SU783279A1 - Ceramic mass for making brick - Google Patents
Ceramic mass for making brick Download PDFInfo
- Publication number
- SU783279A1 SU783279A1 SU792720856A SU2720856A SU783279A1 SU 783279 A1 SU783279 A1 SU 783279A1 SU 792720856 A SU792720856 A SU 792720856A SU 2720856 A SU2720856 A SU 2720856A SU 783279 A1 SU783279 A1 SU 783279A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- ceramic mass
- bricks
- ceramic
- mass
- making brick
- Prior art date
Description
(54) КЕРАМИЧЕСКАЯ МАССА ДЛЯ ИЗГОТОВЛЕНИЯ КИРПИЧА(54) CERAMIC MASS FOR MAKING A BRICK
1one
Изобретение относитс к промышлен сти строительных материалов, а именно к изготовлению кирпичей из керамической массы.The invention relates to the industry of building materials, namely the manufacture of bricks from ceramic mass.
Известна керамическа масса включающа аргиллит и глину в соотношении5 30:70 tl.Ceramic mass is known including mudstone and clay in the ratio 5 30:70 tl.
Недостатком указанной массы вл етс использование ее в составе качественгной глины.The disadvantage of this mass is its use in the composition of quality clay.
Наиболее близкой к изобретению вп - етс керамическа масса дл изготовлени кирпича,, включающа аргиллит 70 вес,% и кварцевый песок 30 вес..Ceramic mass for the manufacture of bricks, including an argilite of 70 wt.%, And a quartz sand of 30 wt., Comes closest to the invention.
Недостатком такой массы вл етс относительно низка прочность получаемого кирпича - 250 кг/смЯThe disadvantage of this mass is the relatively low strength of the resulting brick - 250 kg / cm²
Цель изобретени - повышение прочности кирпича и расширение сырьевой базы „ керамической промышленности.The purpose of the invention is to increase the strength of bricks and expand the raw material base of the ceramic industry.
Указанна цель достигаетс тем, ч-то керамическа масса дл изготовлени кирпича , включающа аргиллит, содержит дополнительно туфоаргиллит при следующем соотношении компонентов, вес.%: Аргиллит2О-25This goal is achieved by the fact that a ceramic mass for making bricks, including argillite, additionally contains tuffargillite in the following ratio of components, wt.%: Argillite 2 O-25
Туфоаргиллит75-80Tufoargillit75-80
Туфоаргиллиты - вскрышные породы, по Огчаемые при добыче песчанников, используемых в металлургической промышленности . Химический состав туфоаргилли тов , вес.%: SiO - 58,45; ,- 18,61;, Fе-О3, - 9,88; СаО l ,O6i MgO - 1,56; SOj - 0,26; J ВдО i ,Ol; KgO - 2,OO; п.п.п. - 7,17.Tufoargillites are overburden rocks that are used in the extraction of sandstone used in the metallurgical industry. The chemical composition of tufoargill tov, wt.%: SiO - 58.45; , - 18.61 ;, Fe-О3, - 9.88; CaO l, O6i MgO - 1.56; SOj — 0.26; J W iD, Ol; KgO - 2, OO; ppt - 7.17.
Аргиллиты - это породы, сопутствук щие угольным породам как отход при Добыче угл .Mudstones are the rocks accompanying coal as a waste in coal mining.
Химический состав аргиллитов следующий , вес.%: 5 О( - 53,46; ,41| , - 3,99; СаО - 1, ,74; Sot, - 0,32; Н agO - 1,О8; - 2,2; п.п.п. - 18,86.The chemical composition of mudstones is as follows, wt.%: 5 O (- 53.46;, 41 |, - 3.99; CaO - 1;, 74; Sot, - 0.32; H agO - 1, O8; - 2, 2; ppt - 18.86.
Зл получени глин ного кирпича готов т смеси, включак пие туфоаргиплит и аргиллит. При изготовлении изделий из туфоаргиллита и аргиллита их тонко из- - -- -:, ---. - .-. / . ,..-.y,:if,f:,fi,-,-::.t sa«a v fv - мвт чагот . ПрбХбй через сито № 0,5 9О% . Смесь формируют методом пластического формовани , высушивают и обжигают при Эбо-Эвоос -- ; ;:,,.-.-ч Получсенкые издели имеют зико-мехайические свойства, прввёдёшые в таблице. Лднные таблицы свидетельствуют 6 возможности испопьзовани туфоаргиплитов и О р м У Я а и 3 о б р е т ё ja И Я Керамическа масса дл изготбвлени Кирпича, включающа аргиллит, о т л и Ч а ю ш а с тем, что, с целью повышени прочности кирпича и расширени сырьевой базы керамической промыйп енности , она содержит дополнительно туфо аргиллит при следующем соотношении ком понентов, вес.%: 7 79- аргиллитов; в качестве минерального сырь Дл получени кирпича с повышенной механической прочностью. Использование керамической массы ал получени глин ного кирпича позволит расширить сырьевую базу и использовать отходы промышленности. Аргиллит20-25: Туфоаргиллит 75-80 Источники информации, прин тые во внимание при экспертизе 1.Реферативна информаци ВНИИЭСМ, сер. Промышленность керамических стеновых материалов и пористых заполнителей , М,, 1977, вып. 4, с. 11. 2.Авторское свидетельство СССР N 97904, кл. С 04 В 21/06, 1953.Evils for clay bricks are used to make mixtures, including tuff-argiplite and argillite. In the manufacture of products from tuffoargillite and argillite, they are thin from - - - -: ---. - .-. /. , ..-. y,: if, f:, fi, -, - ::. t sa "a v fv - mw chagot. PrbHby through a sieve number 0.5 9O%. The mixture is formed by plastic molding, dried and calcined at Ebo-Evoos -; ;: ,,.-.- h Poluchsenkye products have ziko-mekhayicheskie properties, first in the table. The long tables show 6 possibilities of using tuffarglyplite and Ou rmu Ia and 3 obreto ja ja Ii Ceramic mass for the manufacture of bricks, including mudstone, that is, with the goal of increasing the strength of bricks and expanding the raw material base of ceramic materials; it additionally contains tuff-argillate in the following ratio of components, wt.%: 7 79-mudstones; as a mineral raw material for producing bricks with increased mechanical strength. The use of ceramic mass to obtain clay bricks will expand the raw material base and use industrial waste. Argillite20-25: Tufoargillite 75-80 Sources of information taken into account during the examination 1. Referative information VNIIESM, ser. The industry of ceramic wall materials and porous aggregates, M ,, 1977, vol. 4, s. 11. 2. The author's certificate of the USSR N 97904, cl. From 04 To 21/06, 1953.
Claims (1)