RU2325342C1 - Glass - Google Patents

Glass Download PDF

Info

Publication number
RU2325342C1
RU2325342C1 RU2006143366/03A RU2006143366A RU2325342C1 RU 2325342 C1 RU2325342 C1 RU 2325342C1 RU 2006143366/03 A RU2006143366/03 A RU 2006143366/03A RU 2006143366 A RU2006143366 A RU 2006143366A RU 2325342 C1 RU2325342 C1 RU 2325342C1
Authority
RU
Russia
Prior art keywords
glass
cdo
cao
sio
mgo
Prior art date
Application number
RU2006143366/03A
Other languages
Russian (ru)
Inventor
Юли Алексеевна Щепочкина (RU)
Юлия Алексеевна Щепочкина
Original Assignee
Юлия Алексеевна Щепочкина
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Юлия Алексеевна Щепочкина filed Critical Юлия Алексеевна Щепочкина
Priority to RU2006143366/03A priority Critical patent/RU2325342C1/en
Application granted granted Critical
Publication of RU2325342C1 publication Critical patent/RU2325342C1/en

Abstract

FIELD: chemistry.
SUBSTANCE: invention relates to glass compositions and may used in production of utility glassware. The glass contains, percent by mass: SiO2 60-0-68.0; B2O3 8.0-12.0; ZnO 6.0-9.0; K2O 2.0-3.0; Na2O 2.0-3.0; CaO 1.0-2.0; CdO 0.7-1.7; Se 0.5-1.0; Al2O3 2.0-3.5; MgO 3.0-4.0; La2O3 0.1-0.2; S 0.1-0.2; TiO2 4.0-5.0.
EFFECT: increase in glass thermal stability.
1 tbl

Description

Изобретение относится к области технологии силикатов, а именно к составам стекла, которое может быть использовано для изготовления, например, сортовой посуды.The invention relates to the field of technology of silicates, namely, compositions of glass, which can be used for the manufacture of, for example, high-quality tableware.

Известно стекло, включающее, мас.%: SiO2 70,0-75,0; Na2O 14,29-19,0; CaO 4,96-14,9; CdO 0,6-0,85; Se 0,13-0,3; S 0,08-0,12 [1].Known glass, including, wt.%: SiO 2 70,0-75,0; Na 2 O 14.29-19.0; CaO 4.96-14.9; CdO 0.6-0.85; Se 0.13-0.3; S 0.08-0.12 [1].

Известно стекло, содержащее, мас.%: SiO2 68,0-70,0; B2O3 7,0-12,0; ZnO 7,0-11,0; K2O 0,5-3,0; Na2O 3,0-7,0; CaO 0,7-3,0; CdO 0,2-1,6; Se 0,2-1,0; Al2O3 1,0-3,5; MgO 0,7-3,0; La2O3 0,1-1,0; S 0,1-1,0 [2].Known glass containing, wt.%: SiO 2 68,0-70,0; B 2 O 3 7.0-12.0; ZnO 7.0-11.0; K 2 O 0.5-3.0; Na 2 O 3.0-7.0; CaO 0.7-3.0; CdO 0.2-1.6; Se 0.2-1.0; Al 2 O 3 1.0-3.5; MgO 0.7-3.0; La 2 O 3 0.1-1.0; S 0.1-1.0 [2].

Задачей изобретения является повышение термостойкости стекла.The objective of the invention is to increase the heat resistance of glass.

Поставленная задача решается тем, что в состав стекла дополнительно вводят TiO2, при следующем соотношении компонентов, мас.%: SiO2 60,0-68,0; B2O3 8,0-12,0; ZnO 6,0-9,0; K2O 2,0-3,0; Na2O 2,0-3,0; CaO 1,0-2,0; CdO 0,7-1,7; Se 0,5-1,0; Al2O3 2,0-3,5; MgO 3,0-4,0; La2O3 0,1-0,2; S 0,1-0,2; TiO2 4,0-5,0.The problem is solved in that TiO 2 is additionally introduced into the glass composition, in the following ratio of components, wt.%: SiO 2 60.0-68.0; B 2 O 3 8.0-12.0; ZnO 6.0-9.0; K 2 O 2.0-3.0; Na 2 O 2.0-3.0; CaO 1.0-2.0; CdO 0.7-1.7; Se 0.5-1.0; Al 2 O 3 2.0-3.5; MgO 3.0-4.0; La 2 O 3 0.1-0.2; S 0.1-0.2; TiO 2 4.0-5.0.

В таблице приведены составы стекла.The table shows the compositions of glass.

ТаблицаTable Состав №Composition No. Компоненты, мас.%:Components, wt.%: Термостойкость, °СHeat resistance, ° С SiO2 SiO 2 B2O3 B 2 O 3 ZnOZno K2OK 2 O Na2ONa 2 O CaOCao CdOCdo SeSe Al2O3 Al 2 O 3 MgOMgO La2O3 La 2 o 3 SS TiO2 TiO 2 1one 60,060.0 12,012.0 9,09.0 3,03.0 2,02.0 1,01,0 1,71.7 1,01,0 2,02.0 4,04.0 0,10.1 0,20.2 4,04.0 280280 22 63,063.0 10,010.0 7,57.5 2,52,5 2,52,5 1,51,5 1,21,2 0,70.7 2,82,8 3,53,5 0,150.15 0,150.15 4,54,5 280280 33 68,068.0 8,08.0 6,06.0 2,02.0 3,03.0 2,02.0 0,70.7 0,50.5 3,53,5 3,03.0 0,20.2 0,10.1 5,05,0 280280

Температура варки стекла 1400°С, среда восстановительная. Температура выработки в зависимости от ассортимента изделий.The temperature of glass melting is 1400 ° C, the recovery medium. Production temperature depending on the range of products.

Источники информацииInformation sources

1. Авторское свидетельство СССР №1158513, С03С 4/02, 1985.1. USSR author's certificate No. 1158513, С03С 4/02, 1985.

2. Авторское свидетельство СССР №726042, С03С 3/08, 1980.2. USSR author's certificate No. 726042, С03С 3/08, 1980.

Claims (1)

Стекло, содержащее SiO2, B2O3, ZnO, K2O, Na2O, CdO, Se, Al2O3, MgO, CaO, La2О3, S, отличающееся тем, что дополнительно содержит TiO2 при следующем соотношении компонентов, мас.%: SiO2 60,0-68,0; В2О3 8,0-12,0; ZnO 6,0-9,0; К2О 2,0-3,0; Na2O 2,0-3,0; CaO 1,0-2,0; CdO 0,7-1,7; Se 0,5-1,0; Al2О3 2,0-3,5; MgO 3,0-4,0; La2O3 0,1-0,2; S 0,1-0,2; TiO2 4,0-5,0.Glass containing SiO 2, B 2 O 3, ZnO, K 2 O, Na 2 O, CdO, Se, Al 2 O 3, MgO, CaO, La 2 O 3, S, characterized in that it further comprises TiO 2 at the following ratio of components, wt.%: SiO 2 60,0-68,0; B 2 O 3 8.0-12.0; ZnO 6.0-9.0; K 2 O 2.0-3.0; Na 2 O 2.0-3.0; CaO 1.0-2.0; CdO 0.7-1.7; Se 0.5-1.0; Al 2 O 3 2.0-3.5; MgO 3.0-4.0; La 2 O 3 0.1-0.2; S 0.1-0.2; TiO 2 4.0-5.0.
RU2006143366/03A 2006-12-07 2006-12-07 Glass RU2325342C1 (en)