SA115370057B1 - كتلة بناء رغوة/ بلاطة متكاملة - Google Patents
كتلة بناء رغوة/ بلاطة متكاملة Download PDFInfo
- Publication number
- SA115370057B1 SA115370057B1 SA115370057A SA115370057A SA115370057B1 SA 115370057 B1 SA115370057 B1 SA 115370057B1 SA 115370057 A SA115370057 A SA 115370057A SA 115370057 A SA115370057 A SA 115370057A SA 115370057 B1 SA115370057 B1 SA 115370057B1
- Authority
- SA
- Saudi Arabia
- Prior art keywords
- foam
- layer
- geopolymer
- sodium silicate
- hydrogen peroxide
- Prior art date
Abstract
تشمل كتلة بناء بوليمر هندسي geopolymer وحدة نمطية مزدوجة متكاملة integral dual module رغوة داخلية للعزل وسطح بلاطة مكثف خارجي على الجانب الخارجي للوحدة النمطية module لرغوة داخلية للحماية من الطقس. تشمل الوحدة النمطية module المسامية الخارجية عجينة بوليمر هندسي geopolymer متضمنة رقائق سليكات الصوديوم sodium silicate وهيدروكسيد الصوديوم sodium hydroxide مذابة في سليكات الصوديوم sodium silicate لتشكيل محلول تنشيط وإضافة صلصال كاولين kaolin متكلس إلى محلول تنشيط لتشكيل عجينة. طبقة بلاطة كثيفة نسبيا أولى لها سمك حوالي 0.5 إلى 1.5 سم. تشكل طبقة بوليمر هندسي geopolymer ثانية مصنوعة من كتلة ثانية من عجينة مخلوطة مع فوق أكسيد الهيدروجين hydrogen peroxide رغوة بوليمر هندسي geopolymer لها سُمك حوالي 5 سم و15 سم. شكل 1.
Description
— \ — ABS بناء رغوة/ بلاطة متكاملة AN integral tile/foam building block الوصف الكامل خلفية الاختراع يتعلق هذا الاختراع بكتلة بناء بوليمر هندسي كتلة oly رغوة/ بلاطة متكاملة integral geopolymer building block 1116/1080 وطريقة لصنع ABS رغوة/ بلاطة بوليمر هندسي وتحديدا أكثر بكتلة رخغوة/ بلاطة مع بناء بلاط كثيف للحماية من الطقس وبناء رغوة داخلي للعزل. ° يتضمن نموذجيا عزل الجدار الخارجي تثبيت طبقة من مادة عازلة للجدار وتغطيتها بجبس أو تكسية. هذا يوفر نظام من طبقتين؛ واحدة للعزل والأخرى للحماية من الطقس. تتبع هذه الطرق أيضا للعزل الحراري للجدران الموجودة. تستعمل طريقة إضافية للعزل طبقتين من جدران كتلة مجوفة وتكون طبقة داخلية من الجدار سميكة نسبياء في Jie هذه الترتيبات؛ يتم فصل الطبقتين بواسطة طبقة عزل حراري. Va أنظمة الطبقتان مكلفة ومستهلكة للوقت. بالإضافة إلى هذاء ارتباط الطبقات يتطلب حرص لمنع الانفصال. طبقا لذلك» هناك عدد من الأساليب لإيجاد طريقة أكثر كفاءة وأقل تكلفة لتحسين العزل وبناء الجدار. على سبيل المثال؛ تكشف براءة الاختراع الأمريكية المنسوبة إلى Motaki et al رقم: 419719548 عن تركيبات عازلة للحرارة ALE لتكوين الرغوة المحتوية على سليكات قلوية Alkali Silicate وأسمنت ألومينا Cement 000108ل. كما تم الكشف عن عملية لتصنيع sale ٠ عازلة للحرارة غير عضوية بواسطة خلط سليكات قلوية قابل للذوبان في co Lal أسمنت ألوميناء قاعدة فلزية » عامل رغوي وعامل تثبيت 353 في حالة عجينة في وجود ماء. تُصنّع sale عازلة للحرارة بواسطة هذه العملية وتكون مفيدة لجدران عازلة للحرارة لمباني وألواح عازلة تندمج في مجال الآلات. تتعلق براءة الاختراع الأمريكية الأكثر حداثة رقم: 771360449 المنسوبة إلى Faulkner et al ٠ بنظام تسقيف تغطية متباعد وطريقة لتثبيته. يوضع النظام والطريقة لكسوة السقف على oovy
ا صفوف شرائح متمركزة على العوارض الخشبية للسقف. ترتبط كسوة السقف باستخدام لاصق. يفضل أن يكون المكون الرابط لاصق بوليمر» يفضل أكثر بولي يورثان «polyurethane للالتصاق مع كسوة السقف. يفضل أن يرش اللاصق على السطح السفلي لكسوة السقف بينما يرش أيضا على الشرائط السميكة والعوارض الخشبية المدعمة للجمالون. يربط اللاصق المرشوش كسوة 0 السقف المجاورة ويربط أيضا كسوة السقف مع الشرائح السميكة معا لتشكيل بناء موحد. بصورة إضافية؛ تشكل طبقة اللاصق المرشوش طبقة Jie بينما تشكل أيضا حاجز ضد الماء. بغض النظر عما سبقء يُعتقد حاليا أن هناك حاجة للمادة العازلة من بلاط/ رغوة محسنة. يجب أن تكون هناك حاجة وسوق تجاري محتمل لأن النظام يوفر التكاليف والوقت للمقاولين وفي تشييد المباني. ٠ الوصف العام للاختراع في الحقيقة؛ يدرس الاختراع الحالي كتلة بناء بوليمر هندسي وحدة نمطية مزدوجة متكاملة integral dual module geopolymer building block مصنوعة من وحدة نمطية رغوةٌ داخلية للعزل وسطح بلاط كثيف خارجي على الجانب الخارجي للوحدة النمطية الرغوية الداخلية للحماية من الطقس. الوحدة النمطية المزدوجة لها وحدة نمطية كثيفة خارجية مشتملة على عجينة Vo بوليمر هندسي متضمنة رقائق سليكات الصوديوم sodium silicate وهيدروكسيد الصوديوم hydroxide 5001000 مذابة في سليكات الصوديوم لتشكيل محلول تنشيط» وصلصال كاولين kaolin متكلس مخلوط مع محلول التنشيط لتشكيل كتلة عجينة بوليمر هندسي. تتشكل طبقة بلاطة كثيفة نسبيا أولى لها سمك حوالي ١,5 إلى ١,5 سم من ABS أولى من عجينة بوليمر هندسي. تصنع طبقة رغوة ثانية من عجينة بوليمر هندسي من كتلة ثانية من عجينة Yo بوليمر هندسي مع إضافة فوق أكسيد الهيدروجين .(H202) hydrogen peroxide يخلط 2 ببتركيز (AV مع عجينة بوليمر هندسي وتتفاوت من حوالي 70,5 إلى حوالي 77 بالوزن من عجينة بوليمر هندسي لتشكيل رغوة بوليمر هندسي لها سمك حوالي © سم إلى حوالي ٠5 سم. تعالج الوحدة النمطية بعدئذ عند حوالي aE لمدة ساعة واحدة وعند حوالي ٠ مثوية sad حوالي YY ساعة. oovy
— ¢ — سيتم وصف الاختراع الآن في اتصال مع الأشكال المرفقة. شرح مختصر للرسومات شكل ١ هو مخطط يوضح طريقة لصنع abs بناء بوليمر هندسي تركيبية مزدوجة متكاملة؛ و. 8 شكل ؟ هو توضيح تخطيطي لكتلة بناء بوليمر هندسي تركيبية مزدوجة متكاملة طبقا للاختراع. الوصف التفصيلى: يتضمن إنتاج كتلة بناء بوليمر هندسي تركيبية مزدوجة متكاملة استخدام صلصال ميتاكاولين metakaolin الذي يتكلس عند 60٠70”مثوية-806"مئوية sad حوالي ؟ ساعات. في A الخطوة المبدئية من صنع عجينة بوليمر هندسي alg توفير وخلط رقائق سليكات الصوديوم «(Na2SiO3) sodium silicate هيدروكسيد الصوديوم (NaOH) sodium hydroxide مذابة في سليكات الصوديوم وصلصال كاولين متكلس لتشكيل كتلة من عجينة بوليمر هندسي كما هو محدد في الخطوات NYS ٠١ ad عجينة بوليمر هندسي المتشكلة بذلك في الخطوة YY إلى مجموعتين. على سبيل (JB Vo الخطوة التالية 4 ١ مطلوبة لتشكيل طبقة كثيفة (DL) dense layer مصنوعة من عجينة بوليمر هندسي بينما في الخطوة 77 تصنع طبقة أكثر سمكا من رغوة بوليمر هندسي من خلط خطوة YE يمكن أن تسبق أو تلي الخطوة 776 بينما الخطوة YT يمكن أن تسبق أو تلي الخطوة ؟؛؟. في WK الحالتين» تتشكل وحدة نمطية مزدوجة مع رغوة طبقة سميكة نسبيا لعزل حوالي 0 YY إلى VO سم مع طبقة رقيقة نسبيا من بوليمر هندسي كثيف حوالي 0,8 إلى حوالي ٠,9 سم لمقاومة الطقس. لاا
Qo _ _ تعالج بعدئذ الوحدة النمطية من الخطوة YA عند حوالي ٠0 ؟”مثوية لمدة ساعة تقريبا وعند حوالي 860"مثئوية لمدة YY ساعة تقريبا في الخطوة Vo لإنتاج mite نهائي وهو ABS بناء رغوة/ بلاطة في الخطوة JV في المثال المذكور أعلاه؛ تركيبة أكسيد صلصال كاولين متكلس تكون كما يلي: 0 جدول :١ تركيبة أكسيد من كاولين الأكسيدات الموجود «,Yo calcium oxide (CaO) ثاني أكسيد السليكون 6,1٠ silicon dioxide (Si02) ¥1,A4 aluminum (1) (AI203) oxide أكسيد الحديد )1( «,Y4 iron (11 oxide (Fe203) 38 أكسيد الكبريت ١١ sulfur trioxide (SO3) أكسيد البوتاسيوم ١9 sovy
h —_ _ potassium oxide (K20) ثاني أكسيد التيتانيوم ١6 titanium dioxide (1102) ثلاثي أكسيد الفوسفورز vA phosphorus (P203) trioxide AS, A = Jay! فقد الاشتعال- ٠7 يتعلق الاختراع JEAN لغرض هذه المواصفة بتطوير رغوة- بلاطة بوليمر هندسي مقاومة للحرائق وبتكلفة قليلة؛ بوزن خفيف جديدة لعزل Shall والصوت بالإضافة إلى الحماية من الطقس للجدران الخارجية. تتبين بشكل واضح التفاصيل المميزة لهذا النظام الجديد في الوصف التالي وتتبع نفس © الإشارات المرجعية لتشير إليه. يتضمن إنتاج رغوة- بلاطة بوليمر هندسي استخدام ميتاكاولين ناتج من تكليس كاولين متاح محليا عند 6٠730١-800"مثوية لمدة ؟ ساعات تقريبا. ang تركيبة الأكسيد النموذجية من كاولين في جدول .١ ميتاكاولين الناتج يكون له محتوى سليكا silica عالي بنسبة جزيئية جرامية من 502 : 203 .Y , 1 Al معيار PRE ميتاكاولين لا يجب أن يكون أقل نقاوة من ta) ميكرون . ٠ مواد أخرى مستخدمة هي سليكات الصوديوم وهيدروكسيد الصوديوم. تتكون سليكات الصوديوم من Na20 7,4 5:02 7776 و1120 211,١ بنسبة وزن لأجل Na20/Si02 = حت ويستخدم ثقل نوعي عند a gia’ ٠١ = © آرا. يستخدم فوق أكسيد الهيدروجين لصنع جزء رغخوة من البلاطة. sovy
توجد تركيبة نموذجية من بوليمر هندسي في جدول WY يستخدم ANaOH شكل LS بنقاء JAY من أجل بوليمر هندسي رغوة؛ يضاف 77 (في نطاق: 71,5 إلى 77,5) من فوق أكسيد الهيدروجين بتركيز 775 إلى عجينة بوليمر هندسي.
يوصف الإجراء لإنتاج بوليمر هندسي فيما يلي:
° - رقائق هيدروكسيد الصوديوم المذابة في سليكات الصوديوم لتشكيل محلول منشط قلوي. - إضافة محلول منشط قلوي إلى ميتاكاولين. يؤدي هذا إلى تشكيل عجينة بوليمر هندسي. - لأجل جزء رغوة من رغوة-بلاطة بوليمر هندسي؛ يخلط فوق أكسيد الهيدروجين مع عجينة بوليمر هندسي أثناء الخلط لتشكيل بوليمر هندسي رغوي. Ve جدول ؟: تركيبة بوليمر هندسي المدى بالنسبة النسبة المئوية المادة المثوية المستخدمة ميتاكاولين $A o0o0—%0 سليكات الصوديوم (قلوي سائل 6 Liv أكسيد 0-6 لل الصوديوم (NaO) sodium oxide رقائق من هيدروكسيد الصوديوم A, 0 ١١-١ الإجمالي Vo
لا تتضمن تركيبة بوليمر هندسي إدراج أي تركيبات أسمنت تقليدية؛ مثل الأسمنت البورتلاندي العادي Ordinary Portland Cement يقلل بذلك انبعاث غاز الاحتباس الحراري (أي؛ ثاني أكسيد الكربون) وبالتالي حماية البيئة.
تنتج Sale بوليمر هندسي في المختبر باستخدام التركيبة المعطاة في جدول ١ واستخدام
7,3 الإجراء المذكور مسبقا. اكتشف أن مقاومة انضغاط البوليمر الهندسي لمدة 7 أيام هي Vo ام
A —_ _ ميجابإسكال بينما اكتشف أن مقاومة انضغاط رغوة بوليمر هندسي تتنوع من 0 إلى ١ ميجاباسكال مقابل الاختلاف في كمية فوق أكسيد الهيدروجين المتفاوتة من 70,5 إلى 77. كثافة بوليمر هندسي هي ١18 كجم/ Va بينم وجد أن كثافة رغوة بوليمر هندسي تتفاوت من 760 إلى ٠ 7 4 كجم/ Va . o الوزن التقريبي لبلاطة واحدة 719 YO سم يكون: sale - صلبة ١ سم ورخوة 2 Sp لالط كت FESS sal - صلبة ١ سم ورغوة VE سم: ٠,795 كجم تنتج رغوة- بلاطة بوليمر هندسي بواسطة صب طبقة من عجينة بوليمر هندسي لأجل طبقة صلبة يليها طبقة أخرى من عجينة بوليمر هندسي- رغوة لأجل الطبقة المسامية. يمكن ٠ تحديد sald) elds الصلبة والطبقات المسامية اعتمادا على متطلبات الحماية الحرارية. يبقى Sle الطبقة الصلبة عند حوالي cam ١ بينما يختلف الملمك النموذجي للطبقة المسامية من © إلى Vo سم اعتمادا على متطلبات العزل الحراري. من أجل dalled) يبقى بوليمر هندسي عند 460 "مئوية لمدة ساعة تقريبا ثم يبقى Ae die “مثوية لمدة YY ساعة إضافية. تكون البلاطة مستقرة الأبعاد وتوضح قوة تحمل على المدى الطويل بدون أي علامة على ١ تغيير الحجم أو تشوهات حتى في الظروف الجوية القاسية. يستخدم نظام العزل التقليدي طبقة من مادة عازلة Jie بوليستيرين polystyrene متمدد thermocol صوف معدني؛ رغوة بولي يورثان أو رغوة فينولية cphenolic foam التي يتم إدخالها في تجويف كتل مجوفة. هذا الأسلوب من العزل الحراري يترك جسور حرارية التي تجعله أقل فعالية في السيطرة على انتقال shall عبر الجدران. بينما استخدام سطح مستمر للعزل ٠ الحراري يتطلب الارتباط ليس فقط لاتصال طبقة العزل مع الجدار لكن أيضا لأجل اتصال بلاط خارجي مع الجدار. oovy
q —_ _ الرغوة هي جزء مركب من رغوة- بلاطة بوليمر هندسي؛ هناك ارتباط جيد بين المادتين الذي يكون بخلاف ذلك ضعيفا أو شبه معدوم في أنظمة من طبقتين تقليدية متكونة من عزل وطبقات حماية من الطقس. السطح المكشوف من البلاطة يكون له أي لون مرغوب تستخدم فيه إضافات اللون. يمكن © أن يكون للسطح المكشوف من البلاطة أيضا صقل أفضل وقوام مبهج باستخدام قوالب ذات نوعية جيدة واضافات في طبقة بوليمر هندسي الخارجية من بلاطة- رغوة بوليمر هندسي. تتحدد موصلية حرارية لطبقات صلبة ومسامية من البلاطة باستخدام موصلية حرارية بمقياس 6F ,0 و609١ وات/ متر لكل كيلو على التوالي. بذلك المقاومة الحرارية (قيمة (R لمادة صلبة سميكة ١ سم وطبقات رغوة © سم للبلاط تكون ١607 و9576 م؟ لكل كيلو/ وات على ٠ التوالي. يمكن أن تزداد المقاومة الحرارية لطبقة الرغوة من البلاط إلى ٠,١١ بزيادة مُمكها إلى ٠١ سم استخدام هذا البلاط على جدران خارجية يؤدي إلى توفير في الطاقة بنسبة 77١8 وهي غالبا نفس النسبة التي تحققت عند استخدام بوليستيرين المتمدد. بسبب استخدام بوليمر هندسي وخصوصا رغوة بوليمر هندسي؛ يتم توقع وجود معدل Yo مقاومة حرائق محسن وصوتيات أفضل للبلاط. يمكن أن ينتج البلاط طبقا للاختراع الحالي بأحجام مختلفة ells مختلف لمادة صلبة وطبقات رغوة اعتمادا على متطلبات المجال. من أجل اتصال البلاطة مع الجدارء يمكن استخدام طبقة من ملاط أسمنت تقليدي. Sl الملاط يكون حوالي Yo ملليمتر (شكل 7). يمكن أيضا استخدام مواد لاصقة أخرى Jie ملاط Yo إيبوكسي epoxy ملاط لاتكس latex أو ملاط أكريليكي 8017/116. لأجل بلاط أكثر (el بالإضافة إلى اللاصق؛ يمكن أيضا استخدام مرسى ميكانيكية من أجل اتصال مناسب للبلاط مع الجدار. oovy
“yam integral geopolymer building block بناء بوليمر هندسي متكاملة ABS تتضمن من عجينة Yo first or outer relatively thin layer طبقة رقيقة نسبيا أولى أو خارجية v4 بوليمر هندسي مكثفة مصنوعة من رقائق سليكات الصوديوم وهيدروكسيد الصوديوم مذابة في
PY سليكات الصوديوم وصلصال كاولين متكلس. تصنع طبقة عزل ثانية أو داخلية من الخطوة من رقائق سليكات الصوديوم وهيدروكسيد الصوديوم مذابة في سليكات الصوديوم وصلصال كاولين © سم إلى حوالي ١,5 متكلس وفوق أكسيد الهيدروجين. طبقة أولى من خطوة 75 لها سمك حوالي سم. VO حوالي © سم إلى clan لها ؟١7 second layer سم بينما الطبقة الثانية 58 خلال وصف الاختراع في اتصال مع تجسيدات مفضلة منه؛ يجب إدراك أنه يمكن عمل التغييرات والتعديلات هنا بدون الحيود عن نطاق عناصر الحماية الملحقة. oovy
Claims (1)
- -١١- عناصر الحماية من integral tile/foam building block طريقة لإنتاج كتلة بناء رغوة/ بلاطة متكاملة -١ تشمل الطريقة المذكورة: cgeopolymer عجينة بوليمر هندسي متكلس؛ kaolin من كتلة صلصال كاولين geopolymer عجينة بوليمر هندسي pig sodium hydroxide وهيدروكسيد الصوديوم sodium silicate رقائق من سليكات الصوديوم لتشكيل محلول تنشيط وخلط محلول تتشيط في sodium silicate مذابة في سليكات الصوديوم © tgeopolymer متكلس لتشكيل عجينة بوليمر هندسي kaolin صلصال كاولين hydrogen خلط كتلة عجينة بوليمر هندسي 118/ا0م9600 مع فوق أكسيد الهيدروجين 70,9 من حوالي hydrogen peroxide حيث يتفاوت فوق أكسيد الهيدروجين peroxide (H202) hydrogen peroxide بالوزن إلى حوالي 77 بالوزن من فوق أكسيد الهيدروجين Yo بتركيز ٠ إلى جانب geopolymer تصلب طبقة الرغوة؛ وإضافة طبقة من عجينة بوليمر هندسي واحد من الرغوة المتصلبة. من integral tile/foam building block طريقة لإنتاج كتلة بناء رغوة/ بلاطة متكاملة -" تتكون الطريقة المذكورة من: cgeopolymer عجينة بوليمر هندسي متكلس؛ kaolin من كتلة صلصال كاولين geopolymer عجينة بوليمر هندسي pig yo sodium hydroxide وهيدروكسيد الصوديوم sodium silicate رقائق من سليكات الصوديوم لتشكيل محلول تنشيط وخلط كتلة أولى من sodium silicate مذابة في سليكات الصوديوم متكلس ومحلول تنشيط لتشكيل كتلة من عجينة بوليمر هندسي kaolin صلصال كاولين ¢geopolymer سم من كتلة أولى ١,8 إلى ١,5 حوالي del تشكيل طبقة بلاطة مكثفة نسبيا أولى لها ١ tgeopolymer من عجينة بوليمر هندسي hydrogen نيجورديهلا خلط كتلة ثانية من عجينة بوليمر أرضي مع فوق أكسيد (H202) hydrogen peroxide حيث يتفاوت فوق أكسيد الهيدروجين (H202) peroxide (H202) hydrogen peroxide من حوالي 70,5 إلى 77 بالوزن من فوق أكسيد الهيدروجين tgeopolymer بتركيز 775 لتشكيل رغوة بوليمر هندسي Yo oovy“yy على الطبقة المكثفة حيث geopolymer تشكيل طبقة رغوة ثانية من )352 بوليمر هندسي عند geopolymer الطبقة المسامية بين © و5١ سم؛ وتعالج طبقة البوليمر الهندسي clas يكون ساعة لتشكيل طبقة بناء رغوة/ YY لمدة 350A حوالي 460 "مئوية لمدة ساعة تقريبا ثم عند .integral tile foam building block بلاطة متكاملة sovy_ \ Ad — LRT LA ] توفير وخلط NaOH¢ Na 8i0, 1° Meta Kaolins Ane ] YY ليمز هندسي 3 RCT EN TE ليج سن 25 HE ar IER Yio | عجينة تشكيل طبقة مكلفة AHO Bll (DL) . لتشكيل طبقة رغوة تشكيل وحدة نمطية | 0: . a ب > } Se االاسى... X A Aa $3 3a معالجة وهدة نمطلية — 2% هزدوجة 0 رغوة بلاطة aK ١ 7 ١ شكل oovyY ve 2 2 0 مكتف Meta Kaolin 76 Na,$10, | | قر إلى دا سم Meta Kaolin NaOH¢ Na, SiO, ض ) YY هوك 1 I 7 | | سيم ١8 إلى 8 0 و ,11.0 رغوة X ] 5 لمدة سريان هذه البراءة عشرون سنة من تاريخ إيداع الطلب وذلك بشرط تسديد المقابل المالي السنوي للبراءة وعدم بطلانها أو سقوطها لمخالفتها لأي من أحكام نظام براءات الاختراع والتصميمات التخطيطية للدارات المتكاملة والأصناف النباتية والنماذج الصناعية أو لائحته التنفيذية صادرة عن مدينة الملك عبدالعزيز للعلوم والتقنية ؛ مكتب البراءات السعودي ص ب TAT الرياض 57؟؟١١ ¢ المملكة العربية السعودية بريد الكتروني: patents @kacst.edu.sa