SU1298345A1 - Lightweight plugging composition - Google Patents
Lightweight plugging composition Download PDFInfo
- Publication number
- SU1298345A1 SU1298345A1 SU853916693A SU3916693A SU1298345A1 SU 1298345 A1 SU1298345 A1 SU 1298345A1 SU 853916693 A SU853916693 A SU 853916693A SU 3916693 A SU3916693 A SU 3916693A SU 1298345 A1 SU1298345 A1 SU 1298345A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- cement
- asbestos
- solution
- water
- ntfc
- Prior art date
Abstract
Изобретение касаетс креплени нефт ных и газовых скважин и позво- л ет уменьшить усадку, повысить адгезионные свойства цементного камн и его прочность за счет повышени седи- ментационной стабильности тампонажно- го раствора. Раствор содержит портландцемент (Щ) , асбест, нитрилотри- метилфосфоновую кислоту (НТФК), воду и вспученный вермикулит (ВВ) при следующем соотношении компонентов,мае.%: ПЦ 44,145-50,487i НТФК 0,005-0,020 ВВ 2,725-5,825; асбест 0,882-3,500; вода остальное. Раствор получают при смешивании водного раствора НТФК с асбестом и ВВ с последуюш;им затво- рением ПЦ на полученной суспензии. При дозировке ВВ меньшей 2,735 мас.% снижаетс седиментационна устойчи- вость раствора, повышаетс усадка. При ВВ большей 5,825 мас.% раствор расслаиваетс , нарушаетс однородность формирующегос камн понижаетс его прочность и адгези к металлу трубы.1 табл. Ш сл 1чЭ со. 00 со 4 СПThe invention relates to the fastening of oil and gas wells and reduces shrinkage, improves the adhesion properties of cement stone and its strength by increasing the media stability of the cement slurry. The solution contains Portland cement (Y), asbestos, nitrilotrimethylphosphonic acid (NTFC), water and expanded vermiculite (BB) in the following ratio of components, may.%: PC 44.145-50.487i NTFC 0.005-0.020 BB 2.725-5.825; asbestos 0.882-3,500; water the rest. The solution is obtained by mixing an aqueous solution of NTFC with asbestos and explosives followed by mixing them with the resulting suspension. When the dosage of explosives is less than 2.735 wt.%, The sedimentation stability of the solution decreases, shrinkage increases. With explosives greater than 5.825 wt.%, The solution exfoliates, the homogeneity of the forming stone is disturbed, its strength decreases and its adhesion to the metal of the pipe. W SL 1CHE with. 00 from 4 SP
Description
Изобретение относитс к крешгению нефт ных и газовых скважин, в частности к облегченным тампонажным растворам .The invention relates to the crushing of oil and gas wells, in particular to lightweight cement slurries.
Цель изобретени - уменьшение усадки,повышение адгезионных свойств цементного камн и его прочности за счет повышени седиментационной стабильности тампонажного раствора.The purpose of the invention is to reduce shrinkage, increase the adhesive properties of cement stone and its strength by increasing the sedimentation stability of the cement slurry.
Тампонажный раствор получают еле- дующим образом.Cement slurry is obtained in an appropriate manner.
Водный раствор нитрилотриметилфосфоновой кислоты смешивают с ас- бестом и вермикулитом с последующим затворением цемента на полученной суспензии.An aqueous solution of nitrilotrimethylphosphonic acid is mixed with asbestos and vermiculite, followed by mixing of the cement on the resulting suspension.
В таблице приведены технологические свойства тампонажных составов.The table shows the technological properties of cement compositions.
Пример 1. 1000 г тампонажного портландцемента затворили суспензией , содержащей, г: нитрилотриме тилфосфонова кислота 0,11,, вода 1183,3, вспученный вермикулит 61,7, асбест 20, что соответствует соотно- шению ингредиентов, мас.%: Тампонажный портландцемент 44,145 НТФ 0,005 Асбест0,882 Вермикулит2,725 Вода 52,243 Пример 2. 1000 г тампонажного портландцемента затворили на суспензии, содержащем, г: нитрило- триметилфосфонова кислота О,2,асбест 40, вермикулит 90, вода 1000,0, что соответствует, мас.%: Тампонажный портландцемент46 ,950 НТФ0,010 Асбест1,870 Вермикулит 4,220 Вода 46,950Example 1. 1000 g of cement Portland cement was closed with a suspension containing, g: nitrilotrime, tilphosphonic acid, 0.11, water 1183.3, exfoliated vermiculite 61.7, asbestos 20, which corresponds to the ratio of ingredients, wt.%: Cement cement portland 44.145 NTF 0.005 Asbestos 0,882 Vermiculite2,725 Water 52.243 Example 2. 1000 g of cement Portland cement was closed in a suspension containing, g: nitrilotrimethylphosphonic acid O, 2, asbestos 40, vermiculite 90, water 1000.0, which corresponds to wt.% : Tampon Portland cement 46, 950 NTF0,010 Asbestos1,870 Vermiculite 4.220 Water 46,950
Пример 3.. 1000,0 г тампонаж ного портландцемента затворили на суспензии, содержащей, г: НТФ 0,3, асбест 69,3, вермикулит 115,3, вода 795,3, что соответствует мас.%:Example 3 .. 1000.0 g of cement Portland cement was closed on a suspension containing, g: NTF 0.3, asbestos 69.3, vermiculite 115.3, water 795.3, which corresponds to wt.%:
Тампонажный портланд-Ceiling Portland
цемент50,487,cement50,487,
НТФ 0,030NTF 0.030
Асбест3,500Asbestos3,500
Вермикулит5,835Vermiculite5,835
Вода40,168 Water40,168
f5f5
5 О 5 o
з s
45 45
5050
5555
30thirty
3535
4040
Результаты испытаний предлат-аемо- го облегченного тампонажного раствора и его ueMeifTHoro камн представлены в таблице.The results of tests of the pre-aemoe lightweight cement slurry and its ueMeifTHoro stone are presented in the table.
Как видно из табличных данных,там- понажный состав имеет улучшенные технологические характеристики, в частности он характеризуетс низкой усадкой цементного камн ,повышенной величиной адгезии камн с металлом трубы и пределом прочности при изгибе и сжатии. При дозировке вермикулита, меньшей 2,735 мас.%, снижаетс седи- ментационна устойчивость тампонажного раствора, повышаетс усадка. При дозировке вермикулита, большей 5,825 мас.%, происходит расслоение, тампонажного раствора, вследствие чего нарушаетс однородность формирующегос цементного камн , понижаетс его прочность и адгези к металлу трубы. Следовательно, дозировку вермикулита в пределах 2,725- 5,825 мас.%, нужно считать оптимйль- ной дл достижени цели изобретени ,As can be seen from the tabular data, the cement composition has improved technological characteristics, in particular, it is characterized by low shrinkage of the cement stone, an increased adhesion value of the stone with the metal of the pipe, and tensile strength in bending and compression. At the dosage of vermiculite, less than 2.735 wt.%, The mixing stability of the cement slurry decreases, shrinkage increases. When dosing vermiculite, greater than 5.825 wt.%, The separation of the cement slurry occurs, as a result of which the homogeneity of the forming cement stone is disturbed, its strength and adhesion to the pipe metal decreases. Therefore, the dosage of vermiculite in the range of 2.725- 5.825 wt.% Should be considered optimal for achieving the objective of the invention.
Эффективность применени тампонажного раствора заключаетс в повышении качества креплени скважин. Применение его не требует дополнительных капитальных затрат.The effectiveness of cement slurry application is to improve the quality of well casing. Its application does not require additional capital expenditures.
Claims (1)