RU2311378C1

RU2311378C1 - Raw mixture

Info

Publication number: RU2311378C1
Application number: RU2006120873/03A
Authority: RU
Inventors: Юли Алексеевна Щепочкина (RU); Юлия Алексеевна Щепочкина
Original assignee: Юлия Алексеевна Щепочкина
Priority date: 2006-06-13
Filing date: 2006-06-13
Publication date: 2007-11-27

Abstract

FIELD: technology of silicates.

SUBSTANCE: invention relates to compositions of raw mixtures used in manufacturing silicate bricks. The raw mixture comprises lime, waste from concentration of apatite ores, quartz sand and, additionally, caustic magnesite and waste from asbestos-cement industry wherein components are taken in the following ratio, wt.-%: lime, 4.0-5.0; waste from concentration of apatite ores, 20.0-25.0; caustic magnesite, 1.0-2.0; waste from asbestos-cement industry, 10.0-15.0, and quartz sand, the balance. Invention provides enhancing strength of brick.

EFFECT: improved and valuable property of raw mixture.

1 tbl

Description

Изобретение относится к области технологии силикатов и касается составов сырьевых смесей, используемых в производстве силикатного кирпича.The invention relates to the field of technology of silicates and relates to compositions of raw mixes used in the production of silicate brick.

Известна сырьевая смесь, включающая известь, кварцевый песок /1/.Known raw material mixture, including lime, silica sand / 1 /.

Известна сырьевая смесь, содержащая, мас.%: известь 4,8-5,0; отход обогащения апатитовых руд 13,07-24,0; каталин-бактерицид 0,01-0,31; кварцевый песок - остальное /2/.Known raw mix containing, wt.%: Lime 4.8-5.0; apatite ore dressing waste 13.07-24.0; catalin-bactericide 0.01-0.31; quartz sand - the rest / 2 /.

Целью изобретения является повышение прочности кирпича.The aim of the invention is to increase the strength of the brick.

Цель достигается тем, что в состав сырьевой смеси, содержащий известь, отход обогащения апатитовых руд, кварцевый песок, дополнительно вводят каустический магнезит и отход асбестоцементной промышленности, при следующем соотношении компонентов, мас.%: известь 4,0-5,0; отход обогащения апатитовых руд 20,0-25,0; каустический магнезит 1,0-2,0; отход асбестоцементной промышленности 10,0-15,0; кварцевый песок - остальное.The goal is achieved in that in the composition of the raw material mixture containing lime, waste of enrichment of apatite ores, quartz sand, caustic magnesite and waste of the asbestos-cement industry are additionally introduced, in the following ratio of components, wt.%: Lime 4.0-5.0; apatite ore dressing waste 20.0-25.0; caustic magnesite 1.0-2.0; asbestos cement industry waste 10.0-15.0; quartz sand - the rest.

В таблице приведены составы сырьевой смеси и прочность кирпича.The table shows the composition of the raw mix and the strength of the brick.

ТаблицаTable КомпонентыComponents Состав, мас.%:Composition, wt.%: 1one 22 33 ИзвестьLime 4,04.0 4,54,5 5,05,0 Отход обогащения апатитовых рудApatite ore dressing waste 25,025.0 23,023.0 20,020,0 Каустический магнезитCaustic Magnesite 2,02.0 1,51,5 1,01,0 Отход асбестоцементнойAsbestos cement waste 10,010.0 13,013.0 15,015.0 промышленностиindustry Кварцевый песокQuartz sand остальное (59)the rest (59) остальное (58)the rest (58) остальное (59)the rest (59) Прочность кирпича, МПаThe strength of the brick, MPa 40-4540-45 40-4540-45 40-4540-45

Источники информацииInformation sources

1. Филимонов П.И. Справочник молодого каменщика. - М.: Высш. шк., 1990. - С.26.1. Filimonov P.I. Handbook of a young mason. - M .: Higher. school, 1990. - S. 26.

2. Авторское свидетельство СССР №1474137, С04В 28/18, 1989.2. USSR author's certificate No. 1474137, С04В 28/18, 1989.

Claims

The raw material mixture containing lime, apatite ore dressing waste, quartz sand, characterized in that it further contains caustic magnesite and asbestos cement industry waste in the following ratio of components, wt.%:

lime 4.0-5.0 apatite ore dressing waste 20.0-25.0 caustic magnesite 1.0-2.0 asbestos cement waste 10.0-15.0 quartz sand rest