SU1024806A1 - Method of determination of two body adherence - Google Patents
Method of determination of two body adherence Download PDFInfo
- Publication number
- SU1024806A1 SU1024806A1 SU823407795A SU3407795A SU1024806A1 SU 1024806 A1 SU1024806 A1 SU 1024806A1 SU 823407795 A SU823407795 A SU 823407795A SU 3407795 A SU3407795 A SU 3407795A SU 1024806 A1 SU1024806 A1 SU 1024806A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- bodies
- indenter
- adhesion strength
- compliant
- rigid
- Prior art date
Description
Изобретение относитс к исследова нию прочностных свойств материалов, а именно к способам определени проч ности сцеплени двух телThe invention relates to the study of the strength properties of materials, and in particular to methods for determining the adhesion strength of two bodies.
Известен способ определени прочности сцеплени двух тел, по которому производ т нагружение этих тел сдвигом до разрушени соединени по поверхности сцеплени . О прочности сцеплени суд т по величине усили , вызывающего разрушение соединени {.l 0днако способ вл етс разрушающим , так как нарушаетс сплошность соединени , и тела, наход щиес в сцеплении, раздел ютс .There is a known method for determining the adhesion strength of two bodies, which is used to shear these bodies until the joint breaks along the adhesion surface. The strength of adhesion is judged by the magnitude of the force that causes the destruction of the joint. The method, however, is destructive, since the integrity of the joint is broken, and the bodies in the clutch are separated.
Наиболее близким к изобретению по технической сущности и достигаемому результату вл етс способ определени ПРОЧНОСТИ сцеплени двух тел, заключающийс а том, что в границу раздела этих тел вдавливают индентор , измер ют усилие Р вдавливани и параметры трещинообразовани и по результатам измерений суд т о прочности сцеплени- . В качестве параметра трещинообразовани регистрируют размер отпечатка индентора перпендикул рно границе раздела тел 2.The closest to the invention in technical essence and the achieved result is a method for determining the strength of adhesion of two bodies, which consists in the fact that an indenter is pressed into the interface between these bodies, the indentation force P and the parameters of cracking are measured and . As a parameter of cracking, the size of the indenter footprint is recorded perpendicular to the interface of the bodies 2.
Недостатком известного способа вл етс невысока точность при определении прочности сцеплени жесткого И податливого тел с разной прочностью , поскольку граничные трещины в жестком и податливом телах различны по величине, а глубина внедрени индентора . в границу- раздела определ етс твердостью жесткого тела.The disadvantage of this method is the low accuracy in determining the adhesion strength of rigid And malleable bodies with different strengths, since the boundary cracks in rigid and malleable bodies vary in size, and the depth of insertion of the indenter. the boundary-section is determined by the hardness of the rigid body.
Целью.изобретени вл етс повышение точности при определении прочноети сцеплени жесткого и податливого тел с разной прочностью.The purpose of the invention is to improve the accuracy in determining the bond strength of a rigid and compliant body with different strengths.
Указанна цель достигаетс тем, что согласно способу определени прочности сцеплени двух тел, заключающемус в том, что в границу раздела этих тел вдавливают индентор, измер ют усилие Ef вдавливани и параметры трещинообразовани и по результатам измерений суд т о прочности сцеплени , вдавливают индентор в податливое тело с усилием Р, обеспечивающим проникновение индентора на глубине проникновени индентора в податливое тело при вдавливании его в раздела тел, в качестве параметров This goal is achieved in that according to the method of determining the adhesion strength of two bodies, which consists in that the indenter is pressed into the interface between these bodies, the indentation force Ef and the cracking parameters are measured and the adhesion strength is measured according to measurement results, the indenter is pressed into the compliant body with an effort P ensuring the penetration of the indenter at the depth of penetration of the indenter into the compliant body when it is pressed into the body section, as parameters
трещинообразовани измер юу вдоль границы раздела длину А следа трещины в жестком теле и длину А2 следа трещины в податливом теле, а прочность сцеплени рассчитывают пр формуле р рthe crack formation measured along the border of the length A of the crack in a rigid body and the length A2 of the crack in a supple body, and the adhesion strength is calculated using the formula
р . ..Д. + -. - А А .R . ..D. + -. - And a.
На фиг. 1 изображена схема вдавлй FIG. 1 shows the diagram
0 вани индентора в границу раздела Тел; на фиг. 2 - отпечаток индентора на границе раздела. ,0 vanilla indenter at the Tel-interface; in fig. 2 - imprint of the indenter at the interface. ,
Способ осуществл ют следующим образом .The method is carried out as follows.
5 В границу 1 раздела жесткого те- j ла 2 и податливого тела -3 усилием Р вдавливают-инДентор t. При этом отпечаток 5 в твердом теле и отпеча- fOK 6 в податливом теле имеют различные размеры. Это св зано с различной жесткостью тел, а также с естественным рельефом подготовленной поверхности тел: жесткое тело обычно выступает (имеет порог) над податливым телом (фиг. 1). На полученном отпечатке измер ют вдоль границы раздела длину А, следа трещийы в жестком теле, длину следа трещины в податливом теле и глубину h проникновени индентора в податливое тело. При использовании пирамидального индентора, отпечаток дл которого в качестве примера приведен на фиг. 2, достаточно вместо глубины h измерить размер d отпечатка перпендикул рно границе раздела.5 Into the boundary 1 of the rigid body j and the compliant body -3 by the force P is pressed-inDentor t. At the same time, imprint 5 in a solid body and seal-fOK 6 in a compliant body have different sizes. This is due to the different stiffness of the bodies, as well as to the natural relief of the prepared surface of the bodies: the rigid body usually protrudes (has a threshold) over the compliant body (Fig. 1). On the resulting print, the length A, the tracks cracked in the rigid body, the tracks length of the cracks in the compliant body and the depth h of the indenter penetration into the compliant body are measured along the interface. When using a pyramidal indenter, the imprint for which is shown as an example in FIG. 2, it is sufficient to measure, instead of the depth h, the size d of the print perpendicular to the interface.
Затем индентор вдавливают в податливое тело с усилием, обеспечивающим проникновение индентора на глубину h при этом измер ют это усилие P/j..Then the indenter is pushed into the pliable body with a force that ensures the penetration of the indenter to a depth h and this force P / j is measured.
По результатам измерений рассчитывают прочность сцеплени двух тел по формулеAccording to the measurement results, the adhesion strength of two bodies is calculated by the formula
Р , R ,
ПP
А - А,2..A - A, 2 ..
ИсЛользование изобретени позвол ет повысить точность при определении прочности сцеплени жесткого и податливого тел с разной прочностью за счет учета нагрузки, которую воспринимают податливое тело при вдавливании , индентора в границу раздела, и регистрации параметров трещинообразований в ка))дом из соединенных тел.The use of the invention improves the accuracy in determining the adhesion strength of a rigid and pliable body with different strengths by taking into account the load that the pliable body perceives during indentation, the indenter in the interface, and the registration of the parameters of cracking in k) from the connected bodies.
Claims (1)