SU987253A1

SU987253A1 - Method of producing dome-shaped safety membranes

Info

Publication number: SU987253A1
Application number: SU813331628A
Authority: SU
Inventors: Николай Егорович Ольховский
Original assignee: Предприятие П/Я В-8620
Priority date: 1981-08-07
Filing date: 1981-08-07
Publication date: 1983-01-07

Description

(.54) СПОСОБ ИЗГОТОВЛЕНИЯ КУПОЛООБРАЗНЫХ ПРЕДОХРАНИТЕЛЬНЫХ МЕМБРАН(.54) METHOD OF MANUFACTURING DOME PROTECTIVE MEMBRANES

Изобретение относитс к приборостроению , в частности к способам изготовлени куполообразных предохранительных мембран, исполь уемьрс дл защиты пневмо- и гидросистем от опасных перегрузок.The invention relates to instrumentation, in particular, to methods for manufacturing dome-shaped protective membranes, which are used to protect pneumatic and hydraulic systems from dangerous overloads.

Известен способ изготовлени куполообразнь2Х предохранительных мембран , работающих.как на разрыв, так и на потерю устойчивости, путем нагружени плоских дисков-заготовок, жесткозажатых по краевому кольцевому участку, контролируемым давлением га3 {11. .There is a known method of manufacturing dome-shaped protective membranes operating both at the gap and at a loss of stability by loading flat blank disks rigidly compressed along the edge ring section controlled by pressure g3 {11. .

В результате такого нагружени заготовки выпучиваютс , приобрета форму сферических сегментов,т.е.относительное удлинение(пластическа деформаци ) , заготовок во всех направлени х одинаково. Но так как заготовки обычно вырезсцот из материалов, получаемых холодной прокаткой (фольга, лента,лист),т.е.из материалов с резко выраженной механической анизотропией, обусловленной определенным ориентированием зерен при прокатке, то запас пластической деформации заготовок в .направлени х вдоль и поперек прокатки неодинаков. Позтому невозможно добитьс равномерного исчерпани запаса пластической деформации в направлени х вдоль и поперек прокатки при выпучивании заготовок. Это обуславливает неоднородность напр женного , состо ни мембран, способствующую образованию и развитию трещин в местах действи наибольших напр жений, в результате чего снижаетс зксплу .атационна надежность мембран.As a result of such loading, the workpieces bulge, acquiring the shape of spherical segments, i.e. the relative elongation (plastic deformation), of the workpieces in all directions equally. But since billets are usually cut from materials obtained by cold rolling (foil, tape, sheet), i.e. materials with pronounced mechanical anisotropy due to a certain orientation of the grains during rolling, the stock plastic deformation of the billets in the along and across rolling is not the same. Therefore, it is impossible to achieve a uniform exhaustion of the stock of plastic deformation in the directions along and across the rolling during the buckling of the blanks. This causes the heterogeneity of the stressed state of the membranes, which promotes the formation and development of cracks in the places of greatest stress, as a result of which the natural reliability of the membranes decreases.

10ten

Целью изобретени вл етс повышение эксплуатационной надежности мембран путем обеспечени однородного напр женного состо ни .The aim of the invention is to increase the operational reliability of the membranes by providing a uniform stress state.

Эта цель достигаетс тем, что за15 готовки предварительно раст гивают в направлении наибольшего запаса пластической деформации (поперек прокатки ) , снижа тем самым показатель анизотропии пластичности в плоскости This goal is achieved by preliminarily stretching the preparations in the direction of the greatest stock of plastic deformation (across rolling), thereby reducing the plasticity anisotropy in the plane

20 заготовок.20 blanks.

Дл осуществлени данного cnoco(ia сначала из используемого материала (лента, фольга, лист холодной прокатки ) вырезают плоские образцы дл ис25 . Пытаний на обычных разрывных машинах или в,специальных приспособлени х с целью определени относительного удлинени ( запаса пластической деформации ) материала, из которого в даль30 нейшем будут изготовл тьс мембраны.To carry out this cnoco (ia, first from the material used (tape, foil, cold rolling sheet), flat samples are cut out for use.) Tests on conventional tensile machines or special devices to determine the relative elongation (plastic deformation stock) of the material from which membranes will be fabricated in the near future.

Claims

Claim

A method of manufacturing a domed

10 safety membranes by loading flat blanks rigidly clamped along the annular portion controlled by gas or liquid pressure, characterized in that, in order to increase the operational reliability of the membranes, the blanks are pre-stretched in the direction of the greatest plastic deformation margin.