RU2163627C1

RU2163627C1 - Plastic lubricant

Info

Publication number: RU2163627C1
Application number: RU99121165/04A
Authority: RU
Inventors: О.М. Танатаров; И.Р. Хабибуллин
Original assignee: Танатаров Оскар Маратович; Хабибуллин Ирек Раисович
Priority date: 1999-10-06
Filing date: 1999-10-06
Publication date: 2001-02-27

Abstract

FIELD: lubrication of heavily loaded friction units of various mechanisms, more particularly, automobiles, tractors, and combines, and also conveyors in metallurgical industry. SUBSTANCE: lubricant comprises, wt.%: extract of selective purification of oils (petroleum extract) as basic oil, 65- 65.5; slurry of sulfate flows resulting from fatty acid production, 32-35; and calcium hydroxide, 2.0-2.5. EFFECT: improved quality of the lubricant and lower cost price thereof due to utilization of production waste. 3 tbl

Description

Изобретение относится к пластичным смазочным материалам и используется для смазывания тяжелонагруженных механизмов, в частности в основных узлах трения автомобилей, тракторов, комбайнов, а также конвейеров в металлургии. The invention relates to plastic lubricants and is used to lubricate heavily loaded mechanisms, in particular in the main friction units of cars, tractors, combines, as well as conveyors in metallurgy.

Известны пластичные смазки - солидолы, представляющие собой минеральные масла, сгущенные гидратированными кальциевыми мылами высших кислот синтетических или естественных жиров. Их применяют у нас в стране и за рубежом в механизмах, работающих при температурах до 60-70^oC. В настоящее время в странах СНГ выпускаются три марки солидолов: солидол Ж, солидол С и пресс-солидол /Гришин Н.Н., Шибраев С.Б. и др. Химмотология пластичных смазок. М., 1994, с.147/.Plastic greases are known - solid oils, which are mineral oils, condensed with hydrated calcium soaps of higher acids of synthetic or natural fats. They are used in our country and abroad in mechanisms operating at temperatures up to 60-70 ^o C. At present, three grades of solidols are produced in the CIS countries: solidol Zh, solidol C and press solidol / Grishin N.N., Shibraev S.B. and others. Chemotology of greases. M., 1994, p. 147 /.

Наиболее близкой по технической сущности и достигнутому результату к заявляемому изобретению является водостойкая смазка - солидол синтетический (солидол С), предназначенная для смазывания узлов трения, качения и скольжения машин и механизмов, работающих от минус 20^oC до плюс 65^oC, содержащая смесь индустриальных масел И-40А и И-20А, синтетических жирных кислот (СЖК) фракций C₁₈-C₂₂ и C₅-C₉ и гидроокись кальция /ГОСТ 4366-76 Солидол синтетический/.The closest in technical essence and the achieved result to the claimed invention is a waterproof lubricant - synthetic solid oil (solid oil C), intended for lubrication of friction, rolling and sliding units of machines and mechanisms operating from minus 20 ^o C to plus 65 ^o C, containing a mixture of industrial oils I-40A and I-20A, synthetic fatty acids (FFA) fractions C ₁₈ -C ₂₂ and C ₅ -C ₉ and calcium hydroxide / GOST 4366-76 Synthetic solidol /.

Недостатком смазки-прототипа является недостаточно высокие адгезионно-когезионные качества, недостаточная ингибирующая активность, высокая стоимость и узкий спектр сырьевой базы СЖК. The disadvantage of the prototype lubricant is insufficiently high adhesive-cohesive qualities, insufficient inhibitory activity, high cost and a narrow range of raw materials FFA.

Предлагаемое изобретение решает задачу повышения качества смазки, снижения ее себестоимости, а также расширения сырьевой базы. The present invention solves the problem of improving the quality of the lubricant, reducing its cost, as well as expanding the raw material base.

Сущность изобретения заключается в том, что смазка, включающая базовое масло, синтетические жирные кислоты и гидроокись кальция, согласно изобретению содержит в качестве базового масла экстракт селективной очистки масел 3-4 фракций (экстракт нефтяной), а в качестве СЖК - отход их производства - шлам сульфатных стоков со стадии промывки оксидата после обработки H₂SO₄ и NaOH, который идет на сброс в шламовые амбары, представляющие собой смесь недоокисленных парафинов и СЖК широких фракций (C₅-C₇, C₉-C₁₂, C₁₈ и выше), при следующем соотношении компонентов, мас.%:
Экстракт селективной очистки масел - 63,0-65,5
Шлам сульфатных стоков производства СЖК - 32,0-35,0
Гидроокись кальция - 2,0-2,5
Предлагаемая смазка готовится следующим образом. В реактор загружается расчетное количество предварительно отфильтрованного шлама сульфатных стоков производства СЖК, включается обогрев реактора и, после расплавления шлама, загружается расчетное количество экстракта селективной очистки масел. Затем включается перемешивающее устройство и смесь нагревается до 75-80^oC со скоростью 15-20 град/час. Готовится исходная смесь гидроокиси кальция в небольшом количестве экстракта селективной очистки масел (возможно приготовление известкового молока из расчетного количества "пушонки" и 3% воды от общей загрузки компонентов). Готовая суспензия загружается в реактор и реакционная смесь перемешивается в течение 1,5-2 часов при температуре 95-98^oC. В ходе реакции через каждые 30 минут отбираются пробы на текущий анализ. Ходовые анализы состоят из: 1) определения кислотного числа, которое должно равняться 0; 2) определения температуры каплепадения Т_кп > 80^oC; 3) визуального определения пенетрации и прозрачности смазки на стеклянной пластине.The essence of the invention lies in the fact that the lubricant, including the base oil, synthetic fatty acids and calcium hydroxide, according to the invention contains an extract of selective purification of oils of 3-4 fractions (petroleum extract) as the base oil, and the production waste is sludge as the FFA sulfate effluents from the washing stage of the oxidate after treatment with H ₂ SO ₄ and NaOH, which is discharged into sludge pits, which are a mixture of under-oxidized paraffins and FFA of wide fractions (C ₅ -C ₇ , C ₉ -C ₁₂ , C ₁₈ and higher) , in the following ratio of components entov, wt.%:
Extract of selective oil purification - 63.0-65.5
Sludge sludge from the production of SJK - 32.0-35.0
Calcium hydroxide - 2.0-2.5
The proposed lubricant is prepared as follows. The calculated amount of pre-filtered sludge sludge sludge from the FFA production is loaded into the reactor, the reactor heating is turned on and, after the sludge is melted, the calculated amount of the selective oil treatment extract is loaded. Then the mixing device is turned on and the mixture is heated to 75-80 ^o C at a speed of 15-20 degrees / hour. An initial mixture of calcium hydroxide is prepared in a small amount of selective oil purification extract (it is possible to prepare milk of lime from the calculated amount of fluff and 3% water from the total load of the components). The finished suspension is loaded into the reactor and the reaction mixture is stirred for 1.5-2 hours at a temperature of 95-98 ^o C. During the reaction, samples are taken every 30 minutes for the current analysis. Running analyzes consist of: 1) determining the acid number, which should be 0; 2) determine the dropping point T _KP > 80 ^o C; 3) visual determination of penetration and transparency of the lubricant on the glass plate.

При получении положительных анализов готовая смазка сливается в тару. Upon receipt of positive tests, the finished grease is poured into the container.

Проведен ряд испытаний по подбору компонентов и оценке качества получаемой смазки. Были приготовлены составы смазок, приведенные в табл. 1. Для сравнения был взят известный состав смазки - прототип солидол С (синтетический). A series of tests were conducted to select components and evaluate the quality of the resulting lubricant. Were prepared lubricant compositions shown in table. 1. For comparison, a well-known lubricant composition was taken - a prototype solidol C (synthetic).

В табл. 2 приведены данные по испытанию смазок 1 - 3. In the table. 2 shows the test data for lubricants 1 - 3.

Как видно из табл.2, все опробованные смазки отвечают требованиям ГОСТ 4366-76 для солидола С, а по некоторым даже превосходят его, например температура каплепадения предлагаемой смазки составила 85-90^oC (по ГОСТ 4366-76 - 75^oC), это тот показатель от которого зависит рабочая температура использования смазки.As can be seen from table 2, all tested lubricants meet the requirements of GOST 4366-76 for solidol C, and even surpass it in some, for example, the dropping point of the proposed lubricant was 85-90 ^o C (according to GOST 4366-76 - 75 ^o C), this is the indicator on which the operating temperature of the use of the lubricant depends.

Ингибирующая способность предлагаемой смазки выше, чем у стандартного солидола, за счет присутствия в ней небольшого числа эфирных соединений. The inhibitory ability of the proposed lubricant is higher than that of standard solidol, due to the presence of a small number of ether compounds in it.

Из-за вовлечения в процесс получения смазки неомыляемых веществ - парафинов, в количестве до 40% от объема шлама сульфатных стоков производства СЖК предлагаемая смазка по своему типу является мыльно-углеводородной в отличии от солидола (мыльная смазка), что обуславливает ее лучшие адгезионно-когезионные свойства. Due to the involvement of unsaponifiable substances — paraffins — in the amount of up to 40% of the sludge volume from the production of FFA in the lubricant production process, the proposed lubricant is soap-hydrocarbon in type, unlike solid oil (soap lubricant), which leads to its best adhesive-cohesive properties.

Использование в качестве компонента предлагаемой смазки дешевых экстрактов селективной очистки масел вместо дорогостоящих индустриальных масел И-20А и И-40А снижает себестоимость продукции в 2 раза и повышает рентабельность производства до 50%. The use of cheap extracts of selective oil purification as a component of the proposed lubricant instead of expensive industrial oils I-20A and I-40A reduces the cost of production by 2 times and increases the profitability of production up to 50%.

Замена синтетических жирных кислот фракций C₁₈-C₂₂ и C₅-C₉ на отход производства СЖК, идущий на сброс в шламовые амбары, а именно на сульфатный шлам, представляющий собой смесь недоокисленных парафинов и СЖК широких фракций (C₅-C₇, C₉-C₁₂, C₁₆ и т.д.), расширяет сырьевую базу производства смазок, а также снижает себестоимость производства.Replacement of synthetic fatty acids of fractions C ₁₈ -C ₂₂ and C ₅ -C ₉ with waste products of FFA, which is discharged into sludge pits, namely with sulfate sludge, which is a mixture of unoxidized paraffins and FFA of wide fractions (C ₅ -C ₇ , C ₉ -C ₁₂ , C ₁₆ , etc.), expands the raw material base for the production of lubricants, and also reduces the cost of production.

Расчет затрат на сырье производства предлагаемой смазки подтвердил эффективность подобного рода производств и снижение в 2-3 раза себестоимости по сравнению с выпускаемым солидолом С на ОАО "Башнефтехим". Calculation of the cost of raw materials for the production of the proposed lubricant confirmed the effectiveness of this kind of production and a 2-3-fold reduction in cost compared to the produced solidol C at OAO Bashneftekhim.

Технико-экономическое обоснование эффективности промышленного производства смазки на базе сульфатного шлама (нефтешлам) и экстракта селективной очистки масел (экстракт нефтяной), расчет себестоимости по сравнению с выпускаемым солидолом С на ОАО "Башнефтехим" приведен в табл. 3 /Прайс-лист на основную продукцию предприятия ОАО "Башнефтехим", 01.08.99., Прайс-лист на продукцию Учелинского ГОК, 01.09.99./. A feasibility study of the efficiency of industrial production of grease based on sulphate sludge (oil sludge) and an extract for the selective purification of oils (oil extract), the cost calculation in comparison with the produced solidol C at OAO Bashneftekhim is given in table. 3 / Price list for the main products of the enterprise Bashneftekhim OJSC, 08/01/99., Price list for the products of the Uchelinsky GOK, 09/01/99./.

Предлагаемое изобретение может быть реализовано в нефтехимической и нефтеперерабатывающей промышленности, а именно в производстве пластичных смазок, которые могут быть использованы для смазывания тяжелонагруженных механизмов - основных узлов трения автомобилей, тракторов, комбайнов, а также конвейеров в машиностроении и металлургии. The present invention can be implemented in the petrochemical and oil refining industries, namely in the production of greases, which can be used to lubricate heavily loaded mechanisms - the main friction units of cars, tractors, combines, as well as conveyors in mechanical engineering and metallurgy.

Claims

A grease for heavily loaded friction units containing a base oil, synthetic fatty acids and calcium hydroxide, characterized in that the base oil is an extract of selective oil refining (petroleum extract), and synthetic fatty acids are sulphate sludge from synthetic fatty acids (FFA) in the following ratio of components, wt.%:
Extract of selective oil purification - 63 - 65.5
Sludge sludge sludge produced by SJK - 32 - 35
Calcium hydroxide - 2.0 - 2.5