Description
1one
Изобретение относитс к получению глазури дл бытовых изделий и строительной керамики .The invention relates to the production of glazes for household products and building ceramics.
Известна глазурь, включающа SiO9, АЬОз, ZnO, MgO, NagO, LigO, СеОг.Known glaze, including SiO9, HOC3, ZnO, MgO, NagO, LigO, CeOg.
С с 1ижени температуры нлавлени глазурь содержит следующие KONnioHCHTbi вес. %: SiOa AlsOa 9 - 11; ZiiO 11-12; MgO 0,6-1; NaaO 2-4; LiaO 2-4; CeOs 8 - 10 И, кроме того, CaO 5-6, Ч- + + NdoOa 1 -2.From 1 to 5, the glaze contains the following KONnioHCHTbi weight. %: SiOa AlsOa 9-11; ZiiO 11-12; MgO 0.6-1; NaaO 2-4; LiaO 2-4; CeOs 8 - 10 And, moreover, CaO 5-6, H- + + NdoOa 1 -2.
Пример. Глазурь содержит следующие компоненты, в вес.: Si0256; АЬОз Ю; СаО 5,3; ZnO 11,4; MgO 0,8; NajO 3,0; 3,0; CeOo 9,0; LaaOs + + .Nd.Os 1,5.Example. Glaze contains the following components, in weight: Si0256; Hooz Yu; CaO 5.3; ZnO 11.4; MgO 0.8; NajO 3.0; 3.0; CeOo 9.0; LaaOs + + .Nd.Os 1.5.
Темнература разлива глазури 1180 - 1230°C, температура раз.м гчени 600-G50 C, коэффициент термического расширенн п нределахThe temperature of the glaze spill is 1180 - 1230 ° C, the temperature spread is 600-G50 C, the thermal coefficient is extended beyond the limits of
20-400С (60-70) 10--. Термостойкость глазури - отсутствие цека вследствие термоудара нри выходе изделий из печи дл нолитого обжига. Смачивание глазурью череика - нолное , равномерное при отсутствии сборки. Блеск - зеркальный, н,вет - светло-бежевьи.20-400C (60-70) 10--. Heat resistance of the glaze - no tseka due to thermal shock at the exit of products from the furnace for the nolith roasting. Wetting with the glaze of the choreik is complete, uniform with no assembly. Gloss - mirror, n, wet - light beige.
Предмет изобретени Subject invention
Глазурь, включающа SiOa, , ZnO, MgO, Na2O, Li.gO, СеОз, отличающа с тем, что, с нелью снижени температуры плавлени , она содержит указанные компоненты к следующнх количествах, в вес. %: SiOo 52-58; АЬОзЭ-11; ZnO 11 - 12; MgO 0,6-Г; МаЮ 2-4; LioO 2-4; СеОа 8 - 10, и, кроме того, СаО 5-6; 1&2Оз + РгаОа + NdaOs 1-2.Glaze, including SiOa,, ZnO, MgO, Na2O, Li.gO, CeO3, characterized in that, to reduce the melting temperature, it contains these components in the following amounts, by weight. %: SiOo 52-58; ABOze-11; ZnO 11 to 12; MgO 0.6-G; May 2-4; LioO 2-4; CeOa 8 - 10, and, moreover, CaO 5-6; 1 & 2Оз + РгаОа + NdaOs 1-2.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SU1701226A SU404794A1 (en) | 1971-09-28 | 1971-09-28 | GLAZE |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SU1701226A SU404794A1 (en) | 1971-09-28 | 1971-09-28 | GLAZE |
Publications (1)
Publication Number | Publication Date |
---|---|
SU404794A1 true SU404794A1 (en) | 1973-10-22 |
Family
ID=20489078
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
SU1701226A SU404794A1 (en) | 1971-09-28 | 1971-09-28 | GLAZE |
Country Status (1)
Country | Link |
---|---|
SU (1) | SU404794A1 (en) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO1995007865A1 (en) * | 1993-09-14 | 1995-03-23 | Bayer Corporation | Rare earth-containing alkali silicate frits and their use for the preparation of porcelain enamel coatings with improved cleanability |
-
1971
- 1971-09-28 SU SU1701226A patent/SU404794A1/en active
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO1995007865A1 (en) * | 1993-09-14 | 1995-03-23 | Bayer Corporation | Rare earth-containing alkali silicate frits and their use for the preparation of porcelain enamel coatings with improved cleanability |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US3505498A (en) | Cooking utensil with integral dielectric layer and electrical heating element | |
US2007111A (en) | Glazed electric range heating unit and glaze therefor | |
SU404794A1 (en) | GLAZE | |
SU405827A1 (en) | ALL-UNION • 405827DA. \\ l S 03/3/04UDK 00.112.2 (088.8) | |
SU358284A1 (en) | Glass Crystal Emll | |
SU338501A1 (en) | Chemical Resistant Eyes | |
SU413119A1 (en) | ||
SU482406A1 (en) | Acid resistant enamel | |
SU418456A1 (en) | GLASS | |
SU372188A1 (en) | MAYOLIKA GLAZE | |
SU351800A1 (en) | ||
SU391073A1 (en) | ^ SGLISTNKCH | |
SU321485A1 (en) | ELECTRICAL INSULATION GLASS | |
US2426395A (en) | Ceramic composition | |
SU417402A1 (en) | ||
SU449890A1 (en) | Glass | |
SU386857A1 (en) | GLASS FOR THE MANUFACTURE OF FACING MATERIAL | |
SU688453A1 (en) | Glass | |
AT157007B (en) | Brick lining processes for rotary kilns for burning cement, plaster and the like like | |
SU471322A1 (en) | Glaze | |
SU386861A1 (en) | ENAMEL | |
SU725273A1 (en) | Heater | |
SU391076A1 (en) | GLASS FOR RESISTORS | |
SU522146A1 (en) | Enamel | |
SU393221A1 (en) | GLAZE |