SU923216A1 - Aluminium-based alloy - Google Patents
Aluminium-based alloy Download PDFInfo
- Publication number
- SU923216A1 SU923216A1 SU802971510A SU2971510A SU923216A1 SU 923216 A1 SU923216 A1 SU 923216A1 SU 802971510 A SU802971510 A SU 802971510A SU 2971510 A SU2971510 A SU 2971510A SU 923216 A1 SU923216 A1 SU 923216A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- aluminium
- based alloy
- proposed
- alloy
- long
- Prior art date
Description
Химические составы предлагаемого алюминиевого сплаваChemical compositions of the proposed aluminum alloy
Таблица ITable I
Результаты испытаний известного сплава на длительную прочностьThe test results of a known alloy for long-term strength
Значение длительной прочности предлагаемого сплаваThe value of the long-term strength of the proposed alloy
Таблица 2table 2
Таблица 3 Table 3
Таблица 4Table 4
Механические свойства при кратковременных температурных нспытанн х нредлагаемого и известного снлавовMechanical properties at short-term temperature tests of the proposed and known snlavs
Значени механических свойств в искусственно состаренном состо нии предлагаемого и известного сплавовValues of mechanical properties in artificially aged condition of the proposed and known alloys
Зиаченн механических свойств предлагаемогоZiachenn mechanical properties of the proposed
Таблица 5Table 5
Таблица 6Table 6
Таблица 7Table 7
в естественно состаренном состо нии и известного сплавовnaturally aged and well-known alloys
Повышение прочностных характеристик предлагаемого сплава происходит при сохранении достаточно хороших значений пластичности.Increasing the strength characteristics of the proposed alloy occurs while maintaining sufficiently good values of ductility.
Заметное превосходство прочностных характеристик наблюдаетс и при высокотемпературных испытани х. В этом случае необходимо особо отметить результаты длительпых температурных испытаний, показываюш:их увеличение длительности работоспособности нового сплава в 1,5-2,0 раза по сравнению с известным.The marked superiority of the strength characteristics is also observed during high temperature tests. In this case, it is necessary to emphasize the results of long-term temperature tests, showing: their increase in the operating time of the new alloy by 1.5-2.0 times in comparison with the known.
Предлагаемый сплав может найти применение в качестве конструкционного, свариваемого материала, дл изготовлени изделий , работаюших кратковременно и длительно при повышенных температурах.The proposed alloy can be used as a constructional material to be welded for the manufacture of products that work for a short time and for a long time at elevated temperatures.
Claims (2)