SU729263A1 - Method of thermal treatment of bimetallic sheets - Google Patents

Method of thermal treatment of bimetallic sheets Download PDF

Info

Publication number
SU729263A1
SU729263A1 SU782599312A SU2599312A SU729263A1 SU 729263 A1 SU729263 A1 SU 729263A1 SU 782599312 A SU782599312 A SU 782599312A SU 2599312 A SU2599312 A SU 2599312A SU 729263 A1 SU729263 A1 SU 729263A1
Authority
SU
USSR - Soviet Union
Prior art keywords
heat treatment
duration
minutes
quenching
steel
Prior art date
Application number
SU782599312A
Other languages
Russian (ru)
Inventor
Юрий Иванович Белоконь
Людмила Никитична Трилевская
Владимир Михайлович Остапенко
Антон Васильевич Кулик
Николай Андреевич Бондаренко
Виктор Николаевич Карпушин
Виктор Васильевич Шульженко
Original Assignee
Коммунарский горно-металлургический институт
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Коммунарский горно-металлургический институт filed Critical Коммунарский горно-металлургический институт
Priority to SU782599312A priority Critical patent/SU729263A1/en
Application granted granted Critical
Publication of SU729263A1 publication Critical patent/SU729263A1/en

Description

1one

Изобретение относитс  к области черной металлургии.This invention relates to the field of ferrous metallurgy.

Известен способ термической обработки биметаллических листов с основным слоем из углеродистой стали и плакирующим слоем из нержавеющей стали, включающий нормализацию и последующий отпуск в межкристаллическом интервале температур А-А 1.The known method of heat treatment of bimetallic sheets with a main layer of carbon steel and a cladding layer of stainless steel, including the normalization and subsequent tempering in the intercrystalline temperature range A-A 1.

Недостаткомиизвестного способа  вл ютс  низкие механические свойства основного сло  и низка  коррозионна  стойкость, вызванные медленной скоростью охлаждени  в интервале температур выпадени  карбидов.A disadvantage of the well-known method is the low mechanical properties of the base layer and the low corrosion resistance caused by the slow cooling rate in the temperature range of deposition of carbides.

Наиболее близким к предлагаемому по технической сущности и достигаемому результату  вл етс  способ термической обработки двухслойной листовой стали с основным слоем из стали 16 ГС и 09Г2С с плакирующим слоем из стали 08X13 и 12Х18Н10Т, включающий закалку с 940-960°С в прессе и последующий отпуск при 680-720°С 2.The closest to the proposed technical essence and the achieved result is a method of heat treatment of two-layer steel sheets with the main layer of steel 16 HS and 09G2S with a cladding layer of steel 08X13 and 12X18H10T, including quenching from 940-960 ° C in a press and subsequent tempering 680-720 ° C 2.

Недостаток известного способа заключаетс  в том, что длительность процесса термической обработки велика из-за осуществлени  охлаждени  в прессе закалки до цеховой температуры, что в свою очередьThe disadvantage of this method is that the duration of the heat treatment process is long due to cooling in the hardening press to the workshop temperature, which in turn

приводит к увеличению расхода энергоносителей при последующем нагреве под отпуск.leads to an increase in energy consumption during subsequent heating under the vacation.

Целью изобретени   вл етс  сокращение длительности термической обработки и сокращение расхода энергоносител .The aim of the invention is to reduce the duration of heat treatment and reduce the consumption of energy carrier.

Это достигаетс  тем, что охлаждение листа в процессе закалки производ т до 450-500°С.This is achieved by cooling the sheet during the quenching process to 450-500 ° C.

Claims (2)

Охлаждение при закалке выще 500°С приводит к снижению коррозионной стойкости плакирующего сло  в св зи с выпадением карбидов по границам зерен сло . Охлаждение при закалке ниже 450°С не приводит к изменению свойств и увеличивает длительность термической обработки, так, например, при термической обработке листа толщиной 400 мм по известному способу, продолжительность охлаждени  при закалке в прессе до 20°С составл ет 9-10 мин. Длительность последующего отпуска составл ет 2 ч. 40 мин. Продолжительность термической обработки листа той же толщины предлагаемым способом составл ет соответственно охлаждение при закалке до 450- 500°С с 1,5-2,0 мин, отпуск 1 ч. 10 мин - 1 ч. 20 мин. Сокращение длительности термической обработки позвол ет также сократить расход энергоносителей на нагрев листов под высокий отпуск при получении требуемых механических свойств. Листы с основным слоем из стали 16ГС и плакирующим слоем из стали 08X13 толщиной 12 мм после обработки предлагаемым способом имеют следующие СБОЙства:0б 54 кгс/мм2;б 37 кгc/мм ; 8 27%. Формула изобретени  Способ термической обработки биметаллических листов с плакирующим слоем из нержавеющей стали, включающий закалку и отпуск, отличающийс  тем, что, с целью сокращени  длительности термической обработки и сокращени  расхода энергоносител , охлаждение листа в процессе закалки производ т до 450 -500°С. Источники информации, прин тые во внимание при экспертизе 1. Авторское свидетельство СССР № 341849, кл. С 21 D 9/46, 1970. Cooling during quenching more than 500 ° C leads to a decrease in the corrosion resistance of the cladding layer due to the precipitation of carbides along the grain boundaries of the layer. Cooling during quenching below 450 ° C does not change the properties and increases the duration of heat treatment, for example, during heat treatment of a 400 mm thick sheet by a known method, the cooling time during press quenching to 20 ° C is 9-10 minutes. The duration of the next vacation is 2 hours and 40 minutes. The duration of heat treatment of a sheet of the same thickness by the proposed method is, respectively, cooling during quenching to 450-500 ° C for 1.5-2.0 minutes, tempering 1 hour 10 minutes - 1 hour 20 minutes. Reducing the duration of heat treatment also reduces the energy consumption for heating sheets for high tempering when obtaining the required mechanical properties. Sheets with the main layer of 16GS steel and a cladding layer of 08X13 steel 12 mm thick after treatment by the proposed method have the following FAILURES: 0b 54 kgf / mm2; b 37 kgc / mm; 8 27%. The invention The method of heat treatment of bimetallic sheets with a cladding layer of stainless steel, including quenching and tempering, characterized in that, in order to reduce the duration of heat treatment and reduce energy consumption, the sheet is cooled to 450-500 ° C during quenching. Sources of information taken into account during the examination 1. USSR Author's Certificate No. 341849, cl. From 21 D 9/46, 1970. 2. Технологическа  инструкци  Коммунарского металлургического завода по термообработке толстолистовой стали в термоотделении стана 28000. ТИ 6-11-75, табл.5, Коммунарск, 1975.2. Technological instructions of the Kommunar metallurgical plant for the heat treatment of steel plates in the thermal separation of the mill 28000. TI 6-11-75, Table 5, Kommunarsk, 1975.
SU782599312A 1978-04-03 1978-04-03 Method of thermal treatment of bimetallic sheets SU729263A1 (en)