Description
1one
Изобретение относитс к электрои;Ной технике и может быть использсвано дл изготовлени тол сто пленочных пассивных элементов методом трафаретной печати, например сегментов цифровых индикаторов, резисторов иThe invention relates to an electronic device and can be used for the manufacture of thickly film passive elements by screen printing, for example, segments of digital indicators, resistors and
ПРОВОДН11КОВ.WIRES.
Известен токопровод щий материал на основе графита 1 .A conductive material based on graphite 1 is known.
Недостатки данного токопровод щего материала заключаютс в узком диапазоне электрического сопротивлени и низкой адгезии к подложке.The disadvantages of this conductive material are in a narrow range of electrical resistance and low adhesion to the substrate.
Наиболее близким к изобретению по технической сути вл етс токопровод щий материал, содержащий графит и функциональную добавку С2.The closest to the invention in technical terms is a conductive material containing graphite and a functional additive C2.
Недостатки этого токопровод щего материала состо т в узком диапазоне электрического сопротивлени и низкой адгезии к подложке.The disadvantages of this conductive material are in a narrow range of electrical resistance and low adhesion to the substrate.
Цель изобретени - расширение диапазона электрического сопротивлени и повышение адгезии к подложке.The purpose of the invention is to expand the range of electrical resistance and increase adhesion to the substrate.
Цель достигаетс тем, что токопровод щий материал, содержащий графит и функциональную добавку, в качестве функциональной добавки содержит вещество, выбранное из р да, состо щего из алюмини , оксида алюмини , оксида магни , оксида цинка, оксида хрома, оксида титана, оксида циркони , смеси оксида алюмини с одним из указанных оксидо, при следующем количественном соотношении компонентов , вес,:The goal is achieved by the fact that a conductive material containing graphite and a functional additive, as a functional additive, contains a substance selected from a series consisting of aluminum, aluminum oxide, magnesium oxide, zinc oxide, chromium oxide, titanium oxide, zirconium oxide, a mixture of alumina with one of these oxides, with the following ratio of components, weight:
Графит30-95Graphite30-95
Вещество, выбранное из р да, состо щего из алюмини , оксида алюмини , оксида цинка, оксида хрома оксида титана, оксида циркони , смеси оксида алюмини с одним из указанных оксидов5-70A substance selected from a series consisting of aluminum, alumina, zinc oxide, chromium oxide, titanium oxide, zirconium oxide, a mixture of aluminum oxide with one of these oxides 5-70
398959Токопровод щий материал получают путем смешивани компонентов и перетирани их на пастотерке в течение 30 мин. Из полученного токопровод щего материала готов т пасту путем s добавлени сверх 100 весД органического св зующего в количестве 40 вес., состо щего из 90 вес, вининола и 10 весД стеаринового аммони . Пасту нанос т через трафарет на подложку по о заданной схеме сегментов цифр вакуумного люминесцентного индикатора, затем провод т сушку при 250-300°С и вжигание при БО-ЗОО С,398959Component material is obtained by mixing the components and grinding them on a pastor for 30 minutes. From the resulting conductive material, a paste is prepared by adding over 100 pounds of organic binder in an amount of 40 pts. Consisting of 90 pts of vininol and 10 pounds of stearic ammonium. The paste is applied through a stencil to the substrate according to a predetermined pattern of the digit segments of the vacuum luminescent indicator, then drying is carried out at 250-300 ° C and calcined at BO-ZOO C,
Составы токопровод щего материала is и данные по электрическому сопротивлению приведены в таблице.The compositions of the conductive material is and the data on the electrical resistance are given in the table.
Claims (2)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SU802906369A SU989590A1 (en) | 1980-04-08 | 1980-04-08 | Current conducting material |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SU802906369A SU989590A1 (en) | 1980-04-08 | 1980-04-08 | Current conducting material |
Publications (1)
Publication Number | Publication Date |
---|---|
SU989590A1 true SU989590A1 (en) | 1983-01-15 |
Family
ID=20888156
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
SU802906369A SU989590A1 (en) | 1980-04-08 | 1980-04-08 | Current conducting material |
Country Status (1)
Country | Link |
---|---|
SU (1) | SU989590A1 (en) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
RU2810995C1 (en) * | 2023-04-04 | 2024-01-09 | Общество с ограниченной ответственностью "Компания ЭЛТА" | Carbon conductive paste for screen printing |
-
1980
- 1980-04-08 SU SU802906369A patent/SU989590A1/en active
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
RU2810995C1 (en) * | 2023-04-04 | 2024-01-09 | Общество с ограниченной ответственностью "Компания ЭЛТА" | Carbon conductive paste for screen printing |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
SU989590A1 (en) | Current conducting material | |
US3962143A (en) | Reactively-bonded thick-film ink | |
JPS63196672A (en) | Carbon paste composition | |
KR100213343B1 (en) | Resistance material and resistance paste and resistor comprising the material | |
JPS6316601A (en) | Voltage nonlinear resistance element | |
JPS54118599A (en) | Thermistor composition | |
JPS6288301A (en) | Resistance material | |
JPS6288305A (en) | Resistance material | |
SU551397A1 (en) | Molybdenum-based composite material | |
JPH03269908A (en) | Thick film composition and thick film hybrid integrated circuit (ic) using the same | |
JPS61276869A (en) | Resistance coating material | |
JP2937072B2 (en) | Resistance material composition, resistance paste and resistor | |
JPS62104002A (en) | Resistance material | |
JPS5445800A (en) | Thick film dielectric paste | |
JPH03149803A (en) | Method of forming thick film resistor | |
SU945908A1 (en) | Resistive material | |
JPS61235473A (en) | Paint for resistor | |
JP2654824B2 (en) | Resistance composition and method for producing thick film resistor | |
SU960966A1 (en) | Resistor composition | |
SU688012A1 (en) | Resistive material | |
JPS6046005A (en) | Voltage nonlinear resistor | |
SU692586A3 (en) | Electrically conducting paste | |
JPS6288303A (en) | Resistance material | |
JPS63158801A (en) | Resistor | |
JPS63175496A (en) | Thick film circuit board |