715 A TW 110105715A TW 110105715 A TW110105715 A TW 110105715A TW 202143802 A TW202143802 A TW 202143802A
- Authority
- TW
- Taiwan
- Prior art keywords
- processing chamber
- aluminum
- layer
- semiconductor processing
- component
- Prior art date
Abstract
提供在半導體處理腔室中使用之構件的製造方法。從導電材料形成構件本體,該導電材料的熱膨脹係數低於10.0x10-6
/K。接著,在該構件本體的表面上方設置金屬氧化物層。
Description
本揭露整體上係關於半導體裝置的製造。更具體而言,本揭露係關於在基板或晶圓的處理中所使用的半導體處理腔室構件、及其製造/調整方法。
[相關申請案的交互參照]
本申請案係主張2020年2月19日提交的美國臨時申請案第62/978,610號之優先權,該臨時申請案的所有方面係作為參考文獻而引入本文中。
在半導體晶圓的處理期間,係將電漿處理腔室用於處理半導體裝置。電漿處理腔室會經受電漿、鹵素、及/或氧,而可能使該電漿處理腔室中的構件劣化。一些電漿處理腔室具有矽部件,例如電極、噴淋頭、及邊緣環。
此處所提供之先前技術描述係為了一般性呈現本揭露之背景的目的。本案列名發明人的工作成果、至此先前技術段落的所述範圍、以及申請時可能不適格作為先前技術的實施態樣,均不明示或暗示承認為對抗本揭露內容的先前技術。
為了達成上述並符合本揭露的目的,提供在半導體處理腔室中使用之構件的製造方法。從導電材料形成構件本體,該導電材料具有低熱膨脹係數(例如,熱膨脹係數低於10.0x10-6
/K)。接著,在該構件本體的表面上方設置金屬氧化物層。
在另一實施方式中,提供在電漿處理腔室中使用的構件。該構件具有構件本體。該構件本體包括低熱膨脹係數(例如,熱膨脹係數低於10.0x10-6
/K)的導電材料。在該構件本體的表面上方設置金屬氧化物層。
本揭露的這些及其他特徵將結合隨附圖式而較詳細地描述於下方的本揭露的實施方式中。
現在將參照隨附圖式中所繪示的數個較佳實施例而詳細地對本揭露進行描述。在下方敘述中,許多特定細節係闡述以提供對於本揭露的透徹理解。然而,對於本發明所屬技術領域中具有通常知識者將係顯而易知的是,本揭露可在缺少這些特定細節的一部或全部的情況下實施。在其他情況下,並未詳細描述習知的處理步驟及/或結構,以避免非必要地模糊本揭露。
本文所述的各種實施例提供複數半導體處理腔室構件,該等半導體處理腔室構件對於處理(例如,電漿蝕刻)的電弧及/或腐蝕所造成的損害係具抗性的,而因此抑制或最小化該構件的消耗,其中構件的消耗可能係發生自半導體處理系統(例如,電漿處理腔室)中所固有的電漿及蝕刻處理。
為了助於理解,圖1係製造及使用半導體處理腔室(例如,電漿處理腔室)之構件的第一處理實施例的高階流程圖。提供構件本體(步驟104)。構件本體包括導電材料,其中該導電材料具有低線性熱膨脹係數(CTE)。在一實施例中,係將「低CTE」材料定義為CTE小於10.0x10-6
/K的材料。在進一步實施例中,係將「低CTE」材料定義為CTE小於5.0x10-6
/K的材料。如以下將進一步詳細解說的,構件本體的導電率及低CTE對於半導體處理腔室(例如,電漿處理腔室)之構件的使用係特別有幫助的。在一實施例中,對導電半導體或低CTE金屬進行鑄造以例如透過將熔融半導體或金屬倒入或注入模具中而形成指定構件形狀,藉以形成該構件本體。在對導電半導體材料進行鑄造的實施例中,熔融半導體係在模具中冷卻及硬化而形成具有大晶粒尺寸的多晶結構。在另一實施例中,對導電半導體粉末進行燒結而形成導電陶瓷構件,藉以形成構件本體。圖2A為構件本體204的橫截面示意圖。在此示例中,構件本體204形成邊緣環。在此實施例中,構件本體204係形成自矽、矽碳化物、或石墨的導電半導體。導電的矽或矽碳化物係藉由對矽或矽碳化物進行摻雜而提供。在另一實施例中,構件本體204係形成自導電、低CTE金屬,例如鈦、鉬等。
在構件本體204上沉積鋁阻障層(步驟108)。在此實施例中,係使用電鍍而提供純度以質量計為99.9%的鋁層。電鍍處理涉及標準電化學槽,其中待電鍍的部件為陰極,而陽極為超高純度鋁,且兩構件均浸沒在電解液中。為了提供足夠高純度的鋁阻障層,需要導電的有機基底溶液,而並非水基底溶液。圖2B為已沉積鋁阻障層208過後的構件本體204的橫截面示意圖。在此示例中,鋁阻障層208包覆著構件本體204。在其他實施例中,鋁阻障層208可位於構件本體204的一表面上。
透過陽極化而形成金屬氧化物層(步驟112)。在此實施例中,將鋁阻障層208的表面進行硬式陽極化(亦稱為硬式塗覆、或第III型陽極化),故金屬氧化物層為鋁氧化物(Al2
O3
)。硬式陽極化處理在高Al純度的鋁阻障層208之表面上形成極硬的耐磨損多孔氧化物。該陽極化機構亦為一典型的電化學槽,其中經純Al塗覆的部件為酸浴(通常為硫酸)中的陽極。當在電化學槽中通過電流時,在陰極處釋出氫,而在鋁陽極的表面處釋出氧,從而使鋁氧化物積聚。圖2C係已將鋁阻障層208的表面進行硬式陽極化而形成金屬氧化物層212過後的構件本體的橫截面圖。由於鋁阻障層208具有高純度,故該陽極化處理亦提供高純度的金屬氧化物層212。
將構件本體安裝在半導體處理腔室(例如,電漿處理腔室)中(步驟116)。在此示例中,構件本體係使用作為邊緣環。圖3係在一實施例中對基板進行電漿處理所用的電漿處理腔室300的示意圖,其中構件本體可安裝在該電漿處理腔室內。在一些實施例中,電漿處理腔室300包括位在由腔室壁350所包圍的電漿處理腔室304中的一提供氣體入口的氣體分配板306、及一靜電卡盤(ESC)316。在電漿處理腔室304內,基板307係位於ESC 316的頂部上。ESC 316可提供來自ESC功率源348的偏壓。氣體源310係經由氣體分配板306而連接至電漿處理腔室304。ESC溫度控制器351係連接至ESC 316並提供對ESC 316的溫度控制。射頻(RF)功率源330將RF功率提供至ESC 316及上電極。在此實施例中,上電極係氣體分配板306。在較佳實施例中,13.56兆赫(MHz)、2 MHz、60 MHz及/或任選地27 MHz功率源構成RF功率源330及ESC功率源348。控制器335係可控制地連接至RF功率源330、ESC功率源348、排氣幫浦320、及氣體源310。高流量襯套360係位於電漿處理腔室304內的襯套。高流量襯套侷限著來自氣體源的氣體,並且具有狹槽362。狹槽362維持著受控制的氣流,以從氣體源310傳至排氣幫浦320。邊緣環364圍繞著基板307,並大部分由石英環368所防護而免於經受電漿。這種電漿處理腔室的示例係由Lam Research Corporation of Fremont, CA所製造的Flex®
蝕刻系統。處理腔室可為電容耦合電漿(CCP)反應器、或感應耦合電漿(ICP)反應器。
電漿處理腔室304使用邊緣環364以對基板307進行電漿處理(步驟120)。所述電漿處理可為蝕刻、沉積、鈍化、或另一電漿處理之中的一或更多者。所述電漿處理還可與非電漿處理結合執行。這種處理可能會將邊緣環364暴露於含鹵素及/或氧的電漿。
由於邊緣環在半導體處理腔室中的位置及功能,其通常為消耗性物品。邊緣環的頂表面需要與基板的頂表面為整平的(level)。因此,當邊緣環消耗時,可提供各種機制來移動該邊緣環,使邊緣環的頂表面與基板的頂表面保持齊平。另外,一旦邊緣環被充分地消耗,便必須替換邊緣環而造成電漿處理腔室停工。在其他實施例中,可將這種構件設置在被防護著而免於經受電漿的位置中。理想中,邊緣環具有低熱膨脹係數、以及良好的電及熱傳導率。
在此實施例中,經硬式陽極化的金屬氧化物層212對於電漿腐蝕係具有充分的蝕刻抗性,使得邊緣環不再是消耗品、或是最小化地消耗而不再需要經常更換。用以形成高純度鋁阻障層208的鋁電鍍將任何合金或其他不純物從待進行硬式陽極化的鋁移除。當高純度鋁阻障層208氧化時,其提供更具蝕刻抗性的鋁氧化物層,以及避免在電漿處理期間產生不純物。另外,鋁阻障層208的電鍍形成薄、均勻且保形的鋁層。硬式陽極化可僅稍微增加所得到的經硬式陽極化層的厚度。因此,將不需要進行加工以將經硬式陽極化層平整化及/或薄化,使邊緣環在電漿處理腔室300中符合尺寸。另外,經硬式陽極化層的薄保護層係較少遭遇熱膨脹的問題。對鋁阻障層208進行電鍍、以及對鋁阻障層208進行硬式陽極化係能夠提供金屬氧化物層212的相對較不昂貴的處理。在此實施例中,透過電鍍所沉積的鋁阻障層208具有1微米至100微米範圍內的厚度。透過硬式陽極化所形成的金屬氧化物層212具有高純度,且具有介於5微米至100微米之間的厚度。高純度的金屬氧化物層212比低純度的金屬氧化物層更具有蝕刻抗性。
各種電漿處理腔室300可使用具有鋁、或金屬氧化物層、或塗層的其他構件。這種構件包括ESC 316、峰部(pinnacle)、高流量襯套360、氣體分配板306等。鋁或金屬氧化物塗層對於電漿處理腔室的消耗性構件係最為實用的。
介電質塗層的完整性對於維持電性隔絕及化學抗性兩者而言係至關重要的。較厚的介電質塗層較能容許破裂。較薄的介電質塗層未能提供充分的絕緣性,以避免被電漿處理腔室300所使用的電壓所損害。
在各種實施例中,可使用電漿電解氧化(PEO)、或第I、II、或III型陽極化以對鋁阻障層208的表面進行陽極化,而形成金屬氧化物層212。在其他實施例中,係將金屬氧化物層212噴灑塗覆在鋁阻障層208上。所述噴灑塗覆可為熱噴灑塗覆、或電漿噴灑塗覆。熱噴灑/電漿噴灑係形成厚塗層的最佳方法。在一些實施例中,可使用氣溶膠沉積以提供密實塗層。然而,氣溶膠沉積對於3D幾何形狀來說可能係較具挑戰性的。噴灑塗覆可能形成較厚且不均勻的塗層。因此,若使用噴灑塗覆,則可能需要進行加工使金屬氧化物層212平滑化。在一些實施例中,可能需要較厚的金屬氧化物層212以提供經改善的合適性。若需要較薄的金屬氧化物層212,則將使用加工使金屬氧化物層212薄化。在各種實施例中,可使用化學氣相沉積、或各種噴灑處理、或其他沉積處理來沉積鋁阻障層208。金屬氧化物的熱噴灑塗覆處理包括一熱源(火焰或電漿),該熱源將原料(粉末形式)熔化成為極小的微滴,並以高速將其噴灑於基板上。這種處理得以高沉積速率(相較於其他塗覆技術)而在複雜的幾何形狀上沉積厚的塗層。
在其他實施例中,可藉由熱噴灑以在鋁阻障層208上沉積其他金屬氧化物。這種其他的金屬氧化物可為氧化釔(Y2
O3
)、例如釔鋁石榴石(Y3
Al5
O12
(YAG))、釔鋁單斜晶體(Y4
Al2
O9
(YAM))、或釔鋁鈣鈦礦(YAlO3
(YAP))的三相氧化釔-氧化鋁氧化物、或是釔安定氧化鋯(YSZ)。
在另一實施例中,於構件本體204的表面上直接熱噴灑金屬氧化物層,而不是沉積鋁阻障層(步驟108)。圖4係構件400的橫截面示意圖,其中金屬氧化物層412係直接噴灑於構件本體404上。透過熱噴灑所沉積的金屬氧化物層412可具有0.5至2 mm範圍內的厚度。
圖5顯示半導體處理腔室(例如,電漿處理腔室)之構件的製造及使用方法的第二實施例的高階流程圖。提供基板本體(步驟504)。請參照圖6A至6C,可將所提供的基板本體604形成為在電漿處理腔室中所使用的構件形狀,例如係具有中央內徑608的邊緣環,其中該中央內徑608至少部分地圍繞著靜電卡盤(ESC)。圖6A係基板本體的俯視圖,而圖6B係基板本體的橫截面圖。圖6C顯示基板本體表面612的截面A-A的特寫圖。應當理解的是,圖6A至圖8中顯示的圖像僅係作為說明的目的,並可變更尺寸、形式及特徵。基板本體604可透過如加工、模造、燒結、拋光、化學蝕刻等的數種製造處理而形成。
根據實施例,基板本體604包括導電材料,其中該導電材料具有低熱膨脹係數(例如,小於10.0x10-6
/K)。在進一步實施例中,基板本體604包括導電半導體,且更具體地係導電的多晶摻雜矽或矽碳化物半導體材料。在替代實施例中,基板本體可包括其他導電半導體(例如,鍺、石墨等)、或其他低CTE材料如鈦、鉬等。在各種實施例中,半導體可為多晶的。多晶矽(Multi-crystalline silicon)的晶粒平均係大於複晶矽(poly-crystalline silicon)的晶粒。多晶矽的平均晶粒尺寸係大於1 mm。低熱膨脹係數通常在構件之間提供較小的應力、磨損、以及較佳的合適性。尤其,在腔室處理期間,邊緣環及其他相鄰部件(尤其係ESC底板)將會處於不同溫度。由於電漿導致的加熱,邊緣環通常會遠比ESC底板還熱(在150o
C至250o
C的範圍內),其中該ESC底板的溫度係受主動控制的(在-40o
C至50o
C的範圍內)。當選擇小熱膨脹係數的邊緣環材料時,有效地減低邊緣環與相鄰部件(ESC)之間的間隙尺寸的偏差,從而可達成二導體之間的較一致電容。因此,將具有較一致的電性能。
請參照圖5及圖6D,在提供基板本體604後,係在基板本體604的表面612上方形成高純度鋁層616(圖6D)(步驟508)。根據一些實施例,係使用電鍍沉積方法藉以沉積鋁層616,該電鍍沉積方法提供實質均勻且無缺陷的鋁層616,其中鋁層616係高純度鋁且與下方的基板本體604具有高的結合強度。在替代實施例中,可使用如原子層沉積(ALD)或電漿電解氧化(PEO)的沉積方法。在一實施例中,矽基板係經處理以在進行鋁沉積之前,先從表面移除或實質上移除由製造處理所造成的任何氧化物(例如,矽氧化物)、及表面損傷。這亦可在電鍍處理中執行,以確保在鋁層616與基板本體604之間不存在、或是存在極少的氧化物、氧化、或鬆散微粒。
鋁層616係有助於形成陽極化層624(敘述於下),其中陽極化層624比起鋁合金(例如Al 6061)的陽極化而言係較均勻、具有最小的孔隙率、並具有較低的殘留汙染物。經組合的鋁層616/陽極化層624提供對侵略性電漿環境具有腐蝕抗性的阻障物,亦提供對於高電壓電漿環境的電壓隔絕保護。根據實施例,鋁層616係以質量計為至少99%的純鋁。根據另一實施例,鋁層616係以質量計為至少99.5%的純鋁。根據又另一實施例,鋁層616係以質量計為至少99.9%的純鋁。在一實施例中,電鍍步驟508係透過AlumiPlate處理(AlumiPlate, Inc., Coon Rapids, MN)所執行,其中經電鍍鋁層616的純度係包括以質量計大於99.9%的純鋁。
鋁層616的厚度可隨著一或更多因素而變動,包括構件類型、構件位置、構件的幾何形狀、基板材料的性質、成本等。根據一實施例,鋁層616的厚度係介於約20微米(µm)至150 µm之間。在另一實施例中,鋁層616的厚度係介於約25 µm至125 µm之間。根據另一實施例,鋁層616的厚度係介於約25 µm與50 µm之間。在進一步實施例中,鋁層616的厚度係介於約25 µm與35 µm之間。
請參照圖5及圖6E,在鋁層616形成後,係將鋁層616的表面620進行陽極化(步驟512),以形成具有陽極化層624的電漿處理構件600。圖6E顯示矽基板本體604的一部分經陽極化過後的實施例之橫截面圖。如圖6E中所顯示,鋁層616的一部分係經滲透而產生陽極化層624,而在陽極化層624與基板本體604之間仍留下至少一部份的鋁層616。陽極化層624的附加層深度係附加在鋁層616的原始表面620上方,而因此使部件的整體厚度增加。在一實施例中,陽極化層624的深度大約50%係滲透在表面620下方,而50%係附加沉積在表面620上方。需要使至少一部份的鋁層616保持原樣(亦即,未被陽極化),原因在於其對於陽極化層624與基板本體604界面之間的接合係有顯著的益處。由於陽極化層624與矽基板本體604係相對硬的表面,因此柔軟、可展延的鋁層係作為緩衝物,以舒緩在腔室中進行電漿蝕刻處理期間加諸於層體上的熱應力。若未將熱應力舒緩,則當經受溫度變化時,陽極化層可能會從矽基板本體604分離。在各種實施例中,當陽極化層624與矽基板本體604經受數種極端熱循環時,鋁層616防止分離。另外,形成矽氧化物將會在矽基板本體604與陽極化層624之間的界面處造成熱破裂。熱破裂產生矽基板本體604的暴露部分。矽基板本體604的暴露部分將會受到腐蝕。
在一實施例中,陽極化步驟512包括硬式塗覆或第III型陽極化處理(亦稱為硬式陽極化、或硬式塗覆陽極化),其中鍍鋁的矽基板本體604係在0o
C至3o
C的溫度及高壓(起始為25V DC,並隨著處理的進行而提升至60-100V)下經受硫酸浴,以形成氧化物或陽極化層。第III型陽極化處理形成厚度高達、或大於約50 µm的陽極化層624。在此實施例中,陽極化過後並未執行水封、或其他熱液、或沉澱手段;原因在於這種密封有較高的可能性會從電漿處理破裂或劣化。陽極化處理形成具有間隔的柱體。所述間隔為柱體提供膨脹的空間而不破裂。密封使所述間隔消除或減少,使得當柱體因加熱而膨脹時,陽極化層較容易破裂。破裂會降低該層體所提供的保護性。另外,密封可能會導致水鋁石形成,並因此使表面磨損抗性減低。此外,可使用例如第II型的其他陽極化處理、或混酸、或草酸以將電鍍Al轉變成為陽極化保護層。
在一些實施例中,陽極化氧化物層614至少為10 µm的厚度,並可為50 µm以上的厚度。在其他實施例中,陽極化氧化物層614的厚度係落在5 µm與50 µm的範圍內。在其他實施例中,陽極化氧化物層614的厚度係落在12 µm與38 µm的範圍內。在進一步實施例中,陽極化氧化物層614的厚度係落在25 µm與35 µm的範圍內。在各種實施例中,鋁層616未經陽極化的部分係具有範圍落在7 µm至113 µm內的厚度。在各種實施例中,鋁層616未經陽極化的部分係具有範圍落在12 µm至32 µm內的厚度。
根據實施例,陽極化層624係鋁氧化物層,其中鋁氧化物的純度以質量計為至少99%。根據另一實施例,陽極化氧化物層614係鋁氧化物層,其中鋁氧化物的純度以質量計為至少99.5%。根據又另一實施例,陽極化層624係鋁氧化物層,其中鋁氧化物的純度以質量計為至少99.9%。
如上所詳細描述,依圖5之步驟504至512的處理進行製造所得到的鋁層616/陽極化層624具有最少的汙染物(舉例來說,與習知鋁合金6061中所發現的180 ppm相比,為5 ppm的鋅含量)、以及提高的腐蝕抗性(與利用混酸或草酸進行陽極化的鋁6061的5-13小時相比,鹽酸(HCl)氣泡測試係得到高達140小時的測試抗性)。另外,經測量,鋁層616/陽極化層624具有高達2500 V/0.001”的介電強度。
在將構件600適當地經由圖5的步驟504至512進行處理過後,接著將其安裝在半導體處理腔室(例如,電漿處理腔室)中(步驟516,圖5)。圖5中所繪示的製造處理對於製造電漿處理腔室的消耗性介電質構件係特別實用的。更具體來說,由圖5、及圖6A至圖6E中繪示的處理所形成的構件600係特別適合用於形成及/或調整電漿處理腔室的一或更多構件,以抑制或最小化該構件被電漿、反應性鹵素物種、或其他能量離子、及電漿處理腔室中所固有的蝕刻處理所造成的消耗。
在下方的實施例中,係將由圖5、及圖6A至圖6E中繪示的處理所形成的構件600指向特定的應用,以作為靜電卡盤(ESC)組件或系統(例如,圖7中的ESC組件700)內的邊緣環或類似構件,而用於電漿處理腔室(例如,圖8中顯示的電漿處理腔室804)中。然而,應當理解的是,除了高流量襯套、氣體分配板等之外,可將由圖5、及圖6A至圖6E中繪示的處理所形成的構件600實施為ESC組件700或電漿處理腔室804內的任何數量之構件,例如峰部及靜電卡盤(ESC)等其他部件,以擴展所需的高腐蝕抗性、良好導電性、及低熱膨脹係數的性質。
圖7繪示在電漿處理系統中所使用的ESC組件700之一部分(由圖8中的截面B-B所界定)的截面圖,其中該ESC組件700之該部分具有可動式邊緣環配置。ESC組件700包括頂邊緣環724,其中頂邊緣環724係配置成圍繞靜電卡盤(ESC)704。亦可將ESC 704稱作基板支撐件,用於在處理期間支撐著處理晶圓866。頂邊緣環724具有環形下凹部726,其中環形下凹部726係由可動式邊緣環708所支撐。可動式邊緣環708係垂直地接鉸在(articulate)由內徑向側部與外徑向側部所界定的空腔內,其中該內徑向側部包括ESC 704、加熱板752、及中間內邊緣環728,而該外徑向側部包括固定式邊緣環716、外邊緣環712、及覆蓋邊緣環720。覆蓋邊緣環720具有將頂邊緣環724部分覆蓋的徑向內突出部722。
由於在處理晶圓866的處理過程中,頂邊緣環724會暴露於腐蝕性電漿及蝕刻劑,故頂邊緣環724無可避免地會隨著暴露的增加而受到磨蝕,並因此在高度方向中減低其厚度。於是,可動式邊緣環708係用於將頂邊緣環724升高,而恢復頂邊緣環724的頂表面與處理晶圓/基板866之間的高度關係。為了實現這種高度調整,一或更多升降銷740係垂直作動(透過ESC 704中的孔口748、及固定式邊緣環716中的孔口718)以推升可動式邊緣環708,而因此調整頂邊緣環724的垂直定位。套筒744係繞著升降銷740的圓周設置,以將ESC 704的孔口748密封。
根據實施例,構件600係根據圖5、及圖6A至圖6E的處理所製造,以形成可動式邊緣環708而安裝在ESC組件700中。由於可動式邊緣環708在腔室中的位置、以及在處理晶圓866的處理過程中鄰近/暴露於電漿(亦即,具有一或更多「面向電漿表面」),可動式邊緣環708係大幅受益於構件600的鋁層616/陽極化層624的抗腐蝕性質。在示例中,電漿可能在頂邊緣環724、外邊緣環712、與覆蓋邊緣環720之間通過而到達可動式邊緣環708的外表面、及固定式邊緣環716的內表面。電漿的通過量係取決於頂邊緣環724的位置。此外,在圖8中顯示的位置中,頂邊緣環724可防止電漿從頂邊緣環724與中間內邊緣環728之間穿過而到達可動式邊緣環708的內表面。當可動式邊緣環708將頂邊緣環724升起時,在頂邊緣環724與中間內邊緣環728之間形成間隙以允許電漿到達可動式邊緣環708的內表面。
在一實施例中,可動式邊緣環708的整體外表面可為經處理的,以包括如同在構件600中所提供的鋁層616/陽極化層624。然而,應當理解的是,僅一部分的構件之外部表面係需要被處理的。舉例來說,可將可動式邊緣環708的外或外部徑向表面排除在鋁電鍍及/或陽極化之外(例如,利用遮罩或類似處理),使得僅面向電漿表面(例如,中央內徑608的內徑向表面,請參見圖6B)包括鋁層616/陽極化層624。這種部分塗覆處理可能需要遮蔽不塗覆的部分。面向電漿表面係在電漿處理期間係暴露至電漿、或是在高溫及低壓下暴露至反應性鹵素物種的表面。反應性鹵素物種可形成自遠端電漿、或熱反應性氟。在一些實施例中,可動式邊緣環708上的複數點係未經塗覆的,原因在於該等點可在電鍍處理期間用於與電極連接。
另外,可動式邊緣環708係伴隨著固定式邊緣環716而提供到達ESC 704的RF傳導(交流電)路徑,以在腔室處理期間達成較均勻的電漿,藉以改善晶圓邊緣附近的處理均勻度,並因此受益於構件600基板本體604的導電本質。於是,可使用圖5、及圖6A至圖6E中所繪示的處理來形成固定式邊緣環716、頂邊緣環724、以及在ESC組件700及電漿處理腔室系統800中的其他構件,以具有構件600的電鍍鋁層616及陽極化層624。
請參照回到圖5所揭露的處理,構件600係使用於電漿處理腔室中,以利於處理晶圓866上的半導體製造(步驟520)。電漿處理可為蝕刻、沉積、鈍化、或另一電漿處理的其中一或更多處理。還可將電漿處理與非電漿處理結合執行。
為了助於理解,圖8示意性地繪示可用於實施例中的電漿處理腔室系統800的示例。電漿處理腔室系統800包括電漿反應器802,在電漿反應器802中具有電漿處理腔室804。由功率匹配網路808所調整的電漿電源806將功率提供至位於介電質感應功率窗812附近的變壓器耦合電漿(TCP)線圈810,以藉由提供感應耦合功率而在電漿處理腔室804中產生電漿814。峰部872從電漿處理腔室804的腔室壁876延伸至介電質感應功率窗812而形成峰部環。峰部872相對於腔室壁876及介電質感應功率窗812係呈一角度。舉例來說,峰部872與腔室壁876之間的內角、以及峰部872與介電質感應功率窗812之間的內角可各自大於90o
且小於180o
。如圖所示,峰部872在電漿處理腔室804的頂部附近提供呈角度的環。可將TCP線圈(上功率源)810配置以在電漿處理腔室804內產生均勻的擴散輪廓。舉例來說,可將TCP線圈810配置以在電漿814中產生環形功率分佈。介電質感應功率窗812係被提供以將TCP線圈810與電漿處理腔室804分離,同時允許能量從TCP線圈810傳遞至電漿處理腔室804。當處理晶圓866位於ESC組件700上時,由偏壓匹配網路818所調整的晶圓偏壓電源816將功率提供至ESC組件700以進行偏壓設定。控制器824控制著電漿電源806及晶圓偏壓電源816。
電漿電源806及晶圓偏壓電源816可配置以在特定射頻下進行操作,例如13.56兆赫(MHz)、27 MHz、2MHz、60 MHz、400千赫(KHz)、2.54吉赫(GHz)、或其組合。可適當地為電漿電源806及晶圓偏壓電源816制定尺寸以供應一範圍的功率,藉以達到期望的處理性能。舉例而言,在一實施例中,電漿電源806可供應範圍為50至5000瓦的功率,而晶圓偏壓電源816可供應範圍為20至3000伏(V)的偏壓。另外,TCP線圈810及/或ESC組件700可包括二或更多的子線圈、或子電極。所述子線圈或子電極可由單一電源供電、或由複數電源供電。
如圖8所顯示,電漿處理腔室系統800更包括氣體源/氣體供應機構830。氣體源830係透過例如氣體注入器840的氣體入口而與電漿處理腔室804流體連接。氣體注入器840具有至少一鑿孔841,以允許氣體通過氣體注入器840而到達電漿處理腔室804中。氣體注入器840可位於電漿處理腔室804中任何有利的位置,並可為注入氣體所用的任何形式。然而,可較佳地將氣體入口配置以產生「可調整的」氣體注入輪廓。可調整的氣體注入輪廓允許對到達電漿處理腔室804中多個區域的各別氣體流量獨立地進行調整。更較佳地,氣體注入器係安裝至介電質感應功率窗812。氣體注入器可安裝在功率窗上、安裝在功率窗中、或形成功率窗的一部分。處理氣體及副產物係透過壓力控制閥842及幫浦844而從電漿處理腔室804移除。壓力控制閥842及幫浦844亦用於維持電漿處理腔室804中的特定壓力。壓力控制閥342可在處理期間維持著小於1托的壓力。可將一或更多邊緣環圍繞著ESC組件700的頂部設置。氣體源/氣體供應機構830係由控制器824進行控制。可使用由Lam Research Corp.®
of Fremont, CA所製造的Kiyo®
、Strata®
、或 Vector®
以實行實施例。
如圖8所顯示,處理晶圓866係被設置電漿處理腔室804中,更具體地係位於ESC組件700上或之中。對處理晶圓866施加電漿處理(例如,圖1的步驟120)。在此示例中,對於處理晶圓866的電漿處理係用以對處理晶圓866上的堆疊的一部分提供蝕刻,例如對堆疊中的含鎢層進行蝕刻。在此實施例中,電漿處理係加熱至550o
C之上的溫度。另外,電漿處理在電漿處理腔室804的內部上沉積殘留物。對處理晶圓866進行電漿處理後,係將處理晶圓866從電漿處理腔室804移除。對電漿處理腔室804進行清潔以移除所沉積的殘留物。在此實施例中,來自遠端氟電漿的反應性氟係用以清潔電漿處理腔室804的內部。提供範圍為1毫托(mTorr)至10 Torr內的壓力。ESC組件700並未完全冷卻,並維持在高於500o
C的溫度。完成清潔後,可將新的處理晶圓866放置在電漿處理腔室804中以開始新的循環。在另一示例中,電漿處理係用以提供包括碳層、複晶矽層、或氧化物/氮化物層的蝕刻。在這種示例中,係將晶圓溫度控制在0o
C至150o
C的範圍內,並在晶圓處理過後利用原位O2
及NF3
電漿對腔室進行清潔。
在各種實施例中,可將電鍍鋁層616及陽極化層624、及構件600的特徵部實施在電漿處理腔室804的各種部件中,例如限制環、邊緣環、靜電卡盤、接地環、腔室襯套、門襯套、峰部、噴淋頭、介電質功率窗、氣體注入器、邊緣環、陶瓷轉移臂(transfer arm)、或其他構件。舉例來說,可在頂邊緣環724上形成鋁電鍍及陽極化層。雖然在圖8的實施例中係將構件600及ESC組件700顯示為使用在電漿處理腔室系統800的感應耦合電漿(ICP)反應器中,但應當理解的是,可使用其他構件、及/或電漿處理腔室的類型。可使用構件600的其他電漿處理腔室類型之示例為電容耦合電漿(CCP)處理腔室、晶邊電漿處理腔室、以及類似的處理腔室。在另一示例中,電漿處理腔室可為介電質處理腔室、或導體處理腔室。這種電漿處理腔室的示例係由Lam Research Corporation® of Fremont, CA所製造的Exelan Flex®
蝕刻系統。
與金屬合金不同的是,經陽極化的實質純鋁(以質量計至少為99%的純鋁)使固有的汙染風險減低。實質純鋁允許鋁氧化物層614的後續陽極化免於缺陷及空洞的疑慮。高純度鋁材料還提供使來自基板、或陽極化層中的電漿蝕刻腔室汙染大幅減低的附加益處。相較於在金屬基質複合物上進行獨立、標準的酸式陽極化,此種較優秀的結構在腐蝕、介電、及磨損性能中得到改善。
儘管本揭露已根據數個較佳實施例而進行描述,但存在著落入本揭露之範疇內的變更、置換、修改、及各種替代等同物。還應注意的是,存在著實行本揭露之方法及設備的許多替代方法。因此,係意旨將以下隨附之申請專利範圍解釋為包括落入本揭露的真實精神及範圍內的所有這種變更、置換、及各種替代等同物。
104,108,112,116,120:步驟
204:構件本體
208:鋁阻障層
212:金屬氧化物層
300:電漿處理腔室
304:電漿處理腔室
306:氣體分配板
307:基板
310:氣體源
316:靜電卡盤(ESC)
320:排氣幫浦
330:射頻(RF)功率源
335:控制器
348:ESC功率源
350:腔室壁
351:ESC溫度控制器
360:高流量襯套
362:狹槽
364:邊緣環
368:石英環
400:構件
404:構件本體
412:金屬氧化物層
504,508,512,516,520:步驟
600:電漿處理構件
604:基板本體
608:中央內徑
612:表面
616:鋁層
620:表面
624:陽極化層
700:ESC組件
704:靜電卡盤(ESC)
708:可動式邊緣環
712:外邊緣環
716:固定式邊緣環
718:孔口
720:覆蓋邊緣環
722:徑向內突出部
724:頂邊緣環
726:環形下凹部
728:中間內邊緣環
740:升降銷
744:套筒
748:孔口
752:加熱板
800:電漿處理腔室系統
802:電漿反應器
804:電漿處理腔室
806:電漿電源
808:功率匹配網路
810:變壓器耦合電漿(TCP)線圈
812:介電質感應功率窗
814:電漿
816:晶圓偏壓電源
818:偏壓匹配網路
824:控制器
830:氣體源
840:氣體注入器
841:鑿孔
842:壓力控制閥
844:幫浦
866:處理晶圓
872:峰部
876:腔室壁
本揭露係以示例性,而非限制性地被繪示於隨附圖式的圖中,且其中類似的元件符號係指相似元件,其中:
圖1為實施例的高階流程圖。
圖2A至圖2C係根據實施例所處理之邊緣環的橫截面示意圖。
圖3係可在實施例中使用的電漿處理腔室的示意圖。
圖4係根據另一實施例所處理之邊緣環的橫截面示意圖。
圖5為另一實施例的高階流程圖。
圖6A至圖6E顯示在電漿處理腔室中使用的邊緣環構件的製造方法的另一實施例。圖6A為邊緣環形式的構件基板的俯視圖。圖6B為圖6A之構件基板的橫截面圖。圖6C為圖6A之基板的表面的詳細橫截面圖。圖6D為將高純度鋁層電鍍至圖6A之基板的詳細橫截面圖。圖6E係圖6D的經電鍍結構進行陽極化,以形成電漿處理腔室所用之構件過後的詳細橫截面圖。
圖7為電漿處理腔室之一部分的截面圖。
圖8係可在實施例中使用的另一電漿處理腔室的示意圖。
104,108,112,116,120:步驟
Claims (24)
- 一種在半導體處理腔室中使用之構件的製造方法,包括: 從導電材料形成構件本體,該導電材料的熱膨脹係數低於10.0x10-6 /K;以及 在該構件本體上沉積金屬氧化物塗層。
- 如請求項1所述之在半導體處理腔室中使用之構件的製造方法,其中該沉積該金屬氧化物塗層係包括以該金屬氧化物塗層包覆該構件本體。
- 如請求項1所述之在半導體處理腔室中使用之構件的製造方法,其中該沉積該金屬氧化物塗層係包括: 沉積鋁阻障層;以及 將該鋁阻障層進行陽極化,以形成鋁氧化物塗層。
- 如請求項3所述之在半導體處理腔室中使用之構件的製造方法,其中係藉由電鍍而沉積該鋁阻障層。
- 如請求項1所述之在半導體處理腔室中使用之構件的製造方法,其中該構件本體包括導電半導體、鉬、或鈦本體,且其中沉積該金屬氧化物塗層係包括: 在該構件本體的表面上電鍍鋁層,該鋁層具有厚度;以及 對該鋁層的該厚度的一部分進行陽極化,以形成陽極化層; 其中該鋁層的該厚度的一部分係未經陽極化的,以在該陽極化層與該構件本體之間形成阻障物。
- 如請求項5所述之在半導體處理腔室中使用之構件的製造方法,其中該電鍍該鋁層係形成厚度介於約20微米(µm)至150 µm之間的鋁層。
- 如請求項5所述之在半導體處理腔室中使用之構件的製造方法,其中該電鍍該鋁層係形成厚度介於約25 µm至50 µm之間的鋁層。
- 如請求項5所述之在半導體處理腔室中使用之構件的製造方法,其中該陽極化層的厚度係介於約5 µm至50 µm之間,且其中未經陽極化的該鋁層的其中一些係形成厚度介於約7 µm至113 µm之間的鋁層。
- 如請求項5所述之在半導體處理腔室中使用之構件的製造方法,其中該對該鋁層的該厚度的一部分進行陽極化係包括在0o C至3o C的溫度、及大於60V的電壓下使該鋁層經受硫酸浴,而形成無水封的該陽極化層。
- 如請求項5所述之在半導體處理腔室中使用之構件的製造方法,其中該鋁層係直接與該構件本體相鄰設置,而無任何中間氧化物層。
- 如請求項3所述之在半導體處理腔室中使用之構件的製造方法,該鋁阻障層係以質量計為至少99%的純鋁。
- 如請求項1所述之在半導體處理腔室中使用之構件的製造方法,其中該導電材料包括矽、矽碳化物、及石墨的至少一者。
- 如請求項1所述之在半導體處理腔室中使用之構件的製造方法,其中該導電材料的熱膨脹係數低於5.0x10-6 /K。
- 一種在半導體處理腔室中使用的構件,包括: 構件本體,由熱膨脹係數低於10.0x10-6 /K的導電材料所製成;以及 金屬氧化物層,設置在該構件本體的表面上。
- 如請求項14所述之在半導體處理腔室中使用的構件,其中該導電材料包括導電半導體、鉬、或鈦。
- 如請求項14所述之在半導體處理腔室中使用的構件,其中該導電材料包括矽、矽碳化物、及石墨的至少一者。
- 如請求項14所述之在半導體處理腔室中使用的構件,其中該導電材料的熱膨脹係數低於5.0x10-6 /K。
- 如請求項14所述之在半導體處理腔室中使用的構件,更包括介於該構件本體與鋁氧化物層之間的鋁阻障層,且該鋁氧化物層係形成該金屬氧化物層。
- 如請求項18所述之在半導體處理腔室中使用的構件,其中該鋁阻障層的厚度係介於約20微米(µm)至150 µm之間。
- 如請求項18所述之在半導體處理腔室中使用的構件,其中該鋁氧化物層的厚度係介於約5 µm至50 µm之間。
- 如請求項20所述之在半導體處理腔室中使用的構件,其中鋁層的未經陽極化的一部分係形成厚度介於約7 µm至113 µm之間的鋁層。
- 如請求項18所述之在半導體處理腔室中使用的構件,其中該鋁阻障層係以質量計為至少99.9%的純度。
- 如請求項14所述之在半導體處理腔室中使用的構件,其中該構件係在該電漿處理腔室中使用的電極、噴淋頭、邊緣環、或高流量襯套的至少一者。
- 如請求項23所述之在半導體處理腔室中使用的構件,其中該構件形成邊緣環,該邊緣環圍繞著該電漿處理腔室內的靜電卡盤,而該靜電卡盤係支撐著晶圓以進行處理。