SK5393Y1 - Mixture for building purposes - Google Patents
Mixture for building purposes Download PDFInfo
- Publication number
- SK5393Y1 SK5393Y1 SK5048-2009U SK50482009U SK5393Y1 SK 5393 Y1 SK5393 Y1 SK 5393Y1 SK 50482009 U SK50482009 U SK 50482009U SK 5393 Y1 SK5393 Y1 SK 5393Y1
- Authority
- SK
- Slovakia
- Prior art keywords
- weight
- cement
- pulp
- composition
- recycled plastic
- Prior art date
Abstract
Description
Technické riešenie sa týka zmesí na stavebné účely obsahujúcich spojivo a plnivo, pričom ako plnivo obsahuje zmes až 85 % hmotn. častíc recyklovanej plastovej drviny s veľkosťou až 100 mm.The invention relates to building compositions comprising a binder and a filler, wherein the mixture contains as a filler up to 85 wt. particles of recycled plastic crumb up to 100 mm in size.
Doterajší stav technikyBACKGROUND OF THE INVENTION
Zo stavebníctva je veľmi dobre známe množstvo stavebných hmôt a spolu s tým aj nepreberné množstvo výrobkov, slúžiacich na rozmanité účely.The construction industry is well known for a variety of building materials and with it a plethora of products serving a variety of purposes.
Základnými spojivami na stavebné účely sú maltoviny, ku ktorým patrí cement, vápno a iné, ale k spojivám sa radia aj lepidlá, ako sú napr. cementové stavebné lepidlá a spojivové primesi, napríklad tmely a peny. Spoločne s plnivami a vodou potom konkrétny druh maltovinového spojiva vytvára betón, maltu či umelý kameň, ktoré sú formované do konkrétnych výrobkov.The basic binders for construction purposes are mortars, which include cement, lime and others, but adhesives such as e.g. cementitious building adhesives and binders, such as cements and foams. Together with fillers and water, a particular type of mortar binder forms concrete, mortar or artificial stone, which are formed into specific products.
Týmito výrobkami sú podľa účelu použitia rôzne druhy stavebných dielcov, ako sú montážne a prefabrikované dielce, panely, stenové prefabrikáty, cestné dielce, dielce protihlukových stien, preklady, a tak pod., ale aj tvárnice, tehly, priečkovky a tvarovky, strešné krytiny, dlažby, obklady, obrubníky, kanalizačné skruže, odtokové žľaby a rúry a mnoho ďalších výrobkov.These products are, depending on the purpose of use, various types of building components, such as assembly and prefabricated components, panels, wall prefabricated elements, road components, sound insulation panels, lintels and the like, but also blocks, bricks, partition walls and fittings, roofing, paving, tiling, curbs, sewer rings, drainage troughs and pipes and many other products.
Doteraz je v stavebníctve ako plnivo používaný tradične najmä prírodný drvený kameň, kamenivo, štrk a piesok s rôznou veľkosťou častíc. Dostupnosť týchto materiálov v prírode je stále ťažšia, teda ich cena neustále stúpa, Čím narastá cena výsledného výrobku.Up to now, naturally crushed stone, aggregates, gravel and sand of various particle sizes have been traditionally used as a filler in the construction industry. The availability of these materials in nature is increasingly difficult, so their price is constantly increasing, thus increasing the price of the final product.
Nezanedbateľným znakom týchto výrobkov je však vďaka týmto materiálom aj ich pomerne vysoká hmotnosť. Zo stavu techniky je známe, že niektoré stavebné hmoty na báze ílu a cementu obsahujú ako vyľahčujúce plnivo napr. priemyselne vyrábané guľôčky z polystyrénu či ľahčeného polystyrénu alebo podobného vyľahčujúceho materiálu. Aj tieto priemyselne vyrábané vyľahčujúce materiály sú však stále drahšie.However, due to these materials, their relatively high weight is a significant feature of these products. It is known in the art that some clay and cement-based building materials contain e.g. industrially manufactured balls of polystyrene or expanded polystyrene or similar lightweight material. However, these industrially produced lightening materials are also increasingly expensive.
Na druhej strane, ako dôsledok ľudskej činnosti, dochádza k produkcii mnohých odpadových materiálov, ktoré sa pre človeka a životné prostredie stávajú stále viac zaťažujúcimi, avšak z dôvodov nutných ďalších nákladov potrebných na ich využitie sa ďalej takmer nespracovávajú a hromadia sa, aj napriek stále sa zvyšujúcim poplatkom za ich uloženie, na skládkach. Jedným z týchto odpadových materiálov je aj odpadový plast, zahŕňajúci rôzne termoplasty, tvorené z veľkej časti rôznymi použitými obalmi potravín a termoplastickým odpadom z priemyslu, avšak aj odpadové plasty na báze termosetov, najmä s obsahom ďalších zložiek, ako sú napr. sklenené vlákna, ktorým doteraz nebola venovaná dostatočná pozornosť.On the other hand, as a result of human activity, many waste materials are produced, which are becoming increasingly burdensome for humans and the environment, but due to the additional costs required for their use, they are almost no longer processed and accumulated, despite increasing the fee for their storage in landfills. One of these waste materials is also waste plastic, comprising various thermoplastics, consisting largely of the different food packaging used and thermoplastic waste from industry, but also waste plastics based on thermosetting, especially containing other ingredients such as e.g. glass fibers which have not been given enough attention so far.
Napriek tomu sa nielen vo svete, ale aj v Českej republike prejavuje určitá snaha o recykláciu plastov. Doteraz sa ale len veľmi malá časť tohto objemu odpadových plastov recykluje, a to len za určitých obmedzujúcich podmienok.Nevertheless, not only in the world, but also in the Czech Republic, there is some effort to recycle plastics. To date, however, only a very small proportion of this volume of waste plastics is recycled, and only under certain restrictive conditions.
Vzhľadom na vyššie uvedené problémy tu existuje stále veľká potreba využiť a v čo najväčšej miere jednoduchým spôsobom zužitkovať uvedené skládkové odpadové plasty, a to aj plasty na báze termosetov, ktoré môžu obsahovať aj ďalšie anorganické či organické zložky.In view of the above problems, there is still a great need to utilize and utilize as widely as possible waste dump plastics, including thermosetting plastics, which may also contain other inorganic or organic components.
Podstata technického riešeniaThe essence of the technical solution
Vyššie uvedené nedostatky aspoň čiastočne odstraňuje zmes na stavebné účely podľa tohto technického riešenia, obsahujúca okrem bežného spojiva ako plnivo plast na báze termosetov so širokým koncentračným obsahom anorganickej zložky, ako sú sklené vlákna, keď po prípadnej úprave veľkosti častíc, t. j. napr. po konkrétnom rozdrvení, mletí, či rozstrúhaní alebo lisovaní plastu, je možné recyklovaňou plastovou drvinou nahradiť v stavebnej zmesi drahé, najmä prírodné plnivá, a tým zlacniť, a zároveň tiež znížiť hmotnosť výsledných stavebných výrobkov.The aforementioned drawbacks are at least partially overcome by the construction composition according to the present invention, comprising, in addition to the conventional binder, a thermosetting plastics material with a broad concentration of inorganic component such as glass fibers, as a filler, if after adjusting the particle size. j. e.g. after the concrete crushing, grinding, shredding or molding of the plastic, it is possible to replace the expensive, especially natural fillers, in the construction mixture with recycled plastic crumb, and thus to reduce the weight of the resulting construction products.
Podstatou tohto technického riešenia je zmes na stavebné účely, najmä na výrobu rôznych stavebných dielcov, ktorá zahŕňa spojivo a plnivo, pričom ako plnivo zmes obsahuje až 85 % hmotn. častíc recyklovanej plastovej drviny, s veľkosťou častíc drviny až 100 mm, ktorého podstata spočíva v tom, že recyklovanou plastovou drvinou je drvina na báze termosetu obsahujúca až 60 % hmotn. sklených vláken, vztiahnuté na hmotnosť plastovej drviny.The essence of this technical solution is a mixture for building purposes, in particular for the production of various building components, which comprises a binder and a filler, the mixture containing up to 85 wt. particles of recycled plastic pulp, with a particle size of up to 100 mm, characterized in that the recycled plastic pulp is a thermoset based pulp containing up to 60 wt. glass fibers, based on the weight of the plastic crushed material.
Ako v opise prihlášky technického riešenia tak v nárokoch na ochranu sú koncentrácie všetkých zložiek vztiahnuté na celkovú hmotnosť zmesi, ak nie je uvedené mak.In both the specification and the claims, the concentrations of all components are based on the total weight of the composition, unless poppy is mentioned.
Cieľom tohto technického riešenia je využiť pre plnivo výhodné fyzikálno-chemické vlastnosti konkrétneho recyklovaného termosetového plastu, ktorý sám o sebe obsahuje vhodnú prísadu sklených vláken, a zvyšuje tak konečnú úžitkovú hodnotu konkrétneho stavebného výrobku.The object of the present invention is to utilize, for the filler, the advantageous physicochemical properties of a particular recycled thermosetting plastic which itself contains a suitable glass fiber additive and thus increases the end-use value of a particular construction product.
Predkladaným technickým riešením sa rieši problém plastového odpadu a v rámci rccyklácie je možné tento odpad - konkrétne vyššie uvedenú recyklovanú plastovú drvinu veľmi dobre využiť ako základné plni2The present technical solution solves the problem of plastic waste and in the context of recycling it is possible to use this waste - namely the above recycled plastic pulp - very well as basic fillers2.
SK 5393 Υ1 vo pri výrobe stavebných hmôt a nahradiť tak tradičnú drahú prírodnú surovinu, akou sú najmä prírodný drvený kameň, kamenivo, štrk alebo piesok.SK 5393 Υ1 in the manufacture of building materials and thus replace a traditional expensive natural raw material, such as in particular natural crushed stone, aggregates, gravel or sand.
Plastom na báze termosetu je výhodne nenasýtená polyesterová živica.The thermosetting plastic is preferably an unsaturated polyester resin.
Uvedenú recyklovanú plastovú drvinu je možné miešať so spojivom, konkrétne s cementom, vápnom, cementovými alebo inými stavebnými lepidlami, ostatnými maltovinovými spojivami okrem sadry či spojivovými prímesami, podľa druhu požadovanej výslednej zmesi alebo výrobku.Said recycled plastic crumb may be mixed with a binder, in particular with cement, lime, cement or other building adhesives, other mortar binders except gypsum or binder admixtures, depending on the type of final mixture or product desired.
Vápnom môže byť výhodne vzdušné alebo hydraulické vápno.The lime may preferably be air lime or hydraulic lime.
Cementom sú výhodne bežné druhy cementov, ako je portlandský cement alebo struskoportlandský cement.The cement is preferably a conventional type of cement, such as Portland cement or slag-portland cement.
Typickým maltovinovým spojivom je výhodne výrobok firmy Lafarge Cement s označením Multibat, alebo Multibat Plus pozostávajúci z portlandského slinku, minerálnych prísad a špeciálnych prímesí.A typical mortar binder is preferably a Lafarge Cement product designated Multibat or Multibat Plus consisting of Portland clinker, mineral additives and special additives.
Spojivovými prímesami sú výhodne bežne v stavebníctve používané tmely alebo peny.The binder ingredients are preferably the commonly used cements or foams in the construction industry.
V závislosti od druhu požadovanej stavebnej hmoty a požadovaného druhu stavebného výrobku je volená rôzna granulometria a hmotnostné zastúpenie tejto recyklovanej plastovej drviny v uvedenej zmesi.Depending on the type of building material required and the desired type of construction product, different granulometry and the proportion by weight of the recycled plastic material in the mixture are chosen.
Vo výhodnom uskutočnení je veľkosť častíc vyššie uvedenej recyklovanej plastovej drviny upravená drvením, mletím, strúhaním, prípadne lisovaním.In a preferred embodiment, the particle size of the aforementioned recycled plastic pulp is adjusted by crushing, grinding, grating or pressing.
Vďaka širokému percentuálnemu zastúpeniu sklených vláken v recyklovanej termosetovej plastovej drvine, ktorou je vo výhodnom uskutočnení recyklovaná drvina z polyesterovej živice, sa pri jej použití ako plniva v zmesi pri konkrétnych výrobkoch zvýšila mechanická odolnosť ako je húževnatosť, oderuvzdomosť a odolnosť voči nárazu či otrasu, a čiastočne aj odolnosť voči ohybu. V dôsledku nižšej mernej hmotnosti tejto drviny sa vďaka tomuto plnivu znížila aj hustota stavebnej zmesi, a tým aj samotná hmotnosť následne vyrobených výrobkov oproti výrobkom vyrobeným podľa doterajšieho stavu techniky. Zmes je odolná voči účinkom mrazu a chemických, najmä rozmrazovacích látok.Due to the broad percentage of glass fibers in the recycled thermosetting plastic pulp, which is preferably recycled polyester resin pulp, when used as a filler in a mixture for specific products, mechanical resistance such as toughness, abrasion resistance and impact or shock resistance have been increased, and partly also resistance to bending. Due to the lower specific gravity of the pulp, the filler density and hence the weight of the products produced in comparison with the prior art products have also been reduced by this filler. The mixture is resistant to the effects of frost and chemical, in particular deicing agents.
Spolu so spojivami je k uvedenej recyklovanej plastovej drvine ďalej výhodné pridať činidlá proti U V žiareniu a/alebo činidlá proti kyslým dažďom a/alebo pigmenty a pod.In addition to the binders, it is furthermore advantageous to add to the recycled plastic crumb anti-UV agents and / or acid rain agents and / or pigments and the like.
Konkrétne sú pri výrobe suchých betónových zmesí výhodne použité ako častice plniva recyklované plastové drviny na báze polyesterovej živice s obsahom sklených vláken až do 60 % hmotn., vztiahnuté na hmotnosť plastovej drviny, s väčšou granulometriou, výhodne s veľkosťou častíc 10 až 100 mm, v množstve 15 až 75 % hmotn., pričom 25 až 84,5 % hmotn. tvorí cement. Cementom je výhodne portlandský cement.In particular, in the production of dry concrete mixtures, recycled polyester resin-based plastic crumbs having a glass fiber content of up to 60% by weight, based on the weight of the plastic crumb, with a larger granulometry, preferably with a particle size of 10 to 100 mm, are preferably used as filler particles. 15 to 75 wt.%, with 25 to 84.5 wt. forms cement. The cement is preferably Portland cement.
Zmes podľa technického riešenia výhodne obsahuje 3 až 4 hmotn. diely častíc uvedenej recyklovanej plastovej drviny obsahom sklených vláken 5 až 30 % hmotn., vztiahnuté na hmotnosť plastovej drviny, s veľkosťou častíc 5 až 10 mm a 3 hmotn. diely maltovinového spojiva. Táto zmes sa výhodne použije ako suchá maltová zmes.The composition according to the invention preferably contains 3 to 4 wt. parts of the particles of said recycled plastic pulp having a glass fiber content of 5 to 30 wt.%, based on the weight of the plastic pulp, with a particle size of 5 to 10 mm and 3 wt. parts of mortar binder. This mixture is preferably used as a dry mortar mixture.
Výhodným riešením je tiež zmes, ktorá obsahuje 4 hmotn. diely recyklovanej plastovej drviny s obsahom sklených vláken od 20 do 50 % hmotn., vztiahnuté na hmotnosť plastovej drviny, s veľkosťou častíc 20 až 50 mm a 1 hmotn. diel cementu, ktorá je vhodná pre následnú výrobu tehál a tvárnic. Cementom je výhodne struskoportlandský cement.A preferred solution is also a composition comprising 4 wt. parts of recycled plastic pulp having a glass fiber content of 20 to 50% by weight, based on the weight of the plastic pulp, with a particle size of 20 to 50 mm and 1% by weight parts of cement, which is suitable for the subsequent production of bricks and blocks. The cement is preferably slag-portland cement.
Ďalším technickým riešením je zmes, ktorá výhodne obsahuje 60 až 75 % hmotn. uvedenej recyklovanej plastovej drviny s veľkosťou častíc max. 2 mm a 25 až 39,5 % hmotn. vápna.Another technical solution is a mixture which preferably contains 60 to 75 wt. of said recycled plastic pulp with a particle size of max. 2 mm and 25 to 39.5 wt. lime.
Táto zmes obsahuje veľmi jemné častice uvedenej recyklovanej plastovej drviny, ktoré boli preosiate na veľkosť častíc do max. 2 mm a spolu s vyššie uvedeným množstvom vápna bola táto zmes výhodne použitá ako suchá štuková zmes.This mixture contains very fine particles of said recycled plastic pulp which have been sieved to a particle size of max. 2 mm, and together with the above amount of lime, this mixture was preferably used as a dry stucco mixture.
Výhodne je možné ďalej k vyššie uvedeným zmesiam pridať až do 0,4 % hmotn. činidla proti U V žiareniu a/alebo činidla proti kyslým dažďom, a/alebo až do 0,05 % hmotn. pigmentu.Advantageously, up to 0.4 wt. % anti-UV agents and / or acid rain agents, and / or up to 0.05 wt. pigment.
Podľa technického riešenia je tiež možné vyrobiť konkrétne výrobky, najmä stavebné dielce, predovšetkým v tvare tehál, tvárnic, montážne a prefabrikované dielce, ako sú panely, stenové prefabrikáty, preklady alebo stĺpy, dielce protihlukových stien, dlažby, obklady, strešné krytiny, priečkovky a tvarovky, kanalizačné skruže, odtokové žľaby a rúry, a izolačné dosky.According to the technical solution it is also possible to produce specific products, in particular building components, in particular in the form of bricks, blocks, assembly and prefabricated parts such as panels, wall prefabricated elements, lintels or columns, noise barriers, paving, tiles, roofing, partition walls and fittings, sewage rings, drainage channels and pipes, and insulating boards.
Technické riešenie sa konkrétne výhodne týka stavebného betónového dielca, ako je panel, stenový prefabrikát, cestný dielec, preklad, stĺp, ktorý je podľa technického riešenia výhodne vyrobený zo zmesi obsahujúcej 3 až 5 hmotn. dielov recyklovanej plastovej drviny, 1 hmotn. diel cementu a až 1 hmotn. diel zámesovej vody.More particularly, the technical solution relates to a structural concrete part, such as a panel, a prefabricated wall, a road element, a lintel, a column, which according to the technical solution is preferably made of a mixture containing 3 to 5 wt. parts by weight of recycled plastic pulp, 1 wt. parts of cement and up to 1 wt. water.
Ak je požadovaný stavebný dielec v tvare tvárnice alebo tehly, je podľa technického riešenia výhodne vyrobený zo zmesi, ktorá obsahuje 3 až 5 hmotn. dielov recyklovanej plastovej drviny s veľkosťou častíc 20 až 50 mm, 1 hmotn. diel cementu a až 1 hmotn. diel zámesovej vody.If the desired component is in the form of a block or a brick, it is preferably made from a mixture containing 3 to 5 wt. parts by weight of recycled plastic material with a particle size of 20 to 50 mm; parts of cement and up to 1 wt. water.
Ďalším výhodným variantom podľa technického riešenia je strešná krytina, kanalizačná skruž, rúra alebo odtokový žľab, ktoré sú vyrobené zo zmesi obsahujúcej uvedenú recyklovanú plastovú drvinu obsahujúcu 15 až 40 % hmotn. sklených vláken, vztiahnuté na hmotnosť drviny.Another preferred variant according to the invention is a roof covering, sewer ring, pipe or drain, which is made of a mixture comprising said recycled plastic material containing 15 to 40 wt. glass fibers, based on the weight of the pulp.
SK 5393 Υ1SK 5393 Υ1
Výhodnou modifikáciou riešenia je obklad vyrobený zo zmesi obsahujúcej 50 až 65 % hmotn. recyklovanej plastovej drviny s obsahom sklených vláken od 15 až 40 % hmotn., vztiahnuté na hmotnosť plastovej drviny, s veľkosťou častíc 1 až 5 mm, 24,5 až 39,6 % hmotn. cementu a do 10 % hmotn. zámesovej vody.A preferred modification of the solution is a cladding made from a mixture containing 50 to 65 wt. recycled plastic pulp having a glass fiber content of 15 to 40% by weight, based on the weight of the plastic pulp, with a particle size of 1 to 5 mm, 24.5 to 39.6% by weight. % cement and up to 10 wt. mixed water.
Ešte ďalším variantom riešenia je izolačná lisovaná, tvarovaná doska zo zmesi obsahujúcej 65 až 80 % hmotn. recyklovanej plastovej drviny, s veľkosťou častíc 10 až 100 mm, 9,5 až 24,5 hmotn. % cementu a do 10 hmotn. % zámesovej vody.Yet another variant of the solution is an insulated molded board of a mixture comprising 65 to 80 wt. % recycled plastic pulp, with a particle size of 10 to 100 mm, 9.5 to 24.5 wt. % cement and up to 10 wt. % mixing water.
Výhodne môžu vyššie uvedené konkrétne výrobky obsahovať až do 0,4 % hmotn. činidlá proti UV žiareniu a/alebo činidlá proti kyslým dažďom a/alebo až do 0,05 % hmotn. pigmentu.Advantageously, the aforementioned particular products may contain up to 0.4 wt. % anti-UV agents and / or acid rain agents and / or up to 0.05 wt. pigment.
Príklady uskutočneniaEXAMPLES
Príklad 1Example 1
Recyklovaná plastová drvina v množstve 60 % hmotn., na báze polyesterovej živice s obsahom až 60 % hmotn. sklených vláken, vztiahnuté na hmotnosť plastovej drviny, s veľkosťou častíc 10 až 100 mm bola dokonale premiešaná so 40 % hmotn. portlandského cementu. Táto suchá zmes je vhodná na použitie pre betónovú zrne s.Recycled plastic crumb in an amount of 60% by weight, based on polyester resin containing up to 60% by weight. % of glass fibers, based on the weight of plastic pulp, with a particle size of 10 to 100 mm, was intimately mixed with 40 wt. Portland cement. This dry mix is suitable for use with concrete grains with.
Príklad 2Example 2
Za sucha boli premiešané veľmi starostlivo 4 hmotn. diely recyklovanej plastovej drviny na báze polyesterovej živice, ktorá obsahovala 5 až 30 % hmotn. sklených vláken, vztiahnuté na hmotnosť plastovej drviny, s veľkosťou častíc 5 až 10 mm, s 3 hmotn. dielmi maltovinového spojiva, konkrétne maltovinové spojivo zn. Multibat (firmy Lafarge Cement). Získala sa vhodná suchá maltová zmes.When dry, 4 wt. % parts of recycled polyester resin-based plastic pulp containing 5 to 30 wt. of glass fibers, based on the weight of plastic crush, with a particle size of 5 to 10 mm, with 3 wt. parts of a mortar binder, in particular a mortar binder of ref. Multibat (Lafarge Cement). A suitable dry mortar mixture was obtained.
Príklad 4Example 4
Recyklovaná plastová drvina na báze polyesterovej živice s obsahom až 60 % hmotn. sklených vláken, vztiahnuté na hmotnosť plastovej drviny, bola podrobená preosievaniu a následne boli použité do zmesi veľmi jemné prachové častice tejto drviny s veľkosťou maximálne 2 mm v množstve 70 % hmotn., potom bola drvina dokonale premiešaná s 30 % hmotn. hydraulického vápna. Uvedená zmes je vhodná ako štuková zmes.Recycled plastic resin based on polyester resin containing up to 60 wt. The glass fibers, based on the weight of the plastic pulp, were subjected to screening, and then very fine dust particles of this pulp size of not more than 2 mm in an amount of 70% by weight were used, then the pulp was thoroughly mixed with 30%. hydraulic lime. Said mixture is suitable as a stucco mixture.
Príklad 4 hmotn. diely recyklovanej plastovej drviny na báze polyesterovej živice s obsahom 20 až 50 % hmotn. sklených vláken, vztiahnuté na hmotnosť plastovej drviny, s veľkosťou častíc 20 až 50 mm, boli dokonale premiešané s 1 hmotn. dielom struskoportlandského cementu a zvyšok bol tvorený zámesovou vodou, ktorá predstavovala do 100 % hmotn. zmesi. Zmes bola potom vnesená do foriem príslušného tvaru, t. j. tvaru tvárnic a tehál a nechala sa stuhnúť a stvrdnúť.Example 4 wt. % parts of recycled plastic resin based on polyester resin containing 20 to 50 wt. The glass fibers, based on the weight of plastic pulp, with a particle size of 20 to 50 mm, were intimately mixed with 1 wt. % of the slag-portland cement and the remainder consisted of blending water, which represented up to 100 wt. mixture. The mixture was then introduced into molds of appropriate shape, i. j. shaped blocks and bricks and allowed to solidify and harden.
Príklad 5 diely recyklovanej plastovej drviny na báze polyesterovej živice s obsahom až 60 % hmotn. sklených vláken, vztiahnuté na hmotnosť plastovej drviny, boli veľmi starostlivo premiešané s 1 dielom portlandského cementu a zvyšok predstavovala zámesová voda. Zmes bola potom vnesená do foriem príslušného tvaru, t. j. tvaru stenového prefabrikátu, panelu, prekladu alebo stĺpu a nechala sa stuhnúť a stvrdnúť.EXAMPLE 5 parts of recycled polyester resin based crumb containing up to 60 wt. The glass fibers, based on the weight of the plastic crumb, were mixed very carefully with 1 part of Portland cement and the remainder was mixed water. The mixture was then introduced into molds of appropriate shape, i. j. in the form of a prefabricated wall, panel, lintel or column and allowed to solidify and harden.
Podľa skúšok podľa ČSN 72 2602, ČSN 72 2603, a ČSN 72 2605 posudzujúcej pevnosti v ťahu za ohybu a pevnosti betónu v tlaku (tabuľky 1 a 2), boli u tejto stvrdnutej zmesi zistené nasledujúce hodnoty:According to the tests according to ČSN 72 2602, ČSN 72 2603, and ČSN 72 2605 assessing the flexural tensile strength and concrete compressive strength (Tables 1 and 2), the following values were found for this hardened mixture:
Tabuľka 1Table 1
Tabuľka 2Table 2
Podľa skúšok podľa ČSN 73 1326, metóda A posudzujúca odolnosť povrchu betónu proti pôsobeniu vody a chemických rozmrazovacích látok (tabuľka 3), boli u tejto stvrdnutej zmesi zistené nasledujúce hodnoty:According to tests according to ČSN 73 1326, method A assessing the resistance of the concrete surface to water and chemical de-icing agents (Table 3), the following values were found for this hardened mixture:
SK 5393 Υ1SK 5393 Υ1
Tabuľka 3Table 3
*Predpísaná hodnota odolnosti podľa ČSN 73 6131 (betónové dlažby a dielce) je maximálne 1000 g/m2 po 100 cykloch metódou A.* The prescribed resistance value according to ČSN 73 6131 (concrete paving and components) is maximum 1000 g / m 2 after 100 cycles by method A.
Príklad 6Example 6
Recyklovaná plastová drvina (55 % hmotn.) na báze polyesterovej živice s obsahom 15 až 40 % hmotn. sklených vláken, vztiahnuté na hmotnosť plastovej drviny, s veľkosťou častíc 1 až 5 mm bola veľmi starostlivo premiešaná s 34,6 % hmotn. cementu a boli pridané činidlá proti UV žiareniu a/alebo činidlá proti kyslým dažďom a pigment v celkovom množstve 0,4 % hmotn. Následne bola pridaná zámesová voda v množstve 10 % hmotn. Zmes bola potom vnesená do foriem príslušného tvaru, t. j. tvaru obkladu, a nechala sa stuhnúť.Recycled plastic crumb (55 wt.%) Based on polyester resin containing 15 to 40 wt. % of glass fibers, based on the weight of plastic pulp, with a particle size of 1 to 5 mm, were mixed very carefully with 34.6 wt. % of the cement, and UV agents and / or acid rain agents and pigment were added in a total amount of 0.4 wt. Subsequently, the mixing water was added in an amount of 10% by weight. The mixture was then introduced into molds of appropriate shape, i. j. shaped tiles, and allowed to solidify.
Príklad 5Example 5
Recyklovaná plastová drvina (65 % hmotn.) s obsahom až 60 % hmotn. sklených vláken, vztiahnuté na hmotnosť plastovej drviny, s veľkosťou častíc 10 až 70 mm bola veľmi starostlivo premiešaná s 25 % hmotn. portlandského cementu a potom s 10 % hmotn. zámesovej vody. Zmes bola následne podrobená lisovaniu, pričom bol získaný výsledný produkt - tvarovaná izolačná doska.Recycled plastic crumb (65 wt.%) Containing up to 60 wt. % of glass fibers, based on the weight of plastic pulp, with a particle size of 10 to 70 mm, was mixed very carefully with 25 wt. % Portland cement and then with 10 wt. mixed water. The mixture was then subjected to compression to give the final product, a shaped insulating board.
Príklad 8 % hmotn. recyklovanej plastovej drviny na báze polyesterovej živice s obsahom 55 % hmotn. sklených vláken, vztiahnuté na hmotnosť plastovej drviny, s veľkosťou častíc 5 až 10 mm bolo veľmi starostlivo premiešané s 23,95 % hmotn. portlandského cementu, s 0,05 % hmotn. činidla proti UV žiareniu a proti vplyvu kyslých dažďov. Pridalo sa 8 % hmotn. zámesovej vody. Zmes bola potom vnesená do foriem príslušného tvaru, t. j. tvaru stavebných dielcov protihlukovej steny. Následne bolo uskutočnené vyarmovanie a zmes bola podrobená vibrolisovaniu a nechala sa stuhnúť a stvrdnúť.Example 8 wt. % recycled plastic resin based on polyester resin containing 55 wt. % of glass fibers, based on the weight of plastic crumb, with a particle size of 5 to 10 mm, was mixed very carefully with 23.95 wt. % Portland cement, with 0.05 wt. anti-UV and acid rain agents. 8 wt. mixed water. The mixture was then introduced into molds of appropriate shape, i. j. the shape of the soundproofing building components. Subsequently, sparging was carried out and the mixture was subjected to vibro-pressing and allowed to solidify and harden.
Príklad 9 % hmotn. recyklovanej plastovej drviny na báze polyesterovej živice s obsahom 60 % hmotn. sklených vláken, vztiahnuté na hmotnosť plastovej drviny, s veľkosťou častíc 5 až 15 mm bolo veľmi starostlivo premiešané s 30 % hmotn. portlandského cementu, a potom s 10 % hmotn. zámesovej vody. Zmes bola vnesená do foriem strateného bednenia a následne bola podrobená vibrolisovaniu a nechala sa stuhnúť a stvrdnúť.Example 9 wt. % recycled plastic resin based on polyester resin containing 60 wt. % of glass fibers, based on the weight of plastic pulp, with a particle size of 5 to 15 mm, was mixed very carefully with 30 wt. % Portland cement, and then with 10 wt. mixed water. The mixture was introduced into forms of lost formwork and was subsequently subjected to vibrolisation and allowed to solidify and harden.
Výsledné výrobky obsahujúce zatvrdnutú zmes majú vynikajúce tepelne izolačné vlastnosti, s hodnotou koeficientu Xokolo λ = 0,11.The resulting products containing the hardened mixture have excellent thermal insulating properties, with a coefficient of Xokolo λ = 0.11.
Priemyselná využiteľnosťIndustrial usability
Zmes podľa technického riešenia je možné použiť v stavebníctve na výrobu betónových zmesí, makových zmesí alebo štukových zmesí, ktoré je možné podľa účelu využiť na výrobu stavebných dielcov, napríklad v tvare tehál, tvárnic, betónových, montážnych a prefabrikovaných dielcov, ako sú panely, stenové prefabrikáty, preklady alebo stĺpy, dielce protihlukových stien, pre dlažby, obklady, priečkovky a tvarovky, kanalizačné skruže, odtokové žľaby a rúry, pre strešné krytiny rôznych tvarov a použitia, ďalej pre izolačné dosky a iné výrobky, kde tento recyklovaný odpadový plast je možné využiť ako plnohodnotnú náhradu za tradičnú surovinu - plnivo, ako sú štrky a piesky, a tak znižovať množstvo odpadového plastu zaťažujúceho skládkami prírodné prostredie.The composition according to the invention can be used in the construction industry for the production of concrete mixtures, poppy mixes or stucco mixtures, which can be used according to purpose for the production of building components, for example bricks, blocks, concrete, assembly and prefabricated parts such as panels, wall prefabricated elements, lintels or columns, soundproofing wall panels, for paving, tiling, partition walls and fittings, sewer rings, drainage troughs and pipes, for roof coverings of various shapes and applications, insulation boards and other products where this recycled waste plastic is possible use as a full substitute for traditional raw material - fillers such as gravel and sand - and thus reduce the amount of waste plastic burdening the natural environment with landfills.
Claims (16)