SU292299A1 - - Google Patents
Info
- Publication number
- SU292299A1 SU292299A1 SU1303461A SU1303461A SU292299A1 SU 292299 A1 SU292299 A1 SU 292299A1 SU 1303461 A SU1303461 A SU 1303461A SU 1303461 A SU1303461 A SU 1303461A SU 292299 A1 SU292299 A1 SU 292299A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- electrochemical
- aluminum
- film
- anodizing
- alloys
- Prior art date
Description
СПОСОБ ЭЛЕКТРОХИМИЧЕСКОГО АНОДИРОВАНИЯMETHOD OF ELECTROCHEMICAL ANODIZATION
НИЯ И ЕГО СПЛАВОВNIA AND ITS ALLOYS
Изобретение относитс к электро.химической обработке металлов, в частности к способам анодировани алюмини и его сплавов.The invention relates to the electro-chemical treatment of metals, in particular, to methods for the anodizing of aluminum and its alloys.
Известен способ электрохимического анодировани алюмини и его сплавов в электролите , содержащем серную кислоту. Однако известным способом нельз получить анодную пленку разнообразных цветов.There is a method of electrochemical anodizing of aluminum and its alloys in an electrolyte containing sulfuric acid. However, it is not possible to obtain an anode film of various colors in a known manner.
Предложен способ электрохимического анодировани алюмини и его сплавов в электролите , содержащем серную кислоту, по которому дл получени гаммы цветов от светлобронзового до черного в электролит ввод т малеиновую сульфокислоту при следующем соотнощении компонентов (в г/л):A method is proposed for electrochemical anodizing of aluminum and its alloys in an electrolyte containing sulfuric acid, according to which maleic sulfonic acid is introduced into the electrolyte to obtain a range of colors from light bronze to black at the following ratio of components (g / l):
Малеинова сульфокислота10-300Maleic sulfonic acid 10-300
Серна кислотаДо 15Sulfuric acid up to 15
.и процесс ведут при температуре от -10 до +50°С и плотности посто нного тока 0,5- 10 а/Ли2..and the process is carried out at a temperature of from -10 to + 50 ° C and a density of direct current of 0.5-10 A / Li2.
Хорошее качество анодной пленки получают при концентрации малеиновой сульфокислоты 50-200 г/л серной кислоты 0,5-8 г/л при температуре 15-30°С и применении посто нного , переменного или пульсирующего тока. При посто нном токе плотность его составл АЛЮМИет 1-4 а/дл1-. Толщина получаемой пленки 10-50 .«к.Good quality of the anodic film is obtained when the concentration of maleic sulfonic acid is 50–200 g / l of sulfuric acid, 0.5–8 g / l at a temperature of 15–30 ° C and the application of a constant, alternating or pulsating current. At a constant current its density is ALUMIET 1-4 a / dl1-. Thickness of the received film 10-50. "To.
Перед анодированием издели обрабатывают дл получен 1 матовой или блест щей поверхности . Матовую поверхность получают химическим или электрохимическим травлением , например, в растворе, содержащем 50 г/л соды при температуре 50°С в течение 10 мин с последующей промывкой водой, погружением в азотную кислоту и снова промывкой водой . Блест щую поверхность получают механическим полированием, химической или электрохимической; обработкой.Before anodizing, the product is processed to obtain 1 matte or glossy surface. A matt surface is obtained by chemical or electrochemical etching, for example, in a solution containing 50 g / l of soda at 50 ° C for 10 minutes, followed by washing with water, immersion in nitric acid, and again washing with water. The shiny surface is made by mechanical polishing, chemical or electrochemical; processing.
Измен температуру и плотность тока при анодировании, можно получить желаемую окраску пленки. Цвет пленки будет светлее, если плотность тока меньще, а температура электролита выше.By changing the temperature and current density during anodization, you can get the desired color of the film. The color of the film will be lighter if the current density is less and the electrolyte temperature is higher.
Состав алюмини или алюминневого сплава также вли ет на окраску получаемой анодной пленки. Так, например, дл полученн темной анодной пленки нспользуют сплав, содержащий марганец.. Например, на сплаве алюмини ,The composition of aluminum or aluminum alloy also affects the color of the resulting anode film. For example, for a dark anode film, an alloy containing manganese is used .. For example, on an aluminum alloy,
Лоты, при температуре 20°С и плотности посто нного тока 1,5 ajdM после уплотнени получают бронзовую пленку толщиной 18 мк, однородную и стойкую нри ультрафлолетовом йзлучении.Lots, at a temperature of 20 ° C and a current density of 1.5 ajdM, after compaction, a bronze film 18 microns thick, uniform and resistant to ultraviolet radiation, is obtained.
После электрохимического анодировани анодную пленку уплотн ют кип чеиием в течение 30 мин в дистиллированной воде, содержащей 0,5-2 г/л ацетата никел .After electrochemical anodization, the anode film is compacted by boiling for 30 minutes in distilled water containing 0.5-2 g / l of nickel acetate.
Предложенный способ анодировани нозвол ет получать гамму цветов от светло-бронзового до черного непосредственно пр.и электрохимическом анодировании алюмини и его сплавов.The proposed method of anodizing allows to obtain a range of colors from light bronze to black directly and electrochemical anodizing of aluminum and its alloys.
Предмет изобретени Subject invention
Способ электрохимического анодировании алюмини и его сплавов в электролите, содержащем серную кислоту, отличающийс тем, что, с целью получени гаммы цветов от светло-бронзового до черного, в электролит ввод т малеиновую сульфокислоту при следующем соотнощении компонентов (в г/л): Малеинова сульфокислота10-300The method of electrochemical anodizing of aluminum and its alloys in an electrolyte containing sulfuric acid, characterized in that, in order to obtain a range of colors from light bronze to black, maleic sulfonic acid is introduced into the electrolyte at the following ratio of components (in g / l): Malein sulfonic acid 10 -300
Серна кислотаДо 15Sulfuric acid up to 15
и процесс ведут лри температуре от -10 до +50°С и плотности посто нного тока 0,5- 10 а/(.и2.and the process is conducted at a temperature of from -10 to + 50 ° C and a density of direct current of 0.5 to 10 a / (. u2.