SU1158510A1

SU1158510A1 - Ceramic brown pigment

Info

Publication number: SU1158510A1
Application number: SU843686966A
Authority: SU
Inventors: Галина Николаевна Кукушкина; Алла Николаевна Демидовская; Ольга Трофимовна Ирклиевская; Валентина Николаевна Мохорт
Original assignee: Украинский Научно-Исследовательский Институт Стекольной И Фарфоро-Фаянсовой Промышленности
Priority date: 1984-01-05
Filing date: 1984-01-05
Publication date: 1985-05-30

Abstract

КЕРАМИЧЕСКИЙ ПИГМЕНТ КОРИЧНЕВЫЙ , включакщий Те,О}, ZnO, Alj, GI , о т л и Ч а ю щ и и с тем, что, с целью повьппени чистоты тона, он дополнительно Содержит при следующем соот ношении компонентовvMac %: Fej,.35,5-36,5 tnO49-53 AliO.,9,5-12,0 ,0-2,5CERAMIC PIGMENT BROWN, including Those, O}, ZnO, Alj, GI, and the fact that, in order to keep the tone pure, it additionally contains the following component ratio vMac%: Fej ,. 35.5-36.5 tnO49-53 AliO., 9.5-12.0, 0-2.5

Description

0101

РОRo

СП Изобретение относитс к керамической промьппленности, в частности к декорированию фарфоровых изделий Известен керамический пигмент коричневый, включакщий, вес.%: 2ГгОг 0; AljO} 10; 2hO 20; FejOj 20; CfiO, 10 p. Недостатком известного состава вл етс невысока чистота тона 30%. Наиболее близким к изобретению в л етс керамический пигмент коричне включаилций следующие компоненты,вес 4,33; ZnO 36,) 17,7; 4,77; ZhOt 37,3; SbtOj О ,6 Недостатком указанного состава вл етс невысока чистота тона 45 Цель изобретени -. повышение чистоты тона. Поставленна цель достигаетс тем, что керамический пигмент кори невьй, включающий AljGj, дополнительно содержит KjO при следующем соотношении компонен тон, мас,%: ГегО%35,5-36,5 ZnO49-53 AljOj9,5-12,0 ,0-2,5 Исходные сырьевые материалы перемешивают и измельчают мокрым способом в шаровой мельнице, приче ввод т в состав пигментов в виде калиевой се1|итры KWO . При эт весовое соотношение материалов, ме лющих тел и водал должно составл ть 1:1,3:0,5. Готова шихта должна иметь остаток 0,3 мас.% на сите № 0056 (10856 отв/см)по ГОСТ 3584 Размолотую шихту после предвари тельного подсупшвани при 120±10°С до конечной влажности, не превышаю щей 0,3 мас.% и просеивани через сито 07 (100 отв/см, обжигают при ШОО-ПОО С. В табл, I приведены конкретные составы пигмента. Т а б л и ц а Содержание,, мае, Компоненты составе П одолжение табл | мас.% в Содержание, омпоненты составе Цвет пигментов после обжига интенсивный светло-коричневый. Предложенный пигмент в сочетании с кислотостойким флюсом № 91-к может быть использован дл получени надглазурной краски светло-коричневого цвета. Флюс № 91-к имеет следуинций состав: РЬз04 54.2: SiOj 26.4; 10,8; AljOj 4,0; CaCOj 0,17; М§0 0,1; ZhO 2,43; Xi Oj, 1,9. Керамические надглазурные краски ев е тло-коричнево го цв е та, полученные на основе за вл емого пигмента имеют физико-технические характеристики, приведенные в табл. 2. лица 2| Устойчивость к воздействию. ;4%-ного раствора уксусной кислоты в течение 4ч Вьщерживают без изменени Рабочие свойства при различных способах декорировани (.согласно РСТ УССР 1449-77 по п тибальной шкале)The invention relates to ceramic industry, in particular, to the decoration of porcelain products. The ceramic pigment brown is known, inclusive, in wt.%: GyOg 0; AljO} 10; 2hO 20; FejOj 20; CfiO, 10 p. A disadvantage of the known composition is a low purity of 30%. Closest to the invention, brown ceramic pigment includes the following components, weight 4.33; ZnO 36,) 17.7; 4.77; ZhOt 37.3; SbtOj O, 6 The disadvantage of this composition is the low purity of the tone. 45 The purpose of the invention is. increase the purity of the tone. The goal is achieved by the fact that the ceramic pigment of measles nevi, including AljGj, additionally contains KjO in the following ratio of components, wt,%: GeOO% 35.5-36.5 ZnO49-53 AljOj9.5-12.0, 0-2 , 5 Raw materials are mixed and ground by a wet method in a ball mill, and the pigments are introduced into the composition of pigments in the form of potassium sulfur (1) KWO. With this, the weight ratio of materials, grinding media and water should be 1: 1.3: 0.5. The finished batch should have a residue of 0.3 wt.% On a sieve No. 0056 (10856 holes / cm) according to GOST 3584 Ground milled after pretreatment at 120 ± 10 ° С to a final moisture content not exceeding 0.3 wt.% And sifting through a sieve 07 (100 holes / cm, calcined at SCHO-VET C. Table I shows the specific pigment compositions. Table of contents, May, Components of the composition Components Composition Color of pigments after firing is intense light brown.The proposed pigment in combination with acid-resistant flux No. 91-K can be used to obtain a light brown overglaze paint. Flux No. 91-K has the following compositions: Pz04 54.2: SiOj 26.4; 10.8; AljOj 4.0; CaCOj 0.17; Mg0 0.1; ZhO 2.43; Xi Oj, 1.9. Ceramic overglaze paints of the E of the e-brown color, obtained on the basis of the claimed pigment, have the physico-technical characteristics shown in Table 2. Faces 2 | Resistance to Effects; 4% - acetic acid solution for 4 hours. Remain unchanged. Operating properties for various methods of decoration (. According to PCT USSR 1449-77 on a five-point scale)

3 3

Положительный эффект при исполь-в улучшении качества декора за счетPositive effect when used to improve the quality of the decor due to

зевании за вл емого керамическогостабильности и насыщенности ЗДета,the yawning of the claimed ceramic stability and saturation of ZD,

пигмента светло-коричневого цвета -хороших рабочих свойств при полном ,pigment light brown color - good working properties with full,

дл получени иадглаэурной керами- .отсутствии цекообразовани , а/такжеto obtain iadglare ceramics- no cementation, and / also

ческой краски дл декорировани f5 .за счет широкого использовани в самыхpaint for decorating f5. due to its wide use in the most

фарфорофа нсовых изделий выразитс (разнообразных методах декорировани /The porcelain of porcelain products is expressed (various methods of decorating /

Claims

CERAMIC PIGMENT BROWN, including TejOj, ZnO, Alj, O _s , with the fact that, in order to improve the purity of the tone, it additionally contains K _x 0 in the following ratio of components * May * X :

Fe _t O> 35.5-36.5

7p0 49-53

A1 ₂ 0 ₃ 9.5-12.0

K _g 0 2.0-2.5

1 1158510 2