SU687001A1 - Способ осветлени стекломассы - Google Patents
Способ осветлени стекломассыInfo
- Publication number
- SU687001A1 SU687001A1 SU782589934A SU2589934A SU687001A1 SU 687001 A1 SU687001 A1 SU 687001A1 SU 782589934 A SU782589934 A SU 782589934A SU 2589934 A SU2589934 A SU 2589934A SU 687001 A1 SU687001 A1 SU 687001A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- clarification
- glass
- boric anhydride
- clarifier
- furnace
- Prior art date
Description
(54) СПОСОБ ОСВЕТЛЕНИЯ СТЕКЛОМАССЫ
Claims (2)
- Изобретение относитс к промышленности строительства и стройматериалов , в частности к технологии стекловарени и касаетс осветлени стекломассы. Известен способ осветлени ,который заключаетс в том, что в стекол ную шихту ввод т специальные осветлители и SbjOj. Однако при так способе используют такие дорогосто щие и токсичные вещества, как 20и SbjOj Известен также способ осветлени стекломассы с помощью осветлител , при котором предварительно готов т фритту с введением серосодержащих компонентов при температуре 1280t2 Способ длителен по времени и требуе дополнительных энергозатрат. Цель изобретени - повышение про изводительности способа. Это достигаетс тем, что в качестве осветлител используют борный ангидрид, который распыл ют на поверхности стекломассы в зоне осветл ни . Над зеркалом стекломассы в зоне осветлени распыл ют при 1460°С с помощью форсунки борный ангидрид,ко торый оседает на поверхность зеркгша стекломассы мономолекул рным слоем. В результате образовани на поверхности стекломассы мономолекул рного сло борного ангидрида снижаетс поверхностное нат жение на границе раздела двух фаз: стекломасса - газова среда печи. Количество борного ангидрида, введенного в газовую среду, должно составл ть 0,2-0,4% от общего количества шихты, загружаемой в печь. Распыление прюизвод т периодически в совокупности со сжиганием газообразного или иного топлива, или автономно . Такой способ осветлени позвол ет ускорить процесс осветлени , преимущественно пр моточной печи на 60-70%, против естественного и увеличить производительность печи в 1,2-1,3 раза. Формула изобрет« ни Способ осветлени стекломассы с помощью осветлител , о т л и ч а ющ и и с т, что, с целью повышени производительности, в качестве осветлител используют борный ангид36870014РИД, который распыл ют на поверхнос- i. Авторское свидетельство СССРти стекломассы в зоне осветлени . 133204, С 03 В 5/22, 1960.Источники информации, прин тые во
- 2. Патент США № 3511629, 65-134,внимание при экспертизе1970.