RU2472619C1

RU2472619C1 - Method of making general mechanical rubber goods from elastomer compositions based on butadiene-nitrile rubber

Info

Publication number: RU2472619C1
Application number: RU2011133793/05A
Authority: RU
Inventors: Иван Соломонович Пятов; Юлия Ибремовна Врублевская; Олег Николаевич Шевердяев; Юлия Анатольевна Максимова; Татьяна Викторовна Бычкова; Владимир Дмитриевич Данилов
Original assignee: Иван Соломонович Пятов
Priority date: 2011-08-12
Filing date: 2011-08-12
Publication date: 2013-01-20

Abstract

FIELD: process engineering.

SUBSTANCE: invention relates to making general mechanical rubber goods from butadiene-nitrile rubber-base elastomer compositions and may be used in various industries. Proposed method comprises plasticising butadiene-nitrile rubber at rolls, adding vulcanisation activator, anti-ageing agent, powder filler, and plasticiser. Curing agent is introduced after mixing. Rubber mix is heated at rolls. Blanks are shaped to make rubber articles by hot forming at electrically heated vulcanising press. After mixing and prior to adding vulcanising agent, polyatomic spirit modifiers are introduced into rubber mix. Finished rubber article is additionally subjected to adsorption-absorption modification by curing finished product in liquid polyethylene oxide.

EFFECT: better mechanical properties.

3 cl, 2 tbl

Description

Изобретение относится к области производства резиновых изделий различного назначения, а именно к способу изготовления резинотехнических изделий из эластомерных композиций на основе бутадиен-нитрильного каучука, в том числе гидрированного, и может быть широко использовано в различных областях народного хозяйства.The invention relates to the production of rubber products for various purposes, and in particular to a method for manufacturing rubber products from elastomeric compositions based on nitrile butadiene rubber, including hydrogenated rubber, and can be widely used in various fields of national economy.

Известен способ изготовления резинотехнических изделий на основе бутадиен-нитрильного каучука, включающий пластикацию бутадиен-нитрильного каучука на вальцах, введение активатора вулканизации, противостарителя, порошкового наполнителя и пластификатора, введение после перемешивания вулканизующего агента, разогрев резиновой смеси на вальцах, профилирование заготовок с последующим изготовлением резинотехнических изделий методом прямого прессования на вулканизационном прессе с электрическим обогревом (см. Корнев А.Е., Буканов A.M., Шевердяев О.Н., Технология эластомерных материалов, НППА «Истек», Москва, 2009 г., с.267-325).A known method of manufacturing rubber products based on nitrile butadiene rubber, including mastication of nitrile butadiene rubber on rollers, the introduction of a vulcanization activator, antioxidant, powder filler and plasticizer, the introduction of a vulcanizing agent after mixing, heating the rubber mixture on the rollers, profiling rubber blanks with subsequent manufacturing rubber products by direct pressing on a vulcanizing press with electric heating (see Kornev A.E., Bukanov AM, She erdyaev ON, Technology elastomeric materials NPPA "expired", Moscow, 2009, s.267-325).

Однако известный способ изготовления резинотехнических изделий при своем использовании имеет следующие недостатки:However, the known method of manufacturing rubber products in its use has the following disadvantages:

не обеспечивает изготовление резинотехнических изделий на основе бутадиен-нитрильного каучука с высокими антифрикционными свойствами в процессе эксплуатационного трения по полированным металлическим поверхностям (коэффициент трения в процессе эксплуатационного трения по полированным металлическим поверхностям контр-тела составляет 0,23 при скорости вращения 1,74 м/с и 0,16 при скорости вращения 4,18 м/с).does not provide the manufacture of rubber products based on nitrile butadiene rubber with high antifriction properties during operational friction on polished metal surfaces (the friction coefficient during operational friction on polished metal surfaces of the counterbody is 0.23 at a speed of 1.74 m / s and 0.16 at a rotation speed of 4.18 m / s).

- не обеспечивает изготовление резинотехнических изделий на основе бутадиен-нитрильного каучука с высокой стабильностью коэффициента трения (0,66-0,72),- does not provide for the manufacture of rubber products based on nitrile butadiene rubber with high stability of the coefficient of friction (0.66-0.72),

- не обеспечивает изготовление резинотехнических изделий на основе бутадиен-нитрильного каучука с низким износом в процессе эксплуатационного трения по полированным металлическим поверхностям (износ при трении по полированным металлическим поверхностям контр-тела из высокопрочной стали составляет (5×10^-5мкм/км),- does not provide for the manufacture of rubber products based on nitrile butadiene rubber with low wear during operational friction on polished metal surfaces (wear during friction on the polished metal surfaces of the counterbody made of high-strength steel is (5 × 10 ^-5 μm / km),

- не всегда обеспечивает изготовление резинотехнических изделий на основе бутадиен-нитрильного каучука с минимальным моментом страгивания.- does not always ensure the manufacture of rubber products based on nitrile butadiene rubber with a minimum moment of breaking.

Задача изобретения - разработка способа изготовления резинотехнических изделий из эластомерных композиций на основе бутадиен-нитрильного каучука.The objective of the invention is the development of a method of manufacturing rubber products from elastomeric compositions based on nitrile butadiene rubber.

Техническим результатом является изготовление резинотехнических изделий на основе бутадиен-нитрильного каучука, в том числе гидрированного, с высокими антифрикционными свойствами в процессе эксплуатационного трения по полированным металлическим поверхностям контр-тела, в том числе снижение коэффициента трения и износа при трении по полированным металлическим поверхностям контр-тела из высокопрочной стали, а также повышение стабильности коэффициента трения. Кроме того, техническим результатом является изготовление резинотехнических изделий на основе бутадиен-нитрильного каучука, в том числе гидрированного, с минимальным моментом страгивания при одновременном сохранении условной прочности при растяжении, относительного удлинения, твердости по Шор А и температурного предела хрупкости.The technical result is the manufacture of rubber products based on nitrile butadiene rubber, including hydrogenated, with high antifriction properties in the process of operational friction on the polished metal surfaces of the counter body, including a decrease in the coefficient of friction and wear during friction on the polished metal surfaces of the counter bodies made of high strength steel, as well as increased stability of the coefficient of friction. In addition, the technical result is the manufacture of rubber products based on nitrile butadiene rubber, including hydrogenated rubber, with a minimum breaking moment while maintaining conditional tensile strength, elongation, Shore A hardness and brittle temperature limit.

Технический результат достигается в предложенном способе сочетанием использованных технологических параметров, последовательностью их выполнения в способе, а также количественными характеристиками выполнения технологических приемов.The technical result is achieved in the proposed method by a combination of the used technological parameters, the sequence of their implementation in the method, as well as quantitative characteristics of the implementation of technological methods.

Технический результат при осуществлении изобретения достигается тем, что предложен способ изготовления резинотехнических изделий из эластомерных композиций на основе бутадиен-нитрильного каучука, включающий пластикацию бутадиен-нитрильного каучука на вальцах, введение активатора вулканизации, противостарителя, порошкового наполнителя и пластификатора, введение после перемешивания вулканизующего агента, разогрев резиновой смеси на вальцах, профилирование заготовок с последующим изготовлением резинотехнических изделий методом прямого прессования на вулканизационном прессе с электрическим обогревом, при этом после выполнения перемешивания и перед введением вулканизующего агента в объем резиновой смеси на основе бутадиен-нитрильного каучука дополнительно вводят модификаторы - многоатомные спирты, в качестве которых используют поли-этиленоксид, полипропиленгликоль или смесь полиэтиленоксида с полипропиленгликолем, причем используют полиэтиленоксид с молекулярной массой 100-630, полиэтиленоксид с молекулярной массой 760-9000, смесь полиэтиленоксида с молекулярной массой 100-630 с полиэтиленоксидом с молекулярной массой 760-9000, полипропиленгликоль с молекулярной массой 150-4000 или смесь полиэтиленоксида с молекулярной массой 100-630 с полипропиленгликолем с молекулярной массой 150-4000, при этом количество вводимого в резиновую смесь модификатора выбрано от 0,5 до 8 мас. частей на 100 мас. частей бутадиен-нитрильного каучука, а готовое резинотехническое изделие дополнительно подвергают адсорбционно-абсорционной модификации выдерживанием готового резинотехнического изделия в жидком полиэтиленоксиде с молекулярной массой 100-2000 при температуре 115-200°С в течение 30-150 минут. При этом при выполнении объемной модификации резиновой смеси на основе бутадиен-нитрильного каучука используют смесь полиэтиленоксида с 10-45 мас.% полипропиленгликоля. При этом при выполнении объемной модификации резиновой смеси на основе бутадиен-нитрильного каучука используют смесь полиэтиленоксида с молекулярной массой 100-630 с 15-45 мас.% полиэтиленоксида с молекулярной массой 760-9000.The technical result in the implementation of the invention is achieved by the fact that the proposed method of manufacturing rubber products from elastomeric compositions based on nitrile butadiene rubber, including mastication of nitrile butadiene rubber on rollers, the introduction of a vulcanization activator, antioxidant, powder filler and plasticizer, the introduction after mixing of the vulcanizing agent, heating the rubber mixture on rollers, profiling blanks followed by the manufacture of rubber products by the method of direct pressing on a vulcanizing press with electric heating, and after mixing and before introducing a vulcanizing agent into the volume of the rubber mixture based on nitrile butadiene rubber, modifiers are additionally introduced - polyhydric alcohols, which use polyethylene oxide, polypropylene glycol or a mixture of polyethylene oxide with polypropylene glycol and using polyethylene oxide with a molecular weight of 100-630, polyethylene oxide with a molecular weight of 760-9000, a mixture of polyethylene oxide with molecular th mass of 100-630 with polyethylene oxide with a molecular weight of 760-9000, polypropylene glycol with a molecular weight of 150-4000 or a mixture of polyethylene oxide with a molecular weight of 100-630 with polypropylene glycol with a molecular weight of 150-4000, while the amount of modifier introduced into the rubber mixture is selected from 0 5 to 8 wt. parts per 100 wt. parts of nitrile butadiene rubber, and the finished rubber product is additionally subjected to adsorption-absorption modification by keeping the finished rubber product in liquid polyethylene oxide with a molecular weight of 100-2000 at a temperature of 115-200 ° C for 30-150 minutes. In this case, when performing bulk modification of a rubber mixture based on nitrile butadiene rubber, a mixture of polyethylene oxide with 10-45 wt.% Polypropylene glycol is used. Moreover, when performing bulk modification of a rubber mixture based on nitrile butadiene rubber, a mixture of polyethylene oxide with a molecular weight of 100-630 with 15-45 wt.% Polyethylene oxide with a molecular weight of 760-9000 is used.

Способ осуществляют следующим образом. В процессе изготовления эластомерных композиций на основе бутадиен-нитрильного каучука, в том числе гидрированного, для последующего изготовления резинотехнических изделий выполняют пластикацию бутадиен-нитрильного каучука на вальцах СМ 1500 в течение 10 минут. Затем загружают на вальцы на 100 мас.ч. бутадиен-нитрильного каучука 5 мас.ч. белил цинковых, 1 мас.ч. диафена ФП, 2 мас.ч. ацетонанила Р, 1 мас.ч. стеарина и перемешивают в течение 4-5 минут. Затем добавляют на 100 мас.ч. бутадиен-нитрильного каучука 120 мас.ч. технического углерода П-803 и 20 мас.ч. дибутилсебацината и перемешивают с подрезами в течение 12-14 минут. Затем в подготовленный объем резиновой смеси вводят модификаторы - многоатомные спирты, в качестве которых используют полиэтиленоксид, полипропиленгликоль или смесь полиэтиленоксида с полипропиленгликолем. При этом используют полиэтиленоксид с молекулярной массой 100-630, или полиэтиленоксид с молекулярной массой 760-9000, или смесь полиэтиленоксида с молекулярной массой 100-630 с 15-45 мас.% полиэтиленоксида с молекулярной массой 760-9000, или полипропиленгликоль с молекулярной массой 150-4000 или смесь полиэтиленоксида с молекулярной массой 100-630 с 10-45 мас.% полипропиленгликоля с молекулярной массой 150-4000.The method is as follows. In the manufacturing process of elastomeric compositions based on nitrile butadiene rubber, including hydrogenated rubber, plasticization of nitrile butadiene rubber on CM 1500 rollers is performed for 10 minutes for the subsequent manufacture of rubber products. Then loaded onto rollers per 100 parts by weight nitrile butadiene rubber 5 parts by weight white zinc, 1 parts by weight diafena FP, 2 parts by weight acetonanil R, 1 parts by weight stearin and mix for 4-5 minutes. Then add to 100 parts by weight nitrile butadiene rubber 120 wt.h. carbon black P-803 and 20 parts by weight dibutyl sebacinate and mixed with undercuts for 12-14 minutes. Then, modifiers - polyhydric alcohols, which are used as polyethylene oxide, polypropylene glycol or a mixture of polyethylene oxide with polypropylene glycol, are introduced into the prepared volume of the rubber mixture. In this case, polyethylene oxide with a molecular weight of 100-630, or polyethylene oxide with a molecular weight of 760-9000, or a mixture of polyethylene oxide with a molecular weight of 100-630 with 15-45 wt.% Polyethylene oxide with a molecular weight of 760-9000, or polypropylene glycol with a molecular weight of 150 are used -4000 or a mixture of polyethylene oxide with a molecular weight of 100-630 with 10-45 wt.% Polypropylene glycol with a molecular weight of 150-4000.

В качестве модификатора используют полиэтиленоксид, в том числе по ТУ 2483-007-71150986-2006 и полипропиленгликоль по ТУ 2226-006-10488057-94.Polyethylene oxide is used as a modifier, including those according to TU 2483-007-71150986-2006 and polypropylene glycol according to TU 2226-006-10488057-94.

Используют бутадиен-нитрильный каучук марки БНКС-18, БНКС-28, БНКС-33 и БНКС-40 по ТУ 38.30314-2006, бутадиен-нитрильный каучук марки БНКС-28 по ТУ 38.30313-2006, а также гидрированный бутадиен-нитрильный каучук марки ГБНК-3406.Use nitrile butadiene rubber grade BNKS-18, BNKS-28, BNKS-33 and BNKS-40 according to TU 38.30314-2006, butadiene-nitrile rubber grade BNKS-28 according to TU 38.30313-2006, as well as hydrogenated nitrile butadiene rubber brand GBNK -3406.

Количество вводимого в резиновую смесь модификатора выбрано от 0,5 до 8 мас. частей. Затем выполняют введение 5 мас.ч перкадокса и перемешивание в течение 2-3 минут. Для выпуска заготовок для РТИ использовали предформователь «Барвелл». Предварительно резиновую смесь разогревают на вальцах ПД-800. Готовые заготовки укладывались в лотки. РТИ изготавливали методом прямого прессования на вулканизационном прессе 250×250 с электрическим обогревом по следующему режиму: температура вулканизации - 180°С, время вулканизации - 10 мин, давление на пресс-форму не менее 5 МПа.The amount of modifier introduced into the rubber mixture is selected from 0.5 to 8 wt. parts. Then perform the introduction of 5 parts by weight of percadox and mixing for 2-3 minutes. To produce blanks for rubber goods, the Barwell preformer was used. Pre-rubber mixture is heated on rollers PD-800. Finished blanks were stacked in trays. RTIs were made by direct pressing on a 250 × 250 electrically heated vulcanizing press according to the following regime: vulcanization temperature — 180 ° C, vulcanization time — 10 min, pressure on the mold at least 5 MPa.

Готовое резинотехническое изделие дополнительно подвергают адсорбционно-абсорционной модификации выдерживанием готового резинотехнического изделия в жидком полиэтиленоксиде с молекулярной массой 100-2000 при температуре 115-200°С в течение 30-150 минут. Резинотехническое изделие готово к эксплуатации.The finished rubber product is additionally subjected to adsorption-absorption modification by keeping the finished rubber product in liquid polyethylene oxide with a molecular weight of 100-2000 at a temperature of 115-200 ° C for 30-150 minutes. The rubber product is ready for use.

Среди существенных признаков, характеризующих предложенный способ изготовления резинотехнических изделий из эластомерных композиций на основе бутадиен-нитрильного каучука, отличительными являются:Among the essential features characterizing the proposed method for the manufacture of rubber products from elastomeric compositions based on nitrile butadiene rubber, the following are distinguishing:

- введение после выполнения перемешивания и перед введением вулканизующего агента в объем резиновой смеси на основе бутадиен-нитрильного каучука модификаторов - многоатомных спиртов, в качестве которых используют полиэтиленоксид, полипропиленгликоль или смесь полиэтиленоксида с полипропиленгликолем,- the introduction after mixing and before the introduction of the curing agent into the volume of the rubber mixture based on nitrile butadiene rubber modifiers - polyols, which are used as polyethylene oxide, polypropylene glycol or a mixture of polyethylene oxide with polypropylene glycol,

- использование в процессе объемной модификации полиэтиленоксида с молекулярной массой 100-630, полиэтиленоксида с молекулярной массой 760-9000, смеси полиэтиленоксида с молекулярной массой 100-630 с полиэтиленоксидом с молекулярной массой 760-9000, полипропиленгликоля с молекулярной массой 150-4000 или смеси полиэтиленоксида с молекулярной массой 100-630 с полипропиленгликолем с молекулярной массой 150-4000,- use in the process of volumetric modification of polyethylene oxide with a molecular weight of 100-630, polyethylene oxide with a molecular weight of 760-9000, a mixture of polyethylene oxide with a molecular weight of 100-630 with polyethylene oxide with a molecular weight of 760-9000, polypropylene glycol with a molecular weight of 150-4000, or a mixture of polyethylene oxide with molecular weight 100-630 with polypropylene glycol with a molecular weight of 150-4000,

- введение в резиновую смесь модификатора в количестве от 0,5 до 8 мас. частей на 100 мас. частей бутадиен-нитрильного каучука,- the introduction of a modifier into the rubber mixture in an amount of from 0.5 to 8 wt. parts per 100 wt. parts of nitrile butadiene rubber,

- выполнение адсорбционно-абсорционной модификации выдерживанием готового резинотехнического изделия в жидком полиэтиленоксиде с молекулярной массой 100-2000 при температуре 115-200°С в течение 30-150 минут,- the implementation of the adsorption-absorption modification by keeping the finished rubber product in liquid polyethylene oxide with a molecular weight of 100-2000 at a temperature of 115-200 ° C for 30-150 minutes,

- использование при выполнении объемной модификации резиновой смеси на основе бутадиен-нитрильного каучука смеси полиэтиленоксида с 10-45 мас.% полипропиленгликоля.- use when performing bulk modification of the rubber mixture based on nitrile butadiene rubber, a mixture of polyethylene oxide with 10-45 wt.% polypropylene glycol.

- использование при выполнении объемной модификации резиновой смеси на основе бутадиен-нитрильного каучука смеси полиэтиленоксида с молекулярной массой 100-630 с 15-45 мас.% полиэтиленоксида с молекулярной массой 760-9000.- use when performing bulk modification of the rubber mixture based on nitrile butadiene rubber, a mixture of polyethylene oxide with a molecular weight of 100-630 with 15-45 wt.% polyethylene oxide with a molecular weight of 760-9000.

Экспериментальные и практические исследования предложенного способа изготовления резинотехнических изделий из эластомерных композиций на основе бутадиен-нитрильного каучука показали его высокую эффективность. Было установлено, что с использованием всех существенных признаков предложенного технического решения достигнуто снижение коэффициента трения (коэффициент трения в процессе эксплуатационного трения по полированным металлическим поверхностям контр-тела из стали 30 ХГСА составил 0,16-0,18 при скорости вращения 1,74 м/с и 0,04-0,11 при скорости вращения 4,18 м/с), снижение износа до 2-5×10^-7 мкм/км, а также повышение стабильности коэффициента трения до 0,89-0,92. Кроме того, испытания показали, что на изготовленных предложенным способом резинотехнических изделиях на основе бутадиен-нитрильного каучука достигнуто снижение момента страгивания. Одновременно сохранена условная прочность при растяжении на уровне 12,7-13,5 МПа, относительное удлинение на уровне 128 -163%, твердость по Шор А на уровне 78-80 ед. Шор А и температурный предел хрупкости ниже минус 45°С.Experimental and practical studies of the proposed method for manufacturing rubber products from elastomeric compositions based on nitrile butadiene rubber showed its high efficiency. It was found that using all the essential features of the proposed technical solution, a decrease in the coefficient of friction was achieved (the coefficient of friction during operational friction on the polished metal surfaces of the counterbody made of 30 HGSA steel was 0.16-0.18 at a speed of 1.74 m / s and 0.04-0.11 at a rotation speed of 4.18 m / s), reducing wear to 2-5 × 10 ^-7 μm / km, and also increasing the stability of the coefficient of friction to 0.89-0.92. In addition, the tests showed that on the rubber products made by the proposed method based on nitrile butadiene rubber, a reduction in the breaking moment was achieved. At the same time, conditional tensile strength was maintained at the level of 12.7-13.5 MPa, elongation at the level of 128 -163%, Shore A hardness at the level of 78-80 units. Shore A and the temperature limit of brittleness below minus 45 ° C.

Технология изготовления резинотехнических изделий из эластомерных композиций на основе бутадиен-нитрильного каучука различного трибологического назначения заданных геометрических форм и размеров не требует использования специфического технологического оборудования.The manufacturing technology of rubber products from elastomeric compositions based on nitrile butadiene rubber for various tribological purposes of a given geometric shapes and sizes does not require the use of specific technological equipment.

В таблице 1 показаны технологические параметры объемной и адсорбционно-абсорционной модификаций в процессе изготовления резинотехнических изделий из эластомерных композиций на основе бутадиен-нитрильного каучука, а в таблице 2 приведены характеристики трения и прочностные характеристики изготовленных с использованием предложенного способа износостойких резинотехнических изделий трения различного назначения.Table 1 shows the technological parameters of volumetric and adsorption-absorption modifications in the manufacturing process of rubber products from elastomeric compositions based on nitrile butadiene rubber, and table 2 shows the friction characteristics and strength characteristics made using the proposed method of wear-resistant rubber friction products for various purposes.

Таким образом, результаты экспериментальных исследований показали, что предложенный способ обеспечивает получение резинотехнических изделий с заданными эксплуатационными характеристиками.Thus, the results of experimental studies have shown that the proposed method provides rubber products with desired performance characteristics.

Технологические параметры модификации при изготовлении резинотехнических изделий из эластомерных композиций на основе бутадиен-нитрильного каучукаTechnological parameters of modification in the manufacture of rubber products from elastomeric compositions based on nitrile butadiene rubber (таблица 1)(Table 1) № материа-
лаMaterial No.
la ИзделиеProduct Объемная модификацияVolumetric Modification Адсорбционно-абсорбционная модификацияAdsorption-absorption modification Тип изделияProduct type Марка каучукаRubber grade Тип модификатора, с мол. массойType of modifier, mol. mass Кол-во модификатора, мас.%Amount of modifier, wt.% Тип модификатора, с мол. массойType of modifier, mol. mass Температу
ра, °СTemperature
ra, ° C Время выдержки, минHolding time, min 1one МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)PEO (M.M. 100) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 22 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)PEO (m.m. 400) 0,50.5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 33 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м.630)PEO (m. 630) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 4four МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)PEO (M.M. 100) 4,54,5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 55 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)PEO (m.m. 400) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 66 МанжетаCuff БНКС-18BNKS-18 ПЭО (м.м.630)PEO (m. 630) 4,54,5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 77 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)PEO (M.M. 100) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 88 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)PEO (m.m. 400) 8,08.0 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 99 МанжетаCuff ГБНК-3406GBNK-3406 ПЭО (м.м.630)PEO (m. 630) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 1010 ПодшипникBearing БНКС-33BNKS-33 ППГ (м.м. 760)BCP (m. 760) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 11eleven МанжетаCuff БНКС-28BNKS-28 ППГ (м.м. 4800)BCP (m.m. 4800) 0,50.5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 1212 МанжетаCuff БНКС-28BNKS-28 ППГ (м.м. 9000)BCP (m.m. 9000) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 1313 МанжетаCuff БНКС-28BNKS-28 ППГ (м.м. 760)BCP (m. 760) 4,54,5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 14fourteen ПодшипникBearing БНКС-28BNKS-28 ППГ (м.м. 4800)BCP (m.m. 4800) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 15fifteen ПодшипникBearing ГБНК-3406GBNK-3406 ППГ (м.м. 9000)BCP (m.m. 9000) 4,54,5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 1616 МанжетаCuff БНКС-28BNKS-28 ППГ (м.м. 760)BCP (m. 760) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 1717 МанжетаCuff БНКС-33BNKS-33 ППГ (м.м. 4800)BCP (m.m. 4800) 8,08.0 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 18eighteen МанжетаCuff ГБНК-3406GBNK-3406 ППГ (м.м. 9000)BCP (m.m. 9000) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 1919 МанжетаCuff БНКС-40BNKS-40 ПЭО (м.м. 100)+10 мас.% ППГ (м.м. 760)PEO (m.m. 100) +10 wt.% BCP (m.m. 760) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 20twenty МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+10 мас.% ППГ (м.м. 760)PEO (m.m. 100) +10 wt.% BCP (m.m. 760) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 2121 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+10 мас.% ППГ (м.м. 760)PEO (m.m. 100) +10 wt.% BCP (m.m. 760) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 2222 МанжетаCuff БНКС-33BNKS-33 ПЭО (м.м. 100)+30 мас.% ППГ (м.м. 760)PEO (m.m. 100) +30 wt.% BCP (m.m. 760) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 2323 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+30 мас.% ППГ (м.м. 760)PEO (m.m. 100) +30 wt.% BCP (m.m. 760) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 2424 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+30 мас.% ППГ (м.м. 760)PEO (m.m. 100) +30 wt.% BCP (m.m. 760) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 2525 МанжетаCuff ГБНК-3406GBNK-3406 ПЭО (м.м. 100)+45 мас.% ППГ (м.м. 760)PEO (m.m. 100) +45 wt.% BCP (m.m. 760) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 2626 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+45 мас.% ППГ (м.м. 760)PEO (m.m. 100) +45 wt.% BCP (m.m. 760) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 2727 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+45 мас.% ППГ (м.м. 760)PEO (m.m. 100) +45 wt.% BCP (m.m. 760) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 2828 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+10 мас.% ППГ (м.м. 4800)PEO (m.m. 100) +10 wt.% BCP (m.m. 4800) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 2929th МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+10 мас.% ППГ (м.м. 4800)PEO (m.m. 100) +10 wt.% BCP (m.m. 4800) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 30thirty ПодшипникBearing БНКС-28BNKS-28 ПЭО (м.м. 100)+10 мас.% ППГ (м.м. 4800)PEO (m.m. 100) +10 wt.% BCP (m.m. 4800) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 3131 ПодшипникBearing БНКС-28BNKS-28 ПЭО (м.м. 100)+30 мас.% ППГ (м.м. 4800)PEO (m.m. 100) +30 wt.% BCP (m.m. 4800) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 3232 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+30 мас.% ППГ (м.м. 4800)PEO (m.m. 100) +30 wt.% BCP (m.m. 4800) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 3333 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+30 мас.% ППГ (м.м. 4800)PEO (m.m. 100) +30 wt.% BCP (m.m. 4800) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 3434 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+45 мас.% ППГ (м.м. 4800)PEO (m.m. 100) +45 wt.% BCP (m.m. 4800) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 3535 МанжетаCuff БНКС-33BNKS-33 ПЭО (м.м. 100)+45 мас.% ППГ (м.м. 4800)PEO (m.m. 100) +45 wt.% BCP (m.m. 4800) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 3636 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+45 мас.% ППГ (м.м. 4800)PEO (m.m. 100) +45 wt.% BCP (m.m. 4800) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 3737 МанжетаCuff ГБНК-3406GBNK-3406 ПЭО (м.м. 100)+10 мас.% ППГ (м.м. 9000)PEO (m.m. 100) +10 wt.% BCP (m.m. 9000) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 3838 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+10 мас.% ППГ (м.м. 9000)PEO (m.m. 100) +10 wt.% BCP (m.m. 9000) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 3939 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+10 мас.% ППГ (м.м. 9000)PEO (m.m. 100) +10 wt.% BCP (m.m. 9000) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 4040 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+30 мас.% ППГ (м.м. 9000)PEO (m.m. 100) +30 wt.% BCP (m.m. 9000) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 4141 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+30 мас.% ППГ (м.м. 9000)PEO (m.m. 100) +30 wt.% BCP (m.m. 9000) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 4242 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+30 мас.% ППГ (м.м. 9000)PEO (m.m. 100) +30 wt.% BCP (m.m. 9000) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 4343 ПодшипникBearing БНКС-18BNKS-18 ПЭО (м.м. 100)+45 мас.% ППГ (м.м. 9000)PEO (m.m. 100) +45 wt.% BCP (m.m. 9000) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 4444 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+45 мас.% ППГ (м.м. 9000)PEO (m.m. 100) +45 wt.% BCP (m.m. 9000) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 4545 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+45 мас.% ППГ (м.м. 9000)PEO (m.m. 100) +45 wt.% BCP (m.m. 9000) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 4646 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+10 мас.% ППГ (м.м. 760)PEO (m.m. 400) +10 wt.% BCP (m.m. 760) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 4747 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+10 мас.% ППГ (м.м. 760)PEO (m.m. 400) +10 wt.% BCP (m.m. 760) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 4848 ПодшипникBearing БНКС-28BNKS-28 ПЭО (м.м. 400)+10 мас.% ППГ (м.м. 760)PEO (m.m. 400) +10 wt.% BCP (m.m. 760) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 4949 МанжетаCuff БНКС-33BNKS-33 ПЭО (м.м. 400)+30 мас.% ППГ (м.м. 760)PEO (m.m. 400) +30 wt.% BCP (m.m. 760) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 50fifty МанжетаCuff БНКС-18BNKS-18 ПЭО (м.м. 400)+30 мас.% ППГ (м.м. 760)PEO (m.m. 400) +30 wt.% BCP (m.m. 760) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 5151 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+30 мас.% ППГ (м.м. 760)PEO (m.m. 400) +30 wt.% BCP (m.m. 760) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 5252 МанжетаCuff ГБНК-3406GBNK-3406 ПЭО (м.м. 400)+45 мас.% ППГ (м.м. 760)PEO (m.m. 400) +45 wt.% BCP (m.m. 760) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 5353 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+45 мас.% ППГ (м.м. 760)PEO (m.m. 400) +45 wt.% BCP (m.m. 760) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 5454 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+45 мас.% ППГ (м.м. 760)PEO (m.m. 400) +45 wt.% BCP (m.m. 760) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 5555 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+10 мас.% ППГ (м.м. 4800)PEO (m.m. 400) +10 wt.% BCP (m.m. 4800) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 5656 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+10 мас.% ППГ (м.м. 4800)PEO (m.m. 400) +10 wt.% BCP (m.m. 4800) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 5757 ПодшипникBearing БНКС-28BNKS-28 ПЭО (м.м. 400)+10 мас.% ППГ (м.м. 4800)PEO (m.m. 400) +10 wt.% BCP (m.m. 4800) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 5858 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+30 мас.% ППГ (м.м. 4800)PEO (m.m. 400) +30 wt.% BCP (m.m. 4800) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 5959 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+30 мас.% ППГ (м.м. 4800)PEO (m.m. 400) +30 wt.% BCP (m.m. 4800) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 6060 МанжетаCuff ГБНК-3406GBNK-3406 ПЭО (м.м. 400)+30 мас.% ППГ (м.м. 4800)PEO (m.m. 400) +30 wt.% BCP (m.m. 4800) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 6161 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+45 мас.% ППГ (м.м. 4800)PEO (m.m. 400) +45 wt.% BCP (m.m. 4800) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 6262 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+45 мас.% ППГ (м.м. 4800)PEO (m.m. 400) +45 wt.% BCP (m.m. 4800) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 6363 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+45 мас.% ППГ (м.м. 4800)PEO (m.m. 400) +45 wt.% BCP (m.m. 4800) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 6464 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+10 мас.% ППГ (м.м. 9000)PEO (m.m. 400) +10 wt.% BCP (m.m. 9000) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 6565 ПодшипникBearing ГБНК-3406GBNK-3406 ПЭО (м.м. 400)+10 мас.% ППГ (м.м. 9000)PEO (m.m. 400) +10 wt.% BCP (m.m. 9000) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 6666 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+10 мас.% ППГ (м.м. 9000)PEO (m.m. 400) +10 wt.% BCP (m.m. 9000) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 6767 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+30 мас.% ППГ (м.м. 9000)PEO (m.m. 400) +30 wt.% BCP (m.m. 9000) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 6868 МанжетаCuff БНКС-18BNKS-18 ПЭО (м.м. 400)+30 мас.% ППГ (м.м. 9000)PEO (m.m. 400) +30 wt.% BCP (m.m. 9000) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 6969 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+30 мас.% ППГ (м.м. 9000)PEO (m.m. 400) +30 wt.% BCP (m.m. 9000) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 7070 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+45 мас.% ППГ (м.м. 9000)PEO (m.m. 400) +45 wt.% BCP (m.m. 9000) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 7171 ПодшипникBearing БНКС-28BNKS-28 ПЭО (м.м. 400)+45 мас.% ППГ (м.м. 9000)PEO (m.m. 400) +45 wt.% BCP (m.m. 9000) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 7272 ПодшипникBearing БНКС-28BNKS-28 ПЭО (м.м. 400)+45 мас.% ППГ (м.м. 9000)PEO (m.m. 400) +45 wt.% BCP (m.m. 9000) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 7373 МанжетаCuff БНКС-33BNKS-33 ПЭО (м.м. 630)+10 мас.% ППГ (м.м. 760)PEO (m.m. 630) +10 wt.% BCP (m.m. 760) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 7474 МанжетаCuff БНКС-40BNKS-40 ПЭО (м.м. 630)+10 мас.% ППГ (м.м. 760)PEO (m.m. 630) +10 wt.% BCP (m.m. 760) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 7575 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+10 мас.% ППГ (м.м. 760)PEO (m.m. 630) +10 wt.% BCP (m.m. 760) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 7676 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+30 мас.% ППГ (м.м. 760)PEO (m.m. 630) +30 wt.% BCP (m.m. 760) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 7777 МанжетаCuff ГБНК-3406GBNK-3406 ПЭО (м.м. 630)+30 мас.% ППГ (м.м. 760)PEO (m.m. 630) +30 wt.% BCP (m.m. 760) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 7878 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+30 мас.% ППГ (м.м. 760)PEO (m.m. 630) +30 wt.% BCP (m.m. 760) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 7979 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+45 мас.% ППГ (м.м. 760)PEO (m.m. 630) +45 wt.% BCP (m.m. 760) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 8080 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+45 мас.% ППГ (м.м. 760)PEO (m.m. 630) +45 wt.% BCP (m.m. 760) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 8181 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+45 мас.% ППГ (м.м. 760)PEO (m.m. 630) +45 wt.% BCP (m.m. 760) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 8282 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+10 мас.% ППГ (м.м. 4800)PEO (m.m. 630) +10 wt.% BCP (m.m. 4800) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 8383 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+10 мас.% ППГ (м.м. 4800)PEO (m.m. 630) +10 wt.% BCP (m.m. 4800) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 8484 ПодшипникBearing БНКС-28BNKS-28 ПЭО (м.м. 630)+10 мас.% ППГ (м.м. 4800)PEO (m.m. 630) +10 wt.% BCP (m.m. 4800) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 8585 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+30 мас.% ППГ (м.м. 4800)PEO (m.m. 630) +30 wt.% BCP (m.m. 4800) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 8686 ПодшипникBearing БНКС-28BNKS-28 ПЭО (м.м. 630)+30 мас.% ППГ (м.м. 4800)PEO (m.m. 630) +30 wt.% BCP (m.m. 4800) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 8787 МанжетаCuff БНКС-18BNKS-18 ПЭО (м.м. 630)+30 мас.% ППГ (м.м. 4800)PEO (m.m. 630) +30 wt.% BCP (m.m. 4800) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 8888 ПодшипникBearing ГБНК-3406GBNK-3406 ПЭО (м.м. 630)+45 мас.% ППГ (м.м. 4800)PEO (m.m. 630) +45 wt.% BCP (m.m. 4800) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 8989 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+45 мас.% ППГ (м.м. 4800)PEO (m.m. 630) +45 wt.% BCP (m.m. 4800) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 9090 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+45 мас.% ППГ (м.м. 4800)PEO (m.m. 630) +45 wt.% BCP (m.m. 4800) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 9191 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+10 мас.% ППГ (м.м. 9000)PEO (m.m. 630) +10 wt.% BCP (m.m. 9000) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 9292 МанжетаCuff БНКС-33BNKS-33 ПЭО (м.м. 630)+10 мас.% ППГ (м.м. 9000)PEO (m.m. 630) +10 wt.% BCP (m.m. 9000) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 9393 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+10 мас.% ППГ (м.м. 9000)PEO (m.m. 630) +10 wt.% BCP (m.m. 9000) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 9494 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+30 мас.% ППГ (м.м. 9000)PEO (m.m. 630) +30 wt.% BCP (m.m. 9000) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 9595 МанжетаCuff БНКС-33BNKS-33 ПЭО (м.м. 630)+30 мас.% ППГ (м.м. 9000)PEO (m.m. 630) +30 wt.% BCP (m.m. 9000) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 9696 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+30 мас.% ППГ (м.м. 9000)PEO (m.m. 630) +30 wt.% BCP (m.m. 9000) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 9797 МанжетаCuff ГБНК-3406GBNK-3406 ПЭО (м.м. 630)+45 мас.% ППГ (м.м. 9000)PEO (m.m. 630) +45 wt.% BCP (m.m. 9000) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 9898 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+45 мас.% ППГ (м.м. 9000)PEO (m.m. 630) +45 wt.% BCP (m.m. 9000) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 9999 МанжетаCuff БНКС-40BNKS-40 ПЭО (м.м. 630)+45 мас.% ППГ (м.м. 9000)PEO (m.m. 630) +45 wt.% BCP (m.m. 9000) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 100one hundred МанжетаCuff БНКС-18BNKS-18 ПЭО (м.м. 100)+15 мас.% ПЭО (м.м. 760)PEO (m.m. 100) +15 wt.% PEO (m.m. 760) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 101101 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+15 мас.% ПЭО (м.м. 760)PEO (m.m. 100) +15 wt.% PEO (m.m. 760) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 102102 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+15 мас.% ПЭО (м.м. 760)PEO (m.m. 100) +15 wt.% PEO (m.m. 760) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 103103 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+15 мас.% ПЭО (м.м. 4800)PEO (m.m. 100) +15 wt.% PEO (m.m. 4800) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 104104 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+15 мас.% ПЭО (м.м. 4800)PEO (m.m. 100) +15 wt.% PEO (m.m. 4800) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 105105 ПодшипникBearing БНКС-28BNKS-28 ПЭО (м.м. 100)+15 мас.% ПЭО (м.м. 4800)PEO (m.m. 100) +15 wt.% PEO (m.m. 4800) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 106106 МанжетаCuff ГБНК-3406GBNK-3406 ПЭО (м.м. 100)+15 мас.% ПЭО (м.м. 9000)PEO (m.m. 100) +15 wt.% PEO (m.m. 9000) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 107107 МанжетаCuff БНКС-33BNKS-33 ПЭО (м.м. 100)+15 мас.% ПЭО (м.м. 9000)PEO (m.m. 100) +15 wt.% PEO (m.m. 9000) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 108108 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+15 мас.% ПЭО (м.м. 9000)PEO (m.m. 100) +15 wt.% PEO (m.m. 9000) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 109109 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+30 мас.% ПЭО (м.м. 760)PEO (m.m. 100) +30 wt.% PEO (m.m. 760) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 110110 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+30 мас.% ПЭО (м.м. 760)PEO (m.m. 100) +30 wt.% PEO (m.m. 760) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 111111 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+30 мас.% ПЭО (м.м. 760)PEO (m.m. 100) +30 wt.% PEO (m.m. 760) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 112112 МанжетаCuff БНКС-40BNKS-40 ПЭО (м.м. 100)+30 мас.% ПЭО (м.м. 4800)PEO (m.m. 100) +30 wt.% PEO (m.m. 4800) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 113113 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+30 мас.% ПЭО (м.м. 4800)PEO (m.m. 100) +30 wt.% PEO (m.m. 4800) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 114114 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+30 мас.% ПЭО (м.м. 4800)PEO (m.m. 100) +30 wt.% PEO (m.m. 4800) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 115115 МанжетаCuff ГБНК-3406GBNK-3406 ПЭО (м.м. 100)+30 мас.% ПЭО (м.м. 9000)PEO (m.m. 100) +30 wt.% PEO (m.m. 9000) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 116116 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+30 мас.% ПЭО (м.м. 9000)PEO (m.m. 100) +30 wt.% PEO (m.m. 9000) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 117117 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+30 мас.% ПЭО (м.м. 9000)PEO (m.m. 100) +30 wt.% PEO (m.m. 9000) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 118118 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+45 мас.% ПЭО (м.м. 760)PEO (m.m. 100) +45 wt.% PEO (m.m. 760) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 119119 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+45 мас.% ПЭО (м.м. 760)PEO (m.m. 100) +45 wt.% PEO (m.m. 760) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 120120 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+45 мас.% ПЭО (м.м. 760)PEO (m.m. 100) +45 wt.% PEO (m.m. 760) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 121121 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+45 мас.% ПЭО (м.м. 4800)PEO (m.m. 100) +45 wt.% PEO (m.m. 4800) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 122122 МанжетаCuff ГБНК-3406GBNK-3406 ПЭО (м.м. 100)+45 мас.% ПЭО (м.м. 4800)PEO (m.m. 100) +45 wt.% PEO (m.m. 4800) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 123123 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+45 мас.% ПЭО (м.м. 4800)PEO (m.m. 100) +45 wt.% PEO (m.m. 4800) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 124124 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 100)+45 мас.% ПЭО (м.м. 9000)PEO (m.m. 100) +45 wt.% PEO (m.m. 9000) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 125125 МанжетаCuff БНКС-33BNKS-33 ПЭО (м.м. 100)+45 мас.% ПЭО (м.м. 9000)PEO (m.m. 100) +45 wt.% PEO (m.m. 9000) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 126126 ПодшипникBearing БНКС-28BNKS-28 ПЭО (м.м. 100)+45 мас.% ПЭО (м.м. 9000)PEO (m.m. 100) +45 wt.% PEO (m.m. 9000) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 127127 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+15 мас.% ПЭО (м.м. 760)PEO (m.m. 400) +15 wt.% PEO (m.m. 760) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 128128 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+15 мас.% ПЭО (м.м. 760)PEO (m.m. 400) +15 wt.% PEO (m.m. 760) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 129129 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+15 мас.% ПЭО (м.м. 760)PEO (m.m. 400) +15 wt.% PEO (m.m. 760) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 130130 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+15 мас.% ПЭО (м.м. 4800)PEO (m.m. 400) +15 wt.% PEO (m.m. 4800) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 131131 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+15 мас.% ПЭО (м.м. 4800)PEO (m.m. 400) +15 wt.% PEO (m.m. 4800) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 132132 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+15 мас.% ПЭО (м.м. 4800)PEO (m.m. 400) +15 wt.% PEO (m.m. 4800) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 133133 МанжетаCuff ГБНК-3406GBNK-3406 ПЭО (м.м. 400)+15 мас.% ПЭО (м.м. 9000)PEO (m.m. 400) +15 wt.% PEO (m.m. 9000) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 134134 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+15 мас.% ПЭО (м.м. 9000)PEO (m.m. 400) +15 wt.% PEO (m.m. 9000) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 135135 ПодшипникBearing БНКС-33BNKS-33 ПЭО (м.м. 400)+15 мас.% ПЭО (м.м. 9000)PEO (m.m. 400) +15 wt.% PEO (m.m. 9000) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 136136 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+30 мас.% ПЭО (м.м. 760)PEO (m.m. 400) +30 wt.% PEO (m.m. 760) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 137137 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+30 мас.% ПЭО (м.м. 760)PEO (m.m. 400) +30 wt.% PEO (m.m. 760) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 138138 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+30 мас.% ПЭО (м.м. 760)PEO (m.m. 400) +30 wt.% PEO (m.m. 760) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 139139 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+30 мас.% ПЭО (м.м. 4800)PEO (m.m. 400) +30 wt.% PEO (m.m. 4800) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 140140 МанжетаCuff БНКС-40BNKS-40 ПЭО (м.м. 400)+30 мас.% ПЭО (м.м. 4800)PEO (m.m. 400) +30 wt.% PEO (m.m. 4800) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 141141 МанжетаCuff ГБНК-3406GBNK-3406 ПЭО (м.м. 400)+30 мас.% ПЭО (м.м. 4800)PEO (m.m. 400) +30 wt.% PEO (m.m. 4800) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 142142 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+30 мас.% ПЭО (м.м. 9000)PEO (m.m. 400) +30 wt.% PEO (m.m. 9000) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 143143 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+30 мас.% ПЭО (м.м. 9000)PEO (m.m. 400) +30 wt.% PEO (m.m. 9000) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 144144 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+30 мас.% ПЭО (м.м. 9000)PEO (m.m. 400) +30 wt.% PEO (m.m. 9000) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 145145 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+45 мас.% ПЭО (м.м. 760)PEO (m.m. 400) +45 wt.% PEO (m.m. 760) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 146146 МанжетаCuff ГБНК-3406GBNK-3406 ПЭО (м.м. 400)+45 мас.% ПЭО (м.м. 760)PEO (m.m. 400) +45 wt.% PEO (m.m. 760) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 147147 ПодшипникBearing БНКС-28BNKS-28 ПЭО (м.м. 400)+45 мас.% ПЭО (м.м. 760)PEO (m.m. 400) +45 wt.% PEO (m.m. 760) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 148148 ПодшипникBearing БНКС-28BNKS-28 ПЭО (м.м. 400)+45 мас.% ПЭО (м.м. 4800)PEO (m.m. 400) +45 wt.% PEO (m.m. 4800) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 149149 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+45 мас.% ПЭО (м.м. 4800)PEO (m.m. 400) +45 wt.% PEO (m.m. 4800) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 150150 МанжетаCuff БНКС-18BNKS-18 ПЭО (м.м. 400)+45 мас.% ПЭО (м.м. 4800)PEO (m.m. 400) +45 wt.% PEO (m.m. 4800) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 151151 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+45 мас.% ПЭО (м.м. 9000)PEO (m.m. 400) +45 wt.% PEO (m.m. 9000) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 152152 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+45 мас.% ПЭО (м.м. 9000)PEO (m.m. 400) +45 wt.% PEO (m.m. 9000) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 153153 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 400)+45 мас.% ПЭО (м.м. 9000)PEO (m.m. 400) +45 wt.% PEO (m.m. 9000) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 154154 МанжетаCuff ГБНК-3406GBNK-3406 ПЭО (м.м. 630)+15 мас.% ПЭО (м.м. 760)PEO (m.m. 630) +15 wt.% PEO (m.m. 760) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 155155 МанжетаCuff БНКС-33BNKS-33 ПЭО (м.м. 630)+15 мас.% ПЭО (м.м. 760)PEO (m.m. 630) +15 wt.% PEO (m.m. 760) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 156156 МанжетаCuff БНКС-18BNKS-18 ПЭО (м.м. 630)+15 мас.% ПЭО (м.м. 760)PEO (m.m. 630) +15 wt.% PEO (m.m. 760) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 157157 МанжетаCuff БНКС-40BNKS-40 ПЭО (м.м. 630)+15 мас.% ПЭО (м.м. 4800)PEO (m.m. 630) +15 wt.% PEO (m.m. 4800) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 158158 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+15 мас.% ПЭО (м.м. 4800)PEO (m.m. 630) +15 wt.% PEO (m.m. 4800) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 159159 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+15 мас.% ПЭО (м.м. 4800)PEO (m.m. 630) +15 wt.% PEO (m.m. 4800) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 160160 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+15 мас.% ПЭО (м.м. 9000)PEO (m.m. 630) +15 wt.% PEO (m.m. 9000) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 161161 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+15 мас.% ПЭО (м.м. 9000)PEO (m.m. 630) +15 wt.% PEO (m.m. 9000) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 162162 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+15 мас.% ПЭО (м.м. 9000)PEO (m.m. 630) +15 wt.% PEO (m.m. 9000) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 163163 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+30 мас.% ПЭО (м.м. 760)PEO (m.m. 630) +30 wt.% PEO (m.m. 760) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 164164 МанжетаCuff БНКС-33BNKS-33 ПЭО (м.м. 630)+30 мас.% ПЭО (м.м. 760)PEO (m.m. 630) +30 wt.% PEO (m.m. 760) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 165165 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+30 мас.% ПЭО (м.м. 760)PEO (m.m. 630) +30 wt.% PEO (m.m. 760) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 166166 МанжетаCuff ГБНК-3406GBNK-3406 ПЭО (м.м. 630)+30 мас.% ПЭО (м.м. 4800)PEO (m.m. 630) +30 wt.% PEO (m.m. 4800) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 167167 ПодшипникBearing БНКС-28BNKS-28 ПЭО (м.м. 630)+30 мас.% ПЭО (м.м. 4800)PEO (m.m. 630) +30 wt.% PEO (m.m. 4800) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 168168 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+30 мас.% ПЭО (м.м. 4800)PEO (m.m. 630) +30 wt.% PEO (m.m. 4800) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 169169 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+30 мас.% ПЭО (м.м. 9000)PEO (m.m. 630) +30 wt.% PEO (m.m. 9000) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 170170 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+30 мас.% ПЭО (м.м. 9000)PEO (m.m. 630) +30 wt.% PEO (m.m. 9000) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 171171 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+30 мас.% ПЭО (м.м. 9000)PEO (m.m. 630) +30 wt.% PEO (m.m. 9000) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 172172 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+45 мас.% ПЭО (м.м. 760)PEO (m.m. 630) +45 wt.% PEO (m.m. 760) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 173173 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+45 мас.% ПЭО (м.м. 760)PEO (m.m. 630) +45 wt.% PEO (m.m. 760) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 174174 МанжетаCuff ГБНК-3406GBNK-3406 ПЭО (м.м. 630)+45 мас.% ПЭО (м.м. 760)PEO (m.m. 630) +45 wt.% PEO (m.m. 760) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 175175 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+45 мас.% ПЭО (м.м. 4800)PEO (m.m. 630) +45 wt.% PEO (m.m. 4800) 0,50.5 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 176176 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+45 мас.% ПЭО (м.м. 4800)PEO (m.m. 630) +45 wt.% PEO (m.m. 4800) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 177177 ПодшипникBearing БНКС-28BNKS-28 ПЭО (м.м. 630)+45 мас.% ПЭО (м.м. 4800)PEO (m.m. 630) +45 wt.% PEO (m.m. 4800) 8,08.0 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 178178 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+45 мас.% ПЭО (м.м. 9000)PEO (m.m. 630) +45 wt.% PEO (m.m. 9000) 0,50.5 ПЭО с м.м. 100PEO with m.m. one hundred 200200 30thirty 179179 МанжетаCuff БНКС-28BNKS-28 ПЭО (м.м. 630)+45 мас.% ПЭО (м.м. 9000)PEO (m.m. 630) +45 wt.% PEO (m.m. 9000) 4,54,5 ПЭО с м.м. 1100PEO with m.m. 1100 155155 9090 180180 МанжетаCuff ГБНК-3406GBNK-3406 ПЭО (м.м. 630)+45 мас.% ПЭО (м.м. 9000)PEO (m.m. 630) +45 wt.% PEO (m.m. 9000) 8,08.0 ПЭО с м.м. 2000PEO with m.m. 2000 115115 150150 Обозначения: Designations: БНКС - бутадиен-нитрильный каучук,BNKS - nitrile butadiene rubber, ГБНК - гидрированный бутадиен-нитрильный каучукGBNA - hydrogenated nitrile butadiene rubber ПЭО - полиэтиленоксид,PEO - polyethylene oxide, ППГ - полипропиленгликоль,BCP - polypropylene glycol, ПЭО+25 мас.% ППГ - полиэтиленоксид+25 мас.% полипропиленгликоля,PEO + 25 wt.% PPG - polyethylene oxide + 25 wt.% Polypropylene glycol, ПЭО+30 мас.% ПЭО - полиэтиленоксид+30 мас.% полиэтиленоксида,PEO + 30 wt.% PEO - polyethylene oxide + 30 wt.% Polyethylene oxide, М.м. - молекулярная масса.M.m. - molecular mass.

Свойства изготовленных из эластомерных композиций на основе бутадиен-нитрильного каучука резинотехнических изделийProperties of rubber products made from elastomeric compositions based on nitrile butadiene rubber (таблица 2) (table 2) № материалаMaterial No. Коэффициент трения по контр-телу стали 30 ХГСА при скорости вращения,The friction coefficient on the counterbody of steel 30 HGSA at a speed of rotation, Стабильность коэффициента тренияFriction Stability Износ, мкм/кмDepreciation, mkm / km Условная прочность, МПаConditional Strength, MPa Относитель
ное удлинение, %Relative
elongation,% Твердость по Шор А, ед. Шор АShore A hardness, units Shore a Момент страгиванияMoment of breaking 1,74 м/сек1.74 m / s 4,18 м/сек4.18 m / s 1one 0,180.18 0,090.09 0,920.92 5×10^-7 5 × 10 ^-7 13,513.5 163163 7878 НизкийLow 22 0.160.16 0,040.04 0,890.89 4×10^-7 4 × 10 ^-7 12.712.7 160160 8080 НизкийLow 33 0,170.17 0,090.09 0,910.91 3×10^-7 3 × 10 ^-7 13,113.1 142142 7979 НизкийLow 4four 0,180.18 0,100.10 0,890.89 4×10^-7 4 × 10 ^-7 12,912.9 163163 7878 НизкийLow 55 0.160.16 0,050.05 0,920.92 3×10^-7 3 × 10 ^-7 13,513.5 128128 7878 НизкийLow 66 0,170.17 0,110.11 0,910.91 2×10^-7 2 × 10 ^-7 12,812.8 160160 7878 НизкийLow 77 0,170.17 0,100.10 0,920.92 4×10^-7 4 × 10 ^-7 13,413,4 135135 7878 НизкийLow 88 0.160.16 0,060.06 0,890.89 2×10^-7 2 × 10 ^-7 12.712.7 149149 7878 НизкийLow 99 0,170.17 0,090.09 0,910.91 3×10^-7 3 × 10 ^-7 13,013.0 128128 7878 НизкийLow 1010 0,180.18 0,100.10 0,900.90 4×10^-7 4 × 10 ^-7 13,513.5 163163 7878 НизкийLow 11eleven 0,170.17 0,110.11 0,890.89 3×10^-7 3 × 10 ^-7 12,912.9 142142 7979 НизкийLow 1212 0.160.16 0,090.09 0,920.92 5×10^-7 5 × 10 ^-7 13,413,4 128128 8080 НизкийLow 1313 0,170.17 0,100.10 0,910.91 3×10^-7 3 × 10 ^-7 12,812.8 160160 7979 НизкийLow 14fourteen 0,170.17 0,090.09 0,890.89 4×10^-7 4 × 10 ^-7 13,213,2 149149 7878 НизкийLow 15fifteen 0,170.17 0,070,07 0,890.89 3×10^-7 3 × 10 ^-7 13,513.5 128128 7878 НизкийLow 1616 0,180.18 0,090.09 0,890.89 4×10^-7 4 × 10 ^-7 12,912.9 163163 7878 НизкийLow 1717 0,170.17 0,040.04 0,900.90 2×10^-7 2 × 10 ^-7 13,313.3 142142 7979 НизкийLow 18eighteen 0.160.16 0,100.10 0,920.92 3×10^-7 3 × 10 ^-7 13,113.1 163163 8080 НизкийLow 1919 0,170.17 0,100.10 0,890.89 3×10^-7 3 × 10 ^-7 12,812.8 160160 7878 НизкийLow 20twenty 0,180.18 0,090.09 0,900.90 4×10^-7 4 × 10 ^-7 12.712.7 135135 7878 НизкийLow 2121 0,170.17 0,100.10 0,920.92 2×10^-7 2 × 10 ^-7 13,513.5 163163 7878 НизкийLow 2222 0,170.17 0,080.08 0,890.89 3×10^-7 3 × 10 ^-7 13,213,2 142142 7878 НизкийLow 2323 0,180.18 0,100.10 0,920.92 5×10^-7 5 × 10 ^-7 12,912.9 163163 8080 НизкийLow 2424 0.160.16 0,090.09 0,900.90 4×10^-7 4 × 10 ^-7 12,812.8 149149 7979 НизкийLow 2525 0,170.17 0,100.10 0,910.91 3×10^-7 3 × 10 ^-7 13,413,4 142142 7878 НизкийLow 2626 0,170.17 0,040.04 0,890.89 2×10^-7 2 × 10 ^-7 12,812.8 163163 7979 НизкийLow 2727 0.160.16 0,090.09 0,920.92 3×10^-7 3 × 10 ^-7 13,013.0 128128 8080 НизкийLow 2828 0,170.17 0,090.09 0,900.90 4×10^-7 4 × 10 ^-7 12,912.9 160160 7979 НизкийLow 2929th 0.160.16 0,050.05 0,890.89 3×10^-7 3 × 10 ^-7 13,513.5 135135 7878 НизкийLow 30thirty 0,170.17 0,090.09 0,900.90 2×10^-7 2 × 10 ^-7 12.712.7 163163 8080 НизкийLow 3131 0,180.18 0,090.09 0,920.92 3×10^-7 3 × 10 ^-7 13,313.3 142142 8080 НизкийLow 3232 0.160.16 0,060.06 0,910.91 3×10^-7 3 × 10 ^-7 13,413,4 149149 7979 НизкийLow 3333 0,170.17 0,090.09 0,890.89 4×10^-7 4 × 10 ^-7 12,812.8 163163 7878 НизкийLow 3434 0,170.17 0,080.08 0,890.89 2×10^-7 2 × 10 ^-7 13,513.5 142142 7979 НизкийLow 3535 0.160.16 0,100.10 0,890.89 4×10^-7 4 × 10 ^-7 12,912.9 163163 8080 НизкийLow 3636 0,170.17 0,090.09 0,920.92 3×10^-7 3 × 10 ^-7 13,113.1 160160 7878 НизкийLow 3737 0.160.16 0,040.04 0,900.90 4×10^-7 4 × 10 ^-7 12,812.8 160160 7979 НизкийLow 3838 0.160.16 0,090.09 0,890.89 5×10^-7 5 × 10 ^-7 13,313.3 135135 7878 НизкийLow 3939 0.160.16 0,050.05 0,920.92 2×10^-7 2 × 10 ^-7 12.712.7 163163 7979 НизкийLow 4040 0.160.16 0,040.04 0,900.90 3×10^-7 3 × 10 ^-7 13,013.0 142142 8080 НизкийLow 4141 0,180.18 0,090.09 0,890.89 4×10^-7 4 × 10 ^-7 12,912.9 149149 7878 НизкийLow 4242 0,170.17 0,090.09 0,900.90 3×10^-7 3 × 10 ^-7 13,513.5 163163 7979 НизкийLow 4343 0,170.17 0,050.05 0,910.91 3×10^-7 3 × 10 ^-7 12,812.8 135135 8080 НизкийLow 4444 0.160.16 0,090.09 0,920.92 4×10^-7 4 × 10 ^-7 13,413,4 163163 7979 НизкийLow 4545 0.160.16 0,040.04 0,890.89 2×10^-7 2 × 10 ^-7 13,213,2 149149 7878 НизкийLow 4646 0,170.17 0,090.09 0,890.89 3×10^-7 3 × 10 ^-7 13,113.1 128128 7979 НизкийLow 4747 0.160.16 0,060.06 0,900.90 4×10^-7 4 × 10 ^-7 12,912.9 160160 8080 НизкийLow 4848 0.160.16 0,110.11 0,920.92 5×10^-7 5 × 10 ^-7 12,812.8 142142 7878 НизкийLow 4949 0.160.16 0,090.09 0,890.89 4×10^-7 4 × 10 ^-7 13,413,4 163163 7979 НизкийLow 50fifty 0,170.17 0,040.04 0,900.90 3×10^-7 3 × 10 ^-7 13,013.0 149149 8080 НизкийLow 5151 0.160.16 0,090.09 0,920.92 2×10^-7 2 × 10 ^-7 13,313.3 163163 7878 НизкийLow 5252 0,170.17 0,060.06 0,890.89 2×10^-7 2 × 10 ^-7 13,513.5 128128 7979 НизкийLow 5353 0,180.18 0,090.09 0,890.89 3×10^-7 3 × 10 ^-7 12,812.8 135135 8080 НизкийLow 5454 0.160.16 0,100.10 0,890.89 4×10^-7 4 × 10 ^-7 13,213,2 163163 7878 НизкийLow 5555 0.160.16 0,090.09 0,900.90 3×10^-7 3 × 10 ^-7 13,513.5 149149 7979 НизкийLow 5656 0.160.16 0,100.10 0,920.92 2×10^-7 2 × 10 ^-7 12,912.9 142142 7979 НизкийLow 5757 0.160.16 0,050.05 0,890.89 3×10^-7 3 × 10 ^-7 12.712.7 160160 7878 НизкийLow 5858 0.160.16 0,090.09 0,920.92 4×10^-7 4 × 10 ^-7 13,413,4 163163 7878 НизкийLow 5959 0,170.17 0,040.04 0,910.91 3×10^-7 3 × 10 ^-7 13,113.1 142142 8080 НизкийLow 6060 0,170.17 0,090.09 0,910.91 5×10^-7 5 × 10 ^-7 12,812.8 163163 7878 НизкийLow 6161 0.160.16 0,090.09 0,890.89 2×10^-7 2 × 10 ^-7 13,513.5 149149 7979 НизкийLow 6262 0.160.16 0,060.06 0,890.89 2×10^-7 2 × 10 ^-7 12,912.9 163163 8080 НизкийLow 6363 0.160.16 0,090.09 0,890.89 2×10^-7 2 × 10 ^-7 13,313.3 135135 7878 НизкийLow 6464 0.160.16 0,090.09 0,890.89 3×10^-7 3 × 10 ^-7 13,513.5 160160 7878 НизкийLow 6565 0,180.18 0,100.10 0,920.92 4×10^-7 4 × 10 ^-7 12.712.7 149149 8080 НизкийLow 6666 0.160.16 0,050.05 0,900.90 3×10^-7 3 × 10 ^-7 13,413,4 128128 7979 НизкийLow 6767 0,170.17 0,090.09 0,890.89 2×10^-7 2 × 10 ^-7 13,513.5 163163 7878 НизкийLow 6868 0,170.17 0,040.04 0,920.92 3×10^-7 3 × 10 ^-7 12,812.8 142142 7878 НизкийLow 6969 0.160.16 0,110.11 0,900.90 4×10^-7 4 × 10 ^-7 13,113.1 163163 7979 НизкийLow 7070 0.160.16 0,090.09 0,890.89 2×10^-7 2 × 10 ^-7 13,313.3 135135 8080 НизкийLow 7171 0.160.16 0,060.06 0,910.91 4×10^-7 4 × 10 ^-7 13,013.0 149149 7979 НизкийLow 7272 0,170.17 0,090.09 0,920.92 5×10^-7 5 × 10 ^-7 12,912.9 163163 8080 НизкийLow 7373 0,180.18 0,100.10 0,900.90 3×10^-7 3 × 10 ^-7 13,413,4 149149 7878 НизкийLow 7474 0.160.16 0,070,07 0,890.89 2×10^-7 2 × 10 ^-7 12,812.8 142142 7878 НизкийLow 7575 0.160.16 0,090.09 0,910.91 3×10^-7 3 × 10 ^-7 12.712.7 160160 7979 НизкийLow 7676 0.160.16 0,040.04 0,920.92 4×10^-7 4 × 10 ^-7 13,513.5 163163 8080 НизкийLow 7777 0,170.17 0,040.04 0,890.89 4×10^-7 4 × 10 ^-7 13,213,2 142142 8080 НизкийLow 7878 0,170.17 0,090.09 0,900.90 3×10^-7 3 × 10 ^-7 12.712.7 135135 7979 НизкийLow 7979 0.160.16 0,060.06 0,920.92 2×10^-7 2 × 10 ^-7 13,313.3 163163 7878 НизкийLow 8080 0.160.16 0,090.09 0,890.89 3×10^-7 3 × 10 ^-7 13,413,4 149149 7878 НизкийLow 8181 0.160.16 0,050.05 0,920.92 4×10^-7 4 × 10 ^-7 12,812.8 128128 7878 НизкийLow 8282 0,170.17 0,100.10 0,900.90 3×10^-7 3 × 10 ^-7 12,912.9 163163 7878 НизкийLow 8383 0.160.16 0,080.08 0,920.92 3×10^-7 3 × 10 ^-7 13,313.3 142142 7878 НизкийLow 8484 0.160.16 0,090.09 0,890.89 4×10^-7 4 × 10 ^-7 12.712.7 160160 7979 НизкийLow 8585 0,180.18 0,040.04 0,910.91 2×10^-7 2 × 10 ^-7 13,513.5 135135 8080 НизкийLow 8686 0,170.17 0,100.10 0,920.92 3×10^-7 3 × 10 ^-7 13,313.3 163163 8080 НизкийLow 8787 0.160.16 0,090.09 0,890.89 4×10^-7 4 × 10 ^-7 12,812.8 149149 7979 НизкийLow 8888 0.160.16 0,050.05 0,920.92 3×10^-7 3 × 10 ^-7 13,213,2 160160 7878 НизкийLow 8989 0.160.16 0,050.05 0,900.90 2×10^-7 2 × 10 ^-7 13,413,4 128128 7878 НизкийLow 9090 0,170.17 0,090.09 0,890.89 4×10^-7 4 × 10 ^-7 13,113.1 163163 7979 НизкийLow 9191 0,180.18 0,060.06 0,920.92 3×10^-7 3 × 10 ^-7 13,513.5 135135 8080 НизкийLow 9292 0.160.16 0,090.09 0,890.89 5×10^-7 5 × 10 ^-7 12.712.7 142142 8080 НизкийLow 9393 0.160.16 0,070,07 0,910.91 2×10^-7 2 × 10 ^-7 13,513.5 163163 7979 НизкийLow 9494 0.160.16 0,060.06 0,890.89 3×10^-7 3 × 10 ^-7 12,912.9 149149 7878 НизкийLow 9595 0.160.16 0,090.09 0,890.89 3×10^-7 3 × 10 ^-7 12,812.8 142142 7878 НизкийLow 9696 0,170.17 0,040.04 0,900.90 4×10^-7 4 × 10 ^-7 13,413,4 135135 8080 НизкийLow 9797 0,180.18 0,090.09 0,920.92 3×10^-7 3 × 10 ^-7 13,013.0 160160 7979 НизкийLow 9898 0.160.16 0,100.10 0,890.89 3×10^-7 3 × 10 ^-7 13,513.5 149149 8080 НизкийLow 9999 0.160.16 0,050.05 0,910.91 2×10^-7 2 × 10 ^-7 12,912.9 163163 7878 НизкийLow 100one hundred 0.160.16 0,090.09 0,920.92 2×10^-7 2 × 10 ^-7 12.712.7 149149 7878 НизкийLow 101101 0,170.17 0,040.04 0,890.89 2×10^-7 2 × 10 ^-7 13,313.3 142142 7878 НизкийLow 102102 0,180.18 0,080.08 0,900.90 4×10^-7 4 × 10 ^-7 13,413,4 163163 7979 НизкийLow 103103 0.160.16 0,090.09 0,920.92 3×10^-7 3 × 10 ^-7 12,812.8 135135 8080 НизкийLow 104104 0.160.16 0,100.10 0,890.89 5×10^-7 5 × 10 ^-7 12.712.7 128128 8080 НизкийLow 105105 0.160.16 0,040.04 0,920.92 2×10^-7 2 × 10 ^-7 12.712.7 160160 7979 НизкийLow 106106 0.160.16 0,090.09 0,910.91 3×10^-7 3 × 10 ^-7 13,413,4 142142 7979 НизкийLow 107107 0,170.17 0,050.05 0,890.89 4×10^-7 4 × 10 ^-7 13,213,2 163163 8080 НизкийLow 108108 0,180.18 0,090.09 0,900.90 3×10^-7 3 × 10 ^-7 12,912.9 149149 7878 НизкийLow 109109 0.160.16 0,050.05 0,890.89 3×10^-7 3 × 10 ^-7 13,513.5 142142 7979 НизкийLow 110110 0.160.16 0,090.09 0,920.92 2×10^-7 2 × 10 ^-7 13,313.3 160160 7878 НизкийLow 111111 0,170.17 0,050.05 0,900.90 2×10^-7 2 × 10 ^-7 12,812.8 135135 7878 НизкийLow 112112 0,170.17 0,090.09 0,890.89 4×10^-7 4 × 10 ^-7 12,812.8 163163 7878 НизкийLow 113113 0.160.16 0,100.10 0,890.89 3×10^-7 3 × 10 ^-7 12.712.7 149149 7979 НизкийLow 114114 0.160.16 0,050.05 0,890.89 2×10^-7 2 × 10 ^-7 13,413,4 142142 8080 НизкийLow 115115 0.160.16 0,090.09 0,920.92 5×10^-7 5 × 10 ^-7 13,113.1 135135 7878 НизкийLow 116116 0,180.18 0,060.06 0,920.92 3×10^-7 3 × 10 ^-7 13,513.5 160160 7979 НизкийLow 117117 0.160.16 0,090.09 0,910.91 2×10^-7 2 × 10 ^-7 13,313.3 128128 8080 НизкийLow 118118 0.160.16 0,050.05 0,890.89 3×10^-7 3 × 10 ^-7 12,812.8 163163 7878 НизкийLow 119119 0,180.18 0,090.09 0,900.90 4×10^-7 4 × 10 ^-7 12.712.7 142142 7878 НизкийLow 120120 0.160.16 0,100.10 0,890.89 3×10^-7 3 × 10 ^-7 12,912.9 135135 7878 НизкийLow 121121 0,170.17 0,060.06 0,910.91 5×10^-7 5 × 10 ^-7 13,213,2 149149 7878 НизкийLow 122122 0,170.17 0,090.09 0,920.92 2×10^-7 2 × 10 ^-7 12,812.8 163163 7979 НизкийLow 123123 0.160.16 0,040.04 0,890.89 3×10^-7 3 × 10 ^-7 13,513.5 160160 8080 НизкийLow 124124 0,170.17 0,040.04 0,900.90 4×10^-7 4 × 10 ^-7 13,013.0 142142 7979 НизкийLow 125125 0,180.18 0,090.09 0,910.91 3×10^-7 3 × 10 ^-7 12.712.7 135135 7878 НизкийLow 126126 0,170.17 0,060.06 0,920.92 5×10^-7 5 × 10 ^-7 13,513.5 163163 8080 НизкийLow 127127 0.160.16 0,110.11 0,890.89 4×10^-7 4 × 10 ^-7 12,912.9 142142 8080 НизкийLow 128128 0.160.16 0,060.06 0,900.90 2×10^-7 2 × 10 ^-7 13,413,4 163163 7878 НизкийLow 129129 0.160.16 0,090.09 0,920.92 3×10^-7 3 × 10 ^-7 13,213,2 149149 7979 НизкийLow 130130 0.160.16 0,040.04 0,910.91 4×10^-7 4 × 10 ^-7 12,812.8 135135 7878 НизкийLow 131131 0,170.17 0,090.09 0,890.89 3×10^-7 3 × 10 ^-7 12.712.7 160160 7878 НизкийLow 132132 0,170.17 0,040.04 0,920.92 5×10^-7 5 × 10 ^-7 13,513.5 128128 7979 НизкийLow 133133 0.160.16 0,090.09 0,900.90 2×10^-7 2 × 10 ^-7 12,912.9 149149 8080 НизкийLow 134134 0,170.17 0,050.05 0,890.89 4×10^-7 4 × 10 ^-7 13,413,4 142142 7878 НизкийLow 135135 0,180.18 0,100.10 0,890.89 3×10^-7 3 × 10 ^-7 12,812.8 163163 7979 НизкийLow 136136 0.160.16 0,060.06 0,900.90 2×10^-7 2 × 10 ^-7 13,313.3 135135 8080 НизкийLow 137137 0,170.17 0,040.04 0,920.92 3×10^-7 3 × 10 ^-7 13,513.5 163163 7979 НизкийLow 138138 0.160.16 0,090.09 0,910.91 5×10^-7 5 × 10 ^-7 13,113.1 160160 7878 НизкийLow 139139 0.160.16 0,050.05 0,890.89 2×10^-7 2 × 10 ^-7 12,912.9 142142 7878 НизкийLow 140140 0.160.16 0,090.09 0,900.90 3×10^-7 3 × 10 ^-7 12.712.7 163163 7878 НизкийLow 141141 0,170.17 0,040.04 0,890.89 4×10^-7 4 × 10 ^-7 13,413,4 135135 7878 НизкийLow 142142 0,180.18 0,090.09 0,920.92 3×10^-7 3 × 10 ^-7 13,013.0 149149 8080 НизкийLow 143143 0.160.16 0,050.05 0,890.89 2×10^-7 2 × 10 ^-7 12,812.8 142142 7878 НизкийLow 144144 0.160.16 0,090.09 0,900.90 3×10^-7 3 × 10 ^-7 13,513.5 128128 7878 НизкийLow 145145 0.160.16 0,040.04 0,920.92 2×10^-7 2 × 10 ^-7 12.712.7 128128 7878 НизкийLow 146146 0.160.16 0,100.10 0,890.89 3×10^-7 3 × 10 ^-7 13,313.3 163163 8080 НизкийLow 147147 0,170.17 0,060.06 0,920.92 5×10^-7 5 × 10 ^-7 13,413,4 135135 7979 НизкийLow 148148 0,170.17 0,090.09 0,890.89 2×10^-7 2 × 10 ^-7 12.712.7 163163 7878 НизкийLow 149149 0.160.16 0,080.08 0,890.89 2×10^-7 2 × 10 ^-7 13,213,2 142142 7878 НизкийLow 150150 0.160.16 0,090.09 0,900.90 3×10^-7 3 × 10 ^-7 12.712.7 135135 7979 НизкийLow 151151 0.160.16 0,070,07 0,920.92 4×10^-7 4 × 10 ^-7 12.712.7 163163 8080 НизкийLow 152152 0,180.18 0,100.10 0,890.89 2×10^-7 2 × 10 ^-7 13,513.5 142142 7979 НизкийLow 153153 0,170.17 0,040.04 0,890.89 3×10^-7 3 × 10 ^-7 13,413,4 163163 7878 НизкийLow 154154 0.160.16 0,090.09 0,910.91 2×10^-7 2 × 10 ^-7 12,812.8 149149 8080 НизкийLow 155155 0.160.16 0,050.05 0,890.89 3×10^-7 3 × 10 ^-7 12.712.7 135135 7878 НизкийLow 156156 0,170.17 0,040.04 0,900.90 4×10^-7 4 × 10 ^-7 13,513.5 163163 7979 НизкийLow 157157 0.160.16 0,090.09 0,920.92 2×10^-7 2 × 10 ^-7 12,812.8 149149 8080 НизкийLow 158158 0,170.17 0,060.06 0,910.91 3×10^-7 3 × 10 ^-7 13,413,4 142142 7878 НизкийLow 159159 0.160.16 0,080.08 0,890.89 5×10^-7 5 × 10 ^-7 12.712.7 163163 7878 НизкийLow 160160 0,170.17 0,100.10 0,910.91 3×10^-7 3 × 10 ^-7 13,313.3 135135 7878 НизкийLow 161161 0,180.18 0,040.04 0,900.90 2×10^-7 2 × 10 ^-7 13,413,4 160160 7979 НизкийLow 162162 0.160.16 0,090.09 0,920.92 3×10^-7 3 × 10 ^-7 12.712.7 128128 8080 НизкийLow 163163 0.160.16 0,070,07 0,910.91 4×10^-7 4 × 10 ^-7 13,513.5 163163 7979 НизкийLow 164164 0.160.16 0,090.09 0,890.89 3×10^-7 3 × 10 ^-7 12,812.8 149149 7878 НизкийLow 165165 0,170.17 0,060.06 0,900.90 2×10^-7 2 × 10 ^-7 13,413,4 142142 8080 НизкийLow 166166 0,170.17 0,090.09 0,920.92 3×10^-7 3 × 10 ^-7 13,213,2 135135 7878 НизкийLow 167167 0.160.16 0,100.10 0,910.91 5×10^-7 5 × 10 ^-7 13,113.1 149149 7979 НизкийLow 168168 0,170.17 0,050.05 0,910.91 2×10^-7 2 × 10 ^-7 13,513.5 163163 8080 НизкийLow 169169 0,170.17 0,060.06 0,890.89 3×10^-7 3 × 10 ^-7 13,413,4 142142 7878 НизкийLow 170170 0,170.17 0,090.09 0,900.90 3×10^-7 3 × 10 ^-7 12.712.7 135135 7979 НизкийLow 171171 0.160.16 0,060.06 0,920.92 2×10^-7 2 × 10 ^-7 13,313.3 128128 8080 НизкийLow 172172 0,170.17 0,080.08 0,910.91 3×10^-7 3 × 10 ^-7 13,413,4 163163 7878 НизкийLow 173173 0,170.17 0,080.08 0,890.89 2×10^-7 2 × 10 ^-7 12,812.8 160160 7979 НизкийLow 174174 0,180.18 0,040.04 0,920.92 4×10^-7 4 × 10 ^-7 13,313.3 142142 7878 НизкийLow 175175 0.160.16 0,060.06 0,910.91 3×10^-7 3 × 10 ^-7 13,413,4 135135 7979 НизкийLow 176176 0.160.16 0,090.09 0,900.90 4×10^-7 4 × 10 ^-7 12.712.7 149149 7878 НизкийLow 177177 0.160.16 0,050.05 0,890.89 2×10^-7 2 × 10 ^-7 13,313.3 142142 8080 НизкийLow 178178 0.160.16 0,040.04 0,910.91 3×10^-7 3 × 10 ^-7 13,413,4 163163 8080 НизкийLow 179179 0.160.16 0,090.09 0,910.91 3×10^-7 3 × 10 ^-7 13,313.3 128128 7878 НизкийLow 180180 0.160.16 0,060.06 0,920.92 2×10^-7 2 × 10 ^-7 13,113.1 160160 7979 НизкийLow

Claims

1. A method of manufacturing rubber products from elastomeric compositions based on nitrile butadiene rubber, including mastication of nitrile butadiene rubber on rollers, introducing a vulcanization activator, antioxidant, powder filler and plasticizer, introducing a vulcanizing agent after mixing, heating the rubber mixture on rollers, profiling blanks followed by the manufacture of rubber products by direct compression on a vulcanizing press with electric heating, featuring keep in mind that after mixing and before introducing the curing agent into the volume of the rubber mixture based on nitrile butadiene rubber, modifiers are additionally introduced - polyhydric alcohols, which are used as polyethylene oxide, polypropylene glycol or a mixture of polyethylene oxide with polypropylene glycol, and polyethylene oxide with a molecular weight of 100- 630, polypropylene glycol with a molecular weight of 760-9000 or a mixture of polyethylene oxide with a molecular weight of 100-630 with polypropylene glycol with a molecular weight of 760-900 0, while the amount of modifier introduced into the rubber mixture is selected from 0.5 to 8 wt. hours per 100 wt. including nitrile butadiene rubber, and the finished rubber product is additionally subjected to adsorption-absorption modification by keeping the finished rubber product in liquid polyethylene oxide with a molecular weight of 100-2000 at a temperature of 115-200 ° C for 30-150 minutes.

2. The method according to claim 1, characterized in that when performing bulk modification of the rubber mixture based on nitrile butadiene rubber, a mixture of polyethylene oxide with 10-45 wt.% Polypropylene glycol is used.

3. The method according to claim 1, characterized in that when performing bulk modification of the rubber mixture based on nitrile butadiene rubber, a mixture of polyethylene oxide with a molecular weight of 100-630 with 15-45 wt.% Polyethylene oxide with a molecular weight of 760-9000 is used.