RU2165844C1 - Method for manufacture of moulded materials - Google Patents

Method for manufacture of moulded materials Download PDF

Info

Publication number
RU2165844C1
RU2165844C1 RU2000110396A RU2000110396A RU2165844C1 RU 2165844 C1 RU2165844 C1 RU 2165844C1 RU 2000110396 A RU2000110396 A RU 2000110396A RU 2000110396 A RU2000110396 A RU 2000110396A RU 2165844 C1 RU2165844 C1 RU 2165844C1
Authority
RU
Russia
Prior art keywords
formaldehyde
containing oligomers
resin
modifier
preparation
Prior art date
Application number
RU2000110396A
Other languages
Russian (ru)
Inventor
Л.В. Медведева
В.А. Хуршудов
М.П. Дудко
И.Т. Матюшин
А.Е. Анохин
Original Assignee
Медведева Лидия Владимировна
Хуршудов Вадим Александрович
Дудко Михаил Петрович
Матюшин Иван Тимофеевич
Анохин Анатолий Евгеньевич
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Медведева Лидия Владимировна, Хуршудов Вадим Александрович, Дудко Михаил Петрович, Матюшин Иван Тимофеевич, Анохин Анатолий Евгеньевич filed Critical Медведева Лидия Владимировна
Priority to RU2000110396A priority Critical patent/RU2165844C1/en
Application granted granted Critical
Publication of RU2165844C1 publication Critical patent/RU2165844C1/en

Abstract

FIELD: forest and wood-working industry, in particular, manufacture of ecologically pure moulded materials. SUBSTANCE: preparation of moulted materials involves introduction of a modifier from the group of reserve plant carbohydrates within 0.1-99.9 mas.pts of the resin mass. Formaldehyde-containing oligomers are resin, and mixing of vegetable particles is carried out with a binder, having formaldehyde bound by modifier. EFFECT: facilitated procedure. 25 cl, 5 tbl

Description

Изобретение относится к лесной и деревообрабатывающей промышленности, в частности к производству экологически чистых прессованных материалов. The invention relates to the forestry and woodworking industries, in particular to the production of environmentally friendly pressed materials.

Известен способ производства древесных материалов, включающий взаимосвязанные между собой подготовку древесных частиц, смешивание их со связующим, формирование ковра и прессование древесных материалов /см. а.с. СССР N 406738, кл. B 27 K 5/06, 1973/. A known method for the production of wood materials, including interconnected preparation of wood particles, mixing them with a binder, forming a carpet and pressing wood materials / see A.S. USSR N 406738, class B 27 K 5/06, 1973 /.

Известен также способ производства прессованных материалов, включающий взаимосвязанные между собой подготовку растительных частиц и связующего, смешивание растительных частиц со связующим, формирование ковра и прессование древесных материалов с термообработкой /см. а.с. N 415175, кл. B 27 N 3/02, 1974/. There is also a known method for the production of pressed materials, including interconnected preparation of plant particles and a binder, mixing plant particles with a binder, forming a carpet and pressing wood materials with heat treatment / cm. A.S. N 415175, CL B 27 N 3/02, 1974 /.

Недостатками известных способов является относительно высокая токсичность прессованных материалов из-за наличия несвязанного формальдегида относительно высокого расхода смолы и относительно низкой водостойкости материалов. The disadvantages of the known methods is the relatively high toxicity of pressed materials due to the presence of unbound formaldehyde, relatively high resin consumption and relatively low water resistance of materials.

Цель изобретения - повышение качества прессованных материалов за счет гашения несвязанного формальдегида. The purpose of the invention is to improve the quality of pressed materials by extinguishing unbound formaldehyde.

Достигается это тем, что подготовку смолы осуществляют с введением модификатора из группы резервных углеводов растений в количестве 0,1 - 99,9 мас. ч. от веса смолы, при этом в качестве смолы используют формальдегидосодержащие олигомеры, а смешивание растительных частиц выполняют со связующим, имеющим связанный модификатором формальдегид. This is achieved by the fact that the preparation of the resin is carried out with the introduction of a modifier from the group of reserve carbohydrates of plants in an amount of 0.1 - 99.9 wt. including the weight of the resin, while formaldehyde-containing oligomers are used as the resin, and the mixing of plant particles is carried out with a binder having a formaldehyde bound modifier.

Целесообразно, что подготовку смолы производили с концентрацией 35 - 75 процентов. It is advisable that the preparation of the resin was carried out with a concentration of 35 to 75 percent.

Полезно, что в качестве формальдегидосодержащих олигомеров используют мочевиноформальдегидную смолу. It is useful that urea-formaldehyde resin is used as formaldehyde-containing oligomers.

Полезно, что в качестве формальдегидосодержащих олигомеров использовали меламиноформальдегидную смолу. It is useful that melamine-formaldehyde resin was used as formaldehyde-containing oligomers.

Полезно, что в качестве формальдегидосодержащих олигомеров используют фенолоформальдегидную смолу. It is useful that phenol-formaldehyde resin is used as formaldehyde-containing oligomers.

Целесообразно, что в качестве формальдегидосодержащих олигомеров используют алкидную смолу. It is advisable that alkyd resin is used as formaldehyde-containing oligomers.

Полезно, что в качестве формальдегидосодержащих олигомеров используют эпоксидную смолу. It is useful that epoxy resin is used as formaldehyde-containing oligomers.

Целесообразно, что в качестве формальдегидосодержащих олигомеров используют поликонденсационные смолы. It is advisable that polycondensation resins are used as formaldehyde-containing oligomers.

Полезно, что в качестве формальдегидосодержащих олигомеров используют капралактам. It is useful that capralactam is used as formaldehyde-containing oligomers.

Целесообразно, что в качестве формальдегидосодержащих олигомеров используют винилхлорид. It is advisable that vinyl chloride is used as formaldehyde-containing oligomers.

Полезно, что в качестве формальдегидосодержащих олигомеров используют стирол. It is useful that styrene is used as formaldehyde-containing oligomers.

Целесообразно, что в качестве формальдегидосодержащих олигомеров используют капролактам. It is advisable that caprolactam is used as formaldehyde-containing oligomers.

Полезно, что в качестве формальдегидосодержащих олигомеров используют акрилонитрил. It is useful that acrylonitrile is used as formaldehyde-containing oligomers.

Целесообразно, что в качестве формальдегидосодержащих олигомеров используют полистирол. It is advisable that polystyrene is used as formaldehyde-containing oligomers.

Полезно, что в качестве формальдегидосодержащих олигомеров используют полиэтилен. It is useful that polyethylene is used as formaldehyde-containing oligomers.

Целесообразно, что в качестве формальдегидосодержащих олигомеров используют поливинилхлорид. It is advisable that polyvinyl chloride is used as formaldehyde-containing oligomers.

Полезно, что в качестве формальдегидосодержащих олигомеров используют полиэтилентерефталат. It is useful that polyethylene terephthalate is used as formaldehyde-containing oligomers.

Целесообразно, что в качестве формальдегидосодержащих олигомеров используют поликарбонаты. It is advisable that polycarbonates are used as formaldehyde-containing oligomers.

Полезно, что в качестве модификатора принимают крахмал. It is useful that starch is used as a modifier.

Целесообразно, что в качестве модификатора принимают окисленный крахмал. It is advisable that oxidized starch is used as a modifier.

Полезно, что в качестве модификатора принимают гидролизованный крахмал. It is useful that hydrolyzed starch is used as a modifier.

Целесообразно, что в качестве модификатора принимают частицы, полученные из зерновых и крахмалосодержащих растений. It is advisable that as a modifier accept particles obtained from grain and starch-containing plants.

Полезно, что в качестве модификатора принимают декстрины. It is useful that dextrins are used as a modifier.

Целесообразно, что в качестве модификатора принимают камеди. It is advisable that gum is used as a modifier.

Полезно, что в качестве модификатора принимают полисахариды. It is useful that polysaccharides are used as a modifier.

Способ производства прессованных материалов соответствует всем требованиям критериев, используемых для характеристики способа, а именно
- критерию наличия действия или совокупности действия, поскольку подготовку смолы осуществляют с введением модификатора из группы резервных углеводов растений в количестве 0,1 - 99,9 м.ч. от веса смолы,
- критерию порядка выполнения таких действий во времени /последовательно, одновременно, в различных сочетаниях/, поскольку в качестве смолы используют формальдегидосодержащие олигомеры, а смешивание растительных частиц выполняют со связующим, имеющим связанный модификатором формальдегид,
- критерию условий осуществления действий, режим, использование веществ - исходного сырья и др., устройств - приспособлений, инструментов, оборудования и др. , поскольку в качестве формальдегидосодержащих олигомеров используют мочевиноформальдегидную смолу.The method of production of pressed materials meets all the requirements of the criteria used to characterize the method, namely
- the criterion for the presence of an action or a combination of actions, since the preparation of the resin is carried out with the introduction of a modifier from the group of reserve carbohydrates of plants in an amount of 0.1 - 99.9 m.h. by weight of resin
- the criterion of the order in which such actions are performed in time / sequentially, simultaneously, in various combinations /, since formaldehyde-containing oligomers are used as the resin, and the mixing of plant particles is performed with a binder having formaldehyde bound by a modifier,
- criteria for the conditions for the implementation of the action, mode, use of substances - feedstock, etc., devices - devices, tools, equipment, etc., since urea-formaldehyde resin is used as formaldehyde-containing oligomers.

В табл. 1 приведены данные соотношений исходных компонентов для модификации формальдегидосодержащих смол окисленным крахмалом. In the table. 1 shows the ratios of the starting components for the modification of formaldehyde-containing resins with oxidized starch.

В табл. 2 приведены режимы приготовления клеев, связующих, пропиточных растворов. In the table. 2 shows the modes of preparation of adhesives, binders, impregnating solutions.

В табл. 3, 3А приведены свойства связующих. In the table. 3, 3A show the properties of binders.

В табл. 4 - то же, прессованных материалов. In the table. 4 - the same, pressed materials.

Способ производства прессованных материалов включает взаимосвязанные между собой технологические операции - подготовку растительных частиц, подготовку смолы, смешивание растительных частиц и связующего, формирование ковра и прессование материалов с термообработкой, при этом подготовку смолы осуществляют с введением модификатора из группы резервных углеводов растений в количестве 0,1 - 99,9 м.ч. от веса смолы, при этом в качестве смолы используют формальдегидосодержащие олигомеры, а смешивание растительных частиц выполняют со связующим, имеющим связанный модификатором формальдегид, причем подготовку смолы производят с концентрацией 35 - 75 процентов, в качестве формальдегидосодержащих олигомеров используют мочевиноформальдегидную смолу, или используют меламиноформальдегидную смолу, или используют фенолоформальдегидную смолу, или используют алкидную смолу, или карбамидную смолу, или поликонденсационные смолы, или используют капралактам, или используют винилхлорид, или используют стирол, или используют капролактам, или используют акрилонитрил, или используют полистирол, или полиэтилен, или поливинилхлорид, или полиэтилентерефталат, или поликарбонаты, а в качестве модификатора принимают крахмал, или принимают окисленный крахмал, или гидролизованный крахмал, или принимают частицы, полученные из зерновых и/или крахмалосодержащих растений, или принимают декстрины, или камеди, или полисахариды. A method for the production of pressed materials involves interconnected technological operations — preparation of plant particles, preparation of resin, mixing of plant particles and a binder, carpet formation and pressing of materials with heat treatment, while preparation of the resin is carried out with the introduction of a modifier from the group of reserve carbohydrates of plants in an amount of 0.1 - 99.9 mph the weight of the resin, while formaldehyde-containing oligomers are used as the resin, and vegetable particles are mixed with a binder having formaldehyde bound by a modifier, the resin being prepared at a concentration of 35-75 percent, urea-formaldehyde resin is used as formaldehyde-containing oligomers, or melamine-formaldehyde resin is used or use a phenol-formaldehyde resin, or use an alkyd resin, or a urea resin, or polycondensation resins, or use capralactam, or use vinyl chloride, or use styrene, or use caprolactam, or use acrylonitrile, or use polystyrene, or polyethylene, or polyvinyl chloride, or polyethylene terephthalate, or polycarbonates, and starch is used as a modifier, or oxidized starch or hydrolyzed starch is used or take particles derived from cereals and / or starchy plants, or take dextrins, or gums, or polysaccharides.

Claims (25)

1. Способ производства прессованных материалов, включающий взаимосвязанные между собой подготовку растительных частиц, подготовку смолы, смешивание растительных частиц и связующего, формирование ковра и прессование материалов с термообработкой, отличающийся тем, что подготовку смолы осуществляют с введением модификатора из группы резервных углеводов растений в количестве 0,1-99,9 мас.ч. от веса смолы, при этом в качестве смолы используют формальдегидосодержащие олигомеры, а смешивание растительных частиц выполняют со связующим, имеющим связанный модификатором формальдегид. 1. A method for the production of pressed materials, including interconnected preparation of plant particles, preparation of resin, mixing of plant particles and a binder, carpet formation and pressing of materials with heat treatment, characterized in that the preparation of the resin is carried out with the introduction of a modifier from the group of reserve carbohydrates of plants in an amount of 0 1-99.9 parts by weight the weight of the resin, while formaldehyde-containing oligomers are used as the resin, and the mixing of plant particles is carried out with a binder having formaldehyde bound by a modifier. 2. Способ по п.1, отличающийся тем, что подготовку смолы производят с концентрацией 35-75%. 2. The method according to claim 1, characterized in that the preparation of the resin is carried out with a concentration of 35-75%. 3. Способ по п.1, отличающийся тем, что в качестве формальдегидосодержащих олигомеров используют мочевиноформальдегидную смолу. 3. The method according to claim 1, characterized in that urea-formaldehyde resin is used as formaldehyde-containing oligomers. 4. Способ по п.1, отличающийся тем, что в качестве формальдегидосодержащих олигомеров используют меламиноформальдегидную смолу. 4. The method according to claim 1, characterized in that melamine-formaldehyde resin is used as formaldehyde-containing oligomers. 5. Способ по п.1, отличающийся тем, что в качестве формальдегидосодержащих олигомеров используют фенолоформальдегидную смолу. 5. The method according to claim 1, characterized in that phenol-formaldehyde resin is used as formaldehyde-containing oligomers. 6. Способ по п.1, отличающийся тем, что в качестве формальдегидосодержащих олигомеров используют алкидную смолу. 6. The method according to claim 1, characterized in that alkyd resin is used as formaldehyde-containing oligomers. 7. Способ по п.1, отличающийся тем, что в качестве формальдегидосодержащих олигомеров используют карбимидную смолу. 7. The method according to claim 1, characterized in that the carbimide resin is used as formaldehyde-containing oligomers. 8. Способ по п.1, отличающийся тем, что в качестве формальдегидосодержащих олигомеров используют поликонденсационные смолы. 8. The method according to claim 1, characterized in that polycondensation resins are used as formaldehyde-containing oligomers. 9. Способ по п.1, отличающийся тем, что в качестве формальдегидосодержащих олигомеров используют капралактам. 9. The method according to claim 1, characterized in that capralactam is used as formaldehyde-containing oligomers. 10. Способ по п. 1, отличающийся тем, что в качестве формальдегидосодержащих олигомеров используют винилхлорид. 10. The method according to p. 1, characterized in that the formaldehyde-containing oligomers use vinyl chloride. 11. Способ по п. 1, отличающийся тем, что в качестве формальдегидосодержащих олигомеров используют стирол. 11. The method according to p. 1, characterized in that styrene is used as formaldehyde-containing oligomers. 12. Способ по п. 1, отличающийся тем, что в качестве формальдегидосодержащих олигомеров используют капролактам. 12. The method according to p. 1, characterized in that caprolactam is used as formaldehyde-containing oligomers. 13. Способ по п. 1, отличающийся тем, что в качестве формальдегидосодержащих олигомеров используют акрилонитрил. 13. The method according to p. 1, characterized in that as formaldehyde-containing oligomers use acrylonitrile. 14. Способ по п. 1, отличающийся тем, что в качестве формальдегидосодержащих олигомеров используют полистирол. 14. The method according to p. 1, characterized in that polystyrene is used as formaldehyde-containing oligomers. 15. Способ по п. 1, отличающийся тем, что в качестве формальдегидосодержащих олигомеров используют полиэтилен. 15. The method according to p. 1, characterized in that polyethylene is used as formaldehyde-containing oligomers. 16. Способ по п. 1, отличающийся тем, что в качестве формальдегидосодержащих олигомеров используют поливинилхлорид. 16. The method according to p. 1, characterized in that as the formaldehyde-containing oligomers use polyvinyl chloride. 17. Способ по п. 1, отличающийся тем, что в качестве формальдегидосодержащих олигомеров используют полиэтилентерефталат. 17. The method according to p. 1, characterized in that polyethylene terephthalate is used as formaldehyde-containing oligomers. 18. Способ по п. 1, отличающийся тем, что в качестве формальдегидосодержащих олигомеров используют поликарбонаты. 18. The method according to p. 1, characterized in that polycarbonates are used as formaldehyde-containing oligomers. 19. Способ по п.1, отличающийся тем, что в качестве модификатора принимают крахмал. 19. The method according to claim 1, characterized in that as a modifier take starch. 20. Способ по п.1, отличающийся тем, что в качестве модификатора принимают окисленный крахмал. 20. The method according to claim 1, characterized in that the oxidized starch is used as a modifier. 21. Способ по п.1, отличающийся тем, что в качестве модификатора принимают гидролизованный крахмал. 21. The method according to claim 1, characterized in that hydrolyzed starch is used as a modifier. 22. Способ по п.1, отличающийся тем, что в качестве модификатора принимают частицы, полученные из зерновых и крахмалосодержащих растений. 22. The method according to claim 1, characterized in that as a modifier accept particles obtained from grain and starch-containing plants. 23. Способ по п.1, отличающийся тем, что в качестве модификатора принимают декстрины. 23. The method according to claim 1, characterized in that as a modifier take dextrins. 24. Способ по п.1, отличающийся тем, что в качестве модификатора принимают камеди. 24. The method according to claim 1, characterized in that gum is taken as a modifier. 25. Способ по п.1, отличающийся тем, что в качестве модификатора принимают полисахариды. 25. The method according to claim 1, characterized in that as a modifier take polysaccharides.
RU2000110396A 2000-04-27 2000-04-27 Method for manufacture of moulded materials RU2165844C1 (en)