RU2076120C1 - Binder - Google Patents

Binder Download PDF

Info

Publication number
RU2076120C1
RU2076120C1 RU93021394A RU93021394A RU2076120C1 RU 2076120 C1 RU2076120 C1 RU 2076120C1 RU 93021394 A RU93021394 A RU 93021394A RU 93021394 A RU93021394 A RU 93021394A RU 2076120 C1 RU2076120 C1 RU 2076120C1
Authority
RU
Russia
Prior art keywords
lignosulfonate
binder
modifying additive
formaldehyde resin
product
Prior art date
Application number
RU93021394A
Other languages
Russian (ru)
Other versions
RU93021394A (en
Inventor
В.И. Соломатов
В.И. Бузулуков
В.Д. Черкасов
В.П. Селяев
В.А. Русаков
Original Assignee
Мордовский государственный университет им.Н.П.Огарева
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Мордовский государственный университет им.Н.П.Огарева filed Critical Мордовский государственный университет им.Н.П.Огарева
Priority to RU93021394A priority Critical patent/RU2076120C1/en
Publication of RU93021394A publication Critical patent/RU93021394A/en
Application granted granted Critical
Publication of RU2076120C1 publication Critical patent/RU2076120C1/en

Abstract

FIELD: building materials production. SUBSTANCE: proposed binder contains 45-75 mass % of phenol-formaldehyde resin and 25-55 mass % of modifying additive. Product of oxidation of lignosulfonate by Perhydrole at their ratio 19:1 respectively is used as mentioned above modifying additive. EFFECT: improves quality of desired product. 2 tbl

Description

Изобретение относится к производству строительных материалов и может быть использовано для изготовления древесностружечных плит. The invention relates to the production of building materials and can be used for the manufacture of chipboards.

Известно вяжущее для изготовления древесностружечных плит, содержащее карбамидную или фенолформальдегидную смолу и модифицирующую добавку [1]
Однако известное вяжущее имеет низкую прочность, а полученные на его основе материалы имеют низкую водостойкость.Known binder for the manufacture of chipboards containing urea or phenol-formaldehyde resin and a modifying additive [1]
However, the known binder has a low strength, and the materials obtained on its basis have a low water resistance.

Известно другое вяжущее, включающее фенолформальдегидную смолу и модифицирующую добавку на основе лигносульфоната [2]
Однако известное вяжущее также обладает невысокой прочностью, а получаемые древесностружечные плиты имеют низкую водостойкость.Another binder is known, including phenol-formaldehyde resin and a modifying additive based on lignosulfonate [2]
However, the known binder also has low strength, and the resulting chipboards have low water resistance.

Техническим результатом данного вяжущего является повышение прочности и водостойкости изготавливаемых на его основе древесностружечных плит. The technical result of this binder is to increase the strength and water resistance of wood chipboards made on its basis.

Для достижения технического результата в предлагаемом вяжущем, включающем фенолформальдегидную смолу и модифицирующую добавку на основе лигносульфоната, в качестве модифицирующей добавки оно содержит продукт окисления лигносульфоната пергидролем в весовом соотношении 19:1, при следующем соотношении компонентов, мас. To achieve a technical result in the proposed binder, including phenol-formaldehyde resin and a modifying additive based on lignosulfonate, as a modifying additive it contains the oxidation product of lignosulfonate with perhydrol in a weight ratio of 19: 1, in the following ratio of components, wt.

Фенолформальдегидная смола 45 75
Продукт окисления лигносульфоната пергидролем в соотношении 19:1 25 - 55
Пример. Продукт окисления лигносульфоната пергидролем это однородная густая жидкость, темно-коричневого цвета с плотностью 1230 1241 кг/м3, вязкость по ВЗ-1, содержанием сухих веществ 55 60% Продукт окисления получают в результате взаимодействия лигносульфоната с пергидролем, взятых в соотношении 19: 1 при температурной обработке 85oС в течение 2 ч. Образующийся продукт окисления совмещают с фенолформальдегидной смолой и затем полученное вяжущее наносят на древесные частицы. Готовые изделия получают путем прессования при 130 200oС и давлении 2,5 МПа.Phenol formaldehyde resin 45 75
The product of the oxidation of lignosulfonate perhydrol in a ratio of 19: 1 25 - 55
Example. The product of the oxidation of lignosulfonate by perhydrol is a uniform, thick, dark brown liquid with a density of 1230 1241 kg / m 3 , viscosity VZ-1, solids content of 55 60%. The oxidation product is obtained as a result of the interaction of lignosulfonate with perhydrol, taken in a ratio of 19: 1 at a temperature treatment of 85 o C for 2 hours. The resulting oxidation product is combined with phenol-formaldehyde resin and then the resulting binder is applied to wood particles. Finished products are obtained by pressing at 130,200 o C and a pressure of 2.5 MPa.

В табл. 1 и 2 приведены составы данного вяжущего и прототипа и физико-механические свойства древесных плит, полученных на основе этих вяжущих. In the table. 1 and 2 show the compositions of this binder and prototype and the physicomechanical properties of wood boards obtained on the basis of these binders.

Древесностружечные плиты, полученные на основе данного вяжущего, имеют высокие показатели прочности и водостойкости. Particle boards based on this binder have high strength and water resistance.

Claims (1)

Вяжущее, включающее фенолформальдегидную смолу и модифицирующую добавку на основе лигносульфоната, отличающееся тем, что в качестве модифицирующей добавки оно содержит продукт окисления лигносульфоната пергидролем в весовом соотношении 19 1 при следующем соотношении компонентов, мас. A binder comprising a phenol-formaldehyde resin and a modifying additive based on lignosulfonate, characterized in that as a modifying additive it contains the product of the oxidation of lignosulfonate with perhydrol in a weight ratio of 19 1 in the following ratio of components, wt. Фенолформальдегидная смола 45 75
Продукт окисления лигносульфоната пергидролем в соотношении 19 1 25 - 55Phenol formaldehyde resin 45 75
The product of the oxidation of lignosulfonate perhydrol in a ratio of 19 1 25 - 55
RU93021394A 1993-04-23 1993-04-23 Binder RU2076120C1 (en)