SE527531C2 - Materials for packaging purposes, process for making the material and packaging process - Google Patents

Materials for packaging purposes, process for making the material and packaging process

Info

Publication number
SE527531C2
SE527531C2 SE0202528A SE0202528A SE527531C2 SE 527531 C2 SE527531 C2 SE 527531C2 SE 0202528 A SE0202528 A SE 0202528A SE 0202528 A SE0202528 A SE 0202528A SE 527531 C2 SE527531 C2 SE 527531C2
Authority
SE
Sweden
Prior art keywords
layer
primer
material according
otr
layers
Prior art date
Application number
SE0202528A
Other languages
Swedish (sv)
Other versions
SE0202528L (en
SE0202528D0 (en
Inventor
Karl Nideborn
Mattias Bragvad
Original Assignee
Amcor Flexibles Lund Ab
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Amcor Flexibles Lund Ab filed Critical Amcor Flexibles Lund Ab
Priority to SE0202528A priority Critical patent/SE527531C2/en
Publication of SE0202528D0 publication Critical patent/SE0202528D0/en
Priority to PCT/SE2003/001324 priority patent/WO2004020304A1/en
Priority to EP03791526A priority patent/EP1534602A1/en
Priority to AU2003253553A priority patent/AU2003253553A1/en
Publication of SE0202528L publication Critical patent/SE0202528L/en
Priority to NO20051436A priority patent/NO20051436L/en
Publication of SE527531C2 publication Critical patent/SE527531C2/en

Abstract

The present invention relates to a material for packaging purposes, which material comprises a first layer composed of thermoplastic polymer, a second layer composed of thermoplastic polymer and an intermediate barrier layer in the form of a primer, where one of the said first and second layers exhibits an oxygen permeability (OTR) which is greater than 6.0 and less than 45 cm<3>/[m<2> day atm] at 23 °C, 50 % relative atmospheric humidity and on a plane sheet, and the said barrier layer in the form of primer on either one of the layers contributing to the said material exhibiting an OTR which is less than 9.0 cm<3>/[m<2> day atm] and the said primer layer exhibiting adhesion against the said non-primer-treated layer and the ability to be heat-sealed against polyolefin systems and polyester systems, and to a process for producing the said material, and to a process for packaging using the said material.

Description

oo O oo: 0 o oo o o o OI IOII o o o! oo oooo oo I 0 o I I lo: I o I o att OIII Oo oo co o o o O o I o I o o o l o O! C000 10 15 20 25 30 REDOGÖRELSE FÖR UPPFlNNlNGEN Föreliggande uppfinning avser ett material för förpackningsändamäl, omfattande ett första skikt av termoplastisk polymer, ett andra skikt av termoplastisk po|ymer och ett mellanliggande barriärskikt i form av en primer, varvid det ena av nämnda första och andra skikt uppvisar en syrgaspermeabilitet (OTR) som är större än 6,0 och mindre än 45 cma /[m2 dag atm] vid 23° C, 50% relativ luftfuktighet och på plan folie, att nämnda barriärskikt i form av primer på endera av skikten bidrar till att nämnda material uppvisar en OTR som är mindre än 9,0 cma /[m2 dag atm] och att nämnda primer uppvisar adhesion mot det icke primerbehandlade skiktet och värmeförseglingsbarhet mot polyolefin-system och polyeestersystem. oo O oo: 0 o oo o o o OI IOII o o o! oo oooo oo I 0 o I I lo: I o I o att OIII Oo oo co o o o o O I I o I o o o o l o! DISCLOSURE OF THE INVENTION The present invention relates to a material for packaging purposes, comprising a first layer of thermoplastic polymer, a second layer of thermoplastic polymer and an intermediate barrier layer in the form of a primer, wherein one and said first and other layers exhibit an oxygen permeability (OTR) greater than 6.0 and less than 45 cma / [m2 day atm] at 23 ° C, 50% relative humidity and on planar foil, said barrier layer in the form of primer on either of the layers contribute to said material exhibiting an OTR of less than 9.0 cma / [m2 day atm] and to said primer exhibiting adhesion to the non-primed layer and heat sealability to polyolefin and polyester systems.

Nämnda material är lämpligen ett flexibelt material i film- eller foliefomi som ' är användbart vid förpackning, t.ex. vid förpackning omfattande användning av svetsverktyg för försegling såsom värmebackar eller andra energiöverförande verktyg.Said material is suitably an ibexable material in mlm or foil form which is useful in packaging, e.g. in packaging comprising the use of welding tools for sealing such as heating jaws or other energy transfer tools.

Vidare kan nämnda första skikt, exempelvis, vara av amorf polyester, expanerad polyester eller orienterad polyamid. Nämnda första skikt kan vara ett skikt som är termoformningsbart eller värmeresístent.Furthermore, said first layer may, for example, be of amorphous polyester, expanded polyester or oriented polyamide. Said first layer may be a layer which is thermoformable or heat resistant.

Nämnda andra skikt kan, exempelvis, vara av polyeten eller polypropen som är lämpligt då värmeförseglingsbarhet mot polyolefin-system önskas, och ha en tjocklek av 20 till 80 um. Är nämnda andra skikt värmeförseglingsbart, kan nämnda andra skikt såsom andra värmeförseglingsbara skikt värrneförseglas till ett objekt exempelvis genom användning av svetsverktyg såsom värmebackar. Nämnda objekt är, tex., av samma material som nämnda första skikt, exempelvis, amorf polyester. Polyolefin-system kan innefatta, exempelvis, polyeten (PE) eller polypropen (PP). Då nämnda andra skikt är av polyeten kan det även ge en ”peeP-effekt, vilket innebär att förpackningar innefattande denna ”peeP-effekt kan rivas upp. 000 0 00 00 00 00 0 0 0 0 0 0 0 0 O O I l 000 0 0 0 0 0 0 0 00 0000 00 0000 000 10 15 20 25 30 innefattar en Barriärskiktskompositionen i form av en primer adhesionskomponent samt en barriärkomponent.Said second layer may, for example, be of polyethylene or polypropylene which is suitable when heat sealability against polyolefin systems is desired, and have a thickness of 20 to 80 μm. If said second layer is heat-sealable, said second layer such as other heat-sealable layers can be heat-sealed to an object, for example by using welding tools such as heat jaws. Said object is, for example, of the same material as said first layer, for example, amorphous polyester. Polyole fi n systems may include, for example, polyethylene (PE) or polypropylene (PP). As said second layer is of polyethylene, it can also give a "peeP effect, which means that packages comprising this" peeP effect can be torn up. A barrier layer composition in the form of a primer adhesion component and a barrier component.

Vidare uppvisar nämnda första skikt en syrgasperrneabilitet (OTR) som är större än 6,0 och mindre än 45 cma l[m2 dag atm] vid 23° C, 50% relativ luftfuktighet och på plan folie, vilket tillsammans med nämnda barriärskikt bidrar till att det färdiga materialet uppvisar en OTR som är mindre än 9,0 cma I [m2 dag atm].Furthermore, said first layer exhibits an oxygen permeability (OTR) greater than 6.0 and less than 45 cma l [m2 day atm] at 23 ° C, 50% relative humidity and on flat foil, which together with said barrier layer contributes to the finished material has an OTR of less than 9.0 cma I [m2 day atm].

Nämnda barriärskikt verkar som en barriär för gas- och/eller ånga. Det har visats sig att nämnda barriärskikt effektivt har kunnat bildats på nämnda första eller andra skikt genom behandlingen med en barriärskiktskomposition i form av en primer. Därigenom har genom nämnda material mängden komponenter i det färdiga materialet samt antalet maskinoperationer vid dess tillverkning minskat i jämförelse med tidigare kända likvärdiga material. Med "mängden" menas här mängd enligt gängse betydelse, men här kan också "mängden" mena antal. Vidare menas här med komponenter allt som ingår i det färdiga materialet enligt föreliggande uppfinning och i varje specifikt tidigare känt likvärdigt material. I För har även nämnda material mängden övrigt genom tillverkningskomponenter samt antal tillverkningssteg som ingär i framställningen av nämnda material minskat i jämförelse med vad som ingår i framställning av tidigare kända material. Här är ”mängden” definierad som tidigare och ”tillverkningskomponenter” definierade som ”komponenter” tidigare men som ingående i tillverkningen av materialet istället. Genom valet i nämnda material av specifika termoplastiska polymerer som tillverkningskomponenter för nämnda första skikt, varvid nämnda första skikt uppvisar en syrgaspermeabilitet (OTR) som är större än 6,0 och mindre än 45 cma /[m2 dag atm], har en perfekt balans uppnåtts mellan graden av syrgasbarriär i det första skiktet och förekomst av små områden som saknar primer i nämnda barriärskikt. Dessa kan liknas vid ”pinho|es' i barriärskiktet, 10 15 20 25 30 527 531 vilka minskar barriärskiktet barriäregenskaper, uppkommer då barriärskiktet bildas pà det första eller andra skiktet. Perfekt balans innebär här att syrgaspermeabiliteten (OTR) hos nämnda första skikt tillsammans med förekomsten av "pinho|es” i nämnda barriärskikt ger ett försumbart bidrag till nämnda materials syrgaspermeabilitet (OTR), samtidigt som dyrare tillverkningskomponenter med ännu lägre syrgaspermeabilitet (OTR) för tillverkning av det första skiktet har kunnat undvikas. Med andra ord har tillverkningskomponenter som har "lagom bra" barriäregenskaper valts för nämnda första skikt.Said barrier layer acts as a barrier for gas and / or vapor. It has been found that said barrier layer has been effectively formed on said first or second layer by the treatment with a barrier layer composition in the form of a primer. As a result, through said material, the amount of components in the finished material as well as the number of machine operations in its manufacture has decreased in comparison with previously known equivalent materials. By "quantity" is meant here quantity according to the usual meaning, but here "quantity" can also mean number. Furthermore, by components is meant everything that is included in the finished material according to the present invention and in any specific previously known equivalent material. In For, the said material has also the amount otherwise through manufacturing components and the number of manufacturing steps that are included in the production of said material has decreased in comparison with what is included in the production of previously known materials. Here, “quantity” is defined as before and “manufacturing components” are defined as “components” previously but as part of the manufacture of the material instead. By the choice in said material of specific thermoplastic polymers as manufacturing components for said first layer, said first layer having an oxygen permeability (OTR) greater than 6.0 and less than 45 cma / [m2 day atm], a perfect balance has been achieved between the degree of oxygen barrier in the first layer and the presence of small areas lacking primer in said barrier layer. These can be likened to 'pinholes' in the barrier layer, which reduce the barrier layer barrier properties, arising when the barrier layer is formed on the first or second layer. Perfect balance here means that the oxygen permeability (OTR) of said first layer together with the presence of "pinho | es" in said barrier layer makes a negligible contribution to said oxygen permeability (OTR) of said material, while more expensive manufacturing components with even lower oxygen permeability (OTR) for manufacturing In other words, manufacturing components having "reasonably good" barrier properties have been selected for said first layer.

Syrgaspermeabiliteten (OTR) hos nämnda första skikt är t.ex. cirka 18 cma/lmz dag atm] som hos amorf eller expanderad polyester, och ”pinholes” utgör cirka 10 % av nämnda barriärskikt. Således blir det bidrag som nämnda första skikts syrgaspermeabilitet (OTR) tillsammans med nämnda barriärskikts ”pinholes” ger till nämnda materials syrgaspermeabilitet (OTR) i ett material enligt föreliggande uppfinning cirka _1,8 cm° l[m2 dag atm]. Om polypropen, som har en syrgaspermeabilitet (OTR) pà cirka 2500 cma/[mz dag atm], istället skulle användas i det första skiktet blir motsvarande bidrag cirka 250 cma/[mz dag atm], vilket ger ett material med dåliga barriäregenskaper. Alltså om tillverkningskomponenter, orienterad PET eller orienterad polypropylen (PP), som har för hög syrgaspermeabilitet (OTR) skulle väljas för nämnda första skikt i ett material för förpackningsändamàl, så skulle ett material med en OTR som är mycket hög, dvs betydligt större än 9,0 cm: /[m2 dag atm], erhållas. t.ex.The oxygen permeability (OTR) of said first layer is e.g. about 18 cma / lmz day atm] as in amorphous or expanded polyester, and "pinholes" make up about 10% of said barrier layer. Thus, the contribution that said first layer oxygen permeability (OTR) together with said barrier layer "pinholes" makes to the oxygen permeability (OTR) of said material in a material according to the present invention is about _1.8 cm ° l [m2 day atm]. If polypropylene, which has an oxygen permeability (OTR) of about 2500 cma / [mz day atm], were instead used in the first layer, the corresponding contribution would be about 250 cma / [mz day atm], which gives a material with poor barrier properties. Thus, if manufacturing components, oriented PET or oriented polypropylene (PP), which have too high oxygen permeability (OTR) were to be selected for said first layer in a material for packaging purposes, then a material with an OTR which is very high, i.e. significantly greater than 9 .0 cm: / [m2 day atm], obtained. for example

Vidare har det också visats sig att nämnda material enligt föreliggande uppfinning går att framställa i ett steg, och därvid kan man med mycket enkla medel erhålla ett material med ett lågt OTR. Nämnda material även visats sig ha egenskaper som gör att materialet lämpars sig för svetsning, exempelvis vid förpackning medelst materialet.Furthermore, it has also been found that said material according to the present invention can be produced in one step, and in this case a material with a low OTR can be obtained with very simple means. Said material has also been found to have properties which make the material suitable for welding, for example when packaging by means of the material.

M... ....._..___...._..__._,. 10 15 20 25 30 -527 531 Med ett material enligt föreliggande uppfinning har överraskande för första gången ett material för förpackningsändamàl erhållits som i ett och samma alla de ovan beskrivna fördelaktiga material innehar, eller medför, egenskaperna, dvs att nämnda första skikt uppvisar ”lagom bra" barriäregenskaper, dvs en syrgaspermeabilitet (OTR) som är större än 6,0 och mindre än 45 cm3 /Imz dag atm] vid 23° C, 50 % relativ luftfuktighet och på plan folie, och att nämnda barriärskikt bidrar till att nämnda material uppvisar en OTR som är mindre än 9,0 oma l[m2 dag atm], minskning av mängden komponenter, tillverkningskomponenter, och antal arbetsoperationer eller tillverkningssteg som ingår i dess framställning, värmeförseglingsbarhet mot polyolefin-system, samt lämplighet för att bearbetas med svetsning.M ... ....._..___...._..__._ ,. With a material according to the present invention, surprisingly for the first time a material for packaging purposes has been obtained which in one and all of the above-described advantageous materials possesses, or entails, the properties, i.e. that said first layer exhibits "adequate good "barrier properties, ie an oxygen permeability (OTR) greater than 6.0 and less than 45 cm3 / Imz day atm] at 23 ° C, 50% relative humidity and on flat foil, and that said barrier layer contributes to said material exhibits an OTR that is less than 9.0 oma l [m2 day atm], reduction in the amount of components, manufacturing components, and number of work operations or manufacturing steps involved in its manufacture, heat sealability to polyolefine systems, and suitability for machining by welding.

Att nämnda första skikts OTR är mindre än 45 cm3 /[m2 dag atm], vilket innebär att det i sig självt uppvisar relativt bra barriäregenskaper, är nödvändigt för att erhålla ett material med nämnda barriärskikt framställt pà nämnda första eller andra skikt, varvid materialet har en OTR som är mindre än 9,0 cma/[mz dag atm]. Om nämnda första skikt istället uppvisar alltför dåliga barriäregenskaper, dvs skikt med en OTR som ofta är betydligt större än 45 cms l[m2 dag atm], erhålls dä material med barriärskikt vilka material har en OTR som ofta är betydligt större än 9,0 cma l[m2 dag atm]. Material som har en OTR som är större än 9,0 cm° l[m2 dag atm] uppvisar prestanda som är otillräckliga vid mànga förpackningsändamâl.That the first OTR of said first layer is less than 45 cm 3 / [m2 day atm], which means that it in itself exhibits relatively good barrier properties, is necessary to obtain a material with said barrier layer produced on said first or second layer, the material having an OTR less than 9.0 cma / [mz day atm]. If said first layer instead exhibits too poor barrier properties, ie layers with an OTR which is often significantly larger than 45 cm 2 [m2 day atm], then materials with barrier layers are obtained which materials have an OTR which is often significantly larger than 9.0 cm l [m2 day atm]. Materials having an OTR greater than 9.0 cm ° l [m2 day atm] exhibit performance that is insufficient for many packaging purposes.

I föreliggande uppfinning beräknas nämnda materials OTR enligt: 1/( materialets OTR)=1/( första skiktets OTR)+1/(barriärskiktets OTR) j I n I' "g an: nu! 0' 'g . . . .'. . .. g - Ü . o n 0 0 ' ; u o n I ' ' g a a. nu 00 OI Il to 000: 0A c 0 I i u n o 0 o 0 n a u a n o I O n o oo nova 0000 Oc In n I 10 15 20 25 I ett ytterligare utförande avses ett material för förpackningsändamål enligt föreliggande uppfinning, varvid det ena av nämnda första och andra skikt uppvisar en syrgaspermeabilitet (OTR) som är större än 10 och mindre än 30 cm” /[m2 dag atm] vid 23° C, 50% relativ luftfuktighet och pà plan folie.In the present invention, the OTR of said material is calculated according to: 1 / (OTR of the material) = 1 / (OTR of the first layer) + 1 / (OTR of the barrier layer) j I n I '"g an: nu! 0' 'g...' g .. Ü. on 0 0 '; uon I' 'ga a. nu 00 OI Il to 000: 0A c 0 I iuno 0 o 0 nauano IO no oo nova 0000 Oc In n I 10 15 20 25 I a further embodiment refers to a material for packaging purposes according to the present invention, wherein one of said first and second layers has an oxygen permeability (OTR) greater than 10 and less than 30 cm 2 / [m2 day atm] at 23 ° C, 50 % relative humidity and on flat foil.

Ett ytterligare utförande enligt föreliggande uppfinning avser ett material, varvid nämnda material uppvisar en OTR som är mindre än 8,0 cms l[m2 dag atm]. l en utföringsform enligt föreliggande uppfinning avses ett material, varvid nämnda primerbehandlade skikt är av amorf polyester, och nämnda primerbehandlade skikt kan då, exempelvis, ha en tjocklek som ligger i ett intervall fràn 90 till 800 um. l en ytterligare utföringsform enligt föreliggande uppfinning avses ett material, varvid nämnda primerbehandlade skikt är av expanderad polyester, och nämnda primerbehandlade skikt kan då, exempelvis, ha en tjocklek som ligger i ett intervall från 300 till 1000 pm.A further embodiment according to the present invention relates to a material, wherein said material has an OTR which is less than 8.0 cm 2 [m2 day atm]. In an embodiment according to the present invention, a material is referred to, wherein said primer-treated layer is of amorphous polyester, and said primer-treated layer can then, for example, have a thickness which is in a range from 90 to 800 μm. In a further embodiment according to the present invention is meant a material, wherein said primer-treated layers are of expanded polyester, and said primer-treated layers can then, for example, have a thickness which is in a range from 300 to 1000 μm.

Ytterligare en utföringsform enligt föreliggande uppfinning avser ett material, varvid nämnda primerbehandlade skikt är av orienterad polyamid, och nämnda primerbehandlade skikt kan då, exempelvis, ha en tjocklek som ligger i ett intervall fràn 8 till 100 pm.A further embodiment according to the present invention relates to a material, wherein said primer-treated layers are of oriented polyamide, and said primer-treated layers can then, for example, have a thickness which is in a range from 8 to 100 μm.

Ett ytterligare utförande enligt föreliggande uppfinning avser ett material, varvid nämnda icke-primerbehandlade skikt är av polyeten, polypropen eller polyester.A further embodiment according to the present invention relates to a material, wherein said non-primer-treated layers are of polyethylene, polypropylene or polyester.

OOOO O' O I O I I I I 0 0 a 000 0 00 0000 000 0 0 0 0 0 0 0 0 0 0 I 0 OI III! OO ÛOIO COD IIOI OI 10 15 20 25 30 Ännu ett ytterligare utförande enligt föreliggande uppfinning avser ett material, varvid nämnda icke-primerbehandlade skikt har en tjocklek som ligger i ett intervall frän 20 till 80 pm.OOOO O 'O I O I I I I I I 0 0 a 000 0 00 0000 000 0 0 0 0 0 0 0 0 0 0 0 I 0 OI III! Yet another embodiment of the present invention relates to a material, said non-primer-treated layers having a thickness ranging from 20 to 80 microns.

Vidare avser föreliggande uppfinning ett förfarande för framställning av ett material som här har beskrivits, varvid nämnda förfarande innefattar bildande av nämnda första skikt samt nämnda andra skikt med konventionell teknik och därefter bildande av nämnda barriärskikt på nämnda första skikt eller andra skikt genom behandling av nämnda första eller andra skikt med nämnda primer, varvid det första och andra skiktet lamineras till varandra med barriärskiktet mellanliggande.The present invention further relates to a method of making a material as described herein, said method comprising forming said first layer and said second layer by conventional techniques and then forming said barrier layer on said first layer or second layers by treating said first layer. or second layer with said primer, the first and second layers being laminated to each other with the barrier layer intermediate.

Ett ytterligare utförande enligt föreliggande uppfinning avser ett förfarande varvid nämnda behandling innefattar ett primerverk. Primerverket kan innefatta en tryckvals, och barriärprimerkompositionen kan, t.ex., vara vattenlöslig och/eller löslig i alkohol.A further embodiment according to the present invention relates to a method wherein said treatment comprises a primer. The primer may comprise a pressure roller, and the barrier primer composition may, for example, be water-soluble and / or soluble in alcohol.

Föreliggande uppfinning avser även ett förfarande för att förpacka, varvid ett material som här har beskrivits användes för nämnda förfarande.The present invention also relates to a method of packaging, wherein a material as described herein is used for said method.

Vidare kan nämnda förfarande för att förpacka med nämnda material innefatta, exempelvis, termoformning, värmeförsegllng mot kompatibelt material, t.ex., ett förpackningstråg, svetsning och/eller liknande.Furthermore, said method of packaging with said material may comprise, for example, thermoforming, heat sealing against compatible material, for example, a packaging tray, welding and / or the like.

UTFÖRINGSEXEMPEL Exemgel 1 Tillverkning av ett material för förpackningsändamál, omfattande ett första skikt av amorf polyester, ett andra skikt av polyeten, och ett barriärskikt i form av en primer mellan nämnda första och andra skikt oo o o oo o o o n o o oono o o o o n o o n oo oooo oon oooo on oo o o o o o o o o oo oooo 10 15 20 25 30 Först bildas ett första skikt med en tjocklek på 300 pm av amorf polyester med konventionell teknik och därefter bildas ett barriärskikt på det första skiktet genom behandling av det första skiktet med en primer innefattande en adhesionskomponent och en barriärkomponent. Därefter bildas ett andra skikt med en tjocklek på 40 pm av polyeten med konventionell teknik, varvid det andra skiktet lamineras på barriärskiktet.EMBODIMENT EXAMPLE 1 Manufacture of a packaging end material, comprising a first layer of amorphous polyester, a second layer of polyethylene, and a barrier layer in the form of a primer between said first and second layers oo oo oo ooonoo oono oooonoon oo oooo oon oooo on oo First, a first layer having a thickness of 300 μm is formed of amorphous polyester by conventional techniques, and then a barrier layer is formed on the first layer by treating the first layer with a primer comprising an adhesion component and a barrier component. Then a second layer with a thickness of 40 μm is formed of polyethylene by conventional technique, the second layer being laminated on the barrier layer.

Exempel 2 Tillverkning av ett material för förpackningsändamål, omfattande ett första skikt av expanderad polyester, ett andra skikt av polyeten, och ett barriärskikt i form av en primer mellan nämnda första och andra _ skikt Materialet i Exempel 2 tillverkades på samma sätt som materialet i Exempel 1 med skillnaden att här har det första skiktet en tjocklek på 800 um och är av expanderad polyester.Example 2 Manufacture of a material for packaging purposes, comprising a first layer of expanded polyester, a second layer of polyethylene, and a barrier layer in the form of a primer between said first and second layers. The material of Example 2 was manufactured in the same way as the material of Example 1 with the difference that here the first layer has a thickness of 800 μm and is of expanded polyester.

Exemgl 3 fillverkning av ett material för förpackningsändamál, omfattande ett första skikt av orienterad polyamid, ett andra skikt av polyeten, och ett barriärskikt i form av en primer mellan nämnda första och andra skikt Materialet i Exempel 3 tillverkades pà samma sätt som materialet i Exempel 1 med skillnaden att här har det första skiktet en tjocklek på 12 pm och är av orienterad polyamid.Example 3 Effect of a packaging end material comprising a first layer of oriented polyamide, a second layer of polyethylene, and a barrier layer in the form of a primer between said first and second layers The material of Example 3 was made in the same manner as the material of Example 1. with the difference that here the first layer has a thickness of 12 μm and is of oriented polyamide.

Claims (13)

10 15 20 25 30 527 531 PATENTKRAV10 15 20 25 30 527 531 PATENT REQUIREMENTS 1. Material för förpackningsändamál, omfattande ett första skikt av termoplastisk polymer, ett andra skikt av termoplastisk polymer och ett mellanliggande barriärskikt i form av en primer, k ä n n e t e c k n at a v att det ena av nämnda första och andra skikt uppvisar en syrgaspermeabilitet (OTR) som är större än 6,0 och mindre än 45 cm° l[m2 dag atm] vid 23° C, 50% relativ luftfuktighet och pä plan folie, att nämnda barriärskikt i form av primer pà endera av skikten bidrar till att nämnda material uppvisar en OTR som är mindre än 9,0 cm3 /[m2 dag atm] och att nämnda primer uppvisar adhesion mot det icke primerbehandlade skiktet och vämieförseglingsbarhet mot polyolefin-system och polyeestersystem.Packaging end material, comprising a first layer of thermoplastic polymer, a second layer of thermoplastic polymer and an intermediate barrier layer in the form of a primer, characterized in that one of said first and second layers exhibits an oxygen permeability (OTR) which is greater than 6.0 and less than 45 cm ° l [m2 day atm] at 23 ° C, 50% relative humidity and on flat foil, that said barrier layer in the form of primer on either of the layers contributes to said material having an OTR of less than 9.0 cm 3 / [m2 day atm] and that said primer exhibits adhesion to the non-primer treated layer and heat sealability to polyolefin and polyester systems. 2. Material enligt patentkrav 1, k ä n n e t e c k n at a v att nämnda material uppvisar en OTR som är mindre än 8,0 cma llmz dag atm].Material according to claim 1, characterized in that said material has an OTR which is less than 8.0 cma llmz day atm]. 3. Material enligt något av patentkrav 1 till 2, k ä n n e t eckn at av att nämnda primerbehandlade skikt är av amorf polyester.Material according to any one of claims 1 to 2, characterized in that said primer-treated layer is of amorphous polyester. 4. Material enligt patentkrav 3, k ä n n e t e c k n a t a v att nämnda primerbehandlade skikt har en tjocklek som ligger i ett intervallfrän 90 till 800 pm.Material according to claim 3, characterized in that said primer-treated layer has a thickness which is in a range from 90 to 800 μm. 5. Material enligt något av patentkrav 1 till 2, k ä n n ete ck n at a v att nämnda primerbehandlade skikt är av expanderad polyester.Material according to any one of claims 1 to 2, characterized in that said primer-treated layer is of expanded polyester. 6. Material enligt patentkrav 5, k ä n n e t e c k n at a v att nämnda primerbehandlade skikt har en tjocklek som ligger i ett intervall från 300 till 1000 um. 10 15 20 25 527 531 10Material according to claim 5, characterized in that said primer-treated layer has a thickness which is in a range from 300 to 1000 μm. 10 15 20 25 527 531 10 7. Material enligt något av patentkrav 1 till 2, k ä n n et e ck n at a v att nämnda primerbehandlade skikt är av orienterad polyamid.Material according to any one of claims 1 to 2, characterized in that said primer-treated layer is of oriented polyamide. 8. Material enligt patentkrav 7, k ä n n e t e c k n at a v att nämnda primerbehandlade skikt har en tjocklek som ligger i ett intervall frân 8 till 100 LLITI.Material according to claim 7, characterized in that said primer-treated layers have a thickness ranging from 8 to 100 LLITI. 9. Material enligt något av föregående patentkrav, k ä n n e t e c k n at a v att nämnda icke-primerbehandlade skikt är av polyeten, polypropen eller polyester.9. A material according to any one of the preceding claims, characterized in that said non-primer treated layers are of polyethylene, polypropylene or polyester. 10. Material enligt patentkrav 9, k ä n n et e c k n at a v att nämnda icke- primerbehandlade skikt har en tjocklek som ligger i ett intervall från 20 till 80 pm.10. A material according to claim 9, characterized in that said non-primer treated layer has a thickness ranging from 20 to 80 μm. 11. Förfarande för framställning av ett material enligt något av föregående patentkrav, k ä n n e t e c k n at a v att nämnda förfarande innefattar bildande av nämnda första skikt samt nämnda andra skikt med konventionell teknik och därefter bildande av nämnda barriärskikt på nämnda första skikt eller andra skikt genom behandling av nämnda första eller andra skikt med nämnda primer, varvid det första och andra skiktet lamineras till varandra med barriärskiktet mellanliggande.A method of making a material according to any one of the preceding claims, characterized in that said method comprises forming said first layer and said second layer by conventional techniques and then forming said barrier layer on said first layer or second layer by treatment. of said first or second layer with said primer, the first and second layers being laminated to each other with the barrier layer intermediate. 12. Förfarande enligt patentkrav 11, k ä n n e t e c k n at a v att nämnda behandling innefattar ett primerverk.A method according to claim 11, characterized in that said treatment comprises a primer. 13. Förfarande för att förpacka, k ä n n e t e c k n at a v att ett material enligt något av patentkrav 1 till 10 användes för nämnda förfarande.13. A method of packaging, characterized in that a material according to any one of claims 1 to 10 is used for said method.
SE0202528A 2002-08-28 2002-08-28 Materials for packaging purposes, process for making the material and packaging process SE527531C2 (en)