SU775089A1 - Ceramic mass - Google Patents
Ceramic mass Download PDFInfo
- Publication number
- SU775089A1 SU775089A1 SU782686797A SU2686797A SU775089A1 SU 775089 A1 SU775089 A1 SU 775089A1 SU 782686797 A SU782686797 A SU 782686797A SU 2686797 A SU2686797 A SU 2686797A SU 775089 A1 SU775089 A1 SU 775089A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- ceramic mass
- zircon
- titanium dioxide
- basalt
- oxide
- Prior art date
Description
(54) КЕРАМИЧЕСКАЯ МАССА(54) CERAMIC MASS
1one
Изобретение относитс к составу керамических масс дл изготовлени химической аппаратуры и может быть использовано в химической промышленности и в промышленности строительных материалов.The invention relates to the composition of ceramic masses for the manufacture of chemical apparatus and can be used in the chemical industry and in the building materials industry.
Известна керамическа масса 1J дл изготовлени химически стойких изделий, включающа следующие компоненты, вес.%:Ceramic mass 1J for the manufacture of chemically resistant products is known, including the following components, wt%:
Каолин15 - 30 .Kaolin15-30.
Глина10-20Clay10-20
Пегматит10 - 20Pegmatit10 - 20
Фарфоровый бойЮ - 20Porcelain battle - 20
Двуокись титана0,5 - 7Titanium dioxide 0.5 - 7
Окись хрома0,5 - 5Chromium oxide0.5 - 5
Циркон10 - 30Zircon 10 - 30
Наиболее близкой к изобретению вл етс керамическа масса дл изготовлени кислотостойких изделий, включающа следующие компоненты , вес.%:Closest to the invention is a ceramic mass for the manufacture of acid-resistant products, comprising the following components, wt%:
Глина10 - 23,9Clay10 - 23.9
Каолин13-35Kaolin13-35
Циркон20-35Zircon 20-35
Пегматит8-15Pegmatite8-15
Бой фарфоровый8-25Porcelain fight8-25
Двуокись титана1-3Titanium dioxide1-3
Окись хрома0,1 - 1Chromium oxide0.1 - 1
Базальт 4 - 9 2.Basalt 4 - 9 2.
Известные составы имеют следующие недостатки: низка ударна в зкость, малый предел прочности при изгибе и большой коэффициент истираемости из-за большого количества образовавшейс в процессе обжига стеклофазы.Known compositions have the following disadvantages: low impact viscosity, low flexural strength, and high coefficient of abrasion due to the large amount of glass phase formed during the firing process.
Цель изобретени - повышение ударной в зкости, предела прочности при изгибе и снижение козффищ1ента истираемости.The purpose of the invention is to increase the toughness, the flexural strength and the reduction of the wear resistance.
Указанна цель достигаетс тем, что в керамическую массу, включающую глину, каолин, циркон, пегматит, бой фарфоровый, двуокись титана, окись хрома и базальт, дополнительно ввод т глинозем и окись цинка при следующем соотношении компонентов, вес.%:This goal is achieved by the fact that alumina and zinc oxide are additionally introduced into the ceramic mass, including clay, kaolin, zircon, pegmatite, porcelain, titanium dioxide, chromium oxide and basalt, in the following ratio of components, wt.%:
Глина10-15Clay10-15
Каолин17-20Kaolin17-20
Циркон22 - 26Zircon 22 - 26
Пегматит8-12Pegmatite8-12
Бой фарфоровый6 - 17Porcelain fight6 - 17
Двуокись титана1 - 3Titanium dioxide 1 - 3
Окись хрома0,5 - 1,0Chromium oxide0.5 - 1.0
Claims (1)