SK125397A3 - Composition for preventing the formation of inorganic scales in an aqueous system - Google Patents
Composition for preventing the formation of inorganic scales in an aqueous system Download PDFInfo
- Publication number
- SK125397A3 SK125397A3 SK1253-97A SK125397A SK125397A3 SK 125397 A3 SK125397 A3 SK 125397A3 SK 125397 A SK125397 A SK 125397A SK 125397 A3 SK125397 A3 SK 125397A3
- Authority
- SK
- Slovakia
- Prior art keywords
- composition
- polyphosphate
- coatings
- amount
- formation
- Prior art date
Abstract
Description
Doterajší stav technikyBACKGROUND OF THE INVENTION
Znečistenie povrchov môže byť vážnym ekonomickým problémom pri mnohých komerčných a priemyselných vodných procesoch. Toto znečistenie je zvyčajne spôsobené tvorením organických alebo anorganických materiálov na povrchu, ktorý je vo vodnom systéme. Zvlášť nepríjemné sú anorganické znečisteniny vo forme povlakov. K tvorbe povlaku dochádza ako dôsledok ukladania minerálnych zlúčenín prítomných vo vode používanej vo vodnom systéme. Pretože pri kontakte s vodou tvorí tvrdý, kameňu sa podobajúci povlak na povrchoch, ako sú steny potrubí, zásobníky, nádrže a ďalšie uzavreté prvky vo vodných priemyselných systémoch, tvorba povlakov môže spôsobiť vážne problémy pri práci vo vodných priemyselných systémoch. Tvorba povlaku je zvlášť problematická v tých geografických oblastiach, ktoré majú tvrdú vodu.Surface contamination can be a serious economic problem in many commercial and industrial water processes. This contamination is usually caused by the formation of organic or inorganic materials on the surface that is in the aqueous system. Inorganic contaminants in the form of coatings are particularly unpleasant. Coating occurs as a result of deposition of mineral compounds present in the water used in the aqueous system. Since contact with water forms a hard, stone-like coating on surfaces such as pipe walls, reservoirs, tanks and other enclosed elements in aqueous industrial systems, coating can cause serious problems when working in aqueous industrial systems. Coating is particularly problematic in those geographic areas that have hard water.
Medzi príklady anorganických znečistenín, ktoré sa môžu objavovať ako povlaky vo vodnom systéme, patrí síran bamatý, uhličitan vápenatý, síran vápenatý, fosforečnan vápenatý, šťavelan vápenatý a ďalšie anorganické soli kovov, ktoré sú dobre známe v oblasti techniky. Často sa ako povlak objavuje zmes niekoľkých znečisťujúcich materiálov.Examples of inorganic contaminants that may appear as coatings in an aqueous system include barium sulfate, calcium carbonate, calcium sulfate, calcium phosphate, calcium oxalate, and other inorganic metal salts well known in the art. Often a mixture of several contaminants appears as a coating.
Ak sa tvorba povlakov nereguluje, tvorba tohto materiálu môže interferovať s postupom operácií, môže znižovať účinnosť procesu, môže sa plytvať energiou a znižovať kvalita produktu. Výsledkom sú vážne ekonomické nevýhody. Napríklad vodné priemyselné systémy, ako sú papierne, papiernické stroje,naftové vrty a podobne, sa môžu stretávať s problémami, ktoré pochádzajú z ukladania anorganických povlakov. Uložené povlaky môžu upchať alebo zaniesť alebo inak znižovať tok vodných roztokov a/alebo suspenzií v potrubiach dodávajúcich vodu, v kondenzačných trubkách a na iných povrchoch súvisiacich s vodnými systémami.If coating is not regulated, the formation of this material may interfere with the operation process, may reduce process efficiency, may waste energy, and reduce product quality. This results in serious economic disadvantages. For example, aqueous industrial systems such as paper mills, paper machines, oil wells and the like may encounter problems arising from the deposition of inorganic coatings. The deposited coatings may clog or clog or otherwise reduce the flow of aqueous solutions and / or suspensions in water supply pipes, condensation tubes, and other surfaces associated with aqueous systems.
Je veľmi dobre známe, že ošetrenie vodného systému niektorými chemickými prísadami môže znižovať alebo zabraňovať tvorbe anorganických povlakov na povrchoch vodného priemyselného systému. V rôznych situáciách sa môžu používať rôzne prísady, podľa typu poťahu, ktorý spôsobuje problém, a tiež podľa stavov priemyselného systému, v ktorom dochádza k tvorbe povlakov. Pre tento účel sa môžu k vodnému systému pridávať napríklad niektoré organické polyméry a kopolyméry, vrátane polymérov a kopolymérov vyrobených z takých monomérov, ako je kyselina akrylová, akrylamid, vinylsulfónová kyselina, kyselina maleinová alebo anhydrid kyseliny maleinovej, polymérov a kopolymérov vyrobených z kyseliny maleinovej a terpolymérov a kopolymérov používajúcich tieto a ďalšie podobné zložky.It is well known that treatment of the aqueous system with some chemical additives may reduce or prevent the formation of inorganic coatings on the surfaces of the aqueous industrial system. Various additives may be used in different situations, depending on the type of coating that causes the problem, and also according to the conditions of the industrial coating system. For this purpose, for example, some organic polymers and copolymers can be added to the aqueous system, including polymers and copolymers made from such monomers as acrylic acid, acrylamide, vinyl sulfonic acid, maleic acid or maleic anhydride, polymers and copolymers made from maleic acid, and terpolymers and copolymers using these and other similar components.
Inou skupinu prísad, ktorá sa používa na zníženie tvorby alebo na predchádzanie tvorby anorganických povlakov na povrchoch vo vodných systémoch, sú polyfosfáty. Táto skupina môže zahrňovať, ale bez obmedzenia na ne, difosforečnan draselný, trifosforečnan sodný, hexametafosforečnan sodný a podobne.Another group of additives that is used to reduce or prevent the formation of inorganic coatings on surfaces in aqueous systems are polyphosphates. This group may include, but is not limited to, potassium pyrophosphate, sodium triphosphate, sodium hexametaphosphate and the like.
V boji s tvorbou anorganického povlaku sa používajú organické zlúčeniny, ktoré obsahujú skupinu s atómom fosforu. Medzi tieto zlúčeniny obsahujúce atóm fosforu patria, ale bez obmedzenia na ne, produkty, ktoré sa zvyčajne označujú ako fosfónové kyseliny, fosfonokarboxylové kyseliny, organické fosfátové estery a podobné.Organic compounds containing a phosphorus atom group are used to combat inorganic coating. Such phosphorus-containing compounds include, but are not limited to, products commonly referred to as phosphonic acids, phosphonocarboxylic acids, organic phosphate esters, and the like.
Použitie akejkoľvek z hore uvedených konvenčných zlúčenín alebo prísad je veľmi dobre známe odborníkom z oblasti techniky odstraňovania povlakov v priemyselných systémoch.The use of any of the above conventional compounds or additives is well known to those skilled in the art of coating removal in industrial systems.
V mnohých prípadoch je možné dosiahnuť zvýšenej aktivity vzhľadom na problém vzniku povlaku použitím rôznych kombinácií hore uvedených zlúčenín a prísad alebo použitím podobných zlúčenín a prísad a ich kombinácií.In many cases, increased activity can be achieved due to the problem of coating formation by using various combinations of the above compounds and additives or by using similar compounds and additives and combinations thereof.
Je napríklad známe, že zmesi polyfosfátov s organickými polymérmi, podobajúce sa a zahrňujúce poly(akrylové kyseliny), sú účinné na znižovanie tvorby povlakov síranu barnatého. Produkty obsahujúce túto kombináciu sa používali komerčne veľa rokov. Ich používaním sa dosiahol značný prospech znížením prestojov v priemyselných procesoch a zlepšenie kvality produktu vyrábaného v týchto systémoch.For example, it is known that mixtures of polyphosphates with organic polymers, similar to and including poly (acrylic acids), are effective to reduce barium sulfate coatings. Products containing this combination have been used commercially for many years. Their use has achieved considerable benefits by reducing downtime in industrial processes and improving the quality of the product produced in these systems.
I keď hore uvedené prísady a kombinácie poskytovali rôzne výhody a úžitky, je vždy výhodné a prospešné zvýšiť účinnosť znížením alebo predchádzať rast povlakov vo vodných systémoch.While the aforementioned additives and combinations have provided various advantages and benefits, it is always advantageous and beneficial to increase efficiency by reducing or preventing the growth of coatings in aqueous systems.
Podstata vynálezuSUMMARY OF THE INVENTION
Predložený vynález sa teda týka prostriedku a spôsobu zlepšenia prevencie, zníženia alebo inhibície rastu povlakov na povrchoch, ktoré sú uvedené do kontaktu s vodným prostredím v priemyselných systémoch.Accordingly, the present invention relates to a composition and method for improving the prevention, reduction or inhibition of the growth of coatings on surfaces that are contacted with the aqueous environment in industrial systems.
Hlavnou výhodou predloženého vynálezu je získanie prostriedku a spôsobu na predchádzanie, zníženie a/alebo inhibíciu povlaku síranu barnatého a/alebo iných typov povlakov na povrchoch, ktoré sú v kontakte s vodným prostredím v priemyselných systémoch, v ktorých sa používajú veľké množstvá vody.The main advantage of the present invention is to provide a composition and method for preventing, reducing and / or inhibiting barium sulfate coating and / or other types of coatings on surfaces in contact with the aqueous environment in industrial systems using large amounts of water.
Ďalšie znaky a výhody vynálezu budú ďalej uvedené v opise, ktorý nasleduje, a sčasti budú zrejmé z opisu alebo je ich možné pochopiť z praktického uplatnenia vynálezu. Predmety a ďalšie výhody vynálezu sa budú realizovať a dosahovať prostriedkom a spôsobom, ktoré sú tu uvedené v písomnom opise, v nárokoch a tiež na pripojených výkresoch.Other features and advantages of the invention will be set forth in the description which follows, and in part will be apparent from the description, or may be understood by the practice of the invention. The objects and other advantages of the invention will be realized and attained by the means and method set forth herein in the written description, claims, and also in the accompanying drawings.
Na dosiahnutie týchto a ďalších výhod a v súlade s účelom vynálezu, a ako je tu zhrnuté a obšírne opísané, sa predložený vynález týka prostriedku na predchádzanie, zníženie a/alebo inhibíciu rastu povlaku v systémoch používajúcich vodné prostredie.To achieve these and other advantages, and in accordance with the purpose of the invention, and as summarized and broadly described herein, the present invention relates to a composition for preventing, reducing and / or inhibiting the growth of a coating in systems using an aqueous environment.
Podľa jedného aspektu vynálezu sa teda získava prostriedok, ktorý obsahuje aniónový organický polymér, polyfosfátovú zlúčeninu a zlúčeninu organofosfonovej kyseliny, v ktorom sú tieto tri zložky prítomné v takom množstve, ktoré je účinné na regulovanie tvorby anorganických povlakov vo vodnom systéme. Medzi tieto povlaky patria povlaky obsahujúce síran barnatý, síran vápenatý, uhličitan vápenatý, fosforečnan vápenatý a šťavelan vápenatý.Accordingly, in one aspect of the invention there is provided a composition comprising an anionic organic polymer, a polyphosphate compound and an organophosphonic acid compound wherein the three components are present in an amount effective to control the formation of inorganic coatings in the aqueous system. Such coatings include coatings comprising barium sulfate, calcium sulfate, calcium carbonate, calcium phosphate and calcium oxalate.
Podľa iného aspektu tohto vynálezu sa získava prostriedok na regulovanie tvorby povlakov obsahujúcich síran barnatý na povrchoch priemyselných systémov, ktoré sú v kontakte s vodným prostredím obsahujúcim síran barnatý, pričom tento prostriedok je zmesou aniónového organického polyméru, polyfosfátovej zlúčeniny a zlúčeniny organofosfonovej kyseliny. Zistilo sa, že zmesi obsahujúce tieto tri zložky sú veľmi účinné na reguláciu zrážania alebo tvornia povlakov síranu bamatého.According to another aspect of the present invention, there is provided a composition for controlling the formation of barium sulphate-containing coatings on surfaces of industrial systems in contact with an aqueous barium sulphate-containing composition, which composition is a mixture of an anionic organic polymer, polyphosphate compound and organophosphonic acid compound. Mixtures containing these three components have been found to be very effective in controlling the precipitation or formation of barium sulfate coatings.
Podľa ďalšieho aspektu predloženého vynálezu sa získava spôsob regulovania tvorby anorganických povlakov na povrchoch v kontakte s vodným prostredím vo vodnom systéme. Pojem „kontakt“, ktorý sa tu používa, zahrňuje periodický alebo občasný kontakt ako aj nepretržitý kontakt s vodným systémom. Vodný systém sa uvedie do kontaktu s prostriedkom, ktorý obsahuje aniónový organický polymér, polyfosfátovú zlúčeninu a zlúčeninu organofosfonovej kyseliny. Tieto tri zložky sú prítomné v takom kombinovanom množstve, ktoré je synergicky účinné na reguláciu tvorby anorganických povlakov vo vodnom systéme.According to a further aspect of the present invention there is provided a method of controlling the formation of inorganic coatings on surfaces in contact with an aqueous environment in an aqueous system. The term "contact" as used herein includes periodic or occasional contact as well as continuous contact with the aqueous system. The aqueous system is contacted with a composition comprising an anionic organic polymer, a polyphosphate compound, and an organophosphonic acid compound. The three components are present in a combined amount that is synergistically effective to control the formation of inorganic coatings in the aqueous system.
Autori vynálezu zistili, že pridanie organofosfónovej kyseliny k hore opísaným kombináciám polyfosfát/organický polymér poskytuje hlavný prospech zvýšením účinnosti na znižovanie alebo predchádzanie rastu povlakov na povrchoch vo vodných systémoch.The inventors have found that adding an organophosphonic acid to the polyphosphate / organic polymer combinations described above provides a major benefit by increasing efficiency to reduce or prevent the growth of coatings on surfaces in aqueous systems.
Ak sa zlúčenina organofosfónovej kyseliny používa v kombinácii s polyfosfátovou zlúčeninou a aniónovými organickými polymérmi podľa predloženého vynálezu, existuje synergický účinok pri predchádzaní, odstránení, znížení a/alebo inhibícii rastu anorganického povlaku na povrchoch, ktoré sú v kontakte s vodnými prostrediami (vrátane vody), ktoré obsahujú anorganické soli tvoriace povlaky, v systémoch a procesoch, ktoré používajú takéto vodné prostredia, a ktoré sú tu definované ako vodné systémy alebo vodné priemyselné systémy. Ako sa uvádza v nasledujúcom opise a v nasledujúcich príkladoch, synergický účinok kombinácie aspoň jednej zlúčeniny organofosfónovej kyseliny s aspoň jedným aniónovým organickým polymérom a aspoň jednou polyfosfátovou zlúčeninou vedie k podstatnému zníženiu zrážania síranu barnatého z vodného prostreda obsahujúceho síran barnatý. Prostriedok podľa predloženého vynálezu je teda podstatne účinnejší ako zmesi a materiály bežne známe alebo dostupné na zabránenie rastu povlaku. Pojem zabránenie tvorby povlakov, ako sú povlaky síranu barnatého, ako sa tu tento pojem používa, sa definuje ako odstránenie, predchádzanie, zníženie a/alebo inhibovanie tvorby týchto povlakov.When the organophosphonic acid compound is used in combination with the polyphosphate compound and the anionic organic polymers of the present invention, there is a synergistic effect in preventing, removing, reducing and / or inhibiting the growth of the inorganic coating on surfaces in contact with aqueous media (including water), containing inorganic salt-forming coatings in systems and processes using such aqueous media, and defined herein as aqueous systems or aqueous industrial systems. As mentioned in the following description and in the following examples, the synergistic effect of combining at least one organophosphonic acid compound with at least one anionic organic polymer and at least one polyphosphate compound results in a significant reduction in precipitation of barium sulfate from an aqueous barium sulfate-containing medium. Thus, the composition of the present invention is substantially more effective than the compositions and materials commonly known or available to prevent coating growth. The term coating prevention, such as barium sulfate coatings, as used herein, is defined as the removal, prevention, reduction and / or inhibition of the formation of such coatings.
Hore uvedené a ďalšie výhody a znaky tohto vynálezu budú zrejmé po zhrnutí nasledujúceho podrobného opisu. Pripojený graf je tu zahrnutý pre ďalšie objasnenie tohto vynálezu a predstavuje časť tohto spisu. Ilustruje niekoľko uskutočnení podľa vynálezu a spoločne s opisom slúži na vysvetlenie podstaty vynálezu.The foregoing and other advantages and features of the present invention will be apparent from the following detailed description. The accompanying graph is included herein to further illustrate the present invention and is part of this disclosure. It illustrates several embodiments of the invention and together with the description serves to explain the essence of the invention.
V ďalšom odstavci sa stručne opisuje obrázok.The next paragraph briefly describes the figure.
Obrázok 1 je grafická reprezentácia porovnania ceny inhibítorov povlaku síranu barnatého. Na ilustráciu výhod predloženého vynálezu sa uvádza faktor ceny proti inhibícii povlaku vo vodnom prostredí pri pH 5. Pri veľkom rozsahu aplikovaných dávok poskytuje kombinácia polyakrylovej kyseliny a polyfosfátu výsledok označený AP. Pridanie organických fosfónových kyselín k tejto zmesi poskytuje porozuhodne zlepšené výsledky, ako ukazuje krivka A (pre vzorec A) a krivka B (pre vzorec B).Figure 1 is a graphical representation of a price comparison of barium sulfate coating inhibitors. To illustrate the advantages of the present invention, a cost factor against inhibition of the coating in an aqueous medium at pH 5 is given. For a wide range of dosages applied, the combination of polyacrylic acid and polyphosphate gives a result labeled AP. The addition of organic phosphonic acids to this mixture provides remarkably improved results, as shown by Curve A (for Formula A) and Curve B (for Formula B).
V ďalšej časti spisu sa uvádza najlepší spôsob uskutočnenia vynálezu.The best mode of carrying out the invention is described below.
Podľa predloženého vynálezu musií prostriedok obsahovať aspoň jednu každú nasledujúcu zlúčeninu: aniónový organický polymér, polyfosfátovú zlúčeninu a zlúčeninu organofosfónovej kyseliny. Tieto tri zložky prostriedku sú prítomné v takom kombinovanom množstve, ktoré je účinné na zabránenie tvorby anorganických povlakov vo vodnom systéme. Podľa vynálezu, kombinovaným množstvom aniónového organického polyméru, polyfosfátovej zlúčeniny a zlúčeniny organofosfónovej kyseliny sa dosahuje lepšie zabránenie tvorby anorganických povlakov ako rovnakým množstvom ktorejkoľvek z týchto troch zložiek samotnej alebo ako rovnakým množstvom ktorejkoľvek kombinácie dvoch z týchto zložiek. Prostriedky podľa predloženého vynálezu poskytujú synergické výsledky na reguláciu tvorby povlakov.According to the present invention, the composition must comprise at least one of each of the following: an anionic organic polymer, a polyphosphate compound, and an organophosphonic acid compound. The three components of the composition are present in a combined amount effective to prevent the formation of inorganic coatings in the aqueous system. According to the invention, a combined amount of anionic organic polymer, polyphosphate compound and organophosphonic acid compound results in better prevention of the formation of inorganic coatings than the same amount of any of the three components alone or the same amount of any combination of the two. The compositions of the present invention provide synergistic results for controlling coating formation.
Aniónové organické polyméry (vrátane oligomérov, homopolymérov, kopolymérov, terpolymérov atď.) použité v prostriedku a spôsobom podľa predloženého vynálezu zahrňujú akékoľvek konvenčné aniónové organické polyméry používané pri aplikáciách znižovania povlaku. Aniónové organické polyméry, ako sa tu používajú, zahrňujú, ale bez obmedzenia na ne, polyméry pochádzajúce z polymerizácie jedného alebo viacej nasledujúcich monomérov: kyseliny akrylovej, akrylamidu, vinylsulfónovej kyseliny, kyseliny maleinovej, anhydridu kyseliny maleinovej a podobných. Medzi príklady týchto aniónových organických polymérov patria, ale bez obmedzenia na ne, polyakryláty, polymaleinová kyselina, anhydridy polymaleinovej kyseliny, hydrolyzovaný polyakrylonitril, polymetakrylová kyselina, sulfonovaný AMPS, vinylsulfónová kyselina a ich soli. Ďalšie aniónové organické polyméry, ktoré sa môžu používať ako polyméry (s výhodou kopolyméry), pochádzajú z polymerizácie jedného alebo viacej hore uvedených monomérov s jedným alebo viacej neiónovými monomérmi, ako je akrylamid, styrén a podobné. Molekulová hmotnosť aniónových organických polymérov (vrátane kopolymérov) nie je rozhodujúca. Aniónové organické polyméry používané podľa predloženého vynálezu môžu mať akúkoľvek molekulovú hmotnosť, ako je dobre známe z oblasti techniky.The anionic organic polymers (including oligomers, homopolymers, copolymers, terpolymers, etc.) used in the composition and process of the present invention include any conventional anionic organic polymers used in coating reduction applications. Anionic organic polymers as used herein include, but are not limited to, polymers derived from the polymerization of one or more of the following monomers: acrylic acid, acrylamide, vinyl sulfonic acid, maleic acid, maleic anhydride and the like. Examples of such anionic organic polymers include, but are not limited to, polyacrylates, polymaleic acid, polymaleic acid anhydrides, hydrolyzed polyacrylonitrile, polymethacrylic acid, sulfonated AMPS, vinyl sulfonic acid, and salts thereof. Other anionic organic polymers that can be used as polymers (preferably copolymers) are derived from the polymerization of one or more of the above monomers with one or more nonionic monomers such as acrylamide, styrene, and the like. The molecular weight of the anionic organic polymers (including copolymers) is not critical. The anionic organic polymers used in the present invention may have any molecular weight as is well known in the art.
Časť mechanizmu predchádzania povlakom pri ich tvorení predstavuje „dispergovanie“ vyzrážaných materiálov. Aniónový polymér sa pripojí na pôvodný kryštál vyzrážaného materiálu a potiahne ho aniónovým nábojom. Tým sa zníži pravdepodobnosť, že tieto kryštály budú aglomerovať a vytvárať povrchy pri kontakte s vodnými roztokmi používanými vo vodných systémoch, napr. na stenách trubiek, zásobníkov a podobných. Navyše majú tieto povrchy tendenciu byť aniónové, takže tu dochádza tiež k odpudzovaniu.Part of the coating prevention mechanism in forming them is to "disperse" the precipitated materials. The anionic polymer is attached to the original crystal of the precipitated material and coated with an anionic charge. This will reduce the likelihood that these crystals will agglomerate and form surfaces in contact with aqueous solutions used in aqueous systems, e.g. on the walls of pipes, containers and the like. Moreover, these surfaces tend to be anionic so that repulsion also occurs here.
Aniónové polyméry používané podľa predloženého vynálezu sú zvyčajne rozpustné vo vode alebo sú dispergovateľné vo vode. S výhodou sú rozpustné vo vode.The anionic polymers used according to the present invention are usually water-soluble or water-dispersible. They are preferably water soluble.
Aniónový organický polymér v prostriedku podľa predloženého vynálezu s výhodou znamená polyakrylátovú zlúčeninu alebo jej soli. Výhodnejšie aniónový organický polymér znamená polymér kyseliny akrylovej (napr. homopolymér kyseliny akrylovej). Aniónovým organickým polymérom je najvýhodnejšie kopolymér kyseliny akrylovej a akrylamidu s molekulovou hmotnosťou asi 3000 až asi 5000. Podľa predloženého vynálezu sa môže používať napríklad BSI 91, kyselina polyakrylová, a BSI 75, kopolymér polyakrylovej kyseliny. Obidve tieto zlúčeniny sú dostupné od firmy Buckman Laboratories International, Inc., Memphis, Tennessee.The anionic organic polymer in the composition of the present invention is preferably a polyacrylate compound or salts thereof. More preferably, the anionic organic polymer is an acrylic acid polymer (e.g., a homopolymer of acrylic acid). The anionic organic polymer is most preferably a copolymer of acrylic acid and acrylamide having a molecular weight of about 3000 to about 5000. According to the present invention, for example, BSI 91, polyacrylic acid, and BSI 75, a polyacrylic acid copolymer can be used. Both of these compounds are available from Buckman Laboratories International, Inc., Memphis, Tennessee.
Polyfosfátové zlúčeniny používané v prostriedku a spôsobom podľa predloženého vynálezu zahrňujú akékoľvek konvenčné polyfosfátové zlúčeniny, s výhodou tie, ktoré sa používajú na znižovanie povlaku. Medzi príklady polyfosfátových zlúčenín, ktoré sa môžu používať podľa predloženého vynálezu, patria, ale bez obmedzenia na ne, difosforečnany a polyfosfáty koordinované so sodíkom alebo draslíkom, ako je trifosforečnan sodný, difosforečnan draselný a hexametafosforečnan sodný. Hexametafosforečnan sodný sa s výhodou používa pri pH okolo 5 až 6. Výhodnou polyfosfátovou zlúčeninou používanou v prostriedku a spôsobom podľa predloženého vynálezu je trifosforečnan. Trifosforečnany sa s výhodou používajú pri pH okolo 10 až 11. Výhodnejšie sa ako polyfosfátové zlúčenina podľa predloženého vynálezu používa trifosforečnan sodný.The polyphosphate compounds used in the composition and method of the present invention include any conventional polyphosphate compounds, preferably those used to reduce the coating. Examples of polyphosphate compounds that can be used according to the present invention include, but are not limited to, pyrophosphates and polyphosphates coordinated with sodium or potassium, such as sodium triphosphate, potassium pyrophosphate and sodium hexametaphosphate. Sodium hexametaphosphate is preferably used at a pH of about 5 to 6. The preferred polyphosphate compound used in the composition and process of the present invention is triphosphate. The triphosphates are preferably used at a pH of about 10-11. More preferably sodium triphosphate is used as the polyphosphate compound of the present invention.
Medzi zlúčeniny kyseliny organofosfónovej používanej v prostriedku a spôsobom podľa predloženého vynálezu patria akékoľvek konvenčné organické zlúčeniny obsahujúce atóm fosforu používané na ošetrenie vody. Podľa predloženého vynálezu sa môže použiť akákoľvek zlúčenina organofosfónovej kyseliny, pokiaľ poskytuje synergický účinok na predchádzanie, odstraňovanie, zníženie a/alebo inhibíciu tvorby anorganického povlaku, vrátane rastu povlaku síranu barnatého, na povrchoch, ktoré sú v kontakte s vodným prostredím, ak sa kombinuje s aniónovým organickým polymérom a polyfosfátovou zlúčeninou. Tieto organické fosfo'nové kyseliny s výhodou znamenajú zlúčeniny všeobecného vzorca r—p—OHThe organophosphonic acid compounds used in the composition and method of the present invention include any conventional phosphorus-containing organic compounds used to treat water. Any organophosphonic acid compound can be used according to the present invention as long as it provides a synergistic effect to prevent, remove, reduce and / or inhibit the formation of an inorganic coating, including barium sulfate coating growth, on surfaces that are in contact with the aqueous environment when combined with an anionic organic polymer and a polyphosphate compound. These organic phosponic acids are preferably compounds of the general formula r-p-OH
II
OHOH
Táto molekula typicky obsahuje aspoň niekoľko skupín fosfonovej kyseliny. Podľa vlastností substituenta R môže byť rozpustná vo vode. Napríklad substituent R môže znamenať organický amín. Takéto organofosfónové zlúčeniny sa opisujú v práci z 5. apríla 1991 podané Association of Water Technologies v San Antóniu,This molecule typically contains at least several phosphonic acid groups. Depending on the properties of R, it may be water-soluble. For example, R can be an organic amine. Such organophosphone compounds are disclosed in the April 5, 1991 application of the Association of Water Technologies in San Antonio,
Texas, Róbertom Cavanom s názvom „Phosphonates: Lore and Legend“; táto práca je tu zahrnutá ako citácia.Texas, Rob Cavan, entitled "Phosphonates: Lore and Legend"; this work is incorporated herein by reference.
Medzi príklady organofosfónových kyselín, ktoré sa môžu používať v predloženom vynáleze, patria, ale bez obmedzenia na ne, aminotris(metylénfosfónová kyselina), dietyléntriaminpenta(metylénfosfónová kyselina), hydroxyetylidénbis(fosfónová kyselina), tetrakismetylénfosfónová kyselina diaminocyklohexanu, tetrakismetylénfosfónová kyselina diaminometylpentanu, soli týchto kyselín a podobné. Organofosfónová kyselina je s výhodou vybraná zo skupiny pozostávajúcej z aminotris(metylénfosfónovej kyseliny), hydroxyetylidénbis(fosfónovej kyseliny), tetrakismetylénfosfónovej kyseliny diaminocyklohexanu a tetrakismetylénfosfónovej kyseliny diaminometylpentanu.Examples of organophosphonic acids that may be used in the present invention include, but are not limited to, aminotris (methylene phosphonic acid), diethylene triaminepenta (methylene phosphonic acid), hydroxyethylidene bis (phosphonic acid), tetrakismethylene phosphonic acid diaminacyclohexane, and so on. Preferably, the organophosphonic acid is selected from the group consisting of aminotris (methylene phosphonic acid), hydroxyethylidene bis (phosphonic acid), tetrakismethylene phosphonic acid, diaminocyclohexane, and tetrakismethylene phosphonic acid, diaminomethylpentane.
Množstvom zlúčeniny organofosfónovej kyseliny, polyfosfátovej zlúčeniny a aniónového organického polyméru v prostriedku a spôsobu podľa predloženého vynálezu je také množstvo, ktoré je účinné na reguláciu tvorby rastu anorganického povlaku na povrchoch v kontakte s vodnými prostrediami v systémoch, ktoré používajú vodné prostredia, t. j. vo vodných systémoch alebo vodných priemyselných systémoch, a na získanie tu diskutovaného synergického účinku. I keď tu nie je žiadny zámer obmedzenia špecifickými množstvami, v niektorých aspektoch predloženého vynálezu prostriedok obsahuje asi 0,1 % až asi 60,0 % zlúčeniny organofosfónovej kyseliny, asi 1,0 % až asi 50,0 % polyfosfátovej zlúčeniny a asi 1,0 % až asi 60,0 % aniónového organického polyméru. V niektorých výhodných uskutočneniach prostriedok obsahuje asi 0,1 % až asi 10,0 % zlúčeniny organofosfónovej kyseliny, asi 1,0 % až asi 20,0 % polyfosfátovej zlúčeniny a asi 1,0 % až asi 30,0 % aniónového organického polyméru. V najvýhodnejších uskutočneniach prostriedok obsahuje asi 0,1 % až asi 4,0 % zlúčeniny organofosfónovej kyseliny, asi 1,0 % až asi 10,0 % polyfosfátovej zlúčeniny a asi 1,0 % až asi 20,0 % aniónového organického polyméru. Všetky množstvá sú uvedené ako hmotnostné percentá vzťažené na celkovú hmotnosť prostriedku.The amount of organophosphonic acid compound, polyphosphate compound and anionic organic polymer in the composition and method of the present invention is an amount effective to control the formation of inorganic coating growth on surfaces in contact with aqueous media in systems that use aqueous media, i. j. in aqueous systems or aqueous industrial systems, and to obtain the synergistic effect discussed herein. While there is no intention of limiting specific amounts, in some aspects of the present invention, the composition comprises about 0.1% to about 60.0% organophosphonic acid compound, about 1.0% to about 50.0% polyphosphate compound, and about 1%, 0% to about 60.0% of an anionic organic polymer. In some preferred embodiments, the composition comprises about 0.1% to about 10.0% of an organophosphonic acid compound, about 1.0% to about 20.0% of a polyphosphate compound, and about 1.0% to about 30.0% of an anionic organic polymer. In most preferred embodiments, the composition comprises about 0.1% to about 4.0% of an organophosphonic acid compound, about 1.0% to about 10.0% of a polyphosphate compound, and about 1.0% to about 20.0% of an anionic organic polymer. All amounts are given as weight percent based on the total weight of the composition.
Prostriedky podľa predloženého vynálezu sú všeobecne rozpustné vo vode alebo sú vo vode dispergovateľné. Môžu sa pridávať priamo do vodných prúdov procesu a/alebo zásobníka a podobne ako pevné látky, napr. ako voľne sypké prášky, alebo môžu sa rozpustiť vo vode na akékoľvek žiadané koncentrácie, napr. asi 25 % až asi 75 % (hmotn.) a pridávať do vodných prúdov procesu, zásobníka a podobne v roztokoch. Ak sa prostriedky podľa predloženého vynálezu pridávajú do prúdu vodného procesu, do zásobníka obsahujúceho vodné prostredie alebo do akéhokoľvek iného vodného prostredia vo vodnom systéme, tento prostriedok je v kontakte s povrchmi (napr. stenami trubiek, zásobníkov a podobne) vo vodnom systéme a reguluje rast anorganického povlaku na povrchu, t. j. eliminuje, predchádza, znižuje a/alebo inhibuje tvorbu týchto povlakov na povrchu. Predložený vynález funguje ako prítomnosťou prostriedkov podľa vynálezu vo vodných prostrediach tak uvedením prostriedkov do kontaktu s povrchmi v hore uvedených médiách.The compositions of the present invention are generally water-soluble or water-dispersible. They may be added directly to the aqueous process streams and / or reservoirs and like solids, e.g. as free-flowing powders, or can be dissolved in water to any desired concentration, e.g. about 25% to about 75% (w / w) and added to the aqueous streams of the process, reservoir, and the like in solutions. When the compositions of the present invention are added to an aqueous process stream, a container containing an aqueous medium, or any other aqueous medium in an aqueous system, the composition is in contact with surfaces (e.g., tube walls, containers, and the like) in the aqueous system to control growth an inorganic coating on the surface, i. j. eliminates, prevents, reduces and / or inhibits the formation of such coatings on the surface. The present invention functions both by the presence of the compositions of the invention in aqueous media and by contacting the compositions with the surfaces in the above media.
V prostriedkoch a pri spôsobe podľa predloženého vynálezu sa môžu používať ďalšie prísady, pokiaľ nemajú nepriaznivý vplyv na reguláciu tvorby povlakov. Napríklad v prostriedku a pri spôsobe podľa predloženého vynálezu sa môžu používať konvenčné zlúčeniny na aplikáciu do vody. Prostriedok podľa predloženého vynálezu sa môže používať pri akomkoľvek pH, s ktorým sa normálne stretávame vo vodných systémoch, napríklad v ropných vrtoch, holendroch, pri postupoch výroby papiera a pod.Other additives may be used in the compositions and process of the present invention as long as they do not adversely affect the control of the coating. For example, conventional compounds for application to water may be used in the composition and method of the present invention. The composition of the present invention can be used at any pH normally encountered in aqueous systems such as oil wells, holenders, paper making processes and the like.
Predložený vynález sa ďalej týka spôsobu na regulovanie tvorby anorganických povlakov na povrchoch vo vodnom systéme. Vodný systém sa uvedie do kontaktu s prostriedkom obsahujúcim aniónový organický polymér, polyfosfát a organofosfónovú kyselinu. Tieto tri zložky sú prítomné v takom kombinovanom množstve, ktoré je synergicky účinné na regulovanie tvorby anorganických povlakov vo vodnom systéme.The present invention further relates to a method for controlling the formation of inorganic coatings on surfaces in an aqueous system. The aqueous system is contacted with a composition comprising an anionic organic polymer, polyphosphate, and organophosphonic acid. The three components are present in a combined amount that is synergistically effective to control the formation of inorganic coatings in the aqueous system.
Predložený vynález je zvlášť užitočný na znižovanie alebo predchádzanie povlakov obsahujúcich síran bamatý. Povlaky síranu barnatého, rovnako ako povlaky obsahujúce iné anorganické zlúčeniny, je možné nájsť vo vodných priemyselných systémoch, ako sú papierne, holendre a ropné vrty.The present invention is particularly useful for reducing or preventing coatings containing barium sulfate. Barium sulfate coatings, as well as coatings containing other inorganic compounds, can be found in aqueous industrial systems such as paper mills, holenders and oil wells.
Prostriedok a spôsob podľa predloženého vynálezu sa ilustruje spôsobom nasledujúcich príkladov. Tomu je treba rozumieť tak, že tento vynález nie je obmedzený na špecifické podmienky alebo podrobnosti uvedené v týchto príkladoch, pokiaľ takéto obmedzenia nie sú uvedené v pripojených nárokoch.The composition and method of the present invention is illustrated by the following examples. It is to be understood that the invention is not limited to the specific conditions or details set forth in these examples, unless such limitations are set forth in the appended claims.
Príklady uskutočnenia vynálezuDETAILED DESCRIPTION OF THE INVENTION
Príklad 1Example 1
Údaje, ktoré sú uvedené nižšie v tabuľke 1 a v tabuľke 2, ilustrujú synergizmus získaný prostriedkom podľa predloženého vynálezu. Pri obidvoch hodnotách pH 5 i 7 bol aditívny účinok oddelených zložiek omnoho menší ako pozorovaný výsledok kombinovaných materiálov.The data presented in Table 1 and Table 2 below illustrate the synergism obtained by the composition of the present invention. At both pH 5 and pH 7, the additive effect of the separated components was much less than the observed result of the combined materials.
Najprv sa pripravia nasledujúce roztoky:First, the following solutions are prepared:
- 300 ppm roztok chloridu barnatého, ktorý sa pripraví rozpustením 0,5336 g dihydrátu chloridu barnatého v jednom litri deionizovanej vody,- 300 ppm barium chloride solution, prepared by dissolving 0,5336 g of barium chloride dihydrate in one liter of deionized water,
- 200 ppm roztok síranu sodného, ktorý sa pripraví rozpustením 0,2957 g síranu sodného v jednom litri deionizovanej vody, a- a 200 ppm sodium sulphate solution prepared by dissolving 0,2957 g of sodium sulphate in one liter of deionized water, and
- 111,11 ppm roztok chloridu draselného, ktorý sa pripraví rozpustením 0,1111 g chloridu draselného v jednom litri deionizovanej vody.- 111,11 ppm potassium chloride solution, prepared by dissolving 0,1111 g of potassium chloride in one liter of deionized water.
0,05 % účinné roztoky prostriedku podľa predloženého vynálezu sa pripravia tak, že sa vyrobí 0,5 % účinný roztok a ten sa 10x zriedi. Prostriedok A obsahoval takéto dávky každej zložky v ppm, ako je uvedené nižšie v tabuľke 1. Výsledky testu s použitím prostriedku A sú tiež uvedené v tabuľkel.0.05% active solutions of the composition of the present invention are prepared by making 0.5% active solution and diluting 10x. Formulation A contained such doses of each component in ppm as shown in Table 1 below. The results of the assay using Formulation A are also shown in the table.
Prostriedok A: 4,05 dielu trifosforečnanu sodnéhoFormulation A: 4.05 parts of sodium triphosphate
4,57 dielu kyseliny polyakrylovej (X)4.57 parts of polyacrylic acid (X)
1,38 dielu aminotris(metylénfosfónovej kyseliny) (A)1.38 parts of aminotris (methylenephosphonic acid) (A)
Polyakrylová kyselina (X) bola kopolymérom kyseliny akrylovej a akrylamidu.Polyacrylic acid (X) was a copolymer of acrylic acid and acrylamide.
ml roztoku chloridu bamatého sa zmieša s kombináciou prostriedku A vml of barium chloride solution is mixed with the combination of formulation A in
100 ml fľaši. Pridaním hydroxidu sodného sa pH prostriedku A upraví na 10 až 11. To je výhodné pH, ak sa pracuje s trifosforečnanom sodným. Potom sa pridá 25 ml roztoku síranu sodného, ktorého pH sa upraví hydroxidom sodným. Fľaša sa uzavrie a nechá sa stáť cez noc pri 25 eC. Pripravia sa kontroly, ktoré obsahujú 25 ml roztoku chloridu barnatého a 25 ml roztoku síranu. Pripravia sa slepé pokusy, ktoré obsahujú 25 ml roztoku chloridu barnatého a 25 ml deionizovanej vody.100 ml bottle. The pH of composition A is adjusted to 10-11 by the addition of sodium hydroxide. This is preferably the pH when working with sodium triphosphate. 25 ml of sodium sulfate solution are then added, the pH of which is adjusted with sodium hydroxide. The bottle was capped and allowed to stand overnight at 25 e C. Controls were made containing 25 ml of the barium solution and 25 ml of sodium sulphide. Prepare blank experiments containing 25 ml of barium chloride solution and 25 ml of deionized water.
Z fľaše sa odoberie 2 ml vzorka a umiestni sa s 18 ml roztoku chloridu draselného v odstredivkovej skúmavke a zmes sa pretrepe. Vzorka sa potom analyzuje atómovým absorpčným spektrofotometrom na bárium. Vypočíta sa percento inhibície, vzťažené na ppm bária pri kontrole odpočítaných od ppm bária v testovanej vzorke, delené ppm bária pri kontrole odpočítaných od ppm bária pri slepom pokuse. To je uvedené v tabuľkách 1 a 2 ako percento zníženia zrazeniny.A 2 ml sample is taken from the flask and placed with 18 ml of potassium chloride solution in a centrifuge tube and shaken. The sample is then analyzed by atomic absorption spectrophotometer for barium. Calculate the percent inhibition based on ppm barium in the control subtracted from ppm barium in the test sample, divided by ppm barium in the control subtracted from ppm barium in the blank. This is shown in Tables 1 and 2 as a percentage of reduction of the precipitate.
Tabuľka 1Table 1
Údaje v tabuľke 2 sú odvodené od variácie (prostriedok B), v ktorej sa na výrobu prostriedka podľa vynálezu použije iný komerčne dostupný polyakrylát (homopolymér kyseliny akrylovej) a iná komerčne dostupná kyselina fosfónová. Prostriedok B, ktorého zložky sú uvedené nižšie, obsahoval dávku každej zložky v ppm tak, ako je uvedené nižšie v tabuľke 2. Výsledky testu s použitím prostredka B sú tiež uvedené v tabuľke 2. Opäť kombinácia poskytla omnoho lepšie výsledky ako sa očakávalo.The data in Table 2 is derived from a variation (composition B) in which another commercially available polyacrylate (acrylic acid homopolymer) and other commercially available phosphonic acid are used to make the composition of the invention. Formulation B, the components of which are listed below, contained the dose of each component in ppm as shown below in Table 2. The results of the assay using Composition B are also shown in Table 2. Again, the combination yielded much better results than expected.
Prostriedok AB 4,05 dielu trifosforečnanu sodnéhoFormulation AB 4.05 parts of sodium triphosphate
4,57 dielu kyseliny polyakrylovej (Y)4.57 parts of polyacrylic acid (Y)
1,38 dielu hydroxyetylidénbis(fosfónovej kyseliny) (B)1.38 parts of hydroxyethylidene bis (phosphonic acid) (B)
Tabuľka 2Table 2
Obrázok 1 Iným spôsobom ilustruje výhodu predloženého vynálezu. Kombinácia polyakrylovej kyseliny a polyfosfátu, účinný komerčne dostupný produkt, vo veľkom rozmedzí pomerov ošetrení poskytla výsledok označený AP. Pridanie organických fosfónových kyselín k tejto zmesi poskytlo pozoruhodne zlepšené výsledky, ako ukazuje krivka A (pre prostriedok A) a krivka B (pre prostriedok B). Graf 1 ukazuje výsledky pri pH 5.Figure 1 Another way illustrates the advantage of the present invention. The combination of polyacrylic acid and polyphosphate, an effective commercially available product, over a wide range of treatment ratios gave a result labeled AP. The addition of organic phosphonic acids to this mixture gave remarkably improved results, as shown by curve A (for composition A) and curve B (for composition B). Figure 1 shows the results at pH 5.
Príklad 2Example 2
Predložený vynález sa testoval tiež na mieste, v papierni. Táto papiereň vyrába viac ako 700 ton lepenky za deň. Problémom, ktorý sa v priebehu rokov stále vracal, bol rast povlaku síranu barnatého vo výrobnom zariadení, vrátane nátokových skrini a čističiek. Tento povlak môže upchať diery v nátokovej skrini, čo znižuje kvalitu vyrobeného papiera.The present invention was also tested on site, in a paper mill. This paper produces more than 700 tons of cardboard per day. A problem that has continued to recur over the years has been the growth of the barium sulfate coating in the production facility, including headboxes and purifiers. This coating can clog holes in the headbox, which reduces the quality of the paper produced.
Na zníženie problémov a zvýšení doby medzi odstávkami stroja pre potrebné čistenie sa použila kombinácia polyfosfátu a polyakrylovej kyseliny. V istých štádiách ošetrenia môže táto kombinácia veľmi dobre pracovať. Typickým ošetrením v tomto prípade je asi 0,25 ppm (dielov z milióna) polyfosfátu v celkovom toku vody a 0,10 ppm kyseliny polyakrylovej.A combination of polyphosphate and polyacrylic acid was used to reduce problems and increase the time between machine shutdowns for necessary cleaning. At certain stages of treatment, this combination may work very well. A typical treatment in this case is about 0.25 ppm (parts per million) of polyphosphate in total water flow and 0.10 ppm of polyacrylic acid.
Pri pokuse zlepšiť uskutočnenie sa pri nasledujúcom ošetrení miesto kombinácie polyfosfát/polyakrylová kyselina použil prostriedok podľa predloženého vynálezu, t. j. kyselina fosfónová, polyfosfát a kyselina polyakrylová. Pri revidovanom ošetrení bola cena rovnaká ako pri pôvodnom ošetreni. 25 % pôvodného ošetrenia sa nahradilo kyselinou fosfónovou. Pomery pridania boli približne 0,19 ppm polyfosfátu, 0,075 ppm kyseliny polyakrylovej a 0,09 ppm kyseliny fosfónovej.In an attempt to improve the performance of the following treatment, the composition of the present invention was used instead of the polyphosphate / polyacrylic acid combination, i. j. phosphonic acid, polyphosphate and polyacrylic acid. In the revised treatment, the price was the same as in the original treatment. 25% of the original treatment was replaced with phosphonic acid. The addition rates were approximately 0.19 ppm polyphosphate, 0.075 ppm polyacrylic acid and 0.09 ppm phosphonic acid.
Výsledkom tohto programu bolo významné zníženie rastu povlaku síranu barnatého v tomto papiernickom stroji. Po tom, čo tento program prebiehal 6 týždňov, boli všetky diery v nátokovej skrini čisté a neupchaté. Malé množstvo povlaku, ktoré bolo vidieť, bolo mimoriadne tenké a neproblematické. Táto papiereň teraz používa kombináciu podľa tohto vynálezu na reguláciu povlaku síranu barnatého.This program resulted in a significant reduction in barium sulfate coating growth in this papermaking machine. After this program was run for 6 weeks, all holes in the headbox were clean and not clogged. The small amount of coating that was visible was extremely thin and unproblematic. This paper now uses the combination of the present invention to control the barium sulfate coating.
Claims (12)