TR201704502A2 - DECORATIVE WALL PLASTER WITH HEAT AND SOUND INSULATION - Google Patents
DECORATIVE WALL PLASTER WITH HEAT AND SOUND INSULATION Download PDFInfo
- Publication number
- TR201704502A2 TR201704502A2 TR2017/04502A TR201704502A TR201704502A2 TR 201704502 A2 TR201704502 A2 TR 201704502A2 TR 2017/04502 A TR2017/04502 A TR 2017/04502A TR 201704502 A TR201704502 A TR 201704502A TR 201704502 A2 TR201704502 A2 TR 201704502A2
- Authority
- TR
- Turkey
- Prior art keywords
- cotton
- crumb
- masonry
- powder
- feature
- Prior art date
Abstract
Buluş konusu ısı ve ses yalıtımlı dekoratif duvar sıvası, temel yapılanmasında vermikulit, sodyum karbokstimetil selüloz ? cmc, asel td 700, asel td 2000, asel ty 300, asel hv, su, pamuk (saf, toz, kırık, granül ve kumaş hali), mika taşı, yün kumaş, kaya tuzu (toz hali), saman ve yulaf parçası, toz halinde ponza taşı, mixs veya toz halinde bimiss taşından en az bir kaçını içerebilecek şekilde, farklı yapılanmalarda meydana getirilebilmektedir. Tüm ürünler uygulama esnasında su ile hamur kıvamına getirilene kadar karıştırılır ve mika mala ile sıvanır.The heat and sound insulating decorative wall plaster subject of the invention is vermiculite, sodium carboxymethyl cellulose in its basic structure. cmc, asel td 700, asel td 2000, asel ty 300, asel hv, water, cotton (pure, powder, broken, granule and fabric state), mica stone, wool fabric, rock salt (powder state), straw and oat piece It can be formed in different configurations, including at least a few of powdered pumice stone, mixs or powdered bimiss stone. During the application, all products are mixed with water until it becomes a dough and plastered with a mica trowel.
Description
TARIFNAME Teknik Alan Bulus evlerde, yurtlarda, çocuk kreslerinde, hastanelerde, ofislerde, otel ve motel benzeri kapali mekanlarda, sivama, yapistirma, baski ve presleme yöntemleri ile meydana getirilen dekoratif ses izolasyonu ve isi yalitimi saglayan siva duvar sivasi kaplamasi ile ilgilidir. Önceki Teknik Bilinen teknikte piyasada görsel olarak dekoratif amaçli renkli sivalar bulunmaktadir. DESCRIPTION Technical Area Bulus can be found in homes, dorms, kindergartens, hospitals, offices, hotels and motels. in similar closed spaces, with plastering, gluing, printing and pressing methods. plaster wall plaster that provides decorative sound insulation and heat insulation relates to the coating. Prior Art In the known technique, there are colored plasters for visually decorative purposes in the market.
Bu ürünler yüksek isiya karsi dayanikli olmamalari, alev almalari, ses izolasyonlarinin yetersiz olmasi, kullanim alaninda dökülmelerden dolayi ömürlerinin kisa olmasi, tehlikeli atik malzemeler ve kimyasal içerikli malzemeden yapilmalari, iletken olmalari, uygulama esnasinda elleri tahris etmeleri, yanma esnasinda zehirli gaz çikarmalari gibi sorunlara sebep olmaktadirlar. These products are not resistant to high heat, flaming, sound Inadequate insulation, loss of life due to spills in the usage area. they are short, they are made of hazardous waste materials and chemical-containing materials, being conductive, irritating hands during application, toxic during burning they cause problems such as gas extraction.
Bulus konusu dekoratif duvar sivasi bilinen teknikte bahsedilen sorunlarin üstesinden gelinmesi amaci ile meydana getirilmistir. The decorative wall plaster of the invention overcomes the problems mentioned in the prior art. was created for the purpose.
Bulus konusu isi ve ses yalitimli dekoratif duvar sivasi saf uygulandiginda yanmaz, alev almaz olmasi, isi ve ses yalitim özellikleri yüksek olmasi, kimyasal madde içermemesi, dogal malzemelerden meydana gelmesi, iletken olmamasi belli oranda pamuk katilarak renk çesitliligi saglamasi, çesitli görselliklerde ve sekillerde uygulanabilmesi, mevcut duvar kagidi ya da kaplamalarina yanmazlik özelligi ve dekoratiftik katmasi, su ile karistirilarak kolay hazirlanir ve uygulanabilir olmasi, kokusuz olmasi, içeriklerinden dolayi uzun ömürlü olmasi, genlesebilen malzemelerden dolayi esnek yapida olmasi, maliyetinin diger dekoratif benzerlerine göre düsük olmasi, pasli demir yüzeyi hariç her türlü zemine kisa sürede astarsiz kolayca uygulanabilir olmasi, istenilebilir kalinlikta yapilabilmesi, kalinlik arttikça isi ve ses izolasyon özelliklerinin artmasi özelliklerine sahip olacak sekilde meydana getirilmistir. The subject of the invention is heat and sound insulating decorative wall plaster that does not burn when applied purely, being non-flammable, having high heat and sound insulation properties, chemical substance It does not contain, consists of natural materials, is not conductive to a certain extent. providing color diversity by adding cotton, in various visuals and shapes It can be applied to existing wallpaper or coatings, its non-flammability feature and decorative additive, easy to prepare and applicable by mixing with water, being odorless, long-lasting due to its contents, expandable It has a flexible structure due to materials, its cost is comparable to other decorative counterparts. being low compared to its surface, it can be used on all kinds of floors in a short time, without primer, except for the rusty iron surface. it can be applied easily, it can be made in a desired thickness, the heat is increased as the thickness increases. and increase in sound insulation properties. has been brought.
Bulusun Açiklamasi Bulus konusu isi ve ses yalitimli dekoratif duvar sivasi, temel yapilanmasinda vermikulit, sodyum karbokstimetil selüloz - cmc, asel td 700, asel td 2000, asel ty 300, asel hv, su, pamuk (saf, toz, kirik, granül ve kumas hali), mika tasi, yün kumas, kaya tuzu (toz hali), saman ve yulaf parçasi, toz halinde ponza tasi, mixs veya toz halinde bimiss tasindan en az bir kaçini içerebilecek sekilde, farkli yapilanmalarda meydana getirilebilmektedir. Tüm ürünler uygulama esnasinda su ile hamur kivamina getirilene kadar karistirilir ve mika mala ile sivanir. Description of the Invention The subject of the invention is heat and sound insulating decorative wall plaster, used in foundation structuring. vermiculite, sodium carboxymethyl cellulose - cmc, asel td 700, asel td 2000, asel ty 300, asel hv, water, cotton (pure, powder, broken, granule and fabric), mica stone, wool fabric, rock salt (powder), straw and oat flakes, pumice stone in powder form, mixes or powder In different configurations, it can contain at least a few of the bimiss stone. can be generated. All products are mixed with water during application. It is mixed until it is brought out and it is plastered with a mica trowel.
Tuz sicaklikta sogutucu bir etkisi oldugundan, vermikulit ile beraber bir mikserde 2 saat karistirilarak ürün hazirlanir ve de bu sekilde yanan alana püskürtülerek yangin söndürülür. Vermikulit yanmaz oldugundan ve yanginin oksijenle temasini kestiginden yangin söner. Since salt has a cooling effect on temperature, it is mixed with vermiculite in a mixer. The product is prepared by stirring the clock and in this way, it is sprayed on the burned area and the fire is fired. is turned off. Vermiculite is non-combustible and prevents fire from contacting oxygen. When it cuts off, the fire goes out.
Bulus konusu duvar sivasinin meydana getirildigi bir birinci formülü; agirlikça yaklasik %60 vermikulit, %10 kaya tuzu tozu, % 30 sodyum karbonstimetil cmd ve Asel td 700 içermektedir. Üretim yönteminde; 2-3 cm lik genlesmis vermikulitler granül kirma makinesinde kullanicinin istedigi büyüklük ve görsellikte kirilmasinin ardindan mikserde diger ürünlerle birlikte ortalama 35 dk. boyunca karistirilarak kivama hazir hale getirilir. Ardindan posetlenerek kullanima hazir hale getirilir. A first formula in which the wall plaster of the invention is formed; by weight approximately 60% vermiculite, 10% rock salt powder, 30% sodium carbonstimethyl cmd and Includes Asel td 700. In the production method; 2-3 cm of expanded vermiculite crushing in the size and visuality desired by the user in the granule crushing machine. then an average of 35 minutes with other products in the mixer. mixed throughout the consistency is made ready. Then it is packaged and made ready for use.
Bulus konusu duvar sivisinin uygulanacagi yüzeyin nemli ve rutubetli olmasi durumuna göre diger yapistiricilar da kullanilabilecektir. Moisture and dampness of the surface on which the wall liquid of the invention will be applied Depending on the situation, other adhesives may also be used.
Bulus konusu duvar sivasinin meydana getirildigi bir ikinci formülü; agirlikça yaklasik tuzu tozu, %22,5 Sodyum karbonstimetil - cmc veya asel td 700, %25 vermikulit, Bulus konusu duvar sivasinin meydana getirildigi bir üçüncü formülü; agirlikça yaklasik %15 vermikulit, %30 Sodyum karbonstimetil selüloz- cmc ve Asel td 700, 7mm)) içermektedir. A second formula by which the wall plaster of the invention is formed; by weight approx. salt powder, 22.5% Sodium carbonstimethyl - cmc or asel td 700, 25% vermiculite, A third formula in which the wall plaster of the invention is formed; by weight approximately 15% vermiculite, 30% sodium carbonstimethyl cellulose- cmc and Asel td 700, 7mm)).
Bulus konusu duvar sivasinin meydana getirildigi bir dördüncü formülü; agirlikça yaklasik %20 Kumas pamuk kirintisi (saf ve granül halinde pamuk(6mm-7mm)), %30 sodyum karbonstimetil selüloz-cmc Asel td 700, %15 kaya tuzu tozu, %35 Vermikulit içermektedir. A fourth formula in which the wall plaster of the invention is formed; by weight about 20% Fabric cotton crumb (pure and granular cotton (6mm-7mm)), 30% sodium carbonstimethyl cellulose-cmc Asel td 700, 15% rock salt powder, 35% Vermiculite contains.
Bulus konusu duvar sivasinin meydana getirildigi bir besinci formülü; agirlikça yaklasik %40 kumas pamuk kirintisi (saf ve granül halinde pamuk(6mm-7mm)), %5 kâgit kirintisi, %15 seffaf veya altin mika tasi, %30 Sodyum karbonstimetil selüloz- cmc ve Asel td 700, toz halinde %10 tuz içermektedir. A fifth formula by which the inventive wall plaster is produced; by weight about 40% fabric cotton crumb (pure and granulated cotton (6mm-7mm)), 5% Paper crumb, 15% clear or gold mica stone, 30% Sodium carbonstimethyl cellulose- cmc and Asel td 700 contain 10% salt in powder form.
Bulus konusu duvar sivasinin meydana getirildigi bir altinci formülü; agirlikça yaklasik %20 pelit tozu, %30 kumas pamuk kirintisi (saf ve granül halinde Bulus konusu duvar sivasinin meydana getirildigi bir yedinci formülü; agirlikça yaklasik %20 ponza tasi tozu, %30 kumas pamuk kirintisi (saf ve granül halinde pamuk(5mm-7mm)), %30 viskozitesi yüksek carboxs metil selüloz, %20 mika tasi tozu içermektedir. A sixth formula by which the inventive wall plaster is formed; by weight approximately 20% pelite dust, 30% fabric cotton crumb (pure and in granular form) A seventh formula by which the wall plaster which is the subject of the invention is formed; by weight approximately 20% pumice stone powder, 30% fabric cotton crumb (in pure and granular form) cotton(5mm-7mm)), 30% high viscosity carboxes methyl cellulose, 20% mica stone contains powder.
Bulus konusu duvar sivasinin meydana getirildigi bir sekizinci formülü; agirlikça yaklasik %20 bimis veya mixs tasi tozu, %20 kumas pamuk kirintisi (saf ve granül halinde pamuk(5mm-7mm)), %30 viskozitesi yüksek carboxs metil selüloz, %20 mika tasi tozu ile %10 kaya tuzu tozu içermektedir. An eighth formula by which the wall plaster of the invention is formed; by weight approximately 20% bimis or mix stone powder, 20% fabric cotton crumb (pure and granular) in the form of cotton (5mm-7mm), 30% high viscosity carboxes methyl cellulose, 20% mica It contains stone powder and 10% rock salt powder.
Bulus konusu duvar sivasinin meydana getirildigi bir dokuzuncu formülü; agirlikça yaklasik %20 vermikulit büyük boy, %30 viskozitesi yüksek carboxs metil selüloz, Bulus konusu duvar sivasinin meydana getirildigi bir onuncu formülü; agirlikça yaklasik %35 pamuk kirintisi (saf ve granül halinde pamuk(5mm-7mm)), %10 saman kirintisi, %30 viskozitesi yüksek carboxs metil selüloz, %10 kaya tuzu tozu, %15 vermikulit içermektedir. A ninth formula by which the inventive wall plaster is formed; by weight approximately 20% vermiculite large size, 30% high viscosity carboxs methyl cellulose, A tenth formula by which the inventive wall plaster is produced; by weight about 35% cotton crumb (pure and granulated cotton (5mm-7mm)), 10% straw crumb, 30% high viscosity carboxes methyl cellulose, 10% rock salt powder, 15% Contains vermiculite.
Bulus konusu duvar sivasinin meydana getirildigi bir on birinci formülü; agirlikça yaklasik %35 pamuk kirintisi (saf ve granül halinde pamuk(5mm-7mm)), %15 saman kirintisi, %30 viskozitesi yüksek carboxs metil selüloz, %10 kaya tuzu tozu, %10 vermikulit içermektedir. An eleventh formula by which the inventive wall plaster is produced; by weight about 35% cotton crumb (pure and granulated cotton (5mm-7mm)), 15% straw crumb, 30% high viscosity carboxes methyl cellulose, 10% rock salt powder, 10% Contains vermiculite.
Bulus konusu duvar sivasinin meydana getirildigi bir on ikinci formülü; agirlikça yaklasik %20 pamuk kirintisi (saf ve granül halinde pamuk(5mm-7mm)), %10 yulaf kirintisi, %30 viskozitesi yüksek carboxs metil selüloz, %10 kaya tuzu tozu, %30 vermikulit içermektedir. A twelfth formula by which the inventive wall plaster is produced; by weight about 20% cotton crumb (pure and granulated cotton (5mm-7mm)), 10% oats crumb, 30% high viscosity carboxes methyl cellulose, 10% rock salt powder, 30% Contains vermiculite.
Bulus konusu duvar sivasinin meydana getirildigi bir on üçüncü formülü; agirlikça yaklasik %30 vermikulit, %50 5 m2 duvar kâgidi, %20 viskozitesi yüksek carboxs metil selüloz Bulus konusu duvar sivasinin meydana getirildigi bir on dördüncü formülü; agirlikça yaklasik toz halinde %50 vermikulite, tuzu toz halinde %50 kaya içermektedir. A thirteenth formula by which the inventive wall plaster is produced; by weight approximately 30% vermiculite, 50% 5 m2 wallpaper, 20% high viscosity carboxes methyl cellulose A fourteenth formula by which the inventive wall plaster is produced; by weight It contains approximately 50% vermiculite in powder form and 50% rock in powder form.
Bulus konusu duvar sivasinin meydana getirildigi bir on besinci formülü; agirlikça yaklasik %20 Kaya tuzu tozu, %80 Vermikulit içermektedir. Bu ürünler mikserde hafif suyla nemlendirip birbirine nüfuz edecek sekilde karistirilip hazirlanir. Formüldeki ürünler karistirici (mikser) içine konulur. 45 dk. Boyunca karistirilmasi saglanir. Bu sürede ürünler birbirine nüfuz eder. Kivama ulastiktan sonra paketlenir ve uygulamaya hazir hale getirilir. Duvar kâgidi üzerine degisik boyalar vermikulit selüloz ile su ile karistirilarak hamur kivaminda sürülür. A fifteenth formula by which the inventive wall plaster is formed; by weight It contains approximately 20% Rock salt powder, 80% Vermiculite. These products are light in mixer It is prepared by moistening with water and mixing to penetrate each other. in the formula The products are put into the mixer (mixer). 45 min. It is ensured to be mixed throughout. This In time, the products penetrate each other. After reaching the consistency, it is packaged and made ready for implementation. Different paints on wallpaper vermiculite It is applied in the form of dough by mixing cellulose with water.
Bulusta belirtiler formüller sonucu elde edilen duvar sivalarinin kullaniminda yaklasik 1000 gr. bir karisima ortalama 2,5-3 lt arasinda temiz su karistirilarak hamur kivamina getirilir. Plastik mala yardimi ile duvara tatbiki (sivasi) yapilir. Standart olarak siva kalinligi 3- 4 mm arasidir. Gerektiginde bu kalinlik 6 ve 10 mm'e kadar çikarilabilir. The indications in the invention are approximate in the use of wall plasters obtained as a result of formulas. 1000 gr. A mixture is mixed with approximately 2.5-3 liters of clean water and the dough is mixed. it is brought to consistency. It is applied to the wall (plaster) with the help of a plastic trowel. Standard The plaster thickness is between 3 and 4 mm. This thickness is up to 6 and 10 mm if required. removable.
Vermikulit sentetik ve kimyasal yapistiricilar ile kullanilmasi halinde preslenerek levha halinde isi yalitimi amaci ile elektrik panolarinda veya isi yalitimi engellemek amaci ile her türlü alanda kullanilabilir. Çimento, alçi vb. ürünler ile karistirilarak sivada kullanilabilir. tekstil sektörüne entegre edilerek iç-dis giysi kumas haline dönüstürülüp korunakli ve yanmaya dayanikli kiyafet üretimi elektronik esyalarda iletkenligi engellemek ve isi yalitimi amaci ile kullanilabilir. Vermiculite can be pressed when used with synthetic and chemical adhesives. For the purpose of thermal insulation in sheet form, in electrical panels or to prevent thermal insulation It can be used in all kinds of fields. Cement, plaster etc. mixed with products can be used in plaster. by integrating into the textile industry, it has become a fabric for underwear and outerwear. The production of protected and fire resistant clothing by converting is in electronic goods. It can be used to prevent conductivity and heat insulation.
Bulus konusu yanmaz duvar sivasinin meydana getirildigi formüllere ek olarak, kullanilan vermikulit ayristirilip içerisine Iateks benzeri türdeki yapistiricilar eklenerek dis cephede, duvar kâgitlarinin yapistirilmasinda da kullanilabilir. Ayrica ayristirilarak kemik tozu ve proteinli, karbonhidratli ürünler ilave edilerek hayvansal yemler de meydana getirilebilecektir. In addition to the formulas in which the inventive non-combustible wall plaster is formed, The vermiculite used is separated and glues of a type similar to Iatex are added into it. It can also be used on the exterior, for sticking wallpapers. By separating By adding bone powder and protein and carbohydrate products, animal feeds are also added. can be created.
Claims (16)