Description
(54) ПАСТА ДЛЯ МЕТАЛЛИЗАЦИИ КЕРАМИКИ(54) PASTE FOR METALIZATION OF CERAMICS
покрыгвбм при пайке. Мехшагхе ва прочность на изгиб 1ГОВ пайке медью состаол па 1000 кгс/см ,Coating when soldering. Mehshaghe wa bending strength 1GOV brazing copper composites PA 1000 kgf / cm,
: П р и р 2. Пасту состава, % : Мо - 70.S&t%- 12.6, МпО - 6,9, МД. 5,8, СаО 4,7 готовлг по способу, ук: P p and p 2. Paste of the composition,%: Mo - 70.S & t% - 12.6, MpO - 6.9, MD. 5.8, CaO 4.7 ready by the way, UK
эан ому в гфимерв 1, Механическа Проч-( Boqrb на иэгаб при пайке медью равна This method is used in gfimerv 1, Mechanical Proc- (Boqrb on ingab during brazing is equal to
1400 кгс/см. Количество вакуумплотных образцов после т мохшклов 20-60О.20°С составл ет 100%, М«ханическаа огромность на изгиб, после 30-тн термоцнклов . 1200 кгс/см .1400 kgf / cm. The number of vacuum-tight specimens after tons of 20–60 ° C 20 ° C is 100%, the M bending is enormous, after 30 tons of thermal glasses. 1200 kgf / cm.
Пример 3, Пасту состава, % : Мо - 60, SiOg, - 16,8, МпО - 9,2, 7,7, СаО - 6,3 готов т по способу, указанному в примере 1, Механическа про«. i ность на изгиб при пайке медью 1ООО кгс/см Example 3, Composition paste,%: Mo - 60, SiOg, - 16.8, MpO - 9.2, 7.7, CaO - 6.3 prepared according to the method indicated in Example 1, Mechanical Pro. bending during brazing with 1OOO kgf / cm copper
Вжиганае металлизацнонного покрыти можно проводить в среде сухого водорода; кристаллиаадн стекла позвол ет получать прочные, вакуукшошютные; термостойкие соединени при пайке медью.Vzhiganay metal coating can be carried out in an environment of dry hydrogen; crystalline glass makes it possible to obtain durable, vacuum-closed; heat-resistant brazing compounds.
ФF
ормула нзобретевиInvention formula
Паста дл металлизашш керамики, включающа Мо, МпО, StjJ , AtwO. , СаО, от ч а ю ш а ; вм. irro, .с целью получени ,прочных, вакуумно-плотных , термостойких мегаллокерамическнх соединений при пайке высокотемпературными припо ми, она содержит указанные компоненты в следующем соотношении, вес.%:Paste for metallisations of ceramics, including Mo, MpO, StjJ, AtwO. , Cao, from h and y w a; vm irro,. with the aim of obtaining strong, vacuum-tight, heat-resistant megalloceramic compounds when brazing with high-temperature solders, it contains these components in the following ratio, wt.%:
МоОсноваMoon
МпО6,&-9MpO6, & - 9
SiOa11,7-12,6 ,1-5,9SiOa11.7-12.6, 1-5.9
. aO4,2-4,8. aO4,2-4,8
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SU2042973A SU514797A1 (en) | 1974-07-08 | 1974-07-08 | Ceramic Metallization Paste |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SU2042973A SU514797A1 (en) | 1974-07-08 | 1974-07-08 | Ceramic Metallization Paste |
Publications (1)
Publication Number | Publication Date |
---|---|
SU514797A1 true SU514797A1 (en) | 1976-05-25 |
Family
ID=20590665
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
SU2042973A SU514797A1 (en) | 1974-07-08 | 1974-07-08 | Ceramic Metallization Paste |
Country Status (1)
Country | Link |
---|---|
SU (1) | SU514797A1 (en) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0265231A2 (en) * | 1986-10-21 | 1988-04-27 | Ngk Insulators, Ltd. | A metallizing paste and a process for metallizing ceramic articles by using such a metallizing paste |
-
1974
- 1974-07-08 SU SU2042973A patent/SU514797A1/en active
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0265231A2 (en) * | 1986-10-21 | 1988-04-27 | Ngk Insulators, Ltd. | A metallizing paste and a process for metallizing ceramic articles by using such a metallizing paste |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
GB1283848A (en) | Process for soldering difficultly solderable metals | |
SU514797A1 (en) | Ceramic Metallization Paste | |
US3736649A (en) | Method of making ceramic-to-metal seal | |
US2667431A (en) | Method of metallizing ceramics | |
JPS5567544A (en) | Glass fusion bonding method for metal plate for seal bonding | |
SU564293A1 (en) | Method for ceramics plating | |
SU617438A1 (en) | Vacuum-tight ceramics | |
SU1164228A1 (en) | Paste for depositing metal coating on ceramics | |
EP0373220A4 (en) | Superconducting oxide material and method of obtaining it | |
SU612767A1 (en) | Solder for blanching and soldering ceramic and glass-ceramic articles | |
SU104210A1 (en) | Method of soldering tungsten and molybdenum parts | |
SU1759817A1 (en) | Ceramic soldering alloy | |
SU1606295A1 (en) | Solder for soldering nickel | |
JPS525608A (en) | Aluminium alloy having excellent moldability and production process of its thin sheet | |
US3647519A (en) | Method for metallizing beryllium oxide at low temperatures | |
SU682331A1 (en) | Method of brazing ceramic and metal | |
SU787395A1 (en) | Paste for metallizing corundum ceramics | |
SU478823A1 (en) | Nonmetallic Metallizing Paste | |
SU464427A1 (en) | Paste for soldering ceramics and sapphire with metal | |
GB1023135A (en) | A metallising coating for ceramics | |
SU541825A1 (en) | Paste for plating alumina ceramics | |
SU597662A1 (en) | Composition for metallising ceramics | |
SU135741A1 (en) | The method of obtaining junctions of metal parts of stainless steel type IX18H9T with ceramics | |
SU765243A1 (en) | Paste for metallizing ceramics | |
SU654584A1 (en) | Ceramic solder |