RU2629949C1 - Gear lubricant composition - Google Patents

Gear lubricant composition Download PDF

Info

Publication number
RU2629949C1
RU2629949C1 RU2016120813A RU2016120813A RU2629949C1 RU 2629949 C1 RU2629949 C1 RU 2629949C1 RU 2016120813 A RU2016120813 A RU 2016120813A RU 2016120813 A RU2016120813 A RU 2016120813A RU 2629949 C1 RU2629949 C1 RU 2629949C1
Authority
RU
Russia
Prior art keywords
additive
viscosity
syntolux
sulfur
phosphorus
Prior art date
Application number
RU2016120813A
Other languages
Russian (ru)
Inventor
Леонид Самойлович Яновский
Василий Михайлович Ежов
Александр Владимирович Карпов
Александр Александрович Молоканов
Раиса Михайловна Степанова
Ксения Вячеславовна Шаранина
Алексей Анатольевич Усанов
Николай Николаевич Шкилевич
Елена Валерьевна Малышева
Original Assignee
Федеральное государственное унитарное предприятие "Центральный институт авиационного моторостроения имени П.И. Баранова"
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Федеральное государственное унитарное предприятие "Центральный институт авиационного моторостроения имени П.И. Баранова" filed Critical Федеральное государственное унитарное предприятие "Центральный институт авиационного моторостроения имени П.И. Баранова"
Priority to RU2016120813A priority Critical patent/RU2629949C1/en
Application granted granted Critical
Publication of RU2629949C1 publication Critical patent/RU2629949C1/en

Abstract

FIELD: chemistry.
SUBSTANCE: gear lubricant composition comprises a base composition based on a polyalphaolefin oil comprising dibasic acid ester, a thickening additive and an additive package including antioxidant additives in the form of phenylalpha-naphthylamine and 4-methyl-2,6-di-tert-butylphenol, a sulfur-phosphorus-containing additive, and an antifoam additive. The composition as a base composition contains a mixture of polyalphaolefin oil Spectrasyn 10 with a viscosity of 10 mm2/s at 100°C with dibasic acid ester Syntolux L-439 with a viscosity of 3.9 mm2/s at 100°C and a thickening additive Syntolux V-7, which is a vinyl-alkyl polymer with a viscosity of 200 to 5000 mm2/s at 100°C, and additionally, the additive package additionally contains methylene-bis-(dibutyldithiocarbamate), a sulfur-containing additive Crumson 100M with a sulfur content of, at least, 16.0% and phosphorus of, at least, 1.2%, as well as an antifoam silicon additive polydimethylsiloxane PMS-200A.
EFFECT: lubricant composition according to the invention is characterized by a high value of flash point and solves the problem of improving the operational characteristics of a lubricant composition when used in heavy-duty aircraft gears throughout the range of operating temperatures.
2 tbl

Description

Изобретение относится к области смазочных композиций для трансмиссий летательных аппаратов, в частности для смазки трансмиссий вертолетов.The invention relates to the field of lubricating compositions for transmissions of aircraft, in particular for the lubrication of transmissions of helicopters.

Известна трансмиссионная смазочная композиция, которая содержит признаки, совпадающие с существенными признаками описываемого изобретения, а именно содержащая базовое масло и пакет присадок, включающий антиокислительные присадки в виде фенил-альфа-нафтиламина и 4-метил-2,6-ди-трет-бутилфенола, антипенную и антикоррозионную присадки (патент US №7829511). Известная смазочная композиция содержит органофосфитовые добавки, которые придают ей высокую коррозионную активность, поэтому эта композиция не может быть использована для смазки трансмиссии вертолетов.Known transmission lubricant composition, which contains signs that match the essential features of the described invention, namely containing a base oil and an additive package including antioxidant additives in the form of phenyl-alpha-naphthylamine and 4-methyl-2,6-di-tert-butylphenol, antifoam and anticorrosive additives (US patent No. 7829511). Known lubricating composition contains organophosphite additives that give it high corrosion activity, therefore, this composition cannot be used to lubricate the transmission of helicopters.

Известна трансмиссионная смазочная композиция, которая содержит признаки, совпадающие с существенными признаками описываемого изобретения, а именно содержащая базовый состав на основе углеводородного полиальфаолефинового масла и пакет присадок, включающий антиокислительные присадки в виде фенил-альфа-нафтиламина и 4-метил-2,6-ди-трет-бутилфенола, антипенную и антикоррозионную присадки (патент RU №2058379).Known transmission lubricant composition, which contains signs that match the essential features of the described invention, namely containing a basic composition based on hydrocarbon polyalphaolefin oil and an additive package including antioxidant additives in the form of phenyl-alpha-naphthylamine and 4-methyl-2,6-di tert-butylphenol, antifoam and anticorrosive additives (patent RU No. 2058379).

Известная композиция имеет недостаточно высокие трибологические свойства для использования ее в тяжелонагруженных трансмиссиях вертолетов.The known composition has insufficiently high tribological properties for use in heavily loaded transmissions of helicopters.

Известна трансмиссионная смазочная композиция, которая содержит признаки, совпадающие с существенными признаками описываемого изобретения, а именно содержащая базовый состав, включающий сложный эфир двухосновной кислоты Syntolux L-439 с вязкостью 3,9 мм2/с при 100°С, загущающую присадку Syntolux V, представляющую собой винилалкиловый полимер с вязкостью от 200 до 5000 мм2/с при 100°С, и пакет присадок, включающий антиокислительные присадки в виде фенил-альфа-нафтиламина и 4-метил-2,6-ди-трет-бутилфенола, антикоррозионную присадку и антипенную присадку (патент RU №2573829).Known transmission lubricant composition, which contains signs that match the essential features of the described invention, namely containing a base composition comprising a dibasic ester Syntolux L-439 with a viscosity of 3.9 mm 2 / s at 100 ° C, a thickening additive Syntolux V, which is a vinyl alkyl polymer with a viscosity of 200 to 5000 mm 2 / s at 100 ° C, and an additive package including antioxidant additives in the form of phenyl-alpha-naphthylamine and 4-methyl-2,6-di-tert-butylphenol, an anti-corrosion additive and antifoam additive (pa UNT RU №2573829).

В известной смазочной композиции в качестве основы базового масла используется минеральное масло с вязкостью от 2,0 до 6,0 мм2/с при 100°С, что способствует повышению коррозионной устойчивости и улучшению низкотемпературных характеристик смазочной композиции. Однако известная смазочная композиция обладает недостаточно высоким уровнем трибологических показателей и низкой температурой вспышки, что ограничивает возможность ее применения для трансмиссий вертолетов.In the known lubricating composition, mineral oil with a viscosity of 2.0 to 6.0 mm 2 / s at 100 ° C is used as the base of the base oil, which contributes to an increase in corrosion resistance and an improvement in the low temperature characteristics of the lubricant composition. However, the known lubricating composition has an insufficiently high level of tribological parameters and a low flash point, which limits the possibility of its use for helicopter transmissions.

Наиболее близким аналогом изобретения является трансмиссионная смазочная композиция для трансмиссий вертолетов, которая содержит признаки, совпадающие с существенными признаками описываемого изобретения, а именно содержащая базовый состав на основе полиальфаолефинового масла, включающий сложный эфир двухосновной кислоты, загущающую присадку и пакет присадок, включающий антиокислительные присадки в виде фенил-альфа-нафтиламина и 4-метил-2,6-ди-трет-бутилфенола, серуфосфоросодержащую присадку и антипенную присадку (патент RU №2122569).The closest analogue of the invention is a transmission lubricant composition for helicopter transmissions, which contains features that match the essential features of the described invention, namely, containing a base composition based on polyalphaolefin oil, including a dibasic acid ester, a thickening additive and an additive package including antioxidant additives in the form phenyl-alpha-naphthylamine and 4-methyl-2,6-di-tert-butylphenol, a phosphorus-containing additive and an antifoam additive (patent RU No. 2122569).

Известная смазочная композиция обладает достаточно высокими вязкостными, антикоррозионными и трибологическими свойствами для использования ее для смазки трансмиссий летательных аппаратов. Однако эта композиция обладает недостаточно высокой температурой вспышки, что ограничивает возможность ее применения в соответствии с условиями обеспечения безопасной работы трансмиссии.The known lubricating composition has a sufficiently high viscosity, anticorrosion and tribological properties for use in lubricating the transmissions of aircraft. However, this composition does not have a sufficiently high flash point, which limits the possibility of its use in accordance with the conditions for ensuring the safe operation of the transmission.

Технической проблемой, решаемой изобретением, является улучшение эксплуатационных характеристик смазочной композиции при использовании ее в тяжелонагруженных трансмиссиях летательных аппаратов.The technical problem solved by the invention is the improvement of the operational characteristics of the lubricating composition when used in heavily loaded transmissions of aircraft.

Техническим результатом изобретения является повышение температуры вспышки трансмиссионной смазочной композиции при сохранении ею высоких вязкостных, антикоррозионных и трибологических характеристик.The technical result of the invention is to increase the flash point of the transmission lubricating composition while maintaining high viscosity, anticorrosion and tribological characteristics.

Указанный результат достигается тем, что трансмиссионная смазочная композиция содержит базовый состав на основе полиальфаолефинового масла, включающий сложный эфир двухосновной кислоты, загущающую присадку и пакет присадок, включающий антиокислительные присадки в виде фенил-альфа-нафтиламина и 4-метил-2,6-ди-трет-бутилфенола, серофосфоросодержащую присадку и антипенную присадку. Согласно изобретению смазочная композиция в качестве базового состава содержит смесь полиальфаолефинового масла Spectrasyn 10 с вязкостью 10 мм2/с при 100°С со сложным эфиром двухосновной кислоты Syntolux L-439 с вязкостью 3,9 мм2/с при 100°С и загущающей присадкой Syntolux V-7, представляющей собой винилалкиловый полимер с вязкостью от 200 до 5000 мм2/с при 100°С, и, кроме этого, пакет присадок дополнительно содержит метилен-бис-(дибутилдитиокарбамат), серуфосфоросодержащую присадку Кримсон 100М с содержанием серы не менее 16,0% и фосфора не менее 1,2%, а также антипенную кремнийорганическую присадку полидиметилсилоксан ПМС-200А при следующем соотношении компонентов, мас.%:This result is achieved in that the transmission lubricating composition contains a base composition based on polyalphaolefin oil, including a dibasic acid ester, a thickening additive and an additive package including antioxidant additives in the form of phenyl-alpha-naphthylamine and 4-methyl-2,6-di tert-butylphenol, a phosphorus-containing additive and an antifoam additive. According to the invention, the lubricating composition as a base composition contains a mixture of Spectrasyn 10 polyalphaolefin oil with a viscosity of 10 mm 2 / s at 100 ° C with a dibasic ester of Syntolux L-439 with a viscosity of 3.9 mm 2 / s at 100 ° C and a thickening additive Syntolux V-7, which is a vinyl alkyl polymer with a viscosity of 200 to 5000 mm 2 / s at 100 ° C, and, in addition, the additive package additionally contains methylene bis- (dibutyl dithiocarbamate), a sulfur-containing additive, Crimson 100M, with a sulfur content of at least 16.0% and phosphorus at least 1.2%, as well as anti-foam w polydimethylsiloxane silicone additive ICP-200A with the following component ratio, wt.%:

4-метил-2,6-ди-третбутил-фенол4-methyl-2,6-di-tert-butyl-phenol 0,3-1,00.3-1.0 фенил-альфа-нафтиламинphenyl alpha naphthylamine 0,2-0,60.2-0.6 метилен-бис-(дибутилдитиокарбамат)methylene bis (dibutyl dithiocarbamate) 0,5-2,60.5-2.6 серуфосфоросодержащая присадка Кримсон 100МCrimson Sulfur Additive 100M 3,0-9,03.0-9.0 кремнийорганическая присадка ПМС-200Аorganosilicon additive PMS-200A 0,001-0,010.001-0.01 базовый составbase composition до 100up to 100

в том числеincluding

полиальфаолефиновое масло Spectrasyn 10Spectrasyn 10 polyalphaolefin oil 40-6040-60 сложный эфир двухосновной кислоты Syntolux L-439dibasic ester Syntolux L-439 20-3020-30 винилалкиловый полимер Syntolux V-7vinylalkyl polymer Syntolux V-7 20-3020-30

Технология приготовления смазочной композиции включает следующие этапы:The technology for preparing the lubricating composition includes the following steps:

- приготовление базового состава путем смешивания полиальфаолефинового масла Spectrasyn 10 по ТУ 38.1011136-87 с вязкостью 10 мм2/с при 100°С со сложным эфиром двухосновной кислоты Syntolux L-439 с вязкостью 3,9 мм2/с при 100°С при подогреве до 70°С и перемешивании;- preparation of the basic composition by mixing Spectrasyn 10 polyalphaolefin oil according to TU 38.1011136-87 with a viscosity of 10 mm 2 / s at 100 ° С with a dibasic ester of Syntolux L-439 with a viscosity of 3.9 mm 2 / s at 100 ° С when heated up to 70 ° C and with stirring;

- добавление загущающей присадки Syntolux V-7, представляющей собой винилалкиловый полимер с вязкостью от 200 до 5000 мм2/с при 100°С,- adding a thickening agent Syntolux V-7, which is a vinyl alkyl polymer with a viscosity of from 200 to 5000 mm 2 / s at 100 ° C,

- дозировка и добавление пакета присадок в базовый состав;- dosage and addition of the additive package to the base composition;

- перемешивание до полного растворения присадок при температуре 70-80°С;- mixing until complete dissolution of the additives at a temperature of 70-80 ° C;

- охлаждение и фильтрация полученной смазочной композиции.- cooling and filtering the resulting lubricant composition.

Для иллюстрации сущности изобретения были приготовлены два образца смазочной композиции, которые не должны толковаться как ограничивающие область изобретения (см. таблицу 1).To illustrate the essence of the invention, two samples of a lubricating composition were prepared, which should not be construed as limiting the scope of the invention (see table 1).

Figure 00000001
Figure 00000001

Для приготовления образцов использовались товарные сырьевые компоненты:For the preparation of samples used commodity raw materials:

- полиальфаолефиновое масло Spectrasyn 10 по ТУ 38.1011136-87 с вязкостью 10 мм2/с при 100°С;- Spectrasyn 10 polyalphaolefin oil according to TU 38.1011136-87 with a viscosity of 10 mm 2 / s at 100 ° C;

- сложный эфир двухосновной кислоты Syntolux L-439 по СТО 57175009-004-2015 с вязкостью 3,9 мм2/с при 100°С;- ester of dibasic acid Syntolux L-439 according to STO 57175009-004-2015 with a viscosity of 3.9 mm 2 / s at 100 ° C;

- загущающая присадка Syntolux V-7 по СТО 57175009-005-2011, представляющая собой винилалкиловый полимер с вязкостью от 200 до 5000 мм2/с при 100°С и молекулярной массой;- thickening additive Syntolux V-7 according to STO 57175009-005-2011, which is a vinyl alkyl polymer with a viscosity of 200 to 5000 mm 2 / s at 100 ° C and a molecular weight;

- антиокислительные присадки 4-метил-2,6-ди-трет-бутилфенол (Агидол-1) по ТУ 38.5901237-90 и Фенил-альфа-нафтиламин (Неозон А) по ТУ 6-14-202-74);- antioxidant additives 4-methyl-2,6-di-tert-butylphenol (Agidol-1) according to TU 38.5901237-90 and Phenyl-alpha-naphthylamine (Neozone A) according to TU 6-14-202-74);

- антиоксидантная присадка метилен-бис-(дибутилдитиокарбамат);- antioxidant additive methylene bis- (dibutyl dithiocarbamate);

- многофункциональная серуфосфоросодержащая присадка Кримсон 100М по ТУ 0257-004-52211396-2002;- multifunctional sulfur-phosphorus-containing additive Crimson 100M according to TU 0257-004-52211396-2002;

- антипенная присадка ПМС-200А, представляющая собой полидиметилсилоксановую жидкость по ОСТ 6-02-20-79.- antifoam additive PMS-200A, which is a polydimethylsiloxane liquid according to OST 6-02-20-79.

У этих образцов оценивали вязкостно-температурные характеристики и трибологические характеристики на четырехшариковой машине трения по ГОСТ 9490-75, а также измеряли содержание серы и температуру вспышки.The viscosity-temperature characteristics and tribological characteristics of the four-ball friction machine according to GOST 9490-75 were evaluated for these samples, and the sulfur content and flash point were measured.

Результаты испытаний опытных образцов смазочной композиции в сравнении с маслом по патенту RU №2122569 и ТС-гип, применяющимся для смазки трансмиссий вертолетов, приведены в таблице 2.The test results of the prototypes of the lubricating composition in comparison with the oil according to patent RU No. 2122569 and TC-gip, used for lubricating helicopter transmissions, are shown in table 2.

Figure 00000002
Figure 00000002

Из данных таблицы 2 следует, что предлагаемое трансмиссионное масло превосходит известные смазочные композиции по показателю температуры вспышки и не уступает по вязкостно-температурным и трибологическим характеристикам (критическая нагрузка, диаметр пятна износа), определенным при проведении испытаний по ГОСТ 9490-75.From the data of table 2 it follows that the proposed gear oil surpasses the known lubricating composition in terms of flash point and is not inferior in viscosity-temperature and tribological characteristics (critical load, wear spot diameter), determined during testing in accordance with GOST 9490-75.

Смазочная композиция согласно изобретению решает проблему улучшения эксплуатационных характеристик и повышения работоспособности при использовании ее в тяжелонагруженных трансмиссиях вертолетов во всем диапазоне эксплуатационных температур.The lubricating composition according to the invention solves the problem of improving performance and improving performance when used in heavy-duty transmissions of helicopters in the entire range of operating temperatures.

Claims (4)

Трансмиссионная смазочная композиция, содержащая базовый состав на основе полиальфаолефинового масла, включающий сложный эфир двухосновной кислоты, загущающую присадку и пакет присадок, включающий антиокислительные присадки в виде фенил-альфа-нафтиламина и 4-метил-2,6-ди-трет-бутилфенола, серуфосфоросодержащую присадку и антипенную присадку, отличающаяся тем, что в качестве базового состава содержит смесь полиальфаолефинового масла Spectrasyn 10 с вязкостью 10 мм2/с при 100°C со сложным эфиром двухосновной кислоты Syntolux L-439 с вязкостью 3,9 мм2/с при 100°C и загущающей присадкой Syntolux V-7, представляющей собой винилалкиловый полимер с вязкостью от 200 до 5000 мм2/с при 100°C, и, кроме этого, пакет присадок дополнительно содержит метилен-бис-(дибутилдитиокарбамат), серуфосфоросодержащую присадку Кримсон 100М с содержанием серы не менее 16,0% и фосфора не менее 1,2%, а также антипенную кремнийорганическую присадку полидиметилсилоксан ПМС-200А при следующем соотношении компонентов, мас.%:Transmission lubricating composition containing a base composition based on polyalphaolefin oil, including a dibasic acid ester, a thickening additive and an additive package including antioxidant additives in the form of phenyl-alpha-naphthylamine and 4-methyl-2,6-di-tert-butylphenol, sulfur-phosphorus-containing antifoam additive and the additive, characterized in that as the base composition comprises a mixture of polyalphaolefin oils Spectrasyn 10 having a viscosity of 10 mm 2 / s at 100 ° C with an ester of a dibasic acid Syntolux L-439 having a viscosity of 3.9 mm 2 / s When 100 ° C and thickening additive Syntolux V-7, which is a vinyl alkyl polymer having a viscosity of from 200 to 5000 mm 2 / s at 100 ° C, and, in addition, the additive package further comprises methylene-bis (dibutyldithiocarbamate), additive serufosforosoderzhaschuyu Crimson 100M with a sulfur content of at least 16.0% and phosphorus at least 1.2%, as well as an antifoam silicone additive polydimethylsiloxane PMS-200A in the following ratio, wt.%: 4-метил-2,6-ди-третбутил-фенол4-methyl-2,6-di-tert-butyl-phenol 0,3-1,00.3-1.0 фенил-альфа-нафтиламинphenyl alpha naphthylamine 0,2-0,60.2-0.6 метилен-бис-(дибутилдитиокарбамат)methylene bis (dibutyl dithiocarbamate) 0,5-2,60.5-2.6 серуфосфоросодержащая присадка Кримсон 100МCrimson Sulfur Additive 100M 3,0-9,03.0-9.0 кремнийорганическая присадка ПМС-200Аorganosilicon additive PMS-200A 0,001-0,010.001-0.01 базовый составbase composition до 100up to 100
в том числеincluding полиальфаолефиновое масло Spectrasyn 10Spectrasyn 10 polyalphaolefin oil 40-6040-60 сложный эфир двухосновной кислоты Syntolux L-439dibasic ester Syntolux L-439 20-3020-30 винилалкиловый полимер Syntolux V-7vinylalkyl polymer Syntolux V-7 20-3020-30
RU2016120813A 2016-05-27 2016-05-27 Gear lubricant composition RU2629949C1 (en)