SU481561A1 - The method of obtaining crystalline filler, for example, gypsum " - Google Patents
The method of obtaining crystalline filler, for example, gypsum "Info
- Publication number
- SU481561A1 SU481561A1 SU1921785A SU1921785A SU481561A1 SU 481561 A1 SU481561 A1 SU 481561A1 SU 1921785 A SU1921785 A SU 1921785A SU 1921785 A SU1921785 A SU 1921785A SU 481561 A1 SU481561 A1 SU 481561A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- gypsum
- obtaining crystalline
- crystalline filler
- filler
- obtaining
- Prior art date
Description
,34, 34
В табл. 2 приводитс зависимость преде- полугидрата гипса от времени введени ла прочности при сжатии заливочной . последнего после дегидраташи при темпезиции на Ьснове полиэфирной смоды. ГШ-1 .иратуре 80°С в вакууме 750 мм рт. ст.In tab. Figure 2 shows the dependence of gypsum precidihydrate on the time of injection of the compressive strength of the casting. the latter after dehydratachy at tempesiatsii on the B of the polyester mode. GSH-1. Mouth 80 ° C in a vacuum of 750 mm Hg. Art.
Времй введени в композицию наполнител после дегидр1атации , минTime of introduction to the composition of the filler after dehydration, min
Предел прочности при сжатии,Compressive Strength
кгс/смkgf / cm
481561 481561
Таблииа2Tabliya2
2020
100100
30thirty
6О6O
654654
624624
60О60O
595595
Предел прочности при сжатии образцов композиций, наполненных полугидратом гипс Полученйым при 120-145°С, HW более 57О кгс/см2. : Предмет изобретени Способ получени кристаллогидратного наполнител , например гипса, путем дегидатации его под вакуумом при повышенной Температуре, отличающийс тем, что, с целью повышени качества ш-ле. вого продукта, процесс осуществл ют крц 7О-1ОО С.The compressive strength of samples of compositions filled with hemihydrate gypsum obtained at 120-145 ° C, HW more than 57O kgf / cm2. : Object of the Invention A method for producing a crystalline hydrate filler, such as gypsum, by dehydrating it under vacuum at elevated Temperature, characterized in that, in order to improve the quality of the scoop. product, the process is carried out by CRC 7O-1OO C.