SU1071659A1 - Pulverulent composition for chromosiliconizing products of nickel-plated carbon steels - Google Patents
Pulverulent composition for chromosiliconizing products of nickel-plated carbon steels Download PDFInfo
- Publication number
- SU1071659A1 SU1071659A1 SU823504295A SU3504295A SU1071659A1 SU 1071659 A1 SU1071659 A1 SU 1071659A1 SU 823504295 A SU823504295 A SU 823504295A SU 3504295 A SU3504295 A SU 3504295A SU 1071659 A1 SU1071659 A1 SU 1071659A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- oxide
- aluminum
- products
- nickel
- carbon steels
- Prior art date
Abstract
ПОРОШКООБРАЗНЫЙ СОСТАВ ДЛЯ ХРОМОСИЛИЦИРОВАНИЯ ИЗДЕЛИЙ ИЗ BHKEjmf | ОВАННЫХ УГЛЕРОДИСТЫХ СТАЛЕЙ, вклютчакнций окись алюмини , окись хрома, ато1Ф1ний, силикокальций и хлористый аммоний о тли ч а. ю щи и с тем,что, с целью йовьииени коррозионной стойкости обрабатываемых изделий в фосфорной кислоте, он дополнительно содержит окись вольфрама и окись магни при следукхцем соотнс дении компонентов, мае.%: Окись магни 34-36 Окись хрома . 6,5-8,5 АЛЮМИНИЙ 5,38-6,37 Силикокальций 1,12-2,13 Окись вольфрама 1-3 Хлористый С1ММОНИЙ Остальное Окисв алюьй)ни POWDERED COMPOSITION FOR CHROMOSILICATION OF PRODUCTS FROM BHKEjmf | AUGUSTED CARBON STEELS, including alumina, chromium oxide, atom1F1nium, silicocalcium and ammonium chloride or aphid a. also with the fact that, in order to reduce the corrosion resistance of the processed products in phosphoric acid, it additionally contains tungsten oxide and magnesium oxide at the following ratio of components, May.%: Magnesium oxide 34-36 Chromium oxide. 6.5-8.5 ALUMINUM 5.38-6.37 Silikokaltsy 1.12-2.13 Oxide of tungsten 1-3 Chlorine C1MMONI Rest Oxide in aluminum) nor
Description
сь елhave eaten
со Изобретение относитс к- металлу ргии , а именно к химико-термической обработке металлов и сплавов в порсШ ковых средах и может быть использовано дл повышени эксплуатационных характеристик изделий из предварительно никелированных углеродистых сталей, примен емых в приборостроительной , нефт ной, машиноцтроительной , химической и пищевой отрасл х промышленности. Известен состав дл диффузионного хромосилицировани из порсшковых сме сей на основе феррохрома и ферросилици СИ . Однако термодиффузиоииа обработк предварительно никелированных углеродистых сталей иэ этих составов не позвол ет получать на них диффузионные слои с высокой кбррюзионной стой костью из-за неудовлетворительного качества поверхности обрабатываемых материалов поJлe химико-термической обработки. Наиболее близким по технической сущности и достигаекюму эффекту к предлагаемому вл етс состав дл хромосилицировани t2l, содержаний, мае.%: 11-13 Алюминий 7,2-9,6 Силикокальций 38,4-40,3 Окись хрома Хлористый 0,5-1,5 аммоний 0,5-1,5 Фтороборат кали Остальное Окись алюмини Однако коррозионна стойкость предварительно никелированных углерОThe invention relates to a rhy-metal, namely, the chemical-thermal treatment of metals and alloys in porous media and can be used to improve the performance characteristics of products from pre-nickel-plated carbon steels used in instrument-making, petroleum, machine building, chemical and food industry A known composition for diffusion chromosilication from powder mixtures based on ferrochrome and ferrosilicon SI. However, thermal diffusion treatment of pre-nickel-plated carbon steels with these compositions does not allow them to receive diffusion layers with a high corrosion resistance due to the unsatisfactory quality of the surface of the processed materials after chemical-thermal treatment. The closest to the technical essence and achievable effect to the proposed is the composition for chromosilicating t2l, contents, May.%: 11-13 Aluminum 7.2-9.6 Silicocalcium 38.4-40.3 Chromium oxide Chloride 0.5-1 , 5 ammonium 0.5-1.5 Potassium Fluoroborate Else Aluminum oxide However, the corrosion resistance of pre-nickel-plated carbon
Состав насыщающей среды, Мас.%The composition of the saturating medium, wt.%
ИзвестныйFamous
40 Al Oj+ll Al + 38,4 + + 9,6 Каси+0,5 ,5.КН4,С140 Al Oj + ll Al + 38.4 + + 9.6 Kasi + 0.5, 5.KN4, C1
ПредлагаемыйProposed
47 Alj,O,+ 2 МаО + 7,5 А1 +47 Alj, O, + 2 MaO + 7.5 A1 +
+ 34 + 2,130VO, ++ 34 + 2,130VO, +
+6,37 Каси + -1 +6.37 Kasi + -1
45 Al2.0j +3 8,5 Al 45 Al2.0j +3 8.5 Al
+35 Cfj,0j +1, + +35 Cfj, 0j +1, +
+5,38 Каси + 2 НН,С1+5.38 Kasi + 2 NN, C1
44 А1гОа+ 4 + 6,5 Al +44 A1gOa + 4 + 6.5 Al +
+ 36 +1, ++ 36 +1, +
+5,78 Каси + 3 ЫН,С1+5.78 Kasi + 3 UN, C1
КТОWHO
Коррозионна стойгг ,ч кость в фосфорной кислоте; Corrosion corrosion, h bone in phosphoric acid;
900900
10ten
11eleven
12 дистых сталей после обработки в известном составе не вл етс достаточной при работе деталей из этих матвч риалов в высокоагрессивных средах химической, нефт ной и пищевой промыишенности . Целью изобретени вл етс повышение коррозионной стойкости обрабатываемых изделий в фосфорной кислоте . Указанна цель достигаетс тем, что порошкообразный состав дл хромосилицировани изделий из никелированных углеродистых сталей, включалоадий окись алюмини , окись хрома, алюминий, Силикокальций и хлористый аммоний, дополнительно содержит окись вольфрама и окись магни при следующем соотношении компонентов, мае.%: . Окись магни 2-4 Окись хрома 34-36 Алюминий 6,5-8., 5 Силикокальций 5,38-6,37 Окись вольфрама 1,12--2,13 - Хлористый аммоний 1-3 Окись алюмини Остальное Хромосилициррвание в предлагаемой порошковой среде осуществл ют при в течение 4 ч в контейнерах с плавким затвором. Сравнительные данные по коррозионной стойкости предварительно никелированной Ст. 20 в 10%-ном раство- . ре фосфорной кислоты при использовании известного и предлагаемого составов приведены в таблице.The 12 distal steels after treatment in a known composition are not sufficient for the operation of parts from these matrices in highly aggressive chemical, petroleum and food products. The aim of the invention is to increase the corrosion resistance of processed products in phosphoric acid. This goal is achieved in that the powdered composition for chromosilicating nickel-plated carbon steel products, including aluminum oxide, chromium oxide, aluminum, silicocalcium, and ammonium chloride, additionally contains tungsten oxide and magnesium oxide in the following ratio of components,% by weight:. Magnesium oxide 2-4 Chromium oxide 34-36 Aluminum 6.5-8., 5 Silicocalcium 5.38-6.37 Tungsten oxide 1.12--2.13 - Ammonium chloride 1-3 Aluminum oxide Rest Chromosilicon in the proposed powder the medium is carried out for 4 hours in containers with a fusible closure. Comparative data on the corrosion resistance of pre-nickel-plated Art. 20 in 10% solution-. of phosphoric acid when using the known and proposed formulations are given in the table.
S10716594S10716594
Таким образом, использование прьмрасшир ет области промышленного ислагаемого состава позвол ет повыситьпользовани процесса хромосилицирокоррозионную стойкость в фосфорнойвани никелированных углэродистыхThus, the use of the wider area of the industrial composition of the composition makes it possible to increase the use of the chromosilicon-corrosion process in the phosphorus nickel-plated carbonaceous
кислоте в 10 раз, что значительносталей..acid 10 times, which is significant the stalled ..
Claims (1)