RU2102351C1 - Polymer mineral mixture - Google Patents

Polymer mineral mixture Download PDF

Info

Publication number
RU2102351C1
RU2102351C1 SU4922554A RU2102351C1 RU 2102351 C1 RU2102351 C1 RU 2102351C1 SU 4922554 A SU4922554 A SU 4922554A RU 2102351 C1 RU2102351 C1 RU 2102351C1
Authority
RU
Russia
Prior art keywords
mixture
white
cement
polymer
portland cement
Prior art date
Application number
Other languages
Russian (ru)
Inventor
Валерий Васильевич Пахарьков
Original Assignee
Валерий Васильевич Пахарьков
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Валерий Васильевич Пахарьков filed Critical Валерий Васильевич Пахарьков
Priority to SU4922554 priority Critical patent/RU2102351C1/en
Application granted granted Critical
Publication of RU2102351C1 publication Critical patent/RU2102351C1/en

Abstract

FIELD: as coating by marking highways; as finishing and decorative coatings for building constructions. SUBSTANCE: polymer mineral mixture comprises, mas. %: butadiene-styrene latex or polyvinyl acetate dispersion, 6-7; white portland cement, 20-21; slaked lime, 8-10; white quartz sand, 26-28; or its mixture with swollen vermiculite, 12-15; nitrocellulose varnish 15-16; water, the balance. Compressive strength of sample is 350 kgf/cm2 or more, cohesion strength is 10 kgf/cm2 or more, period of drying (hardening) is 40-60 min, useful life is not less than 10 years. EFFECT: improved quality of product.

Description

Полимерминеральная смесь предназначается, в основном, в качестве покрытия при разметке проезжей части дорог и может быть использовано в различных отраслях народного хозяйства, например для отделочно-декоративных покрытий при строительстве зданий и сооружений. Polymermineral mixture is intended mainly as a coating for marking the carriageway and can be used in various sectors of the economy, for example, for decorative coatings in the construction of buildings and structures.

Известна композиция для отделочных работ, включающая, мас. дивинилстирольный лактекс 1,5-3,0, известняковый порошок 71-75, жидкое натриевое стекло 2,0-4,0, вода остальное /1/. Known composition for finishing work, including, by weight. divinyl styrene lactex 1.5-3.0, limestone powder 71-75, liquid sodium glass 2.0-4.0, water the rest / 1 /.

Наиболее близкий по технической сущности к достигаемому результату к заявляемой является полимерминеральная смесь, включающая, мас. The closest in technical essence to the achieved result to the claimed is a polymer-mineral mixture, including, by weight.

Стабилизированный дивинилстирольный латекс 7,0-7,2
Портландцемент 15,8-16,0
Кварцевый песок 65,0-67,0
Гашеная известь 2,1-2,5
Вода Остальное /2/.Stabilized divinyl styrene latex 7.0-7.2
Portland cement 15.8-16.0
Quartz sand 65.0-67.0
Slaked lime 2.1-2.5
Water The rest / 2 /.

Решение технической задачи направлено на повышение атмосферостойкости, прочности и ускорение процесса отверждения. The solution to the technical problem is aimed at improving weather resistance, strength and accelerating the curing process.

Это достигается тем, что полимерминеральная смесь для отделочно-декоративных покрытий, включающая полимерное связующее, цемент, известь гашеную, минеральный наполнитель и воду, дополнительно содержит нитроцеллюлозный лак НЦ 134, в качестве полимерного связующего бутадиенстирольный латекс или поливинилацетатную дисперсию, в качестве цемента белый портландцемент, а в качестве минерального наполнителя песок кварцевый белый или его смесь со вспученным вермикулитом в количествах соответственно 26-28 мас. и 12-15 мас. при следующем соотношении компонентов, мас. This is achieved by the fact that the polymer-mineral mixture for decorative coatings, including a polymer binder, cement, slaked lime, mineral filler and water, additionally contains NTs 134 nitrocellulose varnish, styrene-butadiene latex or polyvinyl acetate dispersion as a polymer binder, white Portland cement as a cement, and as a mineral filler, white quartz sand or its mixture with expanded vermiculite in amounts of 26-28 wt. and 12-15 wt. in the following ratio of components, wt.

Указанное полимерное связующее 6-7
Портландцемент белый 20-21
Известь гашеная 8-10
Указанный минеральный 38-43
Наполнитель нитроцеллюлозный лак НЦ 134 15-16
Вода Остальное.The specified polymer binder 6-7
Portland cement white 20-21
Slaked lime 8-10
Specified Mineral 38-43
Filler nitrocellulose varnish NTs 15 15-16
Water The rest.

Смесь приготавливают в смесителе типа СБ-43 в следующем порядке: сначала в смеситель загружают песок, цемент или песок, цемент и вермикулит и тщательно их перемешивают. Затем сухую смесь затворяют эмульсией, приготовленной из бутадиенстирольного латекса или поливинилацетатной дисперсии, нитроцеллюлозного лака, гашеной извести и воды. Смесь вновь перемешивают до готовности рабочей консистенции. The mixture is prepared in a mixer of type SB-43 in the following order: first, sand, cement or sand, cement and vermiculite are loaded into the mixer and mixed thoroughly. Then the dry mixture is closed with an emulsion made from styrene-butadiene latex or polyvinyl acetate dispersion, nitrocellulose varnish, slaked lime and water. The mixture is again mixed until a working consistency is obtained.

Характеристики используемых компонентов:
Латекс 50ГПС ГОСТ 14053-78
или поливинилацетатная дисперсия ПВАД Д50Н
ГОСТ 18992-80
Портландцемент белый ПЦ 400 ГОСТ 965-66
Известь гашеная ГОСТ 9179-70
Песок кварцевый белый фракции до 0,3. ГОСТ 8736-67.Characteristics of the components used:
Latex 50GPS GOST 14053-78
or polyvinyl acetate dispersion PVAD D50N
GOST 18992-80
Portland cement white PC 400 GOST 965-66
Slaked lime GOST 9179-70
Sand quartz white fractions up to 0.3. GOST 8736-67.

Лак нитроцеллюлозный НЦ 134 ТУ 6-10-1291-77
Лак НЦ 134 раствор нитрата целлюлозы и смол в смеси органических растворителей, представляющий собой жидкость светло-желтого цвета, рабочая вязкость 28-30с по визкозиметру В34, температура сушки 18-22oC, продолжительность высыхания от пыли не более 10 минут.Nitrocellulose varnish NTs 134 TU 6-10-1291-77
Varnish SC 134 a solution of cellulose nitrate and resins in a mixture of organic solvents, which is a light yellow liquid, working viscosity 28-30 s on a B34 viscometer, drying temperature 18-22 o C, drying time from dust no more than 10 minutes.

Прочность образцов из предлагаемой полимерминеральной смеси на сжатие составляет ≥350 кгс/см2, на сцепление ≥10 кгс/см2, время высыхания /твердения/ 40-60 минут, истираемость 0,003-0,05 г/см2, подвижность 25-30 см /по осадке конуса/, долговечность не менее 10 лет, коэффициент светоотражения смеси без вермикулита ≥0,6 усл. ед. с вермикулитом ≥7 усл. ед.The compressive strength of samples of the proposed polymer-mineral mixture is ≥350 kgf / cm 2 , adhesion ≥10 kgf / cm 2 , drying / hardening time / 40-60 minutes, abrasion 0.003-0.05 g / cm 2 , mobility 25-30 cm / cone settlement /, durability at least 10 years, light reflectance of the mixture without vermiculite ≥0.6 conv. units with vermiculite ≥7 conv. units

Claims (1)

Полимерминеральная смесь для отделочно-декоративных покрытий, преимущественно для дорожной разметки, включающая полимерное связующее, цемент, известь, гашеную, минеральный наполнитель и воду, отличающаяся тем, что она дополнительно содержит нитроцеллюлозный лак НЦ 134, в качестве полимерного связующего бутадиенстирольный латекс или поливинилацетатную дисперсию, в качестве цемента белый портландцемент, а в качестве минерального наполнителя песок кварцевый белый или его смесь со вспученным вермикулитом в количествах соответственно 26 28 мас. и 12 15 мас. при следующем соотношении компонентов, мас. A polymer-mineral mixture for decorative coatings, mainly for road marking, including a polymer binder, cement, lime, slaked, mineral filler and water, characterized in that it additionally contains NTs 134 nitrocellulose varnish, butadiene-styrene latex or polyvinyl acetate dispersion as a polymer binder, white Portland cement as cement, and white quartz sand as a mineral filler or its mixture with expanded vermiculite in amounts, respectively 26 28 wt. and 12 to 15 wt. in the following ratio of components, wt. Указанное полимерное связующее 6 7
Портландцемент белый 20 21
Известь гашеная 8 10
Указанный минеральный наполнитель 38 43
Нитроцеллюлозный лак НЦ 134 15 16
Вода ОстальноееSpecified polymer binder 6 7
Portland cement white 20 21
Slaked lime 8 10
Specified mineral filler 38 43
Nitrocellulose lacquer NTs 15 15 16
Water Rest
SU4922554 1991-02-04 1991-02-04 Polymer mineral mixture RU2102351C1 (en)