SE425729B - COATING FOR ROADS, STREETS AND OPENING AND / OR PUBLIC PLACES AND PROCEDURES FOR THE PRODUCTION OF THEMSELVES - Google Patents
COATING FOR ROADS, STREETS AND OPENING AND / OR PUBLIC PLACES AND PROCEDURES FOR THE PRODUCTION OF THEMSELVESInfo
- Publication number
- SE425729B SE425729B SE7706969A SE7706969A SE425729B SE 425729 B SE425729 B SE 425729B SE 7706969 A SE7706969 A SE 7706969A SE 7706969 A SE7706969 A SE 7706969A SE 425729 B SE425729 B SE 425729B
- Authority
- SE
- Sweden
- Prior art keywords
- furnace slag
- blast furnace
- weight
- finely ground
- coating
- Prior art date
Description
15 20 25 30 35 7106969-3 Den uppfinningsenliga beläggningen kan på vanligt sätt antingen an- ' bringas direkt på marken i form av ett genomgående skikt eller komma till användning i Form av stenar, plattor, tegel eller liknande Form- stenar, som exempelvis Formas i fabriker till sådant formande föremål vilka på sedvanligt sätt läggs ut på förbrukningsstället exempelvis i sand eller betong. The coating according to the invention can in the usual way either be applied directly to the ground in the form of a continuous layer or be used in the form of stones, tiles, bricks or similar molding stones, such as Forms. in factories for such forming objects which are laid out in the usual way at the place of consumption, for example in sand or concrete.
Den uppfinningsenliga-beläggningen innefattar finmald, granulerad * masugnsslagg som uppvisar hydrauliska egenskaper och som tjänar såsom bindemedel med en tillsats av alkaliska och/eller sulfatiska hårdhets- framkallare såsom kalk, jordalkalisulfot, alkali- eller jordalkali- klorid samt ett ballastmaterial såsom kristallin masugnsslagg, maka- dam, grus eller sprängsten. Beläggningen kännetecknas av en halt av 0,5 till 10 vikts -% av filterstoft som till övervägande del består av järnoxider. Fördelaktiga utföringsformer är beskrivna i underan- språken. K I följande beskrivning hänför sig alla uppgifter till vikts4% av den torra, färdiga, hydrauliskt bindande blandningen med undantag av uppgifterna i % För material med en kornstorlek under 0,075 mm, vilka bara häntär sig till det givna materialet.The coating according to the invention comprises finely ground, granulated blast furnace slag which exhibits hydraulic properties and which serves as a binder with an addition of alkaline and / or sulphate hardness developers such as lime, alkaline earth sulphate, alkali or alkaline earth metal chloride and a ballast material such as crystalline blast furnace slag, dam, gravel or blasted stone. The coating is characterized by a content of 0.5 to 10% by weight of filter dust which consists predominantly of iron oxides. Advantageous embodiments are described in the sub-claims. K In the following description, all data refers to weight 4% of the dry, finished, hydraulically binding mixture with the exception of the data in% For materials with a grain size of less than 0.075 mm, which only apply to the given material.
Vid framställning av stål erhålls stora mängder av masugnsslagger som hittills redan använts för olika ändamål, t ex för framställning av stenar för stenanläggningar eller, i krossad form, såsom tillsats- material vid vägbyggande (se DIN-norm 4301). Denna mqsugnsslagg ef- hålls antingen i form av normalt kyld d v s en kristallin masugns- slagg s k hyttsten, eller den kan granuleras till s k hyttsand, d v s överföras till granulatform genom påsprutning med vatten. Normalt kyld, kristallin masugnsslagg besitter inga bindningsegenskaper och kan genom uppfinningen användas såsom tillsatsmaterial eller I bal- last. Detta sker efter krossning till den brukliga kornstorleken för erhållande av ett tillsatsmaterial eller en ballast såsom det är känt på Fackområdet för framställning av beläggning och speciellt av gatu- beläggning. Den krossade, kristallina masugnsslaggen kan sålunda upp-D visa en harmonisk kornfördelning eller en kornfärdelning i enlighet med en Fuller-kurva, d v s en sådan kornfärdelning att den ännu inte med vatten uppblandade hydrauliskt bindande blandningen uppvisar en sådan kornfärdelning. Denna tillämpning beträffande kornstorleksfär- delningen gäller naturligtvis också vid användande av andra material som tillsatsmaterial eller ballast. Som sådana andra tillsats- eller ballastmaterial kan nämnas grus, makadam, sprängsten m m, som används 10 15 20 25 30 35 7706969-8 för övrigt även för framställning av vägbeläggningar. Vid belägg- ningar med en inte allt för hög stabilitet kan man även använda fina material innehållande grus, makadam eller sten, t ex med inblandningar av lera.In the production of steel, large quantities of blast furnace slag are obtained that have hitherto already been used for various purposes, for example for the production of stones for stone plants or, in crushed form, as additives in road construction (see DIN standard 4301). This blast furnace slag is maintained either in the form of normally cooled, i.e. a crystalline blast furnace slag, so-called cab stone, or it can be granulated into so-called cab sand, i.e. transferred to granular form by spraying with water. Normally cooled, crystalline blast furnace slag has no bonding properties and can be used by the invention as an additive material or in ballast. This is done after crushing to the usual grain size to obtain an additive material or a ballast as is known in the art for the production of pavement and especially of street pavement. The crushed, crystalline blast furnace slag can thus show a harmonious grain distribution or a grain distribution according to a Fuller curve, i.e. such a grain distribution that the hydraulically binding mixture not yet mixed with water has such a grain distribution. This application regarding grain size distribution naturally also applies to the use of other materials such as additives or aggregates. As such other additive or aggregate materials may be mentioned gravel, macadam, blasted stone, etc., which are also used for the production of road surfaces. For coatings with a not too high stability, you can also use fine materials containing gravel, macadam or stone, for example with mixtures of clay.
Filterstoftet utgörs av det vid stålframstöllníng i avgasfiltren erhållna materialet vilket till största delen består av jörnoxider.The filter dust consists of the material obtained during steel production in the exhaust filters, which for the most part consists of iron oxides.
Detta stoft är sålunda en avfallsprodukt, som hittills icke kommit till någon väsentlig användning. Då filtermaterialet förutom den större andelen av järnoxid innehåller även andra beståndsdelar, vilka avsevärt försvårar den metallurgiska värderingen, lagrades detta mate- rial f n som slagg på slaggtippar. Överraskande nog har man nu funnit att den uppfinningsenliga beläggningens hållfasthet kan förstärkas genom tillsats av sådant filtermaterial. Det är vidare möjligt att vid vissa, fördelaktiga utföringsformer enligt uppfinningen till- sätta ännu en jordalkalisulfat till den hydrauliskt bindande bland- ningen, i synnerhet kalciumsulfat d v s gips. Även härigenom uppnås en förbättring av hållfasthetsegenskaperna. Slutligen är det fördel- aktigt att som ett ytterligare speciellt bíndemedel tillsätta alkali- eller jordalkaliklorider, när specifika tillsats- eller ballastmate- rial kommer till användning. Som exempel på sådana klorider kan nämnas kalciumklorid, magnesiumklorid, natriumklorid o s v. Den härvid till- satta mängden uppgår till 0,1 - 5 % företrädesvis 0,5 - 2 %.This substance is thus a waste product which has not hitherto come to any essential use. As the filter material, in addition to the larger proportion of iron oxide, also contains other constituents, which considerably complicate the metallurgical valuation, this material is currently stored as slag on slag tips. Surprisingly, it has now been found that the strength of the coating according to the invention can be enhanced by the addition of such filter material. It is further possible in certain, advantageous embodiments according to the invention to add another alkaline earth sulphate to the hydraulically binding mixture, in particular calcium sulphate, i.e. gypsum. This also achieves an improvement in the strength properties. Finally, it is advantageous to add alkali or alkaline earth chlorides as an additional special binder, when specific additive or aggregate materials are used. Examples of such chlorides are calcium chloride, magnesium chloride, sodium chloride, etc. The amount added here amounts to 0.1 - 5%, preferably 0.5 - 2%.
De i de uppfinningsenliga beläggningarna använda, finkrossade, granulerade masugnsslaggerna, framställs av s k hyttsand d v s av granulerade masugnsslagger, somipå ett i och för sig känt sött fram- ställs genom granulering av smältflytande masugnsslagger med hjälp av vatten. Sådana granulerade masugnsslagger besitter latenta hydraul- iska egenskaper och mals exempelvis till slaggoement tillsammans med cementklinker eller andra tillsatser. Överraskande nog har man funnit att man även kan använda malda granulerade masugnsslagger d v s hytt- sand, på ett gynnsamt sätt såsom hydrauliskt bindande medel för gatu- belüggningar utan sådana tillsatser.The finely crushed, granulated blast furnace slag used in the coatings according to the invention is produced from so-called cab sand, i.e. from granulated blast furnace slag, as a sweet known per se is produced by granulating melt-flowing blast furnace slag with the aid of water. Such granulated blast furnace slag possesses latent hydraulic properties and is ground, for example, into slag elements together with cement clinker or other additives. Surprisingly, it has been found that it is also possible to use ground granulated blast furnace slag, i.e. cab sand, in a favorable manner as a hydraulically binding agent for street coatings without such additives.
Det är av stor betydelse att minst 2 % av den finmalda, granule- rade masugnsslaggen uppvisar en karnstorlek under 0,075 mm d v s att den granulerade masugnsslaggen mals så att minst 2 % går igenom ett såll med en maskvidd av 0,075 mm. Den översta gränsen för andelar med en en kornstorlek under 0,075 mm ligger ur tekniska och ekonomiska synpunkter vid ca 30 %. Naturligtvis vore det också möjligt att an- vända malda, granulerade masugnsslagger med ännu högre halter av 7706969- 8 10 15 20 25 30 -35 4 karnstorlekar under 0,075 mm, men det har visat 'sig vara tillräck- ligt att dessa halter alltid används när vissa minsta halter av en kornstorlek under 0,075 mm av den malda, granulerade masugnsslaggen föreligger beroende på den använda tillsatsen eller ballasten och de önskade hållfasthetsegenskaperna. Så har man exempelvis funnit att, vid användande av krossade, kristallina masugnsslagger såsom till- satsmaterial eller ballast, den minsta halten av den finmalda, granu- lerade masungsslaggen med en kornstorlek under 0,075 mm uppgår till -2 %, I sådana fall är det i allmänhet inte nödvändigt att mer än ca 10 % av en sådan finandel av den fínmalda granulerade masugnsslaggen ingår i blandningen. _ I Vid användningen av krossad sten, grus, makadam eller sprängsten som tillsatsmaterial eller ballast skall minimumhalten av den fin- malda, granulerade mosugnsslaggen med en kornstorlek under 0,075 mm ligga vid 10 % varvid den övre gränsen befinner sig vid ca 20 %. Vid användningen av krossad sten, grus, makadam eller sprängsten med bi- blandningar av lera av olika slag som tillsatsmateríal eller ballast, skall minimumhalten av den finmalda, granulerade masugnsslaggen med en kornstorlek under 0,075 ligga vid 20 % varvid den övre gränsen be- finner sig vid ca.28 %.It is of great importance that at least 2% of the finely ground, granulated blast furnace slag has a core size below 0.075 mm, i.e. that the granulated blast furnace slag is ground so that at least 2% passes through a sieve with a mesh size of 0.075 mm. The upper limit for proportions with a grain size below 0.075 mm is from a technical and economic point of view at about 30%. Of course, it would also be possible to use ground, granulated blast furnace slag with even higher contents of 7706969- 8 10 15 20 25 30 -35 4 core sizes below 0.075 mm, but it has been found to be sufficient that these contents are always used when certain minimum contents of a grain size below 0.075 mm of the ground, granulated blast furnace slag are present depending on the additive or ballast used and the desired strength properties. For example, when using crushed crystalline blast furnace slag as an additive or aggregate, it has been found that the minimum content of the finely ground, granulated blast furnace slag with a grain size below 0.075 mm is -2%. It is generally not necessary for more than about 10% of such a fine fraction of the finely ground granulated blast furnace slag to be included in the mixture. When using crushed stone, gravel, macadam or blasted stone as additive or aggregate, the minimum content of the finely ground, granulated blast furnace slag with a grain size of less than 0.075 mm should be 10%, the upper limit being about 20%. When using crushed stone, gravel, macadam or blasted stone with admixtures of clay of various kinds as additive material or aggregate, the minimum content of the finely ground, granulated blast furnace slag with a grain size below 0.075 shall be at 20% with the upper limit being at about 28%.
En del av den finmalda, granulerade masugnsslaggen med den rådande halten av finkrossat material som uppvisar en kornstorlek under 0,075 mm kan enligt uppfinningen ersättas av krossade, granulerade kupol- K ugnsslagger, med samma halt av material med en kornstorlek under 0,075 mm som gällde för masugnsslaggerna. Ett fördelaktigt område för tillsats av finmald kupolugnsslagger ligger mellan 5 och 15 % , varvid halten av kupolugnsslaggerna står i förhållande till masugns- slaggerna såsom 3:2 till 1:5 samt i synnerhet 3:2 till 2:3.According to the invention, a part of the finely ground, granulated blast furnace slag with the prevailing content of finely crushed material having a grain size below 0.075 mm can be replaced by crushed, granulated dome kiln slag, with the same content of material with a grain size below 0.075 mm as applied to the blast furnace slag . An advantageous range for the addition of finely ground dome furnace slag is between 5 and 15%, the content of the dome furnace slag being in proportion to the blast furnace slag such as 3: 2 to 1: 5 and in particular 3: 2 to 2: 3.
Den uppfinningsenliga beläggningen kan genom ändringar i till- satserna uppvisa skiljaktiga egenskapsvärden. På detta sätt upp- kommer en stor rad användningsmöjligheter speciellt genom anpass- ning av det befintliga tillöggsmaterialet eller ballasten.The coating according to the invention can exhibit different property values due to changes in the additives. In this way, a large number of possibilities of use arise, especially by adapting the existing additional material or ballast.
Den uppfinningsenliga beläggningen kan exempelvis uppdelas i- följande 3 typer: ' ILLl ' s e En direkt applicerbar ytbeläggning vilken i regel ej är i behov av något speciellt täckskikt då belastbarheten uppgår till ca 120 kg/cm2, innehåller såsom tillsatsmaterial eller ballast krossad, kristallin masugnsslagg och såsom bindemedel finmald, granulerad masugnsslagg 5 10 15 20 25 30 35 7706969-8 samt finmald, granulerad kupolugnsslagg i förhållandet 3:2, varvid minst 2 % av den finmalda, granulerade masugnsslaggen och kupolugns- slaggen går igenom ett såll med en maskvidd av 0,075 mm. Vidare inne- håller denna beläggning en mindre mängd av såväl kalk som filterstoft.The coating according to the invention can be divided, for example, into the following 3 types: 'ILL1' see A directly applicable surface coating which as a rule does not require any special cover layer when the load capacity amounts to about 120 kg / cm2, contains as filler material or ballast crushed, crystalline blast furnace slag and as a binder finely ground, granulated blast furnace slag 5 10 15 20 25 30 35 7706969-8 and finely ground, granulated dome furnace slag in the ratio 3: 2, wherein at least 2% of the finely ground, granulated blast furnace slag and the dome furnace slag pass through a sieve with a mesh size of 0.075 mm. Furthermore, this coating contains a small amount of both lime and filter dust.
DLLÉ i Denna beläggning innehåller tillsatsmaterial såsom grus, makadam, sprängsten o s v samt såsom hydrauliskt bindemedel Finmald, granu- lerad masugnsslagg med en halt av minst 10 % med en kornstorlek under 0,075 mm. Vidare innehåller beläggningen finmald eller krossad gips samt kalk och filtermaterial. Hållfastheten ligger vid 50 - 60 kg/cmz.DLLÉ i This coating contains additive materials such as gravel, macadam, blasted stone, etc. and as hydraulic binder Finmald, granulated blast furnace slag with a content of at least 10% with a grain size below 0.075 mm. Furthermore, the coating contains finely ground or crushed gypsum as well as lime and filter material. The strength is at 50 - 60 kg / cmz.
MJ Denna beläggning som exempelvis kan användas på landsvägar innehåller såsom tillsatsmaterial eller ballast grus, sten samt leror av olika slag, vidare finmald granulerad masugnsslagg med minst 20 % med en kornstorlek under 0,075 mm samt kalk, gips, filtermaterial och alkali- eller jordalkaliklorider. Hållfastheten ligger vid ca 30 - 40 kg/cm2.MJ This coating that can be used on country roads, for example, contains as an additive or aggregate gravel, stone and clays of various kinds, further finely ground granulated blast furnace slag with at least 20% with a grain size below 0.075 mm and lime, gypsum, filter material and alkali or alkaline earth chlorides. The strength is at about 30 - 40 kg / cm2.
Beläggningarna i typ 2 och 3 kan användas för grundstabilisering.The coatings in types 2 and 3 can be used for basic stabilization.
En beläggning av typ 3 borde förses med en ytbeläggning av t ex as- falt.A type 3 coating should be provided with a surface coating of eg asphalt.
Uppfinningen kommer att beskrivas närmare i de följande exemplen.The invention will be described in more detail in the following examples.
Exemgel 1 En torr blandning bestående av 69 % krossad, kristallin, masungsslagg med sedvanlig kornfördelníng, 1 % kalk som aktivator, 5 % filterstoft, 15 % finmald, granulerad masugnsslagg varvid minst 2 % har en korn- storlek under 0,075 mm samt 10 % finkrossad, granulerad kupolugns- slagg med likaledes 2 % med en kornstorlek under 0,075 mm. Dessa material blandas i torrt tillstånd i ett sedvanligt blandníngsverk för gatubeläggningar, varefter inblandas den erforderliga vatten- mängden, vilken kan fastställas genom enkla försök. Blandningen an- vänds därefter antíngen som en kontinuerlig vägbeläggning med efter- följande påvalsning eller bearbetning med vibratorer eller den formas på känt sätt till plattor med dimensionerna 50 x 50 x 8 cm. Såväl väg- beläggningen som plattorna uppvisade en hållfasthet av ca 120 kg/cm2.Example gel 1 A dry mixture consisting of 69% crushed, crystalline, mash slag with the usual grain distribution, 1% lime as activator, 5% filter dust, 15% finely ground, granulated blast furnace slag with at least 2% having a grain size below 0.075 mm and 10% finely crushed , granulated dome furnace slag of also 2% with a grain size below 0.075 mm. These materials are mixed in the dry state in a conventional street paving mixer, after which the required amount of water is mixed in, which can be determined by simple experiments. The mixture is then used either as a continuous pavement with subsequent rolling or machining with vibrators or it is formed in a known manner into plates with the dimensions 50 x 50 x 8 cm. Both the pavement and the tiles showed a strength of about 120 kg / cm2.
Ett täckskikt av exempelvis asfalt var ej nödvändigt.A cover layer of asphalt, for example, was not necessary.
Exempel 2 För gatubeläggning framställdes en blandning av 85 % makadam med sedvanlig kornstorleksfördelning med en vattenhalt av 5 - 10 %, 1,5 % kalk, 0,75 % filtermaterial, 1,5 % gips, 11,25 % finmald granulerad masugnsslagg som hade en halt av 10 % med en kornstorlek under 0,075 mm. 10 15 20 25 27706969- 8 , 67 U Detta material blandades i en för vägbeläggning normal blandare med den erforderliga vättenmängden till en hydrauliskt bindande belägg- ningsblandning och lades ut i form av en genomgående beläggning på den för ändamålet preparerade väggrunden. Denna beläggning hade en belastbarhet av ca 60 kg/cm2. P g a detta var det fördelaktigt att förse beläggningen med ett bituminäst överskíkt.Example 2 For street paving, a mixture of 85% macadam with the usual grain size distribution with a water content of 5 - 10%, 1.5% lime, 0.75% filter material, 1.5% gypsum, 11.25% finely ground granulated blast furnace slag was prepared which had a content of 10% with a grain size below 0.075 mm. 27706969- 8, 67 U This material was mixed in a mixer normal for road paving with the required amount of water to form a hydraulically binding paving mixture and laid out in the form of a continuous coating on the wall base prepared for the purpose. This coating had a load capacity of about 60 kg / cm2. Due to this, it was advantageous to provide the coating with a bituminous overlay.
Exempel 3 En beläggning framställdes fär vilken man använde material från en gammal landsväg innehållande lera och lerhaltigt grus eller makadam.Example 3 A coating was prepared for which material from an old country road containing clay and clayey gravel or macadam was used.
Den gamla vägbeläggníngen krossades och användes som tillsatsmaterial. 85 % av det gamla vägbeläggningsmaterialet, vilket hade en vatten- half mellan 5 _ 10 %, 1,5 % kalk, 0,75 % filterstoff, 1,51% finkmssud gips och 0,25 % CaCl2 samt 10 % fínmald, granulerad masugnsslagg, av vilken 20 % hade en kornstorlek under 0,075 %, blandades på förbruk- ningsstället med den erforderliga vattenmängden till en hydrauliskt bindande blandning och användes såsom beläggning på den gamla vägen.The old pavement was crushed and used as an additive. 85% of the old paving material, which had a water half between 5 - 10%, 1.5% lime, 0.75% filter material, 1.51% fine-grained gypsum and 0.25% CaCl2 and 10% finely ground, granulated blast furnace slag , of which 20% had a grain size below 0.075%, was mixed at the point of consumption with the required amount of water to a hydraulically binding mixture and used as a coating on the old road.
Belastbarheten uppgick till 35 kg/cm2. I anslutning härtill lades som täckskikt ett asfaltskikt.The load capacity was 35 kg / cm2. In connection with this, an asphalt layer was laid as a cover layer.
Företrädesvis fås en gynnsam kornfördelning i tillsatsmaterialet genom att detta består av olika andelar av flera siktfraktioner. T_ex kan tillsatsmaterialet bestå till 35 % av en siktfraktion med en korndiameter av O - 2 mm, till 12 % av en siktfraktion med en korn- diameter av 2 - 5 mm, till 16 % av en siktfraktion med en korndiameter av 5 - 8 mm, till 12 % av en siktfraktion med en korndiameter av 8 - 11 mm, till 13 % av en siktfraktion med en korndiameter av 11 - 16 mm, samt till 12 % av en siktfraktion med en korndiameter av 16 - 22 mm.Preferably, a favorable grain distribution is obtained in the additive material in that it consists of different proportions of several sieve fractions. For example, the additive material may consist of 35% of a sieve fraction with a grain diameter of 0 - 2 mm, of 12% of a sieve fraction with a grain diameter of 2 - 5 mm, of 16% of a sieve fraction with a grain diameter of 5 - 8 mm , to 12% of a sieve fraction with a grain diameter of 8 - 11 mm, to 13% of a sieve fraction with a grain diameter of 11 - 16 mm, and to 12% of a sieve fraction with a grain diameter of 16 - 22 mm.
Claims (6)