SU1296530A1 - Method for making hole in glass - Google Patents

Method for making hole in glass Download PDF

Info

Publication number
SU1296530A1
SU1296530A1 SU823507661A SU3507661A SU1296530A1 SU 1296530 A1 SU1296530 A1 SU 1296530A1 SU 823507661 A SU823507661 A SU 823507661A SU 3507661 A SU3507661 A SU 3507661A SU 1296530 A1 SU1296530 A1 SU 1296530A1
Authority
SU
USSR - Soviet Union
Prior art keywords
glass
hole
tool
drill
heated
Prior art date
Application number
SU823507661A
Other languages
Russian (ru)
Inventor
Геннадий Владимирович Мазурин
Анатолий Николаевич Кривонос
Original Assignee
Г.В.Мазурин и А.Н.Кривонос
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Г.В.Мазурин и А.Н.Кривонос filed Critical Г.В.Мазурин и А.Н.Кривонос
Priority to SU823507661A priority Critical patent/SU1296530A1/en
Application granted granted Critical
Publication of SU1296530A1 publication Critical patent/SU1296530A1/en

Abstract

Изобретение относитс  к промьпп- ленности строительства, к технологии обработки стекл нных изделий. С целью упрощени  процесса сверлени  согласно предложенному способу нагрев стекла осуществл ют трением сверла о стекло, враща  его со скоростью 2000- 3000 об/мин. 3 ил.The invention relates to the construction industry, to the technology of processing glass products. In order to simplify the drilling process according to the proposed method, the glass is heated by rubbing the drill on the glass, rotating it at a speed of 2000-3000 rpm. 3 il.

Description

Изобретение относитс  к промышленности строительства, в частности к технологии обработки стекл нных изделий , а именно к изготовлению отверстий в стекле, ситаплах, кварце и др.материалах.The invention relates to the construction industry, in particular, to the technology of processing glass products, namely to the manufacture of holes in glass, sitaplah, quartz and other materials.

Цель изобретени  - упрощение процесса .The purpose of the invention is to simplify the process.

На фиг.1 изображена крива  в зкости стекол; на фиг. 2 и 3 - схема устройства дл  осуществлени  предлагаемого способа.Figure 1 shows the viscosity curve of glasses; in fig. 2 and 3 is a schematic of the device for carrying out the method.

На кривой в зкости стекол jvi (фиг.1) промежуток между точками 1 и 2  вл етс  интервалом разм гчени . При температуре t,- У стекла про вл ютс  свойства текучести, типичные дл жидкого состо ни . В зкость ц различных типов стекла примерно равна 10 Н с/м. При tj. по вл етс  хру кость, а в зкость возра.стает до Uj, 10 Н-с/м. Дл  большинства примен емых в технике силикатных стекол t(. 00-600°С, а tT 700-900°C, Дл  быстрого сверлени  отверстий в определенном месте стекло должно иметь t 700-9ПО С.Г,On the viscosity curve of jvi (figure 1), the gap between points 1 and 2 is the softening interval. At temperature t, - Glass exhibits flow properties typical of a liquid state. The viscosity of different types of glass is approximately 10 N / m. At tj. stiffness appears, and viscosity rises to Uj, 10 Ns / m. For the majority of silicate glasses used in the technique, t (. 00-600 ° C, and tT 700-900 ° C). To quickly drill holes in a specific place, the glass must have t 700-9PO S.G.

Сверло дл  осуществлени  предлагаемого способа должно быть на конце плоским, т.е. основание 3 сверла 4 должно закрьшать всю плрщадь сверле The drill for carrying out the proposed method must be flat at the end, i.e. the base 3 of the drill 4 should close the entire drill

  ШSh

f5f5

2020

2525

30thirty

ни , Сверло прижимают к стеклу 5 и вращают со скоростью 2000-3000 об/мин. От трени  в месте соприкосновени  вращающегос  сверла и стекла создаетс  температура 700-900 с. При этом быстрым движением сверла выдавливают в стекле сквозное или глухое отверстие . Лишнюю стекломассу с обратной стороны отверсти  срезают обычным способом.Nor, the drill is pressed against the glass 5 and rotated at a speed of 2000-3000 rpm. From friction at the point of contact between the rotating drill and the glass, a temperature of 700-900 s is created. At the same time, a quick movement of the drill squeezes a through or blind hole in the glass. Excess glass melt from the back side of the hole is cut in the usual way.

С целью устранени  теплопередачи от сверла к столу сверло 4 и стекло целесообразно термоизолировать от стола 6 прокладками.In order to eliminate heat transfer from the drill to the table, the drill 4 and the glass should be insulated from the table with 6 gaskets.

Claims (1)

Формула изобретени Invention Formula Способ изготовлени  отверсти  в стекле путем разогрева стекла до температуры разм гчени  в области отверсти  с помощью нагретого инструмента и выдавливани  керна при приложении усилий по продольной оси ин- стр умента, отличающийс  тем, что, с целью упрощени  процесса , нагрев стекла осуществл ют трением путем вращени  инструмента с плоским торцом со скоростью V 2000- 3000 об/мин в месте образовани  от- версти  до температуры в зкости стекла.A method of making a hole in the glass by heating the glass to the softening temperature in the hole area with a heated tool and squeezing out the core while applying forces along the longitudinal axis of the tool, characterized in that, to simplify the process, the glass is heated by friction by rotating a tool with a flat end face with a speed of 2000– 3000 rpm at the place where the hole is formed to the viscosity temperature of the glass. ЛL to tr to tr (риг.1(rig.1 j Фиг1j Fig1 фиг.Зfig.Z Редактор А.ОгарEditor A. Ogar Составитель Т.Парамонова Техред В.КадарCompiled by T.Paramonova Tehred V.Kadar Заказ 712/26 Тираж .428 .ПодписноеOrder 712/26 Circulation .428. Subscription ВНИИПИ Государственного комитета СССРVNIIPI USSR State Committee по делам изобретени и открытий П3035, Москва, Ж-35, Раущска  наб., д. 4/5on affairs of invention and discovery P3035, Moscow, Zh-35, Rauschsk nab. 4/5 Производственно-полиграфическое предпри тие, г.Ужгород, ул.Проектна , 4Production and printing company, Uzhgorod, Projecto st., 4 Корректор С.ЧерниCorrector S.Cherni
SU823507661A 1982-11-03 1982-11-03 Method for making hole in glass SU1296530A1 (en)