SU1062192A1 - Binder - Google Patents
Binder Download PDFInfo
- Publication number
- SU1062192A1 SU1062192A1 SU823388492A SU3388492A SU1062192A1 SU 1062192 A1 SU1062192 A1 SU 1062192A1 SU 823388492 A SU823388492 A SU 823388492A SU 3388492 A SU3388492 A SU 3388492A SU 1062192 A1 SU1062192 A1 SU 1062192A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- glass
- portland cement
- calcium sulfate
- ground
- sio2
- Prior art date
Abstract
ВЯЖУЩЕЕ, включающее б1-фос- фополугидрат сульфата кальци ,портландцемент и пуццолановую добавку, ,о т л и ч а ю щ е е с тем, что, с целью повьшени прочности и водостойкости , оно содержит дополнительно молотый бой технического стекла системы SiO2-R2- Р следующем соот нсшении компонентов, мае.%: сС-фосф ополугидрат сульфата кальци 40-80 Портландцемент 6-24 Пуццоланова добавки4-16 Молотый бой технического стекла системы SiO2-R.O 10-20 СПBINDING, including b1-phosphate calcium sulfate hemihydrate, portland cement and pozzolanic additive, so that, in order to improve strength and water resistance, it also contains ground glass of technical glass of the SiO2-R2 system - P the following ratio of components, wt.%: SC-phosph calcium sulfate hemihydrate 40-80 Portland cement 6-24 Pozzolanum additive4-16 Ground bout of technical glass of the SiO2-RO 10-20 SP system
Description
toto
;о IND Изобретение относитс к строктел ным материалам и может найти примеиение дл изготовлени строительных растворов, бетонов и изделий на их основе. Известно в жущее, содержащее портландцементный клинкер, активную минеральную добавку и гипс Cl2. Наиболее близким к изобретению по технической сущности и достигаемому результату вл етс фосфогипсо цементнопуццолановое в жущее, со-, держащее о.-фосфополугидрат сульфата кальЦи 50 - 80%, активную минеральную добавку 5 - 15% и портландцемент - остальное С2. Недостатками указанных в жущих вл ютс низка прочность и водостойкость изделий на их основе. Целью изобретени вл етс повышение прочности и водостойкости, Цель достигаетс тем, что в жущее , включающее оС-фосфополу гидрат сульфата кальци , портландцемент и пуццолановую добавку, дополнительно содержит молотый бой технического стекла системы SiO2-R2O Р следую щем соотношении компонентов, мас,% oir-Фосфополугидрат сульфата кальци 40-80 I Портландцемент 6-24 Пуццоланова добав-. ка4-16 Молотый бой технического стеьла системы SiO2-R2O Твердение в жущего может- осуществл тьс при нормальной темпера туре в воздушнр-влажнрстной среде или в процессе термовлажностной обработки. Введение в в жущее моло го стекла не оказывает существенро го вли ни на сроки схватывани и нарастани прочности при твердении Издели , полученные на его основе. обладают повышенной прочностью и водостойкостью. Объ сн етс это тем, что при взаимодействии молотого стекла, вход щего в состав в жущего , с водой образуютс различные по составу твердые растворы, а также гидрогранаты, труднорастворимые в воде с повышенной прочностью. Технологи приготовлени в жущего состоит в следующем. Берут бой технического стекла и производ т его помол до удельной поверхности 3000-4500 . Исходные компоненты в жущего при указанном выше соотношении тщательно перемешивают . Пример. Исходные компоненты: ot-фосфополугидрат сульфата кальци , полученный на опытных установках ВНИИСТРОМа, фосфогипсовое в жущее марки 200, портландцемент Воскресенс кого цемештного завода марки 400, Пуццоланова добавка - трепел Бр нского месторождени , молотый до удель ной поверхности 4200 бой технического стекла Васильевского стекольного завода. Химические составы использованных компонентов, %: бой технического стекла системы 6Ь,8 SiO2; 2,5 3,§ 8,4 СаО; 0,8 МдО; 14,7 (Na2O + 1,2 п.п.п; Бр нский трепел 79,5 SiO-; 7,1 3,1 4,1 СаО; 1,7 МдО; 4,3 п.п.п. Получсшзт в жущее смещением исходных компонентов. На полученных в жущих готов т стррительйый раствор состава 1:3, Прочностные испытани растворов провод т в возрасте 28 сут Hci образцах балочках по ГОСТ 310. 4-76. Коэффициент разм гчени определ ют по ОСТ 21-29-77. Примеры составов в жущего и результаты физико-механических испытаний прив€ дены в таблице.About IND The invention relates to construction materials and can be used for making mortars, concretes and products based on them. It is known to contain, containing Portland cement clinker, active mineral additive and gypsum Cl2. The closest to the invention to the technical essence and the achieved result is phosphogypso cement-puztsolanovogo stitching, containing, O.-phospho-hemihydrate calcium sulfate 50 - 80%, active mineral additive 5 - 15% and Portland cement - the rest C2. The disadvantages of these residents are low strength and water resistance of products based on them. The aim of the invention is to increase the strength and water resistance. The goal is achieved by the fact that the calcium sulfate hydrate, portland cement and pozzolanic additive, including os-phosphorus, additionally contains ground bout of technical glass SiO2-R2O P with the following ratio of components, wt.% Oir - Calcium sulphate phosphotoluhydrate 40-80 I Portland cement 6-24 Puzzolanova add-. ka4-16 Ground bout of the technical window of the SiO2-R2O system The hardening of the binder can be carried out at normal temperature in the air-humid environment or during the process of moisture and humidity treatment. The introduction of tough glass into the glass does not significantly affect the setting time and the increase in curing strength of the article obtained from it. possess the increased durability and water resistance. This is explained by the fact that the interaction of ground glass entering the composition of a binder with water results in the formation of various solid solutions, as well as hydrogarnetts, which are difficult to dissolve in water with increased strength. The preparation technology for the live is as follows. They take the battle of technical glass and grind it to a specific surface of 3000-4500. The original components in the binder at the above ratio are thoroughly mixed. Example. Source components: calcium sulfate ot-phospho-hemihydrate, obtained on pilot plants of VNIISTROM, phosphogypsum suspending brand 200, Portland cement Voskresen ce 400 plant 400, Pozzolanova additive - Tripoli of the Brno deposit, ground to 4200 points of industrial glass of Vasilevsky glass, crushed The chemical composition of the components used,%: the battle of the technical glass of the system 6b, 8 SiO2; 2.5 3, § 8.4 CaO; 0.8 MDO; 14.7 (Na2O + 1.2 ppb; Brth throne 79.5 SiO-; 7.1 3.1 4.1 CaO; 1.7 MdO; 4.3 ppp Poluchsht The resulting components are prepared with a 1: 3 composition solution, Strength tests of the solutions are carried out at 28 days of Hci bead samples according to GOST 310. 4-76. The softening factor is determined according to OST 21-29- 77. Examples of compositions in the live and the results of physico-mechanical tests are given in the table.
Известное -в жущее 60 26 14Famous - real 60 26 14
20/620/6
6,06.0
0,690,69
31062192«31062192 "
Как видно из таблицы, повышение Использование в составе в жущего счпрочности при сжатии и изгибе сое-ходов стекольных производств в виде мотавл ет до 25%, повышение водостой-лотого стекла позвол ет снизить долюAs can be seen from the table, an increase in the use of a glass production in the form of a tensile strength in compression and bending of co-moves in the form of crankshafts up to 25%, an increase in water-resistant glass reduces the share
кости по коэффициенту разм гчени портландцемента в составе в жущ оbones according to the softening coefficient of portland cement in composition
до 20%.и тем самым снизить стоимость в жущего.up to 20%. and thereby reduce the cost per person.
Claims (1)