Abstract
Description
Изобретение относится к области технологии силикатов и касается составов фриттованных глазурей, которые могут быть использованы в производстве изделий бытовой керамики.The invention relates to the field of technology of silicates and relates to compositions of fritted glazes that can be used in the manufacture of household ceramics.
Известна глазурь, включающая, мас.%: SiO2 33,00-55,0; Al2O3 2,0-8,0; B2O3 14,0-27,0; K2O 0-22,0; TiO2 0-6,0; ZrO2 0-4,0; F' 0,75-4,0; CaO 0-2,0 [1].Known glaze, including, wt.%: SiO 2 33,00-55,0; Al 2 O 3 2.0-8.0; B 2 O 3 14.0-27.0; K 2 O 0-22.0; TiO 2 0-6.0; ZrO 2 0-4.0; F '0.75-4.0; CaO 0-2.0 [1].
Задача изобретения состоит в повышении водостойкости глазури.The objective of the invention is to increase the water resistance of the glaze.
Технический результат достигается тем, что глазурь, содержащая SiO2, Al2O3, B2O3, K2O, ZrO2, CaO, дополнительно включает Er2O3, при следующем соотношении компонентов, мас.%: SiO2 80,5-81,5; Al2O3 4,0-6,0; B2O3 4,0-5,0; K2O 1,0-2,0; ZrO2 3,0-4,0; CaO 2,5-3,5; Er2O3 1,0-2,0.The technical result is achieved in that the glaze containing SiO 2 , Al 2 O 3 , B 2 O 3 , K 2 O, ZrO 2 , CaO, further includes Er 2 O 3 , in the following ratio, wt.%: SiO 2 80 5-81.5; Al 2 O 3 4.0-6.0; B 2 O 3 4.0-5.0; K 2 O 1.0-2.0; ZrO 2 3.0-4.0; CaO 2.5-3.5; Er 2 O 3 1.0-2.0.
В таблице приведены составы глазури.The table shows the glaze compositions.
Варку фритты глазури проводят при температуре 1500-1530°С. Расплав гранулируют в воду. Фритту размалывают до остатка не более 0,2% мокрым способом до полного прохождения через сетку №0056 и подготавливают суспензию с влажностью 45-47%. Суспензию наносят на керамические изделия и при температуре 1100-1150°С проводят обжиг.Glaze frit cooking is carried out at a temperature of 1500-1530 ° C. The melt is granulated into water. The frit is grinded to a residue of not more than 0.2% by the wet method until it passes completely through mesh No. 0056 and a suspension with a moisture content of 45-47% is prepared. The suspension is applied to ceramic products and at a temperature of 1100-1150 ° C, firing is carried out.
Источник информацииThe source of information
1. EP 0025187 A, C03C 8/06, 1981.1. EP 0025187 A, C03C 8/06, 1981.
Claims (1)
SiO2 80,5-81,5; Al2O3 4,0-6,0, B2O3 4,0-5,0; K2O 1,0-2,0; ZrO2 3,0-4,0; CaO 2,5-3,5; Er2O3 1,0-2,0. Glaze containing SiO 2 , Al 2 O 3 , B 2 O 3 , K 2 O, ZrO 2 , CaO, characterized in that it further includes Er 2 O 3 in the following ratio of components, wt.%:
SiO 2 80.5-81.5; Al 2 O 3, 4,0-6,0, B 2 O 3 4.0-5.0; K 2 O 1.0-2.0; ZrO 2 3.0-4.0; CaO 2.5-3.5; Er 2 O 3 1.0-2.0.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
RU2009102101/03A RU2384533C1 (en) | 2009-01-22 | 2009-01-22 | Glase |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
RU2009102101/03A RU2384533C1 (en) | 2009-01-22 | 2009-01-22 | Glase |
Publications (1)
Publication Number | Publication Date |
---|---|
RU2384533C1 true RU2384533C1 (en) | 2010-03-20 |
Family
ID=42137336
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
RU2009102101/03A RU2384533C1 (en) | 2009-01-22 | 2009-01-22 | Glase |
Country Status (1)
Country | Link |
---|---|
RU (1) | RU2384533C1 (en) |
-
2009
- 2009-01-22 RU RU2009102101/03A patent/RU2384533C1/en active
Similar Documents
Publication | Publication Date | Title |
---|---|---|
RU2384533C1 (en) | Glase | |
RU2382742C1 (en) | Glase | |
RU2384535C1 (en) | Glase | |
RU2306277C1 (en) | Glaze | |
RU2333169C1 (en) | Glaze | |
RU2345004C2 (en) | Glaze | |
RU2326833C1 (en) | Glaze | |
RU2329968C1 (en) | Glaze | |
RU2320565C1 (en) | Glaze | |
RU2316511C1 (en) | Glaze | |
RU2316515C1 (en) | Glaze | |
RU2316516C1 (en) | Glaze | |
RU2306276C1 (en) | Ceramic glaze | |
RU2322413C1 (en) | Glaze | |
RU2322416C1 (en) | Glaze | |
RU2318744C1 (en) | Glaze | |
RU2335473C1 (en) | Glaze | |
RU2329977C1 (en) | Glaze | |
RU2326839C1 (en) | Glaze | |
RU2338707C2 (en) | Glaze | |
RU2322414C1 (en) | Glaze | |
RU2329967C1 (en) | Glaze | |
RU2322412C1 (en) | Glaze | |
RU2326834C1 (en) | Glaze | |
RU2315731C1 (en) | Glaze |