SU685672A1 - Polymeric composition - Google Patents
Polymeric compositionInfo
- Publication number
- SU685672A1 SU685672A1 SU762402062A SU2402062A SU685672A1 SU 685672 A1 SU685672 A1 SU 685672A1 SU 762402062 A SU762402062 A SU 762402062A SU 2402062 A SU2402062 A SU 2402062A SU 685672 A1 SU685672 A1 SU 685672A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- stabilizer
- polymeric composition
- rubber latex
- weight
- latex
- Prior art date
Description
ливаю на стекло, высу1иивают в тече;ние 24 ч при , затем выдерживают 10 мин при и из сн тых со стекла пленок готов т образгц по ГОСТ 260-66. Определение физико-механических показателей npoBOfiRT по ГОрТ 270-64.I poured onto the glass, dried for 24 hours at, then allowed to stand for 10 minutes at and out of the films removed from the glass, a sample was prepared according to GOST 260-66. Determination of physicomechanical indicators npoBOfiRT according to GORT 270-64.
В табл. 2 дано вли ние антиоксидантов на стабильность свойств пленок каучукового латекса при термостарении (температура старени IIOC) .In tab. Table 2 shows the effect of antioxidants on the stability of the properties of rubber latex films during thermal aging (aging temperature IIOC).
Состав композицииComposition
Каучуковый латекс СКС-65ГПRubber latex SKS-65GP
Каучуковый латекс СКС-65ГП+ 4нерзон ДRubber latex SKS-65GP + 4nerzon D
Каучуковый латекс СКС-65ГП- 4продукт То жеRubber latex SKS-65GP-4product The same
Исследовани показали, что ув уличение количества термостабилиэатора больше 5,0 вес.ч. не дает больше эффекта.Studies have shown that the incidence of the amount of heat stabilizer is greater than 5.0 wt.h. no more effect.
Таким образом, использование предложенной композиции увеличивает долговечность примен емых покрытий, клеев, гидроизол ции и пр., так как она обладает повышенной стойкостью к термоокислительной деструкции, а также уменьшаетс стоимость композиции из-за употреблени более дешевого стабилизатора. блица 1Thus, the use of the proposed composition increases the durability of the applied coatings, adhesives, waterproofing, etc., as it has an increased resistance to thermal-oxidative degradation, and also reduces the cost of the composition due to the use of a cheaper stabilizer. blitz 1
Индукционный период окислени каучука, минInduction period of oxidation of rubber, min
ч, h,
2020
240240
1,01.0
900900
12001200
10501050
Claims (1)