TW202032223A - 窗口及包含窗口的顯示裝置 - Google Patents

窗口及包含窗口的顯示裝置 Download PDF

Info

Publication number
TW202032223A
TW202032223A TW108148677A TW108148677A TW202032223A TW 202032223 A TW202032223 A TW 202032223A TW 108148677 A TW108148677 A TW 108148677A TW 108148677 A TW108148677 A TW 108148677A TW 202032223 A TW202032223 A TW 202032223A
Authority
TW
Taiwan
Prior art keywords
coating
window
layer
base layer
exemplary embodiments
Prior art date
Application number
TW108148677A
Other languages
English (en)
Other versions
TWI845588B (zh
Inventor
許眞寧
李吉成
孫晧碩
李鎔錫
李東云
全裕軾
崔汎奎
Original Assignee
南韓商三星顯示器有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 南韓商三星顯示器有限公司 filed Critical 南韓商三星顯示器有限公司
Publication of TW202032223A publication Critical patent/TW202032223A/zh
Application granted granted Critical
Publication of TWI845588B publication Critical patent/TWI845588B/zh

Abstract

一窗口包含基礎層及第一塗層。第一塗層設置在基礎層的第一表面上。第一塗層為單層。第一塗層包含矽氧烷基化合物。矽氧烷基化合物包含氟及氧化矽。

Description

窗口及包含窗口的顯示裝置
相關申請案之交互參照
本申請案主張於2019年1月2日提出之韓國專利申請號第10-2019-0000284號的優先權與效益，其全部揭露內容在此併入全文作為參考。
例示性實施例實質上關於一種窗口及包含窗口的顯示裝置。
顯示裝置包含液晶顯示器(LCD)、有機發光二極體(OLED)顯示器，或其類似物可使用於多種移動電子裝置，例如行動電話、導航系統、數位相機、電子書、攜帶式遊戲機及各種終端等等。使用在這類移動電子裝置的典型的顯示裝置可具有透明的覆蓋窗(在下文稱為窗口(window))，提供在顯示面板的前方且用戶可通過它看到圖像。由於窗口可組成在裝置的最外側的位置，窗口應可耐受外部環境以保護顯示裝置(例如其內部)的顯示面板。更進一步，作為使用按鈕或鍵盤作為輸入裝置的傳統方法的替代，現已應用與顯示螢幕合併的觸控式面板的結構。因此，窗口的表面會比利用傳統輸入機制的移動裝置更頻繁地被手指或類似方式接觸。
在本部份揭露的上述資訊僅用於理解發明概念的背景，也因此可能包含非構成先前技術的資訊。
部分例示性實施例可提供具有簡單製程及薄厚度的窗口。
部分例示性實施例可提供製造具有簡單製程及薄厚度的窗口的方法。
部分例示性實施例可提供包含簡單製程及薄厚度的窗口的顯示裝置。
其他態樣將在下文詳細地說明，且部分將會在揭露中顯而易見，或可從發明概念的實踐來理解。
根據部分例示性實施例，窗口包含基礎層及第一塗層。第一塗層設置在基礎層的第一表面上。第一塗層是一單層。第一塗層包含矽氧烷基化合物。 矽氧烷基化合物包括氟及氧化矽。
根據部分例示性實施例，顯示裝置包含顯示面板及窗口。窗口與顯示面板重疊。窗口包含基礎層及第一塗層。第一塗層設置在基礎層上。第一塗層為一單層。第一塗層包含多孔氧化矽(porous silica)及氣相氧化矽(fumed silica)。
根據部分的例示性實施例，製造窗口的方法包含準備窗口的基礎層；以及藉由濕式塗佈製程將第一塗層形成在基礎層的第一表面上。第一塗層是由單層形成。第一塗層包含多孔氧化矽、氣相氧化矽及矽氧烷基化合物的至少其中之二。矽氧烷基化合物包含氟。
根據各種例示性實施例，可簡化窗口的製程，藉此不僅可減少製造時間，也能降低製造成本。除此之外，藉由窗口（例如窗口的表面）可提供防反光、防眩光、及防指紋的功能。
上述一般說明及下文的詳細說明為示例性及說明性的，目的是為申請專利範圍提供進一步的解釋。
在下文的說明中，基於解釋的目的，闡述了許多具體細節以提供對各種例示性實施例的透徹理解。如本文中所使用的「實施例(embodiment)」及「實施(implementation)」可以互換的使用，並且為採用一個或多個本文中所揭露的發明概念的非限制性的例子。顯而易見的，各種例示性實施例可以在沒有這些具體細節的狀況下或以一種或多種等效佈置以實踐。在其他例子中，以方塊圖的形式示出了習知的結構和設備，以避免不必要的混淆各種例示性實施例。進一步的，各種例示性實施例可以不同，但不互斥。例如，在不偏離本發明概念的狀況下，一個例示性實施例中的特定形狀、構造、特徵可以使用或實施在另一個例示性實施例中。
除非另有明確的指定，所示出的例示性實施例應理解為提供部分例示性實施例的細節變化的例示性的特徵。因此，除非另有明確的指定，在不脫離本發明概念的狀況下，特徵、組件、模組、層、膜、板、區域、態樣等(在下文中獨立或統稱為「元件」)，可以以其他方式組合、分離、互換、及/或重新排列。
附圖中剖面線(cross-hatching)及/或陰影的使用通常是用以澄清相鄰元件的邊界。因此，除非另有指定，否則無論是否存在交叉影線或陰影都不能表達或指示對特定材料、材料特性、尺寸、比例、所示的元件之間的共通性、及/或任何其他特徵、屬性、特性等的偏好或需求。進一步的，附圖中元件的尺寸及相對尺寸為了闡明及/或說明目的而可以誇大。因此各元件的尺寸及相對尺寸不限定於附圖中所示出的尺寸及相對尺寸。當一例示性實施例可以不同的實施時，可以以不同於說明的順序執行特定的步驟順序。例如，兩個連續說明的步驟可以實質上同時執行或以與說明的順序相反的順序執行。此外，相同的元件符號表示相同的元件。
可以理解的是，當一元件，例如，層，稱作在另一元件「上(on)」，或者「連接至(connected to)」、「耦接至(coupled to)」另一元件時，它可以直接在另一元件之上，或者直接連接至、耦接至另一元件，或者可以存在中間元件。然而，當元件稱作「直接在(directly)」另一元件「上(on)」，「直接連接至(directly connected to)」、「直接耦接至(directly coupled to)」另一元件時，則不存在中間元件。其他用於說明元件之間的關係的術語及/或句子應以類似的方式解釋，例如，「之間(between)」與「直接在之間(directly between)」、「相鄰(adjacent)」與「直接相鄰(directly adjacent)」、「上(on)」與「直接在上(directly on)」等。進一步的，術語「連接(connected)」可以為物理、電性、及/或流體連接。除此之外，X軸、Y軸及Z軸不限於直角坐標系的三個軸，而可在更廣泛的意義上解釋。例如，X軸、Y軸及Z軸可互相垂直，也可代表不互相垂直的其他方向。為了本揭露的目的，「X、Y、及Z中的至少一個」及「從包含X、Y、及Z的組合中選擇至少一個」可以被解釋為僅X、僅Y、僅Z，或X、Y、及Z中兩個或複數個的任意組合，例如，XYZ、XYY、YZ、及ZZ。 如本文所使用的，術語「及/或」包含一個或複數個所列出的相關聯項目的任何及所有組合。
儘管術語「第一(first)」、「第二(second)」等在本文中可以用於說明各種類型的元件，但這些元件不應受到這些術語的限定。這些術語用於將一個元件與另一個元件分開。因此，在不脫離本揭露的教導的狀況下，下文中的第一元件可以稱作第二元件。
空間相對術語如「下(beneath)」、「下(below)」、「下(under)」、「低於(lower)」、「上(above)」、「上(upper)」、「上(over)」、「高於(higher)」、「側(side)」(例如，在側壁(sidewall)中)、及其相似詞，在本文中僅用於說明目的，以說明附圖中示出的一個元件與另一個元件之間關係。除了附圖中所示出的方向之外，空間相對術語還意圖包含使用、操作、及/或製造中的裝置的不同方向。例如，當一個圖中的裝置被翻轉後，被說明為在其他元件或特徵「下(beneath)」或「下(below)」的元件將被定向為在其他元件或特徵「上(above)」。因此，例示性術語如「下(below)」可以包含上方及下方兩個方向。進一步的，裝置能以其他方式定向(例如，旋轉90度或其他方向)，並且本文中使用的空間相對術語應做相對應的解釋。更進一步，為了本揭露的目的，片語「在一平面上(on a plane)」意思為從頂部觀看物件的部分，而片語「在一剖面上(或中)(on (or in) a cross-section)」意思為從一側垂直切開的物件部分觀看其截面。
在本文中使用的術語僅用於說明特定實施例的目的，而非限定本發明概念。如本文所使用的單數形式「一(a)」、「一(an)」及「該(the)」也意圖包含複數形式，除非上下文明確的另外指出。此外，在本說明書中使用的術語「包含(comprises)」、「包含(comprising)」、「包含(includes)」、及/或「包含(including)」時，指定所陳述的特徵、整體、步驟、操作、元件、組件、及/或其上的組合存在，但不排除一個或複數個其他特徵、整體、步驟、操作、元件、組件、及/或其上的組合存在或附加。此外，如本文所使用的術語「實質上(substantially)」、「約(about)」和其他類似術語被用作近似詞而非度量詞，並且用於解釋測量、計算、及提供數值的固有誤差，且可以被本領域具有通常知識者所認可。
本文中係以剖面圖、等角視圖、透視圖、平面圖、及/或分解圖以說明各種例示性實施例，這些圖是理想化的例示性實施例及/或中間結構的示意圖。因此，由於如製造技術及/或公差所導致的圖示形狀的變化是可以預期的。因此，本文中所揭露的例示性實施例不應解釋為限定區域的特定示出形狀，而應包含如由於如製造而引起的形狀偏差。為此，附圖中所示出的區域本質上可以是示意性的，並且這些區域的形狀可以不反映裝置的區域的實際形狀，因此，其不應為對本發明的限制。
除非另有定義，本文中所使用的所有術語(包含技術及科學術語)具有與本揭露內容所屬的領域具有通常知識者的通常理解相同的含意。術語，例如在常用字典中定義的術語，應被解釋為具有與相關領域中的術語一致的含義，並且不應以理想化或過於正式的解釋，除非在本文中另有明確的定義。
如本領域的慣例，部分例示性實施例依照附圖中的功能塊、單元、及/或模組以說明及示出。本領域具有通常知識者將可以理解，這些功能塊、單元及/或模組是透過電子(或光學)電路以物理上的實現，例如，邏輯電路、離散組件、微處理器、硬佈線電路、記憶體元件、接線裝置，以及可以使用基於半導體的製造技術或其他製造技術來形成的其類似物。在此狀況下，功能塊、單元、及/或模組透過微處理器及其他相似的硬體實施，其可以使用軟體(例如，微碼)程控及控制以執行本文所討論的各種功能，並且可以選擇性的透過韌體及/或軟體驅動。還可以預期的是，各功能塊、單元及/或模組可以透過專用的硬體以實現，或者由執行部分功能的專用硬體與執行其他功能的處理器（例如，一個或複數個經編程的微處理器和相關電路）的組合以實現。此外，在不脫離本發明概念的狀況下，部分例示性實施例的各功能塊、單元及/或模組可以物理的分開成兩個或更多個相互作用且離散的功能塊、單元及/或模組。進一步的，在不脫離本發明概念的狀況下，部分例示性實施例的功能塊、單元及/或模組可以物理的結合至更多複雜的塊、單元及/或模組。
在下文中，各種例示性實施例將參照附圖進行詳細說明。
現在，參考第1圖及第2圖說明根據部分例示性實施例的顯示裝置。第1圖為根據部分例示性實施例的顯示裝置的剖面示意圖。第2圖為根據部分例示性實施例的多孔氧化矽的剖面示意圖。
如第1圖所示，根據部分例示性實施例的顯示裝置包含顯示面板 100及設置在顯示面板 100上的窗口 300。黏著顯示面板 100及窗口 300的黏著層 220設置在顯示面板 100及窗口 300之間。
顯示面板 100可為可撓的、可伸縮的、可折疊的、可彎折的、可捲的及/或以其它方式變形的。下文中，用語可撓的、可伸縮的、可折疊的、可彎折的、可捲的及/或以其它方式變形的將單獨及/或統稱為可撓的。顯示面板 100可具有可撓性而可彎折，但顯示面板 100不限於此。例如，顯示面板 100可為平坦的或包含至少一部份平坦及至少一部分可撓的，但不限於此。
顯示面板 100可為有機發光顯示(OLED)面板。雖然未示出，顯示面板 100可至少包含基板、設置在基板上的複數個薄膜電晶體、以及複數個電極。
雖然顯示面板 100是說明為OLED面板，但例示性實施例並不限於此。根據部份例示性實施例，顯示面板 100可為液晶顯示面板(LCD)、量子點有機發光顯示面板(QD-OLED)、無機發光顯示面板、量子點液晶顯示面板(QD-LCD)、量子奈米發光顯示面板(QNED)、微發光顯示面板、電泳顯示面板及電濕潤顯示器等等至少其中之一。
黏著層 220置於顯示面板 100及窗口 300之間。黏著層 220結合(或以其他方式耦合)顯示面板 100及窗口 300。黏著層 220可為透明聚合物樹脂層，及例如可包含光學透明膠(optically clear adhesive , OCA)、光學透明樹脂(optically clear resin, OCR)、感壓型黏著劑(PSA)及光學彈性樹脂(super view resin, SVR)至少其中之一，但例示性實施例不限於此。
光阻層 210可設置在黏著劑 220及窗口 300之間。光阻層 210可包含有能力阻擋及/或吸收光的材料。根據部份例示性實施例的光阻層 210可設置以對應顯示裝置的外框區域。根據部分例示性實施例，光阻層 210也可省略。
窗口 300設置在顯示面板 100上，並可藉由黏著層 220附著在顯示面板 100。窗口 300可保護顯示面板 100免於外部的影響，例如保護顯示面板 100免受灰塵、碎屑、濕氣及衝擊等。
根據部份例示性實施例的窗口包含基礎層 310及第一塗層 330。
基礎層 310可為板狀。根據部份例示性實施例的基礎層 310可為玻璃基板或塑膠基板。為便於描述及說明，基礎層 310的結構是由一單層構成，但基礎層 310也可由複數層形成。
基礎層310可包含例如含矽酸鹽的玻璃材料。玻璃材料可進一步含有(或包含)額外的材料以提供耐久性、表面平滑性及透明性。例如，基礎層 310 可包含鋁矽酸鹽(aluminosilicates)、硼矽酸鹽(borosilicates)及硼鋁矽酸鹽(boro-aluminosilicates)或其類似物等至少其中之一。基礎層 310可進一步包含鹼金屬、鹼土金屬及其氧化物中至少其中之一。然而可預期的是，例示性實施例不限於前述用於基礎層 310的材料。
基礎層 310可包含面向第一塗層 330的第一表面 311以及面向顯示面板 100的第二表面 312。此外，基礎層 310包含垂直於第一表面 311及第二表面 312的垂直表面 315。
第一塗層 330設置在窗口 300的外部表面上。第一塗層 330可與基礎層 310的第一表面 311重疊。第一塗層 330可直接接觸到基礎層 310的第一表面 310，但例示性實施例不限於此。第一塗層 330可設置在使用者的觸碰直接執行的第一表面311上。第一塗層 330可具有防眩光、防反射以及防指紋的特徵或功能中至少其中之一，以至少防止(或減少)指紋出現在窗口 300上。
第一塗層 330可為單層。第一塗層 330可藉由單一層來提供防眩光、防反射及/或防指紋特徵的效果。
第一塗層 330可包含含有氟、多孔氧化矽及氣相氧化矽的矽氧烷基化合物中至少其中之二。第一塗層 330可包含含有氟及多孔氧化矽的矽氧烷基化合物、含有氟及氣相氧化矽的矽氧烷基化合物、含有多孔氧化矽及氣相氧化矽的矽氧烷基化合物及/或含有氟、多孔氧化矽及氣相氧化矽的矽氧烷基化合物。
第一塗層 330可包含第一溶液(或化合物)的固化體(cured body)。第一溶液可包含含有氟、多孔氧化矽及氣相氧化矽中至少其中之二的矽氧烷基化合物。第一溶液可包含含有氟及多孔氧化矽的矽氧烷基化合物、含有氟及氣相氧化矽的矽氧烷基化合物、含有多孔氧化矽及氣相氧化矽的矽氧烷基化合物及/或含有氟、多孔氧化矽及氣相氧化矽的矽氧烷基化合物。
含氟的矽氧烷基化合物可包含，例如十七氟癸基三甲氧基矽烷(heptadecafluorodecyltrimethoxysilane)、十三氟代辛烷基三乙氧基矽烷(tridecafluorooctyltriethoxysilane) 或十七氟癸基三異丙氧基矽烷(heptadecafluorodecyl triisopropoxysilane)。含氟的矽氧烷基化合物可含在第一溶液內所有成分中約佔4重量百分比(wt%)至7 wt%。當含氟矽氧烷基化合物的含量超出上述含量時，可能難以同時達到窗口 300的防眩光、防反射及防指紋的效果。此外，含氟的矽氧烷基化合物的含量可介於約5 wt%至約6 wt%、例如約4 wt%至約5 wt%、例如約6 wt%至約7 wt%及例如約4.5 wt%至約6.5 wt%。
根據部分例示性實施例，第一塗層 330包含含有氟的矽氧烷基化合物可為窗口 300提供防指紋效果。第一塗層 330的接觸角可藉由含氟的矽氧烷基化合物增加。
在部分例示性實施例，多孔氧化矽可包含例如二氧化矽。多孔氧化矽可含在第一溶液的全部成分的約4 wt%至7 wt%。如果多孔氧化矽的含量超出上述含量時，可能會難以同時達到窗口 300的防眩光、防反射及防指紋的效果。此外，多孔氧化矽可為含有約5 wt%至約6 wt%的含量、例如約4 wt%至約5 wt%、例如約6 wt%至約7 wt%及例如約4.5 wt%至約6.5 wt%。
如第2圖所示，多孔氧化矽 33可含有空心。多孔氧化矽 33的形狀具有在其中形成中空的空間。例如多孔氧化矽 33可以形成環形構型，但例示性實施例並不限於此。
多孔氧化矽 33的直徑 t1可能從約50 nm至約100 nm、例如約70 nm至約80 nm、例如約50 nm至約70 nm、例如約75 nm至約100 nm、例如約60 nm至約75 nm。多孔氧化矽 33包含的中空的直徑 t3可能從約30 nm至約60 nm、例如約40 nm至約50 nm、例如約30 nm至約45 nm、例如約45 nm至約60 nm、例如約45 nm至約55 nm。環繞中空的外殼的厚度 t2可能從約10 nm至約30 nm、例如約15 nm至約25 nm、例如約20 nm至約30 nm、例如約10 nm至約25 nm及例如約20 nm至約25 nm。
根據部分例示性實施例，含有多孔氧化矽的第一塗層 330可具有防止來自(或形成自)外部光線的反射的效果(或功能)。根據例示性實施例包括多孔氧化矽的第一塗層 330的表面反射率可大於0並小於約2.5%，且可大於0並小於約1.3%。
根據部分例示性實施例的氣相氧化矽可包含例如非晶質氣相氧化矽。氣相氧化矽可包含從約0.1 wt%至約0.5 wt%的第一溶液的全部成分、例如約0.2 wt%至約0.4 wt%、例如0.1 wt%至約0.3 wt%、例如約0.3 wt%至約0.5 wt%及例如0.25 wt%至約0.35 wt%。如果氣相氧化矽的含量超出上述含量，可能會難以同時達到窗口 300的防眩光、防反射及防指紋的效果。
氣相氧化矽的直徑可從約5 nm至約10 nm、例如約6 nm至約9 nm、例如約5 nm至約8 nm、例如約7 nm至約10 nm、例如約7 nm至約8 nm。
根據部分例示性實施例，含氣相氧化矽的第一塗層 330可具有防眩光的效果。包括含氣相氧化矽的第一塗層 330的窗口 300的光澤度(gloss)可從約100 GU(光澤度單位)至約120 GU、例如105 GU至約115 GU、例如 110 GU至約120 GU、例如100 GU至約115 GU及例如108 GU至約112 GU。
此外，第一溶液可含有環氧矽烷、酸催化劑及溶質的至少其中之一。
環氧矽烷可包含例如三乙氧基矽烷(triethoxysilane)。環氧矽烷在第一溶液的全部成分中含有的量可從約3 wt%至約5 wt%、例如從3.5 wt%至4.5 wt%、例如約3 wt%至約4 wt%、例如約4 wt%至約5 wt%及例如約3.8 wt%至約4.2 wt%。
酸催化劑例如可包括苯四羧酸酐(benzene tetracarboxylic anhydride)。酸催化劑在第一溶液的全部成分中含有的量從約0.1 wt%至約0.5 wt%、例如約0.2 wt%至約0.4 wt%、例如約0.1 wt%至約0.3 wt%、例如約0.3 wt%至約0.5 wt%及例如0.25 wt%至約0.35 wt%。
第一溶液可含有剩餘溶劑，並且剩餘溶劑可為例如丙二醇甲醚。
第一溶液的黏度可從約1.0 cps(厘泊)至約5.0 cps、例如約2.0 cps至約4.0 cps、例如約1.0 cps至約3.5 cps、例如3 cps至約5.0 cps及例如約2.5 cps至約3.5 cps。
第一塗層 330可藉由濕式塗佈法形成在基礎層 310上。舉例來說，第一塗層 330可使用滑動式塗佈機(slip coater)、棒塗機(bar coater)、旋塗機(spin coater)、噴塗機(spray coater)及/或類似物來形成。例如第一溶液可利用噴塗機塗佈在基礎層 310上，且塗佈溶液可在180°C至200°C中固化30分鐘後形成第一塗層 330。如果第一塗層 330是使用乾式塗佈法形成，則由於製造過程中提供的基礎層 310的高度差可能發生沉積距離差。因此乾式塗佈法形成的第一塗層可能無法均勻地形成且由乾式塗佈形成的第一塗層可能出現色差。
然而當第一塗層 330是使用濕式塗佈法形成時，根據部分例示性實施例，第一塗層 330可均勻地形成在基礎層 310上。由於可減少窗口 300造成的色差，而能夠提供優異的(或至少改善的)品質的顯示裝置。
根據部分例示性實施例的第一塗層 330可在單層中含有氣相氧化矽、多孔氧化矽及含氟的矽氧烷基化合物。根據部分例示性實施例的第一塗層 330可具有各種由單層提供的效果，其可提供窗口 300 簡單的生產程序及優秀的品質。
接著，參照自第3圖說明根據部分例示性實施例的顯示裝置。第3圖係為根據部分例示性實施例的顯示裝置的剖面圖。與上述結構相同的結構的說明將被省略。
根據部分例示性實施例的顯示裝置可包含外殼 400圍繞顯示面板 100及窗口 300_1。外殼 400不限於所示的形式，且可具有任何圍繞顯示面板 100及窗口 300的形態。
根據部分例示性實施例的窗口 300_1包含基礎層 310_1及第一塗層330_1。
基礎層 310_1可為玻璃基板或塑膠基板。基礎層可包含例如含矽酸鹽的玻璃材料。玻璃材料可進一步包含額外的材料提供耐久性、表面平滑性及透明性。例如基礎層 310_1可包含鋁矽酸鹽、硼矽酸鹽及硼鋁矽酸鹽，及其類似物的至少其中之一。基礎層 310_1可進一步包含鹼金屬、鹼土金屬及其氧化物的至少其中之一，然而，例示性實施例不限於上述材料。
根據部分的例示性實施例，基礎層 310_1包含第一表面 311面向第一塗層 330、第二表面 312面向顯示面板 100、以及垂直表面 315垂直於第一表面 311及第二表面 312。第一表面 311為朝向使用者(或第一塗層 330_1)的表面，且第二表面 312為朝向顯示面板 100並與光阻層 210及黏著層 220重疊的表面。
基礎層 310_1可包含傾斜於第一表面 311的第一傾斜表面 313，例如以大於0°且小於90°的角度傾斜。第一傾斜表面 313連接第一表面 311及垂直表面 315。基礎層 310_1可包含傾斜於第二表面 312的第二傾斜表面 314，例如以大於0°且小於90°的角度傾斜。第二傾斜表面 314連接第二表面 312及垂直表面 315。
第一塗層 330_1可與基礎層 310的第一表面 311重疊。另外，第一塗層 330_1可與第一傾斜表面 313的一部分重疊，但例示性實施例不限於此。
第一塗層 330_1可具有沿著基礎層 310_1的一側傾斜的形狀，例如沿著基礎層 310_1的第一傾斜表面 313。第一塗層 330_1可由具有預定黏度的溶液形成。在塗佈及固化此溶液的過程中，第一塗層 330_1的末端可具有朝向基礎層 310_1的一側的錐形形狀。第一塗層 330_1的末端的厚度可朝向基礎層 310的第一傾斜面 313減少。
接著，根據部分例示性實施例的顯示裝置，參照第4至第6圖說明。第4、5及6圖為根據各種例示性實施例的窗口的剖面圖。省略了與上述元件相同的元件的說明。
首先，參考第4圖，第一塗層 330_2的末端可具有沿著第一傾斜表面 313的傾斜形狀。第一塗層 330_2可由具有預定黏度的溶液形成。在塗佈及固化此溶液的過程中，第一塗層 330_2的末端可具有朝向基礎層 310_1的一側的錐形形狀。第一塗層 330_2的末端的厚度可朝向基礎層 310_1的第一傾斜面 313減少。
另外，第一塗層 330_2的末端可對齊第一傾斜表面 313的末端。然而，例示性實施例不限於此。例如第一塗層 330_2可完全覆蓋在第一傾斜表面 313及其末端可設置在垂直表面 315上。
接著，參考第5圖，連接基礎層310_2的第一表面 311及垂直表面 315的第一傾斜表面 313_1可包含凸狀的曲面。雖然以具有凸狀的曲面的第一傾斜面 313_1進行說明，但例示性實施例不限於此。例如，第一傾斜面 313_1的形狀可包含具有凹狀的曲面或具有曲率的任何形狀。第一塗層 330_1可部分地與凸狀的第一傾斜面 313_1重疊。例如第一塗層 330_1的末端可與凸狀的第一傾斜面 313重疊。
參考第6圖，連接基礎層310_2的第一表面 311及垂直表面 315的第一傾斜表面 313_1可包含凸狀的曲面。
第一塗層 330_3的末端可具有沿著第一傾斜面 313_1的傾斜形狀。第一塗層 330_3可由具有預定黏度的溶液形成。在塗佈及固化此溶液的過程中，第一塗層 330_3的末端可具有朝向基礎層 310_2的一側的錐形形狀。第一塗層 330_3的末端的厚度可朝向基礎層 310_2的第一傾斜面 313減少。
第一塗層 330_3可與凸狀的第一傾斜表面 313_1重疊。第一塗層 330_3可根據部分例示性實施例完全覆蓋凸狀的第一傾斜表面 313_1。第一塗層 330_3的末端可對齊第一傾斜表面 313_1的末端，但例示性實施例不限於此。例如第一塗層 330_3可設置在垂直表面 315上。
接著，參照自第7及第8圖說明例示性實施例及比較例。第7圖顯示比較例及根據部分例示性實施例的反射率圖表。第8圖顯示比較例及根據部分例示性實施例的顏色座標。
參考第7圖，例示性實施例為包含基礎層及由單層構成的第一塗層的窗口，而比較例 1至比較例 4顯示分開地包括基礎層、用於防眩光的表面處理層、防反射塗層及防指紋的塗層的窗口。比較例 1至比較例 4包含相同的表面處理層及塗層，但基礎層的厚度或表現則不同。
如第7圖所示，可確認例示性實施例在 400nm至 700nm的整個波長區域展現幾乎固定的反射率(約 1.3%至 1.7%)。根據例示性實施例的窗口在整個波長區域展現均勻的反射率，因此提供的顏色沒有色差且外部光線的反射減少效果(reflection reduction effect)可十分出色。
另一方面，在比較例 1至比較例 4的情況下，根據波長可觀察到約 5%的反射率差。在這種情況下，部分波長與其他波長相比可能會過度反射，且因此光線提供給使用者的顏色可能會發生色差。
參考第8圖，可確認例示性實施例具有更接近顏色座標中心的顏色座標。換言之，可確認例示性實施例的色純度(color purity)優於比較例。
例如，參考第8圖及下表1，根據部分例示性實施例的顏色座標(a*,b*)可為0.45及0.11，且因此，窗口的外觀表現出中性色(neutral color)。另一方面，在比較例2的情況中，顏色座標可為-1.55及-1.55，並如同第8圖所示，外觀表現出淡藍色。在比較例 3的情況中，可藉由第8圖確認外觀也表現出淡藍色。另一方面，比較例 5的顏色座標可為-0.07及-2.06，並且可確認外觀表現出淡紫色。比較例 5包含了上述比較例1至比較例4相同的表面處理層、塗層，但窗口的基礎層不同。需要注意比較例5沒有在第8圖描繪，而是提供於表1。
表 1
  光澤度 (GU) 表面反射率(%) 外觀 接觸角 (Degrees) 表面硬度
例示性實施例 104.8 1.31 灰色 120.6 5H
比較例2 94.5 0.51 淡藍 119.0 5-6H
比較例5 101.2 0.71 淡紫 114.5 5-6H
另外，可以確認的是例示性實施例的光澤度為約104.8 GU、比較例 2的光澤度為約94.5 GU且比較例 5的光澤度為約101.2 GU。可以確認的是即使例示性實施例僅含有單層，依然可以獲得足夠的光澤度。除此之外，可以確認的是例示性實施例的表面反射、接觸角及表面硬度皆與比較例相類似。與分開地包括防反射層、防指紋層及其類似物的比較例相比，可確認僅包括單層的例示性實施例具有足夠的防止反射效果、表面硬度及防指紋效果(接觸角)。
接著，參考第9及第10圖說明根據部分例示性實施例的第一塗層所包含的材料。第9圖為根據部分例示性實施例的氣相氧化矽(Fumed Silica)的圖式。第10圖為根據部分例示性實施例的多孔氧化矽(Porous Silica)的圖式。
根據第9圖可確認根據部分例示性實施例的氣相氧化矽具有約5 nm至10 nm的直徑。另外根據第10圖可確認根據部分例示性實施例的多孔氧化矽具有包含中空的球形形狀。
在另外一方面，當如至少其中一個比較例將反眩光處理分開執行，且分開地包含防反射層及防指紋層時，製造過程的製造成本會大幅增加。然而，根據各種例示性實施例，製造成本可為比較例中至少其中之一的約六分之一，使其在減少製造成本方面相當優異。
雖然特定的例示性實施例及實施已經在本文中說明，其他實施例及調整將透過本說明而變得顯而易見。相應的，本發明概念不限定於這些實施例，而是屬於所附的申請專利範圍中更廣泛之範圍以及各種顯而易見的修改和等效配置。
33:多孔氧化矽 100:顯示面板 210:光阻層 220:黏著層 300, 300_1, 300_2, 300_3:窗口 310, 310_1, 310_2:基礎層 311:第一表面 312:第二表面 313, 313_1:第一傾斜表面 314:第二傾斜表面 315:垂直表面 330,330_1,330_2,330_3:第一塗層 400:外殼 t1:多孔氧化矽的直徑 t2:環繞中空的外殼的厚度 t3:多孔氧化矽包含的中空的直徑
附圖的圖式係包含以提供對本發明概念進一步的理解，並且併入及構成本說明書的一部份，說明本發明概念的例示性實施例，並與其說明一起用於解釋本發明概念的原則。 第1圖係根據部分例示性實施例的顯示裝置的剖面示意圖。 第2圖係根據部分例示性實施例的多孔氧化矽的剖面示意圖。 第3圖係根據部分例示性實施例的顯示裝置的剖面示意圖。 第4、5及6圖係根據各種例示性實施例的窗口的剖面圖。 第7圖係為比較例及根據部分例示性實施例的反射率的圖表。 第8圖係為比較例及根據部分例示性實施例的顏色座標的圖像。 第9圖係根據部分例示性實施例的氣相氧化矽的圖像。 第10圖係根據部分例示性實施例的多孔氧化矽的圖像。
100:顯示面板
210:光阻層
220:黏著層
300:窗口
310:基礎層
311:第一表面
312:第二表面
315:垂直表面
330:第一塗層

Claims (10)

  1. 一種窗口，其包含： 一基礎層；以及 一第一塗層設置在該基礎層的一第一表面上， 其中： 該第一塗層為一單層； 該第一塗層包含一矽氧烷基化合物；且 該矽氧烷基化合物包含氟及氧化矽。
  2. 如請求項1所述之窗口，其中該氧化矽包含多孔氧化矽及氣相氧化矽。
  3. 如請求項2所述之窗口，其中： 該多孔氧化矽包含一中空；且 該中空的直徑約約30nm至約60nm。
  4. 如請求項1所述之窗口，其中含氟之該矽氧烷基化合物包含十七氟癸基三甲氧基矽烷(heptadecafluorodecyltrimethoxysilane)。
  5. 如請求項1所述之窗口，其中該第一塗層的一末端沿著該基礎層的一表面傾斜。
  6. 如請求項1所述之窗口，其中該基礎層包含： 一第二表面與該第一表面重疊； 一垂直表面垂直於該第一表面及該第二表面； 一第一傾斜表面連結該第一表面及該垂直表面；以及 一第二傾斜表面連結該第二表面及該垂直表面。
  7. 如請求項6所述之窗口，其中該第一塗層與該第一傾斜表面重疊。
  8. 如請求項6所述之窗口，其中該第一傾斜表面為一曲面。
  9. 一種顯示裝置，其包含： 一顯示面板；以及 一窗口與該顯示面板重疊， 其中該窗口包含： 一基礎層；以及 一第一塗層設置在該基礎層上， 其中： 該第一塗層為一單層；且 該第一塗層包含多孔氧化矽及氣相氧化矽。
  10. 如請求項9所述之顯示裝置，其中該第一塗層的一末端沿著該基礎層的一表面傾斜。
TW108148677A 2019-01-02 2019-12-31 窗口及包含窗口的顯示裝置 TWI845588B (zh)