Description
Изобретение относитс к способу ионообменной обработки стекла и стеклоизделий и может быть использовано дл получени матированных стеклоизделий с повышенной термической стойкостью.The invention relates to a method for the ion-exchange treatment of glass and glass products and can be used to produce glass-coated glass products with enhanced thermal stability.
Целью изобретени вл етс получение матированного стелка с повышенной термической стойкостью.The aim of the invention is to obtain a matted insole with increased thermal resistance.
Способ осуществл ют следующимоб- образом..The method is carried out as follows.
Издели из стекла сначала обрабатывают в расплаве солей щелочных металлов, ионный радиус катионов которого больше ионного радиуса катионов стекла, затем провод т термообработку на воздухе до релаксации напр жений в приповерхностном слое, . после чего осуществл ют обработку в расплаве солей щелочного металла, ионный радиус катионов которого меньше ионного радиуса катионов CTetoia. Пример 1, Стекло, содержащее , йасЛ. SiO 71,2; 1,36; . 0,12; СаО 7,76; MgO 4,0; 5,14; SO 0,38, на второй стадииGlass products are first treated in the molten alkali metal salts, the ionic radius of the cations of which is larger than the ionic radius of the glass cations, and then heat treated in air to relax the stresses in the surface layer,. then, the treatment is carried out in the molten alkali metal salt, the ionic radius of the cations of which is less than the ionic radius of the CTetoia cations. Example 1, Glass containing, yasL. SiO 71.2; 1.36; . 0.12; CaO 7.76; MgO 4.0; 5.14; SO 0.38, in the second stage
обрабатывают в расплаве, содержащем, молЛ: ЫЫОз JO; NaNO 90,process in the melt, containing, mol: KOCH JO; NaNO 90,
Результаты обработки приведены в табл Л и 2.The processing results are shown in Table L and 2.
Пример 2. Стекло, содержащее , мас.% SiOj 72; В 0 8; 1; ВаО 5; MgO 2; KjO 12, обрабатьша-, ют в расплаве RbNO , термообрабаты- вают на воздухе, а затем обрабатывают в расплаве NaNO .Example 2. Glass containing, wt.% SiOj 72; B 0 8; one; BAO 5; MgO 2; KjO 12 is processed, melted in RbNO, heat treated in air, and then treated in a melt of NaNO.
Режимы обработки и достигнутые параметры приведены в табл.3.The processing modes and the achieved parameters are given in table 3.
Пример 3. Стекло, содержа- щее, мас.%: SiO, 63,97; 3,12; CaO 2,48; MgO 2,21; ВаО 10,31; KjO 6,32; 8,24; LiO 0,51; ZnO 2,6, обрабатьгоают в расплаве KNOj, затем термообрабатывают на воздухе и обрабатывают в расплаве NaNO, (опыт 1-3) и в расплаве, содерг жащем, мол.%: LiNO 30; NaNO 70 (опыт 4-6).Example 3. Glass containing, in wt.%: SiO, 63.97; 3.12; CaO 2.48; MgO 2.21; BAO 10.31; KjO 6.32; 8.24; LiO 0.51; ZnO 2,6, is treated in the melt KNOj, then heat treated in air and treated in the melt NaNO, (experiment 1-3) and in the melt containing mol.%: LiNO 30; NaNO 70 (experiment 4-6).
Режимы обработки и достигаемые светотехнические параметры приведены в табл.А.Processing modes and achievable lighting parameters are listed in Table A.
Таблица 1Table 1
Таблица 2table 2
Редактор Н.ГунькоEditor N. Gunko
Составитель С.БепобоковаCompiled by S. Bepobokova
Техред А.Кравчук Корректор С.ЧерниTehred A. Kravchuk Proofreader S. Cherni
Заказ 4782/27 Тираж 457 .ПодписноеOrder 4782/27 Circulation 457. Subscription
ВНИШИ Государственного комитета CCGPVNISHI State Committee CCGP
по делам изобретений и открытий 1,13035, Москва, Ж-35, Раушска наб, , д. 4/5for inventions and discoveries 1,13035, Moscow, Zh-35, Raushsk nab, 4/5
1роизводственно-полиграфическое предпри тие, г.Ужгород, ул.Проектна ,4Production and printing company, Uzhgorod, Projecto st., 4
Таблица 4Table 4
Claims (1)
Priority Applications (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| SU833666411A SU1255600A1 (en) | 1983-10-17 | 1983-10-17 | Method of treating glass |
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| SU833666411A SU1255600A1 (en) | 1983-10-17 | 1983-10-17 | Method of treating glass |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| SU1255600A1 true SU1255600A1 (en) | 1986-09-07 |
Family
ID=21090538
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| SU833666411A SU1255600A1 (en) | 1983-10-17 | 1983-10-17 | Method of treating glass |
Country Status (1)
| Country | Link |
|---|---|
| SU (1) | SU1255600A1 (en) |
Cited By (2)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CN103086590A (en) * | 2011-11-02 | 2013-05-08 | 富泰华工业（深圳）有限公司 | Frosted glass manufacturing method |
| RU2751179C1 (en) * | 2020-09-29 | 2021-07-12 | Общество с ограниченной ответственностью «Компания ФОТОТЕХ» | Method for obtaining fire-resistant glass with low-emission coating |
-
1983
- 1983-10-17 SU SU833666411A patent/SU1255600A1/en active
Non-Patent Citations (1)
| Title |
|---|
| Авторское свидетельство СССР № 628108, кл. С 03 С 21/00, 1976. За вка JP № 54-83923, кл. 21 В 72, 1979. * |
Cited By (3)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CN103086590A (en) * | 2011-11-02 | 2013-05-08 | 富泰华工业（深圳）有限公司 | Frosted glass manufacturing method |
| CN103086590B (en) * | 2011-11-02 | 2015-10-21 | 富泰华工业（深圳）有限公司 | Cloudy surface glass-making processes |
| RU2751179C1 (en) * | 2020-09-29 | 2021-07-12 | Общество с ограниченной ответственностью «Компания ФОТОТЕХ» | Method for obtaining fire-resistant glass with low-emission coating |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| US3790430A (en) | Alkali aluminosilicate glass article having an ion-exchanged surface layer | |
| US3873408A (en) | Method of producing a refractive index gradient in glass | |
| CA1322277C (en) | Strengthened glass article and method | |
| GB1076602A (en) | Glass articles having surface compressive stress | |
| KR20060027313A (en) | Alkaline glasses with modified surfaces and method for producing same | |
| KR910010203A (en) | Improved optical device and manufacturing method thereof | |
| SU1671625A1 (en) | Yellow glass | |
| US3660060A (en) | Process of making glass lasers of increased heat dissipation capability | |
| SU1255600A1 (en) | Method of treating glass | |
| CN108821570B (en) | Formula and method for preparing surface-strengthened transparent plate glass | |
| US3741739A (en) | Method of strengthening glass | |
| US3116991A (en) | Desalkalinisation of glass | |
| US5102833A (en) | Strengthening glass articles with electromagnetic radiation and resulting product | |
| CN108623154B (en) | Surface-strengthened transparent glass | |
| GB1342674A (en) | Process for production of glass articles with increased and more durable mechanical strength | |
| SU1315401A1 (en) | Ruby glass | |
| BR8506113A (en) | PROCESS OF PREPARING A GLASS COMPOSITION AND REFINABLE GLASS COMPOSITION | |
| JPH06219788A (en) | Method for decorating glass by ion exchange | |
| SU1276962A1 (en) | Method of checking exchange in melt-glass system | |
| JPH07223843A (en) | Production of chemically tempered glass | |
| CN1199896C (en) | Method for producing glass for goggles | |
| SU604837A1 (en) | Method of manufacturing photochromic glass | |
| SU1313819A1 (en) | Method for machining glassware | |
| JPS57149850A (en) | Surface treatment of glass | |
| SU1636356A1 (en) | High-temperature electric furnace |