RU2420495C1 - Charge to produce coating on tiling - Google Patents
Charge to produce coating on tiling Download PDFInfo
- Publication number
- RU2420495C1 RU2420495C1 RU2010109623/03A RU2010109623A RU2420495C1 RU 2420495 C1 RU2420495 C1 RU 2420495C1 RU 2010109623/03 A RU2010109623/03 A RU 2010109623/03A RU 2010109623 A RU2010109623 A RU 2010109623A RU 2420495 C1 RU2420495 C1 RU 2420495C1
- Authority
- RU
- Russia
- Prior art keywords
- tiling
- charge
- clay
- chalk
- cryolite
- Prior art date
Abstract
Description
Изобретение относится к промышленности строительных материалов и касается составов шихты для получения защитно-декоративных покрытий на керамической черепице.The invention relates to the building materials industry and relates to charge compositions for the production of protective and decorative coatings on ceramic tiles.
Известна шихта для получения покрытия на черепице, содержащая вес.ч.: глину 45; кварцевый песок 6,7; мел 2,5; свинцовый глет 40; окись железа 9,7; пиролюзит 7,5 [1]. Такая шихта не является экологически безопасной, поскольку содержит токсичный компонент - свинцовый глет.Known mixture to obtain coatings on tiles, containing parts by weight: clay 45; silica sand 6.7; chalk 2.5; lead litharge 40; iron oxide 9.7; pyrolusite 7.5 [1]. Such a mixture is not environmentally friendly, because it contains a toxic component - lead litharge.
Задача изобретения состоит в получении экологически безопасной шихты для получения защитно-декоративного покрытия на черепице.The objective of the invention is to obtain an environmentally friendly mixture to obtain a protective and decorative coating on the tiles.
Технический результат достигается тем, что шихта для получения покрытия на черепице, включающая глину, кварцевый песок, мел, окись железа, пиролюзит, дополнительно содержит криолит при следующем соотношении компонентов, вес.ч.: глина 33-37; кварцевый песок 2-3; мел 0,5-1; окись железа 12-15; пиролюзит 7-8; криолит 7-8.The technical result is achieved in that the mixture to obtain a coating on the tile, including clay, quartz sand, chalk, iron oxide, pyrolusite, additionally contains cryolite in the following ratio of components, parts by weight: clay 33-37; silica sand 2-3; chalk 0.5-1; iron oxide 12-15; pyrolusitis 7-8; cryolite 7-8.
Для приготовления шихты могут быть использованы любые глины, в том числе бентонит, лесс и др.For the preparation of the mixture can be used any clay, including bentonite, loess, etc.
Шихту получают следующим образом. Подготавливают и дозируют компоненты, например согласно выбранному из таблицы составу.The mixture is prepared as follows. Components are prepared and dosed, for example according to the composition selected from the table.
Берут, например, 37 кг глины (используемой в производстве черепицы), 3 кг кварцевого песка (промытого и высушенного), 0,5 кг мела, 15 кг окиси железа, 7 кг пиролюзита, 8 кг криолита. Компоненты подвергают помолу по полного прохождения через сетку 008. Подготавливают суспензию с влажностью 45-55%. Суспензию наносят в виде тонкого слоя на поверхность отформованной и высушенной черепицы, вторично сушат изделия с нанесенным слоем и обжигают в интервале температур 1050-1200°С. При обжиге покрытие образует спекшийся слой, прочно удерживающийся на поверхности черепицы. Полученное защитно-декоративное покрытие экологически безопасно, имеет матово-черный цвет.Take, for example, 37 kg of clay (used in the manufacture of tiles), 3 kg of quartz sand (washed and dried), 0.5 kg of chalk, 15 kg of iron oxide, 7 kg of pyrolusite, 8 kg of cryolite. The components are subjected to grinding after complete passage through the mesh 008. Prepare a suspension with a moisture content of 45-55%. The suspension is applied in the form of a thin layer on the surface of the molded and dried tiles, the products with the applied layer are dried again and fired in the temperature range 1050-1200 ° С. When fired, the coating forms a sintered layer, firmly held on the surface of the tile. The resulting protective and decorative coating is environmentally friendly, has a matte black color.
Источники информацииInformation sources
1. Гехт Г. Керамика / Пер. с нем. - Л.-М.: Главная редакция химической литературы, 1938. - С.177.1. Hecht G. Ceramics / Per. with him. - L.-M.: Main edition of the chemical literature, 1938. - P.177.
Claims (1)