SU1254055A1 - Method of applying enamel slip onto pipe - Google Patents
Method of applying enamel slip onto pipe Download PDFInfo
- Publication number
- SU1254055A1 SU1254055A1 SU853852053A SU3852053A SU1254055A1 SU 1254055 A1 SU1254055 A1 SU 1254055A1 SU 853852053 A SU853852053 A SU 853852053A SU 3852053 A SU3852053 A SU 3852053A SU 1254055 A1 SU1254055 A1 SU 1254055A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- slip
- tank
- pipe
- distance
- container
- Prior art date
Description
Изобретение относитс к нанесению в зкопл стичных жидкостей,, в частное ти тликёра эмали на обе поверхности трубы погружением, и может быть использовано в различтих отрасл х хо- з йствл, где треб тотс трубы с двухсторонним эмалевым покрытием.The invention relates to the application of plastic liquids to a private enamel ticking agent on both surfaces of the pipe by immersion, and can be used in various hospitality areas where a double enamel pipe is required.
Целью изобретени вл етс улучшение качества нанесенного сло шликера за счет повышени равномерности .The aim of the invention is to improve the quality of the applied slurry layer by increasing the uniformity.
На чертеже приведена схема осуществлени способа.The drawing shows the scheme of implementation of the method.
Предлагаемый способ осуществл ют с помощьюустройства,состо щего из емкости 1.заполненнойвшикером 2и соединенной посредствомтрубопроводов 3с реактором 4и насосами 5 и 6,причем насос 6 имеет меньшую производительность , чем производительность циркул рного часос а 5. Насос 6 соединен с помощью трубопроводов 7 с емкостью 1 и реактором Д, В емкости 1 размещен вытеснитель 8, а в верхней части емкости 1 - приемный сборник 9. На стенках емкости 1 и вытеснител 8 шликера на рассто нии f от поверхности размещены коллекторы tO дл подачи шликера стру ми к внутренней и наружной поверхност м трубы 11.The proposed method is carried out by means of a device consisting of a tank 1. filled with a flasher 2 and connected via pipelines 3c by reactor 4 and pumps 5 and 6, and pump 6 has a lower capacity than that of a circular clock 5. Pump 6 is connected via pipelines 7 with a capacity of 1 and reactor D, In tank 1, a displacer 8 is placed, and in the upper part of tank 1 is a receiving collector 9. On the walls of tank 1 and displacer 8 of the slip at a distance f from the surface are collectors tO for supplying the slip to jets the inner and outer surfaces of the pipe 11.
Трубу 0 300 мм с тагтщиной стенки 4 мм погружают в емкость, заполненную шликером. При этом шликер в емкости непрерывно привод т в движение подава в емкость 1 насосом 5 через коллекторы 10, расположенные вблизи поверхности на рассто нии f от поверхности шликера, шликер, заполн емкость, переливаетс через верхний край в приемный сборник 9, из которого самотеком по опускным трубам поступает в реактор 4, где его перемешивают и оп ть насосом 5 подают в емкость 1 дл нанесени . Таким образом , емкость 1 дл нанесени шликера вл етс составной частью циркул ционного контура, в котором пшикер находитс в непрерывном движении. Уровень шликера в емкости 1 дл нанесени поддерживают посто нным, поскольку этот уровень образуетс в результате перелива шликера через верхний край емкости 1.Pipe 0 300 mm with a wall thickness of 4 mm is immersed in a container filled with a slip. In this case, the slip in the tank is continuously driven by the pump 5 through the collectors 10, located near the surface at a distance f from the slip surface, the slip, filling the tank, is poured over the top edge into the receiving collector 9, from which by gravity the tubes enter the reactor 4 where it is mixed and again pump 5 is fed to the application tank 1. Thus, the tank 1 for applying the slip is an integral part of the circulation loop, in which the pysher is in continuous motion. The level of the slip in the container 1 for application is kept constant, since this level is formed as a result of the overflow of the slip through the upper edge of the container 1.
На рассто нии f от уровн поверхности шликера, определ емом соотношениемAt a distance f from the level of the surface of the slip, determined by the ratio
f t,....- V f t, ....- V
1one
25А055 где25А055 where
- рассто ние от уровн поверхности до зоны разрушени структурного режима течени шликера; 5 МКС врем , в течение которого - distance from the surface level to the zone of destruction of the structural mode of the slip flow; 5 ISS time during which
восстанавливаетс структур- ньй режим течени шликера, определ емое тиксотропными свойствами шликера,the structural mode of the slip flow, which is determined by the thixotropic properties of the slip, is restored,
О V скорость Движени шликера в емкости, определ ема из конструктивных характеристик циркул ционного контура. Стру ми из коллектора 10 подают шли- 5 кер, непрерывно разруша структурный режим течени шликера в емкости как в объеме, наход щемс снаружи трубы, так и внутри нее. Рассто ние f определ ютс в зависимости от тиксотроп- 20 свойств шликера по формуле, приведенной выше. Характеристиками тиксотропных свойств шликера вл ютс врем Т,„КС скорость V движени шликера в емкости. О V is the speed of the Slip Motion in the tank, determined from the design characteristics of the circulation circuit. The streams from the collector 10 feed the slotted-hole, continuously destroying the structural mode of the flow of the slip into the vessel both in the volume outside the pipe and inside it. The distance f is determined depending on the thixotropic slip properties of the slip according to the formula given above. The characteristics of the thixotropic properties of the slip are the time T, KS, the speed V of the movement of the slip in the tank.
25 в процессе извлечени трубы из емкости, заполненной ишикером как иа внутренней, так и на наружной поверхност х трубы остаетс слой шликера , образующийс в результате 30 увлечени при движении трубы шликера, хорошо смачиваклцего ее поверхность. При этом качество нанесениого на трубу сло шликера, в частности, толщина и равномерность толщины, 35 как показали исследовани , завис т от состо ни шликера вблизи уровн поверхности его в емкости дл нанесени . Образующийс в результате тиксотропных свойств структурный режим 40 течени шликера в емкости дл нанесени разру1цают, дополнительно непрерывно подава шликер в емкость стру ми , но не на поверхность уровн шликера в емкости, а подава допол- 45 нительно шликер стру и в объем на некотором рассто нии f от поверхности шликера в емкости.25, in the process of removing the pipe from a container filled with a desiccant both on the inner and outer surfaces of the pipe, there remains a slurry layer resulting from 30 entrainment when the slurry pipe moves, its surface is well wetted. At the same time, the quality of the slurry layer applied to the pipe, in particular, the thickness and uniformity of thickness, 35 as studies have shown, depend on the state of the slurry near its surface level in the application container. The resulting structural thixotropic properties of the slip current 40 in the application tank are destroyed, additionally continuously feeding the slip into the container with jets, but not onto the surface of the slip level in the container, but feeding additionally with slip and into the volume at a certain distance f from the surface of the slip in the tank.
Приме р. Трубу 0 300 мм с толщиной стенки 4 мм, длиной 10 м погружали в емкость, заполненную шликером, и извлекали из емкости. Шликер характеризовалс следующими рабочими параметрами; тонина помола 2 мл/мин (по методу Лисенко), удель- ный вес 1,7 г/см , консистенци 12 г/дм, Скорость извлечени трубы из емкости 10 м/мин.Primer p. Pipe 0 300 mm with a wall thickness of 4 mm, a length of 10 m was immersed in a container filled with a slip, and removed from the container. The slip was characterized by the following operating parameters; grinding fineness 2 ml / min (according to the Lysenko method), specific gravity 1.7 g / cm, consistency 12 g / dm, The speed of extraction of the pipe from the tank is 10 m / min.
Рассто ние коллекторов от поверхности шликера согласно было выбрано равньм f- 25 мм при скорости движени шликера в емкости, равной V 15 мм/с, и времени восстановлени структурного режима в течение дл данного состава, равном i, 3 с.The distance of the collectors from the surface of the slurry was consistently equal to f-25 mm with the speed of the slurry in the tank equal to V 15 mm / s and the recovery time of the structural mode for a given composition equal to i, 3 s.
Согласно предлагаемому способу структурный режим течени шликера в поверхностном слое разрушают не движением стенок трубы, а стру ми шлиРедактор Л.ПовханAccording to the proposed method, the structural mode of the slip flow in the surface layer is destroyed not by the movement of the pipe walls, but by jets of the editor. L. Povkhan
Составитель В.ОлейниченкоCompiled by V.Oleynichenko
Техред М.Ходанич Корректор М.МаксимишинецTehred M. Khodanich Proofreader M. Maksimishinets
Заказ 4690/31 Тираж 878ПодписноеOrder 4690/31 Circulation 878 Subscription
ВНИИПИ Государственного комитета СССРVNIIPI USSR State Committee
по делам изобретений и открытий 113035, Москва, Ж-35, Раушска наб., д. 4/5for inventions and discoveries 113035, Moscow, Zh-35, Raushsk nab., 4/5
Производсвтенно-полиграфическое предпри тие, г. Ужгород, ул. Проектна , 4Production and printing company, Uzhgorod, st. Project, 4
25А055425А0554
кера, т.е. создают стабильные услови дл нанесени шликера как на начальном участке трубы, так и по всей ее поверхности. Это определ ет бо- 5 лее высокое качество нанесенного сло шликера дл последующего получени покрыт.keru, i.e. create stable conditions for applying the slip both on the initial section of the pipe and on its entire surface. This determines the higher quality of the applied slurry layer for subsequent coating.
Предлагаемый способ позвол ет О получать равномерный слой шликера по всей поверхности трубы.The proposed method allows O to obtain a uniform slip layer over the entire surface of the pipe.
Claims (1)