SU1239203A1 - Composition for making beds and pavings of roads - Google Patents
Composition for making beds and pavings of roads Download PDFInfo
- Publication number
- SU1239203A1 SU1239203A1 SU843782411A SU3782411A SU1239203A1 SU 1239203 A1 SU1239203 A1 SU 1239203A1 SU 843782411 A SU843782411 A SU 843782411A SU 3782411 A SU3782411 A SU 3782411A SU 1239203 A1 SU1239203 A1 SU 1239203A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- composition
- water
- pavings
- roads
- superphosphate
- Prior art date
Description
1one
Изобретение относитс к строительству -и может быть использовано при устройстве дорожных оснований покрытий.The invention relates to the construction of - and can be used in the construction of road pavement bases.
Цель изобретени - повьшение прочности, водо- и морозостойкости композиций.The purpose of the invention is to increase the strength, water and frost resistance of the compositions.
в подготовленный грунт последо- вательно ввод т при перемешивании цемент, суперфосфат, отход разработки нефт ных скважин и воду, при этом отход разработки нефт ных сква жин ввод т совместно с водой затво- рени смеси,-которую затем уплотн ют при оптимальной влажности.Cement, superphosphate, oil development waste and water are successively introduced into the prepared soil with mixing, together with oil from the mixing of the mixture, which is then compacted at optimum humidity.
Взаимодействие суперфосфата (в состав которого входит Ca(E.., POi,)2 «HjQ + CaSOi., + PjOg 14-19%) химическое и адсорбционное, в частности катионов кальци с кремнеземистой составл ющей заполнител , обуславливает образование водостоМих и тгрочных соединений гидросиликатов кальци , ионы фосфора соедин ютс с полуторными окислами железа и алюмини заполнител с образованием устойчивых и нераствори1-1ых в воде фосфорнокислых солей железа и ллюми ни . В результате возникают дополнительные водостойкие кристаллизационные св зи, упрочи лощиес во вре мени..,The interaction of superphosphate (which includes Ca (E .., POi,) 2 "HjQ + CaSOi., + PjOg 14-19%) chemical and adsorption, in particular calcium cations with the silica component of the aggregate, causes the formation of water-resistant and hard compounds calcium hydrosilicates, phosphorus ions combine with sesquioxides of iron and aggregate aluminum to form stable and insoluble in water phosphoric acid salts of iron and aluminum. As a result, additional water-resistant crystallization bonds, strengthening the poloshes in time,
Отход разработки нефт ных скважин (ОРНС) рекомендуетс использовать в предлагаемой смеси в небольших дозировках, где он выполтшет роль активной органической добавки,, котора в результате химической адсорбции ее компонентов тонкодисперсной частью заполнител и ..образовани мономолекул рных или полимолекул рных водоотталкивающих слоев, гидрофобиз ирует материал и придает ему повышенную водо-, морозостойкость и достаточную деформативную устойчивость.Oil development waste (ORNS) is recommended to be used in the proposed mixture in small dosages, where it will play the role of an active organic additive, which, as a result of chemical adsorption of its components into a fine dispersed part of the aggregate and .. forming monomolecular or polymolecular water-repellent layers, will hydrophobize material and gives it increased water, frost resistance and sufficient deformative resistance.
Таким образом, совместное воздействие суперфосфата и ОРНС активирует процесс гидратационного твердени цемента в предлагаемой смеси и повьшает прочность и и морозостойкость материала.Thus, the combined effect of superphosphate and ORNS activates the process of hydration hardening of the cement in the proposed mixture and increases the strength and frost resistance of the material.
ОРНС представл ют собой i-..л., .эид- ную систему, в которой дисперсной средой служит углеводородна фаза, состо ща из дизельного топлива, нефти, углеводорастворимых ПАВ. Дисперсна фаза представлена твердыми частицами извести, барита, глины и в оды.OPCS is an i -... l., Eid system in which the dispersed medium is a hydrocarbon phase consisting of diesel fuel, oil, and carbohydrate-soluble surfactants. The dispersed phase is represented by solid particles of lime, barite, clay, and into odes.
Состав вход щих в ОРНС компонен- ,тов, мас.%:The composition of the components included in the OPCS, wt.%:
Дизельное топливо 15,5-20,6 Битум высокоокисленный3 ,8-4,3 Известь8,0-8,4 S Барит 56,1-57,8 Сульфанол1,1-1,3 СМАД-1 0,2-0,8 Нефть , 0,5-1,8 Вода с глинистымDiesel fuel 15.5-20.6 Highly oxidized bitumen3, 8-4.3 Lime8.0-8.4 S Barite 56.1-57.8 Sulfanol1.1-1.3 SMAD-1 0.2-0.8 Oil, 0.5-1.8 Water with clay
0 компонентомОстальное0 component Else
(МАД-1 - смесь окисленного пет- ролатума и дизельного топлива при соотношении 4:6. Асфальтосмолистые компоненты битума и мьша, образую- 5 щиес в процессе взаимодействи извести с битумом, дизельным, топливом ,, служат структурообразователем в системе. Плотность.ОРНС 1,05- 2j20 г/см. услоБна в зкость 25- 0 , статическое . напр жение сдви- :.:/ 1-12 мг/см .(MAD-1 is a mixture of oxidized petrolatum and diesel fuel at a ratio of 4: 6. Asphalt resin components of bitumen and pellets, which are formed during the interaction of lime with bitumen, diesel, fuel, serve as a structurant in the system. Density. ORNS 1 , 05-2j20 g / cm. Conditional viscosity 25-0, static. Shift-:.: / 1-12 mg / cm.
Готов т несколько составов предлагаемой композиции. Дл этого использзтот т жело.й пылеватый суг- 5 линок с границей текучести 36%, портландцемент марки 400,. ОРНС и суперфосфат простой технический. Изготовление и ис .1мтание образцов производ т в соответствии с методи- Q кой по СН 25-74. Щ пиндрические о6- диаметром и высотой 4 см фор-. муют при оптимальной влажности и давлении уплотнени 15,0 МПа. Твердение их протекает в воздушно- .е Ешажнрй среде при относительной влажности 95% и темпера уре 20-22 С.Prepare several formulations of the proposed composition. To do this, use a yellow-dusting suture with 5 lines with a yield strength of 36%, Portland cement 400 ,. ORNS and superphosphate simple technical. The manufacture and testing of samples was carried out in accordance with the method of Q 25-74. U pindricheskiy o6-diameter and height of 4 cm form-. crush at optimum humidity and compaction pressure of 15.0 MPa. Their hardening proceeds in an air-free environment with a relative humidity of 95% and a temperature of 20-22 C.
Примеры количественного соотношени компонентов предлагаемой композиции и результаты определений ее фийико-механических характеристик представлены в таблице. Как видно из таблицы, предлагаема композици ргмеет высокие показатели прочности, водо- и морозостойкости.Examples of the quantitative ratio of the components of the proposed composition and the results of determining its fiyiko-mechanical characteristics are presented in the table. As can be seen from the table, the proposed composition gives high rates of strength, water and frost resistance.
Claims (1)