В предлагаемом способе вулканизации алош под давлением применена винтил ци котла во врем вулканизационного периода : сохранением давлени в котле.In the proposed method of vulcanization of alosh under pressure, a screw screw of the boiler was used during the vulcanization period: the pressure in the boiler remained unchanged.
На схематическом чертеже изображен Зоковой вид котла, при посредстве которого осуществл етс предлагаемый способ вулканизации.The schematic drawing shows the Zokova view of the boiler through which the proposed vulcanization method is carried out.
По заполнении котла вагонетками с галошами котел герметически закрываетс и давление в нем доводитс до 30 фунтов которое поддерживаетс около часа с повышением 8а этот период температуры от 100° до 125° С, после чего начинаетс при поддержании укаааного давлени вентил ци котла в течение 50 минут попеременным открыванием на 10 минут вентилей 2 к 14, 4 к 12, 3 и 13,5 и 11 и /и /5. По, доведении температуры в котле не. менее чем до 136° С начинают производить вентилирование котла последовательным открыванием вентилей 2 и 14, S 13, 4 к 12 к наконец 5 и //, достига постепенного понижени давлени до атмосферного , при котором продувка продолжаетс 5 - 10 минут, после чего открываютс вентили I, II, III, IV и V дл естественной вентил ции, продолжающейс в течение 10 минут с поддерживанием температуры от 136° до 142° С. Продолжительность вулканизации при описанном способе, по за влению автора .- около трех часов.Upon filling the boiler with trolleys with galoshes, the boiler is hermetically closed and the pressure in it is reduced to 30 pounds which is maintained for about an hour with an increase in 8a this temperature period from 100 ° to 125 ° C, after which the boiler is ventilated for 50 minutes while alternating opening for 10 minutes the valves 2 to 14, 4 to 12, 3 and 13.5 and 11 and / and / 5. By, bringing the temperature in the boiler is not. less than 136 ° C, the boiler ventilation is started by sequential opening of valves 2 and 14, S 13, 4 to 12 to finally 5 and //, reaching a gradual decrease in pressure to atmospheric, at which the blowdown lasts 5 to 10 minutes, after which the valves open I, II, III, IV, and V for natural ventilation, which lasts for 10 minutes, maintaining the temperature from 136 ° to 142 ° C. The duration of vulcanization with the described method, according to the author, is about three hours.
Предмет изобретени .The subject matter of the invention.
Способ вулканизации галош в котле под давлением, отличающнйс тем, что после подъема в котле воздушного давлеНЕ поочередным открытием соответстующих клапанов производ т вентил цию котла с сохранением в нем давлени до койца вулканизационного процесса.The method of vulcanization of galoshes in the boiler under pressure, characterized in that after the air pressure is lifted in the boiler, alternately opening the corresponding valves, the boiler is ventilated to maintain the pressure in the boiler before the vulcanization process.